New and revised materials and properties in MPDB v9.95 as compared to v9.93

Key to property symbols (number of datasets):

DLL = Linear thermal expansion (ΔL/L)	MTE = Mean coefficient of thermal expansion	CTE = Coefficient of thermal expansion	D = Density	AV = Apparent viscosity
TC = Thermal conductivity	SH = Specific heat	HC = Heat capacity	TD = Thermal diffusivity	SV = Specific volume
RHO = Electrical resistivity	SIGMA = Electrical conductivity	SRHO = Surface electrical resistivity	Vis = Viscosity	FS = Flexural strength
E = Elastic/Young's modulus	G = Shear modulus	v = Poisson's ratio	K = Bulk modulus	FM = Flexural modulus
SSC = True stress-strain curve (tension)	SSCC = True stress-strain curve (compression)	HE = Hemispherical total emissivity	NE = Normal total emissivity	ESSC = Engineering stress-strain curve (tension)
UTS = Tensile strength	YS = Yield strength (tension)	UCS = Compressive strength	YSC = Yield strength (compression)	%El = Elongation
FSN = Fatigue S-N curve	FEN = Fatigue ε-N curve	SR = Stress rupture	CRS = Creep strength	ESSCC = Engineering stress-strain curve (compression)
RPB = Relative permeability	AP = Absolute permeability	BH = B-H curve	HB = H-B curve	CRM = Creep modulus
DCRPT = Relative permittivity	DF = Dissipation factor	CL = Core loss	EP = Exciting Power	IC = Isochronous creep
RIW = Refractive index vs λ	RIT = Refractive index vs T	TWL = Transmission vs λ	ST = Surface tension	CRR = Stress vs Creep rate
S = Seebeck coefficient	VP = Vapor pressure

"(N)" indicates the data is new, "(R)" indicates the data has been revised, * indicates the data is the room temperature value only

171 new materials, 3049 new property sets, 146 revised properties, and 1163 new room temperature values

Acetal/POM (polyoxymethylene)

Delrin 100	Delrin 500 (Revised)	Iupital ET-35	Iupital ET-20 (New)	Iupital F30-05 (Revised)
Iupital F40-03 (Revised)	Iupital F10-01 (Revised)	Iupital F10-02 (Revised)	Iupital F20-03 (Revised)	Iupital F20-05 (Revised)
Iupital F20-54 (Revised)	Iupital F20-61 (Revised)	Iupital F30-03 (Revised)	Iupital F10-EW (Revised)	Iupital F20-73R2
Iupital F20-73R1	Iupital F30-73R1 (New)	Iupital F20-55R2 (New)	Iupital FG2025 MZ (New)	Iupital FG2030 (New)
Iupital FX-11JR1 (New)	Iupital FX-11R1 (New)	Iupital MAH25 (New)	Iupital MAL40 (New)	Iupital MAL20 (New)
Iupital MAS30 (New)	Iupital MAS20 (New)	Iupital ST1700 (New)	Iupital ST1800 (New)	Iupital ST2000 (New)
Iupital ST1600 (New)	Iupital ST1700R2 (New)	Iupital ST1800R2 (New)	Iupital TC3030 (New)

Aluminum alloys

2024	2117	2219	4032	5182
6061	6082	6110	7039	7075
333.0	2043 (New)	2139 (New)	2050 (New)	3004 (Revised)
4047 (Revised)	6060 (Revised)	A319	2A12	2A50
A360.0 (Revised)	Al - 25 Si (wt %)	Al - 30 Si (wt %)	Al - 35 Si (wt %)	Al - 41 Si (wt %)
Al - 51 Si (wt %)	Al - 90 Si (wt %)	Al - 12.6 Si (wt %)	Al - 13 Si (wt %)	Al - 15 Si (wt %)
Al - 17 Si (wt %)	Al - 20 Si (wt %)	Al - 22 Si (wt %)	Al - 65 Si (wt %) (New)	Al - 80 Si (wt %) (New)
Al - 60 Si (wt %) (New)	Al - 6 Zn - 2 Mg - 0.5 Ni - 0.3 Fe (wt %) (New)	AlSi8Cu3	Scalmalloy

Carbides

SiC (alpha)

Carbons

Graphite ATJ

Cast irons

A297 HF (20 Cr - 10 Ni (wt %))	A297 HK (26 Cr - 20 Ni (wt %))	Ductile iron ASTM 80-55-06 (EN-GJS-600) (3.6 C - 2.7 Si - 0.2 Mn (wt %))	Gray iron (BS416-2) (New)	JIS FC170 (Revised)
Spherical cast iron (EN-GJS-500-14 5.3109) (New)

Cobalt alloys

Haynes 25 (L-605)

Complex oxides, Silicates, & Slags

MgV₂O₆ (New)

Y₃Al₅O₁₂ (YAG)

90.6 ZrO₂ - 9.4 Y₂O₃ (mol %)

Controlled expansion alloys

Kovar (alloy F15)

Copper alloys

Cu - 10 Al (wt %)	Cu - 30 Ni (wt %)	Cu - 45 Ni (wt %)	Cu - 10 Ni (wt %) (Revised)	Cu - 15 Zn (wt %)
UNS C11000 (ETP)	UNS C10200 (OFHC/OF)	UNS C95200	UNS C10800	UNS C10500
UNS C14200	UNS C14500	UNS C22000	UNS C23000	UNS C26000
UNS C28000	UNS C43500	UNS C46400	UNS C51000	UNS C52400
UNS C63000	UNS C63200	UNS C65100	UNS C71500	UNS C72150
UNS C94700	UNS C96200 (Revised)	UNS C71000 (Revised)

Electro-ceramics

Li₇Sn₃ (Revised)	Li₁₇Sn₄ (Revised)	Li₇Sn₂ (Revised)	Li₁₃Sn₅ (Revised)	Nd₀_.₇Ca₀_.₃CoO₃ (New)
Pr₀_.₉Ca₀_.₁CoO₃ (New)	Pr₀_.₇Ca₀_.₃CoO₃ (New)	(Pr₀_.₈₅Y₀_.₁₅)₀_.₇Ca₀_.₃CoO₃ (New)	(Pr₀_.₉₂₅Y₀_.₀₇₅)₀_.₇Ca₀_.₃CoO₃ (New)

Elements

Aluminum (Revised)	Copper	Lithium	Magnesium	Rhenium
Silver	Tantalum	Tin

Foods

Spaghetti (New)

Intermetallics

KBaBi (New)

Iron alloys

19-9 DX	15-7 Mo PH	17-4 PH	4340	8620
1045	301	302	303	304
308	321	347	405	410
414	420	422	430	4120
4130	4140	431 (Revised)	52100 (Revised)	316 (Revised)
A572 Grade 50	Alloy 709 (NF 709)	AM-350	API X52 pipeline steel (New)	ASME P92 (9 Cr - 0.5 Mo - 2 W (wt %))
CF3	CF8	CF20	2.25 Cr - 1 Mo (ASTM A542) (Revised)	E235
EOS StainlessSteel CX	ER70S-6	Fe - 30 Mn - 5 Al - 1 C + x Mo (wt %) (New)	Greek Ascoloy	304H
316H	HR CP980 SF (New)	HR CP800 SF (New)	HR3C	Incoloy 904 (904L)
Incoloy 800	Incoloy A-286	Incoloy 800H & 800HT	304L	316L
304LN	301LN	422M	Maraging 300 (C-type)	Maraging 250 (C-type)
20MnMoNi5-5 (New)	P91 (9 Cr - 1 Mo (wt %))	S690 / S690QL	S700	SAE 9254 (New)

LCP (liquid crystal polymer)

Kevlar 29 (New)

Magnesium alloys

AE44	AE42	AM60	AM30	AM50
AS21 (New)	AT72 (New)	AT73 (New)	AT51 (New)	AT52 (New)
AT53 (New)	AT61 (New)	AT62 (New)	AT63 (New)	AT71 (New)
AX61 (New)	AZ61 + CaO additions (New)	AZ91 - 0.3 Ca - 0.2 Y (wt %) (New)	AZ61	AZ31
AZ80	AZ91	BA53 (New)	EW75 (New)	EZ33 (Revised)
GW92K (New)	HK31	HM21	LZ91 (New)	Mg + 4 wt% Rare earths (New)
Mg + 5 wt% Rare earths (New)	Mg - 3 Al - 0.6 Ca - 0.2 Gd (wt %) (New)	Mg - 1 Al - 1 Ca - 0.4 Mn (wt %) (New)	Mg - 3 Al - 0.6 Ca (wt %) (New)	Mg - 4 Al - 2 Sn - 0.5 Y - 0.4 Nd (wt %) (New)
Mg - 1 Al (wt %)	Mg - 3 Al (wt %)	Mg - 5 Al (wt %)	Mg - 10 Al (wt %)	Mg - 0.5 Al (wt %)
Mg - 0.23 Ca (wt %) (New)	Mg - 0.3 Ca (wt %) (New)	Mg - 0.5 Ca (wt %) (New)	Mg - 1 Ca (wt %) (New)	Mg - 1.4 Ca (wt %) (New)
Mg - 0.1 Ca (wt %) (New)	Mg - 2 Gd - 0.5 Mn (wt %) (New)	Mg - 7 Gd - 4 Y - 1 Nd - 0.5 Zr (wt %) (New)	Mg - 10 Gd - 1.7 Y - 1 Zn - 0.5 Zr (wt %) (New)	Mg - 10 Gd - 3 Y - 0.1 Zn - 0.4 Zr (wt %) (New)
Mg - 8.3 Gd - 4 Y - 1 Zn - 0.4 Zr (wt %) (New)	Mg - 9 Gd - 3 Y - 1.5 Zn - 0.8 Zr (wt %) (New)	Mg - 9 Gd - 4 Y - 2 Zn - 0.5 Zr (wt %) (New)	Mg - 10 Gd - 3 Y - 0.5 Zr (wt %) (New)	Mg - 8.1 Gd - 4.5 Y - 0.3 Zr (wt %) (New)
Mg - 14 Gd - 0.4 Zr (wt %) (New)	Mg - 8 Li - 3 Al - 2 Zn - 0.5 Y (wt %) (New)	Mg - 21 Li (at %) (New)	Mg - 25 Li (at %) (New)	Mg - 30 Li (at %) (Revised)
Mg - 0.2 Mn (wt %) (New)	Mg - 0.5 Mn (wt %) (New)	Mg - 0.9 Mn (wt %) (New)	Mg - 1.3 Mn (wt %) (New)	Mg - 0.1 Mn (wt %) (New)
Mg - 2 Sn - x Yb (at %) (New)	Mg - 7.7 Sn (wt %) (New)	Mg - 11.7 Sn (wt %) (New)	Mg - 13.5 Sn (wt %) (New)	Mg - 2.6 Sn (wt %) (New)
Mg - 5.1 Sn (wt %) (New)	Mg - 4 Y - 3.5 Nd (wt %) (New)	Mg - 6.8 Y - 2.5 Zn (wt %)	Mg - 2 Y - 8 Zn (wt %) (New)	Mg - 6 Y - 6 Zn (wt %) (New)
Mg - 7 Y - 3 Zn (wt %) (New)	Mg - 1 Y - 6 Zn (wt %) (New)	Mg - 1.1 Y (wt %)	Mg - 2 Y (wt %)	Mg - 3 Y (wt %) (New)
Mg - 5.3 Zn - 0.6 Ca (wt %) (New)	Mg - 6 Zn - 1 Gd - 1 Er (wt %) (New)	Mg - 4.4 Zn - 0.9 Gd (wt %) (New)	Mg - 4.4 Zn - 2.1 Gd (wt %) (New)	Mg - 4.25 Zn - 0.4 Gd (wt %) (New)
Mg - 5 Zn - 4.5 Sn - x Sc (wt %) (New)	Mg - 6 Zn - 1 Y - 1 Ca (wt %) (New)	Mg - 1 Zn (wt %) (New)	Mg - 4.4 Zn (wt %) (New)	Mg - 1 Zr - 0.5 Sr - 1.5 Ho (wt %) (New)
Mg - 1 Zr - 0.5 Sr - 4 Ho (wt %) (New)	Mg - 1 Zr - 0.5 Sr - 0.5 Ho (wt %) (New)	Mg - 0.75 Zr (wt %) (New)	Mg - 1 Zr (wt %) (New)	Mg - 0.1 Zr (wt %) (New)
Mg - 0.25 Zr (wt %) (New)	Mg - 0.4 Zr (wt %) (New)	NZ31 (New)	QE22 (Revised)	WE43 (Revised)
ZE10	ZE20 (New)	ZEK100	ZK60	ZM21
ZX11 (New)

Minerals, Rocks, & Soils

Shot-earth 772 (New)

Nickel alloys

CMSX-4 (Revised)	ERNiCr-3 weld metal	Haynes 282	INCO weld A	Inconel 600
Inconel 718 (Revised)	Inconel HX / Hastelloy X / Nimonic PE13	Inconel MA 754	Monel 400	Ni-Ti (Nitinol)
Nickel TD	Rene 95	TD-NiCr	Udimet 500	Waspaloy

Nylons & PA/PI (polyamides/polyimides)

EXTEM RH1017UCL (Revised)	EXTEM VH1003	EXTEM VH1003F	EXTEM VH1003M	EXTEM VH1003P
EXTEM XH2315 (New)	EXTEM XH2115 (New)	EXTEM XH1015UCL	Zytel HTNWRF51MP20 (Revised)

Other materials

Glyptal (New)

Oxides

Al₂O₃ (alpha)

BeO

ThO₂

PAEK & PEEK (polyaryletherketone)

14% short glass fiber PEEK (PEEK-GF14) (New)

PC (polycarbonates) & blends

Apec 1895	Apec 1897	Makrolon 2407	Makrolon AG2477 DQ	Makrolon AG2677
Makrolon AG2477	Makrolon Ai2675 ST (New)	Makrolon Ai2497 ST (New)	Makrolon Ai2417	Makrolon Ai2415 (New)
Makrolon AL2647	Makrolon AX ST (New)	Makrolon AX2477	Makrolon LED2245	Makrolon OD2015

PLA (polylactic acid)

PLA

PMMA, PMMI, & Acrylics

5105XP acrylate

Polyesters

Selectron 44 polyester

Precious metal & Rare earth alloys

Ag - 0.674 Au (wt %)

Refractory metal alloys

Nb - 2 Cr (wt %) (New)	Nb - 5 V (wt %) (B-33)	Nb - 3 Zr (wt %) (New)	Ta - 10 Mo (wt %) (New)	Ta - 2.5 Mo (wt %) (New)
Ta - 5 Mo (wt %) (New)	Ta - 7.5 Mo (wt %) (New)	Ta - 8 W - 2 Hf (wt %) (T-111)	Ta - 10 W - 2.5 Hf (wt %) (T-222) (New)	Ta - 5 W - 2.5 Mo - 0.5 Zr - 0.07 C (wt %) (New)
Ta - 10 W - 2.5 Mo (wt %)	Ta - 5 W - 5 Mo (wt %) (New)	Ta - 5 W - 2.5 Mo (wt %) (New)	Ta - 7.5 W - 2.5 Mo (wt %) (New)	Ta - 5 W (wt %)
Ta - 10 W (wt %)	Ta - 20 W (wt %) (New)	V - 10 Cr - 5 Ti (wt %)	V - 4 Cr - 4 Ti (wt %)	Zircaloy-2

Resistance alloys

CB Cupron

FERRY alloy

Kanthal Cuprothal 49

Salts (binary mixtures; KCHO₂-LiClO₄)

75 KCl - 25 RbCl (mol %)

25 KCl - 75 RbCl (mol %)

50 KCl - 50 RbCl (mol %)

Salts (monatomic; Br & Cl)

KCl (Revised)

NbCl₅

RbCl (Revised)

Salts (polyatomic)

PbWO₄

Salts (ternary mixtures)

35 KCl - 35 NaCl - 30 NbCl₅ (mol %) (New)	5 KCl - 5 NaCl - 90 NbCl₅ (mol %) (New)	10 KCl - 10 NaCl - 80 NbCl₅ (mol %) (New)	15 KCl - 15 NaCl - 70 NbCl₅ (mol %) (New)	20 KCl - 20 NaCl - 60 NbCl₅ (mol %) (New)
30 KCl - 30 NaCl - 40 NbCl₅ (mol %) (New)

Semi/Superconductors & Optical materials

InP

Silicones & Elastomers

DOWSIL 3-6751 adhesive

DOWSIL 1-4174 adhesive (New)

Solders, Brazes, & Low melting alloys

60 Sn - 40 Pb (wt %)

Thermocouple alloys

Constantan

Thermoelectrics

Mg₂Si₀_.₅₅Sn₀_.₄Ge₀_.₀₅ (Bi doped) (New)	Mg₂Sn + 6.7 wt% Mg (New)	TiFe₁_.₉₆Re₀_.₀₄Sn (New)	TiFe₁_.₉₄Re₀_.₀₆Sn (New)	TiFe₁_.₈Re₀_.₂Sn (New)
TiFe₁_.₉₈Re₀_.₀₂Sn (New)	TiFe₂Sn (New)

Titanium alloys

C-110M (Ti - 8 Mn (wt %))	Ti - 4 Al - 3 Cu - 2 Fe - 4 V (wt %) (New)	Ti - 4 Al - 3 Cu - 2 Fe (wt %) (New)	Ti - 4 Al - 4 Mn (wt %)	Ti - 3.3 Al - 2.8 Mo - 1.2 V (wt %) (New)
Ti - 7 Al - 3 Mo (wt %)	Ti - 8 Al - 2 Nb - 1 Mo - 1 V (wt %) (New)	Ti - 5 Al - 2.5 Sn (Grade 6) (Revised)	Ti - 8 Al - 1 Ta (wt %) (New)	Ti - 6 Al - 4 V (Grade 5)
Ti - 6 Al - 4 V (Revised)	Ti - 6 Al (wt %)	Ti - 15 Cr (wt %) (New)	Ti - 15 Mo (wt %)	Ti - 30 Mo (wt %) (New)
Ti - 16 V - 2.5 Al (wt %) (Revised)	Ti Grade 4	Ti-1300 (New)	Ti-140A (Ti - 2 Cr - 2 Fe - 2 Mo (wt %))	Ti-150A (Ti - 3 Cr - 2 Fe (wt %))
Timetal 685 (New)

Tool steels

M50 (Revised)

UR, PU, & TPU (thermoset polyurethanes)

Iupital FU2005 (New)	Iupital FU2015 (New)	Iupital FU2020 (New)	Iupital FU2010R2 (New)	Iupital FU2020R2 (New)

14% short glass fiber PEEK (PEEK-GF14) (New)

    D     (*):    solid || room temperature value
    E     (*):    solid || room temperature value
    UTS   (*):    solid || room temperature value
    FSN       :    10 Hz to 20 Hz || tested at 20 °C (68 °F), R = -1, axial, stress amplitude || 5.5 x 10⁴ cycles to 1.3 x 10⁷ cycles
    FSN       :    19 kHz || tested at 20 °C (68 °F), R = -1, axial, 19.3 kHz, stress amplitude || 1.4 x 10⁵ cycles to 3.3 x 10⁹ cycles

return to listing

19-9 DX

    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 538 °C (1000 °F), in tension || 1.8 x 10^-⁸/s to 6.68 x 10^-⁷/s
    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 649 °C (1200 °F), in tension || 2.58 x 10^-⁹/s to 1.53 x 10^-⁵/s
    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 732 °C (1350 °F), in tension || 5.27 x 10^-⁹/s to 3.06 x 10^-⁵/s
    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 816 °C (1500 °F), in tension || 5 x 10^-⁹/s to 8.06 x 10^-⁶/s
    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 649 °C (1200 °F), in compression || 2.3 x 10^-⁹/s to 1.03 x 10^-⁷/s
    CRR    (N):    sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || tested at 732 °C (1350 °F), in compression || 9.15 x 10^-¹⁰/s to 5.15 x 10^-⁸/s
    CRR    (N):    bar, hot-rolled, stress relieved at 677 °C (1250 °F) || tested at 538 °C (1000 °F), in tension || 1.5 x 10^-⁸/s to 1.12 x 10^-⁶/s
    CRR    (N):    bar, hot-rolled, stress relieved at 677 °C (1250 °F) || tested at 649 °C (1200 °F), in tension || 3.33 x 10^-⁸/s to 5.06 x 10^-⁷/s
    CRR    (N):    bar, hot-rolled, stress relieved at 677 °C (1250 °F) || tested at 732 °C (1350 °F), in tension || 1.47 x 10^-⁸/s to 1.95 x 10^-⁶/s
    CRR    (N):    bar, hot-rolled, stress relieved at 677 °C (1250 °F) || tested at 816 °C (1500 °F), in tension || 1 x 10^-⁷/s to 7.23 x 10^-⁷/s

return to listing

15-7 Mo PH

CRR (N): TH 950 || tested at 427 °C (800 °F) || 7.36 x 10^-¹¹/s to 7.23 x 10^-⁷/s
CRR (N): TH 950 || tested at 538 °C (1000 °F) || 4.97 x 10^-⁹/s to 2.57 x 10^-⁶/s

return to listing

17-4 PH

    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 0.002/s, H900, Ozsoy et al. || 0 to 0.13 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 400 °C (752 °F), 0.002/s, H900, Ozsoy et al. || 0 to 0.26 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 600 °C (1112 °F), 0.002/s, H900, Ozsoy et al. || 0 to 0.14 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 0.002/s, H900, TiN reinforced, Ozsoy et al. || 0 to 0.13 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 400 °C (752 °F), 0.002/s, H900, TiN reinforced, Ozsoy et al. || 0 to 0.2 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 600 °C (1112 °F), 0.002/s, H900, TiN reinforced, Ozsoy et al. || 0 to 0.01 mm/mm strain
    UTS    (N):    laser powder bed fusion || H900, horizontal, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)
    UTS    (N):    laser powder bed fusion || H900, TiN reinforced, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)
    YS     (N):    laser powder bed fusion || H900, horizontal, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)
    YS     (N):    laser powder bed fusion || H900, TiN reinforced, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)
    %El    (N):    laser powder bed fusion || H900, horizontal, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)
    %El    (N):    laser powder bed fusion || H900, TiN reinforced, Ozsoy et al. || 20 °C (68 °F) to 600 °C (1112 °F)

return to listing

4340

    CRR    (N):    normalized || tested at 538 °C (1000 °F) || 8.6 x 10^-¹⁰/s to 3.3 x 10^-⁸/s
    CRR    (N):    normalized || tested at 593 °C (1100 °F) || 9 x 10^-⁹/s to 2.35 x 10^-⁷/s
    CRR    (N):    oil quenched || tested at 538 °C (1000 °F) || 9.4 x 10^-⁹/s to 7.04 x 10^-⁸/s
    CRR    (N):    oil quenched || tested at 593 °C (1100 °F) || 2.72 x 10^-⁸/s to 1 x 10^-⁷/s

return to listing

8620

FSN (N): case-carburized spur gear || tested at 20 °C (68 °F), R = 0.1, single tooth bending, maximum stress || 355 cycles to 1.17 x 10⁴ cycles

return to listing

1045

FSN (N): normalized || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, stress amplitude || 7.7 x 10³ cycles to 4 x 10⁵ cycles

return to listing

301

CRR (N): annealed then cold-drawn 12.7 mm (0.5 inch) rod || tested at 649 °C (1200 °F) || 1.44 x 10^-⁹/s to 1.23 x 10^-⁶/s
CRR (N): annealed then cold-drawn 12.7 mm (0.5 inch) rod || tested at 732 °C (1350 °F) || 1.98 x 10^-⁹/s to 1.64 x 10^-⁵/s

return to listing

302

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

303

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

304

    SSC    (N):    ASME BPVC Section II || tested at 20 °C (68 °F), full strain range, 6.7 x 10^-⁴/s || 0 to 2 mm/mm strain
    SSC    (N):    ASME BPVC Section II || tested at 316 °C (600 °F), full strain range, 6.7 x 10^-⁴/s || 0 to 1.5 mm/mm strain
    NE     (N):    solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)
    FEN    (N):    soft annealed || tested at 20 °C (68 °F), R = -1, axial, 0.001/s strain rate, equivalent strain amplitude || 560 cycles to 1 x 10⁴ cycles
    FEN    (N):    soft annealed || tested at 20 °C (68 °F), R = -1, torsional, 0.001/s strain rate, equivalent strain amplitude || 2.87 x 10³ cycles to 5 x 10⁴ cycles
    CRR    (N):    annealed || tested at 538 °C (1000 °F) || 5.2 x 10^-¹¹/s to 6.65 x 10^-⁷/s
    CRR    (N):    annealed || tested at 593 °C (1100 °F) || 3.6 x 10^-¹¹/s to 5.75 x 10^-⁶/s
    CRR    (N):    annealed || tested at 649 °C (1200 °F) || 9.9 x 10^-¹¹/s to 1.28 x 10^-⁵/s
    CRR    (N):    annealed || tested at 704 °C (1300 °F) || 2.5 x 10^-¹⁰/s to 7.95 x 10^-⁶/s
    CRR    (N):    annealed || tested at 760 °C (1400 °F) || 1.23 x 10^-⁷/s to 1.18 x 10^-⁴/s
    CRR    (N):    annealed || tested at 816 °C (1500 °F) || 7.4 x 10^-⁸/s to 4 x 10^-⁵/s
    CRR    (N):    effect of neutron irradiation || tested at 760 °C (1400 °F), annealed at 1038 °C (1900 °F) || 1.1 x 10^-⁷/s to 2.01 x 10^-⁷/s
    CRR    (N):    effect of neutron irradiation || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm², annealed at 1038 °C (1900 °F) || 2.16 x 10^-⁷/s to 5.01 x 10^-⁷/s
    CRR    (N):    effect of neutron irradiation || tested at 760 °C (1400 °F), aged at 800 °C (1472 °F) || 1.6 x 10^-⁷/s to 3.06 x 10^-⁷/s
    CRR    (N):    effect of neutron irradiation || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm², aged at 800 °C (1472 °F) || 2.44 x 10^-⁷/s to 3.89 x 10^-⁷/s

return to listing

308

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

321

    CRR    (N):    1.63 mm (0.064 inch) thick sheet, annealed || tested at 538 °C (1000 °F), in tension || 1 x 10^-⁹/s to 1.25 x 10^-⁸/s
    CRR    (N):    1.63 mm (0.064 inch) thick sheet, annealed || tested at 649 °C (1200 °F), in tension || 4.7 x 10^-⁹/s to 1.39 x 10^-⁶/s
    CRR    (N):    1.63 mm (0.064 inch) thick sheet, annealed || tested at 732 °C (1350 °F), in tension || 2 x 10^-⁸/s to 2.23 x 10^-⁵/s
    CRR    (N):    1.63 mm (0.064 inch) thick sheet, annealed || tested at 649 °C (1200 °F), in compression || 3.16 x 10^-⁹/s to 6.95 x 10^-⁸/s
    CRR    (N):    1.63 mm (0.064 inch) thick sheet, annealed || tested at 732 °C (1350 °F), in compression || 5.6 x 10^-⁹/s to 1.56 x 10^-⁶/s

return to listing

347

FEN (N): forged block || tested at 300 °C (572 °F), R = -1, axial, total strain amplitude || 1.9 x 10³ cycles to 2.1 x 10⁶ cycles

return to listing

405

    CRR    (N):    heat treated and tempered || tested at 427 °C (800 °F) || 2.7 x 10^-¹²/s to 8.4 x 10^-¹¹/s
    CRR    (N):    heat treated and tempered || tested at 482 °C (900 °F) || 8 x 10^-¹²/s to 7.51 x 10^-¹¹/s
    CRR    (N):    heat treated and tempered || tested at 538 °C (1000 °F) || 2.7 x 10^-¹²/s to 1.1 x 10^-⁹/s

return to listing

410

    CRR    (N):    wrought bars, heat treated || tested at 499 °C (930 °F) || 2.5 x 10^-¹¹/s to 1.14 x 10^-⁸/s
    CRR    (N):    wrought bars, heat treated || tested at 554 °C (1030 °F) || 3 x 10^-¹¹/s to 3.1 x 10^-⁸/s
    CRR    (N):    cast bars, heat treated || tested at 566 °C (1050 °F) || 2 x 10^-¹¹/s to 5.1 x 10^-⁹/s
    CRR    (N):    cast bars, heat treated || tested at 593 °C (1100 °F) || 5.2 x 10^-¹¹/s to 3.1 x 10^-⁹/s

return to listing

414

    CRR    (N):    tempered and untempered martensite || tested at 482 °C (900 °F) || 5.8 x 10^-⁸/s to 1.6 x 10^-⁵/s
    CRR    (N):    tempered and untempered martensite || tested at 593 °C (1100 °F) || 3.8 x 10^-⁸/s to 2.1 x 10^-⁵/s
    CRR    (N):    tempered and untempered martensite || tested at 649 °C (1200 °F) || 3.8 x 10^-⁸/s to 3 x 10^-⁴/s
    CRR    (N):    tempered martensite || tested at 482 °C (900 °F) || 6.3 x 10^-⁸/s to 8.2 x 10^-⁶/s
    CRR    (N):    tempered martensite || tested at 593 °C (1100 °F) || 2.6 x 10^-⁸/s to 4.5 x 10^-⁵/s
    CRR    (N):    tempered martensite || tested at 649 °C (1200 °F) || 2.2 x 10^-⁸/s to 3.3 x 10^-⁵/s

return to listing

420

CRR (N): 1 h at 1038 °C (1900 °F), tempered 2 h at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 1.6 x 10^-¹⁰/s to 6.9 x 10^-⁹/s
CRR (N): 1 h at 1038 °C (1900 °F), tempered 2 h at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 2 x 10^-¹⁰/s to 2.7 x 10^-⁸/s

return to listing

422

    CRR    (N):    austenitized at 1038 °C (1900 °F), tempered at 441 °C (825 °F) || tested at 316 °C (600 °F) || 7.3 x 10^-¹³/s to 2.26 x 10^-¹⁰/s
    CRR    (N):    austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) || tested at 316 °C (600 °F) || 8 x 10^-¹¹/s to 3.14 x 10^-¹⁰/s
    CRR    (N):    austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) || tested at 427 °C (800 °F) || 1.03 x 10^-⁸/s to 3.73 x 10^-⁸/s
    CRR    (N):    austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) || tested at 482 °C (900 °F) || 7 x 10^-¹¹/s to 1.32 x 10^-⁷/s
    CRR    (N):    1 h at 1038 °C (1900 °F), tempered 2 h at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 5.5 x 10^-¹¹/s to 7 x 10^-⁹/s
    CRR    (N):    1 h at 1038 °C (1900 °F), tempered 2 h at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 3 x 10^-¹⁰/s to 1.4 x 10^-⁹/s
    CRR    (N):    1 h at 1038 °C (1900 °F), tempered 1 h at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 3.8 x 10^-¹¹/s to 8.4 x 10^-⁹/s
    CRR    (N):    1 h at 1038 °C (1900 °F), tempered 1 h at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 3.3 x 10^-¹¹/s to 8.4 x 10^-⁹/s

return to listing

430

    CRR    (N):    wrought, 774 °C (1425 °F) anneal || tested at 482 °C (900 °F) || 6.3 x 10^-⁸/s to 1.3 x 10^-⁵/s
    CRR    (N):    wrought, 774 °C (1425 °F) anneal || tested at 566 °C (1050 °F) || 3 x 10^-⁸/s to 8.2 x 10^-⁶/s
    CRR    (N):    wrought, 774 °C (1425 °F) anneal || tested at 649 °C (1200 °F) || 1 x 10^-⁸/s to 3.1 x 10^-⁵/s
    CRR    (N):    wrought, 774 °C (1425 °F) anneal || tested at 732 °C (1350 °F) || 1.7 x 10^-⁷/s to 2.45 x 10^-⁶/s

return to listing

4120

    UTS   (N*):    hot-rolled || hardness 228 HV || room temperature value
    YS    (N*):    hot-rolled || hardness 228 HV || room temperature value
    %El   (N*):    hot-rolled || hardness 228 HV || room temperature value
    FSN    (N):    hot-rolled, shot peened || tested at 20 °C (68 °F), R = -1, rotating beam, FeS fine particle shot peening, Pf = 10%, stress amplitude || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    hot-rolled, shot peened || tested at 20 °C (68 °F), R = -1, rotating beam, FeS fine particle shot peening, Pf = 50%, stress amplitude || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    hot-rolled, shot peened || tested at 20 °C (68 °F), R = -1, rotating beam, FeS fine particle shot peening, Pf = 90%, stress amplitude || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    gas carburized || tested at 20 °C (68 °F), R = -1, rotating beam, gas carburized & electropolished, stress amplitude || 7.9 x 10³ cycles to 1 x 10⁸ cycles
    FSN    (N):    gas carburized || tested at 20 °C (68 °F), R = -1, rotating beam, gas carburized, electropolished, & multifunction cavitation, stress amplitude || 1.6 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    gas carburized || tested at 20 °C (68 °F), R = -1, rotating beam, electropolished & gas carburized, stress amplitude || 2 x 10⁴ cycles to 1 x 10⁸ cycles

return to listing

4130

    CRR    (N):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 427 °C (800 °F), in compression || 4.6 x 10^-⁹/s to 1 x 10^-⁷/s
    CRR    (N):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 482 °C (900 °F), in compression || 5.7 x 10^-⁹/s to 1.4 x 10^-⁷/s
    CRR    (N):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 538 °C (1000 °F), in compression || 5.5 x 10^-⁹/s to 1.3 x 10^-⁷/s

return to listing

2024

    CRR    (N):    1.63 mm (0.064 inch) sheet, T3 temper || tested at 149 °C (300 °F) || 7.72 x 10^-¹⁰/s to 2.5 x 10^-⁶/s
    CRR    (N):    1.63 mm (0.064 inch) sheet, T3 temper || tested at 232 °C (450 °F) || 4.44 x 10^-⁹/s to 3.56 x 10^-⁶/s
    CRR    (N):    1.63 mm (0.064 inch) sheet, T3 temper || tested at 316 °C (600 °F) || 3.55 x 10^-⁹/s to 2.89 x 10^-⁶/s
    CRR    (N):    4.76 mm (0.1875 inch) plate, T3 temper || tested at 149 °C (300 °F) || 1.55 x 10^-⁹/s to 7.64 x 10^-⁷/s
    CRR    (N):    4.76 mm (0.1875 inch) plate, T3 temper || tested at 232 °C (450 °F) || 3.02 x 10^-⁹/s to 9.56 x 10^-⁷/s
    CRR    (N):    4.76 mm (0.1875 inch) plate, T3 temper || tested at 316 °C (600 °F) || 3.16 x 10^-⁹/s to 8.03 x 10^-⁷/s

return to listing

2117

    CRR    (N):    T4 temper, 9.52 mm (0.375 inch) diameter rivet wire || tested at 149 °C (300 °F) || 1.74 x 10^-⁹/s to 2.78 x 10^-⁸/s
    CRR    (N):    T4 temper, 9.52 mm (0.375 inch) diameter rivet wire || tested at 232 °C (450 °F) || 1.11 x 10^-⁹/s to 8.06 x 10^-⁷/s
    CRR    (N):    T4 temper, 9.52 mm (0.375 inch) diameter rivet wire || tested at 316 °C (600 °F) || 5.44 x 10^-⁹/s to 2.03 x 10^-⁶/s

return to listing

2219

    SSC    (N):    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, axial || 0 to 0.143 mm/mm strain
    CRR    (N):    T6 temper, rod || tested at 204 °C (400 °F) || 1.22 x 10^-⁸/s to 1.9 x 10^-⁸/s
    CRR    (N):    T6 temper, rod || tested at 260 °C (500 °F) || 3.4 x 10^-⁹/s to 1.02 x 10^-⁸/s
    CRR    (N):    T6 temper, rod || tested at 316 °C (600 °F) || 6 x 10^-¹¹/s to 5.56 x 10^-⁷/s
    CRR    (N):    T6 temper, sheet || tested at 204 °C (400 °F) || 2 x 10^-⁹/s to 9.12 x 10^-⁷/s
    CRR    (N):    T6 temper, sheet || tested at 260 °C (500 °F) || 4.5 x 10^-⁹/s to 1.67 x 10^-⁷/s
    CRR    (N):    T6 temper, sheet || tested at 316 °C (600 °F) || 3.69 x 10^-⁹/s to 1.34 x 10^-⁶/s

return to listing

4032

    DLL    (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    MTE    (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    CTE    (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    D      (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    TC     (N):    solid || 20 °C (68 °F) to 400 °C (752 °F)
    SH     (N):    solid || 20 °C (68 °F) to 400 °C (752 °F)
    SH     (N):    liquid || 300 °C (572 °F) to 800 °C (1472 °F)
    TD     (N):    solid || 20 °C (68 °F) to 400 °C (752 °F)

return to listing

5182

    TC     (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    SH     (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    SH     (N):    liquid || 633 °C (1171 °F) to 800 °C (1472 °F)
    TD     (N):    solid || 20 °C (68 °F) to 300 °C (572 °F)

return to listing

6061

    SSC    (N):    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, plate, longitudinal || 0 to 0.19 mm/mm strain
    SSC    (N):    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, forging, axial || 0 to 0.18 mm/mm strain
    SSC    (N):    T4 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, plate, longitudinal || 0 to 0.2 mm/mm strain
    SSC    (N):    T4 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, forging, axial || 0 to 0.158 mm/mm strain
    CRR    (N):    T6 temper sheet || tested at 232 °C (450 °F) || 1.29 x 10^-¹⁰/s to 3.04 x 10^-⁷/s
    CRR    (N):    T6 temper sheet || tested at 260 °C (500 °F) || 3.26 x 10^-⁹/s to 8.84 x 10^-⁷/s

return to listing

6082

    SSC    (N):    sheet || tested at 20 °C (68 °F), T6 temper, transverse, unknown strain rate || 0 to 0.8 mm/mm strain
    FSN    (N):    T6 temper, effect of shear cutting || tested at 20 °C (68 °F), R = -1, axial, trimmed, transverse to the rolling direction, stress amplitude || 2.7 x 10⁴ cycles to 4.5 x 10⁵ cycles
    FSN    (N):    T6 temper, effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, axial, trimmed, transverse to the rolling direction, stress amplitude || 3.4 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, K_t = 2.24, axial, punched, transverse to the rolling direction, stress amplitude || 4.9 x 10⁴ cycles to 6 x 10⁵ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA1 grade, P_s = 10%, maximum stress || 2.2 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA2 grade, P_s = 10%, maximum stress || 4.1 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA3 grade, P_s = 10%, maximum stress || 4.5 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA1 grade, P_s = 50%, maximum stress || 2.2 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA2 grade, P_s = 50%, maximum stress || 4.1 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA3 grade, P_s = 50%, maximum stress || 4.5 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA1 grade, P_s = 90%, maximum stress || 2.2 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA2 grade, P_s = 90%, maximum stress || 4.1 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of impurities || tested at 20 °C (68 °F), R = 0.1, axial, transverse, GA3 grade, P_s = 90%, maximum stress || 4.5 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of corrosion || tested at 20 °C (68 °F), R = 0.01, axial, not recrystallized, not corroded, maximum stress || 3.2 x 10⁴ cycles to 1.6 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of corrosion || tested at 20 °C (68 °F), R = 0.01, axial, recrystallized, not corroded, maximum stress || 3.8 x 10⁴ cycles to 5.3 x 10⁶ cycles
    FSN    (N):    T6 temper, effect of corrosion || tested at 20 °C (68 °F), R = 0.01, axial, not recrystallized, corroded, maximum stress || 2.8 x 10³ cycles to 7.6 x 10⁵ cycles
    FSN    (N):    T6 temper, effect of corrosion || tested at 20 °C (68 °F), R = 0.01, axial, recrystallized, corroded, maximum stress || 5 x 10³ cycles to 8.2 x 10⁵ cycles

return to listing

6110

SSC (N): T6 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s || 0 to 0.6 mm/mm strain
FEN (N): T6 temper || tested at 20 °C (68 °F), R = -1, axial, longitudinal, total strain amplitude || 40 cycles to 6.3 x 10⁵ cycles

return to listing

7039

S (N): solid || T61 temper || -267.1 °C (-448.9 °F) to 20 °C (68 °F)

return to listing

7075

    FSN    (N):    T6 temper, cold spray repaired plate || tested at 20 °C (68 °F), R = 0.1, base material, axial, maximum stress || 2.9 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    T6 temper, cold spray repaired plate || tested at 20 °C (68 °F), R = 0.1, K_t = 2.19, groove notched, axial, maximum stress || 9.3 x 10³ cycles to 1.3 x 10⁶ cycles
    FSN    (N):    T6 temper, cold spray repaired plate || tested at 20 °C (68 °F), R = 0.1, groove notched, cold spray repaired, axial, maximum stress || 5.8 x 10³ cycles to 1 x 10⁶ cycles
    FSN    (N):    T6 temper, cold spray repaired plate || tested at 20 °C (68 °F), R = 0.1, dented, cold spray repaired, axial, maximum stress || 6.5 x 10³ cycles to 1 x 10⁶ cycles

return to listing

333.0

    UTS   (N*):    high pressure, die cast || as-cast || room temperature value
    YS    (N*):    high pressure, die cast || as-cast || room temperature value
    %El   (N*):    high pressure, die cast || as-cast || room temperature value
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 4.56 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 50 Hz, as-cast, stress amplitude || 4.56 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

4140

    FSN    (N):    oil quenched from 850 °C (1562 °F), tempered for 2 h at 600 °C (1112 °F) || tested at 20 °C (68 °F), R = -1, axial, polished, maximum stress || 1.1 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (N):    oil quenched from 850 °C (1562 °F), tempered for 2 h at 600 °C (1112 °F) || tested at 20 °C (68 °F), R = -1, axial, fine particle shot peened, maximum stress || 1.53 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    oil quenched from 850 °C (1562 °F), tempered for 2 h at 600 °C (1112 °F) || tested at 20 °C (68 °F), R = -1, axial, shot peened, maximum stress || 4.67 x 10³ cycles to 1 x 10⁷ cycles
    FSN    (N):    effect of H₂ atmosphere || tested at 400 °C (752 °F), R = -1, axial, 19.3 kHz, tested in air, stress amplitude || 1.3 x 10⁵ cycles to unknown strain rate cycles
    FSN    (N):    effect of H₂ atmosphere || tested at 400 °C (752 °F), R = -1, axial, 19.3 kHz, tested in hot H₂ gas, stress amplitude || 3.8 x 10⁶ cycles to unknown strain rate cycles

return to listing

2043 (New)

    D     (*):    solid || room temperature value
    SSC       :    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, axial || 0 to 0.128 mm/mm strain
    SSC       :    T4 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, axial || 0 to 0.156 mm/mm strain
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, axial || room temperature value
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, axial || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, axial || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, axial || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, axial || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, axial || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value

return to listing

2139 (New)

    D     (*):    solid || room temperature value
    SSC       :    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, longitudinal || 0 to 0.155 mm/mm strain
    SSC       :    T4 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, longitudinal || 0 to 0.211 mm/mm strain
    SSC       :    T4 temper || tested at 20 °C (68 °F), laser powder bed fusion, 0.001/s, vertical || 0 to 0.55 mm/mm strain
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    UTS   (*):    T4 temper || laser powder bed fusion, 0.001/s, vertical || room temperature value
    UTS   (*):    T8 temper || 25.4 mm (1 inch) thick plate, longitudinal || room temperature value
    UTS   (*):    T8 temper || 25.4 mm (1 inch) thick plate, transverse || room temperature value
    UTS   (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, longitudinal || room temperature value
    UTS   (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, transverse || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    YS    (*):    T4 temper || laser powder bed fusion, 0.001/s, vertical || room temperature value
    YS    (*):    T8 temper || 25.4 mm (1 inch) thick plate, longitudinal || room temperature value
    YS    (*):    T8 temper || 25.4 mm (1 inch) thick plate, transverse || room temperature value
    YS    (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, longitudinal || room temperature value
    YS    (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, transverse || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, longitudinal || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, transverse || room temperature value
    %El   (*):    T4 temper || laser powder bed fusion, 0.001/s, vertical || room temperature value
    %El   (*):    T8 temper || 25.4 mm (1 inch) thick plate, longitudinal || room temperature value
    %El   (*):    T8 temper || 25.4 mm (1 inch) thick plate, transverse || room temperature value
    %El   (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, longitudinal || room temperature value
    %El   (*):    T8 temper || 25.4 mm (1 inch) thick plate, friction stir welded, transverse || room temperature value
    FSN       :    T4 temper || tested at 20 °C (68 °F), R = -1, axial, 10 Hz, stress amplitude || 2.52 x 10³ cycles to 1 x 10⁷ cycles
    FSN       :    T4 temper || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, stress amplitude || 2.1 x 10⁷ cycles to unknown strain rate cycles
    FSN       :    T8 temper || tested at 20 °C (68 °F), R = -1, base material, longitudinal, maximum stress || 6.9 x 10⁴ cycles to 2.2 x 10⁷ cycles
    FSN       :    T8 temper || tested at 20 °C (68 °F), R = -1, base material, transverse, maximum stress || 7.3 x 10⁴ cycles to 2.44 x 10⁷ cycles
    FSN       :    T8 temper || tested at 20 °C (68 °F), R = -1, friction stir weld, longitudinal, maximum stress || 6.1 x 10⁴ cycles to 2.21 x 10⁷ cycles
    FSN       :    T8 temper || tested at 20 °C (68 °F), R = -1, friction stir weld, transverse, maximum stress || 1.4 x 10⁵ cycles to 2.34 x 10⁷ cycles

return to listing

2050 (New)

    D     (*):    solid || room temperature value
    SSC       :    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, plate, longitudinal || 0 to 0.14 mm/mm strain
    SSC       :    O temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, forging, axial || 0 to 0.16 mm/mm strain
    SSC       :    T4 temper || tested at 20 °C (68 °F), 3.3 x 10^-⁴/s, plate, longitudinal || 0 to 0.16 mm/mm strain
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, forging, axial || room temperature value
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value
    UTS   (*):    O temper || 3.3 x 10^-⁴/s, forging, transverse || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    UTS   (*):    T4 temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, forging, axial || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value
    YS    (*):    O temper || 3.3 x 10^-⁴/s, forging, transverse || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    YS    (*):    T4 temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, forging, axial || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value
    %El   (*):    O temper || 3.3 x 10^-⁴/s, forging, transverse || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, plate, longitudinal || room temperature value
    %El   (*):    T4 temper || 3.3 x 10^-⁴/s, plate, transverse || room temperature value

return to listing

3004

    DLL    (R):    solid || -50 °C (-58 °F) to 600 °C (1112 °F)
    MTE    (R):    solid || -50 °C (-58 °F) to 600 °C (1112 °F)
    CTE    (R):    solid || -50 °C (-58 °F) to 600 °C (1112 °F)
    D      (R):    solid || -50 °C (-58 °F) to 600 °C (1112 °F)
    TC     (N):    solid || 20 °C (68 °F) to 617 °C (1142 °F)
    TC     (N):    liquid || 383 °C (721 °F) to 900 °C (1652 °F)
    SH     (N):    solid || 20 °C (68 °F) to 600 °C (1112 °F)
    SH     (N):    liquid || 656 °C (1213 °F) to 900 °C (1652 °F)

return to listing

431

    FSN    (N):    AMS 2759/5 || tested at 20 °C (68 °F), R = -1, rotating bending, maximum stress || 3.1 x 10⁴ cycles to 3.4 x 10⁸ cycles
    FSN    (N):    laser metal deposition || tested at 20 °C (68 °F), R = -1, axial, as-built surface, maximum stress || 5 x 10³ cycles to 1 x 10⁷ cycles
    FSN    (N):    laser metal deposition || tested at 20 °C (68 °F), R = -1, axial, burnished surface, maximum stress || 3.8 x 10³ cycles to 1 x 10⁷ cycles
    SR     (R):    tempered and untempered martensite || tested at 482 °C (900 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered and untempered martensite || tested at 593 °C (1100 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered and untempered martensite || tested at 649 °C (1200 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered and untempered martensite || Master curve (LMP) || 14.9 h to 20.1 h
    SR     (R):    tempered martensite || tested at 482 °C (900 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered martensite || tested at 593 °C (1100 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered martensite || tested at 649 °C (1200 °F) || 100 h to 1 x 10⁴ h
    SR     (R):    tempered martensite || Master curve (LMP) || 17.1 h to 22.8 h
    CRR    (N):    tempered and untempered martensite || tested at 482 °C (900 °F) || 3.5 x 10^-⁸/s to 1.3 x 10^-⁵/s
    CRR    (N):    tempered and untempered martensite || tested at 593 °C (1100 °F) || 3 x 10^-⁷/s to 1.3 x 10^-⁵/s
    CRR    (N):    tempered and untempered martensite || tested at 649 °C (1200 °F) || 7.7 x 10^-⁸/s to 6.6 x 10^-⁵/s
    CRR    (N):    tempered martensite || tested at 482 °C (900 °F) || 2.2 x 10^-⁸/s to 1.4 x 10^-⁵/s
    CRR    (N):    tempered martensite || tested at 593 °C (1100 °F) || 4.5 x 10^-⁸/s to 1.2 x 10^-⁵/s
    CRR    (N):    tempered martensite || tested at 649 °C (1200 °F) || 5.6 x 10^-⁸/s to 3.6 x 10^-⁵/s

return to listing

4047

    DLL    (R):    solid || 20 °C (68 °F) to 587 °C (1088 °F)
    MTE    (R):    solid || 20 °C (68 °F) to 587 °C (1088 °F)
    CTE    (R):    solid || 20 °C (68 °F) to 587 °C (1088 °F)
    D      (R):    solid || 20 °C (68 °F) to 587 °C (1088 °F)
    TD     (R):    solid || 20 °C (68 °F) to 587 °C (1088 °F)

return to listing

52100

    E      (R):    solid || standard 52100 || 20 °C (68 °F) to 480 °C (896 °F)
    E      (R):    solid || 52100 VIM/VAR || 20 °C (68 °F) to 480 °C (896 °F)
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 22 °C (72 °F), R = -1, ultrasonic axial, maximum stress || 1.34 x 10⁶ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 200 °C (392 °F), R = -1, ultrasonic axial, maximum stress || 7.6 x 10⁶ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 300 °C (572 °F), R = -1, ultrasonic axial, maximum stress || 8.7 x 10⁵ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F), VIM/VAR grade || tested at 22 °C (72 °F), R = -1, ultrasonic axial, maximum stress || 4.3 x 10⁶ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F), VIM/VAR grade || tested at 200 °C (392 °F), R = -1, ultrasonic axial, maximum stress || 1.4 x 10⁶ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F), VIM/VAR grade || tested at 300 °C (572 °F), R = -1, ultrasonic axial, maximum stress || 8.75 x 10⁵ cycles to unknown strain rate cycles

return to listing

6060

    SSC    (R):    T6 temper || tested at 20 °C (68 °F), 7.7 x 10^-⁴/s || 0 to 0.1 mm/mm strain
    UTS   (N*):    T6 temper || 0.001/s || room temperature value
    YS    (N*):    T6 temper || 0.001/s || room temperature value
    %El   (N*):    T6 temper || 0.001/s || room temperature value
    FSN    (N):    T6 temper || tested at 20 °C (68 °F), R = -1, axial, equivalent stress amplitude || 270 cycles to 7.3 x 10⁴ cycles
    FSN    (N):    T6 temper || tested at 20 °C (68 °F), R = -1, torsional, equivalent stress amplitude || 400 cycles to 5.2 x 10⁴ cycles
    FEN    (N):    T6 temper || tested at 20 °C (68 °F), R = -1, axial, 0.001/s strain rate, equivalent strain amplitude || 270 cycles to 7.3 x 10⁴ cycles
    FEN    (N):    T6 temper || tested at 20 °C (68 °F), R = -1, torsional, 0.001/s strain rate, equivalent strain amplitude || 400 cycles to 5.2 x 10⁴ cycles

return to listing

316

    SSC    (N):    ASME BPVC Section II || tested at 20 °C (68 °F), full strain range, 6.7 x 10^-⁴/s || 0 to 1.8 mm/mm strain
    SSC    (N):    ASME BPVC Section II || tested at 316 °C (600 °F), full strain range, 6.7 x 10^-⁴/s || 0 to 1.7 mm/mm strain
    SSC    (N):    ASME BPVC Section II || tested at 20 °C (68 °F), full strain range, 1.52/s || 0 to 1.7 mm/mm strain
    SSC    (N):    ASME BPVC Section II || tested at 316 °C (600 °F), full strain range, 1.52/s || 0 to 1.7 mm/mm strain
    SR     (R):    annealed at 1050 °C (1922 °F), FR grade || Master curve (LMP) || 16.7 h to 26 h
    CRR    (N):    annealed at 1050 °C (1922 °F), FR grade || tested at 500 °C (932 °F) || 3 x 10^-¹¹/s to 4 x 10^-⁷/s
    CRR    (N):    annealed at 1050 °C (1922 °F), FR grade || tested at 550 °C (1022 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1050 °C (1922 °F), FR grade || tested at 600 °C (1112 °F) || 1 x 10^-¹⁰/s to 2.7 x 10^-⁵/s
    CRR    (N):    annealed || tested at 600 °C (1112 °F) || 2.3 x 10^-¹²/s to 1.27 x 10^-⁸/s
    CRR    (N):    annealed || tested at 650 °C (1202 °F) || 2.3 x 10^-¹¹/s to 4.11 x 10^-⁹/s
    CRR    (N):    annealed || tested at 700 °C (1292 °F) || 8.45 x 10^-¹²/s to 5.08 x 10^-¹¹/s
    CRR    (N):    aged 4,000 h || tested at 550 °C (1022 °F), annealed at 1050 °C (1922 °F), aged 4000 h at 550 °C (1022 °F) || 1 x 10^-⁸/s to 7.4 x 10^-⁸/s
    CRR    (N):    aged 4,000 h || tested at 550 °C (1022 °F), 20% cold worked, aged 4000 h at 550 °C (1022 °F) || 2.8 x 10^-⁸/s to 6.1 x 10^-⁷/s
    CRR    (N):    aged 4,000 h || tested at 650 °C (1202 °F), annealed at 1050 °C (1922 °F), aged 4000 h at 650 °C (1202 °F) || 1 x 10^-⁷/s to 2.25 x 10^-⁶/s
    CRR    (N):    aged 4,000 h || tested at 650 °C (1202 °F), 20% cold worked, aged 4000 h at 650 °C (1202 °F) || 6.7 x 10^-⁹/s to 9.11 x 10^-⁸/s

return to listing

A572 Grade 50

FEN (N): S535 steel, UTS = 541 MPa (78.5 ksi) || tested at 20 °C (68 °F), R = -1, axial, total strain amplitude || 325 cycles to 7.63 x 10⁵ cycles
FEN (N): S535 steel, UTS = 541 MPa (78.5 ksi) || tested at 20 °C (68 °F), R = -1, torsional, total strain amplitude || 380 cycles to 5.53 x 10⁵ cycles

return to listing

A297 HF (20 Cr - 10 Ni (wt %))

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

A297 HK (26 Cr - 20 Ni (wt %))

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

A319

    CRR    (N):    as-cast || tested at 240 °C (464 °F) || 1.8 x 10^-³/s to 4.9 x 10^-³/s
    CRR    (N):    T4 temper || tested at 240 °C (464 °F) || 1.37 x 10^-⁶/s to 2 x 10^-³/s
    CRR    (N):    T7 temper || tested at 240 °C (464 °F) || 6.8 x 10^-⁷/s to 4 x 10^-³/s

return to listing

2A12

D (N*): solid || room temperature value

return to listing

2A50

D (N*): solid || room temperature value

return to listing

A360.0

    SSC    (R):    laser powder bed fusion || tested at 20 °C (68 °F), 0.02/s, as-built, Raus et al. || 0 to 0.43 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, as-built, Lehner et al. || 0 to 0.38 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, T6 temper, Lehner et al. || 0 to 0.54 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 0.001/s, Tahmasbi et al. || 0 to 0.69 mm/mm strain
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, as-built, Razavi et al., maximum stress || 3.2 x 10⁴ cycles to 3.2 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, T6 temper, Razavi et al., maximum stress || 2.2 x 10⁴ cycles to 8 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, as-built, Lehner et al., stress amplitude || 1.7 x 10⁴ cycles to 4.8 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, T6 temper, Lehner et al., stress amplitude || 2.6 x 10⁴ cycles to 4 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, as-built, polished, Lehner et al., stress amplitude || 2.7 x 10⁴ cycles to 3 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, T6 temper, polished, Lehner et al., stress amplitude || 2.2 x 10⁴ cycles to 7.5 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, hourglass, Pf = 90%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, hourglass, Pf = 50%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, hourglass, Pf = 10%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small rod, Pf = 90%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small rod, Pf = 50%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small rod, Pf = 10%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small block, Pf = 90%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small block, Pf = 50%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, small block, Pf = 10%, stress amplitude || 3 x 10⁵ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large block, Pf = 90%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large block, Pf = 50%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large block, Pf = 10%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large rod, Pf = 90%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large rod, Pf = 50%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles
    FSN    (N):    laser powder bed fusion, effect of part geometry || tested at 20 °C (68 °F), R = -1, axial, large rod, Pf = 10%, stress amplitude || 1 x 10⁶ cycles to 1 x 10⁹ cycles

return to listing

AE44

    SSC    (N):    high pressure die cast, as-cast, Dong et al. || tested at 20 °C (68 °F), 2 x 10^-⁴/s || 0 to 0.115 mm/mm strain
    SSC    (N):    high pressure die cast, as-cast, Dong et al. || tested at 150 °C (302 °F), 2 x 10^-⁴/s || 0 to 0.134 mm/mm strain
    SSC    (N):    high pressure die cast, as-cast, Dong et al. || tested at 250 °C (482 °F), 2 x 10^-⁴/s || 0 to 0.31 mm/mm strain
    SSC    (N):    high pressure die cast, as-cast, Dong et al. || tested at 300 °C (572 °F), 2 x 10^-⁴/s || 0 to 0.24 mm/mm strain
    UTS    (N):    high pressure die cast, as-cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)

return to listing

AE42

    UTS   (N*):    high pressure, die cast || as-cast || room temperature value
    YS    (N*):    high pressure, die cast || as-cast || room temperature value
    %El   (N*):    high pressure, die cast || as-cast || room temperature value
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 1.14 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 50 Hz, as-cast, stress amplitude || 1.14 x 10⁵ cycles to 1 x 10⁷ cycles

return to listing

Ag - 0.674 Au (wt %)

S (N): normal silver || -271.1 °C (-456.1 °F) to 20 °C (68 °F)

return to listing

Al - 25 Si (wt %)

ST (N): liquid || 757 °C (1394 °F) to 1700 °C (3092 °F)

return to listing

Al - 30 Si (wt %)

ST (N): liquid || 811 °C (1492 °F) to 1700 °C (3092 °F)

return to listing

Al - 35 Si (wt %)

ST (N): liquid || 927 °C (1700 °F) to 1700 °C (3092 °F)

return to listing

Al - 41 Si (wt %)

ST (N): liquid || 1147 °C (2096 °F) to 1700 °C (3092 °F)

return to listing

Al - 51 Si (wt %)

ST (N): liquid || 1052 °C (1925 °F) to 1700 °C (3092 °F)

return to listing

Al - 90 Si (wt %)

ST (N): liquid || 1357 °C (2474 °F) to 1700 °C (3092 °F)

return to listing

Al - 12.6 Si (wt %)

ST (N): liquid || 569 °C (1056 °F) to 1700 °C (3092 °F)

return to listing

Al - 13 Si (wt %)

ST (N): liquid || 627 °C (1160 °F) to 1700 °C (3092 °F)

return to listing

Al - 15 Si (wt %)

ST (N): liquid || 627 °C (1160 °F) to 1700 °C (3092 °F)

return to listing

Al - 17 Si (wt %)

ST (N): liquid || 647 °C (1196 °F) to 1700 °C (3092 °F)

return to listing

Al - 20 Si (wt %)

ST (N): liquid || 684 °C (1263 °F) to 1700 °C (3092 °F)

return to listing

Al - 22 Si (wt %)

ST (N): liquid || 727 °C (1340 °F) to 1700 °C (3092 °F)

return to listing

Al - 65 Si (wt %) (New)

ST : liquid || 1206 °C (2203 °F) to 1700 °C (3092 °F)

return to listing

Al - 80 Si (wt %) (New)

ST : liquid || 1301 °C (2374 °F) to 1700 °C (3092 °F)

return to listing

Al - 60 Si (wt %) (New)

ST : liquid || 1151 °C (2104 °F) to 1700 °C (3092 °F)

return to listing

Al - 6 Zn - 2 Mg - 0.5 Ni - 0.3 Fe (wt %) (New)

    SSC       :    radial shear rolled || tested at 20 °C (68 °F), 0.002/s || 0 to 0.78 mm/mm strain
    SSC       :    radial shear rolled || tested at 400 °C (752 °F), 0.1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 400 °C (752 °F), 1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 400 °C (752 °F), 10/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 400 °C (752 °F), 50/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 450 °C (842 °F), 0.1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 450 °C (842 °F), 1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 450 °C (842 °F), 10/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 450 °C (842 °F), 50/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 500 °C (932 °F), 0.1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 500 °C (932 °F), 1/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 500 °C (932 °F), 10/s || 0 to 0.93 mm/mm strain
    SSC       :    radial shear rolled || tested at 500 °C (932 °F), 50/s || 0 to 0.93 mm/mm strain

return to listing

Alloy 709 (NF 709)

    CRS    (N):    0.1% plastic strain || tested at 750 °C (1382 °F) || 1.33 h to 460 h
    CRS    (N):    0.3% plastic strain || tested at 750 °C (1382 °F) || 5.6 h to 345 h
    CRS    (N):    0.5% plastic strain || tested at 750 °C (1382 °F) || 10 h to 80 h
    CRS    (N):    1% plastic strain || tested at 750 °C (1382 °F) || 20 h to 320 h
    CRS    (N):    5% plastic strain || tested at 750 °C (1382 °F) || 4 h to 85 h
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 10 h || 0 to 5.16 x 10^-³ mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 15 h || 0 to 7.59 x 10^-³ mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 20 h || 0 to 0.1 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 25 h || 0 to 0.13 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 30 h || 0 to 0.15 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 40 h || 0 to 0.21 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 50 h || 0 to 0.26 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 75 h || 0 to 0.42 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 100 h || 0 to 0.6 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 125 h || 0 to 0.82 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 150 h || 0 to 0.17 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 175 h || 0 to 0.141 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 200 h || 0 to 0.188 mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 250 h || 0 to 8.76 x 10^-³ mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 300 h || 0 to 9.67 x 10^-³ mm/mm strain
    IC     (N):    tested at 750 °C (1382 °F), total strain, hot forged at 1100 °C (2012 °F), water quenched || 350 h || 0 to 0.11 mm/mm strain
    CRR    (N):    hot forged at 1100 °C (2012 °F), water quenched || tested at 700 °C (1292 °F) || 3.5 x 10^-¹⁰/s to 3.77 x 10^-⁷/s
    CRR    (N):    hot forged at 1100 °C (2012 °F), water quenched || tested at 750 °C (1382 °F) || 9.2 x 10^-¹¹/s to 7.63 x 10^-⁷/s
    CRR    (N):    hot forged at 1100 °C (2012 °F), water quenched || tested at 800 °C (1472 °F) || 1.49 x 10^-¹⁰/s to 4.95 x 10^-⁶/s

return to listing

Al₂O₃ (alpha)

    RHO    (N):    liquid || pure || 2150 °C (3902 °F) to 2395 °C (4343 °F)
    SIGMA (N):    liquid || pure || 2150 °C (3902 °F) to 2395 °C (4343 °F)
    CRR    (N):    single crystal, c-axis || tested at 1650 °C (3002 °F) || 9.5 x 10^-⁸/s to 9.06 x 10^-⁶/s
    CRR    (N):    single crystal, c-axis || tested at 1750 °C (3182 °F) || 4.55 x 10^-⁷/s to 9.5 x 10^-⁶/s
    CRR    (N):    single crystal, c-axis || tested at 1850 °C (3362 °F) || 1.28 x 10^-⁶/s to 3.66 x 10^-⁵/s

return to listing

AlSi8Cu3

    UTS    (N):    T6 temper || 20 °C (68 °F) to 150 °C (302 °F)
    YS    (N*):    T6 temper || room temperature value
    %El   (N*):    T6 temper || room temperature value
    FSN    (N):    T6 temper || tested at 150 °C (302 °F), R = 0.0, axial, 19.3 kHz, stress amplitude || 9 x 10⁵ cycles to 1.5 x 10⁹ cycles
    FSN    (N):    T6 temper || tested at 150 °C (302 °F), R = -1, axial, 19.3 kHz, stress amplitude || 8.8 x 10⁶ cycles to 3.4 x 10⁹ cycles

return to listing

Aluminum

ST (R): liquid || in vacuum, PO₂ less than 10^-²⁶ Pa || 1037 °C (1898 °F) to 1287 °C (2348 °F)
ST (N): liquid || fully oxidized surface || 670 °C (1238 °F) to 1680 °C (3056 °F)

return to listing

AM-350

CRR (N): air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h || tested at 427 °C (800 °F) || 1.76 x 10^-⁹/s to 1.78 x 10^-⁸/s
CRR (N): air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h || tested at 538 °C (1000 °F) || 7.9 x 10^-⁹/s to 2.56 x 10^-⁶/s

return to listing

AM60

    SSC    (N):    high pressure die cast, as-cast || tested at 22 °C (72 °F), 9/s || 0 to 0.12 mm/mm strain
    SSC    (N):    high pressure die cast, as-cast || tested at 22 °C (72 °F), 500/s || 0 to 0.75 mm/mm strain
    YS     (N):    high pressure die cast || 7.5 x 10^-⁴/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 0.02/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 1/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 9/s || -143 °C (-226 °F) to 100 °C (212 °F)
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 1.75 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 50 Hz, as-cast, stress amplitude || 1.75 x 10⁵ cycles to 1 x 10⁷ cycles

return to listing

AM30

    SSC    (N):    extrusion, extrusion direction || tested at -143 °C (-225 °F), 7.5 x 10^-⁴/s || 0 to 0.7 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at -110 °C (-166 °F), 7.5 x 10^-⁴/s || 0 to 0.66 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at -80 °C (-112 °F), 7.5 x 10^-⁴/s || 0 to 0.84 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at -50 °C (-58 °F), 7.5 x 10^-⁴/s || 0 to 0.79 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at -20 °C (-4 °F), 7.5 x 10^-⁴/s || 0 to 0.58 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s || 0 to 0.62 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 50 °C (122 °F), 7.5 x 10^-⁴/s || 0 to 0.73 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 100 °C (212 °F), 7.5 x 10^-⁴/s || 0 to 0.76 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 0.02/s || 0 to 0.6 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 1/s || 0 to 0.65 mm/mm strain
    SSC    (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 9/s || 0 to 0.56 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at -143 °C (-225 °F), 7.5 x 10^-⁴/s || 0 to 0.7 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at -50 °C (-58 °F), 7.5 x 10^-⁴/s || 0 to 0.13 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at -20 °C (-4 °F), 7.5 x 10^-⁴/s || 0 to 0.136 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s || 0 to 0.152 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 50 °C (122 °F), 7.5 x 10^-⁴/s || 0 to 0.16 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 100 °C (212 °F), 7.5 x 10^-⁴/s || 0 to 0.16 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 0.02/s || 0 to 0.14 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 1/s || 0 to 0.127 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 9/s || 0 to 0.13 mm/mm strain
    SSC    (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 2800/s || 0 to 0.13 mm/mm strain
    SSCC   (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s || 0 to 0.9 mm/mm strain
    SSCC   (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 0.02/s || 0 to 0.1 mm/mm strain
    SSCC   (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 1/s || 0 to 0.9 mm/mm strain
    SSCC   (N):    extrusion, extrusion direction || tested at 22 °C (72 °F), 1915/s || 0 to 0.15 mm/mm strain
    SSCC   (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s || 0 to 0.54 mm/mm strain
    SSCC   (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 0.02/s || 0 to 0.52 mm/mm strain
    SSCC   (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 1/s || 0 to 0.56 mm/mm strain
    SSCC   (N):    extrusion, transverse direction || tested at 22 °C (72 °F), 1170/s || 0 to 0.88 mm/mm strain
    UTS    (N):    extrusion, 7.5 x 10^-⁴/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 7.5 x 10^-⁴/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 0.02/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 0.02/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 1/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 1/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 9/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    UTS    (N):    extrusion, 9/s || transverse direction || -50 °C (-58 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 7.5 x 10^-⁴/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 7.5 x 10^-⁴/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 0.02/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 0.02/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 1/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 1/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 9/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion, 9/s || transverse direction || -50 °C (-58 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 7.5 x 10^-⁴/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 7.5 x 10^-⁴/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 0.02/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 0.02/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 1/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 1/s || transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 9/s || extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El    (N):    extrusion, 9/s || transverse direction || -50 °C (-58 °F) to 100 °C (212 °F)

return to listing

AM50

    SSC    (N):    high pressure die cast || tested at 22 °C (72 °F), 9/s || 0 to 0.14 mm/mm strain
    SSC    (N):    high pressure die cast || tested at 22 °C (72 °F), 800/s || 0 to 0.92 mm/mm strain
    SSC    (N):    squeeze cast || tested at -142 °C (-224 °F), 7.5 x 10^-⁴/s || 0 to 0.4 mm/mm strain
    SSC    (N):    squeeze cast || tested at -80 °C (-112 °F), 7.5 x 10^-⁴/s || 0 to 0.52 mm/mm strain
    SSC    (N):    squeeze cast || tested at -50 °C (-58 °F), 7.5 x 10^-⁴/s || 0 to 0.67 mm/mm strain
    SSC    (N):    squeeze cast || tested at 23 °C (73 °F), 7.5 x 10^-⁴/s || 0 to 0.86 mm/mm strain
    SSC    (N):    squeeze cast || tested at 50 °C (122 °F), 7.5 x 10^-⁴/s || 0 to 0.1 mm/mm strain
    SSC    (N):    squeeze cast || tested at 100 °C (212 °F), 7.5 x 10^-⁴/s || 0 to 0.1 mm/mm strain
    SSC    (N):    squeeze cast || tested at 23 °C (73 °F), 0.02/s || 0 to 0.8 mm/mm strain
    SSC    (N):    squeeze cast || tested at 23 °C (73 °F), 1/s || 0 to 0.73 mm/mm strain
    SSC    (N):    squeeze cast || tested at 23 °C (73 °F), 9/s || 0 to 0.65 mm/mm strain
    SSCC   (N):    squeeze cast || tested at -142 °C (-224 °F), 7.5 x 10^-⁴/s || 0 to 0.8 mm/mm strain
    SSCC   (N):    squeeze cast || tested at 23 °C (73 °F), 7.5 x 10^-⁴/s || 0 to 0.1 mm/mm strain
    SSCC   (N):    squeeze cast || tested at 23 °C (73 °F), 0.02/s || 0 to 0.1 mm/mm strain
    SSCC   (N):    squeeze cast || tested at -142 °C (-224 °F), 1/s || 0 to 0.11 mm/mm strain
    SSCC   (N):    squeeze cast || tested at 23 °C (73 °F), 1/s || 0 to 0.12 mm/mm strain
    SSCC   (N):    squeeze cast || tested at 23 °C (73 °F), 9/s || 0 to 0.18 mm/mm strain
    YS     (N):    squeeze cast || 7.5 x 10^-⁴/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YS     (N):    squeeze cast || 0.02/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YS     (N):    squeeze cast || 1/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YS     (N):    squeeze cast || 9/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 7.5 x 10^-⁴/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 0.02/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 1/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    high pressure die cast || 9/s || -143 °C (-226 °F) to 100 °C (212 °F)
    YSC    (N):    squeeze cast || 7.5 x 10^-⁴/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YSC    (N):    squeeze cast || 0.02/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YSC    (N):    squeeze cast || 1/s || -142 °C (-224 °F) to 100 °C (212 °F)
    YSC    (N):    squeeze cast || 9/s || -142 °C (-224 °F) to 100 °C (212 °F)
    CRR    (N):    9.2 micron grain size || tested at 150 °C (302 °F) || 1.5 x 10^-⁷/s to 1.4 x 10^-⁴/s
    CRR    (N):    9.2 micron grain size || tested at 175 °C (347 °F) || 3 x 10^-⁷/s to 6.65 x 10^-⁴/s
    CRR    (N):    9.2 micron grain size || tested at 200 °C (392 °F) || 5.7 x 10^-⁷/s to 3.63 x 10^-⁴/s
    CRR    (N):    9.2 micron grain size || tested at 225 °C (437 °F) || 6.54 x 10^-⁷/s to 3.42 x 10^-⁴/s

return to listing

Apec 1895

TWL (N): 4 mm (0.157 inch) thick || color shade 551022, tested at 20 °C (68 °F), external transmission || 320 nm to 840 nm

return to listing

Apec 1897

TWL (N): 4 mm (0.157 inch) thick || color shade 551022, tested at 20 °C (68 °F), external transmission || 391 nm to 840 nm

return to listing

API X52 pipeline steel (New)

    D     (*):    solid || room temperature value
    UTS   (*):    in air || room temperature value
    UTS   (*):    in H₂ || room temperature value
    YS    (*):    in air || room temperature value
    YS    (*):    in H₂ || room temperature value
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 10%, stress amplitude || 1.41 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 50%, stress amplitude || 1.2 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 90%, stress amplitude || 1 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 10%, stress amplitude || 1.45 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 50%, stress amplitude || 1.2 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 90%, stress amplitude || 1 x 10³ cycles to 2 x 10⁴ cycles
    FSN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 10%, stress amplitude || 210 cycles to 2 x 10⁴ cycles
    FSN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 50%, stress amplitude || 100 cycles to 2 x 10⁴ cycles
    FSN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 90%, stress amplitude || 45 cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 10%, total strain amplitude || 1.45 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 50%, total strain amplitude || 1.2 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, solid sample, Pf = 90%, total strain amplitude || 1 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 10%, total strain amplitude || 1.35 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 50%, total strain amplitude || 1.2 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in air || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 90%, total strain amplitude || 1.06 x 10³ cycles to 2 x 10⁴ cycles
    FEN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 10%, total strain amplitude || 200 cycles to 2 x 10⁴ cycles
    FEN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 50%, total strain amplitude || 100 cycles to 2 x 10⁴ cycles
    FEN       :    tested in H₂ || tested at 20 °C (68 °F), R = 0.1, axial, tube sample, Pf = 90%, total strain amplitude || 47 cycles to 2 x 10⁴ cycles

return to listing

AS21 (New)

    D     (*):    solid || room temperature value
    UTS   (*):    high pressure, die cast || as-cast || room temperature value
    YS    (*):    high pressure, die cast || as-cast || room temperature value
    %El   (*):    high pressure, die cast || as-cast || room temperature value
    FSN       :    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 1.1 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN       :    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 50 Hz, as-cast, stress amplitude || 1.1 x 10⁵ cycles to 1 x 10⁷ cycles

return to listing

ASME P92 (9 Cr - 0.5 Mo - 2 W (wt %))

CRR (N): tempered || tested at 600 °C (1112 °F) || 4.9 x 10^-¹¹/s to 1.16 x 10^-⁸/s
CRR (N): tempered || tested at 650 °C (1202 °F) || 2.56 x 10^-¹⁰/s to 8.65 x 10^-⁷/s

return to listing

AT72 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s || 0 to 0.215 mm/mm strain
    SSC       :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 454/s || 0 to 0.31 mm/mm strain
    SSC       :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 768/s || 0 to 0.46 mm/mm strain
    SSC       :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 516/s || 0 to 0.36 mm/mm strain
    SSC       :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 682/s || 0 to 0.38 mm/mm strain
    SSC       :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 520/s || 0 to 0.16 mm/mm strain
    SSC       :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 705/s || 0 to 0.27 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 1935/s || 0 to 0.17 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 2742/s || 0 to 0.195 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 3666/s || 0 to 0.23 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 4332/s || 0 to 0.23 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 4796/s || 0 to 0.215 mm/mm strain
    SSCC      :    ordinary die cast || tested at 20 °C (68 °F), as-cast, 6062/s || 0 to 0.216 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 2142/s || 0 to 0.158 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 3058/s || 0 to 0.192 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 3650/s || 0 to 0.254 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 4320/s || 0 to 0.224 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 5186/s || 0 to 0.193 mm/mm strain
    SSCC      :    vacuum die cast at -75 kPa (-10.9 psi) || tested at 20 °C (68 °F), as-cast, 6395/s || 0 to 0.242 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 2064/s || 0 to 0.16 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 2752/s || 0 to 0.21 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 3705/s || 0 to 0.23 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 4535/s || 0 to 0.23 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 5240/s || 0 to 0.164 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 6241/s || 0 to 0.23 mm/mm strain
    SSCC      :    vacuum die cast at -94 kPa (-13.6 psi) || tested at 20 °C (68 °F), as-cast, 6943/s || 0 to 0.27 mm/mm strain
    UTS   (*):    extruded || 0.002/s || room temperature value
    YS    (*):    extruded || 0.002/s || room temperature value
    %El   (*):    extruded || 0.002/s || room temperature value

return to listing

AT73 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s, 0.2 wt% Mn addition || 0 to 0.18 mm/mm strain
    UTS   (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value
    YS    (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value
    %El   (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value

return to listing

AT51 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s || 0 to 0.2 mm/mm strain
    UTS   (*):    extruded || 0.002/s || room temperature value
    YS    (*):    extruded || 0.002/s || room temperature value
    %El   (*):    extruded || 0.002/s || room temperature value

return to listing

AT52 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s, 0.2 wt% Mn addition || 0 to 0.22 mm/mm strain
    UTS   (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value
    YS    (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value
    %El   (*):    extruded || 0.002/s, 0.2 wt% Mn addition || room temperature value

return to listing

AT53 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s, 0.4 wt% Mn addition || 0 to 0.21 mm/mm strain
    UTS   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    YS    (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    %El   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value

return to listing

AT61 (New)

    SSC       :    hot-rolled, solution treated || tested at 20 °C (68 °F), 0.003/s || 0 to 0.5 mm/mm strain
    SSC       :    hot-rolled, solution treated || tested at 180 °C (356 °F), 0.003/s || 0 to 0.77 mm/mm strain
    SSC       :    0.2 wt% Mn addition || tested at 20 °C (68 °F), 0.002/s, extruded || 0 to 0.2 mm/mm strain
    UTS   (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    UTS   (*):    0.2 wt% Mn addition || 0.002/s, extruded || room temperature value
    YS    (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    YS    (*):    0.2 wt% Mn addition || 0.002/s, extruded || room temperature value
    %El   (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    %El   (*):    0.2 wt% Mn addition || 0.002/s, extruded || room temperature value
    CRS       :    3% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 1.6 h to 44.4 h
    CRS       :    4% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 2.6 h to 34.7 h
    CRS       :    5% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 6.9 h to 21.4 h
    CRS       :    6% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 11.2 h to 32 h
    CRS       :    7% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 14.6 h to 40.9 h
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 1 h || 0 to 0.35 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 3 h || 0 to 0.41 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 10 h || 0 to 0.57 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 30 h || 0 to 0.58 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 50 h || 0 to 0.47 mm/mm strain
    CRR       :    hot-rolled, solution treated || tested at 180 °C (356 °F) || 2.75 x 10^-⁸/s to 3.26 x 10^-⁷/s

return to listing

AT62 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s, 0.4 wt% Mn addition || 0 to 0.2 mm/mm strain
    UTS   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    YS    (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    %El   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value

return to listing

AT63 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s || 0 to 0.2 mm/mm strain
    UTS   (*):    extruded || 0.002/s || room temperature value
    YS    (*):    extruded || 0.002/s || room temperature value
    %El   (*):    extruded || 0.002/s || room temperature value

return to listing

AT71 (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 0.002/s, 0.4 wt% Mn addition || 0 to 0.2 mm/mm strain
    UTS   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    YS    (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value
    %El   (*):    extruded || 0.002/s, 0.4 wt% Mn addition || room temperature value

return to listing

AX61 (New)

    SSC       :    hot-rolled, solution treated || tested at 20 °C (68 °F), 0.003/s || 0 to 0.5 mm/mm strain
    SSC       :    hot-rolled, solution treated || tested at 180 °C (356 °F), 0.003/s || 0 to 0.72 mm/mm strain
    UTS   (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    YS    (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    %El   (*):    hot-rolled, solution treated || 0.003/s || room temperature value
    CRS       :    2% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 1 h to 34.2 h
    CRS       :    3% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 1.1 h to 23.7 h
    CRS       :    4% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 4.35 h to 50 h
    CRS       :    5% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 8.9 h to 33.4 h
    CRS       :    6% plastic strain, hot-rolled, solution treated || tested at 180 °C (356 °F) || 13.4 h to 47.5 h
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 1 h || 0 to 0.29 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 3 h || 0 to 0.36 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 10 h || 0 to 0.52 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 30 h || 0 to 0.48 mm/mm strain
    IC        :    tested at 180 °C (356 °F), plastic strain, hot-rolled, solution treated || 50 h || 0 to 0.63 mm/mm strain
    CRR       :    hot-rolled, solution treated || tested at 180 °C (356 °F) || 8.2 x 10^-⁹/s to 1.46 x 10^-⁷/s

return to listing

AZ61 + CaO additions (New)

    SSC       :    CaO additions || tested at 20 °C (68 °F), 0.001/s, 0 CaO || 0 to 0.144 mm/mm strain
    SSC       :    CaO additions || tested at -150 °C (-238 °F), 0.001/s, 0 CaO || 0 to 0.94 mm/mm strain
    SSC       :    CaO additions || tested at 20 °C (68 °F), 0.001/s, 0.5 CaO || 0 to 0.16 mm/mm strain
    SSC       :    CaO additions || tested at -150 °C (-238 °F), 0.001/s, 0.5 CaO || 0 to 0.125 mm/mm strain
    SSC       :    CaO additions || tested at 20 °C (68 °F), 0.001/s, 1 CaO || 0 to 0.165 mm/mm strain
    SSC       :    CaO additions || tested at -150 °C (-238 °F), 0.001/s, 1 CaO || 0 to 0.125 mm/mm strain
    UTS       :    CaO additions || 0.001/s, 0 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    UTS       :    CaO additions || 0.001/s, 0.50 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    UTS       :    CaO additions || 0.001/s, 1 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    YS        :    CaO additions || 0.001/s, 0 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    YS        :    CaO additions || 0.001/s, 0.50 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    YS        :    CaO additions || 0.001/s, 1 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    %El       :    CaO additions || 0.001/s, 0 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    %El       :    CaO additions || 0.001/s, 0.50 CaO || -150 °C (-238 °F) to 20 °C (68 °F)
    %El       :    CaO additions || 0.001/s, 1 CaO || -150 °C (-238 °F) to 20 °C (68 °F)

return to listing

AZ91 - 0.3 Ca - 0.2 Y (wt %) (New)

    SSC       :    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 300 °C (572 °F), 25:1 || 0 to 0.15 mm/mm strain
    SSC       :    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 400 °C (752 °F), 25:1 || 0 to 0.133 mm/mm strain
    SSCC      :    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 300 °C (572 °F), 25:1 || 0 to 0.132 mm/mm strain
    SSCC      :    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 400 °C (752 °F), 25:1 || 0 to 0.13 mm/mm strain
    UTS   (*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    UTS   (*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    YS    (*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    YS    (*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    YSC   (*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    YSC   (*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    %El   (*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    %El   (*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    FEN       :    normal extrusions || tested at 20 °C (68 °F), R = -1, axial, 0.5 Hz, extruded at 300 °C (572 °F), 25:1, total strain amplitude || 145 cycles to 4.8 x 10³ cycles
    FEN       :    normal extrusions || tested at 20 °C (68 °F), R = -1, axial, 0.5 Hz, extruded at 400 °C (752 °F), 25:1, total strain amplitude || 160 cycles to 9 x 10³ cycles

return to listing

AZ61

    SSC    (N):    homogenized 1 h at 400 °C (752 °F) || tested at 20 °C (68 °F), 0.001/s || 0 to 0.144 mm/mm strain
    SSC    (N):    homogenized 1 h at 400 °C (752 °F) || tested at -150 °C (-238 °F), 0.001/s || 0 to 0.94 mm/mm strain
    SSCC   (N):    solution treated || tested at 250 °C (482 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated || tested at 350 °C (662 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated || tested at 450 °C (842 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated || tested at 250 °C (482 °F), 0.1/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated || tested at 350 °C (662 °F), 0.1/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated || tested at 450 °C (842 °F), 0.1/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 250 °C (482 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 350 °C (662 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 450 °C (842 °F), 0.001/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 250 °C (482 °F), 0.1/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 350 °C (662 °F), 0.1/s || 0 to 0.6 mm/mm strain
    SSCC   (N):    solution treated, 0.33 wt% Sr addition || tested at 450 °C (842 °F), 0.1/s || 0 to 0.6 mm/mm strain
    UTS    (N):    homogenized 1 h at 400 °C (752 °F) || 0.001/s || -150 °C (-238 °F) to 20 °C (68 °F)
    YS     (N):    homogenized 1 h at 400 °C (752 °F) || 0.001/s || -150 °C (-238 °F) to 20 °C (68 °F)
    %El    (N):    homogenized 1 h at 400 °C (752 °F) || 0.001/s || -150 °C (-238 °F) to 20 °C (68 °F)
    CRR    (N):    solution treated at 420 °C (788 °F) || tested at 180 °C (356 °F) || 1 x 10^-⁸/s to 2.45 x 10^-⁷/s

return to listing

AZ31

    SSC    (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s, extrusion direction || 0 to 0.37 mm/mm strain
    SSC    (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s, transverse direction || 0 to 0.167 mm/mm strain
    SSC    (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 0.02/s, transverse direction || 0 to 0.155 mm/mm strain
    SSC    (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 1/s, transverse direction || 0 to 0.147 mm/mm strain
    SSC    (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 2620/s, transverse direction || 0 to 0.153 mm/mm strain
    SSC    (N):    twin roll cast || tested at 20 °C (68 °F), homogenized 6 h at 425 °C (797 °F), unknown strain rate || 0 to 0.132 mm/mm strain
    SSC    (N):    twin roll cast || tested at 20 °C (68 °F), symmetrically rolled, unknown strain rate || 0 to 0.15 mm/mm strain
    SSC    (N):    twin roll cast || tested at 20 °C (68 °F), asymmetrically rolled, unknown strain rate || 0 to 0.132 mm/mm strain
    SSC    (N):    2 mm (0.0787 inch) sheet || tested at 22 °C (72 °F), rolling direction, 7.5 x 10^-⁴/s || 0 to 0.172 mm/mm strain
    SSC    (N):    2 mm (0.0787 inch) sheet || tested at 22 °C (72 °F), transverse direction, 7.5 x 10^-⁴/s || 0 to 0.137 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, CSE process, extrusion direction || 0 to 0.152 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, CSE process, 45 to extrusion direction || 0 to 0.224 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, CSE process, transverse direction || 0 to 0.196 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, PASE process, extrusion direction || 0 to 0.148 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, PASE process, 45 to extrusion direction || 0 to 0.22 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, PASE process, transverse direction || 0 to 0.186 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, SASE process, extrusion direction || 0 to 0.228 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, SASE process, 45 to extrusion direction || 0 to 0.19 mm/mm strain
    SSC    (N):    effect of extrusion process, 2 mm (0.0787 inch) sheet || tested at 20 °C (68 °F), 0.001/s, SASE process, transverse direction || 0 to 0.167 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), as-received, unknown strain rate || 0 to 0.12 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), rolled at 250 °C (482 °F), unknown strain rate || 0 to 0.54 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), rolled at 300 °C (572 °F), unknown strain rate || 0 to 0.45 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), rolled at 350 °C (662 °F), unknown strain rate || 0 to 0.57 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), rolled at 400 °C (752 °F), unknown strain rate || 0 to 0.42 mm/mm strain
    SSC    (N):    effect of rolling temperature || tested at 20 °C (68 °F), rolled at 450 °C (842 °F), unknown strain rate || 0 to 0.55 mm/mm strain
    SSC    (N):    effect of caliber rolling || tested at 20 °C (68 °F), 0.005/s, as-received, 15 mm x 6 mm x 2 mm (0.591 inch x 0.236 inch x 0.0787 inch) gage section || 0 to 0.154 mm/mm strain
    SSC    (N):    effect of caliber rolling || tested at 20 °C (68 °F), 0.005/s, 1 pass, 14.8% reduction in area || 0 to 0.2 mm/mm strain
    SSC    (N):    effect of caliber rolling || tested at 20 °C (68 °F), 0.005/s, 3 passes, 52.8% reduction in area || 0 to 0.183 mm/mm strain
    SSC    (N):    effect of caliber rolling || tested at 20 °C (68 °F), 0.005/s, 5 passes, 74.5% reduction in area || 0 to 0.2 mm/mm strain
    SSC    (N):    effect of caliber rolling || tested at 20 °C (68 °F), 0.005/s, 7 passes, 84.6% reduction in area || 0 to 0.167 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s, extrusion direction || 0 to 0.1 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 0.02/s, extrusion direction || 0 to 0.88 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 1/s, extrusion direction || 0 to 0.1 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 2120/s, extrusion direction || 0 to 0.15 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 7.5 x 10^-⁴/s, transverse direction || 0 to 0.48 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 0.02/s, transverse direction || 0 to 0.48 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 1/s, transverse direction || 0 to 0.72 mm/mm strain
    SSCC   (N):    22 mm (0.866 inch) extrusion (ratio = 6) || tested at 22 °C (72 °F), 1050/s, transverse direction || 0 to 0.11 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 250 °C (482 °F), 0.01/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 250 °C (482 °F), 0.1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 250 °C (482 °F), 1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 300 °C (572 °F), 0.01/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 300 °C (572 °F), 0.1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 300 °C (572 °F), 1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 400 °C (752 °F), 0.01/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 400 °C (752 °F), 0.1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions (20:1) || tested at 400 °C (752 °F), 1/s || 0 to 0.5 mm/mm strain
    SSCC   (N):    extrusions, annealed 3 h at 470 °C (878 °F) || tested at 20 °C (68 °F), 1000/s || 0 to 0.9 mm/mm strain
    SSCC   (N):    extrusions, annealed 3 h at 470 °C (878 °F) || tested at 20 °C (68 °F), 1250/s || 0 to 0.98 mm/mm strain
    SSCC   (N):    hot-rolled plate, annealed 28 h at 350 °C (662 °F) || tested at 350 °C (662 °F), 0.01/s, rolling direction || 0 to 0.1 mm/mm strain
    SSCC   (N):    hot-rolled plate, annealed 28 h at 350 °C (662 °F) || tested at 350 °C (662 °F), 0.01/s, transverse direction || 0 to 0.11 mm/mm strain
    YS     (N):    extrusion || 7.5 x 10^-⁴/s, extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion || 0.02/s, extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion || 1/s, extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    extrusion || 9/s, extrusion direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 7.5 x 10^-⁴/s, rolling direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 0.02/s, rolling direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 1/s, rolling direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 9/s, rolling direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 7.5 x 10^-⁴/s, transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 0.02/s, transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 1/s, transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    YS     (N):    2 mm (0.0787 inch) sheet || 9/s, transverse direction || -143 °C (-226 °F) to 100 °C (212 °F)
    %El   (N*):    extrusion || 7.5 x 10^-⁴/s, extrusion direction || room temperature value
    %El   (N*):    extrusion || 7.5 x 10^-⁴/s, transverse direction || room temperature value
    %El   (N*):    2 mm (0.0787 inch) sheet || 7.5 x 10^-⁴/s, rolling direction || room temperature value
    %El   (N*):    2 mm (0.0787 inch) sheet || 7.5 x 10^-⁴/s, transverse direction || room temperature value

return to listing

AZ80

    SSC    (N):    annular channel angular extruded || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.13 mm/mm strain
    SSC    (N):    back extruded || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s, 1 mm (0.0394 inch) from inner wall || 0 to 0.114 mm/mm strain
    SSC    (N):    back extruded || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s, 8 mm (0.315 inch) from inner wall || 0 to 0.1 mm/mm strain
    SSC    (N):    back extruded || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s, 15 mm (0.591 inch) from inner wall || 0 to 0.8 mm/mm strain
    SSC    (N):    AZ80M || tested at 20 °C (68 °F), 0.001/s, as-cast || 0 to 0.5 mm/mm strain
    SSC    (N):    AZ80M || tested at 20 °C (68 °F), 0.001/s, as-extruded || 0 to 0.128 mm/mm strain
    SSC    (N):    AZ80M || tested at 20 °C (68 °F), 0.001/s, WAAM, vertical || 0 to 0.95 mm/mm strain
    SSC    (N):    AZ80M || tested at 20 °C (68 °F), 0.001/s, WAAM, horizontal || 0 to 0.112 mm/mm strain
    SSC    (N):    extruded (50:1) || tested at 23 °C (73 °F), 0.001/s || 0 to 0.139 mm/mm strain
    SSC    (N):    0.8 wt% Ce addition || tested at 23 °C (73 °F), 0.001/s, as-extruded || 0 to 0.137 mm/mm strain
    SSC    (N):    0.8 wt% Ce addition || tested at 23 °C (73 °F), 0.001/s, single-pass rolled || 0 to 0.58 mm/mm strain
    SSC    (N):    0.8 wt% Ce addition || tested at 23 °C (73 °F), 0.001/s, four-pass rolled || 0 to 0.74 mm/mm strain
    UTS   (N*):    AZ80M || 0.001/s, as-cast || room temperature value
    UTS   (N*):    AZ80M || 0.001/s, as-extruded || room temperature value
    UTS   (N*):    AZ80M || 0.001/s, WAAM, vertical || room temperature value
    UTS   (N*):    AZ80M || 0.001/s, WAAM, horizontal || room temperature value
    YS    (N*):    AZ80M || 0.001/s, as-cast || room temperature value
    YS    (N*):    AZ80M || 0.001/s, as-extruded || room temperature value
    YS    (N*):    AZ80M || 0.001/s, WAAM, vertical || room temperature value
    YS    (N*):    AZ80M || 0.001/s, WAAM, horizontal || room temperature value
    %El   (N*):    AZ80M || 0.001/s, as-cast || room temperature value
    %El   (N*):    AZ80M || 0.001/s, as-extruded || room temperature value
    %El   (N*):    AZ80M || 0.001/s, WAAM, vertical || room temperature value
    %El   (N*):    AZ80M || 0.001/s, WAAM, horizontal || room temperature value

return to listing

AZ91

    SSC    (N):    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 300 °C (572 °F), 25:1 || 0 to 0.122 mm/mm strain
    SSC    (N):    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 400 °C (752 °F), 25:1 || 0 to 0.71 mm/mm strain
    SSC    (N):    high pressure die cast || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, annealed 1 h at 260 °C (500 °F) || 0 to 0.57 mm/mm strain
    SSC    (N):    effect of friction stir process || tested at 20 °C (68 °F), 0.001/s, base material, 72 micron grain size || 0 to 0.1 mm/mm strain
    SSC    (N):    effect of friction stir process || tested at 20 °C (68 °F), 0.001/s, friction stir process, 8.4 micron grain size || 0 to 0.14 mm/mm strain
    SSC    (N):    effect of friction stir process || tested at 20 °C (68 °F), 0.001/s, submerged friction stir process, 2.8 micron grain size || 0 to 0.162 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 4 x 10^-⁴/s, 90 W, 300 mm/s, horizontal || 0 to 0.85 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 4 x 10^-⁴/s, 90 W, 700 mm/s, horizontal || 0 to 7 x 10^-³ mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 4 x 10^-⁴/s, 90 W, 300 mm/s, vertical || 0 to 0.65 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 4 x 10^-⁴/s, 50 W, 300 mm/s, horizontal || 0 to 3.8 x 10^-³ mm/mm strain
    SSCC   (N):    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 300 °C (572 °F), 25:1 || 0 to 0.132 mm/mm strain
    SSCC   (N):    normal extrusions || tested at 20 °C (68 °F), 0.001/s, extruded at 400 °C (752 °F), 25:1 || 0 to 0.1 mm/mm strain
    SSCC   (N):    high pressure die cast || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, annealed 1 h at 260 °C (500 °F) || 0 to 0.27 mm/mm strain
    SSCC   (N):    Spark plasma sintered || tested at 20 °C (68 °F), 0.001/s, sintered at 320 °C (608 °F) || 0 to 0.93 mm/mm strain
    SSCC   (N):    Spark plasma sintered || tested at 20 °C (68 °F), 0.001/s, sintered at 420 °C (788 °F) || 0 to 0.125 mm/mm strain
    SSCC   (N):    Spark plasma sintered || tested at 20 °C (68 °F), 0.001/s, sintered at 520 °C (968 °F) || 0 to 0.111 mm/mm strain
    UTS   (N*):    effect of friction stir process || base material, 72 micron grain size || room temperature value
    UTS   (N*):    effect of friction stir process || friction stir process, 8.4 micron grain size || room temperature value
    UTS   (N*):    effect of friction stir process || submerged friction stir process, 2.8 micron grain size || room temperature value
    UTS   (N*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    UTS   (N*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    UTS   (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 300 mm/s, horizontal || room temperature value
    UTS   (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 700 mm/s, horizontal || room temperature value
    UTS   (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 300 mm/s, vertical || room temperature value
    UTS   (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 50 W, 300 mm/s, horizontal || room temperature value
    YS    (N*):    effect of friction stir process || base material, 72 micron grain size || room temperature value
    YS    (N*):    effect of friction stir process || friction stir process, 8.4 micron grain size || room temperature value
    YS    (N*):    effect of friction stir process || submerged friction stir process, 2.8 micron grain size || room temperature value
    YS    (N*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    YS    (N*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    YS    (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 300 mm/s, horizontal || room temperature value
    YS    (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 700 mm/s, horizontal || room temperature value
    YS    (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 90 W, 300 mm/s, vertical || room temperature value
    YS    (N*):    laser powder bed fusion || 4 x 10^-⁴/s, 50 W, 300 mm/s, horizontal || room temperature value
    UCS   (N*):    Spark plasma sintered || 0.001/s, sintered at 320 °C (608 °F) || room temperature value
    UCS   (N*):    Spark plasma sintered || 0.001/s, sintered at 420 °C (788 °F) || room temperature value
    UCS   (N*):    Spark plasma sintered || 0.001/s, sintered at 520 °C (968 °F) || room temperature value
    YSC   (N*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    YSC   (N*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    YSC   (N*):    Spark plasma sintered || 0.001/s, sintered at 320 °C (608 °F) || room temperature value
    YSC   (N*):    Spark plasma sintered || 0.001/s, sintered at 420 °C (788 °F) || room temperature value
    YSC   (N*):    Spark plasma sintered || 0.001/s, sintered at 520 °C (968 °F) || room temperature value
    %El   (N*):    effect of friction stir process || base material, 72 micron grain size || room temperature value
    %El   (N*):    effect of friction stir process || friction stir process, 8.4 micron grain size || room temperature value
    %El   (N*):    effect of friction stir process || submerged friction stir process, 2.8 micron grain size || room temperature value
    %El   (N*):    normal extrusions || 0.001/s, extruded at 300 °C (572 °F), 25:1 || room temperature value
    %El   (N*):    normal extrusions || 0.001/s, extruded at 400 °C (752 °F), 25:1 || room temperature value
    %El   (N*):    Spark plasma sintered || 0.001/s, sintered at 320 °C (608 °F), in compression || room temperature value
    %El   (N*):    Spark plasma sintered || 0.001/s, sintered at 420 °C (788 °F), in compression || room temperature value
    %El   (N*):    Spark plasma sintered || 0.001/s, sintered at 520 °C (968 °F), in compression || room temperature value
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 4.15 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    high pressure, die cast || tested at 20 °C (68 °F), R = -1, axial, 50 Hz, as-cast, stress amplitude || 4.15 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    Vacural, die cast || tested at 20 °C (68 °F), R = -1, axial, 20 kHz, as-cast, stress amplitude || 8 x 10⁴ cycles to 2 x 10⁹ cycles
    FSN    (N):    sand cast, T6 temper || tested at 20 °C (68 °F), R = -1, axial, 30 Hz, stress amplitude || 580 cycles to 1 x 10⁷ cycles
    FSN    (N):    sand cast, T6 temper || tested at 150 °C (302 °F), R = -1, axial, 30 Hz, stress amplitude || 700 cycles to 1 x 10⁸ cycles
    FEN    (N):    sand cast, T6 temper || tested at 20 °C (68 °F), R = -1, axial, 1 Hz, total strain amplitude || 590 cycles to 1 x 10⁷ cycles
    FEN    (N):    sand cast, T6 temper || tested at 150 °C (302 °F), R = -1, axial, 1 Hz, total strain amplitude || 710 cycles to 1 x 10⁷ cycles
    FEN    (N):    normal extrusions || tested at 20 °C (68 °F), R = -1, axial, 0.5 Hz, extruded at 300 °C (572 °F), 25:1, total strain amplitude || 145 cycles to 2.43 x 10³ cycles
    FEN    (N):    normal extrusions || tested at 20 °C (68 °F), R = -1, axial, 0.5 Hz, extruded at 400 °C (752 °F), 25:1, total strain amplitude || 300 cycles to 8.13 x 10³ cycles

return to listing

BA53 (New)

    SSC       :    extruded (27.4:1) || tested at 23 °C (73 °F), 0.001/s || 0 to 0.12 mm/mm strain
    SSC       :    extruded (50:1) || tested at 23 °C (73 °F), 0.001/s || 0 to 0.1 mm/mm strain
    SSCC      :    extruded (27.4:1) || tested at 23 °C (73 °F), 0.001/s || 0 to 0.16 mm/mm strain
    FSN       :    extruded (27.4:1) || tested at 20 °C (68 °F), R = -1, axial, stress amplitude || 4 x 10³ cycles to 1 x 10⁷ cycles

return to listing

BeO

    CRR    (N):    single crystal, [11̅ 01] direction || tested at 650 °C (1202 °F) || 1.31 x 10^-⁷/s to 7.3 x 10^-⁷/s
    CRR    (N):    single crystal, [11̅ 01] direction || tested at 700 °C (1292 °F) || 3.15 x 10^-⁸/s to 4.5 x 10^-⁶/s
    CRR    (N):    single crystal, [11̅ 01] direction || tested at 750 °C (1382 °F) || 3.8 x 10^-⁷/s to 1.15 x 10^-⁵/s
    CRR    (N):    single crystal, [11̅ 01] direction || tested at 800 °C (1472 °F) || 1.97 x 10^-⁷/s to 8.32 x 10^-⁶/s
    CRR    (N):    single crystal, [11̅ 00] direction || tested at 1650 °C (3002 °F) || 7.2 x 10^-⁹/s to 1.55 x 10^-⁷/s
    CRR    (N):    single crystal, [11̅ 00] direction || tested at 1750 °C (3182 °F) || 3.35 x 10^-⁸/s to 1.11 x 10^-⁶/s
    CRR    (N):    single crystal, [11̅ 00] direction || tested at 1850 °C (3362 °F) || 2.35 x 10^-⁷/s to 4.8 x 10^-⁷/s

return to listing

C-110M (Ti - 8 Mn (wt %))

    UTS   (N*):    effect of interstitials, 0.02/s || annealed, 0.025 C, 0.025 N, 0.228 O, 0.028 H (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.025 C, 0.125 N, 0.209 O, 0.011 H (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 0.02/s || 0.02 C, 0.21 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.18 C, 0.085 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || annealed, 0.025 C, 0.025 N, 0.228 O, 0.028 H (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.025 C, 0.125 N, 0.209 O, 0.011 H (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 2/s || 0.02 C, 0.21 N (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 2/s || 0.02 C, 0.113 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || 0.18 C, 0.085 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.02 C, 0.108 N, 0.361 O, 0.026 H (wt %) || room temperature value
    CRR    (N):    annealed sheet || tested at 316 °C (600 °F) || 1.16 x 10^-⁹/s to 2.05 x 10^-⁸/s
    CRR    (N):    annealed sheet || tested at 371 °C (700 °F) || 2.15 x 10^-⁹/s to 8.42 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 427 °C (800 °F) || 2.8 x 10^-⁸/s to 1.56 x 10^-⁵/s
    CRR    (N):    annealed sheet || tested at 454 °C (850 °F) || 2.16 x 10^-⁷/s to 4.87 x 10^-⁶/s

return to listing

CB Cupron

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

CF3

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

CF8

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

CF20

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

CMSX-4

    TC     (N):    liquid || 1380 °C (2516 °F) to 1600 °C (2912 °F)
    SH     (N):    liquid || 1380 °C (2516 °F) to 1600 °C (2912 °F)
    TD     (R):    liquid || 1380 °C (2516 °F) to 1600 °C (2912 °F)
    CRS    (N):    1% plastic strain, <001> || tested at 850 °C (1562 °F) || 65 h to 3,000 h
    CRS    (N):    1% plastic strain, <001> || tested at 900 °C (1652 °F) || 15 h to 400 h
    CRS    (N):    1% plastic strain, <001> || tested at 950 °C (1742 °F) || 10 h to 1,200 h
    CRS    (N):    1% plastic strain, <001> || tested at 1000 °C (1832 °F) || 20 h to 300 h
    CRS    (N):    1% plastic strain, <001> || tested at 1050 °C (1922 °F) || 35 h to 350 h
    CRS    (N):    1% plastic strain, <001> || tested at 1100 °C (2012 °F) || 10 h to 310 h
    CRS    (N):    1% plastic strain, <001> || Master curve (LMP) || 22.3 h to 28.1 h

return to listing

Constantan

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

Copper

    CRR    (N):    annealed || tested at 149 °C (300 °F) || 3 x 10^-¹²/s to 2.2 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 264 °C (507 °F) || 3 x 10^-¹¹/s to 5 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 149 °C (300 °F) || 3 x 10^-¹²/s to 2.6 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 264 °C (507 °F) || 3 x 10^-¹²/s to 5.6 x 10^-¹⁰/s

return to listing

2.25 Cr - 1 Mo (ASTM A542)

    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 482 °C (900 °F), plastic strain, normalized & tempered || 100,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 510 °C (950 °F), plastic strain, normalized & tempered || 100,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 538 °C (1000 °F), plastic strain, normalized & tempered || 100,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 566 °C (1050 °F), plastic strain, normalized & tempered || 100,000 h || 0 to 0.01 mm/mm strain
    CRR    (N):    annealed || tested at 454 °C (850 °F) || 1 x 10^-¹¹/s to 1.82 x 10^-⁷/s
    CRR    (N):    annealed || tested at 510 °C (950 °F) || 5 x 10^-¹¹/s to 2 x 10^-⁷/s
    CRR    (N):    annealed || tested at 538 °C (1000 °F) || 3.3 x 10^-¹¹/s to 3.62 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 566 °C (1050 °F) || 5.2 x 10^-¹¹/s to 1.5 x 10^-⁶/s
    CRR    (N):    quenched and tempered || tested at 538 °C (1000 °F) || 2.7 x 10^-⁷/s to 8.4 x 10^-⁶/s
    CRR    (N):    quenched and tempered || tested at 593 °C (1100 °F) || 2 x 10^-⁸/s to 1.6 x 10^-⁵/s
    CRR    (N):    quenched and tempered || tested at 704 °C (1300 °F) || 3.8 x 10^-⁸/s to 7.51 x 10^-⁶/s

return to listing

Cu - 10 Al (wt %)

CRR (N): annealed || tested at 250 °C (482 °F) || 1.2 x 10^-¹⁰/s to 1 x 10^-⁸/s

return to listing

Cu - 30 Ni (wt %)

    FSN    (N):    rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, drawn 33%, maximum stress || 7.2 x 10⁵ cycles to 1 x 10⁸ cycles
    CRR    (N):    annealed || tested at 149 °C (300 °F), 25 micron grain size || 2.7 x 10^-¹³/s to 6.81 x 10^-¹²/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 25 micron grain size || 2.55 x 10^-¹²/s to 1.6 x 10^-¹¹/s
    CRR    (N):    drawn 84% || tested at 260 °C (500 °F) || 1.75 x 10^-¹²/s to 1.05 x 10^-¹¹/s

return to listing

Cu - 45 Ni (wt %)

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

Cu - 10 Ni (wt %)

    E      (R):    annealed || -269.1 °C (-452.5 °F) to 261 °C (502 °F)
    CRR    (N):    annealed || tested at 149 °C (300 °F), 30 micron grain size || 7.9 x 10^-¹³/s to 2.7 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 30 micron grain size || 2.7 x 10^-¹²/s to 2.7 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 30 micron grain size || 2.7 x 10^-¹²/s to 2.7 x 10^-¹⁰/s

return to listing

Cu - 15 Zn (wt %)

CRR (N): annealed || tested at 149 °C (300 °F) || 2 x 10^-¹²/s to 6.64 x 10^-¹¹/s

return to listing

Delrin 100

    FS    (N*):    NC010 || at 3.5% strain || room temperature value
    FS    (N*):    NC010 || at yield || room temperature value
    UCS   (N*):    NC010 || ISO 604 || room temperature value
    %El   (N*):    NC010 || at yield || room temperature value

return to listing

Delrin 500

    E      (N):    ISO 527, 1 mm/min || 20 °C (68 °F) to 120 °C (248 °F)
    E      (R):    ASTM D638, 5 mm/min || 20 °C (68 °F) to 70 °C (158 °F)
    E      (N):    average of ASTM and ISO measurements || 20 °C (68 °F) to 70 °C (158 °F)

return to listing

DOWSIL 3-6751 adhesive

    DLL    (N):    solid || 0 °C (32 °F) to 50 °C (122 °F)
    MTE    (N):    solid || 0 °C (32 °F) to 50 °C (122 °F)
    CTE    (N):    solid || 0 °C (32 °F) to 50 °C (122 °F)
    D      (N):    solid || 0 °C (32 °F) to 50 °C (122 °F)
    TC    (N*):    solid || room temperature value
    RHO   (N*):    solid || room temperature value
    SIGMA (N*):    solid || room temperature value
    DCRPT (N):    unknown method || tested at 23 °C (73 °F) || 100 Hz to 100 kHz
    DF     (N):    unknown method || tested at 23 °C (73 °F) || 100 Hz to 100 kHz

return to listing

DOWSIL 1-4174 adhesive (New)

    DLL       :    solid || 0 °C (32 °F) to 50 °C (122 °F)
    MTE       :    solid || 0 °C (32 °F) to 50 °C (122 °F)
    CTE       :    solid || 0 °C (32 °F) to 50 °C (122 °F)
    D         :    solid || 0 °C (32 °F) to 50 °C (122 °F)
    D     (*):    liquid || room temperature value
    TC    (*):    solid || room temperature value
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    Vis   (*):    liquid || room temperature value
    DCRPT    :    unknown method || tested at 23 °C (73 °F) || 100 Hz to 100 kHz

return to listing

Ductile iron ASTM 80-55-06 (EN-GJS-600) (3.6 C - 2.7 Si - 0.2 Mn (wt %))

    DLL    (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    DLL    (N):    liquid || 1300 °C (2372 °F) to 1500 °C (2732 °F)
    MTE    (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    MTE    (N):    liquid || 1300 °C (2372 °F) to 1500 °C (2732 °F)
    CTE    (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    CTE    (N):    liquid || 1300 °C (2372 °F) to 1500 °C (2732 °F)
    D      (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    D      (N):    liquid || 1300 °C (2372 °F) to 1500 °C (2732 °F)
    TC     (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    SH     (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)
    SH     (N):    liquid || 1178 °C (2152 °F) to 1500 °C (2732 °F)
    TD     (N):    solid || 20 °C (68 °F) to 1100 °C (2012 °F)

return to listing

E235

    SSC    (N):    T6 temper || tested at 20 °C (68 °F), 7.7 x 10^-⁴/s || 0 to 0.227 mm/mm strain
    UTS   (N*):    normalized || room temperature value
    YS    (N*):    normalized || room temperature value
    %El   (N*):    normalized || room temperature value
    FEN    (N):    normalized || tested at 20 °C (68 °F), R = -1, axial, 0.001/s strain rate, equivalent strain amplitude || 630 cycles to 4 x 10⁴ cycles
    FEN    (N):    normalized || tested at 20 °C (68 °F), R = -1, torsional, 0.001/s strain rate, equivalent strain amplitude || 970 cycles to 3.7 x 10⁴ cycles

return to listing

EOS StainlessSteel CX

    SSCC   (N):    1/s, as-built || tested at 300 °C (572 °F) || 0 to 0.34 mm/mm strain
    SSCC   (N):    1/s, as-built || tested at 450 °C (842 °F) || 0 to 0.19 mm/mm strain
    SSCC   (N):    1/s, as-built || tested at 550 °C (1022 °F) || 0 to 0.89 mm/mm strain
    SSCC   (N):    1/s, as-built || tested at 600 °C (1112 °F) || 0 to 0.89 mm/mm strain
    SSCC   (N):    1/s, as-built || tested at 650 °C (1202 °F) || 0 to 0.89 mm/mm strain
    SSCC   (N):    1/s, H986 heat treatment || tested at 300 °C (572 °F) || 0 to 0.24 mm/mm strain
    SSCC   (N):    1/s, H986 heat treatment || tested at 450 °C (842 °F) || 0 to 0.9 mm/mm strain
    SSCC   (N):    1/s, H986 heat treatment || tested at 550 °C (1022 °F) || 0 to 0.87 mm/mm strain
    SSCC   (N):    1/s, H986 heat treatment || tested at 600 °C (1112 °F) || 0 to 0.87 mm/mm strain
    SSCC   (N):    1/s, H986 heat treatment || tested at 650 °C (1202 °F) || 0 to 0.88 mm/mm strain

return to listing

ERNiCr-3 weld metal

CRR (N): deposited by the GTAW process || tested at 649 °C (1200 °F) || 3.6 x 10^-¹¹/s to 1.4 x 10^-⁶/s

return to listing

ER70S-6

    UTS   (N*):    wire feedstock || room temperature value
    YS    (N*):    wire feedstock || room temperature value
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, horizontal, total strain amplitude || 140 cycles to 2 x 10⁵ cycles
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, horizontal, plastic strain amplitude || 140 cycles to 2 x 10⁵ cycles
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, horizontal, elastic strain amplitude || 140 cycles to 2 x 10⁵ cycles
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, vertical, total strain amplitude || 84 cycles to 6 x 10⁵ cycles
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, vertical, plastic strain amplitude || 84 cycles to 6 x 10⁵ cycles
    FEN    (N):    wire + arc additive manufacturing (WAAM), axial || tested at 20 °C (68 °F), R =-1, vertical, elastic strain amplitude || 84 cycles to 6 x 10⁵ cycles

return to listing

EW75 (New)

    SSC       :    forged at 410 °C (770 °F) || tested at 20 °C (68 °F), 0.001/s || 0 to 0.16 mm/mm strain
    SSC       :    forged at 440 °C (824 °F) || tested at 20 °C (68 °F), 0.001/s || 0 to 0.157 mm/mm strain
    SSC       :    forged at 470 °C (878 °F) || tested at 20 °C (68 °F), 0.001/s || 0 to 0.2 mm/mm strain
    SSC       :    forged at 500 °C (932 °F) || tested at 20 °C (68 °F), 0.001/s || 0 to 0.61 mm/mm strain
    SSCC      :    extrusion || tested at 27 °C (80 °F), 949/s || 0 to 0.39 mm/mm strain
    SSCC      :    extrusion || tested at 27 °C (80 °F), 1392/s || 0 to 0.61 mm/mm strain
    SSCC      :    extrusion || tested at 27 °C (80 °F), 1992/s || 0 to 0.1 mm/mm strain
    SSCC      :    extrusion || tested at 27 °C (80 °F), 2826/s || 0 to 0.126 mm/mm strain
    SSCC      :    extrusion || tested at 200 °C (392 °F), 1078/s || 0 to 0.41 mm/mm strain
    SSCC      :    extrusion || tested at 200 °C (392 °F), 1406/s || 0 to 0.69 mm/mm strain
    SSCC      :    extrusion || tested at 200 °C (392 °F), 2187/s || 0 to 0.11 mm/mm strain
    SSCC      :    extrusion || tested at 300 °C (572 °F), 1320/s || 0 to 0.69 mm/mm strain
    SSCC      :    extrusion || tested at 300 °C (572 °F), 1978/s || 0 to 0.11 mm/mm strain
    SSCC      :    extrusion || tested at 300 °C (572 °F), 2292/s || 0 to 0.126 mm/mm strain
    SSCC      :    extrusion || tested at 300 °C (572 °F), 3344/s || 0 to 0.2 mm/mm strain
    UTS   (*):    forged at 410 °C (770 °F) || 0.001/s || room temperature value
    UTS   (*):    forged at 440 °C (824 °F) || 0.001/s || room temperature value
    UTS   (*):    forged at 470 °C (878 °F) || 0.001/s || room temperature value
    UTS   (*):    forged at 500 °C (932 °F) || 0.001/s || room temperature value
    YS    (*):    forged at 410 °C (770 °F) || 0.001/s || room temperature value
    YS    (*):    forged at 440 °C (824 °F) || 0.001/s || room temperature value
    YS    (*):    forged at 470 °C (878 °F) || 0.001/s || room temperature value
    YS    (*):    forged at 500 °C (932 °F) || 0.001/s || room temperature value
    %El   (*):    forged at 410 °C (770 °F) || 0.001/s || room temperature value
    %El   (*):    forged at 440 °C (824 °F) || 0.001/s || room temperature value
    %El   (*):    forged at 470 °C (878 °F) || 0.001/s || room temperature value
    %El   (*):    forged at 500 °C (932 °F) || 0.001/s || room temperature value
    FSN       :    forged material || tested at 20 °C (68 °F), R = -1, K_t = 1, axial, longidutinal direction, stress amplitude || 1.4 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN       :    forged material || tested at 20 °C (68 °F), R = -1, K_t = 3, axial, longidutinal direction, stress amplitude || 3.9 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN       :    forged material || tested at 20 °C (68 °F), R = 0.1, K_t = 1, axial, longidutinal direction, stress amplitude || 3.4 x 10⁴ cycles to 1 x 10⁸ cycles

return to listing

EXTEM RH1017UCL

    RIW    (R):    measured in air, grade 1000 || tested at 30 °C (86 °F) || 390 nm to 1540 nm
    RIT    (N):    measured in air, grade 1000 || measured at 850 nm || 30 °C (86 °F) to 120 °C (248 °F)
    RIT    (N):    measured in air, grade 1000 || measured at 1310 nm || 30 °C (86 °F) to 120 °C (248 °F)
    RIT    (N):    measured in air, grade 1000 || measured at 1550 nm || 30 °C (86 °F) to 120 °C (248 °F)

return to listing

EXTEM VH1003

TC (N*): solid || room temperature value

return to listing

EXTEM VH1003F

TC (N*): solid || room temperature value

return to listing

EXTEM VH1003M

TC (N*): solid || room temperature value

return to listing

EXTEM VH1003P

TC (N*): solid || room temperature value

return to listing

EXTEM XH2315 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    D         :    solid || 20 °C (68 °F) to 150 °C (302 °F)
    FS    (*):    ASTM D790 || 1.3 mm/min, at yield || room temperature value
    FS    (*):    ISO 178 || 2 mm/min, at yield || room temperature value
    E     (*):    ASTM D638 || 5 mm/min || room temperature value
    E     (*):    ISO 527 || 1 mm/min || room temperature value
    FM    (*):    ASTM D790 || 1.3 mm/min || room temperature value
    FM    (*):    ISO 178 || 2 mm/min || room temperature value
    UTS   (*):    ASTM D638 || 5 mm/min, at break || room temperature value
    UTS   (*):    ISO 527 || 5 mm/min, at break || room temperature value
    YS    (*):    ASTM D638 || 5 mm/min || room temperature value
    YS    (*):    ISO 527 || 1 mm/min || room temperature value
    %El   (*):    ASTM D638 || 5 mm/min, at yield || room temperature value
    %El   (*):    ASTM D638 || 5 mm/min, at break || room temperature value
    %El   (*):    ISO 527 || 5 mm/min, at yield || room temperature value
    %El   (*):    ISO 527 || 5 mm/min, at break || room temperature value

return to listing

EXTEM XH2115 (New)

    D     (*):    solid || room temperature value
    FS    (*):    ASTM D790 || 1.3 mm/min, at yield || room temperature value
    FS    (*):    ASTM D790 || 1.3 mm/min, at break || room temperature value
    FS    (*):    ISO 178 || 2 mm/min, at yield || room temperature value
    E     (*):    ASTM D638 || 5 mm/min || room temperature value
    E     (*):    ISO 527 || 1 mm/min || room temperature value
    FM    (*):    ASTM D790 || 1.3 mm/min || room temperature value
    FM    (*):    ISO 178 || 2 mm/min || room temperature value
    UTS   (*):    ASTM D638 || 5 mm/min, at break || room temperature value
    UTS   (*):    ISO 527 || 5 mm/min, at break || room temperature value
    %El   (*):    ASTM D638 || 5 mm/min, at break || room temperature value
    %El   (*):    ISO 527 || 5 mm/min, at break || room temperature value
    %El   (*):    ISO 178, in flexure || 2 mm/min, at break || room temperature value

return to listing

EXTEM XH1015UCL

    DLL    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    DLL    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    DLL    (N):    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    MTE    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    MTE    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    MTE    (N):    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    CTE    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    CTE    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 150 °C (302 °F)
    CTE    (N):    solid || weighted average || 20 °C (68 °F) to 150 °C (302 °F)
    D      (N):    solid || 20 °C (68 °F) to 150 °C (302 °F)
    DCRPT (N):    ASTM D150 || tested at 23 °C (73 °F) || 1 kHz to 1 MHz
    RIT   (N*):    measured in air || measured at 589.3 nm || room temperature value
    RIT   (N*):    measured in air || measured at 850 nm || room temperature value
    RIT   (N*):    measured in air || measured at 1350 nm || room temperature value

return to listing

EZ33

    DLL    (R):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    DLL    (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    MTE    (R):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    MTE    (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    CTE    (R):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    CTE    (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    D      (R):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    D      (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    TC     (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    SH     (R):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    SH     (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    TD     (R):    solid || T5 temper, sand cast || 20 °C (68 °F) to 250 °C (482 °F)
    TD     (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)

return to listing

Fe - 30 Mn - 5 Al - 1 C + x Mo (wt %) (New)

    SSC       :    0 wt% Mo || tested at 27 °C (80 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.47 mm/mm strain
    SSC       :    0 wt% Mo || tested at 200 °C (392 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.57 mm/mm strain
    SSC       :    0 wt% Mo || tested at 400 °C (752 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.47 mm/mm strain
    SSC       :    0 wt% Mo || tested at 600 °C (1112 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.35 mm/mm strain
    SSC       :    0 wt% Mo || tested at 700 °C (1292 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.26 mm/mm strain
    SSC       :    0.5 wt% Mo || tested at 27 °C (80 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.43 mm/mm strain
    SSC       :    0.5 wt% Mo || tested at 200 °C (392 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.54 mm/mm strain
    SSC       :    0.5 wt% Mo || tested at 400 °C (752 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.45 mm/mm strain
    SSC       :    0.5 wt% Mo || tested at 600 °C (1112 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.34 mm/mm strain
    SSC       :    0.5 wt% Mo || tested at 700 °C (1292 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.26 mm/mm strain
    SSC       :    2 wt% Mo || tested at 27 °C (80 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.47 mm/mm strain
    SSC       :    2 wt% Mo || tested at 200 °C (392 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.57 mm/mm strain
    SSC       :    2 wt% Mo || tested at 400 °C (752 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.42 mm/mm strain
    SSC       :    2 wt% Mo || tested at 600 °C (1112 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.392 mm/mm strain
    SSC       :    2 wt% Mo || tested at 700 °C (1292 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.312 mm/mm strain
    SSC       :    3 wt% Mo || tested at 27 °C (80 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.457 mm/mm strain
    SSC       :    3 wt% Mo || tested at 200 °C (392 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.6 mm/mm strain
    SSC       :    3 wt% Mo || tested at 400 °C (752 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.43 mm/mm strain
    SSC       :    3 wt% Mo || tested at 600 °C (1112 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.394 mm/mm strain
    SSC       :    3 wt% Mo || tested at 700 °C (1292 °F), 0.003/s, 80% cold-rolled & annealed || 0 to 0.288 mm/mm strain
    UTS       :    0 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    UTS       :    0.5 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    UTS       :    2 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    UTS       :    3 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    YS        :    0 wt% Mo || 80% cold-rolled & annealed, 0.003/s || 20 °C (68 °F) to 700 °C (1292 °F)
    YS        :    0.5 wt% Mo || 80% cold-rolled & annealed, 0.003/s || 20 °C (68 °F) to 700 °C (1292 °F)
    YS        :    2 wt% Mo || 80% cold-rolled & annealed, 0.003/s || 20 °C (68 °F) to 700 °C (1292 °F)
    YS        :    3 wt% Mo || 80% cold-rolled & annealed, 0.003/s || 20 °C (68 °F) to 700 °C (1292 °F)
    %El       :    0 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    %El       :    0.5 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    %El       :    2 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)
    %El       :    3 wt% Mo || 80% cold-rolled & annealed || 20 °C (68 °F) to 700 °C (1292 °F)

return to listing

FERRY alloy

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

Glyptal (New)

SH : solid || -272.1 °C (-457.9 °F) to -173 °C (-280 °F)

return to listing

Graphite ATJ

    CRR    (N):    loaded with the grain || tested at 2300 °C (4172 °F) || 4.67 x 10^-⁷/s to 8.42 x 10^-⁷/s
    CRR    (N):    loaded with the grain || tested at 2400 °C (4352 °F) || 5.7 x 10^-⁷/s to 2.5 x 10^-⁶/s
    CRR    (N):    loaded with the grain || tested at 2500 °C (4532 °F) || 2.64 x 10^-⁷/s to 1.34 x 10^-⁵/s
    CRR    (N):    loaded with the grain || tested at 2600 °C (4712 °F) || 2.12 x 10^-⁷/s to 1.21 x 10^-⁵/s
    CRR    (N):    loaded with the grain || tested at 2700 °C (4892 °F) || 5.5 x 10^-⁷/s to 1.54 x 10^-⁵/s
    CRR    (N):    loaded with the grain || tested at 2800 °C (5072 °F) || 2.4 x 10^-⁷/s to 1.03 x 10^-⁵/s
    CRR    (N):    loaded with the grain || tested at 2900 °C (5252 °F) || 5.5 x 10^-⁷/s to 1.27 x 10^-⁵/s
    CRR    (N):    loaded against the grain || tested at 2300 °C (4172 °F) || 3.9 x 10^-⁷/s to 8.26 x 10^-⁷/s
    CRR    (N):    loaded against the grain || tested at 2400 °C (4352 °F) || 2.8 x 10^-⁷/s to 2.4 x 10^-⁶/s
    CRR    (N):    loaded against the grain || tested at 2500 °C (4532 °F) || 6.8 x 10^-⁷/s to 5.9 x 10^-⁶/s
    CRR    (N):    loaded against the grain || tested at 2600 °C (4712 °F) || 1.28 x 10^-⁶/s to 1.26 x 10^-⁵/s
    CRR    (N):    loaded against the grain || tested at 2700 °C (4892 °F) || 1 x 10^-⁶/s to 1.77 x 10^-⁵/s
    CRR    (N):    loaded against the grain || tested at 2800 °C (5072 °F) || 9 x 10^-⁷/s to 1.05 x 10^-⁵/s
    CRR    (N):    loaded against the grain || tested at 2900 °C (5252 °F) || 1.8 x 10^-⁶/s to 1 x 10^-⁵/s

return to listing

Gray iron (BS416-2) (New)

    E     (*):    solid || room temperature value
    G     (*):    solid || room temperature value
    v     (*):    solid || room temperature value
    K     (*):    solid || room temperature value
    UTS   (*):    solid || room temperature value
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, axial, P_s = 10%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, axial, P_s = 50%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, axial, P_s = 90%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = 0.1, axial, P_s = 10%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = 0.1, axial, P_s = 50%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = 0.1, axial, P_s = 90%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, torsional, P_s = 10%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, torsional, P_s = 50%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, torsional, P_s = 90%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, tension-torsional in-phase, P_s = 50%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    inside surface of spin-cast pipe || tested at 20 °C (68 °F), R = -1, tension-torsional out-of-phase, P_s = 50%, stress amplitude || 1 x 10³ cycles to 1 x 10⁶ cycles

return to listing

Greek Ascoloy

    CRR    (N):    quenched and tempered at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 5.5 x 10^-¹⁰/s to 1.4 x 10^-⁸/s
    CRR    (N):    quenched and tempered at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 1 x 10^-¹⁰/s to 6.2 x 10^-⁹/s
    CRR    (N):    quenched and tempered at 704 °C (1300 °F) || tested at 593 °C (1100 °F) || 9.4 x 10^-¹¹/s to 8 x 10^-¹⁰/s

return to listing

GW92K (New)

    SSC       :    as-extruded || tested at 20 °C (68 °F), 0.001/s || 0 to 0.33 mm/mm strain
    SSC       :    extruded, forged at room temperature || tested at 20 °C (68 °F), 0.001/s || 0 to 0.79 mm/mm strain
    SSC       :    extruded, forged at elevated temperature || tested at 20 °C (68 °F), 0.001/s || 0 to 0.1 mm/mm strain
    UTS   (*):    as-extruded || 0.001/s || room temperature value
    UTS   (*):    extruded, forged at room temperature || 0.001/s || room temperature value
    UTS   (*):    extruded, forged at elevated temperature || 0.001/s || room temperature value
    YS    (*):    as-extruded || 0.001/s || room temperature value
    YS    (*):    extruded, forged at room temperature || 0.001/s || room temperature value
    YS    (*):    extruded, forged at elevated temperature || 0.001/s || room temperature value
    %El   (*):    as-extruded || 0.001/s || room temperature value
    %El   (*):    extruded, forged at room temperature || 0.001/s || room temperature value
    %El   (*):    extruded, forged at elevated temperature || 0.001/s || room temperature value

return to listing

304H

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

316H

    CRR    (N):    annealed at 1010 °C (1850 °F) || tested at 566 °C (1050 °F) || 1.19 x 10^-⁸/s to 8.9 x 10^-⁷/s
    CRR    (N):    annealed at 1010 °C (1850 °F) || tested at 649 °C (1200 °F) || 2.6 x 10^-⁸/s to 2.14 x 10^-⁶/s
    CRR    (N):    annealed at 1010 °C (1850 °F) || tested at 760 °C (1400 °F) || 1.33 x 10^-⁷/s to 2.37 x 10^-⁶/s

return to listing

Haynes 25 (L-605)

    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 649 °C (1200 °F) || 6.12 x 10^-¹⁰/s to 3.14 x 10^-⁷/s
    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 732 °C (1350 °F) || 1 x 10^-⁹/s to 1.8 x 10^-⁶/s
    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 816 °C (1500 °F) || 2.29 x 10^-¹⁰/s to 2.4 x 10^-⁵/s
    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 899 °C (1650 °F) || 2.9 x 10^-⁹/s to 2.4 x 10^-⁵/s
    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 982 °C (1800 °F) || 1.84 x 10^-⁹/s to 3.92 x 10^-⁵/s
    CRR    (N):    annealed at 1232 °C (2250 °F) & quenched || tested at 1093 °C (2000 °F) || 1.5 x 10^-⁹/s to 1.11 x 10^-³/s

return to listing

Haynes 282

    SSC    (N):    GMA deposited || tested at 760 °C (1400 °F), 8.3 x 10^-⁵/s, parallel to build direction || 0 to 0.67 mm/mm strain
    SSC    (N):    GMA deposited || tested at 760 °C (1400 °F), 8.3 x 10^-⁵/s, perpendicular to build direction || 0 to 0.52 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, horizontal, as-processed || 0 to 0.235 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, horizontal, aged || 0 to 0.16 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, horizontal, solution treated & aged || 0 to 0.187 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, vertical, as-processed || 0 to 0.318 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, vertical, aged || 0 to 0.24 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, vertical, solution treated & aged || 0 to 0.251 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, horizontal, as-processed || 0 to 4.6 x 10^-³ mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, horizontal, aged || 0 to 0.24 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, horizontal, solution treated & aged || 0 to 3.05 x 10^-³ mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, vertical, as-processed || 0 to 6.58 x 10^-³ mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, vertical, aged || 0 to 6.58 x 10^-³ mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 800 °C (1472 °F), 2.5 x 10^-⁴/s, vertical, solution treated & aged || 0 to 3.55 x 10^-³ mm/mm strain
    UTS    (N):    single age of 4 h at 800 °C (1472 °F) || 20 °C (68 °F) to 927 °C (1700 °F)
    UTS    (N):    welds || 20 °C (68 °F) to 927 °C (1700 °F)
    YS     (N):    single age of 4 h at 800 °C (1472 °F) || 20 °C (68 °F) to 927 °C (1700 °F)
    YS     (N):    welds || 20 °C (68 °F) to 927 °C (1700 °F)
    %El    (N):    single age of 4 h at 800 °C (1472 °F) || 20 °C (68 °F) to 927 °C (1700 °F)
    %El    (N):    welds || 20 °C (68 °F) to 927 °C (1700 °F)
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 593 °C (1100 °F) || 120 h to 2 x 10⁴ h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 649 °C (1200 °F) || 315 h to 6,825 h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 704 °C (1300 °F) || 410 h to 8,510 h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 760 °C (1400 °F) || 495 h to 2.53 x 10⁴ h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 816 °C (1500 °F) || 425 h to 1.69 x 10⁴ h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 871 °C (1600 °F) || 385 h to 2.03 x 10⁴ h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 927 °C (1700 °F) || 470 h to 1.46 x 10⁴ h
    SR     (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || Master curve (LMP) || 16.5 h to 25.4 h
    SR     (N):    welds || tested at 593 °C (1100 °F) || 450 h to 9,670 h
    SR     (N):    welds || tested at 704 °C (1300 °F) || 350 h to 2,900 h
    SR     (N):    welds || tested at 816 °C (1500 °F) || 550 h to 3,375 h
    SR     (N):    welds || tested at 927 °C (1700 °F) || 1,050 h to 5,900 h
    SR     (N):    welds || Master curve (LMP) || 17 h to 24.9 h
    CRS    (N):    0.5% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 40 h to 125 h
    CRS    (N):    1% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 65 h to 190 h
    CRS    (N):    1.5% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 80 h to 240 h
    CRS    (N):    2% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 100 h to 285 h
    CRS    (N):    3% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 125 h to 350 h
    CRS    (N):    4% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 150 h to 400 h
    CRS    (N):    5% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 165 h to 440 h
    CRS    (N):    7.5% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 195 h to 510 h
    CRS    (N):    10% plastic strain, GMA deposited, parallel || tested at 760 °C (1400 °F) || 215 h to 550 h
    CRS    (N):    0.5% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 25 h to 175 h
    CRS    (N):    1% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 65 h to 120 h
    CRS    (N):    1.5% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 80 h to 140 h
    CRS    (N):    2% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 95 h to 160 h
    CRS    (N):    3% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 115 h to 190 h
    CRS    (N):    4% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 130 h to 210 h
    CRS    (N):    5% plastic strain, GMA deposited, perpendicular || tested at 760 °C (1400 °F) || 140 h to 225 h
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 50 h || 0 to 6.4 x 10^-³ mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 60 h || 0 to 8.7 x 10^-³ mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 70 h || 0 to 0.11 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 80 h || 0 to 0.14 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 90 h || 0 to 0.17 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 100 h || 0 to 0.2 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 110 h || 0 to 0.23 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 120 h || 0 to 0.27 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 130 h || 0 to 0.31 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 140 h || 0 to 0.36 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 150 h || 0 to 0.41 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 160 h || 0 to 0.46 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 170 h || 0 to 0.52 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 180 h || 0 to 0.59 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 190 h || 0 to 0.67 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 200 h || 0 to 0.79 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 210 h || 0 to 0.91 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 220 h || 0 to 0.15 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 230 h || 0 to 0.14 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 240 h || 0 to 0.47 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 250 h || 0 to 0.53 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 260 h || 0 to 0.59 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 270 h || 0 to 0.66 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 280 h || 0 to 0.74 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 290 h || 0 to 0.82 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 300 h || 0 to 0.91 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 310 h || 0 to 0.1 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 320 h || 0 to 0.11 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 330 h || 0 to 0.12 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 340 h || 0 to 0.133 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, parallel || 350 h || 0 to 0.145 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 50 h || 0 to 7.5 x 10^-³ mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 60 h || 0 to 9.2 x 10^-³ mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 70 h || 0 to 0.11 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 80 h || 0 to 0.14 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 90 h || 0 to 0.18 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 100 h || 0 to 0.21 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 110 h || 0 to 0.26 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 120 h || 0 to 0.32 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 130 h || 0 to 0.39 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 140 h || 0 to 0.47 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 150 h || 0 to 0.59 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 160 h || 0 to 0.2 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 170 h || 0 to 0.23 mm/mm strain
    IC     (N):    tested at 760 °C (1400 °F), plastic strain, GMA deposited, perpendicular || 180 h || 0 to 0.27 mm/mm strain
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 593 °C (1100 °F) || 3.32 x 10^-¹¹/s to 2.65 x 10^-⁹/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 649 °C (1200 °F) || 9.7 x 10^-¹¹/s to 9.28 x 10^-¹⁰/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 704 °C (1300 °F) || 2.14 x 10^-¹⁰/s to 6.67 x 10^-⁹/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 760 °C (1400 °F) || 2.16 x 10^-¹⁰/s to 6.92 x 10^-⁹/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 816 °C (1500 °F) || 2.76 x 10^-¹⁰/s to 3.35 x 10^-⁹/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 871 °C (1600 °F) || 3.49 x 10^-¹⁰/s to 3.47 x 10^-⁹/s
    CRR    (N):    single age heat treatment of 4 h at 800 °C (1472 °F) || tested at 927 °C (1700 °F) || 2.59 x 10^-¹⁰/s to 6.18 x 10^-⁹/s

return to listing

HK31

    CRR    (N):    H24 temper, sheet || tested at 204 °C (400 °F) || 2.45 x 10^-¹⁰/s to 5.84 x 10^-⁷/s
    CRR    (N):    H24 temper, sheet || tested at 260 °C (500 °F) || 7.8 x 10^-¹⁰/s to 1.95 x 10^-⁶/s
    CRR    (N):    H24 temper, sheet || tested at 316 °C (600 °F) || 4.63 x 10^-¹¹/s to 2.95 x 10^-⁵/s

return to listing

HM21

    CRR    (N):    T8 temper, sheet || tested at 204 °C (400 °F) || 1.2 x 10^-¹⁰/s to 4.82 x 10^-⁹/s
    CRR    (N):    T8 temper, sheet || tested at 260 °C (500 °F) || 1.8 x 10^-¹⁰/s to 8.3 x 10^-⁷/s
    CRR    (N):    T8 temper, sheet || tested at 316 °C (600 °F) || 3.12 x 10^-¹⁰/s to 1.83 x 10^-⁸/s

return to listing

HR CP980 SF (New)

    SSC       :    sheet || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, transverse || 0 to 0.53 mm/mm strain
    UTS   (*):    sheet || transverse || room temperature value
    YS    (*):    sheet || transverse || room temperature value
    %El   (*):    sheet || transverse || room temperature value
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = -1, axial, trimmed, transverse to the rolling direction, stress amplitude || 4.7 x 10⁴ cycles to 3.3 x 10⁵ cycles
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, axial, trimmed, transverse to the rolling direction, stress amplitude || 7 x 10⁴ cycles to 6.1 x 10⁵ cycles
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, K_t = 2.24, axial, punched, transverse to the rolling direction, stress amplitude || 1 x 10⁵ cycles to 5 x 10⁵ cycles

return to listing

HR CP800 SF (New)

    SSC       :    sheet || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, transverse || 0 to 0.76 mm/mm strain
    UTS   (*):    sheet || transverse || room temperature value
    YS    (*):    sheet || transverse || room temperature value
    %El   (*):    sheet || transverse || room temperature value
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = -1, axial, trimmed, transverse to the rolling direction, stress amplitude || 3.4 x 10⁴ cycles to 6.4 x 10⁵ cycles
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, axial, trimmed, transverse to the rolling direction, stress amplitude || 7 x 10⁴ cycles to 7 x 10⁵ cycles
    FSN       :    effect of shear cutting || tested at 20 °C (68 °F), R = 0.1, K_t = 2.24, axial, punched, transverse to the rolling direction, stress amplitude || 7 x 10⁴ cycles to 1 x 10⁶ cycles

return to listing

HR3C

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

INCO weld A

CRR (N): deposited by the SMAW process || tested at 649 °C (1200 °F) || 3 x 10^-⁸/s to 2.2 x 10^-⁷/s

return to listing

Incoloy 904 (904L)

    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -196.1 °C (-321.1 °F), 6.7 x 10^-⁴/s || 0 to 0.58 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -80 °C (-112 °F), 6.7 x 10^-⁴/s || 0 to 0.5 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -40 °C (-40 °F), 6.7 x 10^-⁴/s || 0 to 0.47 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at 25 °C (77 °F), 6.7 x 10^-⁴/s || 0 to 0.44 mm/mm strain
    UTS    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    YS     (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    %El    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)

return to listing

Incoloy 800

    CRR    (N):    annealed at 1150 °C (2102 °F) || tested at 760 °C (1400 °F) || 7.5 x 10^-⁸/s to 2.25 x 10^-⁶/s
    CRR    (N):    annealed at 1150 °C (2102 °F) || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm² || 7.75 x 10^-⁸/s to 1.7 x 10^-⁶/s
    CRR    (N):    aged at 800 °C (1472 °F) || tested at 760 °C (1400 °F) || 4.72 x 10^-⁸/s to 1.67 x 10^-⁶/s
    CRR    (N):    aged at 800 °C (1472 °F) || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm² || 1.05 x 10^-⁷/s to 1.34 x 10^-⁶/s

return to listing

Incoloy A-286

    SR     (N):    heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 8.5 h to 255 h
    SR     (N):    heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 7 h to 255 h
    CRS    (N):    0.1% plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 0.16 h to 25 h
    CRS    (N):    0.3% plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 0.57 h to 50 h
    CRS    (N):    0.5% plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 1 h to 110 h
    CRS    (N):    1% plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 1.7 h to 160 h
    CRS    (N):    0.1% plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 0.15 h to 12.5 h
    CRS    (N):    0.3% plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 0.65 h to 41 h
    CRS    (N):    0.5% plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 1 h to 65 h
    CRS    (N):    1% plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 1.6 h to 100 h
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 2 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 5 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 50 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 2 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 5 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || 50 h || 0 to 0.01 mm/mm strain
    CRR    (N):    heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 5.9 x 10^-⁹/s to 1.05 x 10^-⁶/s
    CRR    (N):    heat treated at 899 °C (1650 °F), aged at 732 °C (1350 °F) || tested at 704 °C (1300 °F) || 1.26 x 10^-⁸/s to 1.39 x 10^-⁶/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 1.49 x 10^-⁸/s to 1.35 x 10^-⁶/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 704 °C (1300 °F) || 8.3 x 10^-⁸/s to 1.9 x 10^-⁷/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 1.5 x 10^-⁷/s to 4.4 x 10^-⁷/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), sheet || tested at 538 °C (1000 °F) || 1.38 x 10^-⁹/s to 5.56 x 10^-⁹/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), sheet || tested at 649 °C (1200 °F) || 8.3 x 10^-¹⁰/s to 6.78 x 10^-⁷/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), sheet || tested at 732 °C (1350 °F) || 1.11 x 10^-⁹/s to 4.37 x 10^-⁶/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), sheet || tested at 816 °C (1500 °F) || 3.6 x 10^-⁹/s to 1.76 x 10^-⁵/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), bar || tested at 538 °C (1000 °F) || 4.7 x 10^-⁹/s to 6.62 x 10^-⁶/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), bar || tested at 649 °C (1200 °F) || 5 x 10^-⁹/s to 1.03 x 10^-⁷/s
    CRR    (N):    heat treated at 982 °C (1800 °F), aged at 718 °C (1325 °F), bar || tested at 732 °C (1350 °F) || 8 x 10^-⁹/s to 9.73 x 10^-⁷/s

return to listing

Incoloy 800H & 800HT

CRR (N): ASTM B409-73 || tested at 649 °C (1200 °F) || 3.3 x 10^-¹¹/s to 3.2 x 10^-⁷/s

return to listing

Inconel 600

    CRR    (N):    ASTM grain size of 9 || tested at 649 °C (1200 °F) || 6.79 x 10^-⁸/s to 4.84 x 10^-⁶/s
    CRR    (N):    ASTM grain size of 9 || tested at 816 °C (1500 °F) || 2.79 x 10^-⁷/s to 2.63 x 10^-⁵/s
    CRR    (N):    ASTM grain size of 2 || tested at 649 °C (1200 °F) || 6.79 x 10^-⁸/s to 4.83 x 10^-⁶/s
    CRR    (N):    ASTM grain size of 2 || tested at 816 °C (1500 °F) || 2.79 x 10^-⁷/s to 2.63 x 10^-⁵/s

return to listing

Inconel 718

    DLL    (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    MTE    (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    CTE    (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    D      (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    TC     (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    SH     (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    TD     (N):    liquid || 1336 °C (2437 °F) to 1600 °C (2912 °F)
    Vis    (R):    liquid || 1336 °C (2437 °F) to 1500 °C (2732 °F)
    E     (N*):    laser powder bed fusion || AMS 5663 || room temperature value
    UTS   (N*):    laser powder bed fusion || AMS 5663 || room temperature value
    YS    (N*):    laser powder bed fusion || AMS 5663 || room temperature value
    %El   (N*):    laser powder bed fusion || AMS 5663 || room temperature value
    FSN    (N):    solution treated & aged, grain size ASTM 8.5 || tested at 20 °C (68 °F), R = -1, torsion, maximum stress || 2.7 x 10⁵ cycles to 1 x 10⁸ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, as-built, at 10% failure, stress amplitude || 5.8 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, as-built, at 50% failure, stress amplitude || 5.8 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, as-built, at 90% failure, stress amplitude || 5.8 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, machined, at 10% failure, stress amplitude || 1.1 x 10⁵ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, machined, at 50% failure, stress amplitude || 1.1 x 10⁵ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0, axial, AMS 5663, machined, at 90% failure, stress amplitude || 1.1 x 10⁵ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.1, axial, 1179 °C (2155 °F) anneal & aged, maximum stress || 4.7 x 10⁴ cycles to 4.4 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.1, axial, 1179 °C (2155 °F) anneal, aged, & ground, maximum stress || 4.8 x 10⁴ cycles to 8 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.1, axial, 1179 °C (2155 °F) anneal, ground, & aged, maximum stress || 4.65 x 10⁴ cycles to 4 x 10⁶ cycles
    S      (N):    solid || age hardened || -266.1 °C (-447.1 °F) to 27 °C (80 °F)

return to listing

Inconel HX / Hastelloy X / Nimonic PE13

    SSC    (N):    laser powder bed fusion || tested at 260 °C (500 °F), 8.3 x 10^-³/s, HIPed, Cheng et al. || 0 to 0.375 mm/mm strain
    FEN    (N):    laser powder bed fusion || tested at 260 °C (500 °F), R = -1, axial, total strain range || 635 cycles to 2.04 x 10⁴ cycles
    CRR    (N):    AMS 5536G || tested at 649 °C (1200 °F) || 3.6 x 10^-¹¹/s to 3.5 x 10^-⁷/s
    S      (N):    solid || annealed || -266.1 °C (-447.1 °F) to 27 °C (80 °F)

return to listing

Inconel MA 754

    CRR    (N):    as-received, Ebert et al. || tested at 871 °C (1600 °F) || 1.59 x 10^-⁹/s to 4.39 x 10^-⁷/s
    CRR    (N):    as-received, Ebert et al. || tested at 982 °C (1800 °F) || 5.9 x 10^-⁹/s to 1.05 x 10^-⁶/s
    CRR    (N):    cold-rolled 22%, annealed, Ebert et al. || tested at 982 °C (1800 °F) || 1.8 x 10^-⁸/s to 3.4 x 10^-⁶/s
    CRR    (N):    as-received, Nardone et al. || tested at 760 °C (1400 °F) || 1.16 x 10^-⁸/s to 1.8 x 10^-⁶/s
    CRR    (N):    HIPed, Nardone et al. || tested at 760 °C (1400 °F) || 1.05 x 10^-⁸/s to 8.62 x 10^-⁷/s
    CRR    (N):    effect of dispersoid size || tested at 1000 °C (1832 °F), 14.4 nm || 2.2 x 10^-⁹/s to 9.35 x 10^-⁶/s
    CRR    (N):    effect of dispersoid size || tested at 1000 °C (1832 °F), 13.2 nm || 2.9 x 10^-⁹/s to 2.83 x 10^-⁵/s
    CRR    (N):    heat treated || tested at 1093 °C (2000 °F), parallel to extrusion direction || 4.3 x 10^-⁹/s to 2.51 x 10^-⁸/s
    CRR    (N):    heat treated || tested at 1093 °C (2000 °F), long transverse direction || 1 x 10^-⁹/s to 3.81 x 10^-⁸/s

return to listing

InP

    E      (N):    solid || zinc blende, calculated value || -273.1 °C (-459.7 °F) to 627 °C (1160 °F)
    G      (N):    solid || zinc blende, calculated value || -273.1 °C (-459.7 °F) to 627 °C (1160 °F)
    v      (N):    solid || zinc blende, calculated value || -273.1 °C (-459.7 °F) to 627 °C (1160 °F)
    K      (N):    solid || zinc blende, calculated value || -273.1 °C (-459.7 °F) to 627 °C (1160 °F)

return to listing

Iupital ET-35

    DLL    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL    (N):    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE    (N):    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE    (N):    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE    (N):    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE    (N):    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D      (N):    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (N*):    solid || room temperature value
    SIGMA (N*):    solid || room temperature value
    SRHO (N*):    solid || room temperature value
    FS    (N*):    ISO 178 || room temperature value
    E     (N*):    ISO 527 || room temperature value
    FM    (N*):    ISO 178 || room temperature value
    YS    (N*):    ISO 527 || room temperature value

return to listing

Iupital ET-20 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    UTS   (*):    ISO 527 || at break || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital F30-05

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F40-03

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F10-01

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F10-02

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F20-03

YS (R): ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F20-05

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F20-54

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F20-61

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F30-03

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -40 °C (-40 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F10-EW

    FS     (R):    ISO 178 || -40 °C (-40 °F) to 100 °C (212 °F)
    FM     (R):    ISO 178 || -30 °C (-22 °F) to 80 °C (176 °F)
    YS     (R):    ISO 527 || -40 °C (-40 °F) to 100 °C (212 °F)

return to listing

Iupital F20-73R2

    %El   (N*):    ISO 527 || at yield || room temperature value
    %El   (N*):    ISO 527 || at break || room temperature value
    DCRPT (N):    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF     (N):    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

Iupital F20-73R1

    %El   (N*):    ISO 527 || at yield || room temperature value
    %El   (N*):    ISO 527 || at break || room temperature value
    DCRPT (N):    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF     (N):    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

Iupital F30-73R1 (New)

    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital F20-55R2 (New)

    FS    (*):    ISO 178 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FG2025 MZ (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    UTS   (*):    ISO 527 || at break || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FG2030 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    UTS   (*):    ISO 527 || at break || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FU2005 (New)

    D     (*):    ISO 1183 || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FU2015 (New)

    D     (*):    ISO 1183 || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FU2020 (New)

    D     (*):    ISO 1183 || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FU2010R2 (New)

    FS    (*):    ISO 178 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FU2020R2 (New)

    FS    (*):    ISO 178 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FX-11JR1 (New)

    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital FX-11R1 (New)

    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital MAH25 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital MAL40 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital MAL20 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital MAS30 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

Iupital MAS20 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

Iupital ST1700 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital ST1800 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital ST2000 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital ST1600 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital ST1700R2 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital ST1800R2 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 90 °C (194 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 90 °C (194 °F)
    D         :    solid || 20 °C (68 °F) to 90 °C (194 °F)
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    YS    (*):    ISO 527 || room temperature value
    %El   (*):    ISO 527 || at yield || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

Iupital TC3030 (New)

    D     (*):    ISO 1183 || room temperature value
    FS    (*):    ISO 178 || room temperature value
    E     (*):    ISO 527 || room temperature value
    FM    (*):    ISO 178 || room temperature value
    UTS   (*):    ISO 527 || at break || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value

return to listing

JIS FC170

    DLL    (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    DLL    (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)
    MTE    (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    MTE    (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)
    CTE    (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    CTE    (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)
    D      (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    D      (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)
    SH     (R):    solid || 20 °C (68 °F) to 700 °C (1292 °F)
    SH     (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)
    Vis    (N):    liquid || 1190 °C (2174 °F) to 1500 °C (2732 °F)

return to listing

Kanthal Cuprothal 49

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

KBaBi (New)

    DLL       :    solid || polycrystal || -173 °C (-280 °F) to 27 °C (80 °F)
    DLL       :    solid || a-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    DLL       :    solid || c-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    MTE       :    solid || polycrystal || -173 °C (-280 °F) to 27 °C (80 °F)
    MTE       :    solid || a-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    MTE       :    solid || c-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    CTE       :    solid || polycrystal || -173 °C (-280 °F) to 27 °C (80 °F)
    CTE       :    solid || a-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    CTE       :    solid || c-axis || -173 °C (-280 °F) to 27 °C (80 °F)
    D         :    solid || -173 °C (-280 °F) to 27 °C (80 °F)
    RHO       :    solid || 20 °C (68 °F) to 205 °C (401 °F)
    SIGMA    :    solid || 20 °C (68 °F) to 205 °C (401 °F)
    S         :    solid || 20 °C (68 °F) to 215 °C (419 °F)

return to listing

35 KCl - 35 NaCl - 30 NbCl₅ (mol %) (New)

RHO : liquid || 627 °C (1160 °F) to 697 °C (1286 °F)
SIGMA : liquid || 627 °C (1160 °F) to 697 °C (1286 °F)

return to listing

5 KCl - 5 NaCl - 90 NbCl₅ (mol %) (New)

RHO : liquid || 237 °C (458 °F) to 377 °C (710 °F)
SIGMA : liquid || 237 °C (458 °F) to 377 °C (710 °F)

return to listing

10 KCl - 10 NaCl - 80 NbCl₅ (mol %) (New)

RHO : liquid || 297 °C (566 °F) to 377 °C (710 °F)
SIGMA : liquid || 297 °C (566 °F) to 377 °C (710 °F)

return to listing

15 KCl - 15 NaCl - 70 NbCl₅ (mol %) (New)

RHO : liquid || 372 °C (701 °F) to 417 °C (782 °F)
SIGMA : liquid || 372 °C (701 °F) to 417 °C (782 °F)

return to listing

20 KCl - 20 NaCl - 60 NbCl₅ (mol %) (New)

RHO : liquid || 327 °C (620 °F) to 417 °C (782 °F)
SIGMA : liquid || 327 °C (620 °F) to 417 °C (782 °F)

return to listing

30 KCl - 30 NaCl - 40 NbCl₅ (mol %) (New)

RHO : liquid || 427 °C (800 °F) to 597 °C (1106 °F)
SIGMA : liquid || 427 °C (800 °F) to 597 °C (1106 °F)

return to listing

75 KCl - 25 RbCl (mol %)

    E      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    G      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    v      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    K      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)

return to listing

25 KCl - 75 RbCl (mol %)

    E      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    G      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    v      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    K      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)

return to listing

50 KCl - 50 RbCl (mol %)

    E      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    G      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    v      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)
    K      (N):    solid || 20 °C (68 °F) to 227 °C (440 °F)

return to listing

KCl

    E      (R):    solid || -269.1 °C (-452.5 °F) to 700 °C (1292 °F)
    G      (R):    solid || -269.1 °C (-452.5 °F) to 700 °C (1292 °F)
    v      (R):    solid || -269.1 °C (-452.5 °F) to 700 °C (1292 °F)
    K      (R):    solid || -269.1 °C (-452.5 °F) to 700 °C (1292 °F)

return to listing

Kevlar 29 (New)

    D     (*):    solid || yarn || room temperature value
    TC    (*):    solid || yarn || room temperature value
    SH        :    solid || yarn || 20 °C (68 °F) to 180 °C (356 °F)
    TD    (*):    solid || yarn || room temperature value
    E     (*):    conditioned yarns || room temperature value
    E     (*):    resin impregnated strands || room temperature value
    UTS   (*):    conditioned yarns || at break || room temperature value
    UTS   (*):    resin impregnated strands || at break || room temperature value
    %El   (*):    conditioned yarns || at break || room temperature value

return to listing

Kovar (alloy F15)

    CRR    (N):    annealed || tested at 650 °C (1202 °F) || 5 x 10^-⁸/s to 1.15 x 10^-⁶/s
    CRR    (N):    annealed || tested at 750 °C (1382 °F) || 3.19 x 10^-⁷/s to 1.98 x 10^-⁵/s
    CRR    (N):    annealed || tested at 800 °C (1472 °F) || 4.72 x 10^-⁷/s to 1.43 x 10^-⁵/s
    CRR    (N):    annealed || tested at 850 °C (1562 °F) || 3.7 x 10^-⁷/s to 2.65 x 10^-⁵/s
    CRR    (N):    annealed || tested at 900 °C (1652 °F) || 2.2 x 10^-⁶/s to 1.9 x 10^-⁵/s

return to listing

304L

    SSC    (N):    hot-rolled plate || tested at 20 °C (68 °F), 4.17 x 10^-⁴/s, rolling direction || 0 to 1.14 mm/mm strain
    SSC    (N):    hot-rolled plate || tested at 20 °C (68 °F), 4.17 x 10^-⁴/s, transverse direction || 0 to 1.14 mm/mm strain
    SSC    (N):    hot-rolled plate || tested at 300 °C (572 °F), 4.17 x 10^-⁴/s, rolling direction || 0 to 0.88 mm/mm strain
    SSC    (N):    hot-rolled plate || tested at 300 °C (572 °F), 4.17 x 10^-⁴/s, transverse direction || 0 to 0.86 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -196.1 °C (-321.1 °F), 6.7 x 10^-⁴/s || 0 to 0.433 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -80 °C (-112 °F), 6.7 x 10^-⁴/s || 0 to 0.5 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -40 °C (-40 °F), 6.7 x 10^-⁴/s || 0 to 0.54 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at 25 °C (77 °F), 6.7 x 10^-⁴/s || 0 to 0.71 mm/mm strain
    NE     (N):    solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)
    UTS    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    YS     (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    %El    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    FEN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = -1, axial, 1 Hz, total strain amplitude || 3.8 x 10³ cycles to 6.9 x 10⁴ cycles
    FEN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = -1, axial, 1 Hz, with a 1 time hold, total strain amplitude || 2.8 x 10³ cycles to 4.15 x 10⁴ cycles
    FEN    (N):    hot-rolled plate || tested at 300 °C (572 °F), R = -1, axial, 1 Hz, total strain amplitude || 780 cycles to 3.9 x 10³ cycles
    FEN    (N):    hot-rolled plate || tested at 300 °C (572 °F), R = -1, axial, 1 Hz, with a 1 time hold, total strain amplitude || 860 cycles to 4.9 x 10³ cycles
    FEN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = -1, axial, 10 Hz, total strain amplitude || 4.3 x 10³ cycles to 1 x 10⁷ cycles
    FEN    (N):    hot-rolled plate || tested at 300 °C (572 °F), R = -1, axial, 10 Hz, total strain amplitude || 370 cycles to 1 x 10⁷ cycles
    CRR    (N):    ASTM grain size of 6 || tested at 649 °C (1200 °F) || 7.6 x 10^-⁹/s to 1.57 x 10^-⁵/s
    CRR    (N):    ASTM grain size of 6 || tested at 816 °C (1500 °F) || 2.1 x 10^-⁷/s to 3.39 x 10^-⁵/s
    CRR    (N):    ASTM grain size of 1 || tested at 649 °C (1200 °F) || 5.9 x 10^-⁹/s to 4.3 x 10^-⁶/s
    CRR    (N):    ASTM grain size of 1 || tested at 816 °C (1500 °F) || 4.1 x 10^-⁸/s to 4.51 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 760 °C (1400 °F) || 6.67 x 10^-⁷/s to 6.95 x 10^-⁷/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm² || 6.67 x 10^-⁷/s to 7.78 x 10^-⁷/s
    CRR    (N):    aged at 800 °C (1472 °F) || tested at 760 °C (1400 °F) || 5 x 10^-⁷/s to 8.89 x 10^-⁷/s
    CRR    (N):    aged at 800 °C (1472 °F) || tested at 760 °C (1400 °F), irradiated 3.5 x 10²⁰ neutrons/cm² || 3.8 x 10^-⁷/s to 9.45 x 10^-⁷/s

return to listing

316L

    SSC    (N):    directed energy deposition || tested at -196 °C (-320.8 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.58 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 21 °C (70 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.58 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 204 °C (400 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.33 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 427 °C (800 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.34 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 649 °C (1200 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.33 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 871 °C (1600 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.97 mm/mm strain
    SSC    (N):    directed energy deposition || tested at 982 °C (1800 °F), 8.3 x 10^-⁴/s, Lee et al. || 0 to 0.73 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, zx-orientation, 3.5 x 10^-⁴/s, Braun et al. || 0 to 0.24 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, yz-orientation, 3.5 x 10^-⁴/s, Braun et al. || 0 to 0.176 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, xy-orientation, 3.5 x 10^-⁴/s, Braun et al. || 0 to 0.161 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), 0.001/s, stress-relieved 6 h at 550 °C (1022 °F), Behvar et al. || 0 to 0.21 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -196.1 °C (-321.1 °F), 6.7 x 10^-⁴/s || 0 to 0.46 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -80 °C (-112 °F), 6.7 x 10^-⁴/s || 0 to 0.51 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at -40 °C (-40 °F), 6.7 x 10^-⁴/s || 0 to 0.55 mm/mm strain
    SSC    (N):    5 mm (0.197 inch) plate, annealed || tested at 25 °C (77 °F), 6.7 x 10^-⁴/s || 0 to 0.65 mm/mm strain
    UTS    (N):    laser powder directed energy deposition || 8.3 x 10^-⁴/s strain rate || -196.1 °C (-321.1 °F) to 982 °C (1799 °F)
    UTS    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    YS     (N):    laser powder directed energy deposition || 8.3 x 10^-⁴/s strain rate || -196.1 °C (-321.1 °F) to 982 °C (1799 °F)
    YS     (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    %El    (N):    laser powder directed energy deposition || 8.3 x 10^-⁴/s strain rate || -196.1 °C (-321.1 °F) to 982 °C (1799 °F)
    %El    (N):    5 mm (0.197 inch) plate, annealed || 6.7 x 10^-⁴/s || -196.1 °C (-321.1 °F) to 25 °C (77 °F)
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.0, axial, as-built, PS = 50%, stress amplitude, Braun et al. || 4.8 x 10⁴ cycles to 2.1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.5, axial, as-built, PS = 50%, stress amplitude, Braun et al. || 2.3 x 10⁵ cycles to 1.54 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, as-built, PS = 50%, stress amplitude, Braun et al. || 6 x 10⁴ cycles to 2.04 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.0, axial, heat treated, PS = 50%, stress amplitude, Braun et al. || 9.1 x 10⁴ cycles to 1.65 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.5, axial, heat treated, PS = 50%, stress amplitude, Braun et al. || 2.1 x 10⁴ cycles to 1.9 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, heat treated, PS = 50%, stress amplitude, Braun et al. || 1 x 10⁵ cycles to 1.45 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = 0.0, axial, turned & heat treated, PS = 50%, stress amplitude, Braun et al. || 1.34 x 10⁵ cycles to 1.2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, 4-pt bending, stress-relieved 6 h at 550 °C (1022 °F), stress amplitude, Behvar et al. || 5.3 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, 4-pt bending, stress-relieved 6 h at 550 °C (1022 °F), corroded 10 days in 30% HCl solution, stress amplitude, Behvar et al. || 2.35 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    directed energy deposition || tested at 21 °C (70 °F), R = -1, axial, stress amplitude || 1.18 x 10³ cycles to 1.45 x 10⁵ cycles
    FSN    (N):    directed energy deposition || tested at 204 °C (400 °F), R = -1, axial, stress amplitude || 1.82 x 10³ cycles to 1.32 x 10⁴ cycles
    FSN    (N):    directed energy deposition || tested at 427 °C (800 °F), R = -1, axial, stress amplitude || 1.34 x 10³ cycles to 7.74 x 10³ cycles
    FSN    (N):    directed energy deposition || tested at 649 °C (1200 °F), R = -1, axial, stress amplitude || 460 cycles to 1.88 x 10³ cycles
    FSN    (N):    directed energy deposition || tested at 760 °C (1400 °F), R = -1, axial, stress amplitude || 320 cycles to 1.35 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 21 °C (70 °F), R = -1, axial, total strain amplitude || 1.18 x 10³ cycles to 1.45 x 10⁵ cycles
    FEN    (N):    directed energy deposition || tested at 21 °C (70 °F), R = -1, axial, plastic strain amplitude || 1.18 x 10³ cycles to 1.45 x 10⁵ cycles
    FEN    (N):    directed energy deposition || tested at 21 °C (70 °F), R = -1, axial, elastic strain amplitude || 1.18 x 10³ cycles to 1.45 x 10⁵ cycles
    FEN    (N):    directed energy deposition || tested at 204 °C (400 °F), R = -1, axial, total strain amplitude || 1.82 x 10³ cycles to 1.32 x 10⁴ cycles
    FEN    (N):    directed energy deposition || tested at 204 °C (400 °F), R = -1, axial, plastic strain amplitude || 1.82 x 10³ cycles to 1.32 x 10⁴ cycles
    FEN    (N):    directed energy deposition || tested at 204 °C (400 °F), R = -1, axial, elastic strain amplitude || 1.82 x 10³ cycles to 1.32 x 10⁴ cycles
    FEN    (N):    directed energy deposition || tested at 427 °C (800 °F), R = -1, axial, total strain amplitude || 1.34 x 10³ cycles to 7.74 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 427 °C (800 °F), R = -1, axial, plastic strain amplitude || 1.34 x 10³ cycles to 7.74 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 427 °C (800 °F), R = -1, axial, elastic strain amplitude || 1.34 x 10³ cycles to 7.74 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 649 °C (1200 °F), R = -1, axial, total strain amplitude || 460 cycles to 1.88 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 649 °C (1200 °F), R = -1, axial, plastic strain amplitude || 460 cycles to 1.88 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 649 °C (1200 °F), R = -1, axial, elastic strain amplitude || 460 cycles to 1.88 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 760 °C (1400 °F), R = -1, axial, total strain amplitude || 320 cycles to 1.35 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 760 °C (1400 °F), R = -1, axial, plastic strain amplitude || 320 cycles to 1.35 x 10³ cycles
    FEN    (N):    directed energy deposition || tested at 760 °C (1400 °F), R = -1, axial, elastic strain amplitude || 320 cycles to 1.35 x 10³ cycles

return to listing

Li₇Sn₃

SH (R): solid || -268.1 °C (-450.7 °F) to 377 °C (710 °F)
HC (R): solid || -268.1 °C (-450.7 °F) to 377 °C (710 °F)

return to listing

Li₁₇Sn₄

SH (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)
HC (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)

return to listing

Li₇Sn₂

SH (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)
HC (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)

return to listing

Li₁₃Sn₅

SH (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)
HC (R): solid || -268.1 °C (-450.7 °F) to 592 °C (1097 °F)

return to listing

Lithium

S (N): solid || 20 °C (68 °F) to 175 °C (347 °F)
S (N): liquid || 180 °C (356 °F) to 307 °C (584 °F)

return to listing

304LN

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

301LN

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

LZ91 (New)

    D     (*):    solid || room temperature value
    SSC       :    rolled sheet, 70% reduction || tested at 20 °C (68 °F), 0.001/s, rolled at 20 °C (68 °F) || 0 to 0.14 mm/mm strain
    SSC       :    rolled sheet, 70% reduction || tested at 20 °C (68 °F), 0.001/s, rolled at 200 °C (392 °F) || 0 to 0.16 mm/mm strain
    SSC       :    rolled sheet, 70% reduction || tested at 20 °C (68 °F), 0.001/s, rolled at 300 °C (572 °F) || 0 to 0.134 mm/mm strain
    SSC       :    rolled sheet, 70% reduction || tested at 20 °C (68 °F), 0.001/s, cryogenic rolled at -196 °C (-320.8 °F) (LN₂) || 0 to 0.113 mm/mm strain
    SSC       :    100 micron thick foil || tested at 30 °C (86 °F), as-rolled, 2.75 x 10^-³/s || 0 to 0.16 mm/mm strain
    SSC       :    100 micron thick foil || tested at 30 °C (86 °F), annealed at 250 °C (482 °F), 2.75 x 10^-³/s || 0 to 0.78 mm/mm strain

return to listing

422M

    SR     (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 10 h to 2,330 h
    SR     (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || tested at 566 °C (1050 °F) || 15 h to 1,655 h
    SR     (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 15 h to 2,735 h
    SR     (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || Master curve (LMP) || 22.8 h to 26.4 h
    CRR    (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || tested at 538 °C (1000 °F) || 9.7 x 10^-¹⁰/s to 3.62 x 10^-⁹/s
    CRR    (N):    1093 °C (2000 °F), tempered 2 h at 649 °C (1200 °F) || tested at 593 °C (1100 °F) || 1 x 10^-⁹/s to 1.44 x 10^-⁸/s

return to listing

M50

    E      (R):    solid || VIM/VAR grade || 20 °C (68 °F) to 480 °C (896 °F)
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 22 °C (72 °F), R = -1, ultrasonic axial, VIM/VAR grade, maximum stress || 4.17 x 10⁸ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 200 °C (392 °F), R = -1, ultrasonic axial, VIM/VAR grade, maximum stress || 2.75 x 10⁶ cycles to unknown strain rate cycles
    FSN    (N):    quenched from 860 °C (1580 °F) & tempered at 160 °C (320 °F) || tested at 300 °C (572 °F), R = -1, ultrasonic axial, VIM/VAR grade, maximum stress || 2.75 x 10⁶ cycles to unknown strain rate cycles

return to listing

Magnesium

    SSC    (N):    effect of grain size & temperature, extrusions || tested at 25 °C (77 °F), 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || 0 to 0.82 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at 25 °C (77 °F), 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || 0 to 0.45 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at 25 °C (77 °F), 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || 0 to 0.96 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at 25 °C (77 °F), 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || 0 to 0.165 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at 25 °C (77 °F), 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || 0 to 0.233 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -195.1 °C (-319.3 °F), 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || 0 to 0.45 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -195.1 °C (-319.3 °F), 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || 0 to 0.37 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -195.1 °C (-319.3 °F), 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || 0 to 0.28 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -195.1 °C (-319.3 °F), 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || 0 to 0.23 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -195.1 °C (-319.3 °F), 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || 0 to 0.29 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -269.1 °C (-452.5 °F), 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || 0 to 0.88 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -269.1 °C (-452.5 °F), 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || 0 to 0.68 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -269.1 °C (-452.5 °F), 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || 0 to 0.71 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -269.1 °C (-452.5 °F), 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || 0 to 0.43 mm/mm strain
    SSC    (N):    effect of grain size & temperature, extrusions || tested at -269.1 °C (-452.5 °F), 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || 0 to 0.4 mm/mm strain
    UTS    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    UTS    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    UTS    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    UTS    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    UTS    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    YS     (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    YS     (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    YS     (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    YS     (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    YS     (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    %El    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 270 °C (518 °F), 9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    %El    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 220 °C (428 °F), 5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    %El    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 170 °C (338 °F), 3 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    %El    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 120 °C (248 °F), 1.5 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    %El    (N):    effect of grain size & temperature, extrusions || 2.8 x 10^-⁴/s, extruded at 100 °C (212 °F), 0.9 micron grain size || -269.1 °C (-452.5 °F) to 25 °C (77 °F)
    CRR    (N):    extruded || tested at 149 °C (300 °F) || 2.68 x 10^-¹⁰/s to 4.6 x 10^-⁶/s
    CRR    (N):    extruded || tested at 204 °C (400 °F) || 3.3 x 10^-¹⁰/s to 7.55 x 10^-⁶/s
    CRR    (N):    extruded || tested at 260 °C (500 °F) || 6.8 x 10^-¹⁰/s to 1.2 x 10^-⁵/s
    CRR    (N):    extruded || tested at 316 °C (600 °F) || 7.5 x 10^-⁹/s to 1.8 x 10^-⁵/s

return to listing

Makrolon 2407

    TWL    (N):    1 mm (0.0394 inch) thick || color shade 970401, tested at 20 °C (68 °F), external transmission || 657 nm to 1500 nm
    TWL    (N):    1 mm (0.0394 inch) thick || color shade 971000, tested at 20 °C (68 °F), external transmission || 720 nm to 1500 nm
    TWL    (N):    1 mm (0.0394 inch) thick || color shade 770359, tested at 20 °C (68 °F), external transmission || 400 nm to 1500 nm
    TWL    (N):    4 mm (0.157 inch) thick || color shade 970401, tested at 20 °C (68 °F), external transmission || 690 nm to 1500 nm
    TWL    (N):    4 mm (0.157 inch) thick || color shade 971000, tested at 20 °C (68 °F), external transmission || 750 nm to 1500 nm

return to listing

Makrolon AG2477 DQ

    TWL    (N):    3 mm (0.118 inch) thick || color shade 028305, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 028315, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 028325, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 028335, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 028345, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 028355, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm

return to listing

Makrolon AG2677

    TWL    (N):    3 mm (0.118 inch) thick || color shade 755305, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755315, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755325, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755335, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755345, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755355, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755365, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755375, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm

return to listing

Makrolon AG2477

    TWL    (N):    3 mm (0.118 inch) thick || color shade 755305, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755315, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755325, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755335, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755345, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755355, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755365, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755375, tested at 20 °C (68 °F), external transmission || 380 nm to 780 nm

return to listing

Makrolon Ai2675 ST (New)

TWL : 2 mm (0.0787 inch) thick || color shade 978007, tested at 20 °C (68 °F), external transmission || 753 nm to 1600 nm

return to listing

Makrolon Ai2497 ST (New)

    TWL       :    2 mm (0.0787 inch) thick || color shade 978006, tested at 20 °C (68 °F), external transmission || 795 nm to 1600 nm
    TWL       :    2 mm (0.0787 inch) thick || color shade 971064, tested at 20 °C (68 °F), external transmission || 811 nm to 1600 nm
    TWL       :    2 mm (0.0787 inch) thick || color shade 970005, tested at 20 °C (68 °F), external transmission || 824 nm to 1600 nm

return to listing

Makrolon Ai2417

    TWL    (N):    4 mm (0.157 inch) thick || tested at 20 °C (68 °F), external transmission || 350 nm to 1050 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755375, tested at 20 °C (68 °F), external transmission || 380 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755365, tested at 20 °C (68 °F), external transmission || 384 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755355, tested at 20 °C (68 °F), external transmission || 383 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755345, tested at 20 °C (68 °F), external transmission || 385 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755335, tested at 20 °C (68 °F), external transmission || 384 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755325, tested at 20 °C (68 °F), external transmission || 385 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755315, tested at 20 °C (68 °F), external transmission || 386 nm to 1000 nm
    TWL    (N):    3 mm (0.118 inch) thick || color shade 755305, tested at 20 °C (68 °F), external transmission || 390 nm to 1000 nm

return to listing

Makrolon Ai2415 (New)

    DLL       :    solid || parallel to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    DLL       :    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    DLL       :    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    MTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    MTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    MTE       :    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    CTE       :    solid || parallel to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    CTE       :    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    CTE       :    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    D         :    solid || 20 °C (68 °F) to 55 °C (131 °F)
    FS    (*):    ISO 178 || at break || room temperature value
    FS    (*):    ISO 178 || at 3.5% strain || room temperature value
    E     (*):    ISO 527 || 1 mm/min || room temperature value
    FM    (*):    ISO 178 || 2 mm/min || room temperature value
    YS    (*):    ISO 527 || 50 mm/min || room temperature value
    %El   (*):    ISO 527, 50 mm/min || at break || room temperature value
    %El   (*):    ISO 527, 50 mm/min || at yield || room temperature value
    TWL       :    4 mm (0.157 inch) thick || without UV absorber, tested at 20 °C (68 °F), external transmission || 350 nm to 1050 nm

return to listing

Makrolon AL2647

    TWL    (N):    2 mm (0.0787 inch) thick || tested at 20 °C (68 °F), external transmission || 382 nm to 800 nm
    TWL    (N):    3 mm (0.118 inch) thick || tested at 20 °C (68 °F), external transmission || 386 nm to 800 nm
    TWL    (N):    6 mm (0.236 inch) thick || tested at 20 °C (68 °F), external transmission || 391 nm to 800 nm

return to listing

Makrolon AX ST (New)

TWL : 2 mm (0.0787 inch) thick || color shade 978001, tested at 20 °C (68 °F), external transmission || 693 nm to 1600 nm
TWL : 2 mm (0.0787 inch) thick || color shade 978007, tested at 20 °C (68 °F), external transmission || 753 nm to 1600 nm

return to listing

Makrolon AX2477

TWL (N): 1 mm (0.0394 inch) thick || color shade 900346, tested at 20 °C (68 °F), external transmission || 685 nm to 1500 nm
TWL (N): 4 mm (0.157 inch) thick || color shade 900346, tested at 20 °C (68 °F), external transmission || 708 nm to 1500 nm

return to listing

Makrolon LED2245

    TWL    (N):    1 mm (0.0394 inch) thick || neutral, tested at 20 °C (68 °F), external transmission || 350 nm to 800 nm
    TWL    (N):    2 mm (0.0787 inch) thick || neutral, tested at 20 °C (68 °F), external transmission || 350 nm to 800 nm
    TWL    (N):    4 mm (0.157 inch) thick || neutral, tested at 20 °C (68 °F), external transmission || 350 nm to 800 nm
    TWL    (N):    18.1 mm (0.713 inch) thick || neutral, tested at 20 °C (68 °F), external transmission || 350 nm to 800 nm

return to listing

Makrolon OD2015

TWL (N): 1 mm (0.0394 inch) thick || tested at 20 °C (68 °F), external transmission || 300 nm to 2100 nm
TWL (N): 4 mm (0.157 inch) thick || tested at 20 °C (68 °F), external transmission || 300 nm to 2100 nm

return to listing

Maraging 300 (C-type)

    E     (N*):    laser powder bed fusion || build direction || room temperature value
    UTS   (N*):    laser powder bed fusion || build direction || room temperature value
    YS    (N*):    laser powder bed fusion || build direction || room temperature value
    %El   (N*):    laser powder bed fusion || build direction || room temperature value
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, build direction, stress amplitude || 240 cycles to 4.35 x 10⁴ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, torsional, build direction, stress amplitude || 135 cycles to 1 x 10⁵ cycles

return to listing

Maraging 250 (C-type)

    SSC    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), solution annealed, 0.0018/s || 0 to 0.2 mm/mm strain
    SSC    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), solution annealed, deep rolled at 20 °C (68 °F), 0.0018/s || 0 to 0.17 mm/mm strain
    SSC    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), solution annealed, deep rolled at 480 °C (896 °F), 0.0018/s || 0 to 0.15 mm/mm strain
    SSC    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), aged 3 h at 480 °C (896 °F), deep rolled at 20 °C (68 °F), 0.0018/s || 0 to 0.16 mm/mm strain
    SSC    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), aged 3 h at 480 °C (896 °F), 0.0018/s || 0 to 0.14 mm/mm strain
    FSN    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), R = -1, axial, solution annealed, deep rolled at 20 °C (68 °F), stress amplitude || 250 cycles to 4.32 x 10⁵ cycles
    FSN    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), R = -1, axial, solution annealed, deep rolled at 480 °C (896 °F), stress amplitude || 5.1 x 10⁴ cycles to 7.7 x 10⁵ cycles
    FSN    (N):    90 mm (3.54 inch) diameter bar || tested at 20 °C (68 °F), R = -1, axial, aged 3 h at 480 °C (896 °F), deep rolled at 20 °C (68 °F), stress amplitude || 7.1 x 10⁴ cycles to 2.5 x 10⁶ cycles

return to listing

Mg + 4 wt% Rare earths (New)

    SSC       :    high pressure die cast || tested at 20 °C (68 °F), 2 x 10^-⁴/s || 0 to 0.01 mm/mm strain
    SSC       :    high pressure die cast || tested at 150 °C (302 °F), 2 x 10^-⁴/s || 0 to 0.25 mm/mm strain
    SSC       :    high pressure die cast || tested at 250 °C (482 °F), 2 x 10^-⁴/s || 0 to 0.58 mm/mm strain
    SSC       :    high pressure die cast || tested at 300 °C (572 °F), 2 x 10^-⁴/s || 0 to 0.16 mm/mm strain
    UTS       :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)
    YS        :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)
    %El       :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)

return to listing

Mg + 5 wt% Rare earths (New)

    D     (*):    solid || room temperature value
    E         :    high pressure die cast || 20 °C (68 °F) to 350 °C (662 °F)
    SSC       :    high pressure die cast || tested at 20 °C (68 °F), 2 x 10^-⁴/s || 0 to 0.18 mm/mm strain
    SSC       :    high pressure die cast || tested at 150 °C (302 °F), 2 x 10^-⁴/s || 0 to 0.27 mm/mm strain
    SSC       :    high pressure die cast || tested at 250 °C (482 °F), 2 x 10^-⁴/s || 0 to 0.32 mm/mm strain
    SSC       :    high pressure die cast || tested at 300 °C (572 °F), 2 x 10^-⁴/s || 0 to 0.01 mm/mm strain
    UTS       :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)
    YS        :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)
    %El       :    high pressure die cast || 2 x 10^-⁴/s || 20 °C (68 °F) to 300 °C (572 °F)

return to listing

Mg - 3 Al - 0.6 Ca - 0.2 Gd (wt %) (New)

    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, parallel to rolling direction || 0 to 0.15 mm/mm strain
    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 45 degrees to rolling direction || 0 to 0.162 mm/mm strain
    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 90 degrees to rolling direction || 0 to 0.127 mm/mm strain
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value

return to listing

Mg - 1 Al - 1 Ca - 0.4 Mn (wt %) (New)

    SSC       :    as-cast || tested at 20 °C (68 °F), 0.0013/s || 0 to 0.29 mm/mm strain
    SSC       :    extruded (25:1) || tested at 20 °C (68 °F), 0.0013/s, extruded at 1 mm/s || 0 to 0.31 mm/mm strain
    SSC       :    extruded (25:1) || tested at 20 °C (68 °F), 0.0013/s, extruded at 1.5 mm/s || 0 to 0.96 mm/mm strain
    SSC       :    extruded (25:1) || tested at 20 °C (68 °F), 0.0013/s, extruded at 2 mm/s || 0 to 0.11 mm/mm strain
    SSC       :    extruded (25:1) || tested at 20 °C (68 °F), 0.0013/s, extruded at 4 mm/s || 0 to 0.118 mm/mm strain
    SSC       :    extruded (25:1) || tested at 20 °C (68 °F), 0.0013/s, extruded at 7 mm/s || 0 to 0.136 mm/mm strain
    UTS   (*):    as-cast || 0.0013/s || room temperature value
    UTS   (*):    extruded (25:1) || 0.0013/s, extruded at 1 mm/s || room temperature value
    UTS   (*):    extruded (25:1) || 0.0013/s, extruded at 1.5 mm/s || room temperature value
    UTS   (*):    extruded (25:1) || 0.0013/s, extruded at 2 mm/s || room temperature value
    UTS   (*):    extruded (25:1) || 0.0013/s, extruded at 4 mm/s || room temperature value
    UTS   (*):    extruded (25:1) || 0.0013/s, extruded at 7 mm/s || room temperature value
    YS    (*):    as-cast || 0.0013/s || room temperature value
    YS    (*):    extruded (25:1) || 0.0013/s, extruded at 1 mm/s || room temperature value
    YS    (*):    extruded (25:1) || 0.0013/s, extruded at 1.5 mm/s || room temperature value
    YS    (*):    extruded (25:1) || 0.0013/s, extruded at 2 mm/s || room temperature value
    YS    (*):    extruded (25:1) || 0.0013/s, extruded at 4 mm/s || room temperature value
    YS    (*):    extruded (25:1) || 0.0013/s, extruded at 7 mm/s || room temperature value
    %El   (*):    as-cast || 0.0013/s || room temperature value
    %El   (*):    extruded (25:1) || 0.0013/s, extruded at 1 mm/s || room temperature value
    %El   (*):    extruded (25:1) || 0.0013/s, extruded at 1.5 mm/s || room temperature value
    %El   (*):    extruded (25:1) || 0.0013/s, extruded at 2 mm/s || room temperature value
    %El   (*):    extruded (25:1) || 0.0013/s, extruded at 4 mm/s || room temperature value
    %El   (*):    extruded (25:1) || 0.0013/s, extruded at 7 mm/s || room temperature value

return to listing

Mg - 3 Al - 0.6 Ca (wt %) (New)

    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, parallel to rolling direction || 0 to 0.16 mm/mm strain
    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 45 degrees to rolling direction || 0 to 0.14 mm/mm strain
    SSC       :    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 90 degrees to rolling direction || 0 to 0.136 mm/mm strain
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    UTS   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    YS    (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    %El   (*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value

return to listing

Mg - 4 Al - 2 Sn - 0.5 Y - 0.4 Nd (wt %) (New)

    SSC       :    rolled sheet || tested at 20 °C (68 °F), 1.5 x 10^-⁴/s, rolling direction || 0 to 0.11 mm/mm strain
    SSC       :    rolled sheet || tested at 20 °C (68 °F), 1.5 x 10^-⁴/s, 45 degrees from rolling direction || 0 to 0.1 mm/mm strain
    SSC       :    rolled sheet || tested at 20 °C (68 °F), 1.5 x 10^-⁴/s, transverse direction || 0 to 0.91 mm/mm strain
    UTS   (*):    rolled sheet || rolling direction || room temperature value
    UTS   (*):    rolled sheet || 45 degrees from rolling direction || room temperature value
    UTS   (*):    rolled sheet || transverse direction || room temperature value
    YS    (*):    rolled sheet || rolling direction || room temperature value
    YS    (*):    rolled sheet || 45 degrees from rolling direction || room temperature value
    YS    (*):    rolled sheet || transverse direction || room temperature value
    %El   (*):    rolled sheet || rolling direction || room temperature value
    %El   (*):    rolled sheet || 45 degrees from rolling direction || room temperature value
    %El   (*):    rolled sheet || transverse direction || room temperature value

return to listing

Mg - 1 Al (wt %)

    D     (N*):    solid || room temperature value
    SH    (N*):    solid || room temperature value
    TD    (N*):    solid || room temperature value

return to listing

Mg - 3 Al (wt %)

    D     (N*):    solid || room temperature value
    SH    (N*):    solid || room temperature value
    TD    (N*):    solid || room temperature value
    SSC    (N):    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, parallel to rolling direction || 0 to 0.163 mm/mm strain
    SSC    (N):    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 45 degrees to rolling direction || 0 to 0.148 mm/mm strain
    SSC    (N):    hot-rolled, annealed 1 h at 350 °C (662 °F) || tested at 20 °C (68 °F), 6.7 x 10^-⁴/s, 90 degrees to rolling direction || 0 to 0.124 mm/mm strain
    UTS   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    UTS   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    UTS   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    YS    (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    YS    (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    YS    (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value
    %El   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, parallel to rolling direction || room temperature value
    %El   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 45 degrees to rolling direction || room temperature value
    %El   (N*):    hot-rolled, annealed 1 h at 350 °C (662 °F) || 6.7 x 10^-⁴/s, 90 degrees to rolling direction || room temperature value

return to listing

Mg - 5 Al (wt %)

SH (N*): solid || room temperature value
TD (N*): solid || room temperature value

return to listing

Mg - 10 Al (wt %)

SH (N*): solid || room temperature value
TD (N*): solid || room temperature value

return to listing

Mg - 0.5 Al (wt %)

    D     (N*):    solid || room temperature value
    SH    (N*):    solid || room temperature value
    TD    (N*):    solid || room temperature value

return to listing

Mg - 0.23 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.3 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value
    SSC       :    solution treated || tested at 25 °C (77 °F), 0.003/s, rolling direction || 0 to 0.6 mm/mm strain
    SSC       :    solution treated || tested at 25 °C (77 °F), 0.003/s, transverse direction || 0 to 0.16 mm/mm strain
    SSC       :    solution treated || tested at 180 °C (356 °F), 0.003/s, rolling direction || 0 to 0.9 mm/mm strain
    SSC       :    solution treated || tested at 180 °C (356 °F), 0.003/s, transverse direction || 0 to 0.15 mm/mm strain
    SSC       :    solution treated & compressed || tested at 25 °C (77 °F), 0.003/s, rolling direction || 0 to 0.21 mm/mm strain
    SSC       :    solution treated & compressed || tested at 25 °C (77 °F), 0.003/s, transverse direction || 0 to 0.57 mm/mm strain
    SSC       :    solution treated & compressed || tested at 180 °C (356 °F), 0.003/s, rolling direction || 0 to 0.85 mm/mm strain
    SSC       :    solution treated & compressed || tested at 180 °C (356 °F), 0.003/s, transverse direction || 0 to 0.133 mm/mm strain
    UTS   (*):    solution treated || 0.003/s, rolling direction || room temperature value
    UTS   (*):    solution treated || 0.003/s, transverse direction || room temperature value
    UTS   (*):    solution treated & compressed || 0.003/s, rolling direction || room temperature value
    UTS   (*):    solution treated & compressed || 0.003/s, transverse direction || room temperature value
    YS    (*):    solution treated || 0.003/s, rolling direction || room temperature value
    YS    (*):    solution treated || 0.003/s, transverse direction || room temperature value
    YS    (*):    solution treated & compressed || 0.003/s, rolling direction || room temperature value
    YS    (*):    solution treated & compressed || 0.003/s, transverse direction || room temperature value
    %El   (*):    solution treated || 0.003/s, rolling direction || room temperature value
    %El   (*):    solution treated || 0.003/s, transverse direction || room temperature value
    %El   (*):    solution treated & compressed || 0.003/s, rolling direction || room temperature value
    %El   (*):    solution treated & compressed || 0.003/s, transverse direction || room temperature value
    CRS       :    1% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 8.2 h to 29.4 h
    CRS       :    1% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 2.1 h to 11 h
    CRS       :    2% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 11.7 h to 50 h
    CRS       :    2% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 2.2 h to 27.3 h
    CRS       :    3% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 4.7 h to 30 h
    CRS       :    3% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 5.8 h to 50 h
    CRS       :    4% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 7.5 h to 35.5 h
    CRS       :    4% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 8.6 h to 20 h
    CRS       :    5% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 9.3 h to 41.4 h
    CRS       :    5% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 11 h to 27 h
    CRS       :    7.5% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 12.3 h to 35.4 h
    CRS       :    7.5% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 16.4 h to 45.3 h
    CRS       :    10% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 14 h to 42.7 h
    CRS       :    10% total strain, solution treated || tested at 180 °C (356 °F), transverse direction || 21 h to 43.5 h
    CRS       :    14% total strain, solution treated || tested at 180 °C (356 °F), rolling direction || 15 h to 50 h
    CRS       :    1% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 5.3 h to 21 h
    CRS       :    1% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 19.6 h to 31.2 h
    CRS       :    2% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 0.53 h to 45 h
    CRS       :    2% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 2.5 h to 46 h
    CRS       :    3% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 5.3 h to 38.1 h
    CRS       :    3% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 6.9 h to 42.5 h
    CRS       :    4% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 7.1 h to 44.5 h
    CRS       :    4% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 9.8 h to 25.5 h
    CRS       :    5% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 8.3 h to 50 h
    CRS       :    5% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 11.8 h to 30 h
    CRS       :    7.5% total strain, solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 9.8 h to 24.3 h
    CRS       :    7.5% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 15.5 h to 38 h
    CRS       :    10% total strain, solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 18.3 h to 44.5 h
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 1 h || 0 to 0.23 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 2 h || 0 to 0.24 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 3 h || 0 to 0.26 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 4 h || 0 to 0.28 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 5 h || 0 to 0.3 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 6 h || 0 to 0.34 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 7 h || 0 to 0.38 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 8 h || 0 to 0.43 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 9 h || 0 to 0.48 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 10 h || 0 to 0.54 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 11 h || 0 to 0.61 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 12 h || 0 to 0.71 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 13 h || 0 to 0.85 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 14 h || 0 to 0.1 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 15 h || 0 to 0.121 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 16 h || 0 to 0.16 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 18 h || 0 to 0.3 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 20 h || 0 to 0.34 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 22 h || 0 to 0.39 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 24 h || 0 to 0.44 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 26 h || 0 to 0.49 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 28 h || 0 to 0.54 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 30 h || 0 to 0.6 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 32 h || 0 to 0.66 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 34 h || 0 to 0.71 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 36 h || 0 to 0.77 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 38 h || 0 to 0.83 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 40 h || 0 to 0.9 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 42 h || 0 to 0.97 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 44 h || 0 to 0.16 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 46 h || 0 to 0.116 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 48 h || 0 to 0.128 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, rolling direction || 50 h || 0 to 0.144 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 1 h || 0 to 0.17 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 2 h || 0 to 0.19 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 3 h || 0 to 0.22 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 4 h || 0 to 0.24 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 5 h || 0 to 0.27 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 6 h || 0 to 0.3 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 7 h || 0 to 0.34 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 8 h || 0 to 0.38 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 9 h || 0 to 0.41 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 10 h || 0 to 0.45 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 11 h || 0 to 0.5 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 12 h || 0 to 0.54 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 13 h || 0 to 0.58 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 14 h || 0 to 0.63 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 15 h || 0 to 0.68 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 16 h || 0 to 0.73 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 18 h || 0 to 0.48 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 20 h || 0 to 0.52 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 22 h || 0 to 0.56 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 24 h || 0 to 0.6 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 26 h || 0 to 0.63 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 28 h || 0 to 0.67 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 30 h || 0 to 0.71 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 34 h || 0 to 0.79 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 38 h || 0 to 0.87 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 42 h || 0 to 0.96 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 46 h || 0 to 0.17 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated, transverse direction || 50 h || 0 to 0.118 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 1 h || 0 to 0.21 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 2 h || 0 to 0.22 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 3 h || 0 to 0.24 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 4 h || 0 to 0.26 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 5 h || 0 to 0.29 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 6 h || 0 to 0.33 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 7 h || 0 to 0.39 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 8 h || 0 to 0.47 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 9 h || 0 to 0.59 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 10 h || 0 to 0.8 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 11 h || 0 to 0.23 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 12 h || 0 to 0.25 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 13 h || 0 to 0.27 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 14 h || 0 to 0.29 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 15 h || 0 to 0.32 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 16 h || 0 to 0.35 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 17 h || 0 to 0.39 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 18 h || 0 to 0.42 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 19 h || 0 to 0.46 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 20 h || 0 to 0.5 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 21 h || 0 to 0.55 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 22 h || 0 to 0.6 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 23 h || 0 to 0.66 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 24 h || 0 to 0.72 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 25 h || 0 to 0.8 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 26 h || 0 to 0.89 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 28 h || 0 to 0.19 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 30 h || 0 to 0.2 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 32 h || 0 to 0.22 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 34 h || 0 to 0.24 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 36 h || 0 to 0.27 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 38 h || 0 to 0.3 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 40 h || 0 to 0.33 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 42 h || 0 to 0.36 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 44 h || 0 to 0.4 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 46 h || 0 to 0.43 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 48 h || 0 to 0.48 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, rolling direction || 50 h || 0 to 0.52 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 1 h || 0 to 0.18 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 2 h || 0 to 0.19 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 3 h || 0 to 0.2 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 4 h || 0 to 0.23 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 5 h || 0 to 0.25 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 6 h || 0 to 0.28 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 7 h || 0 to 0.3 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 8 h || 0 to 0.33 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 9 h || 0 to 0.37 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 10 h || 0 to 0.41 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 11 h || 0 to 0.45 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 12 h || 0 to 0.51 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 13 h || 0 to 0.57 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 14 h || 0 to 0.64 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 15 h || 0 to 0.71 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 16 h || 0 to 0.79 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 17 h || 0 to 0.88 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 18 h || 0 to 0.97 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 19 h || 0 to 0.16 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 20 h || 0 to 0.117 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 21 h || 0 to 0.13 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 22 h || 0 to 0.147 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 23 h || 0 to 0.168 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 24 h || 0 to 0.196 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 25 h || 0 to 0.39 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 26 h || 0 to 0.41 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 28 h || 0 to 0.46 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 30 h || 0 to 0.51 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 32 h || 0 to 0.57 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 34 h || 0 to 0.62 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 36 h || 0 to 0.69 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 38 h || 0 to 0.75 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 40 h || 0 to 0.82 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 42 h || 0 to 0.9 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 44 h || 0 to 0.98 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 46 h || 0 to 0.16 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 48 h || 0 to 0.115 mm/mm strain
    IC        :    tested at 180 °C (356 °F), total strain, solution treated & compressed, transverse direction || 50 h || 0 to 0.125 mm/mm strain
    CRR       :    solution treated || tested at 180 °C (356 °F), rolling direction || 6.69 x 10^-⁸/s to 5.77 x 10^-⁷/s
    CRR       :    solution treated || tested at 180 °C (356 °F), transverse direction || 1.53 x 10^-⁷/s to 1.57 x 10^-⁶/s
    CRR       :    solution treated & compressed || tested at 180 °C (356 °F), rolling direction || 5.25 x 10^-⁸/s to 4.17 x 10^-⁷/s
    CRR       :    solution treated & compressed || tested at 180 °C (356 °F), transverse direction || 3.83 x 10^-⁸/s to 3.52 x 10^-⁷/s

return to listing

Mg - 0.5 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 1 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 1.4 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.1 Ca (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 2 Gd - 0.5 Mn (wt %) (New)

SSC : as-extruded || tested at 20 °C (68 °F), 0.002/s || 0 to 0.31 mm/mm strain

return to listing

Mg - 7 Gd - 4 Y - 1 Nd - 0.5 Zr (wt %) (New)

    SSCC      :    homogenized ingot || tested at 450 °C (842 °F), 2/s || 0 to 1.7 mm/mm strain
    SSCC      :    homogenized ingot || tested at 475 °C (887 °F), 2/s || 0 to 1.67 mm/mm strain
    SSCC      :    homogenized ingot || tested at 500 °C (932 °F), 2/s || 0 to 1.68 mm/mm strain
    SSCC      :    homogenized ingot || tested at 525 °C (977 °F), 2/s || 0 to 1.7 mm/mm strain
    SSCC      :    homogenized ingot || tested at 550 °C (1022 °F), 2/s || 0 to 1.7 mm/mm strain

return to listing

Mg - 10 Gd - 1.7 Y - 1 Zn - 0.5 Zr (wt %) (New)

    SSC       :    casting, ultrasonically treated melt & semi-solid || tested at 20 °C (68 °F), as-cast, unknown strain rate || 0 to 0.83 mm/mm strain
    SSC       :    casting, ultrasonically treated melt & semi-solid || tested at 20 °C (68 °F), solution treated, unknown strain rate || 0 to 0.194 mm/mm strain
    SSC       :    casting, ultrasonically treated melt & semi-solid || tested at 20 °C (68 °F), aged, 24 h at 200 °C (392 °F), unknown strain rate || 0 to 0.127 mm/mm strain
    SSC       :    casting, ultrasonically treated melt & semi-solid || tested at 20 °C (68 °F), peak aged, 48 h at 200 °C (392 °F), unknown strain rate || 0 to 0.123 mm/mm strain
    UTS   (*):    casting || as-cast || room temperature value
    UTS   (*):    casting || solution treated || room temperature value
    UTS   (*):    casting || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    UTS   (*):    casting, ultrasonically treated melt || as-cast || room temperature value
    UTS   (*):    casting, ultrasonically treated melt || solution treated || room temperature value
    UTS   (*):    casting, ultrasonically treated melt || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    UTS   (*):    casting, ultrasonically treated melt & semi-solid || as-cast || room temperature value
    UTS   (*):    casting, ultrasonically treated melt & semi-solid || solution treated || room temperature value
    UTS   (*):    casting, ultrasonically treated melt & semi-solid || aged, 24 h at 200 °C (392 °F) || room temperature value
    UTS   (*):    casting, ultrasonically treated melt & semi-solid || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    YS    (*):    casting || as-cast || room temperature value
    YS    (*):    casting || solution treated || room temperature value
    YS    (*):    casting || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    YS    (*):    casting, ultrasonically treated melt || as-cast || room temperature value
    YS    (*):    casting, ultrasonically treated melt || solution treated || room temperature value
    YS    (*):    casting, ultrasonically treated melt || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    YS    (*):    casting, ultrasonically treated melt & semi-solid || as-cast || room temperature value
    YS    (*):    casting, ultrasonically treated melt & semi-solid || solution treated || room temperature value
    YS    (*):    casting, ultrasonically treated melt & semi-solid || aged, 24 h at 200 °C (392 °F) || room temperature value
    YS    (*):    casting, ultrasonically treated melt & semi-solid || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    %El   (*):    casting || as-cast || room temperature value
    %El   (*):    casting || solution treated || room temperature value
    %El   (*):    casting || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    %El   (*):    casting, ultrasonically treated melt || as-cast || room temperature value
    %El   (*):    casting, ultrasonically treated melt || solution treated || room temperature value
    %El   (*):    casting, ultrasonically treated melt || peak aged, 48 h at 200 °C (392 °F) || room temperature value
    %El   (*):    casting, ultrasonically treated melt & semi-solid || as-cast || room temperature value
    %El   (*):    casting, ultrasonically treated melt & semi-solid || solution treated || room temperature value
    %El   (*):    casting, ultrasonically treated melt & semi-solid || aged, 24 h at 200 °C (392 °F) || room temperature value
    %El   (*):    casting, ultrasonically treated melt & semi-solid || peak aged, 48 h at 200 °C (392 °F) || room temperature value

return to listing

Mg - 10 Gd - 3 Y - 0.1 Zn - 0.4 Zr (wt %) (New)

    E     (*):    T4 temper || room temperature value
    UTS   (*):    T4 temper || room temperature value
    YS    (*):    T4 temper || room temperature value
    %El   (*):    T4 temper || room temperature value
    FSN       :    T4 temper || tested at 20 °C (68 °F), R = -1, 20 kHz, axial, stress amplitude || 2 x 10⁵ cycles to unknown strain rate cycles

return to listing

Mg - 8.3 Gd - 4 Y - 1 Zn - 0.4 Zr (wt %) (New)

    SSC       :    centrifugal casting, ring-rolling || tested at 20 °C (68 °F), 0.0056/s, 40% total accumulated reduction || 0 to 0.47 mm/mm strain
    SSC       :    centrifugal casting, ring-rolling || tested at 20 °C (68 °F), 0.0056/s, 60% total accumulated reduction || 0 to 0.65 mm/mm strain
    SSC       :    centrifugal casting, ring-rolling || tested at 20 °C (68 °F), 0.0056/s, 80% total accumulated reduction || 0 to 0.11 mm/mm strain
    SSC       :    centrifugal casting, ring-rolling || tested at 20 °C (68 °F), 0.0056/s, 80% total accumulated reduction, peak aged || 0 to 0.46 mm/mm strain
    SSCC      :    homogenized, 0.001/s || tested at 350 °C (662 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.001/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.001/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.01/s || tested at 350 °C (662 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.01/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.01/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.1/s || tested at 350 °C (662 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.1/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 0.1/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 1/s || tested at 350 °C (662 °F) || 0 to 0.24 mm/mm strain
    SSCC      :    homogenized, 1/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized, 1/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.001/s || tested at 350 °C (662 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.001/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.001/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.01/s || tested at 350 °C (662 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.01/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.01/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.1/s || tested at 350 °C (662 °F) || 0 to 0.37 mm/mm strain
    SSCC      :    homogenized & annealed, 0.1/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 0.1/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 1/s || tested at 350 °C (662 °F) || 0 to 0.124 mm/mm strain
    SSCC      :    homogenized & annealed, 1/s || tested at 400 °C (752 °F) || 0 to 0.7 mm/mm strain
    SSCC      :    homogenized & annealed, 1/s || tested at 450 °C (842 °F) || 0 to 0.7 mm/mm strain
    UTS   (*):    centrifugal casting, ring-rolling || 40% total accumulated reduction, 0.0056/s || room temperature value
    UTS   (*):    centrifugal casting, ring-rolling || 60% total accumulated reduction, 0.0056/s || room temperature value
    UTS   (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, 0.0056/s || room temperature value
    UTS   (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, peak aged, 0.0056/s || room temperature value
    YS    (*):    centrifugal casting, ring-rolling || 40% total accumulated reduction, 0.0056/s || room temperature value
    YS    (*):    centrifugal casting, ring-rolling || 60% total accumulated reduction, 0.0056/s || room temperature value
    YS    (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, 0.0056/s || room temperature value
    YS    (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, peak aged, 0.0056/s || room temperature value
    %El   (*):    centrifugal casting, ring-rolling || 40% total accumulated reduction, 0.0056/s || room temperature value
    %El   (*):    centrifugal casting, ring-rolling || 60% total accumulated reduction, 0.0056/s || room temperature value
    %El   (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, 0.0056/s || room temperature value
    %El   (*):    centrifugal casting, ring-rolling || 80% total accumulated reduction, peak aged, 0.0056/s || room temperature value

return to listing

Mg - 9 Gd - 3 Y - 1.5 Zn - 0.8 Zr (wt %) (New)

    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 400 °C (752 °F), 0.1/s, edge || 0 to 0.8 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 400 °C (752 °F), 1/s, edge || 0 to 0.8 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 400 °C (752 °F), 0.1/s, center || 0 to 0.86 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 400 °C (752 °F), 1/s, center || 0 to 0.82 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 450 °C (842 °F), 0.1/s, edge || 0 to 0.92 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 450 °C (842 °F), 1/s, edge || 0 to 0.86 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 450 °C (842 °F), 0.1/s, center || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, no EM field || tested at 450 °C (842 °F), 1/s, center || 0 to 0.85 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, edge || 0 to 0.86 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 400 °C (752 °F), 1/s, edge || 0 to 0.8 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, center || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 400 °C (752 °F), 1/s, center || 0 to 0.82 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, edge || 0 to 0.77 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 450 °C (842 °F), 1/s, edge || 0 to 0.68 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, center || 0 to 0.92 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 68 A and 30 Hz || tested at 450 °C (842 °F), 1/s, center || 0 to 0.82 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, edge || 0 to 0.86 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 400 °C (752 °F), 1/s, edge || 0 to 0.81 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, center || 0 to 0.83 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 400 °C (752 °F), 1/s, center || 0 to 0.81 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, edge || 0 to 0.92 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 450 °C (842 °F), 1/s, edge || 0 to 0.84 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, center || 0 to 0.78 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, EM field at 90 A and 30 Hz || tested at 450 °C (842 °F), 1/s, center || 0 to 0.85 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, edge || 0 to 0.86 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 400 °C (752 °F), 1/s, edge || 0 to 0.81 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 400 °C (752 °F), 0.1/s, center || 0 to 0.74 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 400 °C (752 °F), 1/s, center || 0 to 0.8 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, edge || 0 to 0.74 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 450 °C (842 °F), 1/s, edge || 0 to 0.87 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 450 °C (842 °F), 0.1/s, center || 0 to 0.84 mm/mm strain
    SSCC      :    semi-continuous cast at 55 mm/min, EM field at 65 A and 30 Hz || tested at 450 °C (842 °F), 1/s, center || 0 to 0.86 mm/mm strain

return to listing

Mg - 9 Gd - 4 Y - 2 Zn - 0.5 Zr (wt %) (New)

    UTS   (*):    cast || 0.001/s, as-cast || room temperature value
    UTS   (*):    cast || 0.001/s, homogenized || room temperature value
    UTS   (*):    cast || 0.001/s, homogenized, solution treated, & extruded 16:1 || room temperature value
    UTS   (*):    cast || 0.001/s, homogenized, solution treated, aged, & extruded 16:1 || room temperature value
    YS    (*):    cast || 0.001/s, as-cast || room temperature value
    YS    (*):    cast || 0.001/s, homogenized || room temperature value
    YS    (*):    cast || 0.001/s, homogenized, solution treated, & extruded 16:1 || room temperature value
    YS    (*):    cast || 0.001/s, homogenized, solution treated, aged, & extruded 16:1 || room temperature value
    %El   (*):    cast || 0.001/s, as-cast || room temperature value
    %El   (*):    cast || 0.001/s, homogenized || room temperature value
    %El   (*):    cast || 0.001/s, homogenized, solution treated, & extruded 16:1 || room temperature value
    %El   (*):    cast || 0.001/s, homogenized, solution treated, aged, & extruded 16:1 || room temperature value
    FEN       :    cast || tested at 20 °C (68 °F), R = -1, axial, 0.25 Hz, homogenized, total strain amplitude || 550 cycles to 4.18 x 10³ cycles
    FEN       :    cast || tested at 20 °C (68 °F), R = -1, axial, 0.25 Hz, homogenized, solution treated, & extruded 16:1, total strain amplitude || 960 cycles to 1.4 x 10⁴ cycles
    FEN       :    cast || tested at 20 °C (68 °F), R = -1, axial, 0.25 Hz, homogenized, solution treated, aged, & extruded 16:1, total strain amplitude || 1 x 10³ cycles to 2.7 x 10⁴ cycles

return to listing

Mg - 10 Gd - 3 Y - 0.5 Zr (wt %) (New)

    UTS       :    sand cast || aged 14 h at 225 °C (437 °F) || 20 °C (68 °F) to 300 °C (572 °F)
    UTS       :    sand cast || aged 12 h at 250 °C (482 °F) || 20 °C (68 °F) to 300 °C (572 °F)
    YS        :    sand cast || aged 14 h at 225 °C (437 °F) || 20 °C (68 °F) to 300 °C (572 °F)
    YS        :    sand cast || aged 12 h at 250 °C (482 °F) || 20 °C (68 °F) to 300 °C (572 °F)
    %El       :    sand cast || aged 14 h at 225 °C (437 °F) || 20 °C (68 °F) to 300 °C (572 °F)
    %El       :    sand cast || aged 12 h at 250 °C (482 °F) || 20 °C (68 °F) to 300 °C (572 °F)

return to listing

Mg - 8.1 Gd - 4.5 Y - 0.3 Zr (wt %) (New)

    SSC       :    semi-continuous cast || tested at 20 °C (68 °F), as-cast || 0 to 7.4 x 10^-³ mm/mm strain
    SSC       :    semi-continuous cast || tested at 20 °C (68 °F), as-extruded || 0 to 0.39 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.001/s || tested at 300 °C (572 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.001/s || tested at 350 °C (662 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.001/s || tested at 400 °C (752 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.001/s || tested at 450 °C (842 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.001/s || tested at 500 °C (932 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.01/s || tested at 300 °C (572 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.01/s || tested at 350 °C (662 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.01/s || tested at 400 °C (752 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.01/s || tested at 450 °C (842 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.01/s || tested at 500 °C (932 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.1/s || tested at 300 °C (572 °F) || 0 to 0.23 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.1/s || tested at 350 °C (662 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.1/s || tested at 400 °C (752 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.1/s || tested at 450 °C (842 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 0.1/s || tested at 500 °C (932 °F) || 0 to 0.9 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 1/s || tested at 300 °C (572 °F) || 0 to 0.23 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 1/s || tested at 350 °C (662 °F) || 0 to 0.28 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 1/s || tested at 400 °C (752 °F) || 0 to 0.85 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 1/s || tested at 450 °C (842 °F) || 0 to 0.85 mm/mm strain
    SSCC      :    semi-continuous cast at 65 mm/min, 1/s || tested at 500 °C (932 °F) || 0 to 0.9 mm/mm strain

return to listing

Mg - 14 Gd - 0.4 Zr (wt %) (New)

    UCS       :    sand cast || 0.001/s || 20 °C (68 °F) to 250 °C (482 °F)
    YSC       :    sand cast || 0.001/s || 20 °C (68 °F) to 250 °C (482 °F)
    %El       :    sand cast || 0.001/s, in compression || 20 °C (68 °F) to 250 °C (482 °F)
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 1 h || 0 to 0.13 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 2 h || 0 to 0.14 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 5 h || 0 to 0.16 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 10 h || 0 to 0.17 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 20 h || 0 to 0.19 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 30 h || 0 to 0.21 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 50 h || 0 to 0.24 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 75 h || 0 to 0.28 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 100 h || 0 to 0.32 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 120 h || 0 to 0.37 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 140 h || 0 to 0.41 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 160 h || 0 to 0.46 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 180 h || 0 to 0.52 mm/mm strain
    IC        :    tested at 250 °C (482 °F), sand cast, total strain || 200 h || 0 to 0.58 mm/mm strain
    CRR       :    sand cast || tested at 250 °C (482 °F), in compression || 7.35 x 10^-⁹/s to 4.26 x 10^-⁸/s

return to listing

Mg - 8 Li - 3 Al - 2 Zn - 0.5 Y (wt %) (New)

    SSC       :    as-cast || tested at 20 °C (68 °F), 5.6 x 10^-³/s || 0 to 0.62 mm/mm strain
    SSC       :    solution treated || tested at 20 °C (68 °F), 5.6 x 10^-³/s || 0 to 0.25 mm/mm strain
    SSC       :    as-extruded || tested at 20 °C (68 °F), 5.6 x 10^-³/s || 0 to 0.5 mm/mm strain
    UTS   (*):    as-cast || 5.6 x 10^-³/s || room temperature value
    UTS   (*):    solution treated || 5.6 x 10^-³/s || room temperature value
    UTS   (*):    as-extruded || 5.6 x 10^-³/s || room temperature value
    YS    (*):    as-cast || 5.6 x 10^-³/s || room temperature value
    YS    (*):    solution treated || 5.6 x 10^-³/s || room temperature value
    YS    (*):    as-extruded || 5.6 x 10^-³/s || room temperature value
    %El   (*):    as-cast || 5.6 x 10^-³/s || room temperature value
    %El   (*):    solution treated || 5.6 x 10^-³/s || room temperature value
    %El   (*):    as-extruded || 5.6 x 10^-³/s || room temperature value
    FSN       :    as-cast || tested at 20 °C (68 °F), R = -1, rotary bending, stress amplitude || 3 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN       :    solution treated || tested at 20 °C (68 °F), R = -1, rotary bending, stress amplitude || 5 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN       :    as-extruded || tested at 20 °C (68 °F), R = -1, rotary bending, stress amplitude || 8 x 10⁴ cycles to 1 x 10⁸ cycles

return to listing

Mg - 21 Li (at %) (New)

SH : solid || -80 °C (-112 °F) to 500 °C (932 °F)

return to listing

Mg - 25 Li (at %) (New)

SH : solid || -80 °C (-112 °F) to 500 °C (932 °F)

return to listing

Mg - 30 Li (at %)

SH (R): solid || -80 °C (-112 °F) to 552 °C (1025 °F)

return to listing

Mg - 0.2 Mn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.5 Mn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.9 Mn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 1.3 Mn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.1 Mn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 2 Sn - x Yb (at %) (New)

    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0 || tested at 20 °C (68 °F), 0.001/s || 0 to 0.98 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0 || tested at 100 °C (212 °F), 0.001/s || 0 to 0.98 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0 || tested at 200 °C (392 °F), 0.001/s || 0 to 0.46 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || tested at 20 °C (68 °F), 0.001/s || 0 to 0.67 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || tested at 100 °C (212 °F), 0.001/s || 0 to 0.15 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || tested at 200 °C (392 °F), 0.001/s || 0 to 0.41 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || tested at 20 °C (68 °F), 0.001/s || 0 to 0.8 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || tested at 100 °C (212 °F), 0.001/s || 0 to 0.133 mm/mm strain
    SSC       :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || tested at 200 °C (392 °F), 0.001/s || 0 to 0.32 mm/mm strain
    UTS       :    extruded 2 mm (0.0787 inch) sheet, x = 0 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    UTS       :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    UTS       :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    YS        :    extruded 2 mm (0.0787 inch) sheet, x = 0 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    YS        :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    YS        :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    %El       :    extruded 2 mm (0.0787 inch) sheet, x = 0 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    %El       :    extruded 2 mm (0.0787 inch) sheet, x = 0.1 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)
    %El       :    extruded 2 mm (0.0787 inch) sheet, x = 0.5 || 0.001/s || 20 °C (68 °F) to 200 °C (392 °F)

return to listing

Mg - 7.7 Sn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 11.7 Sn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 13.5 Sn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 2.6 Sn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 5.1 Sn (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 4 Y - 3.5 Nd (wt %) (New)

    SSC       :    hot-rolled || tested at 20 °C (68 °F), 0.001/s, solution treated || 0 to 0.79 mm/mm strain
    SSC       :    hot-rolled || tested at 20 °C (68 °F), 0.001/s, peak aged || 0 to 0.61 mm/mm strain
    SSC       :    hot-rolled || tested at 20 °C (68 °F), 0.001/s, solution treated, compressed 25% at 490 °C (914 °F) || 0 to 0.79 mm/mm strain
    SSC       :    hot-rolled || tested at 20 °C (68 °F), 0.001/s, peak aged, compressed 25% at 490 °C (914 °F) || 0 to 0.67 mm/mm strain
    SSC       :    hot-rolled || tested at 20 °C (68 °F), 0.001/s, solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || 0 to 0.37 mm/mm strain
    SSC       :    hot-rolled || tested at 220 °C (428 °F), 0.001/s, solution treated || 0 to 0.14 mm/mm strain
    SSC       :    hot-rolled || tested at 220 °C (428 °F), 0.001/s, peak aged || 0 to 0.97 mm/mm strain
    SSC       :    hot-rolled || tested at 220 °C (428 °F), 0.001/s, solution treated, compressed 25% at 490 °C (914 °F) || 0 to 0.11 mm/mm strain
    SSC       :    hot-rolled || tested at 220 °C (428 °F), 0.001/s, peak aged, compressed 25% at 490 °C (914 °F) || 0 to 0.1 mm/mm strain
    SSC       :    hot-rolled || tested at 220 °C (428 °F), 0.001/s, solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || 0 to 0.89 mm/mm strain
    UTS   (*):    hot-rolled || 0.001/s, solution treated || room temperature value
    UTS   (*):    hot-rolled || 0.001/s, peak aged || room temperature value
    UTS   (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F) || room temperature value
    UTS   (*):    hot-rolled || 0.001/s, peak aged, compressed 25% at 490 °C (914 °F) || room temperature value
    UTS   (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || room temperature value
    YS    (*):    hot-rolled || 0.001/s, solution treated || room temperature value
    YS    (*):    hot-rolled || 0.001/s, peak aged || room temperature value
    YS    (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F) || room temperature value
    YS    (*):    hot-rolled || 0.001/s, peak aged, compressed 25% at 490 °C (914 °F) || room temperature value
    YS    (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || room temperature value
    %El   (*):    hot-rolled || 0.001/s, solution treated || room temperature value
    %El   (*):    hot-rolled || 0.001/s, peak aged || room temperature value
    %El   (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F) || room temperature value
    %El   (*):    hot-rolled || 0.001/s, peak aged, compressed 25% at 490 °C (914 °F) || room temperature value
    %El   (*):    hot-rolled || 0.001/s, solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || room temperature value
    CRR       :    hot-rolled || tested at 220 °C (428 °F), solution treated || 5.5 x 10^-⁸/s to 1.54 x 10^-⁷/s
    CRR       :    hot-rolled || tested at 220 °C (428 °F), peak aged || 8.57 x 10^-⁸/s to 3.38 x 10^-⁷/s
    CRR       :    hot-rolled || tested at 220 °C (428 °F), solution treated, compressed 25% at 490 °C (914 °F) || 1.68 x 10^-⁸/s to 1.18 x 10^-⁷/s
    CRR       :    hot-rolled || tested at 220 °C (428 °F), peak aged, compressed 25% at 490 °C (914 °F) || 4.61 x 10^-⁹/s to 6.97 x 10^-⁸/s
    CRR       :    hot-rolled || tested at 220 °C (428 °F), solution treated, compressed 25% at 490 °C (914 °F), aged 30 h at 220 °C (428 °F) || 3.36 x 10^-⁸/s to 3.1 x 10^-⁷/s

return to listing

Mg - 6.8 Y - 2.5 Zn (wt %)

    SSCC   (N):    as-cast || tested at 20 °C (68 °F), 0.0017/s || 0 to 0.25 mm/mm strain
    SSCC   (N):    high pressure treated at 6 GPa (870 ksi) || tested at 20 °C (68 °F), 0.0017/s || 0 to 0.19 mm/mm strain
    UCS   (N*):    as-cast || 0.0017/s || room temperature value
    UCS   (N*):    high pressure treated at 6 GPa (870 ksi) || 0.0017/s || room temperature value
    YSC   (N*):    as-cast || 0.0017/s || room temperature value
    YSC   (N*):    high pressure treated at 6 GPa (870 ksi) || 0.0017/s || room temperature value
    %El   (N*):    as-cast || 0.0017/s, in compression || room temperature value
    %El   (N*):    high pressure treated at 6 GPa (870 ksi) || 0.0017/s, in compression || room temperature value

return to listing

Mg - 2 Y - 8 Zn (wt %) (New)

    DLL       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    MTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    CTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    D         :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    TC        :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    RHO       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    SIGMA    :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)

return to listing

Mg - 6 Y - 6 Zn (wt %) (New)

    DLL       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    MTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    CTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    D         :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    TC        :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    RHO       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    SIGMA    :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)

return to listing

Mg - 7 Y - 3 Zn (wt %) (New)

    DLL       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    MTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    CTE       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    D         :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    TC        :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    RHO       :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)
    SIGMA    :    solid || as-cast || 20 °C (68 °F) to 400 °C (752 °F)

return to listing

Mg - 1 Y - 6 Zn (wt %) (New)

    SSC       :    extruded (18:1) || tested at 20 °C (68 °F), 1 x 10^-⁴/s || 0 to 0.168 mm/mm strain
    SSC       :    extruded (18:1) || tested at 100 °C (212 °F), 1 x 10^-⁴/s || 0 to 0.254 mm/mm strain
    SSC       :    extruded (18:1) || tested at 150 °C (302 °F), 1 x 10^-⁴/s || 0 to 0.2 mm/mm strain
    SSC       :    extruded (18:1) || tested at 200 °C (392 °F), 1 x 10^-⁴/s || 0 to 0.327 mm/mm strain
    SSC       :    extruded (18:1) || tested at 250 °C (482 °F), 1 x 10^-⁴/s || 0 to 0.8 mm/mm strain
    SSC       :    extruded (18:1) || tested at 300 °C (572 °F), 1 x 10^-⁴/s || 0 to 1.2 mm/mm strain
    SSC       :    extruded (18:1) || tested at 350 °C (662 °F), 1 x 10^-⁴/s || 0 to 0.78 mm/mm strain
    UTS       :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)
    YS        :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)
    %El       :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)

return to listing

Mg - 1.1 Y (wt %)

    SSC    (N):    extruded, 20 micron grain size || tested at 20 °C (68 °F), 0.001/s || 0 to 0.25 mm/mm strain
    UTS   (N*):    extruded, 20 micron grain size || 0.001/s || room temperature value
    YS    (N*):    extruded, 20 micron grain size || 0.001/s || room temperature value
    %El   (N*):    extruded, 20 micron grain size || 0.001/s || room temperature value

return to listing

Mg - 2 Y (wt %)

    SSC    (N):    extruded, 12 micron grain size || tested at 20 °C (68 °F), 0.001/s || 0 to 0.226 mm/mm strain
    UTS   (N*):    extruded, 12 micron grain size || 0.001/s || room temperature value
    YS    (N*):    extruded, 12 micron grain size || 0.001/s || room temperature value
    %El   (N*):    extruded, 12 micron grain size || 0.001/s || room temperature value

return to listing

Mg - 3 Y (wt %) (New)

    SSC       :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), 0.001/s, extrusion direction || 0 to 0.24 mm/mm strain
    SSC       :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), 0.001/s, transverse direction || 0 to 0.155 mm/mm strain
    SSC       :    extruded (25:1), 13 micron grain size || tested at 20 °C (68 °F), 0.001/s || 0 to 0.2 mm/mm strain
    SSCC      :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), 0.001/s, extrusion direction || 0 to 0.74 mm/mm strain
    SSCC      :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), 0.001/s, transverse direction || 0 to 0.76 mm/mm strain
    UTS   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion direction || room temperature value
    UTS   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, transverse direction || room temperature value
    UTS   (*):    extruded (25:1), 13 micron grain size || 0.001/s || room temperature value
    YS    (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion direction || room temperature value
    YS    (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion transverse || room temperature value
    YS    (*):    extruded (25:1), 13 micron grain size || 0.001/s || room temperature value
    YSC   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion direction || room temperature value
    YSC   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, transverse direction || room temperature value
    %El   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion direction || room temperature value
    %El   (*):    extruded (18.3:1), 10 micron grain size || 0.001/s, extrusion transverse || room temperature value
    %El   (*):    extruded (25:1), 13 micron grain size || 0.001/s || room temperature value
    FEN       :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), R = -1, axial, 0.25 Hz, extrusion direction, total strain amplitude || 90 cycles to 6.85 x 10³ cycles
    FEN       :    extruded (18.3:1), 10 micron grain size || tested at 20 °C (68 °F), R = -1, axial, 0.25 Hz, transverse direction, total strain amplitude || 38 cycles to 2.4 x 10³ cycles

return to listing

Mg - 5.3 Zn - 0.6 Ca (wt %) (New)

    SSC       :    extruded || tested at 20 °C (68 °F), 1.67 x 10^-³/s || 0 to 0.19 mm/mm strain
    SSC       :    extruded & equal channel angular pressing || tested at 20 °C (68 °F), 1.67 x 10^-³/s || 0 to 0.187 mm/mm strain
    SSCC      :    extruded || tested at 20 °C (68 °F), 1.67 x 10^-³/s || 0 to 0.18 mm/mm strain
    SSCC      :    extruded & equal channel angular pressing || tested at 20 °C (68 °F), 1.67 x 10^-³/s || 0 to 0.67 mm/mm strain

return to listing

Mg - 6 Zn - 1 Gd - 1 Er (wt %) (New)

    SSC       :    homogenized || tested at 20 °C (68 °F), 0.001/s || 0 to 0.7 mm/mm strain
    SSC       :    solution treated || tested at 20 °C (68 °F), 0.001/s || 0 to 0.14 mm/mm strain
    SSC       :    aged & extruded (10:1) || tested at 20 °C (68 °F), 0.001/s, aged 12 h at 200 °C (392 °F) || 0 to 0.15 mm/mm strain
    SSC       :    aged & extruded (10:1) || tested at 20 °C (68 °F), 0.001/s, aged 48 h at 200 °C (392 °F) || 0 to 0.124 mm/mm strain
    SSC       :    aged & extruded (10:1) || tested at 20 °C (68 °F), 0.001/s, aged 96 h at 200 °C (392 °F) || 0 to 0.113 mm/mm strain

return to listing

Mg - 4.4 Zn - 0.9 Gd (wt %) (New)

    SSC       :    extruded and aged || tested at 20 °C (68 °F), 8.3 x 10^-⁴/s || 0 to 0.4 mm/mm strain
    UTS   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value

return to listing

Mg - 4.4 Zn - 2.1 Gd (wt %) (New)

    SSC       :    extruded and aged || tested at 20 °C (68 °F), 8.3 x 10^-⁴/s || 0 to 0.23 mm/mm strain
    UTS   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value

return to listing

Mg - 4.25 Zn - 0.4 Gd (wt %) (New)

    SSC       :    extruded and aged || tested at 20 °C (68 °F), 8.3 x 10^-⁴/s || 0 to 0.1 mm/mm strain
    UTS   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value

return to listing

Mg - 5 Zn - 4.5 Sn - x Sc (wt %) (New)

    SSC       :    x = 0 || tested at 20 °C (68 °F), 0.001/s, as-cast || 0 to 0.63 mm/mm strain
    SSC       :    x = 0 || tested at 20 °C (68 °F), 0.001/s, as-rolled || 0 to 0.12 mm/mm strain
    SSC       :    x = 0.1 || tested at 20 °C (68 °F), 0.001/s, as-cast || 0 to 0.83 mm/mm strain
    SSC       :    x = 0.1 || tested at 20 °C (68 °F), 0.001/s, as-rolled || 0 to 0.13 mm/mm strain
    SSC       :    x = 0.3 || tested at 20 °C (68 °F), 0.001/s, as-cast || 0 to 0.1 mm/mm strain
    SSC       :    x = 0.3 || tested at 20 °C (68 °F), 0.001/s, as-rolled || 0 to 0.15 mm/mm strain
    SSC       :    x = 0.4 || tested at 20 °C (68 °F), 0.001/s, as-cast || 0 to 0.61 mm/mm strain
    SSC       :    x = 0.4 || tested at 20 °C (68 °F), 0.001/s, as-rolled || 0 to 0.128 mm/mm strain

return to listing

Mg - 6 Zn - 1 Y - 1 Ca (wt %) (New)

    SSC       :    extruded (18:1) || tested at 20 °C (68 °F), 1 x 10^-⁴/s || 0 to 0.156 mm/mm strain
    SSC       :    extruded (18:1) || tested at 100 °C (212 °F), 1 x 10^-⁴/s || 0 to 0.21 mm/mm strain
    SSC       :    extruded (18:1) || tested at 150 °C (302 °F), 1 x 10^-⁴/s || 0 to 0.21 mm/mm strain
    SSC       :    extruded (18:1) || tested at 200 °C (392 °F), 1 x 10^-⁴/s || 0 to 0.75 mm/mm strain
    SSC       :    extruded (18:1) || tested at 250 °C (482 °F), 1 x 10^-⁴/s || 0 to 0.31 mm/mm strain
    SSC       :    extruded (18:1) || tested at 300 °C (572 °F), 1 x 10^-⁴/s || 0 to 0.66 mm/mm strain
    SSC       :    extruded (18:1) || tested at 350 °C (662 °F), 1 x 10^-⁴/s || 0 to 0.9 mm/mm strain
    UTS       :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)
    YS        :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)
    %El       :    extruded (18:1) || 20 °C (68 °F) to 350 °C (662 °F)

return to listing

Mg - 1 Zn (wt %) (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 20 °C (68 °F) to 175 °C (347 °F)
    SH    (*):    solid || room temperature value
    TD    (*):    solid || room temperature value
    RHO       :    solid || 20 °C (68 °F) to 175 °C (347 °F)
    SIGMA    :    solid || 20 °C (68 °F) to 175 °C (347 °F)
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 18 micron grain size || 0 to 0.162 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 23 micron grain size || 0 to 0.167 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 37 micron grain size || 0 to 0.171 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 49 micron grain size || 0 to 0.171 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 64 micron grain size || 0 to 0.192 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 84 micron grain size || 0 to 0.176 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 97 micron grain size || 0 to 0.178 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 188 micron grain size || 0 to 0.174 mm/mm strain
    SSC       :    effect of grain size || tested at 20 °C (68 °F), 0.001/s, 226 micron grain size || 0 to 0.165 mm/mm strain

return to listing

Mg - 4.4 Zn (wt %) (New)

    SSC       :    extruded and aged || tested at 20 °C (68 °F), 8.3 x 10^-⁴/s || 0 to 0.14 mm/mm strain
    UTS   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded and aged || 8.3 x 10^-⁴/s || room temperature value

return to listing

Mg - 1 Zr - 0.5 Sr - 1.5 Ho (wt %) (New)

    E     (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    SSC       :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.12 mm/mm strain
    SSCC      :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.24 mm/mm strain
    UTS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    UCS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YSC   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in tension || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in compression || room temperature value

return to listing

Mg - 1 Zr - 0.5 Sr - 4 Ho (wt %) (New)

    E     (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    SSC       :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.144 mm/mm strain
    SSCC      :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.25 mm/mm strain
    UTS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    UCS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YSC   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in tension || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in compression || room temperature value

return to listing

Mg - 1 Zr - 0.5 Sr - 0.5 Ho (wt %) (New)

    E     (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    SSC       :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.69 mm/mm strain
    SSCC      :    extruded (36:1) || tested at 20 °C (68 °F), 9.3 x 10^-⁴/s || 0 to 0.15 mm/mm strain
    UTS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YS    (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    UCS   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    YSC   (*):    extruded (36:1) || 9.3 x 10^-⁴/s || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in tension || room temperature value
    %El   (*):    extruded (36:1) || 9.3 x 10^-⁴/s, in compression || room temperature value

return to listing

Mg - 0.75 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 1 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.1 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.25 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg - 0.4 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    TC    (*):    solid || as-cast || room temperature value
    TC    (*):    solid || solution annealed || room temperature value
    SH    (*):    solid || room temperature value
    TD    (*):    solid || as-cast || room temperature value
    TD    (*):    solid || solution annealed || room temperature value
    RHO   (*):    solid || as-cast || room temperature value
    RHO   (*):    solid || solution annealed || room temperature value
    SIGMA (*):    solid || as-cast || room temperature value
    SIGMA (*):    solid || solution annealed || room temperature value

return to listing

Mg₂Si₀_.₅₅Sn₀_.₄Ge₀_.₀₅ (Bi doped) (New)

    D     (*):    x = 0.02 || Mg₂Si₀_.₅₃Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂ || room temperature value
    D     (*):    x = 0.025 || Mg₂Si₀_.₅₂₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂₅ || room temperature value
    D     (*):    x = 0.03 || Mg₂Si₀_.₅₂Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃ || room temperature value
    D     (*):    x = 0.035 || Mg₂Si₀_.₅₁₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃₅ || room temperature value
    TC        :    x = 0.02 || Mg₂Si₀_.₅₃Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂ || 20 °C (68 °F) to 530 °C (986 °F)
    TC        :    x = 0.025 || Mg₂Si₀_.₅₂₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂₅ || 20 °C (68 °F) to 550 °C (1022 °F)
    TC        :    x = 0.03 || Mg₂Si₀_.₅₂Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃ || 20 °C (68 °F) to 550 °C (1022 °F)
    TC        :    x = 0.035 || Mg₂Si₀_.₅₁₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃₅ || 20 °C (68 °F) to 555 °C (1031 °F)
    RHO       :    x = 0.02 || Mg₂Si₀_.₅₃Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂ || 20 °C (68 °F) to 530 °C (986 °F)
    RHO       :    x = 0.025 || Mg₂Si₀_.₅₂₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂₅ || 20 °C (68 °F) to 550 °C (1022 °F)
    RHO       :    x = 0.03 || Mg₂Si₀_.₅₂Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃ || 20 °C (68 °F) to 550 °C (1022 °F)
    RHO       :    x = 0.035 || Mg₂Si₀_.₅₁₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃₅ || 20 °C (68 °F) to 555 °C (1031 °F)
    SIGMA    :    x = 0.02 || Mg₂Si₀_.₅₃Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂ || 20 °C (68 °F) to 530 °C (986 °F)
    SIGMA    :    x = 0.025 || Mg₂Si₀_.₅₂₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂₅ || 20 °C (68 °F) to 550 °C (1022 °F)
    SIGMA    :    x = 0.03 || Mg₂Si₀_.₅₂Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃ || 20 °C (68 °F) to 550 °C (1022 °F)
    SIGMA    :    x = 0.035 || Mg₂Si₀_.₅₁₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃₅ || 20 °C (68 °F) to 555 °C (1031 °F)
    S         :    x = 0.02 || Mg₂Si₀_.₅₃Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂ || 20 °C (68 °F) to 530 °C (986 °F)
    S         :    x = 0.025 || Mg₂Si₀_.₅₂₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₂₅ || 20 °C (68 °F) to 500 °C (932 °F)
    S         :    x = 0.03 || Mg₂Si₀_.₅₂Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃ || 20 °C (68 °F) to 550 °C (1022 °F)
    S         :    x = 0.035 || Mg₂Si₀_.₅₁₅Sn₀_.₄Ge₀_.₀₅Bi₀_.₀₃₅ || 20 °C (68 °F) to 555 °C (1031 °F)

return to listing

Mg₂Sn + 6.7 wt% Mg (New)

    TC        :    as-cast || 20 °C (68 °F) to 450 °C (842 °F)
    TC        :    compressed at 400 °C (752 °F) || 20 °C (68 °F) to 450 °C (842 °F)
    RHO       :    as-cast || 20 °C (68 °F) to 450 °C (842 °F)
    RHO       :    compressed at 400 °C (752 °F) || 20 °C (68 °F) to 450 °C (842 °F)
    SIGMA    :    as-cast || 20 °C (68 °F) to 450 °C (842 °F)
    SIGMA    :    compressed at 400 °C (752 °F) || 20 °C (68 °F) to 450 °C (842 °F)
    S         :    as-cast || 20 °C (68 °F) to 450 °C (842 °F)
    S         :    compressed at 400 °C (752 °F) || 20 °C (68 °F) to 450 °C (842 °F)

return to listing

MgV₂O₆ (New)

    DLL       :    solid || polycrystal || 20 °C (68 °F) to 500 °C (932 °F)
    DLL       :    solid || a-axis || 20 °C (68 °F) to 500 °C (932 °F)
    DLL       :    solid || b-axis || 20 °C (68 °F) to 500 °C (932 °F)
    DLL       :    solid || c-axis || 20 °C (68 °F) to 500 °C (932 °F)
    MTE       :    solid || polycrystal || 20 °C (68 °F) to 500 °C (932 °F)
    MTE       :    solid || a-axis || 20 °C (68 °F) to 500 °C (932 °F)
    MTE       :    solid || b-axis || 20 °C (68 °F) to 500 °C (932 °F)
    MTE       :    solid || c-axis || 20 °C (68 °F) to 500 °C (932 °F)
    CTE       :    solid || polycrystal || 20 °C (68 °F) to 500 °C (932 °F)
    CTE       :    solid || a-axis || 20 °C (68 °F) to 500 °C (932 °F)
    CTE       :    solid || b-axis || 20 °C (68 °F) to 500 °C (932 °F)
    CTE       :    solid || c-axis || 20 °C (68 °F) to 500 °C (932 °F)
    D         :    solid || 20 °C (68 °F) to 500 °C (932 °F)
    SH        :    solid || 20 °C (68 °F) to 500 °C (932 °F)
    HC        :    solid || 20 °C (68 °F) to 500 °C (932 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    K     (*):    solid || room temperature value

return to listing

20MnMoNi5-5 (New)

    FSN       :    tempered martensite || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, stress amplitude || 2.4 x 10³ cycles to 1.7 x 10⁵ cycles
    FSN       :    tempered martensite, effect of surface roughness || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, N3 ISO roughnessstress amplitude || 1.1 x 10⁴ cycles to 7 x 10⁵ cycles
    FSN       :    tempered martensite, effect of surface roughness || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, N5 ISO roughnessstress amplitude || 2.1 x 10⁴ cycles to 8.5 x 10⁵ cycles
    FSN       :    tempered martensite, effect of surface roughness || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, N7 ISO roughnessstress amplitude || 2.2 x 10⁴ cycles to 1.7 x 10⁵ cycles
    FSN       :    tempered martensite, effect of surface roughness || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, N8 ISO roughnessstress amplitude || 1.7 x 10⁴ cycles to 2.3 x 10⁵ cycles
    FSN       :    tempered martensite, effect of surface roughness || tested at 20 °C (68 °F), R = -1, axial, 5 Hz, N9 ISO roughnessstress amplitude || 1.1 x 10⁴ cycles to 2 x 10⁵ cycles

return to listing

Monel 400

CRR (N): mill-annealed 12.7 mm (0.5 inch) rod, at room temperature: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) || tested at 538 °C (1000 °F) || 3.97 x 10^-⁹/s to 1.62 x 10^-⁶/s
CRR (N): mill-annealed 12.7 mm (0.5 inch) rod, at room temperature: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) || tested at 649 °C (1200 °F) || 1.52 x 10^-⁹/s to 1.25 x 10^-⁵/s

return to listing

Nb - 2 Cr (wt %) (New)

    D     (*):    solid || room temperature value
    UTS       :    recrystallized || 650 °C (1202 °F) to 1316 °C (2401 °F)
    YS        :    recrystallized || 650 °C (1202 °F) to 1316 °C (2401 °F)
    CRR       :    recrystallized || tested at 650 °C (1202 °F) || 1 x 10^-⁹/s to 2.78 x 10^-⁷/s
    CRR       :    recrystallized || tested at 800 °C (1472 °F) || 2.75 x 10^-⁹/s to 6.6 x 10^-⁷/s
    CRR       :    recrystallized || tested at 1000 °C (1832 °F) || 2.75 x 10^-⁹/s to 2.78 x 10^-⁷/s

return to listing

Nb - 5 V (wt %) (B-33)

    UTS    (N):    recrystallized 1 h at 1150 °C (2102 °F) || 650 °C (1202 °F) to 1316 °C (2401 °F)
    YS     (N):    recrystallized 1 h at 1150 °C (2102 °F) || 650 °C (1202 °F) to 1316 °C (2401 °F)
    CRR    (N):    recrystallized || tested at 650 °C (1202 °F) || 2.75 x 10^-⁹/s to 3.69 x 10^-⁷/s
    CRR    (N):    recrystallized || tested at 800 °C (1472 °F) || 2.2 x 10^-¹⁰/s to 1.71 x 10^-⁶/s
    CRR    (N):    recrystallized || tested at 1000 °C (1832 °F) || 5.3 x 10^-⁹/s to 2.78 x 10^-⁷/s

return to listing

Nb - 3 Zr (wt %) (New)

    D     (*):    solid || room temperature value
    UTS       :    recrystallized || 650 °C (1202 °F) to 1316 °C (2401 °F)
    YS        :    recrystallized || 650 °C (1202 °F) to 1316 °C (2401 °F)
    CRR       :    recrystallized || tested at 800 °C (1472 °F) || 2.34 x 10^-⁹/s to 2.67 x 10^-⁶/s
    CRR       :    recrystallized || tested at 1000 °C (1832 °F) || 4.6 x 10^-⁹/s to 2.01 x 10^-⁶/s

return to listing

NbCl₅

RHO (N): liquid || 207 °C (404 °F) to 247 °C (476 °F)
SIGMA (N): liquid || 207 °C (404 °F) to 247 °C (476 °F)

return to listing

Nd₀_.₇Ca₀_.₃CoO₃ (New)

    RHO       :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    SIGMA    :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    S         :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)

return to listing

Ni-Ti (Nitinol)

    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, parallel to build direction, 8 x 10^-⁵/s || 0 to 0.31 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), annealed, parallel to build direction, 8 x 10^-⁵/s || 0 to 0.23 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), aged, parallel to build direction, 8 x 10^-⁵/s || 0 to 0.29 mm/mm strain
    UTS   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    UTS   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), annealed, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    UTS   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), aged, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    YS    (N*):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    YS    (N*):    laser powder bed fusion || tested at 20 °C (68 °F), annealed, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    YS    (N*):    laser powder bed fusion || tested at 20 °C (68 °F), aged, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    %El   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), as-built, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    %El   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), annealed, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    %El   (N*):    laser powder bed fusion || tested at 20 °C (68 °F), aged, parallel to build direction, 8 x 10^-⁵/s || room temperature value
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, as-built, parallel to build direction, maximum stress || 200 cycles to 5 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, annealed, parallel to build direction, maximum stress || 5.3 x 10³ cycles to 2 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, annealed & polished, parallel to build direction, maximum stress || 1 x 10⁴ cycles to 2 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, aged, parallel to build direction, maximum stress || 5.7 x 10³ cycles to 1 x 10⁵ cycles
    FSN    (N):    laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, aged & polished, parallel to build direction, maximum stress || 1 x 10⁴ cycles to 3.6 x 10⁵ cycles

return to listing

Nickel TD

CRR (N): stress-relieved 12.7 mm (0.5 inch) bar || tested at 1093 °C (2000 °F), parallel to extrusion direction || 1.6 x 10^-⁹/s to 1.46 x 10^-⁸/s

return to listing

NZ31 (New)

    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, F temper || 0 to 0.49 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T41 temper || 0 to 0.125 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T42 temper || 0 to 0.177 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T61 temper || 0 to 0.43 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T62 temper || 0 to 0.36 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T63 temper || 0 to 0.52 mm/mm strain
    SSC       :    sand cast || tested at 20 °C (68 °F), 0.002/s, T64 temper || 0 to 0.42 mm/mm strain
    UTS   (*):    sand cast || F temper || room temperature value
    UTS   (*):    sand cast || T41 temper || room temperature value
    UTS   (*):    sand cast || T42 temper || room temperature value
    UTS   (*):    sand cast || T61 temper || room temperature value
    UTS   (*):    sand cast || T62 temper || room temperature value
    UTS   (*):    sand cast || T63 temper || room temperature value
    UTS   (*):    sand cast || T64 temper || room temperature value
    YS    (*):    sand cast || F temper || room temperature value
    YS    (*):    sand cast || T41 temper || room temperature value
    YS    (*):    sand cast || T42 temper || room temperature value
    YS    (*):    sand cast || T61 temper || room temperature value
    YS    (*):    sand cast || T62 temper || room temperature value
    YS    (*):    sand cast || T63 temper || room temperature value
    YS    (*):    sand cast || T64 temper || room temperature value
    %El   (*):    sand cast || F temper || room temperature value
    %El   (*):    sand cast || T41 temper || room temperature value
    %El   (*):    sand cast || T42 temper || room temperature value
    %El   (*):    sand cast || T61 temper || room temperature value
    %El   (*):    sand cast || T62 temper || room temperature value
    %El   (*):    sand cast || T63 temper || room temperature value
    %El   (*):    sand cast || T64 temper || room temperature value

return to listing

P91 (9 Cr - 1 Mo (wt %))

    FSN    (N):    tempered martensite || tested at 600 °C (1112 °F), R = -1, axial, 0.05 Hz, stress amplitude || 970 cycles to 1.45 x 10⁴ cycles
    FSN    (N):    tempered martensite || tested at 620 °C (1148 °F), R = -1, axial, 0.05 Hz, stress amplitude || 1.34 x 10³ cycles to 9.35 x 10³ cycles
    FSN    (N):    tempered martensite || tested at 635 °C (1175 °F), R = -1, axial, 0.05 Hz, stress amplitude || 935 cycles to 1 x 10⁵ cycles
    FSN    (N):    tempered martensite || tested at 650 °C (1202 °F), R = -1, axial, 0.05 Hz, stress amplitude || 450 cycles to 4.31 x 10³ cycles
    FSN    (N):    tempered martensite || tested at 600 °C (1112 °F), R = -1, axial, 5 Hz, stress amplitude || 2.2 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    tempered martensite || tested at 620 °C (1148 °F), R = -1, axial, 5 Hz, stress amplitude || 6 x 10⁴ cycles to 1.25 x 10⁶ cycles
    FSN    (N):    tempered martensite || tested at 635 °C (1175 °F), R = -1, axial, 5 Hz, stress amplitude || 4.25 x 10⁴ cycles to 5.3 x 10⁵ cycles
    FSN    (N):    tempered martensite || tested at 650 °C (1202 °F), R = -1, axial, 5 Hz, stress amplitude || 3.1 x 10⁴ cycles to 1 x 10⁷ cycles
    CRR    (N):    minimum creep rate || tested at 500 °C (932 °F) || 1.39 x 10^-¹¹/s to 9.35 x 10^-⁷/s
    CRR    (N):    minimum creep rate || tested at 550 °C (1022 °F) || 1.57 x 10^-¹⁰/s to 1.36 x 10^-⁷/s
    CRR    (N):    minimum creep rate || tested at 600 °C (1112 °F) || 6.35 x 10^-¹¹/s to 2.22 x 10^-⁸/s
    CRR    (N):    minimum creep rate || tested at 625 °C (1157 °F) || 1 x 10^-⁹/s to 9.79 x 10^-⁹/s

return to listing

PbWO₄

    E     (N*):    solid || room temperature value
    G     (N*):    solid || room temperature value
    v     (N*):    solid || room temperature value
    K     (N*):    solid || room temperature value

return to listing

PLA

SSC (N): injection molded || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s, tested to fracture || 0 to 3.45 x 10^-³ mm/mm strain
SSCC (N): injection molded || tested at 20 °C (68 °F), 2.5 x 10^-⁴/s || 0 to 0.23 mm/mm strain

return to listing

Pr₀_.₉Ca₀_.₁CoO₃ (New)

S : solid || -263.1 °C (-441.7 °F) to 27 °C (80 °F)

return to listing

Pr₀_.₇Ca₀_.₃CoO₃ (New)

    TC        :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    RHO       :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    SIGMA    :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    S         :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)

return to listing

(Pr₀_.₈₅Y₀_.₁₅)₀_.₇Ca₀_.₃CoO₃ (New)

    TC        :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    RHO       :    solid || -267.1 °C (-448.9 °F) to 27 °C (80 °F)
    SIGMA    :    solid || -267.1 °C (-448.9 °F) to 27 °C (80 °F)
    S         :    solid || -257.1 °C (-430.9 °F) to 27 °C (80 °F)

return to listing

(Pr₀_.₉₂₅Y₀_.₀₇₅)₀_.₇Ca₀_.₃CoO₃ (New)

    TC        :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    RHO       :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    SIGMA    :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)
    S         :    solid || -269.1 °C (-452.5 °F) to 27 °C (80 °F)

return to listing

QE22

    SH     (N):    solid || 20 °C (68 °F) to 500 °C (932 °F)
    SH     (N):    liquid || 640 °C (1184 °F) to 800 °C (1472 °F)
    TD     (R):    solid || F temper || 20 °C (68 °F) to 250 °C (482 °F)
    TD     (R):    solid || T6 temper || 20 °C (68 °F) to 250 °C (482 °F)
    SSC    (N):    25 mm (0.984 inch) thick plate || tested at 20 °C (68 °F), 0.0033/s, solution treated 8 h at 525 °C (977 °F) || 0 to 0.237 mm/mm strain
    SSC    (N):    25 mm (0.984 inch) thick plate || tested at 20 °C (68 °F), 0.0033/s, under aged || 0 to 0.111 mm/mm strain
    SSC    (N):    25 mm (0.984 inch) thick plate || tested at 20 °C (68 °F), 0.0033/s, peak aged || 0 to 0.1 mm/mm strain
    SSC    (N):    25 mm (0.984 inch) thick plate || tested at 20 °C (68 °F), 0.0033/s, over aged || 0 to 0.15 mm/mm strain
    UTS   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, solution treated 8 h at 525 °C (977 °F) || room temperature value
    UTS   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, under aged || room temperature value
    UTS   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, peak aged || room temperature value
    UTS   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, over aged || room temperature value
    YS    (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, solution treated 8 h at 525 °C (977 °F) || room temperature value
    YS    (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, under aged || room temperature value
    YS    (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, peak aged || room temperature value
    YS    (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, over aged || room temperature value
    %El   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, solution treated 8 h at 525 °C (977 °F) || room temperature value
    %El   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, under aged || room temperature value
    %El   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, peak aged || room temperature value
    %El   (N*):    25 mm (0.984 inch) thick plate || 0.0033/s, over aged || room temperature value

return to listing

RbCl

    E      (R):    solid || -269.1 °C (-452.5 °F) to 227 °C (440 °F)
    G      (R):    solid || -269.1 °C (-452.5 °F) to 227 °C (440 °F)
    v      (R):    solid || -269.1 °C (-452.5 °F) to 227 °C (440 °F)
    K      (R):    solid || -269.1 °C (-452.5 °F) to 227 °C (440 °F)

return to listing

Rene 95

CRR (N): aged || tested at 649 °C (1200 °F), in tension || 7.5 x 10^-⁹/s to 2.72 x 10^-⁵/s
CRR (N): aged || tested at 649 °C (1200 °F), in compression || 2.65 x 10^-⁸/s to 6.01 x 10^-⁵/s

return to listing

Rhenium

    SSCC   (N):    0.003/s || tested at 1150 °C (2102 °F) || 0 to 0.4 mm/mm strain
    SSCC   (N):    0.003/s || tested at 1350 °C (2462 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.003/s || tested at 1550 °C (2822 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.03/s || tested at 1150 °C (2102 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.03/s || tested at 1350 °C (2462 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.03/s || tested at 1550 °C (2822 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.3/s || tested at 1150 °C (2102 °F) || 0 to 0.4 mm/mm strain
    SSCC   (N):    0.3/s || tested at 1350 °C (2462 °F) || 0 to 0.41 mm/mm strain
    SSCC   (N):    0.3/s || tested at 1550 °C (2822 °F) || 0 to 0.41 mm/mm strain

return to listing

S690 / S690QL

    FSN    (N):    quenched and tempered || tested at 20 °C (68 °F), R = -1, axial, ultrasonic, maximum stress || 2 x 10⁵ cycles to unknown strain rate cycles
    FSN    (N):    quenched and tempered || tested at 20 °C (68 °F), R = -1, K_t = 1.15, axial, ultrasonic, maximum stress || 5 x 10⁵ cycles to 2 x 10⁹ cycles
    FSN    (N):    quenched and tempered || tested at 20 °C (68 °F), R = -1, K_t = 1.33, axial, ultrasonic, maximum stress || 4.7 x 10⁵ cycles to 3 x 10⁹ cycles

return to listing

S700

D (N*): solid || room temperature value

return to listing

SAE 9254 (New)

    D     (*):    solid || room temperature value
    E     (*):    solid || room temperature value
    UTS   (*):    solid || room temperature value
    YS    (*):    solid || room temperature value
    FSN       :    quenched & tempered || tested at 20 °C (68 °F), R = -1, torsional, load increase test, maximum stress || 1.8 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

Scalmalloy

FSN (N): laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, maximum stress || 1.1 x 10⁴ cycles to 1 x 10⁸ cycles

return to listing

Selectron 44 polyester

    CRR    (N):    annealed sheet || tested at 27 °C (80 °F) || 1 x 10^-⁹/s to 3.53 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 71 °C (160 °F) || 1.97 x 10^-⁹/s to 5.74 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 93 °C (200 °F) || 4.83 x 10^-¹⁰/s to 6 x 10^-⁷/s

return to listing

Shot-earth 772 (New)

    D     (*):    solid || room temperature value
    FS    (*):    solid || room temperature value
    UCS   (*):    solid || room temperature value
    FSN       :    3-point bending || tested at 23 °C (73 °F), R = 0, stress amplitude || 2.38 x 10⁴ cycles to 5 x 10⁶ cycles
    FSN       :    compression || tested at 23 °C (73 °F), R = 0, stress amplitude || 1.7 x 10³ cycles to 2 x 10⁶ cycles

return to listing

SiC (alpha)

    CRR    (N):    single crystal, 45 degrees from the c-axis || tested at 900 °C (1652 °F) || 7.29 x 10^-⁷/s to 2.5 x 10^-⁶/s
    CRR    (N):    single crystal, 45 degrees from the c-axis || tested at 1000 °C (1832 °F) || 2.65 x 10^-⁷/s to 2.8 x 10^-⁵/s
    CRR    (N):    single crystal, 45 degrees from the c-axis || tested at 1100 °C (2012 °F) || 8.32 x 10^-⁷/s to 1.42 x 10^-⁵/s
    CRR    (N):    single crystal, 45 degrees from the c-axis || tested at 1200 °C (2192 °F) || 1.78 x 10^-⁵/s to 1.36 x 10^-⁴/s
    CRR    (N):    single crystal, c-axis || tested at 1650 °C (3002 °F) || 9.15 x 10^-⁹/s to 6.7 x 10^-⁸/s
    CRR    (N):    single crystal, c-axis || tested at 1750 °C (3182 °F) || 1.5 x 10^-⁸/s to 3.08 x 10^-⁶/s
    CRR    (N):    single crystal, c-axis || tested at 1850 °C (3362 °F) || 3.63 x 10^-⁸/s to 1.42 x 10^-⁷/s

return to listing

Silver

NE (N): solid || polished || -193.1 °C (-315.7 °F) to 27 °C (80 °F)

return to listing

60 Sn - 40 Pb (wt %)

    YSC    (N):    casting || 3.79 x 10^-⁵/s strain rate || -30 °C (-22 °F) to 125 °C (257 °F)
    YSC    (N):    casting || 8.33 x 10^-⁴/s strain rate || -55 °C (-67 °F) to 125 °C (257 °F)
    CRS    (N):    2% total strain || tested at 0 °C (32 °F) || 0.3 h to 1.4 h
    CRS    (N):    2% total strain || tested at 23 °C (73 °F) || 0.16 h to 0.5 h
    CRS    (N):    2% total strain || tested at 75 °C (167 °F) || 0.008 h to 0.5 h
    CRS    (N):    2% total strain || tested at 125 °C (257 °F) || 0.11 h to 0.36 h
    CRS    (N):    3% total strain || tested at -30 °C (-22 °F) || 0.15 h to 0.8 h
    CRS    (N):    3% total strain || tested at 0 °C (32 °F) || 0.8 h to 3.1 h
    CRS    (N):    3% total strain || tested at 23 °C (73 °F) || 0.27 h to 0.21 h
    CRS    (N):    3% total strain || tested at 75 °C (167 °F) || 0.18 h to 0.83 h
    CRS    (N):    3% total strain || tested at 125 °C (257 °F) || 0.175 h to 0.71 h
    CRS    (N):    5% total strain || tested at -30 °C (-22 °F) || 0.5 h to 2.5 h
    CRS    (N):    5% total strain || tested at 0 °C (32 °F) || 0.2 h to 2.4 h
    CRS    (N):    5% total strain || tested at 23 °C (73 °F) || 0.57 h to 0.45 h
    CRS    (N):    5% total strain || tested at 75 °C (167 °F) || 0.41 h to 0.15 h
    CRS    (N):    5% total strain || tested at 125 °C (257 °F) || 0.3 h to 1.33 h
    CRS    (N):    7.5% total strain || tested at -30 °C (-22 °F) || 0.17 h to 5.2 h
    CRS    (N):    7.5% total strain || tested at 0 °C (32 °F) || 0.35 h to 4.5 h
    CRS    (N):    7.5% total strain || tested at 75 °C (167 °F) || 0.7 h to 0.24 h
    CRS    (N):    7.5% total strain || tested at 125 °C (257 °F) || 0.6 h to 2 h
    CRS    (N):    10% total strain || tested at -30 °C (-22 °F) || 0.4 h to 1.3 h
    CRS    (N):    10% total strain || tested at 0 °C (32 °F) || 0.01 h to 6.6 h
    CRS    (N):    10% total strain || tested at 75 °C (167 °F) || 0.95 h to 0.33 h
    CRS    (N):    10% total strain || tested at 125 °C (257 °F) || 0.8 h to 2.6 h
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.02 h || 0 to 0.148 mm/mm strain
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.05 h || 0 to 0.185 mm/mm strain
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.1 h || 0 to 0.219 mm/mm strain
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.2 h || 0 to 0.265 mm/mm strain
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.3 h || 0 to 0.32 mm/mm strain
    IC     (N):    tested at -55 °C (-67 °F), in compression, total strain || 0.4 h || 0 to 0.344 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.1 h || 0 to 0.139 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.2 h || 0 to 0.184 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.3 h || 0 to 0.22 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.4 h || 0 to 0.253 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.5 h || 0 to 0.286 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 0.75 h || 0 to 0.353 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 1 h || 0 to 0.152 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 2 h || 0 to 0.29 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 3 h || 0 to 0.269 mm/mm strain
    IC     (N):    tested at -30 °C (-22 °F), in compression, total strain || 4 h || 0 to 0.33 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.1 h || 0 to 0.223 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.2 h || 0 to 0.321 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.3 h || 0 to 0.68 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.4 h || 0 to 0.83 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.5 h || 0 to 0.97 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 0.75 h || 0 to 0.131 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 1 h || 0 to 0.163 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 2 h || 0 to 0.298 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 3 h || 0 to 0.57 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 4 h || 0 to 0.69 mm/mm strain
    IC     (N):    tested at 0 °C (32 °F), in compression, total strain || 6 h || 0 to 0.92 mm/mm strain
    IC     (N):    tested at 23 °C (73 °F), in compression, total strain || 0.1 h || 0 to 0.243 mm/mm strain
    IC     (N):    tested at 23 °C (73 °F), in compression, total strain || 0.2 h || 0 to 0.352 mm/mm strain
    IC     (N):    tested at 23 °C (73 °F), in compression, total strain || 0.3 h || 0 to 0.144 mm/mm strain
    IC     (N):    tested at 23 °C (73 °F), in compression, total strain || 0.4 h || 0 to 0.173 mm/mm strain
    IC     (N):    tested at 23 °C (73 °F), in compression, total strain || 0.5 h || 0 to 0.194 mm/mm strain
    IC     (N):    tested at 75 °C (167 °F), in compression, total strain || 0.05 h || 0 to 0.57 mm/mm strain
    IC     (N):    tested at 75 °C (167 °F), in compression, total strain || 0.1 h || 0 to 0.16 mm/mm strain
    IC     (N):    tested at 75 °C (167 °F), in compression, total strain || 0.2 h || 0 to 0.64 mm/mm strain
    IC     (N):    tested at 75 °C (167 °F), in compression, total strain || 0.3 h || 0 to 0.92 mm/mm strain
    IC     (N):    tested at 75 °C (167 °F), in compression, total strain || 0.4 h || 0 to 0.121 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 0.2 h || 0 to 0.32 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 0.3 h || 0 to 0.5 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 0.4 h || 0 to 0.67 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 0.5 h || 0 to 0.86 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 0.75 h || 0 to 0.14 mm/mm strain
    IC     (N):    tested at 125 °C (257 °F), in compression, total strain || 1 h || 0 to 0.28 mm/mm strain
    CRR    (N):    casting || tested at -55 °C (-67 °F), in compression || 3.2 x 10^-⁷/s to 1.1 x 10^-³/s
    CRR    (N):    casting || tested at -30 °C (-22 °F), in compression || 5.75 x 10^-⁷/s to 1.46 x 10^-³/s
    CRR    (N):    casting || tested at 0 °C (32 °F), in compression || 1.65 x 10^-⁶/s to 4.1 x 10^-⁴/s
    CRR    (N):    casting || tested at 23 °C (73 °F), in compression || 1.37 x 10^-⁶/s to 5.47 x 10^-⁴/s
    CRR    (N):    casting || tested at 75 °C (167 °F), in compression || 1.53 x 10^-⁶/s to 6.14 x 10^-³/s
    CRR    (N):    casting || tested at 125 °C (257 °F), in compression || 8.4 x 10^-⁶/s to 3.36 x 10^-³/s

return to listing

Spaghetti (New)

    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 60 °C (140 °F) in distilled water, tested to fracture, 30 mm/min || 0 to 0.78 mm/mm strain
    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 80 °C (176 °F) in distilled water, tested to fracture, 30 mm/min || 0 to 0.8 mm/mm strain
    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 100 °C (212 °F) in distilled water, tested to fracture, 30 mm/min || 0 to 0.83 mm/mm strain
    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 100 °C (212 °F) in 0.1 mol/L NaCl, tested to fracture, 30 mm/min || 0 to 0.8 mm/mm strain
    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 100 °C (212 °F) in 1 mol/L NaCl, tested to fracture, 30 mm/min || 0 to 0.75 mm/mm strain
    ESSC      :    moisture content of 1.7 kg-H₂O/kg-d.m. || tested at 20 °C (68 °F), rehydrated at 100 °C (212 °F) in 2 mol/L NaCl, tested to fracture, 30 mm/min || 0 to 0.63 mm/mm strain
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 60 °C (140 °F) in distilled water, 30 mm/min || room temperature value
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 80 °C (176 °F) in distilled water, 30 mm/min || room temperature value
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in distilled water, 30 mm/min || room temperature value
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 0.1 mol/L NaCl, 30 mm/min || room temperature value
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 1 mol/L NaCl, 30 mm/min || room temperature value
    UTS   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 2 mol/L NaCl, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 60 °C (140 °F) in distilled water, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 80 °C (176 °F) in distilled water, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in distilled water, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 0.1 mol/L NaCl, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 1 mol/L NaCl, 30 mm/min || room temperature value
    %El   (*):    moisture content of 1.7 kg-H₂O/kg-d.m. || rehydrated at 100 °C (212 °F) in 2 mol/L NaCl, 30 mm/min || room temperature value

return to listing

Spherical cast iron (EN-GJS-500-14 5.3109) (New)

    D     (*):    solid || room temperature value
    E     (*):    solid || room temperature value
    G     (*):    solid || room temperature value
    v     (*):    solid || room temperature value
    K     (*):    solid || room temperature value
    UTS   (*):    solid || room temperature value
    %El   (*):    solid || room temperature value
    FEN       :    UTS = 532 MPa (77.2 ksi) || tested at 20 °C (68 °F), R = -1, axial, total strain amplitude || 225 cycles to 9.4 x 10⁵ cycles
    FEN       :    UTS = 532 MPa (77.2 ksi) || tested at 20 °C (68 °F), R = -1, torsional, total strain amplitude || 290 cycles to 5 x 10⁵ cycles

return to listing

Ta - 10 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 10 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 1.16 x 10^-⁵/s to 3 x 10^-⁵/s

return to listing

Ta - 2.5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 18 h
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 19 h
    SR        :    recrystallized || Master curve (LMP) || 19.2 h to 27.2 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 6.6 x 10^-⁶/s to 8.75 x 10^-⁵/s
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 1.28 x 10^-⁵/s to 1.59 x 10^-⁴/s

return to listing

Ta - 5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 9 h
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 18 h
    SR        :    recrystallized || Master curve (LMP) || 16.8 h to 23.9 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 1.9 x 10^-⁵/s to 2.23 x 10^-⁵/s
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 1.4 x 10^-⁵/s to 1.9 x 10^-⁵/s

return to listing

Ta - 7.5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 16 h
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 1.73 x 10^-⁵/s to 2.2 x 10^-⁵/s

return to listing

Ta - 8 W - 2 Hf (wt %) (T-111)

    UTS    (N):    cold rolled 90% || stress relieved 1 h at 1093 °C (2000 °F) || -196.1 °C (-321.1 °F) to 1927 °C (3500 °F)
    UTS    (N):    cold rolled 90% || recrystallized 1 h at 1649 °C (3000 °F) || -269.1 °C (-452.5 °F) to 1927 °C (3500 °F)
    UTS    (N):    warm rolled 95% || stress relieved 1 h at 1093 °C (2000 °F) || -196.1 °C (-321.1 °F) to 1649 °C (3000 °F)
    YS     (N):    cold rolled 90% || stress relieved 1 h at 1093 °C (2000 °F) || -269.1 °C (-452.5 °F) to 1927 °C (3500 °F)
    YS     (N):    cold rolled 90% || recrystallized 1 h at 1649 °C (3000 °F) || -196.1 °C (-321.1 °F) to 1927 °C (3500 °F)
    YS     (N):    warm rolled 95% || stress relieved 1 h at 1093 °C (2000 °F) || -196.1 °C (-321.1 °F) to 1649 °C (3000 °F)
    %El    (N):    cold rolled 90% || stress relieved 1 h at 1093 °C (2000 °F) || -269.1 °C (-452.5 °F) to 1927 °C (3500 °F)
    %El    (N):    cold rolled 90% || recrystallized 1 h at 1649 °C (3000 °F) || -269.1 °C (-452.5 °F) to 1927 °C (3500 °F)
    %El    (N):    warm rolled 95% || stress relieved 1 h at 1093 °C (2000 °F) || -196.1 °C (-321.1 °F) to 1649 °C (3000 °F)
    CRR    (N):    cold worked sheet || tested at 1204 °C (2200 °F) || 4.6 x 10^-⁸/s to 3.5 x 10^-⁶/s
    CRR    (N):    cold worked sheet || tested at 1427 °C (2600 °F) || 5.6 x 10^-⁹/s to 1.26 x 10^-⁵/s
    CRR    (N):    cold worked sheet || tested at 1649 °C (3000 °F) || 1.9 x 10^-⁷/s to 1.2 x 10^-⁴/s

return to listing

Ta - 10 W - 2.5 Hf (wt %) (T-222) (New)

    D     (*):    solid || room temperature value
    UTS       :    reduced 90% || stress relieved 1 h at 1093 °C (2000 °F) || 982 °C (1799 °F) to 1205 °C (2201 °F)
    UTS       :    reduced 90% || recrystallized 1 h at 1649 °C (3000 °F) || -196.1 °C (-321.1 °F) to 1927 °C (3500 °F)
    YS        :    reduced 90% || stress relieved 1 h at 1093 °C (2000 °F) || 982 °C (1799 °F) to 1205 °C (2201 °F)
    YS        :    reduced 90% || recrystallized 1 h at 1649 °C (3000 °F) || -196.1 °C (-321.1 °F) to 1927 °C (3500 °F)
    %El       :    reduced 90% || stress relieved 1 h at 1093 °C (2000 °F) || 982 °C (1799 °F) to 1205 °C (2201 °F)
    %El       :    reduced 90% || recrystallized 1 h at 1649 °C (3000 °F) || -196.1 °C (-321.1 °F) to 1927 °C (3500 °F)

return to listing

Ta - 5 W - 2.5 Mo - 0.5 Zr - 0.07 C (wt %) (New)

    D     (*):    solid || room temperature value
    UTS       :    recrystallized || 1477 °C (2690 °F) to 1917 °C (3482 °F)
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 21 h
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 12 h
    SR        :    recrystallized || Master curve (LMP) || 25.2 h to 33.8 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 1.61 x 10^-⁶/s to 3.1 x 10^-⁵/s
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 7.36 x 10^-⁶/s to 2.9 x 10^-⁴/s

return to listing

Ta - 10 W - 2.5 Mo (wt %)

    D     (N*):    solid || room temperature value
    UTS    (N):    1.02 mm (0.04 inch) sheet || annealed 1 h at 1699 °C (3090 °F) || 1482 °C (2699 °F) to 1927 °C (3500 °F)
    YS     (N):    1.02 mm (0.04 inch) sheet || annealed 1 h at 1699 °C (3090 °F) || 1482 °C (2699 °F) to 1927 °C (3500 °F)
    SR     (N):    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 29 h
    SR     (N):    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 16 h
    SR     (N):    recrystallized || Master curve (LMP) || 20.1 h to 29.5 h
    CRR    (N):    recrystallized || tested at 1482 °C (2700 °F) || 1.38 x 10^-⁶/s to 7.92 x 10^-⁵/s
    CRR    (N):    recrystallized || tested at 1927 °C (3500 °F) || 7.4 x 10^-⁶/s to 2.57 x 10^-⁴/s

return to listing

Ta - 5 W - 5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 21 h
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 12 h
    SR        :    recrystallized || Master curve (LMP) || 22.7 h to 31.7 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 5.8 x 10^-⁶/s to 9.22 x 10^-⁶/s
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 1 x 10^-⁵/s to 1.75 x 10^-⁵/s

return to listing

Ta - 5 W - 2.5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    UTS       :    annealed 1 h at 1399 °C (2550 °F) || 1207 °C (2204 °F) to 1927 °C (3500 °F)
    YS        :    annealed 1 h at 1399 °C (2550 °F) || 1207 °C (2204 °F) to 1927 °C (3500 °F)
    SR        :    annealed 1 h at 1399 °C (2550 °F) || tested at 1482 °C (2700 °F) || 0.1 h to 27 h
    SR        :    annealed 1 h at 1399 °C (2550 °F) || tested at 1927 °C (3500 °F) || 0.1 h to 38 h
    SR        :    annealed 1 h at 1399 °C (2550 °F) || Master curve (LMP) || 24.1 h to 34.3 h
    CRR       :    annealed 1 h at 1399 °C (2550 °F) || tested at 1482 °C (2700 °F) || 1.32 x 10^-⁵/s to 1.52 x 10^-⁵/s
    CRR       :    annealed 1 h at 1399 °C (2550 °F) || tested at 1927 °C (3500 °F) || 7.08 x 10^-⁶/s to 4.52 x 10^-⁴/s

return to listing

Ta - 7.5 W - 2.5 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 24 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 4.63 x 10^-⁶/s to 1.59 x 10^-⁵/s

return to listing

Ta - 5 W (wt %)

    SR     (N):    recrystallized || tested at 1482 °C (2700 °F) || 1.1 h to 33 h
    SR     (N):    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 20 h
    SR     (N):    recrystallized || Master curve (LMP) || 26.3 h to 37.4 h
    CRR    (N):    recrystallized || tested at 1482 °C (2700 °F) || 4.4 x 10^-⁶/s to 2.05 x 10^-⁵/s
    CRR    (N):    recrystallized || tested at 1927 °C (3500 °F) || 1.3 x 10^-⁵/s to 8.12 x 10^-⁴/s

return to listing

Ta - 10 W (wt %)

    SR     (N):    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 14 h
    SR     (N):    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 17 h
    SR     (N):    recrystallized || Master curve (LMP) || 21.3 h to 30.2 h
    CRR    (N):    recrystallized || tested at 1482 °C (2700 °F) || 9.7 x 10^-⁶/s to 1.47 x 10^-⁵/s
    CRR    (N):    recrystallized || tested at 1927 °C (3500 °F) || 2.02 x 10^-⁵/s to 1 x 10^-⁴/s
    CRR    (N):    cold worked || tested at 1204 °C (2200 °F) || 3.55 x 10^-⁹/s to 2.84 x 10^-⁶/s
    CRR    (N):    cold worked || tested at 1427 °C (2600 °F) || 6.2 x 10^-¹⁰/s to 3.5 x 10^-⁵/s
    CRR    (N):    cold worked || tested at 1649 °C (3000 °F) || 5 x 10^-⁹/s to 7.75 x 10^-⁶/s

return to listing

Ta - 20 W (wt %) (New)

    D     (*):    solid || room temperature value
    SR        :    recrystallized || tested at 1482 °C (2700 °F) || 0.1 h to 13.5 h
    SR        :    recrystallized || tested at 1927 °C (3500 °F) || 0.1 h to 13.5 h
    SR        :    recrystallized || Master curve (LMP) || 21.7 h to 29.8 h
    CRR       :    recrystallized || tested at 1482 °C (2700 °F) || 1.8 x 10^-⁵/s to 2.22 x 10^-⁵/s
    CRR       :    recrystallized || tested at 1927 °C (3500 °F) || 1.4 x 10^-⁵/s to 4.71 x 10^-⁵/s

return to listing

Tantalum

    CRR    (N):    recrystallized || tested at 1482 °C (2700 °F) || 6.95 x 10^-⁶/s to 1.34 x 10^-⁵/s
    CRR    (N):    cold worked || tested at 1204 °C (2200 °F) || 1.3 x 10^-⁷/s to 6.84 x 10^-⁶/s
    CRR    (N):    cold worked || tested at 1427 °C (2600 °F) || 1.3 x 10^-⁷/s to 1.28 x 10^-⁵/s
    CRR    (N):    cold worked || tested at 1649 °C (3000 °F) || 3.75 x 10^-⁸/s to 4.25 x 10^-⁶/s
    S      (N):    solid || 20 °C (68 °F) to 307 °C (584 °F)

return to listing

TD-NiCr

CRR (N): single-crystal || tested at 1093 °C (2000 °F), parallel to extrusion direction || 4 x 10^-⁹/s to 4.41 x 10^-⁶/s
CRR (N): single-crystal || tested at 1093 °C (2000 °F), long transverse direction || 1.5 x 10^-⁹/s to 5.21 x 10^-⁹/s

return to listing

ThO₂

    CRR    (N):    single crystal, [110] direction || tested at 1650 °C (3002 °F) || 1.37 x 10^-⁸/s to 1.45 x 10^-⁶/s
    CRR    (N):    single crystal, [110] direction || tested at 1750 °C (3182 °F) || 1.02 x 10^-⁷/s to 7.58 x 10^-⁶/s
    CRR    (N):    single crystal, [110] direction || tested at 1850 °C (3362 °F) || 4.58 x 10^-⁷/s to 4.78 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1650 °C (3002 °F) || 5.32 x 10^-⁹/s to 8.83 x 10^-⁶/s
    CRR    (N):    single crystal, [100] direction || tested at 1750 °C (3182 °F) || 4.31 x 10^-⁸/s to 5.93 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1850 °C (3362 °F) || 1.36 x 10^-⁷/s to 1.23 x 10^-⁴/s

return to listing

Ti - 4 Al - 3 Cu - 2 Fe - 4 V (wt %) (New)

SSC : powder metallurgy || tested at 20 °C (68 °F), 5 x 10^-⁴/s || 0 to 0.52 mm/mm strain

return to listing

Ti - 4 Al - 3 Cu - 2 Fe (wt %) (New)

SSC : powder metallurgy || tested at 20 °C (68 °F), 5 x 10^-⁴/s || 0 to 0.48 mm/mm strain

return to listing

Ti - 4 Al - 4 Mn (wt %)

    UTS    (N):    effect of interstitials, 0.02/s || as-received, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || annealed, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.025 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.09 C, 0.04 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 0.02/s || 0.17 C, 0.072 N (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 0.02/s || 0.02 C, 0.18 N, 0.179 O, 0.0073 H (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 0.02/s || 0.02 C, 0.26 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.015 C, 0.09 N, 0.129 O, 0.0024 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.03 C, 0.09 N, 0.15 O, 0.0069 H (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.18 C, 0.13 O, 0.0082 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || as-received, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || annealed, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.025 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.09 C, 0.04 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.17 C, 0.072 N (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 2/s || 0.02 C, 0.18 N, 0.179 O, 0.0073 H (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.26 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.015 C, 0.09 N, 0.129 O, 0.0024 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.03 C, 0.09 N, 0.15 O, 0.0069 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.18 C, 0.13 O, 0.0082 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    %El   (N*):    effect of interstitials, 0.02/s || annealed, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || room temperature value
    %El   (N*):    effect of interstitials, 2/s || as-received, 0.15 C, 0.008 N, 0.097 O, 0.0016 H (wt %) || room temperature value
    %El   (N*):    effect of interstitials, 2/s || 0.09 C, 0.04 N (wt %) || room temperature value
    CRR    (N):    STA condition, bar stock || tested at 371 °C (700 °F) || 6 x 10^-¹¹/s to 5.56 x 10^-⁷/s
    CRR    (N):    STA condition, bar stock || tested at 454 °C (850 °F) || 2 x 10^-⁹/s to 9.12 x 10^-⁷/s
    CRR    (N):    STA condition, bar stock || tested at 538 °C (1000 °F) || 4.6 x 10^-⁹/s to 1.33 x 10^-⁶/s

return to listing

Ti - 3.3 Al - 2.8 Mo - 1.2 V (wt %) (New)

    SSCC      :    0.001/s || tested at 850 °C (1562 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    0.001/s || tested at 900 °C (1652 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    0.001/s || tested at 950 °C (1742 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    0.001/s || tested at 980 °C (1796 °F) || 0 to 0.63 mm/mm strain
    SSCC      :    0.001/s || tested at 1000 °C (1832 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.001/s || tested at 1050 °C (1922 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.001/s || tested at 1100 °C (2012 °F) || 0 to 0.69 mm/mm strain
    SSCC      :    0.01/s || tested at 850 °C (1562 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    0.01/s || tested at 900 °C (1652 °F) || 0 to 0.66 mm/mm strain
    SSCC      :    0.01/s || tested at 950 °C (1742 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    0.01/s || tested at 980 °C (1796 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    0.01/s || tested at 1000 °C (1832 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.01/s || tested at 1050 °C (1922 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.01/s || tested at 1100 °C (2012 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.1/s || tested at 850 °C (1562 °F) || 0 to 0.66 mm/mm strain
    SSCC      :    0.1/s || tested at 900 °C (1652 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    0.1/s || tested at 950 °C (1742 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    0.1/s || tested at 980 °C (1796 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    0.1/s || tested at 1000 °C (1832 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.1/s || tested at 1050 °C (1922 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    0.1/s || tested at 1100 °C (2012 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    1/s || tested at 850 °C (1562 °F) || 0 to 0.64 mm/mm strain
    SSCC      :    1/s || tested at 900 °C (1652 °F) || 0 to 0.64 mm/mm strain
    SSCC      :    1/s || tested at 950 °C (1742 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    1/s || tested at 980 °C (1796 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    1/s || tested at 1000 °C (1832 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    1/s || tested at 1050 °C (1922 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    1/s || tested at 1100 °C (2012 °F) || 0 to 0.67 mm/mm strain
    SSCC      :    10/s || tested at 850 °C (1562 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    10/s || tested at 900 °C (1652 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    10/s || tested at 950 °C (1742 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    10/s || tested at 980 °C (1796 °F) || 0 to 0.65 mm/mm strain
    SSCC      :    10/s || tested at 1000 °C (1832 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    10/s || tested at 1050 °C (1922 °F) || 0 to 0.68 mm/mm strain
    SSCC      :    10/s || tested at 1100 °C (2012 °F) || 0 to 0.69 mm/mm strain

return to listing

Ti - 7 Al - 3 Mo (wt %)

    D     (N*):    solid || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.01 C, 0.008 N, 0.081 O, 0.0169 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.025 C, 0.105 N (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.105 C, 0.205 N, 0.124 O, 0.012 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.12 C, 0.056 N, 0.117 O, 0.013 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.08 C, 0.066 N (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.02 C, 0.087 N, 0.26 O, 0.0038 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.01 C, 0.008 N, 0.081 O, 0.0169 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.025 C, 0.105 N (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.105 C, 0.205 N, 0.124 O, 0.012 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.12 C, 0.056 N, 0.117 O, 0.013 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.08 C, 0.066 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.087 N, 0.26 O, 0.0038 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.155 C, 0.0372 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)

return to listing

Ti - 8 Al - 2 Nb - 1 Mo - 1 V (wt %) (New)

    D     (*):    solid || room temperature value
    UTS   (*):    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || room temperature value
    UTS       :    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    YS    (*):    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || room temperature value
    YS        :    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    %El   (*):    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || room temperature value
    %El       :    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    CRS       :    0.1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 427 °C (800 °F) || 1.2 h to 220 h
    CRS       :    0.1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 538 °C (1000 °F) || 1 h to 430 h
    CRS       :    0.1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 593 °C (1100 °F) || 2 h to 390 h
    CRS       :    0.3% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 427 °C (800 °F) || 5 h to 1,350 h
    CRS       :    0.3% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 538 °C (1000 °F) || 3 h to 560 h
    CRS       :    0.3% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 593 °C (1100 °F) || 3.5 h to 1,070 h
    CRS       :    0.5% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 427 °C (800 °F) || 15 h to 4,250 h
    CRS       :    0.5% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 538 °C (1000 °F) || 5 h to 1,180 h
    CRS       :    0.5% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 593 °C (1100 °F) || 7.3 h to 1,160 h
    CRS       :    1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 427 °C (800 °F) || 45 h to 6,900 h
    CRS       :    1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 538 °C (1000 °F) || 10 h to 1,370 h
    CRS       :    1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 593 °C (1100 °F) || 16 h to 1,120 h
    CRS       :    1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || Master curve (LMP) || 11.2 h to 15.1 h
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 5 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 10 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 20 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 35 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 500 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 700 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 800 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 900 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 1,250 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 427 °C (800 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 1,500 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 3 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 5 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 35 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 500 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 700 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 800 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 900 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 5 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 35 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 500 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 700 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 800 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 900 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    CRR       :    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 538 °C (1000 °F) || 4.38 x 10^-⁹/s to 1.28 x 10^-⁷/s
    CRR       :    1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || tested at 593 °C (1100 °F) || 3.27 x 10^-¹⁰/s to 1.53 x 10^-⁷/s

return to listing

Ti - 5 Al - 2.5 Sn (Grade 6)

    TD     (R):    solid || -251.1 °C (-420.1 °F) to 945 °C (1733 °F)
    UTS    (N):    effect of interstitials, 0.02/s || as-forged, 0.02 C, 0.015 N, 0.052 O, 0.0033 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || annealed, none detected || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.065 C, 0.025 N, 0.097 O, 0.0057 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 0.02/s || 0.105 C, 0.155 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.02 C, 0.125 N, 0.116 O, 0.022 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.02 C, 0.04 N, 0.23 O, 0.0075 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 0.02/s || 0.03 C, 0.155 N, 0.214 O, 0.0097 H (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || as-forged, 0.02 C, 0.015 N, 0.052 O, 0.0033 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || annealed, none detected || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.065 C, 0.025 N, 0.097 O, 0.0057 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.105 C, 0.155 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.125 N, 0.116 O, 0.022 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.01 C, 0.22 N (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.04 N, 0.23 O, 0.0075 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.04 C, 0.235 N, 0.056 O (wt %) || room temperature value
    %El    (N):    effect of interstitials, 0.02/s || as-forged, 0.02 C, 0.015 N, 0.052 O, 0.0033 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    %El    (N):    effect of interstitials, 0.02/s || annealed, none detected || -73 °C (-100 °F) to 24 °C (75 °F)
    %El    (N):    effect of interstitials, 0.02/s || 0.065 C, 0.025 N, 0.097 O, 0.0057 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    %El   (N*):    effect of interstitials, 0.02/s || 0.105 C, 0.155 N (wt %) || room temperature value
    %El    (N):    effect of interstitials, 0.02/s || 0.02 C, 0.125 N, 0.116 O, 0.022 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    %El    (N):    effect of interstitials, 2/s || as-forged, 0.02 C, 0.015 N, 0.052 O, 0.0033 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    %El    (N):    effect of interstitials, 2/s || 0.065 C, 0.025 N, 0.097 O, 0.0057 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    %El   (N*):    effect of interstitials, 2/s || 0.105 C, 0.155 N (wt %) || room temperature value
    %El    (N):    effect of interstitials, 2/s || 0.02 C, 0.125 N, 0.116 O, 0.022 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    %El   (N*):    effect of interstitials, 2/s || 0.04 C, 0.235 N, 0.056 O (wt %) || room temperature value
    CRR    (N):    annealed sheet || tested at 427 °C (800 °F), in tension || 2.85 x 10^-⁹/s to 1.92 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 538 °C (1000 °F), in tension || 3.6 x 10^-⁹/s to 4.73 x 10^-⁶/s
    CRR    (N):    annealed sheet || tested at 427 °C (800 °F), in compression || 1.05 x 10^-⁸/s to 7.23 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 538 °C (1000 °F), in compression || 8.6 x 10^-⁹/s to 6.95 x 10^-⁷/s
    CRR    (N):    annealed 12.7 mm (0.5 inch) diameter bar || tested at 427 °C (800 °F) || 6.9 x 10^-⁹/s to 2.31 x 10^-⁶/s
    CRR    (N):    annealed 12.7 mm (0.5 inch) diameter bar || tested at 538 °C (1000 °F) || 1.66 x 10^-⁸/s to 4.45 x 10^-⁵/s
    S      (N):    solid || annealed || -267.1 °C (-448.9 °F) to 27 °C (80 °F)

return to listing

Ti - 8 Al - 1 Ta (wt %) (New)

    D     (*):    solid || room temperature value
    UTS   (*):    mill annealed sheet || room temperature value
    UTS       :    mill annealed sheet at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    YS    (*):    mill annealed sheet || room temperature value
    YS        :    mill annealed sheet at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    %El   (*):    mill annealed sheet || room temperature value
    %El       :    mill annealed sheet at high temperatures || 427 °C (800 °F) to 594 °C (1101 °F)
    CRS       :    0.1% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 0.1 h to 430 h
    CRS       :    0.1% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 0.3 h to 150 h
    CRS       :    0.3% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 0.6 h to 1,630 h
    CRS       :    0.3% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 1 h to 745 h
    CRS       :    0.5% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 1 h to 2,900 h
    CRS       :    0.5% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 1.5 h to 1,400 h
    CRS       :    1% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 3.8 h to 1,050 h
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 1 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 2 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 5 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 20 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 35 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 60 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 150 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 200 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 250 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 350 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 400 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 450 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 500 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 600 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 700 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 800 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 900 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 1,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 1,100 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 1,250 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 538 °C (1000 °F), plastic strain, mill annealed sheet || 1,500 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 1 h || 0 to 3 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 2 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 5 h || 0 to 5 x 10^-³ mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 10 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 20 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 35 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 60 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 100 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 150 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 200 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 250 h || 0 to 0.01 mm/mm strain
    IC        :    tested at 593 °C (1100 °F), plastic strain, mill annealed sheet || 300 h || 0 to 0.01 mm/mm strain
    CRR       :    mill annealed sheet || tested at 427 °C (800 °F) || 6.92 x 10^-¹⁰/s to 2.09 x 10^-⁹/s
    CRR       :    mill annealed sheet || tested at 538 °C (1000 °F) || 7.9 x 10^-¹⁰/s to 3.2 x 10^-⁷/s
    CRR       :    mill annealed sheet || tested at 593 °C (1100 °F) || 3 x 10^-¹⁰/s to 9.06 x 10^-⁷/s

return to listing

Ti - 6 Al - 4 V (Grade 5)

    DLL    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    MTE    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    CTE    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    D      (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)

return to listing

Ti - 6 Al - 4 V

    DLL    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    MTE    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    CTE    (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    D      (N):    liquid || 1650 °C (3002 °F) to 1900 °C (3452 °F)
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), HT-SB, 8.3 x 10^-⁴/s, vertical, Bologna et al. || 0 to 0.74 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), HT-SB-EP, 8.3 x 10^-⁴/s, vertical, Bologna et al. || 0 to 0.91 mm/mm strain
    SSC    (N):    laser powder bed fusion || tested at 20 °C (68 °F), HPHT-SB-EP, 8.3 x 10^-⁴/s, vertical, Bologna et al. || 0 to 0.65 mm/mm strain
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 5.6 microns, R_t = 27.4 microns, P_s = 90%, maximum stress || 3.7 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 2.5 microns, R_t = 14.7 microns, P_s = 90%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 90%, maximum stress || 2.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 90%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 90%, maximum stress || 3 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 90%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 5.6 microns, R_t = 27.4 microns, P_s = 50%, maximum stress || 3.7 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 2.5 microns, R_t = 14.7 microns, P_s = 50%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 50%, maximum stress || 2.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 50%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 50%, maximum stress || 3 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 50%, maximum stress || 1 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 5.6 microns, R_t = 27.4 microns, P_s = 10%, maximum stress || 3.7 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB, R_a = 2.5 microns, R_t = 14.7 microns, P_s = 10%, maximum stress || 7 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 10%, maximum stress || 2.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 10%, maximum stress || 5 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 3.3 microns, R_t = 13.9 microns, P_s = 10%, maximum stress || 3 x 10⁴ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, axial || tested at 20 °C (68 °F), R = 0.01, axial, HPHT-SB-EP, R_a = 1.7 microns, R_t = 10.5 microns, P_s = 10%, maximum stress || 1 x 10⁵ cycles to 1 x 10⁶ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, torsion || tested at 20 °C (68 °F), R = -1, torsion, as-built, stress amplitude || 3.2 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, torsion || tested at 20 °C (68 °F), R = -1, torsion, HCAF, stress amplitude || 4.4 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (N):    laser powder bed fusion, effect of surface roughness, torsion || tested at 20 °C (68 °F), R = -1, torsion, LCP, stress amplitude || 1 x 10⁵ cycles to 1 x 10⁸ cycles
    SR     (N):    mill annealed sheet || tested at 538 °C (1000 °F) || 1 h to 1,800 h
    SR     (R):    mill annealed sheet || Master curve (LMP) || 13.5 h to 18 h
    CRR    (N):    mill annealed sheet, supplier 1 || tested at 316 °C (600 °F) || 2.54 x 10^-¹⁰/s to 6.48 x 10^-⁹/s
    CRR    (N):    mill annealed sheet, supplier 1 || tested at 427 °C (800 °F) || 4.02 x 10^-¹⁰/s to 1 x 10^-⁵/s
    CRR    (N):    mill annealed sheet, supplier 1 || tested at 538 °C (1000 °F) || 6 x 10^-¹⁰/s to 2.15 x 10^-⁶/s
    CRR    (N):    mill annealed sheet, supplier 2, heat 25586 || tested at 316 °C (600 °F) || 4.5 x 10^-¹⁰/s to 2.28 x 10^-⁹/s
    CRR    (N):    mill annealed sheet, supplier 2, heat 25586 || tested at 427 °C (800 °F) || 1.65 x 10^-⁷/s to 1.8 x 10^-⁵/s
    CRR    (N):    mill annealed sheet, supplier 2, heat 25586 || tested at 538 °C (1000 °F) || 9.9 x 10^-¹⁰/s to 5.83 x 10^-⁷/s
    CRR    (N):    mill annealed sheet, all suppliers and heats || tested at 316 °C (600 °F) || 2.5 x 10^-¹⁰/s to 6.5 x 10^-⁹/s
    CRR    (N):    mill annealed sheet, all suppliers and heats || tested at 427 °C (800 °F) || 4 x 10^-¹⁰/s to 1.8 x 10^-⁵/s
    CRR    (N):    mill annealed sheet, all suppliers and heats || tested at 538 °C (1000 °F) || 6 x 10^-¹⁰/s to 7.23 x 10^-⁶/s
    CRR    (N):    treated at 927 °C (1700 °F), aged at 482 °C (900 °F) || tested at 427 °C (800 °F) || 3 x 10^-⁸/s to 1.69 x 10^-⁶/s
    CRR    (N):    treated at 927 °C (1700 °F), aged at 482 °C (900 °F) || tested at 538 °C (1000 °F) || 4.52 x 10^-⁸/s to 6.75 x 10^-⁷/s

return to listing

Ti - 6 Al (wt %)

    D     (N*):    solid || room temperature value
    E      (N):    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    E      (N):    annealed at 1107 °C (2025 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    E     (N*):    annealed at 1107 °C (2025 °F), air cooled || room temperature value
    E      (N):    as-forged + 10% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    E      (N):    as-forged + 17% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    E      (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    E      (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    E      (N):    average of all conditions || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    annealed at 1107 °C (2025 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS   (N*):    annealed at 1107 °C (2025 °F), air cooled || room temperature value
    UTS    (N):    as-forged + 10% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    as-forged + 17% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (N):    effect of interstitials, 0.02/s || annealed, 0.02 C, 0.018 N, 0.095 O, 0.011 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.02 C, 0.116 N, 0.12 O, 0.0145 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 0.02/s || 0.065 C, 0.06 N, 0.104 O, 0.015 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 0.02/s || 0.1 C, 0.201 N, 0.125 O, 0.0115 H (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 0.02/s || 0.15 C, 0.111 O, 0.012 H (wt %) || room temperature value
    UTS   (N*):    effect of interstitials, 0.02/s || 0.02 C, 0.086 N, 0.242 O, 0.0171 H (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 0.02/s || 0.22 C, 0.025 N, 0.12 O, 0.018 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || annealed, 0.02 C, 0.018 N, 0.095 O, 0.011 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.116 N, 0.12 O, 0.0145 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.065 C, 0.06 N, 0.104 O, 0.015 H (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.1 C, 0.201 N, 0.125 O, 0.0115 H (wt %) || -57 °C (-71 °F) to 24 °C (75 °F)
    UTS   (N*):    effect of interstitials, 2/s || 0.15 C, 0.111 O, 0.012 H (wt %) || room temperature value
    UTS    (N):    effect of interstitials, 2/s || 0.02 C, 0.086 N, 0.242 O, 0.0171 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS    (N):    effect of interstitials, 2/s || 0.22 C, 25 N, 0.12 O, 0.018 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    YS     (N):    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    annealed at 1107 °C (2025 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    YS    (N*):    annealed at 1107 °C (2025 °F), air cooled || room temperature value
    YS     (N):    as-forged + 10% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    as-forged + 17% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    annealed at 1107 °C (2025 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    %El   (N*):    annealed at 1107 °C (2025 °F), air cooled || room temperature value
    %El    (N):    as-forged + 10% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    as-forged + 17% cold work || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || 20 °C (68 °F) to 538 °C (1000 °F)
    SR     (N):    as-forged || tested at 538 °C (1000 °F) || 0.1 h to 105 h
    SR     (N):    annealed at 1107 °C (2025 °F), water quenched || tested at 538 °C (1000 °F) || 0.1 h to 320 h
    SR     (N):    as-forged + 10% cold work || tested at 538 °C (1000 °F) || 0.1 h to 180 h
    SR     (N):    as-forged + 17% cold work || tested at 538 °C (1000 °F) || 0.1 h to 125 h
    SR     (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || tested at 538 °C (1000 °F) || 0.1 h to 355 h
    SR     (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || tested at 538 °C (1000 °F) || 0.1 h to 455 h
    CRR    (N):    as-forged || tested at 538 °C (1000 °F) || 4.44 x 10^-⁸/s to 3.06 x 10^-⁷/s
    CRR    (N):    annealed at 1107 °C (2025 °F), water quenched || tested at 538 °C (1000 °F) || 1.05 x 10^-⁸/s to 6.39 x 10^-⁸/s
    CRR    (N):    as-forged + 10% cold work || tested at 538 °C (1000 °F) || 1.5 x 10^-⁸/s to 2.78 x 10^-⁷/s
    CRR    (N):    as-forged + 17% cold work || tested at 316 °C (600 °F) || 7.77 x 10^-¹⁰/s to 1.58 x 10^-⁹/s
    CRR    (N):    as-forged + 17% cold work || tested at 538 °C (1000 °F) || 2.33 x 10^-⁸/s to 2.75 x 10^-⁶/s
    CRR    (N):    as-forged, 17% cold work, 816 °C (1500 °F), air cool || tested at 538 °C (1000 °F) || 3.88 x 10^-⁹/s to 1.19 x 10^-⁷/s
    CRR    (N):    as-forged, 17% cold work, 927 °C (1700 °F), air cool || tested at 538 °C (1000 °F) || 1.16 x 10^-⁷/s to 2.31 x 10^-⁷/s

return to listing

Ti - 15 Cr (wt %) (New)

    D     (*):    solid || room temperature value
    UTS       :    effect of interstitials, 0.02/s || as-forged, 0.02 C, 0.017 N, 0.04 O, 0.0183 H (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS       :    effect of interstitials, 0.02/s || 0.055 C, 0.055 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS       :    effect of interstitials, 2/s || as-forged, 0.02 C, 0.017 N, 0.04 O, 0.0183 H (wt %) || -54 °C (-65 °F) to 24 °C (75 °F)
    UTS       :    effect of interstitials, 2/s || 0.055 C, 0.055 N (wt %) || -73 °C (-100 °F) to 24 °C (75 °F)
    UTS       :    effect of interstitials, 2/s || 0.01 C, 0.27 N, 0.0342 (wt %) || -196.1 °C (-321.1 °F) to 24 °C (75 °F)

return to listing

Ti - 15 Mo (wt %)

    SSCC   (N):    beta phase || tested at 25 °C (77 °F), 1.1 x 10^-³/s || 0 to 0.22 mm/mm strain
    SSCC   (N):    beta phase || tested at 150 °C (302 °F), 1.2 x 10^-³/s || 0 to 0.21 mm/mm strain
    SSCC   (N):    beta phase || tested at 300 °C (572 °F), 1.2 x 10^-³/s || 0 to 0.21 mm/mm strain
    SSCC   (N):    beta phase || tested at 450 °C (842 °F), 1.1 x 10^-³/s || 0 to 0.215 mm/mm strain
    SSCC   (N):    beta phase || tested at 25 °C (77 °F), 2983/s || 0 to 0.184 mm/mm strain
    SSCC   (N):    beta phase || tested at 150 °C (302 °F), 3383/s || 0 to 0.216 mm/mm strain
    SSCC   (N):    beta phase || tested at 300 °C (572 °F), 3475/s || 0 to 0.212 mm/mm strain
    SSCC   (N):    beta phase || tested at 450 °C (842 °F), 3608/s || 0 to 0.27 mm/mm strain

return to listing

Ti - 30 Mo (wt %) (New)

    D     (*):    solid || room temperature value
    E         :    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    E         :    annealed at 718 °C (1325 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    E         :    annealed at 816 °C (1500 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    E         :    annealed at 816 °C (1500 °F), water quenched, 746 °C (1375 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    E         :    annealed 1 h at 718 °C (1325 °F), water quenched, 3.3% cold work || 315 °C (599 °F) to 538 °C (1000 °F)
    E         :    average of all conditions || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS       :    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS       :    annealed at 718 °C (1325 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS       :    annealed at 816 °C (1500 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS       :    annealed at 816 °C (1500 °F), water quenched, 746 °C (1375 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS       :    annealed 1 h at 718 °C (1325 °F), water quenched, 3.3% cold work || 315 °C (599 °F) to 538 °C (1000 °F)
    YS        :    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    YS        :    annealed at 718 °C (1325 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    YS        :    annealed at 816 °C (1500 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    YS        :    annealed at 816 °C (1500 °F), water quenched, 746 °C (1375 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    YS        :    annealed 1 h at 718 °C (1325 °F), water quenched, 3.3% cold work || 315 °C (599 °F) to 538 °C (1000 °F)
    %El       :    as-forged || 20 °C (68 °F) to 538 °C (1000 °F)
    %El       :    annealed at 718 °C (1325 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    %El       :    annealed at 816 °C (1500 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    %El       :    annealed at 816 °C (1500 °F), water quenched, 746 °C (1375 °F), water quenched || 20 °C (68 °F) to 538 °C (1000 °F)
    %El       :    annealed 1 h at 718 °C (1325 °F), water quenched, 3.3% cold work || 315 °C (599 °F) to 538 °C (1000 °F)
    SR        :    as-forged || tested at 538 °C (1000 °F) || 0.1 h to 135 h
    SR        :    annealed at 718 °C (1325 °F), water quenched || 0.1 h to 1,145 h
    SR        :    annealed at 816 °C (1500 °F), water quenched || 0.1 h to 85 h
    SR        :    annealed at 816 °C (1500 °F), water quenched, 746 °C (1375 °F), water quenched || 0.1 h to 100 h
    CRR       :    as-forged || tested at 538 °C (1000 °F) || 1.27 x 10^-⁸/s to 2.45 x 10^-⁷/s
    CRR       :    annealed at 718 °C (1325 °F), water quenched || tested at 538 °C (1000 °F) || 6.94 x 10^-⁹/s to 1.95 x 10^-⁷/s
    CRR       :    combined data || tested at 538 °C (1000 °F) || 6.94 x 10^-⁹/s to 2.45 x 10^-⁷/s

return to listing

Ti - 16 V - 2.5 Al (wt %)

    UTS   (N*):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || room temperature value
    UTS    (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) at high temperatures || 371 °C (700 °F) to 482 °C (899 °F)
    YS    (N*):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || room temperature value
    YS     (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) at high temperatures || 371 °C (700 °F) to 482 °C (899 °F)
    %El   (N*):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || room temperature value
    %El    (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) at high temperatures || 371 °C (700 °F) to 482 °C (899 °F)
    SR     (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 371 °C (700 °F) || 20 h to 2,275 h
    SR     (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 427 °C (800 °F) || 70 h to 5,600 h
    SR     (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 482 °C (900 °F) || 1 h to 2,025 h
    SR     (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || Master curve (LMP) || 15.7 h to 19.9 h
    SR     (N):    both datasets combined || tested at 371 °C (700 °F) || 12 h to 2,275 h
    SR     (N):    both datasets combined || tested at 427 °C (800 °F) || 0.2 h to 5,600 h
    SR     (N):    both datasets combined || tested at 482 °C (900 °F) || 0.1 h to 2,025 h
    SR     (N):    both datasets combined || Master curve (LMP) || 14.5 h to 18.7 h
    CRS    (N):    0.3% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 371 °C (700 °F) || 0.2 h to 1,080 h
    CRS    (N):    0.3% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 427 °C (800 °F) || 0.24 h to 1,010 h
    CRS    (N):    0.3% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 482 °C (900 °F) || 0.11 h to 1,010 h
    CRS    (N):    0.5% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 371 °C (700 °F) || 0.5 h to 1,100 h
    CRS    (N):    0.5% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 427 °C (800 °F) || 0.58 h to 1,000 h
    CRS    (N):    0.5% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 482 °C (900 °F) || 0.12 h to 950 h
    CRS    (N):    1% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 371 °C (700 °F) || 1.5 h to 1,120 h
    CRS    (N):    1% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 427 °C (800 °F) || 1.6 h to 1,000 h
    CRS    (N):    1% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 482 °C (900 °F) || 0.33 h to 1,080 h
    IC     (R):    tested at 316 °C (600 °F), plastic strain, annealed at 907 °C (1665 °F) to 935 °C (1715 °F), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 316 °C (600 °F), plastic strain, annealed at 907 °C (1665 °F) to 935 °C (1715 °F), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 0.5 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 2 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 4 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 6 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 8 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 40 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 80 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 150 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 250 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 750 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 371 °C (700 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 0.5 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 2 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 4 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 6 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 8 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 40 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 80 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 150 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 250 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 750 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 0.5 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 2 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 4 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 6 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 8 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 20 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 40 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 60 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 80 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 150 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 250 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 400 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 600 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 750 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || 1,000 h || 0 to 0.01 mm/mm strain
    CRR    (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 371 °C (700 °F) || 4.85 x 10^-¹⁰/s to 6.45 x 10^-⁷/s
    CRR    (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 427 °C (800 °F) || 8 x 10^-¹⁰/s to 5.12 x 10^-⁷/s
    CRR    (N):    heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || tested at 482 °C (900 °F) || 8.2 x 10^-¹⁰/s to 9.11 x 10^-⁷/s

return to listing

Ti Grade 4

    CRR    (N):    12.7 mm (0.5 inch) diameter bar, as-received, hot-rolled and annealed || tested at 427 °C (800 °F) || 5 x 10^-⁹/s to 2.39 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, as-received, hot-rolled and annealed || tested at 538 °C (1000 °F) || 1.38 x 10^-⁸/s to 9.17 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal || tested at 427 °C (800 °F) || 5 x 10^-⁹/s to 2.31 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal || tested at 538 °C (1000 °F) || 4.44 x 10^-⁸/s to 9.45 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal || tested at 427 °C (800 °F) || 9.72 x 10^-¹⁰/s to 2.23 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal || tested at 538 °C (1000 °F) || 3.85 x 10^-⁹/s to 1.67 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal + 10.9% cold work || tested at 427 °C (800 °F) || 1.27 x 10^-⁸/s to 8.06 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal + 10.9% cold work || tested at 538 °C (1000 °F) || 2.22 x 10^-⁷/s to 5.28 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal + 31.3% cold work || tested at 316 °C (600 °F) || 2.63 x 10^-⁸/s to 1.03 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal + 31.3% cold work || tested at 427 °C (800 °F) || 1.44 x 10^-⁸/s to 1.67 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 816 °C (1500 °F) anneal + 31.3% cold work || tested at 538 °C (1000 °F) || 3.6 x 10^-⁸/s to 4.45 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal + 10.9% cold work || tested at 316 °C (600 °F) || 4.73 x 10^-¹⁰/s to 1.11 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal + 10.9% cold work || tested at 427 °C (800 °F) || 2.16 x 10^-⁸/s to 6.12 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal + 10.9% cold work || tested at 538 °C (1000 °F) || 5.83 x 10^-⁹/s to 1 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal + 31.3% cold work || tested at 427 °C (800 °F) || 6.67 x 10^-⁹/s to 2.12 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, 927 °C (1700 °F) anneal + 31.3% cold work || tested at 538 °C (1000 °F) || 1.05 x 10^-⁷/s to 2.23 x 10^-⁶/s

return to listing

Ti-1300 (New)

    E     (*):    investment cast || room temperature value
    SSC       :    investment cast, single aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 600 °C (1112 °F) || 0 to 0.72 mm/mm strain
    SSC       :    investment cast, single aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 650 °C (1202 °F) || 0 to 0.76 mm/mm strain
    SSC       :    investment cast, single aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 700 °C (1292 °F) || 0 to 0.25 mm/mm strain
    SSC       :    investment cast, single aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 750 °C (1382 °F) || 0 to 0.15 mm/mm strain
    SSC       :    investment cast, double aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 750 °C (1382 °F) and 570 °C (1058 °F) || 0 to 0.13 mm/mm strain
    SSC       :    investment cast, double aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 750 °C (1382 °F) and 620 °C (1148 °F) || 0 to 0.45 mm/mm strain
    SSC       :    investment cast, double aged || tested at 20 °C (68 °F), 5 x 10^-⁴/s, aged at 750 °C (1382 °F) and 650 °C (1202 °F) || 0 to 0.59 mm/mm strain
    UTS   (*):    investment cast, single aged || aged at 600 °C (1112 °F) || room temperature value
    UTS   (*):    investment cast, single aged || aged at 650 °C (1202 °F) || room temperature value
    UTS   (*):    investment cast, single aged || aged at 700 °C (1292 °F) || room temperature value
    UTS   (*):    investment cast, single aged || aged at 750 °C (1382 °F) || room temperature value
    UTS   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 570 °C (1058 °F) || room temperature value
    UTS   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 620 °C (1148 °F) || room temperature value
    UTS   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 650 °C (1202 °F) || room temperature value
    YS    (*):    investment cast, single aged || aged at 600 °C (1112 °F) || room temperature value
    YS    (*):    investment cast, single aged || aged at 650 °C (1202 °F) || room temperature value
    YS    (*):    investment cast, single aged || aged at 700 °C (1292 °F) || room temperature value
    YS    (*):    investment cast, single aged || aged at 750 °C (1382 °F) || room temperature value
    YS    (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 570 °C (1058 °F) || room temperature value
    YS    (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 620 °C (1148 °F) || room temperature value
    YS    (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 650 °C (1202 °F) || room temperature value
    %El   (*):    investment cast, single aged || aged at 600 °C (1112 °F) || room temperature value
    %El   (*):    investment cast, single aged || aged at 650 °C (1202 °F) || room temperature value
    %El   (*):    investment cast, single aged || aged at 700 °C (1292 °F) || room temperature value
    %El   (*):    investment cast, single aged || aged at 750 °C (1382 °F) || room temperature value
    %El   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 570 °C (1058 °F) || room temperature value
    %El   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 620 °C (1148 °F) || room temperature value
    %El   (*):    investment cast, double aged || aged at 750 °C (1382 °F) and 650 °C (1202 °F) || room temperature value

return to listing

Ti-140A (Ti - 2 Cr - 2 Fe - 2 Mo (wt %))

    UTS    (N):    effect of strain rate and H₂ || 0.005/s, 20 ppm H₂ || -79 °C (-110 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.05/s, 20 ppm H₂ || -79 °C (-110 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.5/s, 20 ppm H₂ || -79 °C (-110 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.005/s, 250 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.05/s, 250 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.5/s, 250 ppm H₂ || -73 °C (-100 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.005/s, 500 ppm H₂ || -73 °C (-100 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.05/s, 500 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    UTS    (N):    effect of strain rate and H₂ || 0.5/s, 500 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    UTS   (N*):    effect of cold work and H₂ || 0% cold work, 8 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 5% cold work, 8 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 10% cold work, 8 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 15% cold work, 8 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 30% cold work, 8 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 0% cold work, 650 ppm H₂ || room temperature value
    UTS   (N*):    effect of cold work and H₂ || 5% cold work, 650 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 0% cold work, 8 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 5% cold work, 8 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 10% cold work, 8 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 15% cold work, 8 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 30% cold work, 8 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 0% cold work, 650 ppm H₂ || room temperature value
    YS    (N*):    effect of cold work and H₂ || 5% cold work, 650 ppm H₂ || room temperature value
    %El    (N):    effect of strain rate and H₂ || 0.005/s, 20 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.05/s, 20 ppm H₂ || -79 °C (-110 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.5/s, 20 ppm H₂ || -79 °C (-110 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.005/s, 250 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.05/s, 250 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.5/s, 250 ppm H₂ || -73 °C (-100 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.005/s, 500 ppm H₂ || -73 °C (-100 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.05/s, 500 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    %El    (N):    effect of strain rate and H₂ || 0.5/s, 500 ppm H₂ || -196.1 °C (-321.1 °F) to 100 °C (212 °F)
    %El   (N*):    effect of cold work and H₂ || 0% cold work, 8 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 5% cold work, 8 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 10% cold work, 8 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 15% cold work, 8 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 30% cold work, 8 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 0% cold work, 650 ppm H₂ || room temperature value
    %El   (N*):    effect of cold work and H₂ || 5% cold work, 650 ppm H₂ || room temperature value
    CRR    (N):    mill annealed 1.6 mm (0.063 inch) thick sheet || tested at 371 °C (700 °F) || 2.64 x 10^-⁸/s to 5.75 x 10^-⁶/s
    CRR    (N):    mill annealed 1.6 mm (0.063 inch) thick sheet || tested at 427 °C (800 °F) || 1.13 x 10^-¹⁰/s to 3.7 x 10^-⁶/s

return to listing

Ti-150A (Ti - 3 Cr - 2 Fe (wt %))

    SR     (N):    annealed at 704 °C (1300 °F), effect of H₂ || tested at 20 °C (68 °F), 250 ppm H₂ || 0.5 h to 1 h
    SR     (N):    annealed at 704 °C (1300 °F), effect of H₂ || tested at 20 °C (68 °F), 10 ppm H₂ || 1.3 h to 18 h
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, as-received, hot-rolled and annealed || tested at 427 °C (800 °F) || 2.36 x 10^-⁷/s to 3.06 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, as-received, hot-rolled and annealed || tested at 538 °C (1000 °F) || 3.05 x 10^-⁹/s to 1.81 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), furnace cool || tested at 427 °C (800 °F) || 1.08 x 10^-⁸/s to 6.95 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), furnace cool || tested at 538 °C (1000 °F) || 1.33 x 10^-⁹/s to 2.23 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), air cooled || tested at 316 °C (600 °F) || 1.19 x 10^-⁸/s to 1.39 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), air cooled || tested at 427 °C (800 °F) || 1.63 x 10^-⁹/s to 3.89 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), air cooled || tested at 538 °C (1000 °F) || 2.47 x 10^-⁹/s to 1.12 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), water quenched || tested at 316 °C (600 °F) || 8.88 x 10^-⁸/s to 1.12 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), water quenched || tested at 427 °C (800 °F) || 4.17 x 10^-⁹/s to 2.05 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), water quenched || tested at 538 °C (1000 °F) || 4.16 x 10^-⁹/s to 9.18 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), furnace cooled || tested at 316 °C (600 °F) || 9.72 x 10^-¹⁰/s to 4.73 x 10^-⁹/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), furnace cooled || tested at 427 °C (800 °F) || 7.77 x 10^-¹¹/s to 4.45 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), furnace cooled || tested at 538 °C (1000 °F) || 1.55 x 10^-⁹/s to 1.72 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), air cooled || tested at 316 °C (600 °F) || 4.44 x 10^-⁹/s to 3.89 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), air cooled || tested at 427 °C (800 °F) || 6.9 x 10^-⁹/s to 2.23 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), air cooled || tested at 538 °C (1000 °F) || 4.44 x 10^-⁹/s to 1.31 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), water quenched || tested at 316 °C (600 °F) || 9.16 x 10^-⁹/s to 2 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), water quenched || tested at 427 °C (800 °F) || 4.44 x 10^-⁹/s to 5.56 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), water quenched || tested at 538 °C (1000 °F) || 2.52 x 10^-⁹/s to 3.89 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), water quenched, annealed at 732 °C (1350 °F) || tested at 316 °C (600 °F) || 2.77 x 10^-⁹/s to 3.06 x 10^-⁹/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), water quenched, annealed at 732 °C (1350 °F) || tested at 538 °C (1000 °F) || 1 x 10^-⁹/s to 1.28 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), air cooled, annealed at 482 °C (900 °F) || tested at 427 °C (800 °F) || 3.88 x 10^-⁷/s to 1 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 816 °C (1500 °F), air cooled, annealed at 482 °C (900 °F) || tested at 538 °C (1000 °F) || 1.94 x 10^-⁹/s to 1.47 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), water quenched, annealed at 482 °C (900 °F) || tested at 427 °C (800 °F) || 1 x 10^-⁸/s to 2.78 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 732 °C (1350 °F), water quenched, annealed at 482 °C (900 °F) || tested at 538 °C (1000 °F) || 1.86 x 10^-⁹/s to 1 x 10^-⁶/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 704 °C (1300 °F), water quenched || tested at 316 °C (600 °F) || 1.86 x 10^-⁸/s to 3.89 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 704 °C (1300 °F), water quenched || tested at 427 °C (800 °F) || 2.11 x 10^-⁹/s to 8.06 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 704 °C (1300 °F), water quenched || tested at 538 °C (1000 °F) || 1.22 x 10^-⁹/s to 2.31 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 538 °C (1000 °F), water quenched || tested at 316 °C (600 °F) || 2.52 x 10^-⁹/s to 2 x 10^-⁸/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 538 °C (1000 °F), water quenched || tested at 427 °C (800 °F) || 5 x 10^-⁹/s to 3.62 x 10^-⁷/s
    CRR    (N):    12.7 mm (0.5 inch) diameter bar, annealed at 982 °C (1800 °F), transformed at 538 °C (1000 °F), water quenched || tested at 538 °C (1000 °F) || 3.33 x 10^-⁹/s to 1.86 x 10^-⁷/s

return to listing

TiFe₁_.₉₆Re₀_.₀₄Sn (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 87.9% dense || 20 °C (68 °F) to 600 °C (1112 °F)
    RHO       :    solid || 87.9% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    SIGMA    :    solid || 87.9% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    S         :    solid || 87.9% dense || 20 °C (68 °F) to 650 °C (1202 °F)

return to listing

TiFe₁_.₉₄Re₀_.₀₆Sn (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 89.8% dense || 20 °C (68 °F) to 600 °C (1112 °F)
    RHO       :    solid || 89.8% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    SIGMA    :    solid || 89.8% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    S         :    solid || 89.8% dense || 20 °C (68 °F) to 650 °C (1202 °F)

return to listing

TiFe₁_.₈Re₀_.₂Sn (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 86.8% dense || 20 °C (68 °F) to 600 °C (1112 °F)
    RHO       :    solid || 86.8% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    SIGMA    :    solid || 86.8% dense || -269.1 °C (-452.5 °F) to 650 °C (1202 °F)
    S         :    solid || 86.8% dense || 20 °C (68 °F) to 650 °C (1202 °F)

return to listing

TiFe₁_.₉₈Re₀_.₀₂Sn (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 84.8% dense || 20 °C (68 °F) to 600 °C (1112 °F)
    RHO       :    solid || 84.8% dense || -269.1 °C (-452.5 °F) to 645 °C (1193 °F)
    SIGMA    :    solid || 84.8% dense || -269.1 °C (-452.5 °F) to 645 °C (1193 °F)
    S         :    solid || 84.8% dense || 20 °C (68 °F) to 650 °C (1202 °F)

return to listing

TiFe₂Sn (New)

    D     (*):    solid || room temperature value
    TC        :    solid || 83.9% dense || 20 °C (68 °F) to 600 °C (1112 °F)
    RHO       :    solid || 83.9% dense || -269.1 °C (-452.5 °F) to 620 °C (1148 °F)
    SIGMA    :    solid || 83.9% dense || -269.1 °C (-452.5 °F) to 620 °C (1148 °F)
    S         :    solid || 83.9% dense || 20 °C (68 °F) to 650 °C (1202 °F)

return to listing

Timetal 685 (New)

    DLL       :    solid || solution annealed & aged || 20 °C (68 °F) to 500 °C (932 °F)
    MTE       :    solid || solution annealed & aged || 20 °C (68 °F) to 500 °C (932 °F)
    CTE       :    solid || solution annealed & aged || 20 °C (68 °F) to 500 °C (932 °F)
    D         :    solid || solution annealed & aged || 20 °C (68 °F) to 500 °C (932 °F)
    TC    (*):    solid || solution annealed & aged || room temperature value
    RHO   (*):    solid || solution annealed & aged || room temperature value
    SIGMA (*):    solid || solution annealed & aged || room temperature value
    E     (*):    solid || solution annealed & aged || room temperature value
    G     (*):    solid || solution annealed & aged || room temperature value
    v     (*):    solid || solution annealed & aged || room temperature value
    K     (*):    solid || solution annealed & aged || room temperature value
    UTS   (*):    solid || solution annealed & aged || room temperature value
    YS    (*):    solid || solution annealed & aged || room temperature value
    %El   (*):    solid || solution annealed & aged || room temperature value
    FSN       :    solution annealed & aged || tested at 20 °C (68 °F), R = -1, maximum stress || 4.5 x 10⁴ cycles to 1.7 x 10⁷ cycles
    FSN       :    solution annealed & aged || tested at 450 °C (842 °F), R = -1, maximum stress || 1.17 x 10⁴ cycles to 1.8 x 10⁷ cycles
    FSN       :    solution annealed & aged || tested at 520 °C (968 °F), R = -1, maximum stress || 1.18 x 10⁴ cycles to 1.8 x 10⁷ cycles
    FSN       :    solution annealed & aged || tested at 450 °C (842 °F), R = 0, maximum stress || 1 x 10⁴ cycles to 1.8 x 10⁷ cycles
    FSN       :    solution annealed & aged || tested at 520 °C (968 °F), R = 0, maximum stress || 1.2 x 10⁴ cycles to 1.8 x 10⁷ cycles
    FSN       :    aligned structure || tested at 20 °C (68 °F), R = 0.1, axial, maximum stress || 500 cycles to 8.5 x 10⁴ cycles
    FSN       :    aligned structure || tested at 20 °C (68 °F), R = 0.1, axial, 2 minute hold, maximum stress || 43 cycles to 1.2 x 10⁴ cycles
    FSN       :    basketweave structure || tested at 20 °C (68 °F), R = 0.1, axial, maximum stress || 150 cycles to 9.5 x 10⁴ cycles
    FSN       :    basketweave structure || tested at 20 °C (68 °F), R = 0.1, axial, 2 minute hold, maximum stress || 110 cycles to 5.6 x 10³ cycles

return to listing

Tin

S (N): solid || 20 °C (68 °F) to 229 °C (444 °F)
S (N): liquid || 237 °C (458 °F) to 277 °C (530 °F)

return to listing

Udimet 500

    CRR    (N):    aged || tested at 649 °C (1200 °F) || 3.2 x 10^-¹⁰/s to 9.3 x 10^-⁶/s
    CRR    (N):    aged || tested at 732 °C (1350 °F) || 1 x 10^-⁹/s to 2.2 x 10^-⁵/s
    CRR    (N):    aged || tested at 816 °C (1500 °F) || 3.8 x 10^-¹⁰/s to 2.15 x 10^-⁵/s
    CRR    (N):    aged || tested at 899 °C (1650 °F) || 6.7 x 10^-¹⁰/s to 1.12 x 10^-⁵/s
    CRR    (N):    aged || tested at 982 °C (1800 °F) || 5.6 x 10^-¹⁰/s to 5.5 x 10^-⁷/s

return to listing

UNS C11000 (ETP)

    CRR    (N):    annealed || tested at 149 °C (300 °F) || 9.2 x 10^-¹²/s to 2.33 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F) || 3.88 x 10^-¹¹/s to 8 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F) || 2.75 x 10^-¹¹/s to 8.4 x 10^-¹⁰/s
    CRR    (N):    cold rolled || tested at 149 °C (300 °F), cold rolled 10% || 1.6 x 10^-¹¹/s to 1.1 x 10^-⁹/s
    CRR    (N):    cold rolled || tested at 204 °C (400 °F), cold rolled 25% || 4 x 10^-¹¹/s to 8 x 10^-¹⁰/s

return to listing

UNS C10200 (OFHC/OF)

    CRR    (N):    annealed || tested at 149 °C (300 °F) || 4.9 x 10^-¹²/s to 2.33 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F) || 1.85 x 10^-¹¹/s to 5.91 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F) || 2.4 x 10^-¹¹/s to 3.8 x 10^-¹⁰/s
    CRR    (N):    cold rolled 25% || tested at 130 °C (266 °F) || 5.9 x 10^-¹¹/s to 1.3 x 10^-¹⁰/s
    CRR    (N):    cold rolled 25% || tested at 205 °C (401 °F) || 1.6 x 10^-¹⁰/s to 1.24 x 10^-⁹/s
    CRR    (N):    cold drawn 40% || tested at 43 °C (110 °F) || 1.1 x 10^-¹⁰/s to 1.8 x 10^-⁸/s
    CRR    (N):    cold drawn 40% || tested at 149 °C (300 °F) || 9.1 x 10^-¹⁰/s to 4.55 x 10^-⁷/s
    CRR    (N):    cold drawn 75% || tested at 43 °C (110 °F) || 7.3 x 10^-¹⁰/s to 2.65 x 10^-⁸/s
    CRR    (N):    cold drawn 75% || tested at 93 °C (200 °F) || 2.2 x 10^-⁹/s to 1.8 x 10^-⁷/s
    CRR    (N):    cold drawn 75% || tested at 121 °C (250 °F) || 2.98 x 10^-¹⁰/s to 2.93 x 10^-⁹/s
    CRR    (N):    cold drawn 75% || tested at 177 °C (350 °F) || 5.6 x 10^-¹¹/s to 2.85 x 10^-⁹/s

return to listing

UNS C95200

CRR (N): cast || tested at 250 °C (482 °F) || 1.1 x 10^-¹⁰/s to 7.4 x 10^-⁹/s
CRR (N): aged || tested at 250 °C (482 °F) || 1.1 x 10^-¹⁰/s to 8.85 x 10^-⁹/s

return to listing

UNS C10800

    CRR    (N):    drawn 84% || tested at 149 °C (300 °F) || 2.2 x 10^-¹²/s to 1.36 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 204 °C (400 °F) || 3.9 x 10^-¹²/s to 1.01 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 260 °C (500 °F) || 1.28 x 10^-¹⁰/s to 8.21 x 10^-⁹/s

return to listing

UNS C10500

CRR (N): drawn 84% || tested at 149 °C (300 °F) || 2.7 x 10^-¹³/s to 1.44 x 10^-¹⁰/s

return to listing

UNS C14200

CRR (N): drawn 84% || tested at 260 °C (500 °F) || 4.1 x 10^-¹²/s to 6.75 x 10^-¹⁰/s

return to listing

UNS C14500

CRR (N): annealed || tested at 149 °C (300 °F) || 4.2 x 10^-¹²/s to 6.2 x 10^-¹¹/s

return to listing

UNS C22000

CRR (N): hard || tested at 199 °C (390 °F) || 9 x 10^-¹¹/s to 5.4 x 10^-¹⁰/s

return to listing

UNS C23000

CRR (N): annealed || tested at 149 °C (300 °F) || 2 x 10^-¹²/s to 6.64 x 10^-¹¹/s

return to listing

UNS C26000

    CRR    (N):    annealed || tested at 204 °C (400 °F), 200 micron grain size || 2.7 x 10^-¹²/s to 1.3 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 200 micron grain size || 2.7 x 10^-¹²/s to 2.5 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 149 °C (300 °F), 85 micron grain size || 1.35 x 10^-¹²/s to 1.7 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 85 micron grain size || 3.5 x 10^-¹²/s to 3.6 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 85 micron grain size || 8.4 x 10^-¹²/s to 1.23 x 10^-⁹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 22 micron grain size || 2.1 x 10^-¹¹/s to 3.3 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 22 micron grain size || 5.9 x 10^-¹¹/s to 1.05 x 10^-⁹/s
    CRR    (N):    annealed || tested at 149 °C (300 °F), 16 micron grain size || 6.8 x 10^-¹²/s to 1.5 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 16 micron grain size || 1.5 x 10^-¹¹/s to 1.2 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 16 micron grain size || 7.4 x 10^-¹¹/s to 1.15 x 10^-⁹/s

return to listing

UNS C28000

CRR (N): annealed || tested at 149 °C (300 °F) || 3 x 10^-¹²/s to 5.5 x 10^-¹¹/s
CRR (N): annealed || tested at 204 °C (400 °F) || 6.3 x 10^-¹²/s to 5.25 x 10^-¹⁰/s

return to listing

UNS C43500

    CRR    (N):    annealed || tested at 204 °C (400 °F), 55 micron grain size || 1.35 x 10^-¹²/s to 4.53 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 149 °C (300 °F), 18 micron grain size || 5.5 x 10^-¹³/s to 1.32 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 18 micron grain size || 7 x 10^-¹²/s to 3.35 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 18 micron grain size || 5.6 x 10^-¹¹/s to 2.65 x 10^-⁹/s
    CRR    (N):    drawn 60% || tested at 204 °C (400 °F) || 3.1 x 10^-¹¹/s to 2.85 x 10^-¹⁰/s
    CRR    (N):    drawn 60% || tested at 260 °C (500 °F) || 1.5 x 10^-¹¹/s to 2.7 x 10^-⁹/s

return to listing

UNS C46400

    CRR    (N):    annealed || tested at 149 °C (300 °F), 25 micron grain size || 4.7 x 10^-¹¹/s to 8.4 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 25 micron grain size || 2.4 x 10^-¹⁰/s to 1.3 x 10^-⁹/s
    CRR    (N):    annealed || tested at 149 °C (300 °F), 45 micron grain size || 2.2 x 10^-¹⁰/s to 1.35 x 10^-⁹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 45 micron grain size || 1.75 x 10^-¹⁰/s to 2.7 x 10^-⁹/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), unknown grain size || 5.75 x 10^-¹¹/s to 2.1 x 10^-⁹/s
    CRR    (N):    hot rolled || tested at 149 °C (300 °F), 20 micron grain size || 8.4 x 10^-¹¹/s to 1.35 x 10^-⁹/s
    CRR    (N):    hot rolled || tested at 204 °C (400 °F), 20 micron grain size || 1.5 x 10^-¹⁰/s to 6.1 x 10^-¹⁰/s
    CRR    (N):    hot rolled || tested at 149 °C (300 °F), 25 micron grain size || 5.25 x 10^-¹¹/s to 1.25 x 10^-⁹/s
    CRR    (N):    hot rolled || tested at 204 °C (400 °F), 25 micron grain size || 1.95 x 10^-¹⁰/s to 2.62 x 10^-⁹/s
    CRR    (N):    hot rolled || tested at 149 °C (300 °F), 45 micron grain size || 2.3 x 10^-¹¹/s to 1.25 x 10^-⁹/s

return to listing

UNS C51000

    CRR    (N):    annealed || tested at 149 °C (300 °F) || 9.4 x 10^-¹³/s to 5.3 x 10^-¹²/s
    CRR    (N):    annealed || tested at 204 °C (400 °F) || 9.4 x 10^-¹³/s to 1.48 x 10^-¹¹/s
    CRR    (N):    drawn 84% || tested at 149 °C (300 °F) || 2.7 x 10^-¹²/s to 7.7 x 10^-¹¹/s
    CRR    (N):    drawn 84% || tested at 204 °C (400 °F) || 7.7 x 10^-¹²/s to 7.82 x 10^-¹¹/s

return to listing

UNS C52400

CRR (N): cast || tested at 204 °C (400 °F) || 3.4 x 10^-¹¹/s to 2.8 x 10^-¹⁰/s

return to listing

UNS C63000

Vis (N): liquid || 1077 °C (1970 °F) to 1500 °C (2732 °F)

return to listing

UNS C63200

SSC (N): laser powder bed fusion || tested at 20 °C (68 °F), unknown strain rate || 0 to 0.16 mm/mm strain
FSN (N): laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, maximum stress || 680 cycles to 3.8 x 10⁶ cycles

return to listing

UNS C65100

    CRR    (N):    annealed || tested at 149 °C (300 °F), 25 micron grain size || 2.6 x 10^-¹²/s to 2.63 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 25 micron grain size || 2.7 x 10^-¹²/s to 2.72 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 149 °C (300 °F), 60 micron grain size || 2.65 x 10^-¹²/s to 2.7 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 60 micron grain size || 2.7 x 10^-¹²/s to 2.7 x 10^-¹⁰/s
    CRR    (N):    cold drawn || tested at 149 °C (300 °F), cold drawn 21% || 2.65 x 10^-¹²/s to 2.7 x 10^-¹¹/s
    CRR    (N):    cold drawn || tested at 204 °C (400 °F), cold drawn 21% || 2.74 x 10^-¹²/s to 2.72 x 10^-¹⁰/s
    CRR    (N):    cold drawn || tested at 149 °C (300 °F), cold drawn 60% || 2.65 x 10^-¹²/s to 2.7 x 10^-¹¹/s
    CRR    (N):    cold drawn || tested at 204 °C (400 °F), cold drawn 60% || 2.65 x 10^-¹²/s to 2.7 x 10^-¹¹/s

return to listing

UNS C71500

    FSN    (N):    flexural fatigue || tested at 20 °C (68 °F), R = -1, UTS = 400 MPa (58 ksi), maximum stress || 1 x 10³ cycles to 2 x 10⁴ cycles
    FSN    (N):    flexural fatigue || tested at 20 °C (68 °F), R = -1, UTS = 675 MPa (97.9 ksi), maximum stress || 4 x 10⁵ cycles to 1 x 10⁸ cycles
    FSN    (N):    rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, drawn 33%, maximum stress || 7.2 x 10⁵ cycles to 1 x 10⁸ cycles
    CRR    (N):    annealed || tested at 149 °C (300 °F), 20 micron grain size || 2.7 x 10^-¹³/s to 6.81 x 10^-¹²/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 20 micron grain size || 2.55 x 10^-¹²/s to 1.6 x 10^-¹¹/s
    CRR    (N):    drawn 84% || tested at 260 °C (500 °F) || 1.75 x 10^-¹²/s to 1.05 x 10^-¹¹/s

return to listing

UNS C72150

FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, annealed, maximum stress || 8 x 10⁴ cycles to 1 x 10⁸ cycles
FSN (N): rotating cantilever fatigue || tested at 20 °C (68 °F), R = -1, cold rolled, maximum stress || 7 x 10⁵ cycles to 4 x 10⁷ cycles

return to listing

UNS C94700

    RHO   (N*):    effect of aging time, cold-rolled sheet || not aged || room temperature value
    RHO   (N*):    effect of aging time, cold-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cold-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cold-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cold-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cold-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || not aged || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    RHO   (N*):    effect of aging time, cryo-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || not aged || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cold-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || not aged || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    SIGMA (N*):    effect of aging time, cryo-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value
    SSC    (N):    rolled at room temperature || tested at 20 °C (68 °F), 0.0028/s, as-rolled || 0 to 3.77 x 10^-³ mm/mm strain
    SSC    (N):    rolled at room temperature || tested at 20 °C (68 °F), 0.0028/s, aged 1 h at 300 °C (572 °F) || 0 to 6.56 x 10^-³ mm/mm strain
    SSC    (N):    cryo-rolled || tested at 20 °C (68 °F), 0.0028/s, as-rolled || 0 to 1.69 x 10^-³ mm/mm strain
    SSC    (N):    cryo-rolled || tested at 20 °C (68 °F), 0.0028/s, aged 1 h at 300 °C (572 °F) || 0 to 6.64 x 10^-³ mm/mm strain
    UTS   (N*):    effect of aging time, cold-rolled sheet || not aged || room temperature value
    UTS   (N*):    effect of aging time, cold-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cold-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cold-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cold-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cold-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || not aged || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || aged 1 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || aged 4 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || aged 8 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || aged 16 h at 300 °C (572 °F) || room temperature value
    UTS   (N*):    effect of aging time, cryo-rolled sheet || aged 24 h at 300 °C (572 °F) || room temperature value

return to listing

UNS C96200

    E      (R):    annealed || -269.1 °C (-452.5 °F) to 261 °C (502 °F)
    CRR    (N):    annealed || tested at 149 °C (300 °F), 30 micron grain size || 7.9 x 10^-¹³/s to 2.7 x 10^-¹¹/s
    CRR    (N):    annealed || tested at 204 °C (400 °F), 30 micron grain size || 2.7 x 10^-¹²/s to 2.7 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 30 micron grain size || 2.7 x 10^-¹²/s to 2.7 x 10^-¹⁰/s

return to listing

UNS C71000

    E      (R):    annealed || 20 °C (68 °F) to 261 °C (502 °F)
    CRR    (N):    annealed || tested at 149 °C (300 °F), 25 micron grain size || 2.6 x 10^-¹³/s to 1.12 x 10^-¹²/s
    CRR    (N):    annealed || tested at 260 °C (500 °F), 25 micron grain size || 1.7 x 10^-¹²/s to 1.7 x 10^-¹¹/s

return to listing

V - 10 Cr - 5 Ti (wt %)

D (N*): solid || room temperature value
CRR (N): recrystallized || tested at 600 °C (1112 °F) || 4.7 x 10^-⁹/s to 1.96 x 10^-⁷/s

return to listing

V - 4 Cr - 4 Ti (wt %)

D (N*): solid || room temperature value
CRR (N): recrystallized || tested at 600 °C (1112 °F) || 3.25 x 10^-⁹/s to 8.93 x 10^-⁸/s

return to listing

Waspaloy

    CRR    (N):    solution treated 0.5 h at 996 °C (1825 °F) || tested at 538 °C (1000 °F), aged 16 h at 760 °C (1400 °F) || 1.4 x 10^-⁹/s to 1.1 x 10^-⁷/s
    CRR    (N):    solution treated 0.5 h at 996 °C (1825 °F) || tested at 593 °C (1100 °F), aged 16 h at 760 °C (1400 °F) || 8 x 10^-¹⁰/s to 3 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 996 °C (1825 °F) || tested at 649 °C (1200 °F), aged 16 h at 760 °C (1400 °F) || 1.2 x 10^-⁹/s to 1.8 x 10^-⁷/s
    CRR    (N):    solution treated 0.5 h at 996 °C (1825 °F) || tested at 704 °C (1300 °F), aged 16 h at 760 °C (1400 °F) || 7.2 x 10^-¹⁰/s to 8.2 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 996 °C (1825 °F) || tested at 649 °C (1200 °F), aged 10 h at 927 °C (1700 °F) || 1 x 10^-⁸/s to 3 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1038 °C (1900 °F) || tested at 538 °C (1000 °F), aged 16 h at 760 °C (1400 °F) || 9.4 x 10^-¹⁰/s to 7.06 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1038 °C (1900 °F) || tested at 649 °C (1200 °F), aged 16 h at 760 °C (1400 °F) || 4.4 x 10^-¹⁰/s to 9.75 x 10^-¹⁰/s
    CRR    (N):    solution treated 0.5 h at 1038 °C (1900 °F) || tested at 538 °C (1000 °F), aged 10 h at 927 °C (1700 °F) || 4.8 x 10^-⁹/s to 7.2 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1038 °C (1900 °F) || tested at 649 °C (1200 °F), aged 10 h at 927 °C (1700 °F) || 6.55 x 10^-¹⁰/s to 5.03 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 538 °C (1000 °F), aged 16 h at 760 °C (1400 °F) || 1.1 x 10^-¹⁰/s to 4.73 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 593 °C (1100 °F), aged 16 h at 760 °C (1400 °F) || 4.4 x 10^-¹⁰/s to 8.4 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 649 °C (1200 °F), aged 16 h at 760 °C (1400 °F) || 2.6 x 10^-¹⁰/s to 3.34 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 704 °C (1300 °F), aged 16 h at 760 °C (1400 °F) || 1.1 x 10^-¹⁰/s to 1.4 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 760 °C (1400 °F), aged 16 h at 760 °C (1400 °F) || 1.1 x 10^-¹⁰/s to 4.73 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 538 °C (1000 °F), aged 10 h at 927 °C (1700 °F) || 4.63 x 10^-¹⁰/s to 7.51 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 593 °C (1100 °F), aged 10 h at 927 °C (1700 °F) || 3.8 x 10^-⁹/s to 1.81 x 10^-⁷/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 649 °C (1200 °F), aged 10 h at 927 °C (1700 °F) || 5 x 10^-¹⁰/s to 1.93 x 10^-⁷/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 704 °C (1300 °F), aged 10 h at 927 °C (1700 °F) || 2.4 x 10^-¹⁰/s to 3.2 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 760 °C (1400 °F), aged 10 h at 927 °C (1700 °F) || 4.1 x 10^-¹⁰/s to 3.1 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 649 °C (1200 °F), aged 24 h at 843 °C (1550 °F) || 3.3 x 10^-¹⁰/s to 3.7 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 704 °C (1300 °F), aged 24 h at 843 °C (1550 °F) || 1.25 x 10^-⁹/s to 4.45 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 760 °C (1400 °F), aged 24 h at 843 °C (1550 °F) || 2.8 x 10^-⁹/s to 1.05 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 538 °C (1000 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 1 x 10^-⁸/s to 1.85 x 10^-⁷/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 593 °C (1100 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 1.1 x 10^-⁹/s to 2.7 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 649 °C (1200 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 7.5 x 10^-¹⁰/s to 3.9 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1079 °C (1975 °F) || tested at 760 °C (1400 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 2.6 x 10^-⁹/s to 6.4 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1177 °C (2150 °F) || tested at 538 °C (1000 °F), aged 16 h at 760 °C (1400 °F) || 4.7 x 10^-¹¹/s to 6.95 x 10^-⁹/s
    CRR    (N):    solution treated 0.5 h at 1177 °C (2150 °F) || tested at 538 °C (1000 °F), aged 10 h at 927 °C (1700 °F) || 8.3 x 10^-¹⁰/s to 1.1 x 10^-⁸/s
    CRR    (N):    solution treated 0.5 h at 1177 °C (2150 °F) || tested at 649 °C (1200 °F), aged 10 h at 927 °C (1700 °F) || 1.6 x 10^-¹⁰/s to 3.1 x 10^-⁸/s
    CRR    (N):    solution treated 4 h at 1079 °C (1975 °F) || tested at 538 °C (1000 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 5.9 x 10^-¹⁰/s to 2.6 x 10^-⁷/s
    CRR    (N):    solution treated 4 h at 1079 °C (1975 °F) || tested at 593 °C (1100 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 1.1 x 10^-⁹/s to 5.75 x 10^-⁸/s
    CRR    (N):    solution treated 4 h at 1079 °C (1975 °F) || tested at 649 °C (1200 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 1.1 x 10^-¹⁰/s to 1.1 x 10^-⁸/s
    CRR    (N):    solution treated 4 h at 1079 °C (1975 °F) || tested at 704 °C (1300 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 8.6 x 10^-¹⁰/s to 7.7 x 10^-⁸/s
    CRR    (N):    solution treated 4 h at 1079 °C (1975 °F) || tested at 760 °C (1400 °F), aged 24 h at 843 °C (1550 °F), 16 h at 760 °C (1400 °F) || 1.3 x 10^-⁹/s to 2.9 x 10^-⁹/s

return to listing

WE43

    SSC    (R):    welded cast plates || tested at 20 °C (68 °F), 0.0016/s, T6 temper || 0 to 0.46 mm/mm strain
    SSC    (R):    welded cast plates || tested at 100 °C (212 °F), 0.0016/s, T6 temper || 0 to 0.95 mm/mm strain
    SSC    (R):    welded cast plates || tested at 150 °C (302 °F), 0.0016/s, T6 temper || 0 to 0.79 mm/mm strain
    SSC    (R):    welded cast plates || tested at 200 °C (392 °F), 0.0016/s, T6 temper || 0 to 0.6 mm/mm strain
    SSC    (R):    welded cast plates || tested at 250 °C (482 °F), 0.0016/s, T6 temper || 0 to 0.93 mm/mm strain
    SSC    (R):    welded cast plates || tested at 300 °C (572 °F), 0.0016/s, T6 temper || 0 to 0.81 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, solution treated || 0 to 0.62 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, peak aged || 0 to 0.36 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, 2 wt% Zn addition, solution treated || 0 to 0.146 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, 2 wt% Zn addition, peak aged || 0 to 0.7 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T4 temper || 0 to 0.14 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T3 temper || 0 to 0.37 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T62 temper || 0 to 0.29 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T6 temper || 0 to 0.41 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T82 temper || 0 to 0.58 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T63 temper || 0 to 0.9 mm/mm strain
    SSC    (N):    castings || tested at 20 °C (68 °F), 0.001/s, T83 temper || 0 to 0.63 mm/mm strain
    UTS   (N*):    castings || solution treated || room temperature value
    UTS   (N*):    castings || solution treated, 2 wt% Zn addition || room temperature value
    UTS   (N*):    castings || peak aged || room temperature value
    UTS   (N*):    castings || peak aged, 2 wt% Zn addition || room temperature value
    YS    (N*):    castings || solution treated || room temperature value
    YS    (N*):    castings || solution treated, 2 wt% Zn addition || room temperature value
    YS    (N*):    castings || peak aged || room temperature value
    YS    (N*):    castings || peak aged, 2 wt% Zn addition || room temperature value
    %El   (N*):    castings || solution treated || room temperature value
    %El   (N*):    castings || solution treated, 2 wt% Zn addition || room temperature value
    %El   (N*):    castings || peak aged || room temperature value
    %El   (N*):    castings || peak aged, 2 wt% Zn addition || room temperature value
    FEN    (N):    sand casting || tested at 20 °C (68 °F), R = -1, axial, T4 temper, total strain amplitude || 70 cycles to 3 x 10³ cycles
    FEN    (N):    sand casting || tested at 20 °C (68 °F), R = -1, axial, T6 temper, total strain amplitude || 130 cycles to 5 x 10³ cycles

return to listing

5105XP acrylate

    CRR    (N):    annealed sheet || tested at 27 °C (80 °F) || 3.5 x 10^-¹⁰/s to 8.8 x 10^-⁶/s
    CRR    (N):    annealed sheet || tested at 71 °C (160 °F) || 3.5 x 10^-¹⁰/s to 7.8 x 10^-⁷/s
    CRR    (N):    annealed sheet || tested at 93 °C (200 °F) || 9 x 10^-¹⁰/s to 5.5 x 10^-⁷/s

return to listing

Y₃Al₅O₁₂ (YAG)

    CRR    (N):    single crystal, [111] direction || tested at 1650 °C (3002 °F) || 1.17 x 10^-⁸/s to 4.36 x 10^-⁷/s
    CRR    (N):    single crystal, [111] direction || tested at 1750 °C (3182 °F) || 1.52 x 10^-⁸/s to 5.62 x 10^-⁶/s
    CRR    (N):    single crystal, [111] direction || tested at 1850 °C (3362 °F) || 8.66 x 10^-⁸/s to 1.78 x 10^-⁴/s
    CRR    (N):    single crystal, [110] direction || tested at 1650 °C (3002 °F) || 1.73 x 10^-⁹/s to 1.14 x 10^-⁶/s
    CRR    (N):    single crystal, [110] direction || tested at 1750 °C (3182 °F) || 1.31 x 10^-¹⁰/s to 1.67 x 10^-⁴/s
    CRR    (N):    single crystal, [110] direction || tested at 1800 °C (3272 °F) || 1.11 x 10^-⁶/s to 1.42 x 10^-⁴/s
    CRR    (N):    single crystal, [110] direction || tested at 1850 °C (3362 °F) || 3.6 x 10^-⁷/s to 3.21 x 10^-³/s
    CRR    (N):    single crystal, [100] direction || tested at 1650 °C (3002 °F) || 2.27 x 10^-⁸/s to 4.25 x 10^-⁷/s
    CRR    (N):    single crystal, [100] direction || tested at 1750 °C (3182 °F) || 2.2 x 10^-⁷/s to 4.81 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1800 °C (3272 °F) || 3.42 x 10^-⁷/s to 4.05 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1850 °C (3362 °F) || 2.17 x 10^-⁷/s to 3.81 x 10^-⁴/s

return to listing

ZE10

    SSC    (N):    O temper || tested at 20 °C (68 °F), 1 x 10^-⁴/s, rolling direction || 0 to 0.138 mm/mm strain
    SSC    (N):    O temper || tested at 20 °C (68 °F), 1 x 10^-⁴/s, transverse direction || 0 to 0.143 mm/mm strain
    SSCC   (N):    O temper || tested at 20 °C (68 °F), 1 x 10^-⁴/s, rolling direction || 0 to 0.141 mm/mm strain
    SSCC   (N):    O temper || tested at 20 °C (68 °F), 1 x 10^-⁴/s, transverse direction || 0 to 0.143 mm/mm strain
    UTS   (N*):    O temper || 1 x 10^-⁴/s, rolling direction || room temperature value
    UTS   (N*):    O temper || 1 x 10^-⁴/s, transverse direction || room temperature value
    YS    (N*):    O temper || 1 x 10^-⁴/s, rolling direction || room temperature value
    YS    (N*):    O temper || 1 x 10^-⁴/s, transverse direction || room temperature value
    YSC   (N*):    O temper || 1 x 10^-⁴/s, rolling direction || room temperature value
    YSC   (N*):    O temper || 1 x 10^-⁴/s, transverse direction || room temperature value

return to listing

ZE20 (New)

    SSCC      :    direct chill cast billets, 0.001/s || tested at 250 °C (482 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.001/s || tested at 300 °C (572 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.001/s || tested at 350 °C (662 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.001/s || tested at 400 °C (752 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.001/s || tested at 450 °C (842 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.01/s || tested at 250 °C (482 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.01/s || tested at 300 °C (572 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.01/s || tested at 350 °C (662 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.01/s || tested at 400 °C (752 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.01/s || tested at 450 °C (842 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.1/s || tested at 250 °C (482 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.1/s || tested at 300 °C (572 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.1/s || tested at 350 °C (662 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.1/s || tested at 400 °C (752 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 0.1/s || tested at 450 °C (842 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 1/s || tested at 250 °C (482 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 1/s || tested at 300 °C (572 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 1/s || tested at 350 °C (662 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 1/s || tested at 400 °C (752 °F) || 0 to 1 mm/mm strain
    SSCC      :    direct chill cast billets, 1/s || tested at 450 °C (842 °F) || 0 to 1 mm/mm strain

return to listing

ZEK100

    UTS   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    UTS   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    YS    (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    YS    (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    %El   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    %El   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value

return to listing

Zircaloy-2

    CRR    (N):    annealed sheet || tested at 150 °C (302 °F) || 5.5 x 10^-¹¹/s to 1.25 x 10^-⁴/s
    CRR    (N):    annealed sheet || tested at 230 °C (446 °F) || 5.55 x 10^-¹¹/s to 2.13 x 10^-⁴/s
    CRR    (N):    annealed sheet || tested at 345 °C (653 °F) || 2.77 x 10^-¹¹/s to 1.09 x 10^-⁴/s
    CRR    (N):    annealed sheet || tested at 425 °C (797 °F) || 4 x 10^-¹¹/s to 7.64 x 10^-⁶/s
    CRR    (N):    annealed sheet || tested at 500 °C (932 °F) || 1 x 10^-¹⁰/s to 4.45 x 10^-⁶/s
    CRR    (N):    cold worked sheet || tested at 150 °C (302 °F) || 5.5 x 10^-¹¹/s to 6.4 x 10^-⁶/s
    CRR    (N):    cold worked sheet || tested at 230 °C (446 °F) || 2.7 x 10^-¹¹/s to 1.25 x 10^-³/s
    CRR    (N):    cold worked sheet || tested at 345 °C (653 °F) || 1.38 x 10^-¹⁰/s to 2.31 x 10^-⁷/s
    CRR    (N):    cold worked sheet || tested at 425 °C (797 °F) || 2 x 10^-¹⁰/s to 7.6 x 10^-⁶/s
    CRR    (N):    cold worked sheet || tested at 500 °C (932 °F) || 2.75 x 10^-¹⁰/s to 2.87 x 10^-⁵/s
    CRR    (N):    annealed bar || tested at 150 °C (302 °F) || 1.27 x 10^-⁸/s to 2.23 x 10^-⁵/s
    CRR    (N):    annealed bar || tested at 230 °C (446 °F) || 2.7 x 10^-¹⁰/s to 8.73 x 10^-⁵/s
    CRR    (N):    annealed bar || tested at 425 °C (797 °F) || 2 x 10^-⁷/s to 1.92 x 10^-⁶/s
    CRR    (N):    annealed bar || tested at 500 °C (932 °F) || 4.72 x 10^-⁸/s to 1.23 x 10^-⁵/s

return to listing

ZK60

    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 2.2 x 10^-³/s, Liu et al. || 0 to 0.126 mm/mm strain
    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 2.2 x 10^-³/s, annealed 1 h at 350 °C (662 °F), Liu et al. || 0 to 0.163 mm/mm strain
    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 2.2 x 10^-³/s, annealed 2 h at 350 °C (662 °F), Liu et al. || 0 to 0.15 mm/mm strain
    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 2.2 x 10^-³/s, annealed 3 h at 350 °C (662 °F), Liu et al. || 0 to 0.164 mm/mm strain
    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 1 x 10^-⁴/s, Silva et al. || 0 to 0.67 mm/mm strain
    SSC    (N):    hot-rolled || tested at 20 °C (68 °F), 1 x 10^-⁴/s, with 1.5 wt% mischmetal, Silva et al. || 0 to 0.12 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 300 °C (572 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 300 °C (572 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 300 °C (572 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 300 °C (572 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 350 °C (662 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 350 °C (662 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 350 °C (662 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 350 °C (662 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 400 °C (752 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 400 °C (752 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 400 °C (752 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 400 °C (752 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 450 °C (842 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 450 °C (842 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 450 °C (842 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    cast & homogenized || tested at 450 °C (842 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 300 °C (572 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 300 °C (572 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 300 °C (572 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 300 °C (572 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 350 °C (662 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 350 °C (662 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 350 °C (662 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 350 °C (662 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 400 °C (752 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 400 °C (752 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 400 °C (752 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 400 °C (752 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 450 °C (842 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 450 °C (842 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 450 °C (842 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in extrusion direction || tested at 450 °C (842 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 300 °C (572 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 300 °C (572 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 300 °C (572 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 300 °C (572 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 350 °C (662 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 350 °C (662 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 350 °C (662 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 350 °C (662 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 400 °C (752 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 400 °C (752 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 400 °C (752 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 400 °C (752 °F), 1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 450 °C (842 °F), 0.001/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 450 °C (842 °F), 0.01/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 450 °C (842 °F), 0.1/s || 0 to 1 mm/mm strain
    SSCC   (N):    extruded, in transverse direction || tested at 450 °C (842 °F), 1/s || 0 to 1 mm/mm strain
    FSN    (N):    effect of ultrasonic peening, hot-extruded sheet || tested at 20 °C (68 °F), R = -1, 20 kHz, axial, not peened, stress amplitude || 8 x 10⁴ cycles to 4 x 10⁸ cycles
    FSN    (N):    effect of ultrasonic peening, hot-extruded sheet || tested at 20 °C (68 °F), R = -1, 20 kHz, axial, peened, stress amplitude || 1 x 10⁶ cycles to 5 x 10⁸ cycles

return to listing

ZM21

    UTS   (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    UTS   (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    UTS   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    UTS   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    YS    (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    YS    (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    YS    (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    YS    (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    %El   (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    %El   (N*):    sheet rolled at 300 °C (572 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value
    %El   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, rolling direction || room temperature value
    %El   (N*):    sheet rolled at 450 °C (842 °F) || tested at 20 °C (68 °F), 0.001/s, transverse direction || room temperature value

return to listing

90.6 ZrO₂ - 9.4 Y₂O₃ (mol %)

    CRR    (N):    single crystal, [111] direction || tested at 1650 °C (3002 °F) || 1.69 x 10^-⁹/s to 3.23 x 10^-⁵/s
    CRR    (N):    single crystal, [111] direction || tested at 1750 °C (3182 °F) || 4.3 x 10^-⁸/s to 1.5 x 10^-⁴/s
    CRR    (N):    single crystal, [111] direction || tested at 1850 °C (3362 °F) || 1.6 x 10^-⁷/s to 8.9 x 10^-⁴/s
    CRR    (N):    single crystal, [110] direction || tested at 1650 °C (3002 °F) || 3.45 x 10^-⁹/s to 1.52 x 10^-⁵/s
    CRR    (N):    single crystal, [110] direction || tested at 1750 °C (3182 °F) || 8.9 x 10^-⁹/s to 1.02 x 10^-⁴/s
    CRR    (N):    single crystal, [110] direction || tested at 1850 °C (3362 °F) || 4.4 x 10^-⁸/s to 8 x 10^-⁴/s
    CRR    (N):    single crystal, [100] direction || tested at 1650 °C (3002 °F) || 1.9 x 10^-⁸/s to 1.25 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1750 °C (3182 °F) || 1.05 x 10^-⁷/s to 7 x 10^-⁵/s
    CRR    (N):    single crystal, [100] direction || tested at 1850 °C (3362 °F) || 4.6 x 10^-⁷/s to 4.61 x 10^-⁴/s

return to listing

ZX11 (New)

    SSC       :    homogenized || tested at 20 °C (68 °F), 2.9 x 10^-³/s || 0 to 0.186 mm/mm strain
    SSC       :    rotary swagged || tested at 20 °C (68 °F), 2.9 x 10^-³/s || 0 to 0.126 mm/mm strain
    UTS   (*):    homogenized || room temperature value
    UTS   (*):    rotary swagged || room temperature value
    YS    (*):    homogenized || room temperature value
    YS    (*):    rotary swagged || room temperature value
    %El   (*):    homogenized || room temperature value
    %El   (*):    rotary swagged || room temperature value
    FSN       :    homogenized || tested at 20 °C (68 °F), R = 0.1, axial, stress amplitude || 9 x 10³ cycles to 1 x 10⁶ cycles
    FSN       :    rotary swagged || tested at 20 °C (68 °F), R = 0.1, axial, stress amplitude || 1 x 10⁴ cycles to 1 x 10⁶ cycles

return to listing

Zytel HTNWRF51MP20

    DLL    (R):    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    DLL    (R):    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    MTE    (R):    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    MTE    (R):    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    CTE    (R):    solid || transverse to the flow direction || 20 °C (68 °F) to 55 °C (131 °F)
    CTE    (R):    solid || weighted average || 20 °C (68 °F) to 55 °C (131 °F)
    D      (R):    solid || 20 °C (68 °F) to 55 °C (131 °F)

return to listing

Changes