Number of datasets below 20 °C = 41,714
Number of datasets at 200 K and below = 11,362
Number of datasets at 80 K and below = 8,846
Number of datasets at 20 K and below = 5,433

Key to property symbols (number of datasets):

D = Density (12,280 / 3,530)	DLL = Linear thermal expansion (ΔL/L) (16,980)	MTE = Mean coefficient of thermal expansion (16,980 / 15)
CTE = Coefficient of thermal expansion (CTE) (16,021)	E = Elastic/Young's modulus (2,158 / 4,799)	G = Shear modulus (939 / 1,574)
v = Poisson's ratio (799 / 1,666)	K = Bulk modulus (818 / 1,575)	TC = Thermal conductivity (5,122 / 2,200)
TD = Thermal diffusivity (1,753 / 1,586)	SH = Specific heat (3,083 / 1,432)	HC = Heat capacity (1,812 / 9)
SSC = True stress-strain curve (tension) (2,876)	SSCC = True stress-strain curve (compression) (2,632)	UTS = Tensile strength (2,651 / 3,423)
YS = Yield strength (tension) (2,242 / 3,323)	UCS = Compressive strength (44 / 62)	YSC = Yield strength (compression) (307 / 41)
%El = Elongation (1,888 / 5,169)	SR = Stress rupture (3,462)	FEN = Fatigue ε-N curve (689)
FSN = Fatigue S-N curve (2,342)	CRS = Creep strength (6,844)	IC = Isochronous creep (11,405)
HE = Hemispherical total emissivity (278)	NE = Normal total emissivity (294)	VP = Vapor pressure (415)
Vis = Viscosity (5,962)	ST = Surface tension (2,408)	RHO = Electrical resistivity (7,107 / 2,975)
SIGMA = Electrical conductivity (7,197 / 2,975)	SV = Specific volume (664)	AV = Apparent viscosity (1,044)
FM = Flexural modulus (348 / 2,408)	FS = Flexural strength (228 / 2,352)	ESSC = Engineering stress-strain curve (tension) (3,543)
ESSCC = Engineering stress-strain curve (compression) (164)	CRM = Creep modulus (876)	RPB = Relative permeability (389)
AP = Absolute permeability (389)	BH = B-H curve (417)	HB = H-B curve (417)
CL = Core loss (453)	EP = Exciting Power (138)	DCRPT = Relative permittivity (3,018)
DF = Dissipation factor (2,689)	RIW = Refractive index vs λ (5,345)	RIT = Refractive index vs T (4,261 / 291)
OTWL = Optical transmission vs λ (1,664)	S = Seebeck coefficient (1,172 / 42)

In the above property list the number after the property is the number of curves available, if there is a second number this is the number of single point values (values at RT only) and is not included in the first number.

Data in Version 9.89

ABS (acrylonitrile butadiene styrene)	Acetal/POM (polyoxymethylene)	Acids	Aluminum alloys
Bimetal alloys	Borides	Carbides	Carbons
Cast irons	Ceramic matrix composites	Cermets	Circuit boards & Antenna substrates
Cobalt alloys	Complex oxides, Silicates, & Slags	Controlled expansion alloys	Copper alloys
DAP & DAIP (diallyl (ortho-, iso-) phthalates)	ECTFE (polyethylene chlorotrifluoroethylene)	Electro-ceramics	Elements
Epoxies	EVA (ethylene-vinyl acetate)	Fluorides	Foods
Glasses	High entropy & Equiatomic alloys	Hydrides	Intermetallics
Iron alloys	LCP (liquid crystal polymer)	m-PPE (modified polyphenylene ether)	Magnesium alloys
Magnetic alloys & Electrical steels	Metal matrix composites	Metallic glasses	Minerals, Rocks, & Soils
Miscellaneous polymer composites	Miscellaneous polymers	Mold materials	Nickel alloys
Nitrides & Oxynitrides	Nylons & PA/PI (polyamides)	Organics & Hydrocarbons mixtures	Organics, Hydrocarbons, & Lubricants
Other materials	Oxides	PAEK & PEEK (polyaryletherketone)	PAI (polyamide-imide)
PARA (polyarylamide)	Parylenes & Polyolefins	PBT (polybutylene terephthalate) & PBT/PET	PC (polycarbonates) & blends
PCT (polycyclohexylenedimethylene terephthalate)	PE (polyethylene)	PEBA (polyether block amide)	PEI (polyetherimide)
PES/PESU (polyether sulfone)	PET (polyethylene terephthalate)	PFA & ETFE (fluorocarbons)	PLA (polylactic acid)
PMMA, PMMI, & Acrylics	Polyesters	PP (polypropylenes)	PPA (polyphthalamides)
PPE/PA (polyphenylene ether/polyamide)	PPE/PP (polyphenylene ether/polyproplyene)	PPE/PS (polyphenylene ether/polystyrene)	PPE/TPE, TPV, & SEBS
PPS (polyphenylene sulfide)	PPSU/PPSF (polyphenyl sulfone)	Precious metal alloys	PSU (polysulfone)
PVF/PVDF/PVC (poly(vinyl/idene fluoride/chloride))	Refractory metal alloys	Resistance alloys	Salts (binary mixtures; Ag-CaF)
Salts (binary mixtures; Ca(NO₂)₂-KBr)	Salts (binary mixtures; KCHO₂-LiClO₄)	Salts (binary mixtures; LiF-Zn)	Salts (monatomic; Br & Cl)
Salts (monatomic; F & I)	Salts (monatomic; S)	Salts (polyatomic)	Salts (ternary mixtures)
Semi/Superconductors & Optical materials	Silicides	Silicones & Elastomers	Solders, Brazes, & Low melting alloys
Structural foams	TCP (thermally conductive polymers)	Thermal coatings	Thermal insulation materials
Thermocouple alloys	Thermoelectrics	Titanium alloys	Tool steels
TPC (thermoplastic copolyester elastomer)	UR, PU, & TPU (thermoset polyurethanes)	Woods	Zinc alloys

Properties with a * are single point room temperature values only.

Elements	Property : Condition // Data range
Hydrogen (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| normal H₂ \|\| -259 °C to -240 °C (-434 °F to -400 °F) D : liquid \|\| para H₂ \|\| -259 °C to -241 °C (-434 °F to -402 °F) D : gas \|\| normal H₂ \|\| -253 °C to 2727 °C (-424 °F to 4940 °F) DLL : liquid \|\| normal H₂ \|\| -259 °C to -240 °C (-434 °F to -400 °F) DLL : liquid \|\| para H₂ \|\| -259 °C to -241 °C (-434 °F to -402 °F) MTE : liquid \|\| normal H₂ \|\| -259 °C to -240 °C (-434 °F to -400 °F) MTE : liquid \|\| para H₂ \|\| -259 °C to -241 °C (-434 °F to -402 °F) TC : solid \|\| -268 °C to -256 °C (-451 °F to -429 °F) TC : liquid \|\| normal H₂ \|\| -258 °C to -240 °C (-433 °F to -400 °F) TC : liquid \|\| para H₂ \|\| -258 °C to -240 °C (-433 °F to -400 °F) TC : gas \|\| normal H₂ \|\| -253 °C to 727 °C (-424 °F to 1340 °F) TC : vapor \|\| normal H₂ \|\| -258 °C to -240 °C (-433 °F to -400 °F) TD : liquid \|\| para H₂ \|\| -258 °C to -242 °C (-433 °F to -403 °F) TD : gas \|\| normal H₂ \|\| -253 °C to 727 °C (-424 °F to 1340 °F) SH : liquid \|\| para H₂ \|\| -258 °C to -242 °C (-433 °F to -403 °F) SH : gas \|\| H \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| normal H₂ \|\| -273 °C to 19727 °C (-460 °F to 35540 °F) HC : liquid \|\| para H₂ \|\| -258 °C to -242 °C (-433 °F to -403 °F) HC : gas \|\| H \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| normal H₂ \|\| -273 °C to 19727 °C (-460 °F to 35540 °F) VP : liquid \|\| normal H₂ \|\| -259 °C to -241 °C (-434 °F to -401 °F) VP : liquid \|\| para H₂ \|\| -259 °C to -240 °C (-434 °F to -400 °F) Vis : liquid \|\| -259 °C to -252 °C (-433 °F to -422 °F) Vis : gas \|\| normal H₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| normal H₂ \|\| -258 °C to -253 °C (-433 °F to -424 °F)
Helium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to -246 °C (-460 °F to -411 °F) D : saturated liquid \|\| -271 °C to -268 °C (-456 °F to -450 °F) D : gas \|\| -269 °C to 2727 °C (-452 °F to 4940 °F) DLL : solid \|\| -273 °C to -246 °C (-460 °F to -411 °F) DLL : saturated liquid \|\| -271 °C to -268 °C (-456 °F to -450 °F) MTE : solid \|\| -273 °C to -246 °C (-460 °F to -411 °F) MTE : saturated liquid \|\| -271 °C to -268 °C (-456 °F to -450 °F) TC : liquid \|\| -271 °C to -268 °C (-455 °F to -451 °F) TC : gas \|\| -272 °C to 2227 °C (-458 °F to 4040 °F) TD : liquid \|\| -271 °C to -268 °C (-455 °F to -451 °F) TD : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) SH : liquid \|\| -271 °C to -268 °C (-456 °F to -451 °F) SH : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : liquid \|\| -271 °C to -268 °C (-456 °F to -451 °F) HC : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : liquid \|\| -271 °C to -268 °C (-456 °F to -450 °F) Vis : liquid \|\| -271 °C to -269 °C (-456 °F to -452 °F) Vis : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) ST : liquid \|\| helium I \|\| -272 °C to -268 °C (-458 °F to -451 °F) ST : liquid \|\| helium III \|\| -273 °C to -270 °C (-460 °F to -454 °F)
Lithium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 115 °C (-460 °F to 239 °F) D : liquid \|\| 181 °C to 2927 °C (358 °F to 5300 °F) DLL : solid \|\| -273 °C to 115 °C (-460 °F to 239 °F) DLL : liquid \|\| 181 °C to 2927 °C (358 °F to 5300 °F) MTE : solid \|\| -273 °C to 115 °C (-460 °F to 239 °F) MTE : liquid \|\| 181 °C to 2927 °C (358 °F to 5300 °F) CTE : solid \|\| -33 °C to 115 °C (-28 °F to 239 °F) CTE : liquid \|\| 181 °C to 2527 °C (358 °F to 4580 °F) E : solid \|\| -195 °C to 25 °C (-319 °F to 77 °F) G : solid \|\| -195 °C to 25 °C (-319 °F to 77 °F) v : solid \|\| -195 °C to 25 °C (-319 °F to 77 °F) K : solid \|\| -195 °C to 25 °C (-319 °F to 77 °F) K : liquid \|\| 181 °C to 1727 °C (358 °F to 3140 °F) TC : solid \|\| -273 °C to 181 °C (-460 °F to 358 °F) TC : liquid \|\| 181 °C to 3727 °C (358 °F to 6740 °F) TC : gas \|\| Li, ideal gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| Li₂, ideal gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| at 500 Pa (0.073 psi) \|\| 827 °C to 2227 °C (1520 °F to 4040 °F) TC : gas \|\| at 1 kPa (0.145 psi) \|\| 927 °C to 2227 °C (1700 °F to 4040 °F) TC : gas \|\| at 5 kPa (0.725 psi) \|\| 1027 °C to 2227 °C (1880 °F to 4040 °F) TC : gas \|\| at 10 kPa (1.45 psi) \|\| 1127 °C to 2227 °C (2060 °F to 4040 °F) TC : gas \|\| at 30 kPa (4.35 psi) \|\| 1227 °C to 2227 °C (2240 °F to 4040 °F) TC : gas \|\| at 80 kPa (11.6 psi) \|\| 1327 °C to 2227 °C (2420 °F to 4040 °F) TC : gas \|\| at 100 kPa (14.5 psi) \|\| 1427 °C to 2227 °C (2600 °F to 4040 °F) TC : gas \|\| at 200 kPa (29.0 psi) \|\| 1527 °C to 2227 °C (2780 °F to 4040 °F) TC : gas \|\| at 400 kPa (58.0 psi) \|\| 1627 °C to 2227 °C (2960 °F to 4040 °F) TC : gas \|\| at 600 kPa (87.0 psi) \|\| 1727 °C to 2227 °C (3140 °F to 4040 °F) TC : gas \|\| at 800 kPa (116 psi) \|\| 1727 °C to 2227 °C (3140 °F to 4040 °F) TC : gas \|\| at saturation \|\| 527 °C to 2227 °C (980 °F to 4040 °F) TD : solid \|\| -270 °C to 115 °C (-454 °F to 239 °F) TD : liquid \|\| 181 °C to 1347 °C (358 °F to 2457 °F) SH : solid \|\| -273 °C to 180 °C (-460 °F to 357 °F) SH : liquid \|\| 180 °C to 1347 °C (357 °F to 2456 °F) SH : gas \|\| Li \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| Li₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -273 °C to 180 °C (-460 °F to 357 °F) HC : liquid \|\| 180 °C to 1347 °C (357 °F to 2456 °F) HC : gas \|\| Li \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| Li₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| 20 °C to 181 °C (68 °F to 358 °F) VP : liquid \|\| 181 °C to 1342 °C (358 °F to 2447 °F) Vis : liquid \|\| 182 °C to 1227 °C (359 °F to 2240 °F) Vis : gas \|\| Li, ideal gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| Li₂, ideal gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| at 500 Pa (0.073 psi) \|\| 827 °C to 2227 °C (1520 °F to 4040 °F) Vis : gas \|\| at 1 kPa (0.145 psi) \|\| 927 °C to 2227 °C (1700 °F to 4040 °F) Vis : gas \|\| at 5 kPa (0.725 psi) \|\| 1027 °C to 2227 °C (1880 °F to 4040 °F) Vis : gas \|\| at 10 kPa (1.45 psi) \|\| 1127 °C to 2227 °C (2060 °F to 4040 °F) Vis : gas \|\| at 30 kPa (4.35 psi) \|\| 1227 °C to 2227 °C (2240 °F to 4040 °F) Vis : gas \|\| at 80 kPa (11.6 psi) \|\| 1327 °C to 2227 °C (2420 °F to 4040 °F) Vis : gas \|\| at 100 kPa (14.5 psi) \|\| 1427 °C to 2227 °C (2600 °F to 4040 °F) Vis : gas \|\| at 200 kPa (29.0 psi) \|\| 1527 °C to 2227 °C (2780 °F to 4040 °F) Vis : gas \|\| at 400 kPa (58.0 psi) \|\| 1627 °C to 2227 °C (2960 °F to 4040 °F) Vis : gas \|\| at 600 kPa (87.0 psi) \|\| 1727 °C to 2227 °C (3140 °F to 4040 °F) Vis : gas \|\| at 800 kPa (116 psi) \|\| 1727 °C to 2227 °C (3140 °F to 4040 °F) Vis : gas \|\| at saturation \|\| 527 °C to 2227 °C (980 °F to 4040 °F) Vis : saturated vapor \|\| 1227 °C to 1727 °C (2240 °F to 3140 °F) ST : liquid \|\| 181 °C to 1000 °C (358 °F to 1832 °F) RHO : solid \|\| -272 °C to 181 °C (-458 °F to 358 °F) RHO : liquid \|\| 181 °C to 1927 °C (358 °F to 3500 °F) SIGMA : solid \|\| -272 °C to 181 °C (-458 °F to 358 °F) SIGMA : liquid \|\| 181 °C to 1927 °C (358 °F to 3500 °F)
Beryllium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) D : liquid \|\| 1287 °C to 1487 °C (2348 °F to 2708 °F) DLL : solid \|\| polycrystal \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) DLL : solid \|\| a-axis \|\| -193 °C to 1000 °C (-316 °F to 1832 °F) DLL : solid \|\| c-axis \|\| -193 °C to 1000 °C (-316 °F to 1832 °F) DLL : solid \|\| hot-pressed, longitudinal \|\| -153 °C to 27 °C (-244 °F to 80 °F) DLL : solid \|\| hot-pressed, transverse \|\| -183 °C to 27 °C (-298 °F to 80 °F) DLL : liquid \|\| 1287 °C to 1487 °C (2348 °F to 2708 °F) MTE : solid \|\| polycrystal \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) MTE : solid \|\| a-axis \|\| -193 °C to 1000 °C (-316 °F to 1832 °F) MTE : solid \|\| c-axis \|\| -193 °C to 1000 °C (-316 °F to 1832 °F) MTE : solid \|\| hot-pressed, longitudinal \|\| -153 °C to 27 °C (-244 °F to 80 °F) MTE : solid \|\| hot-pressed, transverse \|\| -183 °C to 27 °C (-298 °F to 80 °F) MTE : liquid \|\| 1287 °C to 1487 °C (2348 °F to 2708 °F) CTE : solid \|\| polycrystal \|\| 20 °C to 950 °C (68 °F to 1742 °F) CTE : solid \|\| a-axis \|\| 20 °C to 950 °C (68 °F to 1742 °F) CTE : solid \|\| c-axis \|\| 20 °C to 950 °C (68 °F to 1742 °F) CTE : solid \|\| hot-pressed, longitudinal \|\| -153 °C to 27 °C (-244 °F to 80 °F) CTE : solid \|\| hot-pressed, transverse \|\| -183 °C to 27 °C (-298 °F to 80 °F) CTE : liquid \|\| 1287 °C to 1487 °C (2348 °F to 2708 °F) E : solid \|\| -180 °C to 750 °C (-292 °F to 1382 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -273 °C to 1127 °C (-460 °F to 2060 °F) TC : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| annealed \|\| -272 °C to 1000 °C (-458 °F to 1832 °F) SH : solid \|\| -273 °C to 1270 °C (-460 °F to 2318 °F) SH : liquid \|\| 1290 °C to 1927 °C (2354 °F to 3500 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 1270 °C (-460 °F to 2318 °F) HC : liquid \|\| 1290 °C to 1927 °C (2354 °F to 3500 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : S-200E \|\| tested at 400 °C (752 °F), 5.5x10^-⁴/s \|\| 0 to 0.68 mm/mm strain SSC : S-200E \|\| tested at 500 °C (932 °F), 5.5x10^-⁴/s \|\| 0 to 0.59 mm/mm strain SSCC : S-200E \|\| tested at 400 °C (752 °F), 0.001/s \|\| 0 to 0.2 mm/mm strain SSCC : S-200E \|\| tested at 500 °C (932 °F), 0.001/s \|\| 0 to 0.2 mm/mm strain UTS : cross-rolled sheet \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : cross-rolled sheet \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : S-65B \|\| longitudinal \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : S-65B \|\| transverse \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : S-200F \|\| longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : S-200F \|\| transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : S-200E \|\| longitudinal \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : S-200E \|\| transverse \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YS : cross-rolled sheet \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : cross-rolled sheet \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : S-65B \|\| longitudinal \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : S-65B \|\| transverse \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : S-200F \|\| longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : S-200F \|\| transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : S-200E \|\| longitudinal \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YS : S-200E \|\| transverse \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YSC : cross-rolled sheet \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) YSC : cross-rolled sheet \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YSC : RM253939 grade \|\| 0.001/s strain rate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : cross-rolled sheet \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : cross-rolled sheet \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : S-65B \|\| longitudinal \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : S-65B \|\| transverse \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : S-200F \|\| longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : S-200F \|\| transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : S-200E \|\| longitudinal \|\| 20 °C to 1100 °C (68 °F to 2012 °F) %El : S-200E \|\| transverse \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SR : cross-rolled sheet \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h SR : cross-rolled sheet \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h SR : cross-rolled sheet \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h FSN : cross-rolled sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cross-rolled sheet, smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cross-rolled sheet, smooth \|\| tested at 316 °C (600 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cross-rolled sheet, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cross-rolled sheet, notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cross-rolled sheet, notched \|\| tested at 316 °C (600 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.5% plastic strain, cross-rolled sheet \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, cross-rolled sheet \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, cross-rolled sheet \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h HE : solid \|\| polished \|\| -23 °C to 727 °C (-10 °F to 1340 °F) NE : solid \|\| oxidized in steam at 700 °C (1292 °F) \|\| 318 °C to 851 °C (604 °F to 1564 °F) NE : solid \|\| condition not specified \|\| 827 °C to 1220 °C (1520 °F to 2228 °F) VP : solid \|\| 20 °C to 1288 °C (68 °F to 2350 °F) VP : liquid \|\| 1287 °C to 1527 °C (2348 °F to 2780 °F) Vis : liquid \|\| 1287 °C to 1787 °C (2348 °F to 3248 °F) Vis : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 1283 °C to 1527 °C (2341 °F to 2780 °F) RHO : solid \|\| -272 °C to 1227 °C (-458 °F to 2240 °F) SIGMA : solid \|\| -272 °C to 1227 °C (-458 °F to 2240 °F) RIW : measured in vacuum \|\| tested at 20 °C (68 °F) \|\| 5 nm to 60 nm
Boron (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) TC : solid \|\| annealed \|\| -273 °C to 827 °C (-460 °F to 1520 °F) TC : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| annealed \|\| -173 °C to 27 °C (-280 °F to 80 °F) SH : solid \|\| -173 °C to 2077 °C (-280 °F to 3770 °F) SH : liquid \|\| 2077 °C to 5727 °C (3770 °F to 10340 °F) SH : gas \|\| B \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| B₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -173 °C to 2077 °C (-280 °F to 3770 °F) HC : liquid \|\| 2077 °C to 5727 °C (3770 °F to 10340 °F) HC : gas \|\| B \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| B₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 1370 °C to 2076 °C (2498 °F to 3769 °F) VP : liquid \|\| 2076 °C to 3672 °C (3769 °F to 6641 °F) Vis : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 2084 °C to 2810 °C (3783 °F to 5090 °F)
Carbon	see Carbons
Nitrogen (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : saturated liquid \|\| -210 °C to -147 °C (-346 °F to -233 °F) D : gas \|\| -196 °C to 2727 °C (-321 °F to 4940 °F) DLL : saturated liquid \|\| -210 °C to -147 °C (-346 °F to -233 °F) MTE : saturated liquid \|\| -210 °C to -147 °C (-346 °F to -233 °F) CTE : saturated liquid \|\| -210 °C to -161 °C (-346 °F to -258 °F) TC : solid \|\| -269 °C to -247 °C (-452 °F to -413 °F) TC : liquid \|\| -210 °C to -148 °C (-346 °F to -235 °F) TC : gas \|\| -195 °C to 3000 °C (-319 °F to 5432 °F) TC : vapor \|\| -213 °C to -148 °C (-352 °F to -235 °F) TD : liquid \|\| -209 °C to -195 °C (-344 °F to -319 °F) TD : gas \|\| -173 °C to 2727 °C (-280 °F to 4940 °F) SH : solid \|\| N₂ \|\| -258 °C to -210 °C (-433 °F to -346 °F) SH : liquid \|\| N₂ \|\| -209 °C to -195 °C (-344 °F to -319 °F) SH : gas \|\| N₂ \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : solid \|\| N₂ \|\| -258 °C to -210 °C (-433 °F to -346 °F) HC : liquid \|\| N₂ \|\| -209 °C to -195 °C (-344 °F to -319 °F) HC : gas \|\| N₂ \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : solid \|\| -223 °C to -213 °C (-370 °F to -352 °F) VP : liquid \|\| -208 °C to -148 °C (-343 °F to -235 °F) Vis : liquid \|\| -207 °C to -152 °C (-340 °F to -242 °F) Vis : gas \|\| -193 °C to 1877 °C (-316 °F to 3410 °F) ST : liquid \|\| -209 °C to -147 °C (-344 °F to -233 °F)
Oxygen (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| -218 °C to -120 °C (-361 °F to -184 °F) D : gas \|\| -193 °C to 2727 °C (-316 °F to 4940 °F) DLL : liquid \|\| -218 °C to -120 °C (-361 °F to -184 °F) MTE : liquid \|\| -218 °C to -120 °C (-361 °F to -184 °F) CTE : liquid \|\| -218 °C to -124 °C (-361 °F to -191 °F) TC : saturated liquid \|\| -203 °C to -119 °C (-334 °F to -181 °F) TC : gas \|\| O \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| O₂ \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) TC : saturated vapor \|\| -203 °C to -119 °C (-334 °F to -181 °F) TC : fluid \|\| at 100 kPa (14.5 psi), atmospheric pressure \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 1 MPa (145 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 2 MPa (290 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 3 MPa (435 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 4 MPa (580 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 5 MPa (725 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 6 MPa (870 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 7 MPa (1.02 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 8 MPa (1.16 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 9 MPa (1.31 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 10 MPa (1.45 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 15 MPa (2.18 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 20 MPa (2.90 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 25 MPa (3.63 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 30 MPa (4.35 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 35 MPa (5.08 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 40 MPa (5.80 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 45 MPa (6.53 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 50 MPa (7.25 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) TC : fluid \|\| at 60 MPa (8.70 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) TC : fluid \|\| at 70 MPa (10.2 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) TC : fluid \|\| at 80 MPa (11.6 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) TC : fluid \|\| at 90 MPa (13.1 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) TC : fluid \|\| at 100 MPa (14.5 ksi) \|\| -183 °C to 1127 °C (-298 °F to 2060 °F) TD : liquid \|\| -203 °C to -183 °C (-334 °F to -298 °F) TD : gas \|\| O₂ \|\| -173 °C to 2727 °C (-280 °F to 4940 °F) SH : solid \|\| O₂ \|\| -260 °C to -219 °C (-436 °F to -362 °F) SH : liquid \|\| O₂ \|\| -219 °C to -183 °C (-362 °F to -298 °F) SH : gas \|\| O \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| O₂ \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) SH : gas \|\| O₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| O₂ \|\| -260 °C to -219 °C (-436 °F to -362 °F) HC : liquid \|\| O₂ \|\| -219 °C to -183 °C (-362 °F to -298 °F) HC : gas \|\| O \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| O₂ \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : gas \|\| O₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : liquid \|\| -218 °C to -188 °C (-361 °F to -307 °F) Vis : saturated liquid \|\| -203 °C to -119 °C (-334 °F to -182 °F) Vis : gas \|\| O \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| O₂ \|\| -203 °C to 2327 °C (-334 °F to 4220 °F) Vis : saturated vapor \|\| -203 °C to -119 °C (-334 °F to -182 °F) Vis : fluid \|\| at 100 kPa (14.5 psi), atmospheric pressure \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 1 MPa (145 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 2 MPa (290 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 3 MPa (435 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 4 MPa (580 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 5 MPa (725 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 6 MPa (870 psi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 7 MPa (1.02 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 8 MPa (1.16 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 9 MPa (1.31 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 10 MPa (1.45 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 15 MPa (2.18 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 20 MPa (2.90 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 25 MPa (3.63 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 30 MPa (4.35 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 35 MPa (5.08 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 40 MPa (5.80 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 45 MPa (6.53 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 50 MPa (7.25 ksi) \|\| -203 °C to 1127 °C (-334 °F to 2060 °F) Vis : fluid \|\| at 60 MPa (8.70 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) Vis : fluid \|\| at 70 MPa (10.2 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) Vis : fluid \|\| at 80 MPa (11.6 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) Vis : fluid \|\| at 90 MPa (13.1 ksi) \|\| -193 °C to 1127 °C (-316 °F to 2060 °F) Vis : fluid \|\| at 100 MPa (14.5 ksi) \|\| -183 °C to 1127 °C (-298 °F to 2060 °F) ST : liquid \|\| -202 °C to -184 °C (-332 °F to -299 °F)
Fluorine (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : saturated liquid \|\| -208 °C to -168 °C (-343 °F to -271 °F) D : gas \|\| -188 °C to 2727 °C (-307 °F to 4940 °F) DLL : saturated liquid \|\| -208 °C to -168 °C (-343 °F to -271 °F) MTE : saturated liquid \|\| -208 °C to -168 °C (-343 °F to -271 °F) CTE : saturated liquid \|\| -208 °C to -168 °C (-343 °F to -271 °F) TC : liquid \|\| -223 °C to -129 °C (-370 °F to -200 °F) TC : gas \|\| -193 °C to 527 °C (-316 °F to 980 °F) TC : vapor \|\| -223 °C to -129 °C (-370 °F to -200 °F) TD : gas \|\| F₂ \|\| 20 °C to 527 °C (68 °F to 980 °F) SH : gas \|\| F \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| F₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| F \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| F₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : liquid \|\| F₂ \|\| -216 °C to -188 °C (-357 °F to -307 °F) Vis : liquid \|\| -204 °C to -189 °C (-335 °F to -308 °F) Vis : gas \|\| F₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| -202 °C to -188 °C (-332 °F to -307 °F)
Neon (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : saturated liquid \|\| -249 °C to -229 °C (-416 °F to -380 °F) D : gas \|\| -246 °C to 2727 °C (-411 °F to 4940 °F) DLL : saturated liquid \|\| -249 °C to -229 °C (-416 °F to -380 °F) MTE : saturated liquid \|\| -249 °C to -229 °C (-416 °F to -380 °F) E : solid \|\| -265 °C to -250 °C (-445 °F to -418 °F) TC : solid \|\| -272 °C to -249 °C (-458 °F to -416 °F) TC : liquid \|\| -249 °C to -229 °C (-416 °F to -380 °F) TC : gas \|\| -246 °C to 2227 °C (-411 °F to 4040 °F) TC : vapor \|\| -246 °C to -229 °C (-411 °F to -380 °F) TD : liquid \|\| -248 °C to -230 °C (-415 °F to -382 °F) TD : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) SH : solid \|\| -262 °C to -249 °C (-440 °F to -417 °F) SH : saturated liquid \|\| -248 °C to -230 °C (-415 °F to -382 °F) SH : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : solid \|\| -262 °C to -249 °C (-440 °F to -417 °F) HC : saturated liquid \|\| -248 °C to -230 °C (-415 °F to -382 °F) HC : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : solid \|\| -259 °C to -249 °C (-435 °F to -416 °F) VP : liquid \|\| -249 °C to -229 °C (-416 °F to -380 °F) Vis : liquid \|\| -248 °C to -229 °C (-415 °F to -380 °F) Vis : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) ST : liquid \|\| -249 °C to -245 °C (-416 °F to -409 °F)
Sodium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) D : liquid \|\| 98 °C to 2230 °C (208 °F to 4046 °F) DLL : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : liquid \|\| 98 °C to 2230 °C (208 °F to 4046 °F) MTE : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : liquid \|\| 98 °C to 2230 °C (208 °F to 4046 °F) CTE : solid \|\| -103 °C to 27 °C (-154 °F to 80 °F) CTE : liquid \|\| 98 °C to 1827 °C (208 °F to 3320 °F) E : solid \|\| -195 °C to 27 °C (-319 °F to 80 °F) G : solid \|\| -195 °C to 27 °C (-319 °F to 80 °F) v : solid \|\| -195 °C to 27 °C (-319 °F to 80 °F) K : solid \|\| -195 °C to 27 °C (-319 °F to 80 °F) K : liquid \|\| 98 °C to 1727 °C (208 °F to 3140 °F) TC : solid \|\| -273 °C to 98 °C (-460 °F to 208 °F) TC : liquid \|\| 98 °C to 2527 °C (208 °F to 4580 °F) TC : gas \|\| Na \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| Na₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| -272 °C to 27 °C (-458 °F to 80 °F) TD : liquid \|\| 98 °C to 2027 °C (208 °F to 3680 °F) SH : solid \|\| -273 °C to 98 °C (-460 °F to 208 °F) SH : liquid \|\| 98 °C to 2027 °C (208 °F to 3680 °F) SH : gas \|\| Na \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| Na₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -273 °C to 98 °C (-460 °F to 208 °F) HC : liquid \|\| 98 °C to 2027 °C (208 °F to 3680 °F) HC : gas \|\| Na \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| Na₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| 20 °C to 98 °C (68 °F to 208 °F) VP : liquid \|\| 98 °C to 962 °C (208 °F to 1763 °F) Vis : liquid \|\| 98 °C to 2127 °C (208 °F to 3860 °F) Vis : gas \|\| Na \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| Na₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 100 °C to 200 °C (212 °F to 392 °F) RHO : solid \|\| -272 °C to 98 °C (-458 °F to 208 °F) RHO : liquid \|\| 98 °C to 1727 °C (208 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 98 °C (-458 °F to 208 °F) SIGMA : liquid \|\| 98 °C to 1727 °C (208 °F to 3140 °F)
Magnesium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) D : liquid \|\| 650 °C to 727 °C (1202 °F to 1340 °F) DLL : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) DLL : liquid \|\| 650 °C to 727 °C (1202 °F to 1340 °F) MTE : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) MTE : liquid \|\| 650 °C to 727 °C (1202 °F to 1340 °F) CTE : liquid \|\| 650 °C to 727 °C (1202 °F to 1340 °F) E : solid \|\| -273 °C to 150 °C (-460 °F to 302 °F) G : solid \|\| -273 °C to 150 °C (-460 °F to 302 °F) v : solid \|\| -273 °C to 150 °C (-460 °F to 302 °F) K : solid \|\| -273 °C to 150 °C (-460 °F to 302 °F) TC : solid \|\| annealed \|\| -273 °C to 650 °C (-460 °F to 1202 °F) TC : liquid \|\| 650 °C to 927 °C (1202 °F to 1700 °F) TC : gas \|\| Mg \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| Mg₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| annealed \|\| -272 °C to 500 °C (-458 °F to 932 °F) TD : liquid \|\| 650 °C to 927 °C (1202 °F to 1700 °F) SH : solid \|\| -273 °C to 650 °C (-460 °F to 1202 °F) SH : liquid \|\| 650 °C to 1727 °C (1202 °F to 3140 °F) SH : gas \|\| Mg \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Mg₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 650 °C (-460 °F to 1202 °F) HC : liquid \|\| 650 °C to 1727 °C (1202 °F to 3140 °F) HC : gas \|\| Mg \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Mg₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : extruded \|\| tested at 25 °C (77 °F), 1800/s, 9 micron grain size \|\| 0 to 0.13 mm/mm strain SSC : extruded \|\| tested at 25 °C (77 °F), 1800/s, 31 micron grain size \|\| 0 to 0.12 mm/mm strain SSC : annealed \|\| tested at 25 °C (77 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.69 mm/mm strain SSC : annealed \|\| tested at -195 °C (-319 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.14 mm/mm strain SSC : annealed \|\| tested at -269.1 °C (-452.5 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.47 mm/mm strain SSCC : cast & extruded \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.14 mm/mm strain SSCC : annealed \|\| tested at 25 °C (77 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.325 mm/mm strain SSCC : annealed \|\| tested at -195 °C (-319 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.18 mm/mm strain SSCC : annealed \|\| tested at -269.1 °C (-452.5 °F), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.174 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) YS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) UCS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) YSC : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) %El : annealed, in tension \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) %El : annealed, in compression \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| -269 °C to 25 °C (-452 °F to 77 °F) FSN : in air \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1.8x10⁴ cycles to 1x10⁶ cycles FSN : in liquid helium \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 1.1x10⁴ cycles to 3x10⁶ cycles FSN : in liquid hydrogen \|\| tested at -268.9 °C (-452.1 °F), R = -1, axial, maximum stress \|\| 1.1x10⁴ cycles to 2x10⁶ cycles FSN : in liquid oxygen \|\| tested at -183.1 °C (-297.7 °F), R = -1, axial, maximum stress \|\| 2.4x10⁴ cycles to 2x10⁶ cycles VP : solid \|\| 187 °C to 650 °C (368 °F to 1202 °F) VP : liquid \|\| 650 °C to 1147 °C (1202 °F to 2096 °F) Vis : liquid \|\| 650 °C to 1727 °C (1202 °F to 3140 °F) Vis : gas \|\| Mg \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| Mg₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 697 °C to 1327 °C (1286 °F to 2420 °F) RHO : solid \|\| -272 °C to 650 °C (-458 °F to 1202 °F) RHO : liquid \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SIGMA : solid \|\| -272 °C to 650 °C (-458 °F to 1202 °F) SIGMA : liquid \|\| 649 °C to 927 °C (1200 °F to 1700 °F)
Aluminum (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| bulk \|\| -273 °C to 660 °C (-460 °F to 1221 °F) TC : solid \|\| 105 nm thin film \|\| 20 °C to 327 °C (68 °F to 620 °F) TC : solid \|\| 82 nm thin film \|\| 20 °C to 327 °C (68 °F to 620 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TC : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| bulk \|\| -253 °C to 660 °C (-424 °F to 1220 °F) TD : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) HC : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed, 99.5 \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, 240 micron grain size \|\| 0 to 0.325 mm/mm strain SSC : annealed, 99.999 \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, 34 micron grain size \|\| 0 to 0.225 mm/mm strain SSC : annealed, 99.999 \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, 170 micron grain size \|\| 0 to 0.225 mm/mm strain SSC : annealed, 99.999 \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, 240 micron grain size \|\| 0 to 0.325 mm/mm strain SSC : annealed, 99.999 \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, 580 micron grain size \|\| 0 to 0.225 mm/mm strain UTS : annealed \|\| 21 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) UTS : annealed \|\| 27 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) UTS : annealed \|\| 39 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) UTS : annealed \|\| 46 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) UTS : annealed \|\| 65 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) UTS : annealed \|\| 105 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) UTS : annealed \|\| 118 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) UTS : annealed \|\| 143 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 21 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 27 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 39 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 46 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) YS : annealed \|\| 65 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 105 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) YS : annealed \|\| 118 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) YS : annealed \|\| 143 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 21 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 27 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 39 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 46 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) %El : annealed \|\| 65 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 105 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) %El : annealed \|\| 118 micron grain size \|\| -253 °C to 600 °C (-424 °F to 1112 °F) %El : annealed \|\| 143 micron grain size \|\| -253 °C to 127 °C (-424 °F to 260 °F) FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 0.066 mm (0.0026 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 0.39 mm (0.0154 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 1.41 mm (0.0555 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 3.46 mm (0.136 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 9.74 mm (0.383 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles HE : solid \|\| electropolished \|\| -98 °C to 427 °C (-145 °F to 800 °F) HE : solid \|\| grit blasted black anodized \|\| -98 °C to 27 °C (-145 °F to 80 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) Vis : liquid \|\| 660 °C to 1827 °C (1220 °F to 3320 °F) Vis : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 660 °C to 1160 °C (1220 °F to 2120 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)
Silicon (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) D : liquid \|\| 1414 °C to 1727 °C (2577 °F to 3140 °F) DLL : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) DLL : liquid \|\| 1414 °C to 1727 °C (2577 °F to 3140 °F) MTE : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) MTE : liquid \|\| 1414 °C to 1727 °C (2577 °F to 3140 °F) CTE : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) CTE : liquid \|\| 1414 °C to 1727 °C (2577 °F to 3140 °F) E : solid \|\| polycrystal \|\| -200 °C to 650 °C (-328 °F to 1202 °F) E : solid \|\| <100> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) E : solid \|\| <110> axis \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| <111> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) G : solid \|\| polycrystal \|\| -200 °C to 650 °C (-328 °F to 1202 °F) G : solid \|\| <100> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) G : solid \|\| <111> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) v : solid \|\| polycrystal \|\| -200 °C to 650 °C (-328 °F to 1202 °F) v : solid \|\| <100> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) v : solid \|\| <111> axis \|\| -200 °C to 650 °C (-328 °F to 1202 °F) K : solid \|\| polycrystal \|\| -200 °C to 650 °C (-328 °F to 1202 °F) TC : bulk \|\| -273 °C to 1412 °C (-460 °F to 2573 °F) TC : nanowire \|\| 115 nm \|\| -248 °C to 52 °C (-415 °F to 125 °F) TC : nanowire \|\| 56 nm \|\| -248 °C to 52 °C (-415 °F to 125 °F) TC : nanowire \|\| 37 nm \|\| -248 °C to 52 °C (-415 °F to 125 °F) TC : nanowire \|\| 22 nm \|\| -248 °C to 52 °C (-415 °F to 125 °F) TC : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) TC : nanocrystalline film \|\| PECVD, 382 nm thick film, 3x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) TC : nanocrystalline film \|\| HWCVD, 594 nm thick film, no boron \|\| -188 °C to 27 °C (-307 °F to 81 °F) TC : polysilicon LPCVD film \|\| grown at 620 °C (1148 °F) \|\| -223 °C to 40 °C (-370 °F to 104 °F) TC : polysilicon LPCVD film \|\| grown at 525 °C (977 °F) \|\| -250 °C to 40 °C (-418 °F to 104 °F) TC : single crystal layer \|\| 0.42 micron thick \|\| -253 °C to 45 °C (-424 °F to 113 °F) TC : single crystal layer \|\| 0.83 micron thick \|\| -248 °C to 25 °C (-415 °F to 77 °F) TC : single crystal layer \|\| 1.6 micron thick \|\| -253 °C to 25 °C (-424 °F to 77 °F) TC : liquid \|\| 1477 °C to 1677 °C (2690 °F to 3050 °F) TC : gas \|\| Si \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| Si₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| bulk \|\| -272 °C to 727 °C (-458 °F to 1340 °F) TD : liquid \|\| 1477 °C to 1550 °C (2690 °F to 2822 °F) SH : solid \|\| -272 °C to 1412 °C (-458 °F to 2573 °F) SH : liquid \|\| 1090 °C to 1550 °C (1994 °F to 2822 °F) SH : gas \|\| Si \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Si₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Si₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 1412 °C (-458 °F to 2573 °F) HC : liquid \|\| 1090 °C to 1550 °C (1994 °F to 2822 °F) HC : gas \|\| Si \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Si₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Si₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) FSN : 2 micron thick \|\| tested at 20 °C (68 °F), R = -1, vibrating beam, stress amplitude \|\| 3.5x10⁵ cycles to 3.3x10⁸ cycles FSN : 3.5 micron thick \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 1 cycles to 1.6x10⁹ cycles HE : solid \|\| 5.5x10¹³ P doping/cm³ \|\| 200 °C to 800 °C (392 °F to 1472 °F) HE : solid \|\| 10¹⁶/cm² B implanted at 30keV \|\| 300 °C to 700 °C (572 °F to 1292 °F) HE : solid \|\| self-implanted \|\| 350 °C to 800 °C (662 °F to 1472 °F) HE : solid \|\| 3.5x10¹⁸ P doping/cm³ \|\| 280 °C to 800 °C (536 °F to 1472 °F) HE : solid \|\| 600 ohm-cm, n-type \|\| 607 °C to 1227 °C (1124 °F to 2240 °F) HE : solid \|\| 0.04 ohm-cm, n-type \|\| 607 °C to 1227 °C (1124 °F to 2240 °F) HE : solid \|\| 0.1 ohm-cm, n-type \|\| 607 °C to 1277 °C (1124 °F to 2330 °F) HE : solid \|\| 14 ohm-cm, p-type \|\| 607 °C to 1177 °C (1124 °F to 2150 °F) HE : liquid \|\| 1027 °C to 1727 °C (1880 °F to 3140 °F) VP : solid \|\| 20 °C to 1414 °C (68 °F to 2577 °F) VP : liquid \|\| 1414 °C to 3327 °C (2577 °F to 6020 °F) Vis : liquid \|\| 1414 °C to 1627 °C (2577 °F to 2960 °F) Vis : gas \|\| Si \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| Si₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 955 °C to 1557 °C (1751 °F to 2834 °F) RHO : solid \|\| ideally pure \|\| -194 °C to 800 °C (-317 °F to 1472 °F) RHO : solid \|\| 0.0005% B \|\| -190 °C to 493 °C (-310 °F to 919 °F) RHO : solid \|\| 0.001% B \|\| -190 °C to 548 °C (-310 °F to 1018 °F) RHO : solid \|\| 0.002% B \|\| -190 °C to 632 °C (-310 °F to 1169 °F) RHO : solid \|\| 0.005% B \|\| -190 °C to 725 °C (-310 °F to 1337 °F) RHO : solid \|\| 0.01% B \|\| -190 °C to 634 °C (-310 °F to 1173 °F) RHO : solid \|\| 0.1% B \|\| -190 °C to 63 °C (-310 °F to 145 °F) RHO : solid \|\| 1% B \|\| -190 °C to 163 °C (-310 °F to 325 °F) RHO : solid \|\| 0.001% P \|\| -190 °C to 727 °C (-310 °F to 1340 °F) RHO : solid \|\| 0.0057% P \|\| -190 °C to 548 °C (-310 °F to 1018 °F) RHO : solid \|\| 0.1% P \|\| -190 °C to 30 °C (-310 °F to 86 °F) RHO : solid \|\| 1% P \|\| -190 °C to 233 °C (-310 °F to 451 °F) RHO : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) RHO : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) RHO : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) RHO : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) SIGMA : solid \|\| ideally pure \|\| -194 °C to 800 °C (-317 °F to 1472 °F) SIGMA : solid \|\| 0.0005% B \|\| -190 °C to 493 °C (-310 °F to 919 °F) SIGMA : solid \|\| 0.001% B \|\| -190 °C to 548 °C (-310 °F to 1018 °F) SIGMA : solid \|\| 0.002% B \|\| -190 °C to 632 °C (-310 °F to 1169 °F) SIGMA : solid \|\| 0.005% B \|\| -190 °C to 725 °C (-310 °F to 1337 °F) SIGMA : solid \|\| 0.01% B \|\| -190 °C to 634 °C (-310 °F to 1173 °F) SIGMA : solid \|\| 0.1% B \|\| -190 °C to 63 °C (-310 °F to 145 °F) SIGMA : solid \|\| 1% B \|\| -190 °C to 163 °C (-310 °F to 325 °F) SIGMA : solid \|\| 0.001% P \|\| -190 °C to 727 °C (-310 °F to 1340 °F) SIGMA : solid \|\| 0.0057% P \|\| -190 °C to 548 °C (-310 °F to 1018 °F) SIGMA : solid \|\| 0.1% P \|\| -190 °C to 30 °C (-310 °F to 86 °F) SIGMA : solid \|\| 1% P \|\| -190 °C to 233 °C (-310 °F to 451 °F) SIGMA : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) SIGMA : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) SIGMA : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) SIGMA : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) RIW : measured in vacuum \|\| tested at -243.1 °C (-405.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -233.1 °C (-387.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -223.1 °C (-369.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -213.1 °C (-351.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -203.1 °C (-333.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -193.1 °C (-315.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -183.1 °C (-297.7 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -173 °C (-280 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -123 °C (-190 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -73 °C (-100 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -23 °C (-10 °F) \|\| 1.1 µm to 5.5 µm RIW : measured in vacuum \|\| tested at 22 °C (71 °F) \|\| 1.1 µm to 5.5 µm RIT : measured in vacuum \|\| measured at 1100 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 1200 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 1300 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 1400 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 1500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 2000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 2500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 3000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 3500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 4000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 4500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 5000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 5500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) S : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) S : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) S : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F) S : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| -188 °C to 27 °C (-307 °F to 81 °F)
Phosphorus	D* : solid \|\| room temperature value TC : gas \|\| P \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| P₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| P₄ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) SH : solid \|\| white \|\| 20 °C to 44 °C (68 °F to 111 °F) SH : solid \|\| red \|\| 20 °C to 597 °C (68 °F to 1106 °F) SH : liquid \|\| 44 °C to 597 °C (111 °F to 1106 °F) SH : gas \|\| P \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| P₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| P₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| white \|\| 20 °C to 44 °C (68 °F to 111 °F) HC : solid \|\| red \|\| 20 °C to 597 °C (68 °F to 1106 °F) HC : liquid \|\| 44 °C to 597 °C (111 °F to 1106 °F) HC : gas \|\| P \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| P₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| P₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : liquid \|\| 46 °C to 443 °C (115 °F to 829 °F) Vis : gas \|\| P \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| P₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| P₄ \|\| 20 °C to 4727 °C (68 °F to 8540 °F)
Sulfur (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -175 °C to 24 °C (-283 °F to 75 °F) DLL : orthorhombic \|\| a-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) DLL : orthorhombic \|\| b-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) DLL : orthorhombic \|\| c-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) DLL : orthorhombic \|\| polycrystal \|\| -175 °C to 24 °C (-283 °F to 75 °F) MTE : orthorhombic \|\| a-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) MTE : orthorhombic \|\| b-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) MTE : orthorhombic \|\| c-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) MTE : orthorhombic \|\| polycrystal \|\| -175 °C to 24 °C (-283 °F to 75 °F) CTE : orthorhombic \|\| a-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) CTE : orthorhombic \|\| b-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) CTE : orthorhombic \|\| c-axis \|\| -175 °C to 24 °C (-283 °F to 75 °F) CTE : orthorhombic \|\| polycrystal \|\| -175 °C to 24 °C (-283 °F to 75 °F) TC : solid \|\| crystalline \|\| -273 °C to 119 °C (-460 °F to 246 °F) TC : solid \|\| amorphous \|\| -183 °C to 77 °C (-298 °F to 170 °F) TC : liquid \|\| 119 °C to 327 °C (246 °F to 620 °F) TC : gas \|\| S \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| S₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| 20 °C to 24 °C (68 °F to 75 °F) TD : liquid \|\| 165 °C to 400 °C (329 °F to 752 °F) SH : solid \|\| 20 °C to 115 °C (68 °F to 239 °F) SH : liquid \|\| 115 °C to 444 °C (239 °F to 831 °F) SH : gas \|\| S \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₃ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₄ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₅ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₆ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₇ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| S₈ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| 20 °C to 115 °C (68 °F to 239 °F) HC : liquid \|\| 115 °C to 444 °C (239 °F to 831 °F) HC : gas \|\| S \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₃ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₄ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₅ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₆ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₇ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| S₈ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| -33 °C to 115 °C (-28 °F to 239 °F) VP : liquid \|\| 115 °C to 467 °C (239 °F to 872 °F) Vis : gas \|\| S \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| S₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 114 °C to 185 °C (237 °F to 365 °F) RHO : liquid \|\| 348 °C to 900 °C (658 °F to 1652 °F) SIGMA : liquid \|\| 348 °C to 900 °C (658 °F to 1652 °F)
Chlorine (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : saturated liquid \|\| -46 °C to 144 °C (-51 °F to 291 °F) D : gas \|\| -34 °C to 2727 °C (-29 °F to 4940 °F) DLL : saturated liquid \|\| -46 °C to 144 °C (-51 °F to 291 °F) MTE : saturated liquid \|\| -46 °C to 144 °C (-51 °F to 291 °F) TC : liquid \|\| -101 °C to 144 °C (-150 °F to 291 °F) TC : gas \|\| -34 °C to 427 °C (-29 °F to 800 °F) TC : vapor \|\| -73 °C to 144 °C (-100 °F to 291 °F) TD : gas \|\| Cl₂ \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : gas \|\| Cl \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| Cl₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| Cl \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| Cl₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| Cl₂ \|\| -135 °C to -101 °C (-211 °F to -150 °F) VP : liquid \|\| Cl₂ \|\| -101 °C to -35 °C (-150 °F to -31 °F) VP : gas \|\| -33 °C to 137 °C (-28 °F to 278 °F) Vis : gas \|\| Cl₂ \|\| -33 °C to 4727 °C (-28 °F to 8540 °F) ST : liquid \|\| -80 °C to -30 °C (-112 °F to -22 °F)
Argon (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) D : saturated liquid \|\| -189 °C to -183 °C (-308 °F to -298 °F) D : gas \|\| -186 °C to 2727 °C (-303 °F to 4940 °F) DLL : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) DLL : saturated liquid \|\| -189 °C to -183 °C (-308 °F to -298 °F) MTE : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) MTE : saturated liquid \|\| -189 °C to -183 °C (-308 °F to -298 °F) CTE : saturated liquid \|\| -189 °C to -183 °C (-308 °F to -298 °F) K : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) TC : solid \|\| -265 °C to -193 °C (-445 °F to -316 °F) TC : liquid \|\| -189 °C to -122 °C (-308 °F to -188 °F) TC : gas \|\| -185 °C to 2227 °C (-301 °F to 4040 °F) TC : vapor \|\| -188 °C to -122 °C (-307 °F to -188 °F) TD : solid \|\| -265 °C to -193 °C (-445 °F to -316 °F) TD : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) SH : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) SH : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : solid \|\| -269 °C to -190 °C (-452 °F to -310 °F) HC : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : solid \|\| -223 °C to -193 °C (-370 °F to -316 °F) VP : liquid \|\| -188 °C to -123 °C (-307 °F to -190 °F) Vis : saturated liquid \|\| -189 °C to -124 °C (-308 °F to -191 °F) Vis : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) ST : liquid \|\| -189 °C to -181 °C (-308 °F to -294 °F)
Potassium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| 64 °C to 1350 °C (147 °F to 2462 °F) DLL : liquid \|\| 64 °C to 1350 °C (147 °F to 2462 °F) MTE : liquid \|\| 64 °C to 1350 °C (147 °F to 2462 °F) CTE : liquid \|\| 64 °C to 1350 °C (147 °F to 2462 °F) E : solid \|\| -269 °C to 22 °C (-452 °F to 71 °F) G : solid \|\| -269 °C to 22 °C (-452 °F to 71 °F) v : solid \|\| -269 °C to 22 °C (-452 °F to 71 °F) K : solid \|\| -269 °C to 22 °C (-452 °F to 71 °F) K : liquid \|\| 64 °C to 1527 °C (147 °F to 2780 °F) TC : solid \|\| -273 °C to 64 °C (-460 °F to 147 °F) TC : liquid \|\| 64 °C to 2127 °C (147 °F to 3860 °F) TD : liquid \|\| 64 °C to 1327 °C (147 °F to 2420 °F) SH : solid \|\| -273 °C to 63 °C (-460 °F to 146 °F) SH : liquid \|\| 63 °C to 1327 °C (146 °F to 2420 °F) SH : gas \|\| K \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| K₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -273 °C to 63 °C (-460 °F to 146 °F) HC : liquid \|\| 63 °C to 1327 °C (146 °F to 2420 °F) HC : gas \|\| K \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| K₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSC : unknown strain rate \|\| tested at -265.6 °C (-446.2 °F) \|\| 0 to 0.26 mm/mm strain SSC : unknown strain rate \|\| tested at -256.6 °C (-430 °F) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at -251.4 °C (-420.6 °F) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at -261.1 °C (-438.1 °F) \|\| 0 to 0.26 mm/mm strain SSC : unknown strain rate \|\| tested at -233.1 °C (-387.7 °F) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at -243.1 °C (-405.7 °F) \|\| 0 to 0.3 mm/mm strain SSC : unknown strain rate \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at -78 °C (-109 °F) \|\| 0 to 0.26 mm/mm strain UTS : solid \|\| -268 °C to -78 °C (-451 °F to -109 °F) YS : solid \|\| -268 °C to -78 °C (-451 °F to -109 °F) %El : solid \|\| -268 °C to -78 °C (-451 °F to -109 °F) VP : solid \|\| 20 °C to 64 °C (68 °F to 147 °F) VP : liquid \|\| 64 °C to 1327 °C (147 °F to 2420 °F) Vis : liquid \|\| 63 °C to 1727 °C (145 °F to 3140 °F) ST : liquid \|\| 64 °C to 727 °C (147 °F to 1340 °F) RHO : solid \|\| -272 °C to 63 °C (-458 °F to 145 °F) RHO : liquid \|\| 63 °C to 1727 °C (145 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 63 °C (-458 °F to 145 °F) SIGMA : liquid \|\| 63 °C to 1727 °C (145 °F to 3140 °F)
Calcium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -196 °C to 40 °C (-321 °F to 104 °F) D : liquid \|\| 812 °C to 950 °C (1493 °F to 1742 °F) DLL : solid \|\| -196 °C to 40 °C (-321 °F to 104 °F) DLL : liquid \|\| 812 °C to 950 °C (1493 °F to 1742 °F) MTE : solid \|\| -196 °C to 40 °C (-321 °F to 104 °F) MTE : liquid \|\| 812 °C to 950 °C (1493 °F to 1742 °F) CTE : solid \|\| -196 °C to 40 °C (-321 °F to 104 °F) CTE : liquid \|\| 812 °C to 950 °C (1493 °F to 1742 °F) E : solid \|\| -180 °C to 600 °C (-292 °F to 1112 °F) TC : solid \|\| -73 °C to 727 °C (-100 °F to 1340 °F) TD : solid \|\| -73 °C to 40 °C (-100 °F to 104 °F) SH : solid \|\| -273 °C to 842 °C (-460 °F to 1547 °F) SH : liquid \|\| 842 °C to 1727 °C (1547 °F to 3140 °F) SH : gas \|\| Ca \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Ca₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 842 °C (-460 °F to 1547 °F) HC : liquid \|\| 842 °C to 1727 °C (1547 °F to 3140 °F) HC : gas \|\| Ca \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Ca₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 283 °C to 842 °C (541 °F to 1547 °F) VP : liquid \|\| 842 °C to 1555 °C (1547 °F to 2831 °F) Vis : liquid \|\| 812 °C to 1727 °C (1493 °F to 3140 °F) ST : liquid \|\| 850 °C to 1573 °C (1562 °F to 2863 °F) RHO : solid \|\| -272 °C to 840 °C (-458 °F to 1544 °F) RHO : liquid \|\| 840 °C to 950 °C (1544 °F to 1742 °F) SIGMA : solid \|\| -272 °C to 840 °C (-458 °F to 1544 °F) SIGMA : liquid \|\| 840 °C to 950 °C (1544 °F to 1742 °F)
Scandium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) D : liquid \|\| 1541 °C to 1741 °C (2806 °F to 3166 °F) DLL : solid \|\| polycrystal \|\| 0 °C to 1000 °C (32 °F to 1832 °F) DLL : solid \|\| a-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) DLL : solid \|\| c-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) DLL : liquid \|\| 1541 °C to 1741 °C (2806 °F to 3166 °F) MTE : solid \|\| polycrystal \|\| 0 °C to 1000 °C (32 °F to 1832 °F) MTE : solid \|\| a-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) MTE : solid \|\| c-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) MTE : liquid \|\| 1541 °C to 1741 °C (2806 °F to 3166 °F) CTE : solid \|\| polycrystal \|\| 0 °C to 1000 °C (32 °F to 1832 °F) CTE : solid \|\| a-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) CTE : solid \|\| c-axis \|\| 0 °C to 1000 °C (32 °F to 1832 °F) CTE : liquid \|\| 1541 °C to 1741 °C (2806 °F to 3166 °F) TC : solid \|\| annealed \|\| -273 °C to 27 °C (-460 °F to 80 °F) TD : solid \|\| 0 °C to 27 °C (32 °F to 80 °F) SH : solid \|\| -267 °C to 1539 °C (-449 °F to 2802 °F) SH : liquid \|\| 1539 °C to 2727 °C (2802 °F to 4940 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| -267 °C to 1539 °C (-449 °F to 2802 °F) HC : liquid \|\| 1539 °C to 2727 °C (2802 °F to 4940 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : solid \|\| 20 °C to 1541 °C (68 °F to 2806 °F) VP : liquid \|\| 1541 °C to 1727 °C (2806 °F to 3140 °F) ST : liquid \|\| 1540 °C to 1750 °C (2804 °F to 3182 °F)
Titanium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) D : liquid \|\| 1600 °C to 3227 °C (2912 °F to 5841 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : liquid \|\| 1600 °C to 3227 °C (2912 °F to 5841 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : liquid \|\| 1600 °C to 3227 °C (2912 °F to 5841 °F) CTE : liquid \|\| 1600 °C to 1882 °C (2912 °F to 3420 °F) E : solid \|\| -180 °C to 800 °C (-292 °F to 1472 °F) G : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) v : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) K : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| annealed \|\| -273 °C to 1677 °C (-460 °F to 3050 °F) TC : liquid \|\| 1668 °C to 4727 °C (3034 °F to 8541 °F) TD : solid \|\| -263 °C to 871 °C (-442 °F to 1600 °F) TD : liquid \|\| 1527 °C to 1927 °C (2780 °F to 3501 °F) SH : solid \|\| -263 °C to 1671 °C (-442 °F to 3040 °F) SH : liquid \|\| 1668 °C to 1927 °C (3034 °F to 3500 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -263 °C to 1671 °C (-442 °F to 3040 °F) HC : liquid \|\| 1668 °C to 1927 °C (3034 °F to 3500 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSC : annealed plate \|\| tested at 427 °C (800 °F), 0.000027/s \|\| 0 to 0.3 mm/mm strain SSC : annealed plate \|\| tested at 500 °C (932 °F), 0.000027/s \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 100 °C (212 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 100 °C (212 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 125 °C (257 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 225 °C (437 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 225 °C (437 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 625 °C (1157 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 725 °C (1337 °F) \|\| 0 to 0.4 mm/mm strain SSCC : single crystal, 4450/s \|\| tested at 20 °C (68 °F), [0001] \|\| 0 to 0.25 mm/mm strain SSCC : single crystal, 4450/s \|\| tested at 20 °C (68 °F), [10-11] \|\| 0 to 0.265 mm/mm strain UTS : 0.3 mm (0.0118 inch) thick foil \|\| 0.0083/s strain rate \|\| 20 °C to 602 °C (68 °F to 1115 °F) YS : 0.3 mm (0.0118 inch) thick foil \|\| 0.0083/s strain rate \|\| 20 °C to 602 °C (68 °F to 1115 °F) YSC : bar \|\| 0.001/s strain rate \|\| -196 °C to 500 °C (-321 °F to 932 °F) YSC : bar \|\| 0.1/s strain rate \|\| -196 °C to 503 °C (-321 °F to 937 °F) YSC : bar \|\| 2200/s strain rate \|\| -196 °C to 725 °C (-321 °F to 1337 °F) YSC : bar \|\| 8000/s strain rate \|\| 20 °C to 725 °C (68 °F to 1337 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain range \|\| 1 cycles to 2.63x10⁴ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| not oxidized \|\| 827 °C to 1477 °C (1520 °F to 2690 °F) VP : solid \|\| 20 °C to 1668 °C (68 °F to 3034 °F) VP : liquid \|\| 1668 °C to 2127 °C (3034 °F to 3860 °F) Vis : liquid \|\| 1685 °C to 2185 °C (3065 °F to 3965 °F) ST : liquid \|\| 1668 °C to 1800 °C (3034 °F to 3272 °F) RHO : solid \|\| alpha, commercially pure \|\| -196 °C to 827 °C (-321 °F to 1520 °F) RHO : solid \|\| beta, commercially pure \|\| 977 °C to 1427 °C (1790 °F to 2600 °F) RHO : solid \|\| commercially pure with 0.03 wt% O₂ \|\| -5 °C to 957 °C (23 °F to 1754 °F) RHO : solid \|\| commercially pure with 0.3 wt% O₂ \|\| -5 °C to 1050 °C (23 °F to 1922 °F) RHO : solid \|\| commercially pure with 0.8 wt% O₂ \|\| -5 °C to 1187 °C (23 °F to 2168 °F) RHO : solid \|\| commercially pure with 1.4 wt% O₂ \|\| -5 °C to 1330 °C (23 °F to 2426 °F) RHO : solid \|\| commercially pure with 1.9 wt% O₂ \|\| -5 °C to 1515 °C (23 °F to 2759 °F) RHO : solid \|\| commercially pure with 2.7 wt% O₂ \|\| -5 °C to 1391 °C (23 °F to 2536 °F) RHO : liquid \|\| 1670 °C to 2227 °C (3038 °F to 4040 °F) SIGMA : solid \|\| alpha, commercially pure \|\| -196 °C to 827 °C (-321 °F to 1520 °F) SIGMA : solid \|\| beta, commercially pure \|\| 977 °C to 1427 °C (1790 °F to 2600 °F) SIGMA : solid \|\| commercially pure with 0.03 wt% O₂ \|\| -5 °C to 957 °C (23 °F to 1754 °F) SIGMA : solid \|\| commercially pure with 0.3 wt% O₂ \|\| -5 °C to 1050 °C (23 °F to 1922 °F) SIGMA : solid \|\| commercially pure with 0.8 wt% O₂ \|\| -5 °C to 1187 °C (23 °F to 2168 °F) SIGMA : solid \|\| commercially pure with 1.4 wt% O₂ \|\| -5 °C to 1330 °C (23 °F to 2426 °F) SIGMA : solid \|\| commercially pure with 1.9 wt% O₂ \|\| -5 °C to 1515 °C (23 °F to 2759 °F) SIGMA : solid \|\| commercially pure with 2.7 wt% O₂ \|\| -5 °C to 1391 °C (23 °F to 2536 °F) SIGMA : liquid \|\| 1670 °C to 2227 °C (3038 °F to 4040 °F)
Vanadium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -196 °C to 1316 °C (-321 °F to 2400 °F) D : liquid \|\| 1567 °C to 4227 °C (2852 °F to 7641 °F) DLL : solid \|\| -196 °C to 1316 °C (-321 °F to 2400 °F) DLL : liquid \|\| 1567 °C to 4227 °C (2852 °F to 7641 °F) MTE : solid \|\| -196 °C to 1316 °C (-321 °F to 2400 °F) MTE : liquid \|\| 1567 °C to 4227 °C (2852 °F to 7641 °F) CTE : liquid \|\| 1567 °C to 4227 °C (2852 °F to 7641 °F) E : annealed \|\| -269 °C to 1827 °C (-452 °F to 3320 °F) G : annealed \|\| -269 °C to 1600 °C (-452 °F to 2912 °F) v : annealed \|\| -269 °C to 1600 °C (-452 °F to 2912 °F) K : annealed \|\| -269 °C to 1600 °C (-452 °F to 2912 °F) TC : solid \|\| annealed \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) TC : liquid \|\| 1910 °C to 3627 °C (3470 °F to 6561 °F) TD : solid \|\| annealed \|\| -196 °C to 1316 °C (-321 °F to 2400 °F) TD : liquid \|\| 1910 °C to 3627 °C (3470 °F to 6561 °F) SH : solid \|\| superconducting phase \|\| -272 °C to 1917 °C (-458 °F to 3482 °F) SH : solid \|\| non-superconducting phase \|\| -272 °C to 1917 °C (-458 °F to 3482 °F) SH : liquid \|\| 1867 °C to 5727 °C (3392 °F to 10340 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| superconducting phase \|\| -272 °C to 1917 °C (-458 °F to 3482 °F) HC : solid \|\| non-superconducting phase \|\| -272 °C to 1917 °C (-458 °F to 3482 °F) HC : liquid \|\| 1867 °C to 5727 °C (3392 °F to 10340 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSCC : as-received \|\| tested at -196.1 °C (-321.1 °F), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : as-received \|\| tested at 20 °C (68 °F), 2500/s \|\| 0 to 0.49 mm/mm strain SSCC : as-received \|\| tested at 227 °C (440 °F), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : as-received \|\| tested at 427 °C (800 °F), 2500/s \|\| 0 to 0.51 mm/mm strain SSCC : annealed \|\| tested at -196.1 °C (-321.1 °F), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : annealed \|\| tested at 20 °C (68 °F), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : annealed \|\| tested at 227 °C (440 °F), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : annealed \|\| tested at 427 °C (800 °F), 2500/s \|\| 0 to 0.5 mm/mm strain UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) HE : solid \|\| 1607 °C to 1777 °C (2924 °F to 3230 °F) VP : solid \|\| 20 °C to 1910 °C (68 °F to 3470 °F) VP : liquid \|\| 1910 °C to 2227 °C (3470 °F to 4040 °F) Vis : liquid \|\| 1902 °C to 2402 °C (3455 °F to 4355 °F) ST : liquid \|\| 1685 °C to 2010 °C (3065 °F to 3650 °F) RHO : solid \|\| -272 °C to 1929 °C (-458 °F to 3504 °F) RHO : liquid \|\| 1926 °C to 3727 °C (3499 °F to 6740 °F) SIGMA : solid \|\| -272 °C to 1929 °C (-458 °F to 3504 °F) SIGMA : liquid \|\| 1926 °C to 3727 °C (3499 °F to 6740 °F)
Chromium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) D : liquid \|\| 1907 °C to 2227 °C (3464 °F to 4041 °F) DLL : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) DLL : liquid \|\| 1907 °C to 2227 °C (3464 °F to 4041 °F) MTE : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) MTE : liquid \|\| 1907 °C to 2227 °C (3464 °F to 4041 °F) CTE : liquid \|\| 1907 °C to 2227 °C (3464 °F to 4041 °F) E : solid \|\| 20 °C to 1250 °C (68 °F to 2282 °F) TC : solid \|\| annealed \|\| -273 °C to 1845 °C (-460 °F to 3353 °F) TD : solid \|\| annealed \|\| -253 °C to 1000 °C (-424 °F to 1832 °F) SH : solid \|\| -253 °C to 1857 °C (-424 °F to 3374 °F) SH : liquid \|\| 1857 °C to 5727 °C (3374 °F to 10340 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| -253 °C to 1857 °C (-424 °F to 3374 °F) HC : liquid \|\| 1857 °C to 5727 °C (3374 °F to 10340 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) YSC : annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) HE : solid \|\| plated coating \|\| -173 °C to 727 °C (-280 °F to 1340 °F) NE : solid \|\| polished & oxidized \|\| 315 °C to 982 °C (599 °F to 1800 °F) VP : solid \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : liquid \|\| 1907 °C to 2482 °C (3464 °F to 4499 °F) Vis : liquid \|\| 1860 °C to 2360 °C (3380 °F to 4280 °F) ST : liquid \|\| 1850 °C to 2000 °C (3362 °F to 3632 °F) RHO : solid \|\| -73 °C to 727 °C (-100 °F to 1340 °F) SIGMA : solid \|\| -73 °C to 727 °C (-100 °F to 1340 °F)
Manganese (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -188 °C to 948 °C (-307 °F to 1738 °F) D : liquid \|\| 1262 °C to 1565 °C (2303 °F to 2849 °F) DLL : solid \|\| -188 °C to 948 °C (-307 °F to 1738 °F) DLL : liquid \|\| 1262 °C to 1565 °C (2303 °F to 2849 °F) MTE : solid \|\| -188 °C to 948 °C (-307 °F to 1738 °F) MTE : liquid \|\| 1262 °C to 1565 °C (2303 °F to 2849 °F) CTE : liquid \|\| 1262 °C to 1565 °C (2303 °F to 2849 °F) TC : solid \|\| annealed \|\| -271 °C to 27 °C (-456 °F to 80 °F) TD : solid \|\| -271 °C to 27 °C (-456 °F to 81 °F) SH : solid \|\| -272 °C to 1244 °C (-458 °F to 2271 °F) SH : liquid \|\| 1244 °C to 1727 °C (2271 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 1244 °C (-458 °F to 2271 °F) HC : liquid \|\| 1244 °C to 1727 °C (2271 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 534 °C to 1246 °C (993 °F to 2275 °F) VP : liquid \|\| 1246 °C to 2108 °C (2275 °F to 3826 °F) ST : liquid \|\| unknown impurities \|\| 1245 °C to 1500 °C (2273 °F to 2732 °F) ST : liquid \|\| 372 ppm O, 528 ppm S \|\| 1262 °C to 1565 °C (2303 °F to 2849 °F) RHO : solid \|\| -273 °C to 427 °C (-460 °F to 800 °F) SIGMA : solid \|\| -273 °C to 427 °C (-460 °F to 800 °F)
Iron (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) D : liquid \|\| 1535 °C to 2680 °C (2795 °F to 4856 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : liquid \|\| 1535 °C to 2680 °C (2795 °F to 4856 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : liquid \|\| 1535 °C to 2680 °C (2795 °F to 4856 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) CTE : liquid \|\| 1535 °C to 2680 °C (2795 °F to 4856 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| annealed \|\| -272 °C to 1537 °C (-458 °F to 2798 °F) TC : liquid \|\| 1537 °C to 6227 °C (2798 °F to 11240 °F) TD : solid \|\| annealed \|\| -272 °C to 687 °C (-458 °F to 1268 °F) TD : liquid \|\| 1538 °C to 2027 °C (2800 °F to 3680 °F) SH : solid \|\| -272 °C to 1536 °C (-458 °F to 2797 °F) SH : liquid \|\| 1536 °C to 2859 °C (2797 °F to 5178 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -272 °C to 1536 °C (-458 °F to 2797 °F) HC : liquid \|\| 1536 °C to 2859 °C (2797 °F to 5178 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSCC : annealed, 100/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.525 mm/mm strain SSCC : annealed, 100/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.525 mm/mm strain SSCC : annealed, 10/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.525 mm/mm strain SSCC : annealed, 10/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.475 mm/mm strain SSCC : annealed, 1/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s, gamma \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s, gamma \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 100/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.525 mm/mm strain SSCC : annealed, 100/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 10/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 10/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s, alpha \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s, alpha \|\| tested at 500 °C (932 °F) \|\| 0 to 0.55 mm/mm strain YS : solid \|\| 2.5x10^-⁴/s strain rate \|\| -196 °C to 700 °C (-321 °F to 1292 °F) HE : solid \|\| polished \|\| 20 °C to 527 °C (68 °F to 980 °F) NE : solid \|\| polished \|\| -73 °C to 820 °C (-100 °F to 1508 °F) NE : solid \|\| polished & sand blasted \|\| 195 °C to 820 °C (383 °F to 1508 °F) VP : solid \|\| 20 °C to 1538 °C (68 °F to 2800 °F) VP : liquid \|\| 1538 °C to 2927 °C (2800 °F to 5300 °F) Vis : liquid \|\| 1544 °C to 1669 °C (2811 °F to 3036 °F) ST : liquid \|\| in H₂ \|\| 1100 °C to 2225 °C (2012 °F to 4037 °F) ST : liquid \|\| 28 ppm O, Kim et. al. \|\| 1515 °C to 1700 °C (2759 °F to 3092 °F) ST : liquid \|\| 319 ppm O, Kim et. al. \|\| 1515 °C to 1660 °C (2759 °F to 3020 °F) ST : liquid \|\| 606 ppm O, Kim et. al. \|\| 1495 °C to 1710 °C (2723 °F to 3110 °F) ST : liquid \|\| 720 ppm O, Kim et. al. \|\| 1530 °C to 1740 °C (2786 °F to 3164 °F) ST : liquid \|\| 749 ppm O, Kim et. al. \|\| 1345 °C to 1655 °C (2453 °F to 3011 °F) ST : liquid \|\| 895 ppm O, Kim et. al. \|\| 1570 °C to 1665 °C (2858 °F to 3029 °F) ST : liquid \|\| 1213 ppm O, Kim et. al. \|\| 1510 °C to 1655 °C (2750 °F to 3011 °F) RHO : solid \|\| annealed \|\| -173 °C to 1227 °C (-280 °F to 2240 °F) RHO : liquid \|\| 1557 °C to 2097 °C (2834 °F to 3806 °F) SIGMA : solid \|\| annealed \|\| -173 °C to 1227 °C (-280 °F to 2240 °F) SIGMA : liquid \|\| 1557 °C to 2097 °C (2834 °F to 3806 °F) RPB : strip \|\| tested at 20 °C (68 °F) RPB : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) RPB : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) AP : strip \|\| tested at 20 °C (68 °F) AP : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) AP : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) BH : strip \|\| tested at 20 °C (68 °F) BH : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) BH : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) HB : strip \|\| tested at 20 °C (68 °F) HB : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) HB : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) S : solid \|\| 20 °C to 913 °C (68 °F to 1675 °F)
Cobalt (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| polycrystal \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) D : solid \|\| beta phase \|\| 20 °C to 650 °C (68 °F to 1202 °F) D : liquid \|\| 1494 °C to 2227 °C (2721 °F to 4040 °F) DLL : solid \|\| polycrystal \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) DLL : solid \|\| beta phase \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : liquid \|\| 1494 °C to 2227 °C (2721 °F to 4040 °F) MTE : solid \|\| polycrystal \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) MTE : solid \|\| beta phase \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : liquid \|\| 1494 °C to 2227 °C (2721 °F to 4040 °F) CTE : solid \|\| polycrystal \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) CTE : solid \|\| beta phase \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : liquid \|\| 1494 °C to 2227 °C (2721 °F to 4040 °F) E : solid \|\| -269 °C to 250 °C (-452 °F to 482 °F) G : solid \|\| -269 °C to 250 °C (-452 °F to 482 °F) v : solid \|\| -269 °C to 250 °C (-452 °F to 482 °F) K : solid \|\| -269 °C to 250 °C (-452 °F to 482 °F) TC : solid \|\| annealed \|\| -273 °C to 1494 °C (-460 °F to 2721 °F) TC : liquid \|\| 1490 °C to 2227 °C (2714 °F to 4040 °F) TD : solid \|\| 20 °C to 417 °C (68 °F to 782 °F) TD : liquid \|\| 1490 °C to 1567 °C (2714 °F to 2852 °F) SH : solid \|\| -259 °C to 417 °C (-434 °F to 782 °F) SH : liquid \|\| 1506 °C to 1750 °C (2743 °F to 3182 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -259 °C to 417 °C (-434 °F to 782 °F) HC : liquid \|\| 1506 °C to 1750 °C (2743 °F to 3182 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : 12 nanometer grain size \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.68 mm/mm strain SSC : 12 nanometer grain size \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : 12 nanometer grain size \|\| tested at 20 °C (68 °F), 0.0025/s \|\| 0 to 0.4 mm/mm strain SSC : 4.8 micron grain size \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.68 mm/mm strain SSC : 4.8 micron grain size \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.12 mm/mm strain SSC : 4.8 micron grain size \|\| tested at 20 °C (68 °F), 0.0025/s \|\| 0 to 0.12 mm/mm strain SSCC : sintered rod \|\| tested at 1250 °C (2282 °F), 0.001/s \|\| 0 to 0.39 mm/mm strain SSCC : sintered rod \|\| tested at 1250 °C (2282 °F), 3.2/s \|\| 0 to 0.4 mm/mm strain HE : solid \|\| polished \|\| 102 °C to 977 °C (215 °F to 1790 °F) NE : liquid \|\| 1468 °C to 1676 °C (2674 °F to 3049 °F) VP : solid \|\| 20 °C to 1495 °C (68 °F to 2723 °F) VP : liquid \|\| 1495 °C to 1877 °C (2723 °F to 3410 °F) Vis : liquid \|\| 1495 °C to 1827 °C (2723 °F to 3320 °F) ST : liquid \|\| 1500 °C to 1800 °C (2732 °F to 3272 °F) RHO : solid \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) RHO : liquid \|\| 1495 °C to 1927 °C (2723 °F to 3500 °F) SIGMA : solid \|\| -133 °C to 1495 °C (-208 °F to 2723 °F) SIGMA : liquid \|\| 1495 °C to 1927 °C (2723 °F to 3500 °F) RPB : annealed \|\| tested at 20 °C (68 °F) AP : annealed \|\| tested at 20 °C (68 °F) BH : annealed \|\| tested at 20 °C (68 °F) HB : annealed \|\| tested at 20 °C (68 °F)
Nickel (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) D : liquid \|\| 1455 °C to 2097 °C (2651 °F to 3806 °F) DLL : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) DLL : liquid \|\| 1455 °C to 2097 °C (2651 °F to 3806 °F) MTE : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) MTE : liquid \|\| 1455 °C to 2097 °C (2651 °F to 3806 °F) CTE : solid \|\| -223 °C to 527 °C (-370 °F to 980 °F) CTE : liquid \|\| 1455 °C to 2097 °C (2651 °F to 3806 °F) E : solid \|\| -273 °C to 1050 °C (-460 °F to 1922 °F) G : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) v : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) K : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| annealed \|\| -273 °C to 1227 °C (-460 °F to 2240 °F) TC : liquid \|\| 1450 °C to 2727 °C (2642 °F to 4940 °F) TD : solid \|\| -271 °C to 900 °C (-456 °F to 1652 °F) TD : liquid \|\| 1450 °C to 1650 °C (2642 °F to 3002 °F) SH : solid \|\| -272 °C to 1455 °C (-458 °F to 2651 °F) SH : liquid \|\| 1273 °C to 2911 °C (2323 °F to 5272 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 1455 °C (-458 °F to 2651 °F) HC : liquid \|\| 1273 °C to 2911 °C (2323 °F to 5272 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.6 mm/mm strain SSC : 40% cold-drawn \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.2 mm/mm strain UTS : solid \|\| annealed \|\| -196 °C to 816 °C (-321 °F to 1500 °F) UTS : solid \|\| 40% cold drawing \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solid \|\| annealed \|\| -196 °C to 816 °C (-321 °F to 1500 °F) YS : solid \|\| 40% cold drawing \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : solid \|\| annealed \|\| -196 °C to 816 °C (-321 °F to 1500 °F) %El : solid \|\| 40% cold drawing \|\| 23 °C to 816 °C (73 °F to 1500 °F) SR : annealed \|\| tested at 149 °C (300 °F) \|\| 3 h to 8,100 h SR : annealed \|\| tested at 371 °C (700 °F) \|\| 20 h to 2.1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 50 h to 4,000 h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 4 h to 10 h SR : annealed \|\| Master curve (LMP) \|\| 149 °C to 650 °C (300 °F to 1202 °F) FEN : hot finished \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles FEN : hot finished \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 180 cycles to 7.6x10⁴ cycles FEN : 50 micron thick foil \|\| tested at 20 °C (68 °F), R = -1, bending, RD-loaded, total strain amplitude \|\| 2x10⁴ cycles to 1x10⁷ cycles FEN : 50 micron thick foil \|\| tested at 20 °C (68 °F), R = -1, bending, TD-loaded, total strain amplitude \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : 50 micron thick foil \|\| tested at 20 °C (68 °F), R = -1, bending, RD-loaded, stress amplitude \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : 50 micron thick foil \|\| tested at 20 °C (68 °F), R = -1, bending, TD-loaded, stress amplitude \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : 10 micron thick film \|\| tested at 20 °C (68 °F), R = 0.1, axial, stress range \|\| 8x10⁴ cycles to 6x10⁶ cycles FSN : electrodeposited films \|\| tested at 20 °C (68 °F), R = 0.1, axial, 20 micron grains, stress range \|\| 1x10³ cycles to 4x10⁴ cycles FSN : electrodeposited films \|\| tested at 20 °C (68 °F), R = 0.1, axial, 75 micron grains, stress range \|\| 8x10³ cycles to 2x10⁵ cycles FSN : electrodeposited films \|\| tested at 20 °C (68 °F), R = 0.1, axial, 10 micron grains, stress range \|\| 3x10³ cycles to 2x10⁵ cycles HE : solid \|\| polished \|\| -28 °C to 820 °C (-19 °F to 1508 °F) NE : solid \|\| buffed \|\| 310 °C to 660 °C (590 °F to 1220 °F) NE : solid \|\| shot blasted \|\| 315 °C to 535 °C (599 °F to 995 °F) NE : solid \|\| buffed, oxidized \|\| 310 °C to 805 °C (590 °F to 1481 °F) NE : solid \|\| shot blasted, oxidized \|\| 310 °C to 805 °C (590 °F to 1481 °F) NE : solid \|\| plated \|\| -251 °C to -195 °C (-420 °F to -319 °F) VP : solid \|\| 20 °C to 1455 °C (68 °F to 2651 °F) VP : liquid \|\| 1455 °C to 1877 °C (2651 °F to 3410 °F) Vis : liquid \|\| 1394 °C to 1657 °C (2541 °F to 3014 °F) ST : liquid \|\| 997 °C to 1927 °C (1826 °F to 3501 °F) RHO : solid \|\| annealed \|\| -173 °C to 1442 °C (-280 °F to 2627 °F) RHO : liquid \|\| 1477 °C to 1927 °C (2690 °F to 3500 °F) SIGMA : solid \|\| annealed \|\| -173 °C to 1442 °C (-280 °F to 2627 °F) SIGMA : liquid \|\| 1477 °C to 1927 °C (2690 °F to 3500 °F) RPB : annealed \|\| tested at 20 °C (68 °F) AP : annealed \|\| tested at 20 °C (68 °F) BH : annealed \|\| tested at 20 °C (68 °F) HB : annealed \|\| tested at 20 °C (68 °F)
Copper (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) D : liquid \|\| 1085 °C to 1527 °C (1985 °F to 2780 °F) DLL : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) DLL : liquid \|\| 1085 °C to 1527 °C (1985 °F to 2780 °F) MTE : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) MTE : liquid \|\| 1085 °C to 1527 °C (1985 °F to 2780 °F) CTE : solid \|\| -269 °C to 527 °C (-452 °F to 980 °F) CTE : liquid \|\| 1085 °C to 1527 °C (1985 °F to 2780 °F) E : solid \|\| -269 °C to 1057 °C (-452 °F to 1934 °F) E* : 300 nm grain size \|\| room temperature value G : solid \|\| -269 °C to 1057 °C (-452 °F to 1934 °F) v : solid \|\| -269 °C to 1057 °C (-452 °F to 1934 °F) K : solid \|\| -269 °C to 1057 °C (-452 °F to 1934 °F) TC : solid \|\| residual resistivity ratio of 30 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) TC : solid \|\| residual resistivity ratio of 100 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) TC : solid \|\| residual resistivity ratio of 300 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) TC : solid \|\| residual resistivity ratio of 1000 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) TC : solid \|\| residual resistivity ratio of 3000 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) TC : solid \|\| 120 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TC : solid \|\| 181 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TC : solid \|\| 300 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TC : liquid \|\| 1085 °C to 8227 °C (1985 °F to 14840 °F) TD : solid \|\| residual resistivity ratio of 30 \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| residual resistivity ratio of 100 \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| residual resistivity ratio of 300 \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| residual resistivity ratio of 1000 \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| residual resistivity ratio of 3000 \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| 120 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TD : solid \|\| 181 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TD : solid \|\| 300 nm thin film \|\| -173 °C to 202 °C (-280 °F to 395 °F) TD : liquid \|\| 1085 °C to 1200 °C (1985 °F to 2192 °F) SH : solid \|\| -272 °C to 1027 °C (-458 °F to 1880 °F) SH : liquid \|\| 1085 °C to 1775 °C (1985 °F to 3227 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 1027 °C (-458 °F to 1880 °F) HC : liquid \|\| 1085 °C to 1775 °C (1985 °F to 3227 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : bulk \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s, 3.4 micron grain size \|\| 0 to 0.3 mm/mm strain SSC : bulk \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s, 15 micron grain size \|\| 0 to 0.3 mm/mm strain SSC : bulk \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s, 150 micron grain size \|\| 0 to 0.275 mm/mm strain SSC : thin film \|\| tested at 20 °C (68 °F), 5x10^-⁵/s, 0.475 micron thin \|\| 0 to 3x10^-³ mm/mm strain SSC : thin film \|\| tested at 20 °C (68 °F), 5x10^-⁵/s, 0.95 micron thin \|\| 0 to 4x10^-³ mm/mm strain SSC : thin film \|\| tested at 20 °C (68 °F), 5x10^-⁵/s, 2.025 micron thin \|\| 0 to 5x10^-³ mm/mm strain SSC : thin film \|\| tested at 20 °C (68 °F), 5x10^-⁵/s, 2.775 micron thin \|\| 0 to 5x10^-³ mm/mm strain SSCC : equal channel pressed without back-pressure \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.55 mm/mm strain SSCC : equal channel pressed without back-pressure \|\| tested at 100 °C (212 °F), 1x10^-⁴/s \|\| 0 to 0.57 mm/mm strain SSCC : equal channel pressed with back-pressure \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.62 mm/mm strain SSCC : equal channel pressed with back-pressure \|\| tested at 100 °C (212 °F), 1x10^-⁴/s \|\| 0 to 0.59 mm/mm strain UTS : annealed \|\| 10 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 20 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 30 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 40 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 50 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 65 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| 120 micron GS \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : cold worked \|\| 10% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : cold worked \|\| 40% reduction by cold drawing \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : annealed \|\| 10 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 20 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 30 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 40 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 50 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 65 micron GS \|\| -269 °C to 27 °C (-452 °F to 80 °F) YS : annealed \|\| 120 micron GS \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : cold worked \|\| 10% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : cold worked \|\| 40% reduction by cold drawing \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : annealed \|\| annealed (120 micron GS) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : cold worked \|\| 40% reduction by cold drawing \|\| 20 °C to 816 °C (68 °F to 1500 °F) FSN : 0.012 mm (0.000472 inch) electrodeposited film \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 3.3x10⁴ cycles to 1.1x10⁵ cycles FSN : 0.012 mm (0.000472 inch) electrodeposited film \|\| tested at 20 °C (68 °F), R = 0.3, axial, maximum stress \|\| 7x10⁴ cycles to 5.2x10⁵ cycles FSN : 0.012 mm (0.000472 inch) electrodeposited film \|\| tested at 20 °C (68 °F), R = 0.4, axial, maximum stress \|\| 1.8x10⁵ cycles to 1.1x10⁶ cycles FSN : 0.012 mm (0.000472 inch) electrodeposited film \|\| tested at 20 °C (68 °F), R = 0.5, axial, maximum stress \|\| 3.4x10⁵ cycles to 2.4x10⁶ cycles FSN : 0.012 mm (0.000472 inch) electrodeposited film \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 3x10⁵ cycles to 2.1x10⁶ cycles FSN : 300 nm grain size \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 5x10³ cycles to unknown strain rate cycles HE : solid \|\| oxidized \|\| 315 °C to 760 °C (599 °F to 1400 °F) HE : solid \|\| polished \|\| 20 °C to 477 °C (68 °F to 890 °F) NE : solid \|\| oxidized \|\| 315 °C to 760 °C (599 °F to 1400 °F) VP : solid \|\| 20 °C to 1085 °C (68 °F to 1985 °F) VP : liquid \|\| 1085 °C to 1577 °C (1985 °F to 2870 °F) Vis : liquid \|\| 1085 °C to 1827 °C (1985 °F to 3320 °F) ST : liquid \|\| 1083 °C to 1727 °C (1981 °F to 3140 °F) RHO : solid \|\| residual resistivity ratio of 860 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) RHO : liquid \|\| 1085 °C to 1526 °C (1985 °F to 2779 °F) SIGMA : solid \|\| residual resistivity ratio of 860 \|\| -272 °C to 1085 °C (-458 °F to 1985 °F) SIGMA : liquid \|\| 1085 °C to 1526 °C (1985 °F to 2779 °F) S : solid \|\| -173 °C to 1027 °C (-280 °F to 1880 °F)
Zinc (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 617 °C (-460 °F to 1142 °F) D : liquid \|\| 420 °C to 800 °C (788 °F to 1472 °F) DLL : solid \|\| polycrystal \|\| -273 °C to 617 °C (-460 °F to 1142 °F) DLL : solid \|\| a-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) DLL : solid \|\| c-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) DLL : liquid \|\| 420 °C to 800 °C (788 °F to 1472 °F) MTE : solid \|\| polycrystal \|\| -273 °C to 617 °C (-460 °F to 1142 °F) MTE : solid \|\| a-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) MTE : solid \|\| c-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) MTE : liquid \|\| 420 °C to 800 °C (788 °F to 1472 °F) CTE : solid \|\| polycrystal \|\| -8 °C to 617 °C (17 °F to 1142 °F) CTE : solid \|\| a-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) CTE : solid \|\| c-axis \|\| 20 °C to 409 °C (68 °F to 768 °F) CTE : liquid \|\| 420 °C to 800 °C (788 °F to 1472 °F) E : solid \|\| -273 °C to 377 °C (-460 °F to 710 °F) G : solid \|\| -273 °C to 377 °C (-460 °F to 710 °F) v : solid \|\| -273 °C to 377 °C (-460 °F to 710 °F) K : solid \|\| -273 °C to 377 °C (-460 °F to 710 °F) TC : solid \|\| annealed \|\| -273 °C to 420 °C (-460 °F to 788 °F) TC : liquid \|\| 420 °C to 827 °C (788 °F to 1520 °F) TC : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| annealed \|\| -263 °C to 420 °C (-442 °F to 788 °F) TD : liquid \|\| 420 °C to 800 °C (788 °F to 1472 °F) SH : solid \|\| -272 °C to 420 °C (-458 °F to 788 °F) SH : liquid \|\| 420 °C to 5727 °C (788 °F to 10340 °F) SH : gas \|\| -73 °C to 5727 °C (-100 °F to 10340 °F) HC : solid \|\| -272 °C to 420 °C (-458 °F to 788 °F) HC : liquid \|\| 420 °C to 5727 °C (788 °F to 10340 °F) HC : gas \|\| -73 °C to 5727 °C (-100 °F to 10340 °F) SSC : 240 nm grain \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : 240 nm grain \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.34 mm/mm strain SSC : 240 nm grain \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.41 mm/mm strain SSCC : rod, perpendicular, 0.0011/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.6 mm/mm strain SSCC : rod, parallel, 0.0011/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.55 mm/mm strain VP : solid \|\| 20 °C to 420 °C (68 °F to 788 °F) VP : liquid \|\| 420 °C to 477 °C (788 °F to 890 °F) Vis : liquid \|\| 422 °C to 827 °C (791 °F to 1520 °F) Vis : gas \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| negative temperature dependence \|\| 420 °C to 780 °C (788 °F to 1436 °F) ST : liquid \|\| positive temperature dependence \|\| 430 °C to 810 °C (806 °F to 1490 °F) RHO : solid \|\| -272 °C to 420 °C (-458 °F to 788 °F) RHO : liquid \|\| 420 °C to 1327 °C (788 °F to 2420 °F) SIGMA : solid \|\| -272 °C to 420 °C (-458 °F to 788 °F) SIGMA : liquid \|\| 420 °C to 1327 °C (788 °F to 2420 °F) AV : liquid \|\| tested at 450 °C (842 °F) \|\| 0/s to 2.6x10³/s
Gallium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| 30 °C to 977 °C (86 °F to 1790 °F) DLL : liquid \|\| 30 °C to 977 °C (86 °F to 1790 °F) MTE : liquid \|\| 30 °C to 977 °C (86 °F to 1790 °F) CTE : liquid \|\| 30 °C to 977 °C (86 °F to 1790 °F) TC : solid \|\| -273 °C to 30 °C (-460 °F to 86 °F) TC : liquid \|\| 30 °C to 427 °C (86 °F to 800 °F) TD : liquid \|\| 30 °C to 427 °C (86 °F to 800 °F) SH : solid \|\| 20 °C to 30 °C (68 °F to 86 °F) SH : liquid \|\| 30 °C to 1727 °C (86 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 30 °C (68 °F to 86 °F) HC : liquid \|\| 30 °C to 1727 °C (86 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 30 °C (68 °F to 86 °F) VP : liquid \|\| 30 °C to 1327 °C (86 °F to 2420 °F) Vis : liquid \|\| 31 °C to 527 °C (88 °F to 980 °F) ST : liquid \|\| 30 °C to 1027 °C (86 °F to 1880 °F) RHO : solid \|\| 0 °C to 30 °C (32 °F to 86 °F) RHO : liquid \|\| 30 °C to 50 °C (86 °F to 122 °F) SIGMA : solid \|\| 0 °C to 30 °C (32 °F to 86 °F) SIGMA : liquid \|\| 30 °C to 50 °C (86 °F to 122 °F)
Germanium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -233 °C to 812 °C (-388 °F to 1493 °F) D : liquid \|\| 938 °C to 1477 °C (1720 °F to 2690 °F) DLL : solid \|\| -233 °C to 812 °C (-388 °F to 1493 °F) DLL : liquid \|\| 938 °C to 1477 °C (1720 °F to 2690 °F) MTE : solid \|\| -233 °C to 812 °C (-388 °F to 1493 °F) MTE : liquid \|\| 938 °C to 1477 °C (1720 °F to 2690 °F) CTE : solid \|\| -233 °C to 27 °C (-388 °F to 80 °F) CTE : liquid \|\| 938 °C to 1477 °C (1720 °F to 2690 °F) E : solid \|\| polycrystal \|\| -200 °C to 300 °C (-328 °F to 572 °F) E : solid \|\| <111> axis \|\| -157 °C to 287 °C (-251 °F to 548 °F) E : solid \|\| <100> axis \|\| -157 °C to 287 °C (-251 °F to 548 °F) G : solid \|\| polycrystal \|\| -200 °C to 300 °C (-328 °F to 572 °F) v : solid \|\| polycrystal \|\| -200 °C to 300 °C (-328 °F to 572 °F) K : solid \|\| polycrystal \|\| -200 °C to 300 °C (-328 °F to 572 °F) TC : solid \|\| annealed \|\| -273 °C to 927 °C (-460 °F to 1700 °F) TC : liquid \|\| 939 °C to 1107 °C (1722 °F to 2024 °F) TD : solid \|\| annealed \|\| -173 °C to 812 °C (-280 °F to 1493 °F) TD : liquid \|\| 939 °C to 1107 °C (1722 °F to 2024 °F) SH : solid \|\| -173 °C to 938 °C (-280 °F to 1720 °F) SH : liquid \|\| 910 °C to 1110 °C (1670 °F to 2030 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -173 °C to 938 °C (-280 °F to 1720 °F) HC : liquid \|\| 910 °C to 1110 °C (1670 °F to 2030 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 805 °C to 938 °C (1481 °F to 1720 °F) VP : liquid \|\| 938 °C to 2892 °C (1720 °F to 5237 °F) Vis : liquid \|\| 937 °C to 1437 °C (1718 °F to 2618 °F) ST : liquid \|\| 960 °C to 1600 °C (1760 °F to 2912 °F) RHO : liquid \|\| 939 °C to 1107 °C (1722 °F to 2024 °F) SIGMA : liquid \|\| 939 °C to 1107 °C (1722 °F to 2024 °F) RIW : measured in vacuum \|\| tested at -243.1 °C (-405.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -233.1 °C (-387.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -223.1 °C (-369.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -213.1 °C (-351.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -203.1 °C (-333.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -193.1 °C (-315.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -183.1 °C (-297.7 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -173 °C (-280 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -123 °C (-190 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -73 °C (-100 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at -23 °C (-10 °F) \|\| 1.8 µm to 5.5 µm RIW : measured in vacuum \|\| tested at 22 °C (71 °F) \|\| 1.8 µm to 14 µm RIT : measured in vacuum \|\| measured at 1800 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 2000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 2500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 3000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 3500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 4000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 4500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 5000 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F) RIT : measured in vacuum \|\| measured at 5500 nm \|\| -243 °C to 22 °C (-406 °F to 72 °F)
Arsenic (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -73 °C to 227 °C (-100 °F to 440 °F) TD : solid \|\| 20 °C to 227 °C (68 °F to 440 °F) SH : solid \|\| 20 °C to 603 °C (68 °F to 1117 °F) SH : gas \|\| As \|\| 20 °C to 927 °C (68 °F to 1700 °F) SH : gas \|\| As₂ \|\| 20 °C to 927 °C (68 °F to 1700 °F) SH : gas \|\| As₃ \|\| 20 °C to 927 °C (68 °F to 1700 °F) SH : gas \|\| As₄ \|\| 20 °C to 927 °C (68 °F to 1700 °F) HC : solid \|\| 20 °C to 603 °C (68 °F to 1117 °F) HC : gas \|\| As \|\| 20 °C to 927 °C (68 °F to 1700 °F) HC : gas \|\| As₂ \|\| 20 °C to 927 °C (68 °F to 1700 °F) HC : gas \|\| As₃ \|\| 20 °C to 927 °C (68 °F to 1700 °F) HC : gas \|\| As₄ \|\| 20 °C to 927 °C (68 °F to 1700 °F) VP : liquid \|\| 308 °C to 610 °C (586 °F to 1130 °F)
Selenium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : trigonal \|\| -263 °C to 27 °C (-442 °F to 80 °F) D : glassy, amorphous \|\| -263 °C to 27 °C (-442 °F to 80 °F) DLL : trigonal \|\| polycrystal \|\| -263 °C to 27 °C (-442 °F to 80 °F) DLL : trigonal \|\| a-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) DLL : trigonal \|\| c-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) DLL : glassy, amorphous \|\| -263 °C to 27 °C (-442 °F to 80 °F) MTE : trigonal \|\| polycrystal \|\| -263 °C to 27 °C (-442 °F to 80 °F) MTE : trigonal \|\| a-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) MTE : trigonal \|\| c-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) MTE : glassy, amorphous \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : trigonal \|\| polycrystal \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : trigonal \|\| a-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : trigonal \|\| c-axis \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : glassy, amorphous \|\| -263 °C to 27 °C (-442 °F to 80 °F) E* : glassy, amorphous \|\| room temperature value G* : glassy, amorphous \|\| room temperature value v* : glassy, amorphous \|\| room temperature value K* : glassy, amorphous \|\| room temperature value TC : trigonal \|\| polycrystal \|\| -233 °C to -95 °C (-388 °F to -139 °F) TC : trigonal \|\| a-axis \|\| -253 °C to -95 °C (-424 °F to -139 °F) TC : trigonal \|\| c-axis \|\| -253 °C to -95 °C (-424 °F to -139 °F) TC : glassy, amorphous \|\| -173 °C to 27 °C (-280 °F to 80 °F) TC : liquid \|\| 260 °C to 365 °C (500 °F to 689 °F) TD : trigonal \|\| polycrystal \|\| -233 °C to -95 °C (-388 °F to -139 °F) TD : trigonal \|\| a-axis \|\| -233 °C to -95 °C (-388 °F to -139 °F) TD : trigonal \|\| c-axis \|\| -233 °C to -95 °C (-388 °F to -139 °F) TD : glassy, amorphous \|\| -118 °C to 27 °C (-181 °F to 80 °F) TD : liquid \|\| 260 °C to 365 °C (500 °F to 689 °F) SH : solid \|\| trigonal \|\| -263 °C to 221 °C (-442 °F to 430 °F) SH : solid \|\| glassy, amorphous \|\| -273 °C to 221 °C (-460 °F to 430 °F) SH : liquid \|\| 221 °C to 685 °C (430 °F to 1265 °F) SH : gas \|\| Se \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₅ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₆ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₇ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Se₈ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| trigonal \|\| -263 °C to 221 °C (-442 °F to 430 °F) HC : solid \|\| glassy, amorphous \|\| -273 °C to 221 °C (-460 °F to 430 °F) HC : liquid \|\| 221 °C to 685 °C (430 °F to 1265 °F) HC : gas \|\| Se \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₃ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₅ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₆ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₇ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Se₈ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 13 °C to 221 °C (55 °F to 430 °F) VP : liquid \|\| 221 °C to 685 °C (430 °F to 1265 °F) Vis : liquid \|\| 221 °C to 721 °C (430 °F to 1330 °F) ST : liquid \|\| 220 °C to 500 °C (428 °F to 932 °F)
Bromine (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : liquid \|\| room temperature value TC : liquid \|\| -13 °C to 311 °C (8 °F to 592 °F) TC : gas \|\| Br \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| Br₂ \|\| -23 °C to 4727 °C (-10 °F to 8540 °F) TC : vapor \|\| 27 °C to 311 °C (80 °F to 592 °F) TD : liquid \|\| -7 °C to 59 °C (19 °F to 138 °F) SH : solid \|\| Br₂ \|\| -272 °C to -8 °C (-458 °F to 17 °F) SH : liquid \|\| Br₂ \|\| -7 °C to 59 °C (19 °F to 138 °F) SH : gas \|\| Br \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| Br₂ \|\| 60 °C to 5727 °C (140 °F to 10340 °F) HC : solid \|\| Br₂ \|\| -272 °C to -8 °C (-458 °F to 17 °F) HC : liquid \|\| Br₂ \|\| -7 °C to 59 °C (19 °F to 138 °F) HC : gas \|\| Br \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| Br₂ \|\| 60 °C to 5727 °C (140 °F to 10340 °F) VP : solid \|\| Br₂ \|\| -70 °C to -7 °C (-94 °F to 19 °F) VP : liquid \|\| Br₂ \|\| -7 °C to 58 °C (19 °F to 136 °F) Vis : gas \|\| Br \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| Br₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| 5 °C to 50 °C (41 °F to 122 °F)
Krypton (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) D : gas \|\| -153 °C to 2727 °C (-244 °F to 4940 °F) DLL : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) MTE : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) K : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) TC : solid \|\| -272 °C to -157 °C (-458 °F to -251 °F) TC : liquid \|\| -157 °C to -63 °C (-251 °F to -82 °F) TC : gas \|\| -153 °C to 1727 °C (-244 °F to 3140 °F) TC : vapor \|\| -153 °C to -63 °C (-244 °F to -82 °F) TD : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) TD : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) SH : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) SH : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : solid \|\| -269 °C to -158 °C (-452 °F to -253 °F) HC : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : solid \|\| -198 °C to -158 °C (-325 °F to -253 °F) VP : liquid \|\| -153 °C to -68 °C (-244 °F to -91 °F) Vis : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) ST : liquid \|\| -158 °C to -149 °C (-253 °F to -236 °F)
Rubidium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 39 °C to 1030 °C (102 °F to 1886 °F) DLL : liquid \|\| 39 °C to 1030 °C (102 °F to 1886 °F) MTE : liquid \|\| 39 °C to 1030 °C (102 °F to 1886 °F) CTE : liquid \|\| 39 °C to 1030 °C (102 °F to 1886 °F) K : liquid \|\| 40 °C to 1327 °C (104 °F to 2420 °F) TC : solid \|\| -273 °C to 39 °C (-460 °F to 102 °F) TC : liquid \|\| 39 °C to 1727 °C (102 °F to 3140 °F) TD : solid \|\| -272 °C to 39 °C (-458 °F to 102 °F) TD : liquid \|\| 40 °C to 1030 °C (104 °F to 1886 °F) SH : solid \|\| -273 °C to 39 °C (-460 °F to 103 °F) SH : liquid \|\| 39 °C to 1827 °C (103 °F to 3320 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 39 °C (-460 °F to 103 °F) HC : liquid \|\| 39 °C to 1827 °C (103 °F to 3320 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 39 °C (68 °F to 102 °F) VP : liquid \|\| 39 °C to 277 °C (102 °F to 530 °F) Vis : liquid \|\| 40 °C to 1727 °C (104 °F to 3140 °F) ST : liquid \|\| 27 °C to 1100 °C (80 °F to 2012 °F) RHO : solid \|\| -272 °C to 40 °C (-458 °F to 104 °F) RHO : liquid \|\| 40 °C to 1727 °C (104 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 40 °C (-458 °F to 104 °F) SIGMA : liquid \|\| 40 °C to 1727 °C (104 °F to 3140 °F)
Strontium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 768 °C to 880 °C (1414 °F to 1616 °F) DLL : liquid \|\| 768 °C to 880 °C (1414 °F to 1616 °F) MTE : liquid \|\| 768 °C to 880 °C (1414 °F to 1616 °F) CTE : liquid \|\| 768 °C to 880 °C (1414 °F to 1616 °F) TC : solid \|\| -123 °C to 727 °C (-190 °F to 1340 °F) TD* : solid \|\| room temperature value SH : solid \|\| -273 °C to 768 °C (-460 °F to 1414 °F) SH : liquid \|\| 768 °C to 1727 °C (1414 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 768 °C (-460 °F to 1414 °F) HC : liquid \|\| 768 °C to 1727 °C (1414 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 227 °C to 777 °C (440 °F to 1430 °F) VP : liquid \|\| 777 °C to 1400 °C (1430 °F to 2552 °F) Vis : liquid \|\| 768 °C to 1727 °C (1414 °F to 3140 °F) ST : liquid \|\| 770 °C to 1400 °C (1418 °F to 2552 °F) RHO : solid \|\| -272 °C to 769 °C (-458 °F to 1416 °F) RHO : liquid \|\| 769 °C to 887 °C (1416 °F to 1628 °F) SIGMA : solid \|\| -272 °C to 769 °C (-458 °F to 1416 °F) SIGMA : liquid \|\| 769 °C to 887 °C (1416 °F to 1628 °F)
Yttrium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 897 °C (68 °F to 1646 °F) DLL : solid \|\| polycrystal \|\| 20 °C to 897 °C (68 °F to 1646 °F) DLL : solid \|\| a-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) DLL : solid \|\| c-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) MTE : solid \|\| polycrystal \|\| 20 °C to 897 °C (68 °F to 1646 °F) MTE : solid \|\| a-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) MTE : solid \|\| c-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) CTE : solid \|\| polycrystal \|\| 20 °C to 897 °C (68 °F to 1646 °F) CTE : solid \|\| a-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) CTE : solid \|\| c-axis \|\| 20 °C to 897 °C (68 °F to 1646 °F) TC : solid \|\| annealed \|\| -273 °C to 827 °C (-460 °F to 1520 °F) TD : solid \|\| 20 °C to 827 °C (68 °F to 1520 °F) SH : solid \|\| 20 °C to 1526 °C (68 °F to 2779 °F) SH : liquid \|\| 1526 °C to 2227 °C (2779 °F to 4040 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| 20 °C to 1526 °C (68 °F to 2779 °F) HC : liquid \|\| 1526 °C to 2227 °C (2779 °F to 4040 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) YS : solid \|\| 0.23 H, annealed \|\| -195 °C to 200 °C (-319 °F to 392 °F) YS : solid \|\| 5.03 H, annealed \|\| -195 °C to 200 °C (-319 °F to 392 °F) YS : solid \|\| 11.7 H, annealed \|\| -73 °C to 200 °C (-100 °F to 392 °F) YS : solid \|\| 16.3 H, annealed \|\| 20 °C to 200 °C (68 °F to 392 °F) VP : solid \|\| 20 °C to 1526 °C (68 °F to 2779 °F) VP : liquid \|\| 1526 °C to 2027 °C (2779 °F to 3680 °F) ST : liquid \|\| 1520 °C to 1750 °C (2768 °F to 3182 °F)
Zirconium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -216 °C to 1557 °C (-357 °F to 2834 °F) D : liquid \|\| 1427 °C to 3827 °C (2600 °F to 6921 °F) DLL : solid \|\| -216 °C to 1557 °C (-357 °F to 2834 °F) DLL : liquid \|\| 1427 °C to 3827 °C (2600 °F to 6921 °F) MTE : solid \|\| -216 °C to 1557 °C (-357 °F to 2834 °F) MTE : liquid \|\| 1427 °C to 3827 °C (2600 °F to 6921 °F) CTE : solid \|\| 20 °C to 1557 °C (68 °F to 2834 °F) CTE : liquid \|\| 1427 °C to 3827 °C (2600 °F to 6921 °F) E : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TC : solid \|\| annealed \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) TC : liquid \|\| 1855 °C to 4002 °C (3371 °F to 7236 °F) TD : solid \|\| annealed \|\| -216 °C to 1557 °C (-357 °F to 2834 °F) TD : liquid \|\| 1855 °C to 3827 °C (3371 °F to 6921 °F) SH : solid \|\| -253 °C to 1852 °C (-424 °F to 3365 °F) SH : liquid \|\| 1852 °C to 5727 °C (3365 °F to 10340 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -253 °C to 1852 °C (-424 °F to 3365 °F) HC : liquid \|\| 1852 °C to 5727 °C (3365 °F to 10340 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSC : annealed, 10 micron grains \|\| tested at -196.1 °C (-321.1 °F), 4.2x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : annealed, 10 micron grains \|\| tested at 23 °C (73 °F), 4.2x10^-⁴/s \|\| 0 to 0.17 mm/mm strain SSC : annealed, 10 micron grains \|\| tested at 180 °C (356 °F), 4.2x10^-⁴/s \|\| 0 to 0.127 mm/mm strain SSC : annealed, 25 micron grains \|\| tested at 20 °C (68 °F), 0.001/s, in-plane \|\| 0 to 0.2 mm/mm strain SSC : annealed, 47 micron grains \|\| tested at -196.1 °C (-321.1 °F), 4.2x10^-⁴/s \|\| 0 to 0.124 mm/mm strain SSC : annealed, 47 micron grains \|\| tested at 23 °C (73 °F), 4.2x10^-⁴/s \|\| 0 to 0.17 mm/mm strain SSC : annealed, 47 micron grains \|\| tested at 180 °C (356 °F), 4.2x10^-⁴/s \|\| 0 to 0.172 mm/mm strain SSCC : annealed, 0.001/s, in-plane \|\| tested at 20 °C (68 °F), 25 micron grains \|\| 0 to 0.2 mm/mm strain UTS : annealed \|\| -190 °C to 500 °C (-310 °F to 932 °F) UTS : cold worked 50% \|\| -190 °C to 27 °C (-310 °F to 80 °F) YS : annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) %El : annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) %El : cold worked 50% \|\| -190 °C to 27 °C (-310 °F to 80 °F) FSN : 0.003 O₂ (wt %) \|\| tested at 20 °C (68 °F), R = -1, axial, 36 micron grain size, maximum stress \|\| 7.3x10³ cycles to 1x10⁶ cycles FSN : 0.003 O₂ (wt %) \|\| tested at 20 °C (68 °F), R = -1, axial, 110 micron grain size, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : 0.0775 O₂ (wt %) \|\| tested at 20 °C (68 °F), R = -1, axial, 30 micron grain size, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : 0.0775 O₂ (wt %) \|\| tested at 20 °C (68 °F), R = -1, axial, 93 micron grain size, maximum stress \|\| 6.3x10³ cycles to 1x10⁷ cycles HE : solid \|\| polished \|\| 1127 °C to 1827 °C (2060 °F to 3320 °F) HE : solid \|\| smooth \|\| 1227 °C to 1827 °C (2240 °F to 3320 °F) HE : liquid \|\| 1855 °C to 1940 °C (3371 °F to 3524 °F) NE : solid \|\| as-received \|\| 815 °C to 1635 °C (1499 °F to 2975 °F) VP : solid \|\| 20 °C to 1855 °C (68 °F to 3371 °F) VP : liquid \|\| 1855 °C to 2227 °C (3371 °F to 4040 °F) Vis : liquid \|\| 1527 °C to 2352 °C (2780 °F to 4265 °F) ST : liquid \|\| 1577 °C to 1927 °C (2870 °F to 3501 °F) RHO : solid \|\| high purity \|\| -272 °C to 1854 °C (-458 °F to 3369 °F) RHO : solid \|\| 0.33% O₂ \|\| -207 °C to 1019 °C (-341 °F to 1866 °F) RHO : liquid \|\| 1854 °C to 1864 °C (3369 °F to 3387 °F) SIGMA : solid \|\| high purity \|\| -272 °C to 1854 °C (-458 °F to 3369 °F) SIGMA : solid \|\| 0.33% O₂ \|\| -207 °C to 1019 °C (-341 °F to 1866 °F) SIGMA : liquid \|\| 1854 °C to 1864 °C (3369 °F to 3387 °F)
Niobium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 2327 °C (-460 °F to 4220 °F) D : liquid \|\| 2067 °C to 5575 °C (3752 °F to 10067 °F) DLL : solid \|\| -273 °C to 2327 °C (-460 °F to 4220 °F) DLL : liquid \|\| 2067 °C to 5575 °C (3752 °F to 10067 °F) MTE : solid \|\| -273 °C to 2327 °C (-460 °F to 4220 °F) MTE : liquid \|\| 2067 °C to 5575 °C (3752 °F to 10067 °F) CTE : liquid \|\| 2067 °C to 5575 °C (3752 °F to 10067 °F) E : solid \|\| polycrystal \|\| -150 °C to 1677 °C (-238 °F to 3050 °F) E : solid \|\| <100> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) E : solid \|\| <110> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) E : solid \|\| <111> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) G : solid \|\| polycrystal \|\| -150 °C to 477 °C (-238 °F to 890 °F) G : solid \|\| <100> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) G : solid \|\| <110> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) G : solid \|\| <111> axis \|\| -150 °C to 650 °C (-238 °F to 1202 °F) v : solid \|\| polycrystal \|\| -150 °C to 477 °C (-238 °F to 890 °F) K : solid \|\| polycrystal \|\| -150 °C to 477 °C (-238 °F to 890 °F) TC : solid \|\| annealed \|\| -273 °C to 1927 °C (-460 °F to 3500 °F) TC : liquid \|\| 2469 °C to 4227 °C (4476 °F to 7641 °F) TD : solid \|\| annealed \|\| -262 °C to 1927 °C (-440 °F to 3500 °F) TD : liquid \|\| 2469 °C to 4227 °C (4476 °F to 7641 °F) SH : solid \|\| -262 °C to 2427 °C (-440 °F to 4400 °F) SH : liquid \|\| 2067 °C to 2627 °C (3752 °F to 4760 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -262 °C to 2427 °C (-440 °F to 4400 °F) HC : liquid \|\| 2067 °C to 2627 °C (3752 °F to 4760 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSC : electron beam melted, annealed, 0.001/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at -83 °C (-118 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 127 °C (260 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 227 °C (440 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 327 °C (620 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 427 °C (800 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 527 °C (980 °F) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 0.1/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at -83 °C (-118 °F) \|\| 0 to 0.55 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 127 °C (260 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 227 °C (440 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 327 °C (620 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 427 °C (800 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 527 °C (980 °F) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 8000/s \|\| tested at 23 °C (73 °F) \|\| 0 to 0.6 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 1x10^-⁴/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.38 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 1x10^-⁴/s \|\| tested at 1500 °C (2732 °F) \|\| 0 to 0.38 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1350 °C (2462 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1400 °C (2552 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1450 °C (2642 °F) \|\| 0 to 0.38 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1500 °C (2732 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 1, annealed, 0.001/s \|\| tested at 1550 °C (2822 °F) \|\| 0 to 0.4 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.47 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.75 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.124 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1350 °C (2462 °F) \|\| 0 to 0.19 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1400 °C (2552 °F) \|\| 0 to 0.19 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1450 °C (2642 °F) \|\| 0 to 0.2 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 1x10^-⁴/s \|\| tested at 1500 °C (2732 °F) \|\| 0 to 0.22 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.46 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.7 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.2 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1350 °C (2462 °F) \|\| 0 to 0.2 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1400 °C (2552 °F) \|\| 0 to 0.23 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1450 °C (2642 °F) \|\| 0 to 0.25 mm/mm strain SSC : ASTM B393-18 Type 2, annealed, 0.001/s \|\| tested at 1500 °C (2732 °F) \|\| 0 to 0.24 mm/mm strain UTS : solid \|\| annealed, minimum 90% recrystallized \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.00167/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : solid \|\| 6x10^-⁴/s strain rate \|\| -196 °C to 1200 °C (-321 °F to 2192 °F) YS : solid \|\| 2.8/s strain rate \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| -150 °C to 25 °C (-238 °F to 77 °F) YS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) YSC : solid \|\| 3300/s strain rate \|\| -196 °C to 527 °C (-321 °F to 980 °F) YSC : solid \|\| 8000/s strain rate \|\| 20 °C to 627 °C (68 °F to 1160 °F) %El : solid \|\| annealed, minimum 90% recrystallized \|\| 20 °C to 1200 °C (68 °F to 2192 °F) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 0.00167/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33x10^-⁵/s \|\| -150 °C to 25 °C (-238 °F to 77 °F) SR : cold worked \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1,000 h SR : recrystallized \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1,000 h FSN : 85% reduction \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁵ cycles to 3x10⁶ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 1x10⁵ cycles to 3x10⁶ cycles HE : solid \|\| smooth \|\| 1427 °C to 2377 °C (2600 °F to 4310 °F) NE : solid \|\| oxidized at 649 °C (1200 °F) \|\| 773 °C to 996 °C (1423 °F to 1825 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F) Vis : liquid \|\| 2047 °C to 2642 °C (3716 °F to 4787 °F) ST : liquid \|\| 2468 °C to 2668 °C (4474 °F to 4834 °F) RHO : solid \|\| annealed \|\| -261 °C to 2427 °C (-438 °F to 4400 °F) RHO : liquid \|\| 2527 °C to 3027 °C (4580 °F to 5480 °F) SIGMA : solid \|\| annealed \|\| -261 °C to 2427 °C (-438 °F to 4400 °F) SIGMA : liquid \|\| 2527 °C to 3027 °C (4580 °F to 5480 °F)
Molybdenum (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 2227 °C (-460 °F to 4040 °F) D : liquid \|\| 2227 °C to 5627 °C (4040 °F to 10161 °F) DLL : solid \|\| -273 °C to 2227 °C (-460 °F to 4040 °F) DLL : liquid \|\| 2227 °C to 5627 °C (4040 °F to 10161 °F) MTE : solid \|\| -273 °C to 2227 °C (-460 °F to 4040 °F) MTE : liquid \|\| 2227 °C to 5627 °C (4040 °F to 10161 °F) CTE : liquid \|\| 2227 °C to 5627 °C (4040 °F to 10161 °F) E : solid \|\| polycrystal \|\| -180 °C to 2000 °C (-292 °F to 3632 °F) E : solid \|\| [100] \|\| -200 °C to 700 °C (-328 °F to 1292 °F) E : solid \|\| [111] \|\| -200 °C to 700 °C (-328 °F to 1292 °F) E : solid \|\| [110] \|\| -200 °C to 700 °C (-328 °F to 1292 °F) G : solid \|\| polycrystal \|\| 20 °C to 870 °C (68 °F to 1598 °F) v : solid \|\| polycrystal \|\| 20 °C to 870 °C (68 °F to 1598 °F) K : solid \|\| polycrystal \|\| 20 °C to 870 °C (68 °F to 1598 °F) TC : solid \|\| annealed \|\| -273 °C to 2527 °C (-460 °F to 4580 °F) TC : liquid \|\| 2623 °C to 4227 °C (4753 °F to 7640 °F) TD : solid \|\| annealed \|\| -73 °C to 2227 °C (-100 °F to 4040 °F) TD : liquid \|\| 2623 °C to 4227 °C (4753 °F to 7641 °F) SH : solid \|\| -273 °C to 2624 °C (-459 °F to 4755 °F) SH : liquid \|\| 2623 °C to 4727 °C (4753 °F to 8540 °F) SH : gas \|\| 25 °C to 4727 °C (77 °F to 8540 °F) HC : solid \|\| -273 °C to 2624 °C (-459 °F to 4755 °F) HC : liquid \|\| 2623 °C to 4727 °C (4753 °F to 8540 °F) HC : gas \|\| 25 °C to 4727 °C (77 °F to 8540 °F) SSC : annealed, 6x10^-⁴/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.26 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.2 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.7 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 125 °C (257 °F) \|\| 0 to 0.73 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 225 °C (437 °F) \|\| 0 to 0.67 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.72 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.73 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.73 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 625 °C (1157 °F) \|\| 0 to 0.71 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 725 °C (1337 °F) \|\| 0 to 0.72 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.61 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 125 °C (257 °F) \|\| 0 to 0.7 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 225 °C (437 °F) \|\| 0 to 0.73 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.72 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.73 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.7 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 625 °C (1157 °F) \|\| 0 to 0.71 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 725 °C (1337 °F) \|\| 0 to 0.72 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 125 °C (257 °F) \|\| 0 to 0.6 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 225 °C (437 °F) \|\| 0 to 0.66 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.66 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.67 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 725 °C (1337 °F) \|\| 0 to 0.66 mm/mm strain SSCC : annealed, 3100/s \|\| tested at 825 °C (1517 °F) \|\| 0 to 0.6 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 125 °C (257 °F) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.34 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 525 °C (977 °F) \|\| 0 to 0.34 mm/mm strain SSCC : annealed, 8000/s \|\| tested at 725 °C (1337 °F) \|\| 0 to 0.36 mm/mm strain UTS : powder metallurgy \|\| forgings \|\| 20 °C to 2371 °C (68 °F to 4300 °F) UTS : arc-cast \|\| forgings \|\| 20 °C to 2482 °C (68 °F to 4499 °F) YS : powder metallurgy \|\| forgings \|\| 20 °C to 2371 °C (68 °F to 4300 °F) YS : arc-cast \|\| forgings \|\| 20 °C to 2482 °C (68 °F to 4499 °F) YS : arc-cast \|\| forgings, annealed 2 h at 1400 °C (2552 °F) \|\| -90 °C to 40 °C (-130 °F to 104 °F) YSC : powder metallurgy \|\| recrystallized bar \|\| -203 °C to 410 °C (-334 °F to 770 °F) %El : powder metallurgy \|\| forgings \|\| 20 °C to 2371 °C (68 °F to 4300 °F) %El : arc-cast \|\| forgings \|\| 20 °C to 2482 °C (68 °F to 4499 °F) SR : sheet \|\| tested at 1400 °C (2552 °F) \|\| 1 h to 200 h SR : sheet \|\| tested at 1600 °C (2912 °F) \|\| 1 h to 200 h SR : sheet \|\| Master curve (LMP) \|\| 1400 °C to 1601 °C (2552 °F to 2914 °F) SR : 0.7 wt% La₂O₃ ODS sheet \|\| tested at 1400 °C (2552 °F) \|\| 1 h to 700 h SR : 0.7 wt% La₂O₃ ODS sheet \|\| tested at 1600 °C (2912 °F) \|\| 1 h to 700 h SR : 0.7 wt% La₂O₃ ODS sheet \|\| Master curve (LMP) \|\| 1400 °C to 1601 °C (2552 °F to 2914 °F) FSN : powder metallurgy \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4x10⁵ cycles to 1x10⁸ cycles FSN : arc-cast \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4x10⁵ cycles to 1x10⁸ cycles CRS : 0.05% plastic strain \|\| tested at 1538 °C (2800 °F) \|\| 0.00278 h to 0.00694 h CRS : 0.05% plastic strain \|\| tested at 1649 °C (3000 °F) \|\| 0.00278 h to 0.36 h CRS : 0.05% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.00333 h to 0.00889 h CRS : 0.05% plastic strain \|\| Master curve (LMP) \|\| 1537 °C to 1761 °C (2798 °F to 3202 °F) CRS : 0.1% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.00833 h to 0.21 h CRS : 0.2% plastic strain \|\| tested at 1538 °C (2800 °F) \|\| 0.00833 h to 0.49 h CRS : 0.2% plastic strain \|\| tested at 1649 °C (3000 °F) \|\| 0.00556 h to 0.389 h CRS : 0.2% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.28 h to 0.231 h CRS : 0.2% plastic strain \|\| Master curve (LMP) \|\| 1537 °C to 1761 °C (2798 °F to 3202 °F) CRS : 0.5% plastic strain \|\| tested at 1538 °C (2800 °F) \|\| 0.47 h to 0.115 h CRS : 0.5% plastic strain \|\| tested at 1649 °C (3000 °F) \|\| 0.27 h to 0.731 h CRS : 0.5% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.16 h to 0.339 h CRS : 0.5% plastic strain \|\| Master curve (LMP) \|\| 1537 °C to 1761 °C (2798 °F to 3202 °F) CRS : 1% plastic strain \|\| tested at 1538 °C (2800 °F) \|\| 0.16 h to 0.247 h CRS : 1% plastic strain \|\| tested at 1649 °C (3000 °F) \|\| 0.83 h to 3.47 h CRS : 1% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.278 h to 0.322 h CRS : 1% plastic strain \|\| Master curve (LMP) \|\| 1537 °C to 1761 °C (2798 °F to 3202 °F) CRS : 2% plastic strain \|\| tested at 1538 °C (2800 °F) \|\| 0.522 h to 1.5 h CRS : 2% plastic strain \|\| tested at 1649 °C (3000 °F) \|\| 0.2 h to 6.86 h CRS : 2% plastic strain \|\| tested at 1760 °C (3200 °F) \|\| 0.694 h to 4.19 h CRS : 2% plastic strain \|\| Master curve (LMP) \|\| 1537 °C to 1761 °C (2798 °F to 3202 °F) IC : tested at 1538 °C (2800 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 1538 °C (2800 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1538 °C (2800 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1538 °C (2800 °F), plastic strain, in air \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1538 °C (2800 °F), plastic strain, in air \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1566 °C (2850 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 1566 °C (2850 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1566 °C (2850 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1566 °C (2850 °F), plastic strain, in air \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1593 °C (2900 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1593 °C (2900 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1593 °C (2900 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1593 °C (2900 °F), plastic strain, in air \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1621 °C (2950 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1621 °C (2950 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1621 °C (2950 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1677 °C (3050 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1677 °C (3050 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1677 °C (3050 °F), plastic strain, in air \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1704 °C (3100 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1704 °C (3100 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1732 °C (3150 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1732 °C (3150 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1760 °C (3200 °F), plastic strain, in air \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1760 °C (3200 °F), plastic strain, in air \|\| 1 h \|\| 0 to 0.2 mm/mm strain HE : solid \|\| polished \|\| 1727 °C to 2427 °C (3140 °F to 4400 °F) HE : solid \|\| sand blasted \|\| 107 °C to 1000 °C (224 °F to 1832 °F) HE : solid \|\| oxidized \|\| 315 °C to 538 °C (599 °F to 1000 °F) NE : solid \|\| oxidized \|\| 315 °C to 538 °C (599 °F to 1000 °F) NE : solid \|\| polished \|\| 149 °C to 2622 °C (300 °F to 4751 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : liquid \|\| 2727 °C to 4804 °C (4940 °F to 8679 °F) Vis : liquid \|\| 2377 °C to 2727 °C (4310 °F to 4940 °F) ST : liquid \|\| 2377 °C to 2727 °C (4310 °F to 4940 °F) RHO : solid \|\| -272 °C to 2621 °C (-458 °F to 4750 °F) RHO : liquid \|\| 2623 °C to 3327 °C (4753 °F to 6020 °F) SIGMA : solid \|\| -272 °C to 2621 °C (-458 °F to 4750 °F) SIGMA : liquid \|\| 2623 °C to 3327 °C (4753 °F to 6020 °F) S : solid \|\| 0 °C to 2127 °C (32 °F to 3860 °F)
Technetium	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| annealed \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| annealed \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 2127 °C (68 °F to 3861 °F) HC : solid \|\| 20 °C to 2127 °C (68 °F to 3861 °F) VP : solid \|\| 1307 °C to 4727 °C (2384 °F to 8540 °F)
Ruthenium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1952 °C to 2502 °C (3545 °F to 4535 °F) DLL : liquid \|\| 1952 °C to 2502 °C (3545 °F to 4535 °F) MTE : liquid \|\| 1952 °C to 2502 °C (3545 °F to 4535 °F) CTE : liquid \|\| 1952 °C to 2502 °C (3545 °F to 4535 °F) E : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) G : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) v : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) K : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) TC : solid \|\| annealed \|\| -273 °C to 2227 °C (-460 °F to 4040 °F) TD* : solid \|\| room temperature value SH : solid \|\| -273 °C to 2334 °C (-460 °F to 4233 °F) SH : liquid \|\| 2334 °C to 2727 °C (4233 °F to 4940 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -273 °C to 2334 °C (-460 °F to 4233 °F) HC : liquid \|\| 2334 °C to 2727 °C (4233 °F to 4940 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| 20 °C to 2334 °C (68 °F to 4233 °F) Vis : liquid \|\| 2177 °C to 2452 °C (3950 °F to 4445 °F) RHO : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Rhodium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) D : liquid \|\| 1547 °C to 1977 °C (2816 °F to 3590 °F) DLL : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) DLL : liquid \|\| 1547 °C to 1977 °C (2816 °F to 3590 °F) MTE : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) MTE : liquid \|\| 1547 °C to 1977 °C (2816 °F to 3590 °F) CTE : liquid \|\| 1547 °C to 1977 °C (2816 °F to 3590 °F) E : solid \|\| -180 °C to 900 °C (-292 °F to 1652 °F) TC : solid \|\| annealed \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) TD : solid \|\| annealed \|\| -272 °C to 500 °C (-458 °F to 932 °F) SH : solid \|\| -273 °C to 1964 °C (-460 °F to 3567 °F) SH : liquid \|\| 1964 °C to 2227 °C (3567 °F to 4040 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 1964 °C (-460 °F to 3567 °F) HC : liquid \|\| 1964 °C to 2227 °C (3567 °F to 4040 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SR : unknown condition \|\| tested at 1600 °C (2912 °F) \|\| 0.15 h to 28 h SR : unknown condition \|\| tested at 1700 °C (3092 °F) \|\| 0.15 h to 28 h SR : unknown condition \|\| tested at 1800 °C (3272 °F) \|\| 0.13 h to 27 h SR : unknown condition \|\| Master curve (LMP) \|\| 1600 °C to 1801 °C (2912 °F to 3274 °F) VP : solid \|\| 20 °C to 1964 °C (68 °F to 3567 °F) VP : liquid \|\| 1964 °C to 2227 °C (3567 °F to 4040 °F) Vis : liquid \|\| 1600 °C to 2100 °C (2912 °F to 3812 °F) ST : liquid \|\| 1964 °C to 2150 °C (3567 °F to 3902 °F) RHO : solid \|\| -253 °C to 1963 °C (-424 °F to 3565 °F) RHO : liquid \|\| 1963 °C to 2877 °C (3565 °F to 5210 °F) SIGMA : solid \|\| -253 °C to 1963 °C (-424 °F to 3565 °F) SIGMA : liquid \|\| 1963 °C to 2877 °C (3565 °F to 5210 °F)
Palladium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1555 °C (-460 °F to 2831 °F) D : liquid \|\| 1555 °C to 2727 °C (2831 °F to 4940 °F) DLL : solid \|\| -273 °C to 1555 °C (-460 °F to 2831 °F) DLL : liquid \|\| 1555 °C to 2727 °C (2831 °F to 4940 °F) MTE : solid \|\| -273 °C to 1555 °C (-460 °F to 2831 °F) MTE : liquid \|\| 1555 °C to 2727 °C (2831 °F to 4940 °F) CTE : solid \|\| -243 °C to 27 °C (-406 °F to 80 °F) CTE : liquid \|\| 1555 °C to 2727 °C (2831 °F to 4940 °F) E : solid \|\| -243 °C to 927 °C (-406 °F to 1700 °F) G : solid \|\| 0 °C to 827 °C (32 °F to 1520 °F) v : solid \|\| 0 °C to 827 °C (32 °F to 1520 °F) K : solid \|\| 0 °C to 827 °C (32 °F to 1520 °F) TC : solid \|\| annealed \|\| -273 °C to 1527 °C (-460 °F to 2780 °F) TD : solid \|\| annealed \|\| -272 °C to 1527 °C (-458 °F to 2780 °F) SH : solid \|\| -273 °C to 1554 °C (-460 °F to 2829 °F) SH : liquid \|\| 1554 °C to 2227 °C (2829 °F to 4040 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| -273 °C to 1554 °C (-460 °F to 2829 °F) HC : liquid \|\| 1554 °C to 2227 °C (2829 °F to 4040 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) UTS* : 0.25 mm (0.00984 inch) thick foil \|\| vacuum annealed 24 h at 550 °C (1022 °F) \|\| room temperature value UTS : 1.27 mm (0.05 inch) diameter wire \|\| annealed at 1100 °C (2012 °F) for 5 minutes \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YS* : 0.25 mm (0.00984 inch) thick foil \|\| vacuum annealed 24 h at 550 °C (1022 °F) \|\| room temperature value %El* : 0.25 mm (0.00984 inch) thick foil \|\| vacuum annealed 24 h at 550 °C (1022 °F) \|\| room temperature value %El : 1.27 mm (0.05 inch) diameter wire \|\| annealed at 1100 °C (2012 °F) for 5 minutes \|\| 20 °C to 1100 °C (68 °F to 2012 °F) VP : solid \|\| 20 °C to 1555 °C (68 °F to 2831 °F) VP : liquid \|\| 1555 °C to 1827 °C (2831 °F to 3320 °F) Vis : liquid \|\| 1552 °C to 2052 °C (2825 °F to 3725 °F) ST : liquid \|\| 1552 °C to 1750 °C (2825 °F to 3182 °F) RHO : solid \|\| -272 °C to 1554 °C (-458 °F to 2829 °F) RHO : liquid \|\| 1555 °C to 2627 °C (2831 °F to 4760 °F) SIGMA : solid \|\| -272 °C to 1554 °C (-458 °F to 2829 °F) SIGMA : liquid \|\| 1555 °C to 2627 °C (2831 °F to 4760 °F) S : solid \|\| -173 °C to 1727 °C (-280 °F to 3140 °F)
Silver (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 600 °C (-460 °F to 1112 °F) D : liquid \|\| 962 °C to 1300 °C (1763 °F to 2372 °F) DLL : solid \|\| -273 °C to 600 °C (-460 °F to 1112 °F) DLL : liquid \|\| 962 °C to 1300 °C (1763 °F to 2372 °F) MTE : solid \|\| -273 °C to 600 °C (-460 °F to 1112 °F) MTE : liquid \|\| 962 °C to 1300 °C (1763 °F to 2372 °F) CTE : solid \|\| -243 °C to 27 °C (-406 °F to 80 °F) CTE : liquid \|\| 962 °C to 1300 °C (1763 °F to 2372 °F) E : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) G : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) v : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) K : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) TC : solid \|\| annealed \|\| -273 °C to 962 °C (-460 °F to 1763 °F) TC : solid \|\| nanowire \|\| -237 °C to 20 °C (-395 °F to 68 °F) TC : liquid \|\| 962 °C to 6727 °C (1763 °F to 12140 °F) TD : solid \|\| bulk, annealed \|\| -272 °C to 600 °C (-458 °F to 1112 °F) TD : solid \|\| nanowire \|\| -237 °C to 20 °C (-395 °F to 68 °F) TD : liquid \|\| 961 °C to 1300 °C (1762 °F to 2372 °F) SH : solid \|\| -272 °C to 962 °C (-458 °F to 1763 °F) SH : liquid \|\| 962 °C to 5727 °C (1763 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 962 °C (-458 °F to 1763 °F) HC : liquid \|\| 962 °C to 5727 °C (1763 °F to 10340 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed at 700 °C (1292 °F) \|\| tested at -253.1 °C (-423.7 °F), 6.67x10^-⁴/s \|\| 0 to 0.51 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at -195.1 °C (-319.3 °F), 6.67x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at -78 °C (-109 °F), 6.67x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at -68 °C (-91 °F), 6.67x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at 26 °C (79 °F), 6.67x10^-⁴/s \|\| 0 to 0.29 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at 200 °C (392 °F), 6.67x10^-⁴/s \|\| 0 to 0.21 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at 400 °C (752 °F), 6.67x10^-⁴/s \|\| 0 to 0.14 mm/mm strain SSC : annealed at 700 °C (1292 °F) \|\| tested at 600 °C (1112 °F), 6.67x10^-⁴/s \|\| 0 to 0.62 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at -253.1 °C (-423.7 °F), 6.67x10^-⁴/s \|\| 0 to 0.41 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at -196.1 °C (-321.1 °F), 6.67x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at -78 °C (-109 °F), 6.67x10^-⁴/s \|\| 0 to 0.24 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at 26 °C (79 °F), 6.67x10^-⁴/s \|\| 0 to 0.21 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at 200 °C (392 °F), 6.67x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at 400 °C (752 °F), 6.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : annealed at 800 °C (1472 °F) \|\| tested at 600 °C (1112 °F), 6.67x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at -253.1 °C (-423.7 °F), 6.67x10^-⁴/s \|\| 0 to 0.275 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at -196.1 °C (-321.1 °F), 6.67x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at -78 °C (-109 °F), 6.67x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at 27 °C (80 °F), 6.67x10^-⁴/s \|\| 0 to 0.14 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at 200 °C (392 °F), 6.67x10^-⁴/s \|\| 0 to 0.12 mm/mm strain SSC : annealed at 900 °C (1652 °F) \|\| tested at 400 °C (752 °F), 6.67x10^-⁴/s \|\| 0 to 0.6 mm/mm strain UTS : annealing temperature \|\| annealed at 700 °C (1292 °F) \|\| -253 °C to 877 °C (-424 °F to 1610 °F) UTS : annealing temperature \|\| annealed at 800 °C (1472 °F) \|\| -253 °C to 877 °C (-424 °F to 1610 °F) UTS : annealing temperature \|\| annealed at 900 °C (1652 °F) \|\| -253 °C to 877 °C (-424 °F to 1610 °F) YS : annealing temperature \|\| annealed at 700 °C (1292 °F) \|\| -273 °C to 627 °C (-460 °F to 1160 °F) YS : annealing temperature \|\| annealed at 800 °C (1472 °F) \|\| -273 °C to 627 °C (-460 °F to 1160 °F) YS : annealing temperature \|\| annealed at 900 °C (1652 °F) \|\| -273 °C to 877 °C (-460 °F to 1610 °F) VP : solid \|\| 20 °C to 962 °C (68 °F to 1763 °F) VP : liquid \|\| 962 °C to 1327 °C (1763 °F to 2420 °F) Vis : liquid \|\| 961 °C to 1461 °C (1762 °F to 2662 °F) ST : liquid \|\| in vacuum \|\| 951 °C to 1498 °C (1744 °F to 2728 °F) ST : liquid \|\| Ar with 100 Pa O₂ \|\| 951 °C to 1498 °C (1744 °F to 2728 °F) RHO : solid \|\| bulk \|\| -272 °C to 962 °C (-458 °F to 1763 °F) RHO : solid \|\| nanowire \|\| -263 °C to 20 °C (-442 °F to 68 °F) RHO : liquid \|\| 962 °C to 1400 °C (1763 °F to 2552 °F) SIGMA : solid \|\| bulk \|\| -272 °C to 962 °C (-458 °F to 1763 °F) SIGMA : solid \|\| nanowire \|\| -263 °C to 20 °C (-442 °F to 68 °F) SIGMA : liquid \|\| 962 °C to 1400 °C (1763 °F to 2552 °F) RIW : measured in air \|\| tested at 20 °C (68 °F) \|\| 400 µm to 1000 µm S : solid \|\| -173 °C to 927 °C (-280 °F to 1700 °F)
Cadmium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) D : liquid \|\| 321 °C to 627 °C (610 °F to 1160 °F) DLL : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : liquid \|\| 321 °C to 627 °C (610 °F to 1160 °F) MTE : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : liquid \|\| 321 °C to 627 °C (610 °F to 1160 °F) CTE : liquid \|\| 321 °C to 627 °C (610 °F to 1160 °F) E : solid \|\| -273 °C to 300 °C (-460 °F to 572 °F) G : solid \|\| -273 °C to 300 °C (-460 °F to 572 °F) v : solid \|\| -273 °C to 300 °C (-460 °F to 572 °F) K : solid \|\| -273 °C to 300 °C (-460 °F to 572 °F) TC : solid \|\| -273 °C to 321 °C (-460 °F to 610 °F) TC : liquid \|\| 321 °C to 627 °C (610 °F to 1160 °F) TD : solid \|\| -263 °C to 321 °C (-442 °F to 610 °F) TD : liquid \|\| 321 °C to 527 °C (610 °F to 980 °F) SH : solid \|\| -272 °C to 321 °C (-458 °F to 610 °F) SH : liquid \|\| 321 °C to 5727 °C (610 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 321 °C (-458 °F to 610 °F) HC : liquid \|\| 321 °C to 5727 °C (610 °F to 10340 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) UTS : 0.508 mm (0.02 inch) grain size \|\| -269 °C to 24 °C (-452 °F to 75 °F) YS : 0.508 mm (0.02 inch) grain size \|\| -269 °C to 24 °C (-452 °F to 75 °F) VP : solid \|\| 20 °C to 321 °C (68 °F to 610 °F) VP : liquid \|\| 321 °C to 377 °C (610 °F to 710 °F) Vis : liquid \|\| 327 °C to 627 °C (620 °F to 1160 °F) ST : liquid \|\| 321 °C to 800 °C (610 °F to 1472 °F) RHO : liquid \|\| 320 °C to 480 °C (608 °F to 896 °F) SIGMA : liquid \|\| 320 °C to 480 °C (608 °F to 896 °F)
Indium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 106 °C (-460 °F to 223 °F) D : liquid \|\| 157 °C to 827 °C (314 °F to 1520 °F) DLL : solid \|\| -273 °C to 106 °C (-460 °F to 223 °F) DLL : liquid \|\| 157 °C to 827 °C (314 °F to 1520 °F) MTE : solid \|\| -273 °C to 106 °C (-460 °F to 223 °F) MTE : liquid \|\| 157 °C to 827 °C (314 °F to 1520 °F) CTE : solid \|\| -213 °C to 106 °C (-352 °F to 223 °F) CTE : liquid \|\| 157 °C to 827 °C (314 °F to 1520 °F) E : solid \|\| -273 °C to 150 °C (-460 °F to 302 °F) G : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) v : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) K : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) TC : solid \|\| annealed \|\| -273 °C to 157 °C (-460 °F to 314 °F) TC : liquid \|\| 157 °C to 627 °C (314 °F to 1160 °F) TD : solid \|\| -200 °C to 106 °C (-328 °F to 223 °F) TD : liquid \|\| 827 °C to 1827 °C (1520 °F to 3320 °F) SH : solid \|\| -269 °C to 157 °C (-452 °F to 314 °F) SH : liquid \|\| 157 °C to 1727 °C (314 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -269 °C to 157 °C (-452 °F to 314 °F) HC : liquid \|\| 157 °C to 1727 °C (314 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) UTS : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) VP : solid \|\| 20 °C to 157 °C (68 °F to 314 °F) VP : liquid \|\| 157 °C to 1227 °C (314 °F to 2240 °F) Vis : liquid \|\| 156 °C to 727 °C (313 °F to 1340 °F) ST : liquid \|\| 157 °C to 1027 °C (314 °F to 1880 °F) RHO : solid \|\| 20 °C to 280 °C (68 °F to 536 °F) RHO : liquid \|\| 157 °C to 412 °C (314 °F to 773 °F) SIGMA : solid \|\| 20 °C to 280 °C (68 °F to 536 °F) SIGMA : liquid \|\| 157 °C to 412 °C (314 °F to 773 °F)
Tin (UNS L13008) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 151 °C (68 °F to 304 °F) D : liquid \|\| 233 °C to 1127 °C (451 °F to 2060 °F) DLL : solid \|\| polycrystal \|\| 20 °C to 151 °C (68 °F to 304 °F) DLL : solid \|\| a-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) DLL : solid \|\| c-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) DLL : liquid \|\| 233 °C to 1127 °C (451 °F to 2060 °F) MTE : solid \|\| polycrystal \|\| 20 °C to 151 °C (68 °F to 304 °F) MTE : solid \|\| a-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) MTE : solid \|\| c-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) MTE : liquid \|\| 233 °C to 1127 °C (451 °F to 2060 °F) CTE : solid \|\| polycrystal \|\| 20 °C to 151 °C (68 °F to 304 °F) CTE : solid \|\| a-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) CTE : solid \|\| c-axis \|\| 20 °C to 151 °C (68 °F to 304 °F) CTE : liquid \|\| 233 °C to 1127 °C (451 °F to 2060 °F) E : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) G : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) v : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) K : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) TC : solid \|\| annealed \|\| -273 °C to 232 °C (-460 °F to 449 °F) TC : liquid \|\| 232 °C to 1227 °C (449 °F to 2240 °F) TD : solid \|\| annealed \|\| 20 °C to 151 °C (68 °F to 304 °F) TD : liquid \|\| 232 °C to 1127 °C (449 °F to 2060 °F) SH : solid \|\| -263 °C to 232 °C (-442 °F to 449 °F) SH : liquid \|\| 232 °C to 4427 °C (449 °F to 8000 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -263 °C to 232 °C (-442 °F to 449 °F) HC : liquid \|\| 232 °C to 4427 °C (449 °F to 8000 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) UTS* : solid \|\| room temperature value %El* : solid \|\| room temperature value VP : solid \|\| 20 °C to 232 °C (68 °F to 449 °F) VP : liquid \|\| 232 °C to 1577 °C (449 °F to 2870 °F) Vis : liquid \|\| 222 °C to 747 °C (431 °F to 1376 °F) ST : liquid \|\| 264 °C to 912 °C (507 °F to 1673 °F) RHO : solid \|\| -98 °C to 231 °C (-145 °F to 448 °F) RHO : liquid \|\| 235 °C to 1227 °C (455 °F to 2240 °F) SIGMA : solid \|\| -98 °C to 231 °C (-145 °F to 448 °F) SIGMA : liquid \|\| 235 °C to 1227 °C (455 °F to 2240 °F) AV : liquid \|\| tested at 260 °C (500 °F) \|\| 0/s to 2.08x10³/s
Antimony (UNS M00998) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 550 °C (-460 °F to 1022 °F) D : liquid \|\| 630 °C to 746 °C (1166 °F to 1375 °F) DLL : solid \|\| -273 °C to 550 °C (-460 °F to 1022 °F) DLL : liquid \|\| 630 °C to 746 °C (1166 °F to 1375 °F) MTE : solid \|\| -273 °C to 550 °C (-460 °F to 1022 °F) MTE : liquid \|\| 630 °C to 746 °C (1166 °F to 1375 °F) CTE : liquid \|\| 630 °C to 746 °C (1166 °F to 1375 °F) E : solid \|\| -180 °C to 625 °C (-292 °F to 1157 °F) TC : solid \|\| annealed \|\| -273 °C to 631 °C (-460 °F to 1168 °F) TC : liquid \|\| 631 °C to 827 °C (1168 °F to 1520 °F) TD : solid \|\| annealed \|\| 20 °C to 550 °C (68 °F to 1022 °F) TD : liquid \|\| 631 °C to 746 °C (1168 °F to 1375 °F) SH : solid \|\| 20 °C to 631 °C (68 °F to 1168 °F) SH : liquid \|\| 631 °C to 1587 °C (1168 °F to 2888 °F) SH : gas \|\| Sb \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Sb₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Sb₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 631 °C (68 °F to 1168 °F) HC : liquid \|\| 631 °C to 1587 °C (1168 °F to 2888 °F) HC : gas \|\| Sb \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Sb₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Sb₄ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) UTS* : solid \|\| room temperature value VP : solid \|\| 278 °C to 631 °C (532 °F to 1168 °F) VP : liquid \|\| 631 °C to 1689 °C (1168 °F to 3072 °F) Vis : liquid \|\| 624 °C to 730 °C (1155 °F to 1346 °F) ST : liquid \|\| 630 °C to 930 °C (1166 °F to 1706 °F) RHO : solid \|\| 0 °C to 590 °C (32 °F to 1094 °F) RHO : liquid \|\| 661 °C to 1006 °C (1222 °F to 1843 °F) SIGMA : solid \|\| 0 °C to 590 °C (32 °F to 1094 °F) SIGMA : liquid \|\| 661 °C to 1006 °C (1222 °F to 1843 °F)
Tellurium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 200 °C (68 °F to 392 °F) D : liquid \|\| 451 °C to 707 °C (844 °F to 1305 °F) DLL : solid \|\| polycrystal \|\| 20 °C to 200 °C (68 °F to 392 °F) DLL : solid \|\| a-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) DLL : solid \|\| c-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) DLL : liquid \|\| 451 °C to 707 °C (844 °F to 1305 °F) MTE : solid \|\| polycrystal \|\| 20 °C to 200 °C (68 °F to 392 °F) MTE : solid \|\| a-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) MTE : solid \|\| c-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) MTE : liquid \|\| 451 °C to 707 °C (844 °F to 1305 °F) CTE : solid \|\| polycrystal \|\| 20 °C to 200 °C (68 °F to 392 °F) CTE : solid \|\| a-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) CTE : solid \|\| c-axis \|\| 20 °C to 200 °C (68 °F to 392 °F) CTE : liquid \|\| 451 °C to 707 °C (844 °F to 1305 °F) TC : solid \|\| polycrystal \|\| -253 °C to -95 °C (-424 °F to -139 °F) TC : solid \|\| a-axis \|\| -253 °C to -95 °C (-424 °F to -139 °F) TC : solid \|\| c-axis \|\| -253 °C to -95 °C (-424 °F to -139 °F) TD : solid \|\| 300 °C to 439 °C (572 °F to 822 °F) TD : liquid \|\| 486 °C to 584 °C (907 °F to 1083 °F) SH : solid \|\| 20 °C to 450 °C (68 °F to 842 °F) SH : liquid \|\| 450 °C to 989 °C (842 °F to 1812 °F) SH : gas \|\| Te \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Te₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 450 °C (68 °F to 842 °F) HC : liquid \|\| 450 °C to 989 °C (842 °F to 1812 °F) HC : gas \|\| Te \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Te₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 179 °C to 450 °C (354 °F to 842 °F) VP : liquid \|\| 424 °C to 1027 °C (795 °F to 1880 °F) Vis : liquid \|\| 450 °C to 950 °C (842 °F to 1742 °F) ST : liquid \|\| 460 °C to 675 °C (860 °F to 1247 °F) RHO : liquid \|\| 441 °C to 977 °C (826 °F to 1790 °F) SIGMA : liquid \|\| 441 °C to 977 °C (826 °F to 1790 °F) RIW : tested at 23 °C (73 °F), parallel to c-axis \|\| 4 µm to 14 µm RIW : tested at 23 °C (73 °F), perpendicular to c-axis \|\| 4 µm to 14 µm
Iodine (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 114 °C to 314 °C (237 °F to 597 °F) DLL : liquid \|\| 114 °C to 314 °C (237 °F to 597 °F) MTE : liquid \|\| 114 °C to 314 °C (237 °F to 597 °F) CTE : liquid \|\| 114 °C to 314 °C (237 °F to 597 °F) TC : solid \|\| -23 °C to 114 °C (-10 °F to 237 °F) TC : liquid \|\| 114 °C to 512 °C (237 °F to 953 °F) TC : gas \|\| I \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : gas \|\| I₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TC : vapor \|\| 114 °C to 512 °C (237 °F to 953 °F) TD : solid \|\| 20 °C to 113 °C (68 °F to 235 °F) TD : liquid \|\| 114 °C to 184 °C (237 °F to 363 °F) SH : solid \|\| I₂ \|\| 20 °C to 113 °C (68 °F to 235 °F) SH : liquid \|\| I₂ \|\| 113 °C to 184 °C (235 °F to 363 °F) SH : gas \|\| I \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SH : gas \|\| I₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| I₂ \|\| 20 °C to 113 °C (68 °F to 235 °F) HC : liquid \|\| I₂ \|\| 113 °C to 184 °C (235 °F to 363 °F) HC : gas \|\| I \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : gas \|\| I₂ \|\| 20 °C to 2727 °C (68 °F to 4940 °F) VP : solid \|\| -96 °C to 114 °C (-141 °F to 237 °F) VP : liquid \|\| 114 °C to 197 °C (237 °F to 386 °F) Vis : gas \|\| I \|\| 20 °C to 4727 °C (68 °F to 8540 °F) Vis : gas \|\| I₂ \|\| 20 °C to 4727 °C (68 °F to 8540 °F)
Xenon (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to -113 °C (-460 °F to -172 °F) D : gas \|\| -108 °C to 2727 °C (-163 °F to 4940 °F) DLL : solid \|\| -273 °C to -113 °C (-460 °F to -172 °F) MTE : solid \|\| -273 °C to -113 °C (-460 °F to -172 °F) K : solid \|\| -273 °C to -113 °C (-460 °F to -172 °F) TC : solid \|\| -223 °C to -113 °C (-370 °F to -172 °F) TC : liquid \|\| -112 °C to 17 °C (-170 °F to 62 °F) TC : gas \|\| -108 °C to 1227 °C (-163 °F to 2240 °F) TC : vapor \|\| -108 °C to 17 °C (-163 °F to 62 °F) TD : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) SH : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) HC : gas \|\| -173 °C to 19727 °C (-280 °F to 35540 °F) VP : solid \|\| -173 °C to -118 °C (-280 °F to -181 °F) VP : liquid \|\| -113 °C to 7 °C (-172 °F to 44 °F) Vis : gas \|\| -223 °C to 3000 °C (-370 °F to 5432 °F) ST : liquid \|\| -108 °C to 12 °C (-163 °F to 53 °F)
Caesium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| 28 °C to 1030 °C (82 °F to 1886 °F) DLL : liquid \|\| 28 °C to 1030 °C (82 °F to 1886 °F) MTE : liquid \|\| 28 °C to 1030 °C (82 °F to 1886 °F) CTE : liquid \|\| 28 °C to 1030 °C (82 °F to 1886 °F) K : liquid \|\| 29 °C to 1327 °C (84 °F to 2420 °F) TC : solid \|\| -273 °C to 29 °C (-460 °F to 84 °F) TC : liquid \|\| 29 °C to 1727 °C (84 °F to 3140 °F) TD : liquid \|\| 29 °C to 1327 °C (84 °F to 2420 °F) SH : solid \|\| -273 °C to 28 °C (-460 °F to 83 °F) SH : liquid \|\| 28 °C to 1327 °C (83 °F to 2420 °F) SH : gas \|\| Cs \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Cs₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 28 °C (-460 °F to 83 °F) HC : liquid \|\| 28 °C to 1327 °C (83 °F to 2420 °F) HC : gas \|\| Cs \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Cs₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 29 °C (68 °F to 84 °F) VP : liquid \|\| 29 °C to 660 °C (84 °F to 1220 °F) Vis : liquid \|\| 135 °C to 1605 °C (275 °F to 2921 °F) Vis : gas \|\| 630 °C to 970 °C (1166 °F to 1778 °F) ST : liquid \|\| 28 °C to 1100 °C (82 °F to 2012 °F) RHO : solid \|\| -272 °C to 29 °C (-458 °F to 84 °F) RHO : liquid \|\| 29 °C to 1727 °C (84 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 29 °C (-458 °F to 84 °F) SIGMA : liquid \|\| 29 °C to 1727 °C (84 °F to 3140 °F)
Barium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : liquid \|\| 727 °C to 830 °C (1340 °F to 1526 °F) DLL : liquid \|\| 727 °C to 830 °C (1340 °F to 1526 °F) MTE : liquid \|\| 727 °C to 830 °C (1340 °F to 1526 °F) CTE : liquid \|\| 727 °C to 830 °C (1340 °F to 1526 °F) E : solid \|\| -180 °C to 450 °C (-292 °F to 842 °F) TC : liquid \|\| 665 °C to 1227 °C (1229 °F to 2240 °F) TD : liquid \|\| 727 °C to 1227 °C (1340 °F to 2240 °F) SH : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) SH : liquid \|\| 727 °C to 1927 °C (1340 °F to 3500 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) HC : liquid \|\| 727 °C to 1927 °C (1340 °F to 3500 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) VP : liquid \|\| 727 °C to 927 °C (1340 °F to 1700 °F) Vis : liquid \|\| 727 °C to 1727 °C (1340 °F to 3140 °F) ST : liquid \|\| 704 °C to 1573 °C (1299 °F to 2863 °F) RHO : solid \|\| -272 °C to 729 °C (-458 °F to 1344 °F) RHO : liquid \|\| 665 °C to 1227 °C (1229 °F to 2240 °F) SIGMA : solid \|\| -272 °C to 729 °C (-458 °F to 1344 °F) SIGMA : liquid \|\| 665 °C to 1227 °C (1229 °F to 2240 °F)
Lanthanum (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 920 °C to 1120 °C (1688 °F to 2048 °F) DLL : liquid \|\| 920 °C to 1120 °C (1688 °F to 2048 °F) MTE : liquid \|\| 920 °C to 1120 °C (1688 °F to 2048 °F) CTE : liquid \|\| 920 °C to 1120 °C (1688 °F to 2048 °F) E : solid \|\| -180 °C to 450 °C (-292 °F to 842 °F) TC : solid \|\| annealed \|\| -273 °C to 827 °C (-460 °F to 1520 °F) TC : liquid \|\| 1027 °C to 1727 °C (1880 °F to 3140 °F) TD : liquid \|\| 1027 °C to 1727 °C (1880 °F to 3140 °F) SH : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) SH : liquid \|\| 920 °C to 1727 °C (1689 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) HC : liquid \|\| 920 °C to 1727 °C (1689 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F) VP : liquid \|\| 920 °C to 2177 °C (1688 °F to 3950 °F) Vis : liquid \|\| 920 °C to 1420 °C (1688 °F to 2588 °F) ST : liquid \|\| 920 °C to 1770 °C (1688 °F to 3218 °F) RHO : solid \|\| -248 °C to 60 °C (-415 °F to 140 °F) RHO : liquid \|\| 1027 °C to 1727 °C (1880 °F to 3140 °F) SIGMA : solid \|\| -248 °C to 60 °C (-415 °F to 140 °F) SIGMA : liquid \|\| 1027 °C to 1727 °C (1880 °F to 3140 °F)
Cerium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 710 °C (68 °F to 1310 °F) D : liquid \|\| 795 °C to 995 °C (1463 °F to 1823 °F) DLL : solid \|\| 20 °C to 710 °C (68 °F to 1310 °F) DLL : liquid \|\| 795 °C to 995 °C (1463 °F to 1823 °F) MTE : solid \|\| 20 °C to 710 °C (68 °F to 1310 °F) MTE : liquid \|\| 795 °C to 995 °C (1463 °F to 1823 °F) CTE : solid \|\| 20 °C to 710 °C (68 °F to 1310 °F) CTE : liquid \|\| 795 °C to 995 °C (1463 °F to 1823 °F) TC : solid \|\| -273 °C to 727 °C (-460 °F to 1340 °F) TC : liquid \|\| 1027 °C to 1527 °C (1880 °F to 2780 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TD : liquid \|\| 1027 °C to 1527 °C (1880 °F to 2780 °F) SH : solid \|\| 20 °C to 798 °C (68 °F to 1468 °F) SH : liquid \|\| 1258 °C to 2135 °C (2296 °F to 3875 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 798 °C (68 °F to 1468 °F) HC : liquid \|\| 1258 °C to 2135 °C (2296 °F to 3875 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 795 °C (68 °F to 1463 °F) VP : liquid \|\| 795 °C to 2177 °C (1463 °F to 3950 °F) Vis : liquid \|\| 798 °C to 1298 °C (1468 °F to 2368 °F) ST : liquid \|\| 800 °C to 1700 °C (1472 °F to 3092 °F) RHO : liquid \|\| 1027 °C to 1527 °C (1880 °F to 2780 °F) SIGMA : liquid \|\| 1027 °C to 1527 °C (1880 °F to 2780 °F)
Praseodymium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) D : liquid \|\| 935 °C to 1135 °C (1715 °F to 2075 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : liquid \|\| 935 °C to 1135 °C (1715 °F to 2075 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : liquid \|\| 935 °C to 1135 °C (1715 °F to 2075 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : liquid \|\| 935 °C to 1135 °C (1715 °F to 2075 °F) E : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F) G : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F) v : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F) K : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F) TC : solid \|\| annealed \|\| -193 °C to 727 °C (-316 °F to 1340 °F) TD : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) SH : solid \|\| 20 °C to 931 °C (68 °F to 1708 °F) SH : liquid \|\| 931 °C to 1727 °C (1708 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 931 °C (68 °F to 1708 °F) HC : liquid \|\| 931 °C to 1727 °C (1708 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 935 °C (68 °F to 1715 °F) VP : liquid \|\| 935 °C to 1927 °C (1715 °F to 3500 °F) Vis : liquid \|\| 932 °C to 1432 °C (1709 °F to 2609 °F) ST : liquid \|\| 932 °C to 1600 °C (1709 °F to 2912 °F)
Neodymium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 860 °C (68 °F to 1580 °F) D : liquid \|\| 1024 °C to 1224 °C (1875 °F to 2235 °F) DLL : solid \|\| 20 °C to 860 °C (68 °F to 1580 °F) DLL : liquid \|\| 1024 °C to 1224 °C (1875 °F to 2235 °F) MTE : solid \|\| 20 °C to 860 °C (68 °F to 1580 °F) MTE : liquid \|\| 1024 °C to 1224 °C (1875 °F to 2235 °F) CTE : solid \|\| 20 °C to 860 °C (68 °F to 1580 °F) CTE : liquid \|\| 1024 °C to 1224 °C (1875 °F to 2235 °F) TC : solid \|\| -73 °C to 862 °C (-100 °F to 1583 °F) TC : liquid \|\| 947 °C to 1327 °C (1736 °F to 2420 °F) TD : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TD : liquid \|\| 947 °C to 1327 °C (1736 °F to 2420 °F) SH : solid \|\| 20 °C to 855 °C (68 °F to 1571 °F) SH : liquid \|\| 1027 °C to 1327 °C (1880 °F to 2420 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 855 °C (68 °F to 1571 °F) HC : liquid \|\| 1027 °C to 1327 °C (1880 °F to 2420 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1024 °C (68 °F to 1875 °F) VP : liquid \|\| 1024 °C to 1727 °C (1875 °F to 3140 °F) ST : liquid \|\| 1024 °C to 1750 °C (1875 °F to 3182 °F) RHO : solid \|\| -248 °C to 87 °C (-415 °F to 188 °F) RHO : liquid \|\| 1027 °C to 1327 °C (1880 °F to 2420 °F) SIGMA : solid \|\| -248 °C to 87 °C (-415 °F to 188 °F) SIGMA : liquid \|\| 1027 °C to 1327 °C (1880 °F to 2420 °F)
Promethium	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 912 °C (68 °F to 1674 °F) TC : liquid \|\| 1080 °C to 1980 °C (1976 °F to 3596 °F) TD : solid \|\| 20 °C to 912 °C (68 °F to 1674 °F) SH : solid \|\| 20 °C to 1027 °C (68 °F to 1881 °F) HC : solid \|\| 20 °C to 1027 °C (68 °F to 1881 °F)
Samarium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -173 °C to 1087 °C (-280 °F to 1988 °F) D : liquid \|\| 1087 °C to 1627 °C (1988 °F to 2960 °F) DLL : solid \|\| -173 °C to 1087 °C (-280 °F to 1988 °F) DLL : liquid \|\| 1087 °C to 1627 °C (1988 °F to 2960 °F) MTE : solid \|\| -173 °C to 1087 °C (-280 °F to 1988 °F) MTE : liquid \|\| 1087 °C to 1627 °C (1988 °F to 2960 °F) CTE : liquid \|\| 1087 °C to 1627 °C (1988 °F to 2960 °F) TC : solid \|\| annealed \|\| -273 °C to 327 °C (-460 °F to 620 °F) TD : solid \|\| 20 °C to 327 °C (68 °F to 620 °F) SH : solid \|\| 20 °C to 1072 °C (68 °F to 1961 °F) SH : liquid \|\| 1072 °C to 1727 °C (1961 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1072 °C (68 °F to 1961 °F) HC : liquid \|\| 1072 °C to 1727 °C (1961 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1072 °C (68 °F to 1961 °F) ST : liquid \|\| 1072 °C to 1750 °C (1961 °F to 3182 °F)
Europium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -173 °C to 127 °C (-280 °F to 260 °F) TC : solid \|\| annealed \|\| -150 °C to 27 °C (-238 °F to 80 °F) TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 817 °C (68 °F to 1502 °F) SH : liquid \|\| 817 °C to 1727 °C (1502 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 817 °C (68 °F to 1502 °F) HC : liquid \|\| 817 °C to 1727 °C (1502 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 826 °C (68 °F to 1519 °F) ST : liquid \|\| 826 °C to 1775 °C (1519 °F to 3227 °F)
Gadolinium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 932 °C (68 °F to 1709 °F) D : liquid \|\| 1312 °C to 1650 °C (2393 °F to 3002 °F) DLL : solid \|\| 20 °C to 932 °C (68 °F to 1709 °F) DLL : liquid \|\| 1312 °C to 1650 °C (2393 °F to 3002 °F) MTE : solid \|\| 20 °C to 932 °C (68 °F to 1709 °F) MTE : liquid \|\| 1312 °C to 1650 °C (2393 °F to 3002 °F) CTE : solid \|\| 20 °C to 932 °C (68 °F to 1709 °F) CTE : liquid \|\| 1312 °C to 1650 °C (2393 °F to 3002 °F) TC : solid \|\| annealed \|\| -273 °C to 37 °C (-460 °F to 98 °F) TD : solid \|\| annealed \|\| 20 °C to 37 °C (68 °F to 98 °F) SH : solid \|\| 20 °C to 1312 °C (68 °F to 2393 °F) SH : liquid \|\| 1312 °C to 1727 °C (2393 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1312 °C (68 °F to 2393 °F) HC : liquid \|\| 1312 °C to 1727 °C (2393 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1312 °C (68 °F to 2393 °F) VP : liquid \|\| 1312 °C to 1977 °C (2393 °F to 3590 °F) Vis : liquid \|\| 1340 °C to 1530 °C (2444 °F to 2786 °F) ST : liquid \|\| 1340 °C to 1750 °C (2444 °F to 3182 °F) RHO : solid \|\| -248 °C to 171 °C (-415 °F to 340 °F) SIGMA : solid \|\| -248 °C to 171 °C (-415 °F to 340 °F)
Terbium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 940 °C (68 °F to 1724 °F) DLL : solid \|\| 20 °C to 940 °C (68 °F to 1724 °F) MTE : solid \|\| 20 °C to 940 °C (68 °F to 1724 °F) CTE : solid \|\| 20 °C to 940 °C (68 °F to 1724 °F) TC : solid \|\| annealed \|\| -273 °C to 27 °C (-460 °F to 80 °F) TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1357 °C (68 °F to 2474 °F) SH : liquid \|\| 1357 °C to 1727 °C (2474 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1357 °C (68 °F to 2474 °F) HC : liquid \|\| 1357 °C to 1727 °C (2474 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1356 °C (68 °F to 2473 °F) VP : liquid \|\| 1356 °C to 1927 °C (2473 °F to 3500 °F) ST : liquid \|\| 1356 °C to 1800 °C (2473 °F to 3272 °F)
Dysprosium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) D : liquid \|\| 1410 °C to 1677 °C (2570 °F to 3050 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : liquid \|\| 1410 °C to 1677 °C (2570 °F to 3050 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : liquid \|\| 1410 °C to 1677 °C (2570 °F to 3050 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : liquid \|\| 1410 °C to 1677 °C (2570 °F to 3050 °F) E : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) G : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) v : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) K : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) TC : solid \|\| annealed \|\| -273 °C to 1227 °C (-460 °F to 2240 °F) TD : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SH : solid \|\| 20 °C to 1409 °C (68 °F to 2568 °F) SH : liquid \|\| 1409 °C to 1727 °C (2568 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1409 °C (68 °F to 2568 °F) HC : liquid \|\| 1409 °C to 1727 °C (2568 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1407 °C (68 °F to 2564 °F) ST : liquid \|\| 1500 °C to 1750 °C (2732 °F to 3182 °F) RHO : solid \|\| -263 °C to 77 °C (-442 °F to 170 °F) SIGMA : solid \|\| -263 °C to 77 °C (-442 °F to 170 °F)
Holmium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -273 °C to 227 °C (-460 °F to 440 °F) TD : solid \|\| 20 °C to 227 °C (68 °F to 440 °F) SH : solid \|\| 20 °C to 1470 °C (68 °F to 2678 °F) SH : liquid \|\| 1470 °C to 1727 °C (2678 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1470 °C (68 °F to 2678 °F) HC : liquid \|\| 1470 °C to 1727 °C (2678 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1461 °C (68 °F to 2662 °F) ST : liquid \|\| 1500 °C to 1750 °C (2732 °F to 3182 °F)
Erbium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) DLL : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) MTE : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) CTE : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) E : solid \|\| -192 °C to 25 °C (-314 °F to 77 °F) G : solid \|\| -192 °C to 25 °C (-314 °F to 77 °F) v : solid \|\| -192 °C to 25 °C (-314 °F to 77 °F) K : solid \|\| -192 °C to 25 °C (-314 °F to 77 °F) TC : solid \|\| annealed \|\| -273 °C to 1227 °C (-460 °F to 2240 °F) TD : solid \|\| annealed \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 1522 °C (68 °F to 2771 °F) SH : liquid \|\| 1522 °C to 1727 °C (2771 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1522 °C (68 °F to 2771 °F) HC : liquid \|\| 1522 °C to 1727 °C (2771 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1497 °C (68 °F to 2726 °F) VP : liquid \|\| 1497 °C to 1627 °C (2726 °F to 2960 °F) ST : liquid \|\| 1530 °C to 1750 °C (2786 °F to 3182 °F) RHO : solid \|\| -263 °C to 77 °C (-442 °F to 170 °F) SIGMA : solid \|\| -263 °C to 77 °C (-442 °F to 170 °F)
Thulium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -273 °C to 27 °C (-460 °F to 80 °F) TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1545 °C (68 °F to 2813 °F) SH : liquid \|\| 1545 °C to 1727 °C (2813 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1545 °C (68 °F to 2813 °F) HC : liquid \|\| 1545 °C to 1727 °C (2813 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1127 °C (68 °F to 2061 °F)
Ytterbium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 732 °C (68 °F to 1349 °F) DLL : solid \|\| 20 °C to 732 °C (68 °F to 1349 °F) MTE : solid \|\| 20 °C to 732 °C (68 °F to 1349 °F) CTE : solid \|\| 20 °C to 732 °C (68 °F to 1349 °F) TC : solid \|\| -150 °C to 227 °C (-238 °F to 440 °F) TD : solid \|\| 20 °C to 227 °C (68 °F to 440 °F) SH : solid \|\| 20 °C to 824 °C (68 °F to 1515 °F) SH : liquid \|\| 824 °C to 1194 °C (1515 °F to 2181 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 824 °C (68 °F to 1515 °F) HC : liquid \|\| 824 °C to 1194 °C (1515 °F to 2181 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 627 °C (68 °F to 1160 °F) Vis : liquid \|\| 824 °C to 1324 °C (1515 °F to 2415 °F) ST : liquid \|\| 824 °C to 1750 °C (1515 °F to 3182 °F)
Lutetium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) TD* : solid \|\| room temperature value SH : solid \|\| -267 °C to 1663 °C (-449 °F to 3025 °F) SH : liquid \|\| 1663 °C to 1727 °C (3025 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -267 °C to 1663 °C (-449 °F to 3025 °F) HC : liquid \|\| 1663 °C to 1727 °C (3025 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : 0.48 at% H, annealed \|\| tested at 22 °C (71 °F), 3.3x10^-⁵/s \|\| 0 to 0.13 mm/mm strain SSC : 0.48 at% H, annealed \|\| tested at -195.1 °C (-319.3 °F), 3.3x10^-⁵/s \|\| 0 to 0.1 mm/mm strain SSC : 7.1 at% H, annealed \|\| tested at 22 °C (71 °F), 3.3x10^-⁵/s \|\| 0 to 0.15 mm/mm strain SSC : 7.1 at% H, annealed \|\| tested at -195.1 °C (-319.3 °F), 3.3x10^-⁵/s \|\| 0 to 0.7 mm/mm strain YS : annealed \|\| 0.48 at% H \|\| -195 °C to 200 °C (-319 °F to 392 °F) YS : annealed \|\| 12.8 at% H \|\| -73 °C to 200 °C (-100 °F to 392 °F) YS : annealed \|\| 18.4 at% H \|\| 20 °C to 200 °C (68 °F to 392 °F) YS : annealed \|\| 7.1 at% H \|\| -195 °C to 200 °C (-319 °F to 392 °F) VP : solid \|\| 20 °C to 1652 °C (68 °F to 3005 °F) VP : liquid \|\| 1652 °C to 2077 °C (3005 °F to 3770 °F) ST : liquid \|\| 1700 °C to 1750 °C (3092 °F to 3182 °F)
Hafnium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1560 °C (68 °F to 2840 °F) D : liquid \|\| 2233 °C to 4727 °C (4051 °F to 8540 °F) DLL : solid \|\| 20 °C to 1560 °C (68 °F to 2840 °F) DLL : liquid \|\| 2233 °C to 4727 °C (4051 °F to 8540 °F) MTE : solid \|\| 20 °C to 1560 °C (68 °F to 2840 °F) MTE : liquid \|\| 2233 °C to 4727 °C (4051 °F to 8540 °F) CTE : solid \|\| 20 °C to 1560 °C (68 °F to 2840 °F) CTE : liquid \|\| 2233 °C to 4727 °C (4051 °F to 8540 °F) TC : solid \|\| annealed \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) TC : liquid \|\| 2233 °C to 3227 °C (4051 °F to 5841 °F) TD : solid \|\| 20 °C to 1560 °C (68 °F to 2840 °F) TD : liquid \|\| 2233 °C to 2727 °C (4051 °F to 4941 °F) SH : solid \|\| -263 °C to 2197 °C (-442 °F to 3986 °F) SH : liquid \|\| 2197 °C to 2727 °C (3986 °F to 4940 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| -263 °C to 2197 °C (-442 °F to 3986 °F) HC : liquid \|\| 2197 °C to 2727 °C (3986 °F to 4940 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) SSC : annealed, 0.001/s, in-plane \|\| tested at 20 °C (68 °F) \|\| 0 to 0.2 mm/mm strain SSCC : annealed, 0.001/s, in-plane \|\| tested at 20 °C (68 °F) \|\| 0 to 0.2 mm/mm strain SSCC : annealed, 0.001/s through-plane \|\| tested at 20 °C (68 °F) \|\| 0 to 0.2 mm/mm strain SSCC : 5200/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.2 mm/mm strain SSCC : 2700/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.3 mm/mm strain SSCC : 1500/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.15 mm/mm strain SSCC : 3.2/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.45 mm/mm strain SSCC : 2.5x10^-⁴/s, bar \|\| tested at 20 °C (68 °F) \|\| 0 to 0.4 mm/mm strain HE : solid \|\| 827 °C to 2027 °C (1520 °F to 3680 °F) VP : solid \|\| alpha \|\| 1127 °C to 1743 °C (2060 °F to 3169 °F) VP : solid \|\| beta \|\| 1743 °C to 2229 °C (3169 °F to 4044 °F) VP : liquid \|\| 2229 °C to 4627 °C (4044 °F to 8360 °F) Vis : liquid \|\| 2227 °C to 2727 °C (4040 °F to 4940 °F) RHO : solid \|\| -272 °C to 1742 °C (-458 °F to 3167 °F) RHO : liquid \|\| 1742 °C to 2227 °C (3167 °F to 4040 °F) SIGMA : solid \|\| -272 °C to 1742 °C (-458 °F to 3167 °F) SIGMA : liquid \|\| 1742 °C to 2227 °C (3167 °F to 4040 °F)
Tantalum (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -183 °C to 2527 °C (-298 °F to 4580 °F) D : liquid \|\| 2487 °C to 6977 °C (4508 °F to 12590 °F) DLL : solid \|\| -183 °C to 2527 °C (-298 °F to 4580 °F) DLL : liquid \|\| 2487 °C to 6977 °C (4508 °F to 12590 °F) MTE : solid \|\| 20 °C to 2527 °C (68 °F to 4580 °F) MTE : liquid \|\| 2487 °C to 6977 °C (4508 °F to 12590 °F) CTE : liquid \|\| 2487 °C to 6977 °C (4508 °F to 12590 °F) E : solid \|\| -273 °C to 2400 °C (-460 °F to 4352 °F) G : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) v : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) K : solid \|\| 20 °C to 2827 °C (68 °F to 5120 °F) TC : solid \|\| annealed \|\| -273 °C to 2927 °C (-460 °F to 5300 °F) TC : liquid \|\| 3020 °C to 7127 °C (5468 °F to 12861 °F) TD : solid \|\| commercial purity \|\| 20 °C to 1300 °C (68 °F to 2372 °F) TD : solid \|\| calculated \|\| -183 °C to 2527 °C (-298 °F to 4580 °F) TD : liquid \|\| 3020 °C to 5727 °C (5468 °F to 10341 °F) SH : solid \|\| -263 °C to 2985 °C (-442 °F to 5405 °F) SH : liquid \|\| 2985 °C to 5727 °C (5405 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -263 °C to 2985 °C (-442 °F to 5405 °F) HC : liquid \|\| 2985 °C to 5727 °C (5405 °F to 10340 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSCC : annealed, 0.001/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 375 °C (707 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 375 °C (707 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 375 °C (707 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 1000/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 325 °C (617 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 375 °C (707 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.25 mm/mm strain SSCC : annealed, 5000/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.25 mm/mm strain UTS : solid \|\| 20 °C to 1600 °C (68 °F to 2912 °F) YSC : annealed \|\| 0.001/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 0.01/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 0.1/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 1/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 10/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 100/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 1000/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) YSC : annealed \|\| 5000/s strain rate \|\| 20 °C to 727 °C (68 °F to 1340 °F) SR : recrystallized sheet \|\| tested at 750 °C (1382 °F) \|\| 0.4 h to 550 h SR : recrystallized sheet \|\| tested at 1000 °C (1832 °F) \|\| 1 h to 105 h SR : recrystallized sheet \|\| tested at 1200 °C (2192 °F) \|\| 1 h to 310 h SR : recrystallized sheet \|\| tested at 1400 °C (2552 °F) \|\| 1 h to 100 h SR : recrystallized sheet \|\| Master curve (LMP) \|\| 750 °C to 1401 °C (1382 °F to 2554 °F) SR : cold worked sheet \|\| tested at 1204 °C (2200 °F) \|\| 10 h to 1,000 h SR : cold worked sheet \|\| tested at 1427 °C (2600 °F) \|\| 5 h to 550 h SR : cold worked sheet \|\| tested at 1649 °C (3000 °F) \|\| 2 h to 1,300 h SR : cold worked sheet \|\| Master curve (LMP) \|\| 1204 °C to 1649 °C (2199 °F to 3000 °F) FSN : wire annealed at 1141 °C (2085 °F) \|\| tested at 24 °C (75 °F), R = -1, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁷ cycles FSN : wire annealed at 1399 °C (2550 °F) \|\| tested at 24 °C (75 °F), R = -1, maximum stress \|\| 1.9x10⁴ cycles to 1x10⁷ cycles FSN : wire annealed at 1399 °C (2550 °F) \|\| tested at -73 °C (-100 °F), R = -1, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles CRS : 0.5% total strain, recrystallized sheet \|\| tested at 750 °C (1382 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, recrystallized sheet \|\| tested at 1000 °C (1832 °F) \|\| 0.1 h to 1 h CRS : 0.5% total strain, recrystallized sheet \|\| tested at 1200 °C (2192 °F) \|\| 0.1 h to 1 h CRS : 0.5% total strain, recrystallized sheet \|\| tested at 1400 °C (2552 °F) \|\| 0.1 h to 1 h CRS : 0.5% total strain, recrystallized sheet \|\| Master curve (LMP) \|\| 750 °C to 1401 °C (1382 °F to 2554 °F) CRS : 1% total strain, recrystallized sheet \|\| tested at 750 °C (1382 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, recrystallized sheet \|\| tested at 1000 °C (1832 °F) \|\| 0.1 h to 10 h CRS : 1% total strain, recrystallized sheet \|\| tested at 1200 °C (2192 °F) \|\| 0.1 h to 10 h CRS : 1% total strain, recrystallized sheet \|\| tested at 1400 °C (2552 °F) \|\| 0.1 h to 1 h CRS : 1% total strain, recrystallized sheet \|\| Master curve (LMP) \|\| 750 °C to 1401 °C (1382 °F to 2554 °F) CRS : 2% total strain, recrystallized sheet \|\| tested at 750 °C (1382 °F) \|\| 0.1 h to 100 h CRS : 2% total strain, recrystallized sheet \|\| tested at 1000 °C (1832 °F) \|\| 0.1 h to 10 h CRS : 2% total strain, recrystallized sheet \|\| tested at 1200 °C (2192 °F) \|\| 0.1 h to 10 h CRS : 2% total strain, recrystallized sheet \|\| tested at 1400 °C (2552 °F) \|\| 0.1 h to 10 h CRS : 2% total strain, recrystallized sheet \|\| Master curve (LMP) \|\| 750 °C to 1401 °C (1382 °F to 2554 °F) CRS : 5% total strain, recrystallized sheet \|\| tested at 750 °C (1382 °F) \|\| 0.1 h to 100 h CRS : 5% total strain, recrystallized sheet \|\| tested at 1000 °C (1832 °F) \|\| 0.1 h to 100 h CRS : 5% total strain, recrystallized sheet \|\| tested at 1200 °C (2192 °F) \|\| 0.1 h to 100 h CRS : 5% total strain, recrystallized sheet \|\| tested at 1400 °C (2552 °F) \|\| 0.1 h to 10 h CRS : 5% total strain, recrystallized sheet \|\| Master curve (LMP) \|\| 750 °C to 1401 °C (1382 °F to 2554 °F) CRS : 1% plastic strain, cold worked sheet \|\| tested at 1204 °C (2200 °F) \|\| 0.3 h to 220 h CRS : 1% plastic strain, cold worked sheet \|\| tested at 1427 °C (2600 °F) \|\| 0.3 h to 2 h CRS : 1% plastic strain, cold worked sheet \|\| tested at 1649 °C (3000 °F) \|\| 0.7 h to 50 h CRS : 1% plastic strain, cold worked sheet \|\| Master curve (LMP) \|\| 1204 °C to 1649 °C (2199 °F to 3000 °F) CRS : 2% plastic strain, cold worked sheet \|\| tested at 1204 °C (2200 °F) \|\| 0.3 h to 480 h CRS : 2% plastic strain, cold worked sheet \|\| tested at 1427 °C (2600 °F) \|\| 1 h to 10 h CRS : 2% plastic strain, cold worked sheet \|\| tested at 1649 °C (3000 °F) \|\| 0.3 h to 10 h CRS : 2% plastic strain, cold worked sheet \|\| Master curve (LMP) \|\| 1204 °C to 1649 °C (2199 °F to 3000 °F) CRS : 5% plastic strain, cold worked sheet \|\| tested at 1204 °C (2200 °F) \|\| 1.4 h to 60 h CRS : 5% plastic strain, cold worked sheet \|\| tested at 1427 °C (2600 °F) \|\| 0.3 h to 60 h CRS : 5% plastic strain, cold worked sheet \|\| tested at 1649 °C (3000 °F) \|\| 1.5 h to 40 h CRS : 5% plastic strain, cold worked sheet \|\| Master curve (LMP) \|\| 1204 °C to 1649 °C (2199 °F to 3000 °F) CRS : 10% plastic strain, cold worked sheet \|\| tested at 1204 °C (2200 °F) \|\| 3 h to 150 h CRS : 10% plastic strain, cold worked sheet \|\| tested at 1427 °C (2600 °F) \|\| 1.5 h to 165 h CRS : 10% plastic strain, cold worked sheet \|\| tested at 1649 °C (3000 °F) \|\| 5 h to 70 h CRS : 10% plastic strain, cold worked sheet \|\| Master curve (LMP) \|\| 1204 °C to 1649 °C (2199 °F to 3000 °F) IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, recrystallized sheet \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1000 °C (1832 °F), plastic strain, recrystallized sheet \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1000 °C (1832 °F), plastic strain, recrystallized sheet \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1000 °C (1832 °F), plastic strain, recrystallized sheet \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1000 °C (1832 °F), plastic strain, recrystallized sheet \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1000 °C (1832 °F), plastic strain, recrystallized sheet \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1200 °C (2192 °F), plastic strain, recrystallized sheet \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1200 °C (2192 °F), plastic strain, recrystallized sheet \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1200 °C (2192 °F), plastic strain, recrystallized sheet \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1200 °C (2192 °F), plastic strain, recrystallized sheet \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1200 °C (2192 °F), plastic strain, recrystallized sheet \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1400 °C (2552 °F), plastic strain, recrystallized sheet \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1400 °C (2552 °F), plastic strain, recrystallized sheet \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1400 °C (2552 °F), plastic strain, recrystallized sheet \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1400 °C (2552 °F), plastic strain, recrystallized sheet \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1400 °C (2552 °F), plastic strain, recrystallized sheet \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 2 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 3 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 5 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 10 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 30 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 100 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 150 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1204 °C (2200 °F), plastic strain, cold worked sheet \|\| 200 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 2 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 3 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 5 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1427 °C (2600 °F), plastic strain, cold worked sheet \|\| 10 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 2 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 5 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 10 h \|\| 0 to 0.1 mm/mm strain IC : tested at 1649 °C (3000 °F), plastic strain, cold worked sheet \|\| 30 h \|\| 0 to 0.1 mm/mm strain HE : solid \|\| polished & aged \|\| 2000 °C to 2727 °C (3632 °F to 4940 °F) NE : solid \|\| polished, Peletskii et. al. & Worthing \|\| 1027 °C to 2527 °C (1880 °F to 4580 °F) NE : solid \|\| polished, Wood \|\| -208 °C to 1297 °C (-343 °F to 2366 °F) NE : solid \|\| oxidized \|\| 97 °C to 854 °C (206 °F to 1570 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F) Vis : liquid \|\| 2870 °C to 3120 °C (5198 °F to 5648 °F) RHO : solid \|\| -269 °C to 2985 °C (-452 °F to 5405 °F) RHO : liquid \|\| 2985 °C to 7127 °C (5405 °F to 12860 °F) SIGMA : solid \|\| -269 °C to 2985 °C (-452 °F to 5405 °F) SIGMA : liquid \|\| 2985 °C to 7127 °C (5405 °F to 12860 °F)
Tungsten (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 3127 °C (-460 °F to 5660 °F) D : liquid \|\| 3422 °C to 5545 °C (6191 °F to 10013 °F) DLL : solid \|\| -273 °C to 3127 °C (-460 °F to 5660 °F) DLL : liquid \|\| 3422 °C to 5545 °C (6191 °F to 10013 °F) MTE : solid \|\| -273 °C to 3127 °C (-460 °F to 5660 °F) MTE : liquid \|\| 3422 °C to 5545 °C (6191 °F to 10013 °F) CTE : liquid \|\| 3422 °C to 5545 °C (6191 °F to 10013 °F) E : solid \|\| -180 °C to 2400 °C (-292 °F to 4352 °F) G : solid \|\| 0 °C to 1800 °C (32 °F to 3272 °F) v : solid \|\| 0 °C to 1800 °C (32 °F to 3272 °F) K : solid \|\| 0 °C to 1800 °C (32 °F to 3272 °F) TC : solid \|\| Ho et. al. \|\| -273 °C to 3387 °C (-460 °F to 6128 °F) TC : solid \|\| Binkele \|\| 0 °C to 3387 °C (32 °F to 6128 °F) TC : liquid \|\| 3422 °C to 5727 °C (6191 °F to 10341 °F) TD : solid \|\| -272 °C to 3127 °C (-458 °F to 5660 °F) TD : liquid \|\| 3422 °C to 5545 °C (6191 °F to 10013 °F) SH : solid \|\| -272 °C to 3327 °C (-458 °F to 6020 °F) SH : liquid \|\| 3407 °C to 5727 °C (6164 °F to 10340 °F) SH : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) HC : solid \|\| -272 °C to 3327 °C (-458 °F to 6020 °F) HC : liquid \|\| 3407 °C to 5727 °C (6164 °F to 10340 °F) HC : gas \|\| 20 °C to 2727 °C (68 °F to 4940 °F) SSC : recrystallized swaged bar \|\| tested at 316 °C (600 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 427 °C (800 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 538 °C (1000 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 649 °C (1200 °F), unknown strain rate \|\| 0 to 0.325 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 760 °C (1400 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 877 °C (1610 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 977 °C (1790 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : recrystallized swaged bar \|\| tested at 1091 °C (1995 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : CVD <011> \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.75 mm/mm strain SSC : CVD <011> \|\| tested at 20 °C (68 °F), 0.005/s \|\| 0 to 0.75 mm/mm strain SSC : CVD <011> \|\| tested at 20 °C (68 °F), 1800/s \|\| 0 to 0.1 mm/mm strain SSC : CVD <011> \|\| tested at 20 °C (68 °F), 4500/s \|\| 0 to 0.1 mm/mm strain SSC : CVD <011> \|\| tested at 20 °C (68 °F), 6600/s \|\| 0 to 0.1 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 3000/s \|\| 0 to 0.2 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 6500/s \|\| 0 to 0.1 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 7000/s \|\| 0 to 0.15 mm/mm strain SSC : CVD <001> \|\| tested at 20 °C (68 °F), 9500/s \|\| 0 to 0.15 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 0.001/s, as-received \|\| 0 to 0.175 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 0.001/s, annealed at 1750 °C (3182 °F) \|\| 0 to 0.225 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 0.001/s, annealed at 2600 °C (4712 °F) \|\| 0 to 0.25 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 1000/s, annealed at 1750 °C (3182 °F) \|\| 0 to 0.5 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 1000/s, annealed at 2600 °C (4712 °F) \|\| 0 to 0.25 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 3000/s, as-received \|\| 0 to 0.175 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 4000/s, annealed at 1750 °C (3182 °F) \|\| 0 to 0.5 mm/mm strain SSC : powder metallurgy \|\| tested at 20 °C (68 °F), 4000/s, annealed at 2600 °C (4712 °F) \|\| 0 to 0.75 mm/mm strain UTS : 2.54 mm (0.1 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) UTS : 2.54 mm (0.1 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 1371 °C to 1649 °C (2500 °F to 3000 °F) UTS : 1.5 mm (0.0591 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) UTS : 1.5 mm (0.0591 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) UTS : K-doped \|\| 0.203 mm (0.008 inch) wire \|\| 1400 °C to 2000 °C (2552 °F to 3632 °F) UTS : PLANSEE material, pure \|\| 0.052 mm (0.00205 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, pure \|\| 0.127 mm (0.005 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, pure \|\| 0.22 mm (0.00866 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, pure \|\| 0.35 mm (0.0138 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, pure \|\| 1 mm (0.0394 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, K-doped \|\| 0.052 mm (0.00205 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, K-doped \|\| 0.127 mm (0.005 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, K-doped \|\| 0.22 mm (0.00866 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, K-doped \|\| 0.35 mm (0.0138 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : PLANSEE material, K-doped \|\| 1 mm (0.0394 inch) sheet \|\| 300 °C to 800 °C (572 °F to 1472 °F) YS : 2.54 mm (0.1 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) YS : 2.54 mm (0.1 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 1371 °C to 1649 °C (2500 °F to 3000 °F) YS : 1.5 mm (0.0591 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) YS : 1.5 mm (0.0591 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 649 °C to 2482 °C (1200 °F to 4499 °F) YS : PLANSEE material, pure \|\| 0.052 mm (0.00205 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, pure \|\| 0.127 mm (0.005 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, pure \|\| 0.22 mm (0.00866 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, pure \|\| 0.35 mm (0.0138 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, pure \|\| 1 mm (0.0394 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, K-doped \|\| 0.052 mm (0.00205 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, K-doped \|\| 0.127 mm (0.005 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, K-doped \|\| 0.22 mm (0.00866 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, K-doped \|\| 0.35 mm (0.0138 inch) sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : PLANSEE material, K-doped \|\| 1 mm (0.0394 inch) sheet \|\| 300 °C to 800 °C (572 °F to 1472 °F) %El : 2.54 mm (0.1 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) %El : 2.54 mm (0.1 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 1371 °C to 1649 °C (2500 °F to 3000 °F) %El : 1.5 mm (0.0591 inch) sheet \|\| strain relieved at 1149 °C (2100 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) %El : 1.5 mm (0.0591 inch) sheet \|\| recrystallized at 1399 °C (2550 °F) \|\| 20 °C to 2482 °C (68 °F to 4499 °F) SR : rod \|\| tested at 2250 °C (4082 °F) \|\| 0.1 h to 2.3 h SR : rod \|\| tested at 2500 °C (4532 °F) \|\| 0.1 h to 6.7 h SR : rod \|\| tested at 2700 °C (4892 °F) \|\| 0.1 h to 3.4 h SR : rod \|\| tested at 2800 °C (5072 °F) \|\| 0.1 h to 3.4 h SR : rod \|\| Master curve (LMP) \|\| 2250 °C to 2801 °C (4082 °F to 5074 °F) HE : solid \|\| 0 °C to 3227 °C (32 °F to 5840 °F) NE : solid \|\| 1357 °C to 2657 °C (2474 °F to 4814 °F) NE : liquid \|\| 3407 °C to 10642 °C (6164 °F to 19187 °F) VP : solid \|\| 20 °C to 2777 °C (68 °F to 5030 °F) VP : liquid \|\| 3547 °C to 5927 °C (6416 °F to 10700 °F) Vis : liquid \|\| 3125 °C to 3420 °C (5657 °F to 6188 °F) RHO : solid \|\| pure \|\| -273 °C to 3387 °C (-460 °F to 6128 °F) RHO : solid \|\| K-doped \|\| 0 °C to 3127 °C (32 °F to 5660 °F) RHO : liquid \|\| 3387 °C to 4727 °C (6128 °F to 8540 °F) SIGMA : solid \|\| pure \|\| -273 °C to 3387 °C (-460 °F to 6128 °F) SIGMA : solid \|\| K-doped \|\| 0 °C to 3127 °C (32 °F to 5660 °F) SIGMA : liquid \|\| 3387 °C to 4727 °C (6128 °F to 8540 °F) S : solid \|\| 0 °C to 2127 °C (32 °F to 3860 °F)
Rhenium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 0 °C to 2500 °C (32 °F to 4532 °F) D : liquid \|\| 2427 °C to 11527 °C (4400 °F to 20780 °F) DLL : solid \|\| 0 °C to 2500 °C (32 °F to 4532 °F) DLL : liquid \|\| 2427 °C to 11527 °C (4400 °F to 20780 °F) MTE : solid \|\| 0 °C to 2500 °C (32 °F to 4532 °F) MTE : liquid \|\| 2427 °C to 11527 °C (4400 °F to 20780 °F) CTE : solid \|\| 0 °C to 2500 °C (32 °F to 4532 °F) CTE : liquid \|\| 2427 °C to 11527 °C (4400 °F to 20780 °F) E : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) G : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) v : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) K : solid \|\| -269 °C to 650 °C (-452 °F to 1202 °F) TC : solid \|\| annealed \|\| -273 °C to 2327 °C (-460 °F to 4220 °F) TC : liquid \|\| 3180 °C to 3727 °C (5756 °F to 6740 °F) TD : solid \|\| annealed \|\| 20 °C to 1727 °C (68 °F to 3141 °F) SH : solid \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : liquid \|\| 3180 °C to 4227 °C (5756 °F to 7640 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : liquid \|\| 3180 °C to 4227 °C (5756 °F to 7640 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : swaged rods from powders, annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 1 mm/mm strain SSC : plate from powders, as-received rolled condition \|\| tested at 20 °C (68 °F), 5x10^-⁵/s \|\| 0 to 0.1 mm/mm strain SSC : plate from powders, as-received rolled condition \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.138 mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 2400 °C (68 °F to 4352 °F) UTS : solid \|\| 9% worked \|\| 20 °C to 1942 °C (68 °F to 3527 °F) UTS : solid \|\| 15% worked \|\| 20 °C to 2400 °C (68 °F to 4352 °F) %El : solid \|\| annealed \|\| 20 °C to 2400 °C (68 °F to 4352 °F) %El : solid \|\| 9% worked \|\| 20 °C to 2000 °C (68 °F to 3632 °F) %El : solid \|\| 15% worked \|\| -273 °C to 2400 °C (-460 °F to 4352 °F) SR : electron beam refined sheet \|\| tested at 1093 °C (2000 °F) \|\| 20 h to 800 h SR : electron beam refined sheet \|\| tested at 1649 °C (3000 °F) \|\| 4 h to 15 h SR : electron beam refined sheet \|\| tested at 2204 °C (4000 °F) \|\| 0.4 h to 18 h SR : electron beam refined sheet \|\| Master curve (LMP) \|\| 1204 °C to 2205 °C (2199 °F to 4001 °F) SR : commercial powder metallurgical sheet \|\| tested at 1093 °C (2000 °F) \|\| 30 h to 150 h SR : commercial powder metallurgical sheet \|\| tested at 1649 °C (3000 °F) \|\| 0.7 h to 340 h SR : commercial powder metallurgical sheet \|\| tested at 2204 °C (4000 °F) \|\| 0.4 h to 18 h SR : commercial powder metallurgical sheet \|\| Master curve (LMP) \|\| 1204 °C to 2205 °C (2199 °F to 4001 °F) FSN : plate from powders, as-received rolled condition \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 4x10⁴ cycles to 3.3x10⁶ cycles HE : solid \|\| 927 °C to 2727 °C (1700 °F to 4940 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : liquid \|\| 3097 °C to 5627 °C (5606 °F to 10160 °F) RHO : solid \|\| annealed \|\| -73 °C to 2327 °C (-100 °F to 4220 °F) RHO : liquid \|\| 3185 °C to 4227 °C (5765 °F to 7640 °F) SIGMA : solid \|\| annealed \|\| -73 °C to 2327 °C (-100 °F to 4220 °F) SIGMA : liquid \|\| 3185 °C to 4227 °C (5765 °F to 7640 °F)
Osmium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) DLL : solid \|\| polycrystal \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) DLL : solid \|\| a-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) DLL : solid \|\| c-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) MTE : solid \|\| polycrystal \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) MTE : solid \|\| a-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) MTE : solid \|\| c-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) CTE : solid \|\| polycrystal \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) CTE : solid \|\| a-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) CTE : solid \|\| c-axis \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) TC : solid \|\| annealed \|\| -273 °C to 1400 °C (-460 °F to 2552 °F) TD : solid \|\| annealed \|\| 20 °C to 1027 °C (68 °F to 1880 °F) SH : solid \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F)
Iridium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 2446 °C (-460 °F to 4435 °F) D : liquid \|\| 2446 °C to 3727 °C (4435 °F to 6740 °F) DLL : solid \|\| -273 °C to 2446 °C (-460 °F to 4435 °F) DLL : liquid \|\| 2446 °C to 3727 °C (4435 °F to 6740 °F) MTE : solid \|\| -273 °C to 2446 °C (-460 °F to 4435 °F) MTE : liquid \|\| 2446 °C to 3727 °C (4435 °F to 6740 °F) CTE : liquid \|\| 2446 °C to 3727 °C (4435 °F to 6740 °F) E : solid \|\| -180 °C to 1000 °C (-292 °F to 1832 °F) TC : solid \|\| annealed \|\| -273 °C to 2446 °C (-460 °F to 4435 °F) TC : liquid \|\| 2446 °C to 3227 °C (4435 °F to 5840 °F) TD : solid \|\| annealed \|\| -272 °C to 1727 °C (-458 °F to 3140 °F) TD : liquid \|\| 2446 °C to 3227 °C (4435 °F to 5840 °F) SH : solid \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) SH : liquid \|\| 2446 °C to 3227 °C (4435 °F to 5840 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) HC : liquid \|\| 2446 °C to 3227 °C (4435 °F to 5840 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SR : wires & sheets \|\| tested at 1650 °C (3002 °F) \|\| 1 h to 800 h SR : wires & sheets \|\| tested at 1800 °C (3272 °F) \|\| 1 h to 9,000 h SR : wires & sheets \|\| tested at 2000 °C (3632 °F) \|\| 0.1 h to 1,100 h SR : wires & sheets \|\| tested at 2200 °C (3992 °F) \|\| 0.4 h to 100 h SR : wires & sheets \|\| tested at 2300 °C (4172 °F) \|\| 0.2 h to 100 h SR : wires & sheets \|\| Master curve (LMP) \|\| 1649 °C to 2201 °C (3000 °F to 3994 °F) HE : solid \|\| 727 °C to 2227 °C (1340 °F to 4040 °F) VP : solid \|\| 20 °C to 2227 °C (68 °F to 4040 °F) ST : liquid \|\| 2450 °C to 2600 °C (4442 °F to 4712 °F) RHO : solid \|\| 20 °C to 2446 °C (68 °F to 4435 °F) RHO : liquid \|\| 2446 °C to 3277 °C (4435 °F to 5930 °F) SIGMA : solid \|\| 20 °C to 2446 °C (68 °F to 4435 °F) SIGMA : liquid \|\| 2446 °C to 3277 °C (4435 °F to 5930 °F)
Platinum (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1700 °C (-460 °F to 3092 °F) D : liquid \|\| 1769 °C to 4827 °C (3216 °F to 8720 °F) DLL : solid \|\| -273 °C to 1700 °C (-460 °F to 3092 °F) DLL : liquid \|\| 1769 °C to 4827 °C (3216 °F to 8720 °F) MTE : solid \|\| -273 °C to 1700 °C (-460 °F to 3092 °F) MTE : liquid \|\| 1769 °C to 4827 °C (3216 °F to 8720 °F) CTE : solid \|\| -46 °C to 1700 °C (-51 °F to 3092 °F) CTE : liquid \|\| 1769 °C to 3027 °C (3216 °F to 5480 °F) E : solid \|\| -180 °C to 1204 °C (-292 °F to 2200 °F) G : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) v : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) K : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) TC : solid \|\| annealed \|\| -273 °C to 1772 °C (-460 °F to 3221 °F) TD : solid \|\| annealed \|\| -272 °C to 1700 °C (-458 °F to 3092 °F) SH : solid \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) SH : liquid \|\| 1769 °C to 1927 °C (3216 °F to 3500 °F) SH : gas \|\| 20 °C to 1927 °C (68 °F to 3500 °F) HC : solid \|\| -273 °C to 1727 °C (-460 °F to 3140 °F) HC : liquid \|\| 1769 °C to 1927 °C (3216 °F to 3500 °F) HC : gas \|\| 20 °C to 1927 °C (68 °F to 3500 °F) UTS : wires and sheets \|\| annealed at 1100 °C (2012 °F) for 5 minutes \|\| 20 °C to 1400 °C (68 °F to 2552 °F) %El : wires and sheets \|\| annealed at 1100 °C (2012 °F) for 5 minutes \|\| 20 °C to 1400 °C (68 °F to 2552 °F) SR : condition unknown \|\| tested at 900 °C (1652 °F) \|\| 20 h to 1,000 h SR : condition unknown \|\| tested at 1600 °C (2912 °F) \|\| 0.1 h to 1,000 h SR : condition unknown \|\| Master curve (LMP) \|\| 900 °C to 1601 °C (1652 °F to 2914 °F) FSN : DC magnetron sputtered 5 micron film \|\| tested at 20 °C (68 °F), R = 0.3, axial, stress amplitude \|\| 2x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| 727 °C to 1727 °C (1340 °F to 3140 °F) VP : solid \|\| 20 °C to 1768 °C (68 °F to 3214 °F) VP : liquid \|\| 1768 °C to 2227 °C (3214 °F to 4040 °F) Vis : liquid \|\| 1660 °C to 1890 °C (3020 °F to 3434 °F) ST : liquid \|\| 1467 °C to 2040 °C (2672 °F to 3704 °F) RHO : solid \|\| -259 °C to 1727 °C (-434 °F to 3140 °F) RHO : liquid \|\| 1769 °C to 4827 °C (3216 °F to 8720 °F) SIGMA : solid \|\| -259 °C to 1727 °C (-434 °F to 3140 °F) SIGMA : liquid \|\| 1769 °C to 4827 °C (3216 °F to 8720 °F) S : solid \|\| -173 °C to 1727 °C (-280 °F to 3140 °F)
Gold (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 730 °C (-460 °F to 1346 °F) D : liquid \|\| 1085 °C to 1507 °C (1985 °F to 2744 °F) DLL : solid \|\| -273 °C to 730 °C (-460 °F to 1346 °F) DLL : liquid \|\| 1085 °C to 1507 °C (1985 °F to 2744 °F) MTE : solid \|\| -273 °C to 730 °C (-460 °F to 1346 °F) MTE : liquid \|\| 1085 °C to 1507 °C (1985 °F to 2744 °F) CTE : solid \|\| -187 °C to 730 °C (-305 °F to 1346 °F) CTE : liquid \|\| 1085 °C to 1507 °C (1985 °F to 2744 °F) E : solid \|\| -273 °C to 1007 °C (-460 °F to 1844 °F) G : solid \|\| 20 °C to 1007 °C (68 °F to 1844 °F) v : solid \|\| 20 °C to 1007 °C (68 °F to 1844 °F) K : solid \|\| 20 °C to 1007 °C (68 °F to 1844 °F) TC : solid \|\| annealed \|\| -273 °C to 1065 °C (-460 °F to 1949 °F) TC : liquid \|\| 1065 °C to 9000 °C (1949 °F to 16232 °F) TD : solid \|\| annealed \|\| 20 °C to 730 °C (68 °F to 1346 °F) SH : solid \|\| -272 °C to 1065 °C (-458 °F to 1949 °F) SH : liquid \|\| 1065 °C to 1727 °C (1949 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -272 °C to 1065 °C (-458 °F to 1949 °F) HC : liquid \|\| 1065 °C to 1727 °C (1949 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1064 °C (68 °F to 1947 °F) VP : liquid \|\| 1064 °C to 1777 °C (1947 °F to 3230 °F) Vis : liquid \|\| 1063 °C to 1563 °C (1945 °F to 2845 °F) ST : liquid \|\| 1065 °C to 1565 °C (1949 °F to 2849 °F) RHO : solid \|\| -272 °C to 1065 °C (-458 °F to 1949 °F) RHO : liquid \|\| 1065 °C to 1467 °C (1949 °F to 2672 °F) SIGMA : solid \|\| -272 °C to 1065 °C (-458 °F to 1949 °F) SIGMA : liquid \|\| 1065 °C to 1467 °C (1949 °F to 2672 °F) S : solid \|\| -173 °C to 1027 °C (-280 °F to 1880 °F)
Mercury (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to -39 °C (-460 °F to -38 °F) D : liquid \|\| -20 °C to 300 °C (-4 °F to 572 °F) DLL : solid \|\| -273 °C to -39 °C (-460 °F to -38 °F) DLL : liquid \|\| -20 °C to 300 °C (-4 °F to 572 °F) MTE : solid \|\| -273 °C to -39 °C (-460 °F to -38 °F) MTE : liquid \|\| -20 °C to 300 °C (-4 °F to 572 °F) CTE : solid \|\| -273 °C to -39 °C (-460 °F to -38 °F) CTE : liquid \|\| -20 °C to 300 °C (-4 °F to 572 °F) TC : solid \|\| -273 °C to -39 °C (-460 °F to -38 °F) TC : liquid \|\| -39 °C to 1427 °C (-38 °F to 2600 °F) TC : gas \|\| Hg \|\| 20 °C to 4727 °C (68 °F to 8540 °F) TD : solid \|\| -268 °C to -39 °C (-451 °F to -38 °F) TD : liquid \|\| -20 °C to 300 °C (-4 °F to 572 °F) SH : solid \|\| -268 °C to -39 °C (-451 °F to -38 °F) SH : liquid \|\| -38 °C to 500 °C (-37 °F to 932 °F) SH : gas \|\| 20 °C to 357 °C (68 °F to 674 °F) SH : vapor \|\| -38 °C to 500 °C (-37 °F to 932 °F) HC : solid \|\| -268 °C to -39 °C (-451 °F to -38 °F) HC : liquid \|\| -38 °C to 500 °C (-37 °F to 932 °F) HC : gas \|\| 20 °C to 357 °C (68 °F to 674 °F) HC : vapor \|\| -38 °C to 500 °C (-37 °F to 932 °F) VP : liquid \|\| -38 °C to 500 °C (-37 °F to 932 °F) Vis : liquid \|\| -38 °C to 327 °C (-37 °F to 620 °F) Vis : gas \|\| Hg \|\| 20 °C to 4727 °C (68 °F to 8540 °F) ST : liquid \|\| -23 °C to 277 °C (-10 °F to 530 °F) RHO : liquid \|\| -38 °C to 350 °C (-37 °F to 662 °F) SIGMA : liquid \|\| -38 °C to 350 °C (-37 °F to 662 °F)
Thallium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 304 °C to 927 °C (579 °F to 1700 °F) DLL : liquid \|\| 304 °C to 927 °C (579 °F to 1700 °F) MTE : liquid \|\| 304 °C to 927 °C (579 °F to 1700 °F) CTE : liquid \|\| 304 °C to 927 °C (579 °F to 1700 °F) E : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) G : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) v : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) K : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) TC : solid \|\| annealed \|\| -273 °C to 227 °C (-460 °F to 440 °F) TD : solid \|\| annealed \|\| 20 °C to 227 °C (68 °F to 440 °F) SH : solid \|\| 20 °C to 304 °C (68 °F to 579 °F) SH : liquid \|\| 304 °C to 1473 °C (579 °F to 2683 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 304 °C (68 °F to 579 °F) HC : liquid \|\| 304 °C to 1473 °C (579 °F to 2683 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 304 °C (68 °F to 579 °F) VP : liquid \|\| 304 °C to 827 °C (579 °F to 1520 °F) Vis : liquid \|\| 304 °C to 527 °C (579 °F to 980 °F) ST : liquid \|\| 305 °C to 1200 °C (581 °F to 2192 °F) RHO : solid \|\| annealed \|\| 20 °C to 727 °C (68 °F to 1340 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 727 °C (68 °F to 1340 °F)
Lead (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 320 °C (-460 °F to 608 °F) D : liquid \|\| 328 °C to 1127 °C (622 °F to 2060 °F) DLL : solid \|\| -273 °C to 320 °C (-460 °F to 608 °F) DLL : liquid \|\| 328 °C to 1127 °C (622 °F to 2060 °F) MTE : solid \|\| -273 °C to 320 °C (-460 °F to 608 °F) MTE : liquid \|\| 328 °C to 1127 °C (622 °F to 2060 °F) CTE : liquid \|\| 328 °C to 1127 °C (622 °F to 2060 °F) E : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) G : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) v : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) K : solid \|\| -130 °C to 150 °C (-202 °F to 302 °F) K : liquid \|\| 328 °C to 1727 °C (622 °F to 3140 °F) TC : solid \|\| annealed \|\| -273 °C to 327 °C (-460 °F to 620 °F) TC : liquid \|\| 327 °C to 727 °C (620 °F to 1340 °F) TD : solid \|\| annealed \|\| -263 °C to 320 °C (-442 °F to 608 °F) TD : liquid \|\| 328 °C to 727 °C (622 °F to 1340 °F) SH : solid \|\| -263 °C to 328 °C (-442 °F to 622 °F) SH : liquid \|\| 328 °C to 3327 °C (622 °F to 6020 °F) SH : gas \|\| Pb \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SH : gas \|\| Pb₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| -263 °C to 328 °C (-442 °F to 622 °F) HC : liquid \|\| 328 °C to 3327 °C (622 °F to 6020 °F) HC : gas \|\| Pb \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : gas \|\| Pb₂ \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.37 mm/mm strain UTS : as-cast \|\| -253 °C to 27 °C (-424 °F to 80 °F) %El : as-cast \|\| -269 °C to 27 °C (-452 °F to 80 °F) VP : solid \|\| 20 °C to 328 °C (68 °F to 622 °F) VP : liquid \|\| 328 °C to 927 °C (622 °F to 1700 °F) Vis : liquid \|\| 328 °C to 560 °C (622 °F to 1040 °F) ST : liquid \|\| 328 °C to 828 °C (622 °F to 1522 °F) RHO : solid \|\| -266 °C to 277 °C (-447 °F to 530 °F) RHO : liquid \|\| 332 °C to 602 °C (629 °F to 1115 °F) SIGMA : solid \|\| -266 °C to 277 °C (-447 °F to 530 °F) SIGMA : liquid \|\| 332 °C to 602 °C (629 °F to 1115 °F) AV : liquid \|\| tested at 357 °C (675 °F) \|\| 0/s to 2.6x10³/s S : solid \|\| -266 °C to 277 °C (-447 °F to 530 °F)
Bismuth (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 27 °C (-460 °F to 80 °F) D : liquid \|\| 272 °C to 827 °C (521 °F to 1520 °F) DLL : solid \|\| polycrystal \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : solid \|\| a-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) DLL : solid \|\| c-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) DLL : liquid \|\| 272 °C to 827 °C (521 °F to 1520 °F) MTE : solid \|\| polycrystal \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : solid \|\| a-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) MTE : solid \|\| c-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) MTE : liquid \|\| 272 °C to 827 °C (521 °F to 1520 °F) CTE : solid \|\| polycrystal \|\| -215 °C to 27 °C (-355 °F to 80 °F) CTE : solid \|\| a-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) CTE : solid \|\| c-axis \|\| -215 °C to 27 °C (-355 °F to 80 °F) CTE : liquid \|\| 272 °C to 827 °C (521 °F to 1520 °F) E : solid \|\| -269 °C to 271 °C (-452 °F to 520 °F) G : solid \|\| -269 °C to 271 °C (-452 °F to 520 °F) v : solid \|\| -269 °C to 271 °C (-452 °F to 520 °F) K : solid \|\| -269 °C to 271 °C (-452 °F to 520 °F) K : liquid \|\| 272 °C to 1550 °C (521 °F to 2822 °F) TC : solid \|\| polycrystal, annealed \|\| -253 °C to 271 °C (-424 °F to 520 °F) TC : solid \|\| perpendicular to the trigonal axis \|\| -173 °C to 27 °C (-280 °F to 81 °F) TC : solid \|\| parallel to the trigonal axis \|\| -173 °C to 27 °C (-280 °F to 81 °F) TC : liquid \|\| 271 °C to 1027 °C (520 °F to 1880 °F) TD : solid \|\| polycrystal, annealed \|\| -263 °C to 271 °C (-442 °F to 520 °F) TD : solid \|\| perpendicular to the trigonal axis \|\| -173 °C to 27 °C (-280 °F to 80 °F) TD : solid \|\| parallel to the trigonal axis \|\| -173 °C to 27 °C (-280 °F to 80 °F) TD : liquid \|\| 272 °C to 547 °C (521 °F to 1016 °F) SH : solid \|\| -263 °C to 271 °C (-442 °F to 520 °F) SH : liquid \|\| 272 °C to 547 °C (521 °F to 1016 °F) SH : gas \|\| Bi \|\| 20 °C to 1527 °C (68 °F to 2780 °F) SH : gas \|\| Bi₂ \|\| 20 °C to 1527 °C (68 °F to 2780 °F) HC : solid \|\| -263 °C to 271 °C (-442 °F to 520 °F) HC : liquid \|\| 272 °C to 547 °C (521 °F to 1016 °F) HC : gas \|\| Bi \|\| 20 °C to 1527 °C (68 °F to 2780 °F) HC : gas \|\| Bi₂ \|\| 20 °C to 1527 °C (68 °F to 2780 °F) VP : solid \|\| 237 °C to 272 °C (458 °F to 521 °F) VP : liquid \|\| 272 °C to 1627 °C (521 °F to 2960 °F) Vis : liquid \|\| 271 °C to 771 °C (520 °F to 1420 °F) ST : liquid \|\| 410 °C to 560 °C (770 °F to 1040 °F) RHO : solid \|\| polycrystal, annealed \|\| 20 °C to 247 °C (68 °F to 476 °F) RHO : solid \|\| perpendicular to the trigonal axis \|\| -193 °C to 27 °C (-316 °F to 81 °F) RHO : solid \|\| parallel to the trigonal axis \|\| -198 °C to 27 °C (-325 °F to 81 °F) RHO : liquid \|\| 272 °C to 727 °C (521 °F to 1340 °F) SIGMA : solid \|\| polycrystal, annealed \|\| 20 °C to 247 °C (68 °F to 476 °F) SIGMA : solid \|\| perpendicular to the trigonal axis \|\| -193 °C to 27 °C (-316 °F to 81 °F) SIGMA : solid \|\| parallel to the trigonal axis \|\| -198 °C to 27 °C (-325 °F to 81 °F) SIGMA : liquid \|\| 272 °C to 727 °C (521 °F to 1340 °F) S : single crystal \|\| perpendicular to the trigonal axis \|\| -193 °C to 27 °C (-316 °F to 81 °F) S : single crystal \|\| parallel to the trigonal axis \|\| -253 °C to 27 °C (-424 °F to 81 °F) S : polycrystal \|\| -325 to +400 mesh powder, annealed \|\| -173 °C to 30 °C (-280 °F to 86 °F) S : polycrystal \|\| -50 to +100 mesh powder, annealed \|\| -173 °C to 30 °C (-280 °F to 86 °F)
Polonium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value VP : solid \|\| 113 °C to 254 °C (235 °F to 489 °F) VP : liquid \|\| 254 °C to 969 °C (489 °F to 1776 °F)
Astatine (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value VP : solid \|\| -52 °C to 347 °C (-62 °F to 656 °F)
Radon (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : gas \|\| -62 °C to 2727 °C (-80 °F to 4940 °F) TC : liquid \|\| -71 °C to 104 °C (-96 °F to 219 °F) TC : gas \|\| -62 °C to 727 °C (-80 °F to 1340 °F) TC : vapor \|\| -62 °C to 104 °C (-80 °F to 219 °F) VP : liquid \|\| -143 °C to -48 °C (-226 °F to -55 °F)
Francium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : liquid \|\| 8 °C to 18 °C (46 °F to 64 °F) TC : liquid \|\| 8 °C to 18 °C (46 °F to 64 °F) TD* : liquid \|\| room temperature value SH* : solid \|\| room temperature value SH* : liquid \|\| room temperature value SH* : gas \|\| room temperature value HC* : solid \|\| room temperature value HC* : liquid \|\| room temperature value HC* : gas \|\| room temperature value VP : solid \|\| -75 °C to 8 °C (-103 °F to 46 °F) VP : liquid \|\| 8 °C to 617 °C (46 °F to 1142 °F) ST : liquid \|\| 20 °C to 500 °C (68 °F to 932 °F) RHO : solid \|\| -173 °C to 8 °C (-280 °F to 46 °F) RHO : liquid \|\| 8 °C to 1227 °C (46 °F to 2240 °F) SIGMA : solid \|\| -173 °C to 8 °C (-280 °F to 46 °F) SIGMA : liquid \|\| 8 °C to 1227 °C (46 °F to 2240 °F)
Radium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value VP : solid \|\| 163 °C to 1567 °C (325 °F to 2852 °F) RHO : solid \|\| -73 °C to 227 °C (-100 °F to 441 °F) SIGMA : solid \|\| -73 °C to 227 °C (-100 °F to 441 °F)
Actinium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1197 °C (68 °F to 2187 °F) HC : solid \|\| 20 °C to 1197 °C (68 °F to 2187 °F) VP : solid \|\| 772 °C to 3237 °C (1421 °F to 5858 °F)
Thorium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 127 °C (-460 °F to 260 °F) DLL : solid \|\| -273 °C to 127 °C (-460 °F to 260 °F) MTE : solid \|\| -273 °C to 127 °C (-460 °F to 260 °F) E : solid \|\| -180 °C to 500 °C (-292 °F to 932 °F) TC : solid \|\| annealed \|\| -273 °C to 1027 °C (-460 °F to 1880 °F) TD : solid \|\| -173 °C to 127 °C (-280 °F to 260 °F) SH : solid \|\| -173 °C to 1750 °C (-280 °F to 3182 °F) SH : liquid \|\| 1750 °C to 5727 °C (3182 °F to 10340 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| -173 °C to 1750 °C (-280 °F to 3182 °F) HC : liquid \|\| 1750 °C to 5727 °C (3182 °F to 10340 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : solid \|\| 20 °C to 1842 °C (68 °F to 3347 °F) VP : liquid \|\| 1842 °C to 2227 °C (3347 °F to 4040 °F) RHO : solid \|\| 0 °C to 1027 °C (32 °F to 1880 °F) SIGMA : solid \|\| 0 °C to 1027 °C (32 °F to 1880 °F)
Protactinium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1572 °C (68 °F to 2861 °F) SH : liquid \|\| 1572 °C to 2227 °C (2861 °F to 4040 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| 20 °C to 1572 °C (68 °F to 2861 °F) HC : liquid \|\| 1572 °C to 2227 °C (2861 °F to 4040 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : solid \|\| 20 °C to 1568 °C (68 °F to 2854 °F) VP : liquid \|\| 1568 °C to 2227 °C (2854 °F to 4040 °F) RHO : solid \|\| -248 °C to 22 °C (-415 °F to 71 °F) SIGMA : solid \|\| -248 °C to 22 °C (-415 °F to 71 °F)
Uranium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -273 °C to 927 °C (-460 °F to 1700 °F)
Neptunium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value SH : solid \|\| 20 °C to 639 °C (68 °F to 1182 °F) SH : liquid \|\| 639 °C to 2227 °C (1182 °F to 4040 °F) SH : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) HC : solid \|\| 20 °C to 639 °C (68 °F to 1182 °F) HC : liquid \|\| 639 °C to 2227 °C (1182 °F to 4040 °F) HC : gas \|\| 20 °C to 2227 °C (68 °F to 4040 °F) VP : solid \|\| 20 °C to 637 °C (68 °F to 1178 °F) VP : liquid \|\| 637 °C to 2227 °C (1178 °F to 4040 °F) RHO : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F) SIGMA : solid \|\| -253 °C to 27 °C (-424 °F to 80 °F)
Plutonium (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -193 °C to 77 °C (-316 °F to 170 °F)
Americium	D : solid \|\| 20 °C to 605 °C (68 °F to 1121 °F) DLL : solid \|\| polycrystal \|\| 20 °C to 605 °C (68 °F to 1121 °F) DLL : solid \|\| a-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) DLL : solid \|\| c-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) MTE : solid \|\| polycrystal \|\| 20 °C to 605 °C (68 °F to 1121 °F) MTE : solid \|\| a-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) MTE : solid \|\| c-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) CTE : solid \|\| polycrystal \|\| 20 °C to 605 °C (68 °F to 1121 °F) CTE : solid \|\| a-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) CTE : solid \|\| c-axis \|\| 20 °C to 605 °C (68 °F to 1121 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1176 °C (68 °F to 2149 °F) SH : liquid \|\| 1176 °C to 1727 °C (2149 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1176 °C (68 °F to 2149 °F) HC : liquid \|\| 1176 °C to 1727 °C (2149 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1176 °C (68 °F to 2149 °F) VP : liquid \|\| 830 °C to 1180 °C (1526 °F to 2156 °F)
Curium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1345 °C (68 °F to 2453 °F) SH : liquid \|\| 1345 °C to 1727 °C (2453 °F to 3140 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HC : solid \|\| 20 °C to 1345 °C (68 °F to 2453 °F) HC : liquid \|\| 1345 °C to 1727 °C (2453 °F to 3140 °F) HC : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) VP : solid \|\| 20 °C to 1340 °C (68 °F to 2444 °F) VP : liquid \|\| 1340 °C to 1927 °C (2444 °F to 3500 °F)
Berkelium	D* : solid \|\| alpha \|\| room temperature value D* : solid \|\| beta \|\| room temperature value TC* : solid \|\| room temperature value
Californium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Einsteinium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Fermium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Mendelevium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Nobelium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Lawrencium	D* : solid \|\| room temperature value TC* : solid \|\| room temperature value
Iron alloys	Property : Condition // Data range
ARMCO iron (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -196 °C to 982 °C (-321 °F to 1800 °F) TD : solid \|\| -196 °C to 687 °C (-321 °F to 1268 °F) SH : solid \|\| -272 °C to 1536 °C (-458 °F to 2797 °F) SH : liquid \|\| 1536 °C to 2859 °C (2797 °F to 5178 °F) SSCC : 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain YS : solid \|\| 2.5x10^-⁴/s strain rate \|\| -196 °C to 700 °C (-321 °F to 1292 °F) HE : solid \|\| polished \|\| -73 °C to 820 °C (-100 °F to 1508 °F) HE : solid \|\| polished & sand blasted \|\| 195 °C to 820 °C (383 °F to 1508 °F) RHO : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) SIGMA : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) RPB : strip \|\| tested at 20 °C (68 °F) RPB : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) RPB : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) AP : strip \|\| tested at 20 °C (68 °F) AP : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) AP : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) BH : strip \|\| tested at 20 °C (68 °F) BH : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) BH : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) HB : strip \|\| tested at 20 °C (68 °F) HB : rounds & rectangles greater than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F) HB : bars less than 25.4 mm (1 inch) \|\| tested at 20 °C (68 °F)
1006 (UNS G10060) (ASTM A29/A510/A545) (AISI 1006) (SAE J403/J412/J414) (GB & GB/T 05/05F/06TIL/08AI/ML04AI) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -196 °C to 982 °C (-321 °F to 1800 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
1008 (UNS G10080) (WNr 1.0204) (ISO/EN/DIN 2A/C10/C5) (JIS SWRCH8A) (ASTM A108/A510/A519/A545/A549/A575/A576) (AISI 1008) (SAE J403/J412/J414) (GB & GB/T 08/08AI/08F/B1/B1F/BY1/BY1F/Q195-F/Q195-Z/Q195-b) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : rimmed, 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSC : rimmed, 100/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSC : Al killed, 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSC : Al killed, 100/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSCC : plane strain \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain FSN : hot-rolled, as-received \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2.2x10⁴ cycles to 1x10⁸ cycles FSN : decarburized \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1.6x10⁴ cycles to 1x10⁷ cycles FSN : decarburized \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 8.5x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
1010 (UNS G10100) (WNr 1.1121) (ISO/EN/DIN C10/CK10) (JIS S10C) (ASTM A510/A519/A545/A549/A575/A576) (AISI 1010) (SAE J403/J412/J414) (AMS 5040/5042/5044/5050/5053) (GB & GB/T 08MnREL/08TIL/09OIVL/10/10A/10F/10TIL/ER49-1/ER50-4/ML10/ML10AI) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -151 °C to 927 °C (-240 °F to 1700 °F) TD : solid \|\| -157 °C to 849 °C (-251 °F to 1560 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : annealed \|\| tested at 21 °C (70 °F), static test, unknown strain rate \|\| 0 to 0.21 mm/mm strain SSC : annealed \|\| tested at 221 °C (430 °F), static test, unknown strain rate \|\| 0 to 0.83 mm/mm strain SSC : annealed \|\| tested at 371 °C (700 °F), static test, unknown strain rate \|\| 0 to 0.67 mm/mm strain SSC : annealed \|\| tested at 566 °C (1050 °F), static test, unknown strain rate \|\| 0 to 0.33 mm/mm strain SSC : annealed \|\| tested at 760 °C (1400 °F), static test, unknown strain rate \|\| 0 to 0.19 mm/mm strain UTS : annealed and as-received conditions \|\| -196 °C to 761 °C (-321 °F to 1402 °F) YS : annealed and as-received conditions \|\| -196 °C to 761 °C (-321 °F to 1402 °F) %El : annealed and as-received conditions \|\| -196 °C to 27 °C (-321 °F to 80 °F) FSN : axial fatigue \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 204 °C (400 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 316 °C (600 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 371 °C (700 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 427 °C (800 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 482 °C (900 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 538 °C (1000 °F), R = -1, maximum stress \|\| 10 cycles to 4x10⁵ cycles FSN : axial fatigue \|\| tested at 593 °C (1100 °F), R = -1, maximum stress \|\| 10 cycles to 1x10⁶ cycles FSN : axial fatigue \|\| tested at 649 °C (1200 °F), R = -1, maximum stress \|\| 10 cycles to 2x10⁵ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F)
1015 (UNS G10150) (WNr 1.1141) (ISO/EN/DIN C14/C15/C15E/Ck15) (JIS S15C) (ASTM C18RR/XC12/XC15) (AISI 1015) (SAE J403/J412/J414) (AMS 5060) (GB & GB/T 15/15F/15Mn/H15A/H15Mn/H15Mn/ML15/Q235C-Z/Q235D-TZ) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -150 °C to 540 °C (-238 °F to 1004 °F) TD : solid \|\| -150 °C to 540 °C (-238 °F to 1004 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : 0.002/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.3 mm/mm strain SSC : +0.02 Nb, 0.002/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.3 mm/mm strain SSCC : 0.002/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.3 mm/mm strain SSCC : +0.02 Nb, 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.3 mm/mm strain UTS : killed \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : killed \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : killed \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : killed \|\| tested at 454 °C (850 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| Master curve (LMP) \|\| 454 °C to 761 °C (849 °F to 1402 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
1018 (UNS G10180) (WNr 1.0453) (ISO/EN/DIN C14/CK15) (JIS SEV295/SEV345) (ASTM A108/A510/A513/A519/A544/A545/A548/A549/A576/A659) (AISI 1018) (SAE J403/J412/J414) (AMS 5069) (GB & GB/T 410/5312/712/D) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -150 °C to 540 °C (-238 °F to 1004 °F) TD : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : annealed at 500 °C (932 °F) \|\| tested at 20 °C (68 °F), uniform grain size, 3.85x10^-⁵/s \|\| 0 to 0.9 mm/mm strain SSC : annealed at 500 °C (932 °F) \|\| tested at 20 °C (68 °F), gradient grain size, 3.85x10^-⁵/s \|\| 0 to 0.95 mm/mm strain SSC : annealed at 870 °C (1598 °F) \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 1.19 mm/mm strain SSCC : annealed at 870 °C (1598 °F) \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.67 mm/mm strain FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain range \|\| 1 cycles to 1x10⁴ cycles FSN : at RT: UTS = 493 MPa (71.5 ksi), YS = 370 MPa (53.7 ksi) \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 2.3x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
1020 (UNS G10200) (WNr 1.0402) (ISO/EN/DIN C22/CK22) (JIS S20C/S22C/SWRCH20A) (ASTM A510/A519/A544/A576/A659) (AISI 1020) (SAE J403/J412/J414) (AMS 5032/5045) (GB & GB/T 20/20A/20F/20G/A/ML20/ML20AI/Q235q-C) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -247 °C to 800 °C (-413 °F to 1472 °F) TD : solid \|\| 22 °C to 975 °C (71 °F to 1787 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 27 °C (80 °F) \|\| 0 to 0.16 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.72 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.72 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.25 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.72 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.72 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.19 mm/mm strain SSC : 5x10^-⁵/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 100 s \|\| 0 to 0.95 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 27 °C (80 °F) \|\| 0 to 0.18 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.1 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.12 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.5 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.12 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.12 mm/mm strain SSC : 0.01/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.72 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 27 °C (80 °F) \|\| 0 to 0.18 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.72 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.72 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.16 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.72 mm/mm strain SSC : 1/s, hot-rolled \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.95 mm/mm strain SSC : 1000/s, hot-rolled \|\| tested at 20 °C (68 °F) \|\| 0 to 0.2 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain SSC : 0.002/s, martensite \|\| tested at 20 °C (68 °F), as-quenched \|\| 0 to 0.31 mm/mm strain SSC : 0.002/s, martensite \|\| tested at 20 °C (68 °F), quenched & tempered \|\| 0 to 0.35 mm/mm strain SSCC : pre-strained at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSCC : pre-strained at 20 °C (68 °F) \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.2 mm/mm strain UTS : killed \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : as-received \|\| -196 °C to 27 °C (-321 °F to 80 °F) YS : killed \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : as-received \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : killed \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : killed \|\| tested at 454 °C (850 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| tested at 510 °C (950 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : killed \|\| Master curve (LMP) \|\| 454 °C to 538 °C (849 °F to 1000 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, plastic strain range \|\| 2 cycles to 7x10³ cycles FSN : hot-rolled \|\| tested at 20 °C (68 °F), R = -1, unnotched, maximum stress \|\| 6.29x10⁴ cycles to 4.7x10⁷ cycles FSN : hot-rolled \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.9, maximum stress \|\| 2x10⁴ cycles to 3.65x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
1020 + 0.23 Si (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TD : solid \|\| 22 °C to 975 °C (71 °F to 1787 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSCC : 0.001/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.001/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.85 mm/mm strain SSCC : 0.01/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.84 mm/mm strain SSCC : 0.01/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.82 mm/mm strain SSCC : 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.83 mm/mm strain
1023 (UNS G10230) (WNr 1.1151) (ASTM A510/A575/A576) (AISI 1023) (SAE J403/J412/J414) (GB & GB/T Q235A-F/Q235A-b/Q255/Q255A-Z/Q255B-F/Q255B-F/Q255B-Z/Q255B-b) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : longitudinal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain SSC : transverse \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
1030 (UNS G10300) (WNr 1.1172) (ISO/EN/DIN C30) (JIS S30C/SWRH32B) (ASTM A510/A512/A519/A544/A546/A576/A682) (AISI 1030) (SAE J403/J412/J414) (AFNOR AF50C30/XC32) (GB & GB/T 30) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) FEN : cast, normalized & tempered \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 1 cycles to 5x10⁶ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1035 (UNS G10350) (ISO/EN/DIN 35C8/C35/C35Mn75) (JIS S35C/SWRH37B) (ASTM A510/A519/A544/A545/A546/A576/A682) (AISI 1035) (SAE J403/J412/J414) (AMS 5080/5082) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : normalized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSCC : pre-strained at 20 °C (68 °F) \|\| tested at 20 °C (68 °F), 4x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSCC : pre-strained at 250 °C (482 °F) \|\| tested at 20 °C (68 °F), 4x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSCC : 0.2/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.92 mm/mm strain SSCC : 0.2/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 0.2/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 2/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 2/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 2/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.92 mm/mm strain SSCC : 20/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 20/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.94 mm/mm strain SSCC : 20/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.93 mm/mm strain HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1040 (UNS G10400) (WNr 1.1186) (ISO/EN/DIN 45C8/CK45/Ck40) (JIS G4051S40C/SWRH42B) (ASTM A108/A29/A449/A510/A519/A546/A576/A682) (AISI 1040) (SAE J403/J412/J414) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSC : 0.01/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSC : 0.1/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.4 mm/mm strain UTS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : as-received \|\| -196 °C to 27 °C (-321 °F to 80 °F) YS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : as-received \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : as-received \|\| -196 °C to 27 °C (-321 °F to 80 °F) SR : quenched & tempered \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : quenched & tempered \|\| tested at 454 °C (850 °F) \|\| 100 h to 1,000 h SR : quenched & tempered \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : quenched & tempered \|\| Master curve (LMP) \|\| 371 °C to 538 °C (700 °F to 1000 °F) FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = 0, maximum stress \|\| 4x10⁴ cycles to 1x10⁸ cycles FSN : annealed at 899 °C (1650 °F), wrought \|\| tested at 20 °C (68 °F), R = -1, unnotched, rotating beam, maximum stress \|\| 8.9x10⁴ cycles to 1x10⁷ cycles FSN : annealed at 899 °C (1650 °F), wrought \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.2, rotating beam, maximum stress \|\| 4.5x10⁴ cycles to 1x10⁷ cycles FSN : normalized & tempered, wrought \|\| tested at 20 °C (68 °F), R = -1, unnotched, rotating beam, maximum stress \|\| 7.4x10⁴ cycles to 1x10⁷ cycles FSN : normalized & tempered, wrought \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.2, rotating beam, maximum stress \|\| 3.2x10⁴ cycles to 1x10⁷ cycles FSN : annealed at 899 °C (1650 °F), cast \|\| tested at 20 °C (68 °F), R = -1, unnotched, rotating beam, maximum stress \|\| 8.4x10⁴ cycles to 1x10⁷ cycles FSN : annealed at 899 °C (1650 °F), cast \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.2, rotating beam, maximum stress \|\| 4.1x10⁴ cycles to 1x10⁷ cycles FSN : normalized & tempered, cast \|\| tested at 20 °C (68 °F), R = -1, unnotched, rotating beam, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles FSN : normalized & tempered, cast \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.2, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
10B46 (AISI 10B46) (SAE J403) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : lower bainite, transformed at 350 °C (662 °F) \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.27 mm/mm strain SSC : lower bainite, transformed at 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.27 mm/mm strain SSC : lower bainite, transformed at 450 °C (842 °F) \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.27 mm/mm strain SSCC : lower bainite, transformed at 350 °C (662 °F) \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.27 mm/mm strain SSCC : lower bainite, transformed at 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.27 mm/mm strain SSCC : lower bainite, transformed at 450 °C (842 °F) \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.27 mm/mm strain HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F)
1045 (UNS G10450) (WNr 1.1192/1.1730) (ISO/EN/DIN 45C8/C45/C45E/C45U/Ck45) (JIS S45C/SWRH47B) (ASTM A29/A510/A519/A576/A682) (AISI 1045) (SAE J403/J412/J414) (AFNOR XC48) (GB & GB/T 45/45H) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 0 °C to 1200 °C (32 °F to 2192 °F) TD : solid \|\| 0 °C to 562 °C (32 °F to 1043 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : quenched & tempered \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 2 mm/mm strain SSC : as-rolled \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 2.5 mm/mm strain SSC : quenched & spheroidized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 2.25 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, furnace spheroidized for 3 h \|\| 0 to 0.122 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, furnace spheroidized for 6 h \|\| 0 to 0.162 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, furnace spheroidized for 12 h \|\| 0 to 0.2 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, furnace spheroidized for 24 h \|\| 0 to 0.16 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, induction spheroidized for 5 minutes \|\| 0 to 0.68 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, induction spheroidized for 10 minutes \|\| 0 to 0.8 mm/mm strain SSC : quenched & spheroidized at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 0.001/s, induction spheroidized for 15 minutes \|\| 0 to 0.91 mm/mm strain SSCC : hot-rolled bar \|\| tested at 900 °C (1652 °F), 0.1/s \|\| 0 to 0.82 mm/mm strain SSCC : hot-rolled bar \|\| tested at 1000 °C (1832 °F), 0.1/s \|\| 0 to 0.92 mm/mm strain SSCC : hot-rolled bar \|\| tested at 1100 °C (2012 °F), 0.1/s \|\| 0 to 0.92 mm/mm strain SSCC : hot-rolled bar \|\| tested at 1280 °C (2336 °F), 0.1/s \|\| 0 to 0.88 mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 375 °C (68 °F to 707 °F) UTS : solid \|\| unknown condition \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| unknown condition \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| unknown condition \|\| 20 °C to 650 °C (68 °F to 1202 °F) FSN : annealed near 850 °C (1562 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : ultra-fine grain \|\| tested at 20 °C (68 °F), R = 0.1, bending, stress amplitude \|\| 5x10³ cycles to 6x10⁶ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1065 (UNS G10650) (WNr 1.1230) (ISO/EN/DIN 65C6/C67) (JIS S65C/SWRH67B) (AISI 1065) (GB & GB/T 1222/3078/3522/4354/4357/65/6725/6819/699/711) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) VP : solid \|\| 1095 °C to 1443 °C (2003 °F to 2629 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1070 (UNS G10700) (WNr 1.1520) (JIS SWRH72B) (ASTM A510/A576/A682) (AISI 1070) (SAE J403/J412/J414) (AMS 5115) (AFNOR C70E2U) (GB & GB/T 70/70-E/70-F/70-G/CRB1170) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) FEN : in air \|\| tested at 20 °C (68 °F), R = -1, axial, 0.02/s strain rate, total strain range \|\| 80 cycles to 2x10⁶ cycles FEN : in air \|\| tested at 400 °C (752 °F), R = -1, axial, total strain range \|\| 300 cycles to 6x10⁴ cycles FEN : in air \|\| tested at 600 °C (1112 °F), R = -1, axial, 0.02/s strain rate, total strain range \|\| 800 cycles to 5x10⁴ cycles FEN : in air \|\| tested at 600 °C (1112 °F), R = -1, axial, 0.002/s strain rate, total strain range \|\| 140 cycles to 8x10³ cycles FEN : in air \|\| tested at 600 °C (1112 °F), R = -1, axial, 2x10^-⁴/s strain rate, total strain range \|\| 200 cycles to 2x10⁴ cycles FEN : in air \|\| tested at 700 °C (1292 °F), R = -1, axial, 0.02/s strain rate, total strain range \|\| 2x10³ cycles to 3x10⁴ cycles FEN : in air \|\| tested at 700 °C (1292 °F), R = -1, axial, 0.002/s strain rate, total strain range \|\| 200 cycles to 4x10³ cycles FEN : in air \|\| tested at 700 °C (1292 °F), R = -1, axial, 2x10^-⁴/s strain rate, total strain range \|\| 300 cycles to 4x10³ cycles FEN : in helium \|\| tested at 600 °C (1112 °F), R = -1, axial, 0.02/s strain rate, total strain range \|\| 2x10³ cycles to 4x10⁵ cycles FEN : in helium \|\| tested at 600 °C (1112 °F), R = -1, axial, 2x10^-⁴/s strain rate, total strain range \|\| 2x10³ cycles to 1x10⁵ cycles FSN : ultrasonic at 20 kHz \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 5x10⁴ cycles to 1.3x10⁹ cycles FSN : air cooled \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : air cooled \|\| tested at 20 °C (68 °F), R = -1, axial, shot-peened, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1075 (UNS G10750) (WNr 1.0614) (JIS G4801SUP3/SWRH77B) (AISI 1075) (GB & GB/T 4354/4357/6725/699/75/8919) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SSC : quenched & tempered \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at -79 °C (-110 °F), 3.3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at -195.6 °C (-320 °F), 3.3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at -252.7 °C (-422.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.01 mm/mm strain SSC : hot-rolled \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.7 mm/mm strain UTS : bar \|\| quenched & tempered \|\| -253 °C to 27 °C (-424 °F to 80 °F) YS : bar \|\| quenched & tempered \|\| -253 °C to 27 °C (-424 °F to 80 °F) %El : bar \|\| quenched & tempered \|\| -253 °C to 27 °C (-424 °F to 80 °F) FEN : hardened & tempered \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum strain \|\| 3.75x10³ cycles to 1x10⁸ cycles FEN : hardened & tempered \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum strain \|\| 3x10⁴ cycles to 8.3x10⁵ cycles FEN : hardened & tempered \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain \|\| 2.3x10⁴ cycles to 1x10⁷ cycles FEN : hardened & tempered \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain \|\| 6.8x10³ cycles to 1x10⁷ cycles FSN : hardened & tempered \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : hardened & tempered \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 7x10³ cycles to 1x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
1080 (UNS G10800) (WNr 1.1248) (ISO/EN/DIN Ck75) (JIS SWRH82B) (ASTM A29/A510/A576/A682) (AISI 1080) (SAE J403/J412/J414) (AMS 5110) (GB & GB/T 4357/5354/6725/699/80/8919) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : quasi-static \|\| tested at 20 °C (68 °F), spheroidized, unknown strain rate \|\| 0 to 0.19 mm/mm strain SSC : 1/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSC : 500/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.11 mm/mm strain SSC : 500/s \|\| tested at 149 °C (300 °F) \|\| 0 to 0.12 mm/mm strain SSC : 500/s \|\| tested at 260 °C (500 °F) \|\| 0 to 0.12 mm/mm strain SSC : 500/s \|\| tested at 399 °C (750 °F) \|\| 0 to 0.88 mm/mm strain SSC : 1000/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain SSC : 1000/s \|\| tested at 149 °C (300 °F) \|\| 0 to 0.11 mm/mm strain SSC : 1000/s \|\| tested at 260 °C (500 °F) \|\| 0 to 0.11 mm/mm strain SSC : 1000/s \|\| tested at 399 °C (750 °F) \|\| 0 to 0.88 mm/mm strain SSC : 1500/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.94 mm/mm strain SSC : 1500/s \|\| tested at 149 °C (300 °F) \|\| 0 to 0.11 mm/mm strain SSC : 1500/s \|\| tested at 260 °C (500 °F) \|\| 0 to 0.15 mm/mm strain SSC : 1500/s \|\| tested at 399 °C (750 °F) \|\| 0 to 0.11 mm/mm strain HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1250 °C (68 °F to 2282 °F) SIGMA : solid \|\| 20 °C to 1250 °C (68 °F to 2282 °F)
1086 (UNS G10860) (WNr 1.0628) (AISI 1086) (GB & GB/T T8MnA-E/T8MnA-F/T8MnA-G/T9A-E/T9A-F/T9A-G) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 832 °C (68 °F to 1529 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 725 °C (68 °F to 1337 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
1095 (UNS G10950) (WNr 1.0618) (ISO/EN/DIN Ck101) (ASTM A290/A510/A576/A682) (AISI 1095) (SAE J403/J412/J414) (AMS 5121/5122/5132/7304) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -249 °C to 832 °C (-416 °F to 1529 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) VP : solid \|\| 1105 °C to 1465 °C (2021 °F to 2669 °F)

EN08 (WNr 1.0511/1.1186/1.1189) (JIS S40C) (AFNOR AF60C40/AF60C45/XC42HI) (GB & GB/T 40) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : quenched & tempered to condition R, 0.0015/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.46 mm/mm strain SSC : quenched & tempered to condition R, 0.0015/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.43 mm/mm strain SSC : quenched & tempered to condition R, 0.0015/s \|\| tested at 450 °C (842 °F) \|\| 0 to 0.16 mm/mm strain SSC : quenched & tempered to condition R, 0.0015/s \|\| tested at 650 °C (1202 °F) \|\| 0 to 0.48 mm/mm strain SSC : quenched & tempered to condition R, 0.015/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.46 mm/mm strain SSC : quenched & tempered to condition R, 0.15/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSC : quenched & tempered to condition R, 0.15/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.21 mm/mm strain SSC : quenched & tempered to condition R, 0.15/s \|\| tested at 450 °C (842 °F) \|\| 0 to 0.4 mm/mm strain SSC : quenched & tempered to condition R, 0.15/s \|\| tested at 650 °C (1202 °F) \|\| 0 to 0.38 mm/mm strain UTS : quenched & tempered to condition R \|\| strain rate of 0.0015/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : quenched & tempered to condition R \|\| strain rate of 0.15/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : quenched & tempered to condition R \|\| strain rate of 0.0015/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : quenched & tempered to condition R \|\| strain rate of 0.15/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : quenched & tempered to condition R \|\| strain rate of 0.0015/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : quenched & tempered to condition R \|\| strain rate of 0.15/s \|\| 20 °C to 650 °C (68 °F to 1202 °F) HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
LZ45CrV (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 0 °C to 1200 °C (32 °F to 2192 °F) TD : solid \|\| 0 °C to 562 °C (32 °F to 1043 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) FSN : double-normalized and tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
LZ50 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 0 °C to 1200 °C (32 °F to 2192 °F) TD : solid \|\| 0 °C to 562 °C (32 °F to 1043 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSCC : as-received, 0.05/s \|\| tested at 870 °C (1598 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.05/s \|\| tested at 970 °C (1778 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.05/s \|\| tested at 1020 °C (1868 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.05/s \|\| tested at 1070 °C (1958 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.05/s \|\| tested at 1170 °C (2138 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.1/s \|\| tested at 1020 °C (1868 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 0.5/s \|\| tested at 1020 °C (1868 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 1/s \|\| tested at 1020 °C (1868 °F) \|\| 0 to 0.8 mm/mm strain SSCC : as-received, 3/s \|\| tested at 1020 °C (1868 °F) \|\| 0 to 0.8 mm/mm strain FSN : locomotive axle \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.6x10⁴ cycles to 1x10⁷ cycles HE : solid \|\| oxidized \|\| 315 °C to 816 °C (599 °F to 1500 °F) HE : solid \|\| polished \|\| -205 °C to 1193 °C (-337 °F to 2180 °F) RHO : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
G4802 SK5-CSP (JIS G4802SK5-CSP) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) DLL : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) MTE : solid \|\| -253 °C to 700 °C (-424 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 725 °C (68 °F to 1337 °F) FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles
22MnB5	D* : solid \|\| room temperature value SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 500 °C (932 °F), 0.1/s \|\| 0 to 0.5 mm/mm strain SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 650 °C (1202 °F), 0.1/s \|\| 0 to 0.53 mm/mm strain SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 800 °C (1472 °F), 0.1/s \|\| 0 to 0.5 mm/mm strain SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 500 °C (932 °F), 1/s \|\| 0 to 0.37 mm/mm strain SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 650 °C (1202 °F), 1/s \|\| 0 to 0.39 mm/mm strain SSC : heated to 950 °C (1742 °F), austenite phase \|\| tested at 800 °C (1472 °F), 1/s \|\| 0 to 0.42 mm/mm strain SSC : austenitized at 900 °C (1652 °F), martensite phase \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.18 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 2 mm (0.0787 inch) at 420 °C (788 °F) \|\| 0 to 0.29 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 4 mm (0.157 inch) at 420 °C (788 °F) \|\| 0 to 0.215 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 10 mm (0.394 inch) at 420 °C (788 °F) \|\| 0 to 0.258 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 2 mm (0.0787 inch) at 650 °C (1202 °F) \|\| 0 to 0.21 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 4 mm (0.157 inch) at 650 °C (1202 °F) \|\| 0 to 0.233 mm/mm strain SSC : austenitized at 900 °C (1652 °F), elevated temperature strained, quenched \|\| tested at 20 °C (68 °F), 0.001/s, strained 10 mm (0.394 inch) at 650 °C (1202 °F) \|\| 0 to 0.27 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 193 HV1000 \|\| 0 to 0.12 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 222 HV1000 \|\| 0 to 0.95 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 290 HV1000 \|\| 0 to 0.45 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 319 HV1000 \|\| 0 to 0.4 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 376 HV1000 \|\| 0 to 0.35 mm/mm strain SSC : Al-Si coated, hot stamped sheet \|\| tested at 20 °C (68 °F), 0.003/s, hardness 486 HV1000 \|\| 0 to 0.34 mm/mm strain
1110 (UNS G11090/G11100) (WNr 1.0702/1.0703) (JIS SUM11/SUM12) (AISI 1110) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : quasi-static \|\| tested at 20 °C (68 °F), spheroidized, unknown strain rate \|\| 0 to 0.17 mm/mm strain
1112 (AISI 1112) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : 318/s \|\| tested at 20 °C (68 °F) \|\| 0 to 1 mm/mm strain SSC : 0.09/s \|\| tested at 20 °C (68 °F) \|\| 0 to 1 mm/mm strain
1141 (UNS G11410) (AISI 1141) (AFNOR 45MF4) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : air cooled \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : air cooled \|\| tested at 20 °C (68 °F), R = -1, axial, shot-peened, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles
1144 (UNS G11440) (ASTM A29/A311/A510) (AISI 1144) (GB & GB/T Y40Mn) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FEN : heat A \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : heat B \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : heat C \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : average \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FSN : heat A \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles FSN : heat A \|\| tested at 20 °C (68 °F), R = -1, torsion, maximum stress \|\| 1.7x10⁴ cycles to 1x10⁷ cycles FSN : heat B \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles FSN : heat C \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles FSN : heat C \|\| tested at 20 °C (68 °F), R = -1, torsion, maximum stress \|\| 1.1x10⁴ cycles to 1x10⁷ cycles FSN : average \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles FSN : average \|\| tested at 20 °C (68 °F), R = -1, torsion, maximum stress \|\| 1.7x10⁴ cycles to 1x10⁷ cycles
1151 (UNS G11510) (WNr 1.0728) (ISO/EN/DIN 60S20) (AISI 1151) (SAE J1397/J403/J935) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, shot-peened, stress amplitude \|\| 1x10⁴ cycles to 1x10⁷ cycles
1522 (UNS G15220)	D* : solid \|\| room temperature value SSCC : pre-strained at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.15 mm/mm strain SSCC : pre-strained at 20 °C (68 °F) \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.15 mm/mm strain
P355N (WNr 1.0562) (JIS SM490B) (AFNOR A510AP/E355R) (GB & GB/T 20)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
P355NH (WNr 1.0565)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value YS : normalized \|\| less than 20 mm (0.787 inch) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : normalized \|\| 20 mm to 50 mm (0.787 inch to 1.97 inch) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : normalized \|\| 50 mm to 65 mm (1.97 inch to 2.56 inch) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : normalized \|\| 65 mm to 80 mm (2.56 inch to 3.15 inch) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : normalized \|\| 80 mm to 100 mm (3.15 inch to 3.94 inch) \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
P355NL1 (WNr 1.0566)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
P355NL2 (WNr 1.1106)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : normalized \|\| 150 mm to 200 mm (5.91 inch to 7.87 inch) \|\| 20 °C to 460 °C (68 °F to 860 °F) YS : normalized \|\| 150 mm to 200 mm (5.91 inch to 7.87 inch) \|\| 20 °C to 460 °C (68 °F to 860 °F) %El : normalized \|\| 150 mm to 200 mm (5.91 inch to 7.87 inch) \|\| 20 °C to 460 °C (68 °F to 860 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
FMDP pipeline steel	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : 16.1 vol % martensite \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.163 mm/mm strain SSC : 18.6 vol % martensite \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.136 mm/mm strain SSC : 20.5 vol % martensite \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain
API X60 pipeline steel (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : water cooled to 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.003/s, as-pre-strained \|\| 0 to 0.136 mm/mm strain SSC : water cooled to 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.003/s, aged 200 °C (392 °F) \|\| 0 to 0.148 mm/mm strain SSC : water cooled to 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.003/s, aged 250 °C (482 °F) \|\| 0 to 0.133 mm/mm strain SSC : water cooled to 450 °C (842 °F) \|\| tested at 20 °C (68 °F), 0.003/s, as-pre-strained \|\| 0 to 0.15 mm/mm strain SSC : water cooled to 450 °C (842 °F) \|\| tested at 20 °C (68 °F), 0.003/s, aged 200 °C (392 °F) \|\| 0 to 0.14 mm/mm strain SSC : water cooled to 450 °C (842 °F) \|\| tested at 20 °C (68 °F), 0.003/s, aged 250 °C (482 °F) \|\| 0 to 0.156 mm/mm strain
API X65 pipeline steel (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : in air \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.1 mm/mm strain SSC : in vacuum \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.17 mm/mm strain SSC : in-situ hydrogen charged \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.95 mm/mm strain
API X70 pipeline steel	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : acicular ferrite \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : polygonal ferrite + bainite \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.115 mm/mm strain SSC : ferrite + bainite, intercritically annealed \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.13 mm/mm strain
API X80 pipeline steel (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) SSC : heated to 680 °C (1256 °F), air cooled \|\| tested at 20 °C (68 °F), 2.7x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : heated to 1000 °C (1832 °F), 30 minute hold, water quenched, heated to 680 °C (1256 °F), 30 minute hold, air cooled \|\| tested at 20 °C (68 °F), 2.7x10^-⁴/s \|\| 0 to 0.64 mm/mm strain SSC : heated to 250 °C (482 °F), 30 minute hold, air cooled \|\| tested at 20 °C (68 °F), 2.7x10^-⁴/s \|\| 0 to 0.33 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment A \|\| 0 to 0.42 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment B1 \|\| 0 to 0.37 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment B2 \|\| 0 to 0.38 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment B3 \|\| 0 to 0.37 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment B4 \|\| 0 to 0.39 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), heat treatment C \|\| 0 to 0.39 mm/mm strain SSCC : 1000/s \|\| tested at -20 °C (-4 °F), average of all heat treatments \|\| 0 to 0.39 mm/mm strain FSN : rotary bending fatigue \|\| tested at 25 °C (77 °F), R = -1, maximum stress \|\| 7x10⁴ cycles to 1x10⁷ cycles FSN : rotary bending fatigue \|\| tested at -50 °C (-58 °F), R = -1, maximum stress \|\| 4.8x10⁴ cycles to 1x10⁷ cycles FSN : rotary bending fatigue \|\| tested at -80 °C (-112 °F), R = -1, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles
API X90 pipeline steel (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) UTS* : solid \|\| longitudinal \|\| room temperature value UTS* : solid \|\| transverse \|\| room temperature value YS* : solid \|\| longitudinal \|\| room temperature value YS* : solid \|\| transverse \|\| room temperature value %El* : solid \|\| longitudinal \|\| room temperature value %El* : solid \|\| transverse \|\| room temperature value FSN : as-received \|\| tested at 20 °C (68 °F), R = 0.05, axial, longitudinal, stress range \|\| 1x10⁵ cycles to 5x10⁷ cycles FSN : as-received \|\| tested at 20 °C (68 °F), R = 0.7, axial, longitudinal, maximum stress \|\| 2x10⁴ cycles to 5x10⁷ cycles
API X100 pipeline steel	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, longitudinal \|\| 0 to 0.63 mm/mm strain SSC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, transverse \|\| 0 to 0.62 mm/mm strain SSC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, 45 degrees in the LT plane \|\| 0 to 0.54 mm/mm strain SSCC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, longitudinal \|\| 0 to 0.94 mm/mm strain SSCC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, transverse \|\| 0 to 0.9 mm/mm strain SSCC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, 45 degrees in the LT plane \|\| 0 to 0.91 mm/mm strain SSCC : X100 base metal, YS = 650 MPa (94.3 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, short transverse \|\| 0 to 0.89 mm/mm strain
X100Q offshore riser steel	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : X100Q base metal, quenched & tempered, YS = 835 MPa (121 ksi) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.61 mm/mm strain SSC : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, cooled at 10 °C/s \|\| 0 to 0.48 mm/mm strain SSC : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, cooled at 30 °C/s \|\| 0 to 0.49 mm/mm strain SSC : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, cooled at 5 °C/s \|\| 0 to 0.11 mm/mm strain SSC : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, cooled at 10 °C/s \|\| 0 to 0.127 mm/mm strain FEN : X100Q base metal, quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1x10³ cycles to 3.5x10⁴ cycles FEN : X100Q base metal, quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 1x10³ cycles to 3.5x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 10 °C/s, total strain amplitude \|\| 4x10³ cycles to 7.5x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 30 °C/s, total strain amplitude \|\| 3.5x10³ cycles to 6.5x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 10 °C/s, plastic strain amplitude \|\| 4x10³ cycles to 7.5x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 950 °C (1742 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 30 °C/s, plastic strain amplitude \|\| 3.5x10³ cycles to 6.5x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 5 °C/s, total strain amplitude \|\| 3x10³ cycles to 1.15x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 10 °C/s, total strain amplitude \|\| 3x10³ cycles to 7.5x10³ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 5 °C/s, plastic strain amplitude \|\| 3x10³ cycles to 1.15x10⁴ cycles FEN : welded with NiCrMo 2.5-IG filler wire, peak temperature of 750 °C (1382 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, cooled at 10 °C/s, plastic strain amplitude \|\| 3x10³ cycles to 7.5x10³ cycles FSN : X100Q base metal, quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1.5x10³ cycles to 1.5x10⁵ cycles FSN : cross-weld \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 500 cycles to 3x10⁴ cycles
standard pearlitic rail steel	D* : solid \|\| room temperature value SSC : as-received \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.76 mm/mm strain SSC : austenitized, aged at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 200 °C (392 °F) \|\| 0 to 9.6x10^-⁴ mm/mm strain SSC : austenitized, aged at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 400 °C (752 °F) \|\| 0 to 0.72 mm/mm strain SSC : austenitized, aged at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 600 °C (1112 °F) \|\| 0 to 0.67 mm/mm strain SSC : austenitized, aged at 300 °C (572 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 300 °C (572 °F) \|\| 0 to 7.9x10^-³ mm/mm strain SSC : austenitized, aged at 300 °C (572 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 400 °C (752 °F) \|\| 0 to 0.7 mm/mm strain SSC : austenitized, aged at 300 °C (572 °F) \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, double-aged at 600 °C (1112 °F) \|\| 0 to 0.53 mm/mm strain UTS* : effect of heat treatment on RT value \|\| as-received \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 200 °C (392 °F) \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 400 °C (752 °F) \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 600 °C (1112 °F) \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 300 °C (572 °F) \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 400 °C (752 °F) \|\| room temperature value UTS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 600 °C (1112 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| as-received \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 200 °C (392 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 400 °C (752 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 600 °C (1112 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 300 °C (572 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 400 °C (752 °F) \|\| room temperature value YS* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 600 °C (1112 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| as-received \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 200 °C (392 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 400 °C (752 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 200 °C (392 °F) & 600 °C (1112 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 300 °C (572 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 400 °C (752 °F) \|\| room temperature value %El* : effect of heat treatment on RT value \|\| austenitized, aged at 300 °C (572 °F) & 600 °C (1112 °F) \|\| room temperature value

ER70S-6 welding wire (UNS K11140)	E* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value E* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 0.001/s, horizontal \|\| 0 to 0.225 mm/mm strain SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 0.001/s, vertical \|\| 0 to 0.193 mm/mm strain UTS* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value UTS* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value YS* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value YS* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value %El* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value %El* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 90% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 50% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 10% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 90% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 50% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 10% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 90% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 50% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 10% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 90% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 50% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 10% survival, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 90% survival, maximum stress \|\| 4x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 50% survival, maximum stress \|\| 4x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, vertical, 10% survival, maximum stress \|\| 4x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 90% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 50% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : wire + arc additive manufacturing (WAAM), axial + torsional \|\| tested at 20 °C (68 °F), R = 0.01, horizontal, 10% survival, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles
ER100S-1 welding wire	E* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value E* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 0.001/s, horizontal \|\| 0 to 0.115 mm/mm strain SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 0.001/s, vertical \|\| 0 to 0.114 mm/mm strain UTS* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value UTS* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value YS* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value YS* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value %El* : wire + arc additive manufacturing (WAAM) \|\| horizontal \|\| room temperature value %El* : wire + arc additive manufacturing (WAAM) \|\| vertical \|\| room temperature value
ER110S-G welding wire	SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 6.7x10^-⁴/s, low heat input = 221 J/mm \|\| 0 to 0.11 mm/mm strain SSC : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), 6.7x10^-⁴/s, high heat input = 511 J/mm \|\| 0 to 0.11 mm/mm strain UTS* : solid \|\| room temperature value UTS* : wire + arc additive manufacturing (WAAM) \|\| room temperature value YS* : solid \|\| room temperature value YS* : wire + arc additive manufacturing (WAAM) \|\| room temperature value %El* : solid \|\| room temperature value %El* : wire + arc additive manufacturing (WAAM) \|\| room temperature value FSN : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), R = 0.1, low heat input, mean values, stress range \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), R = 0.1, low heat input, mean values minus 2 standard deviations, stress range \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : wire + arc additive manufacturing (WAAM) \|\| tested at 20 °C (68 °F), R = 0.1, low heat input, mean values plus 2 standard deviations, stress range \|\| 5x10⁴ cycles to 1x10⁷ cycles RHO* : solid \|\| wire + arc additive manufacturing (WAAM) \|\| room temperature value SIGMA*: solid \|\| wire + arc additive manufacturing (WAAM) \|\| room temperature value
NiCrMo 2.5-IG filler wire	FEN : NiCrMo 2.5-IG filler wire \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1x10³ cycles to 2x10⁴ cycles FEN : NiCrMo 2.5-IG filler wire \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 1.5x10³ cycles to 2x10⁴ cycles

3140 (UNS G31400) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TD : solid \|\| 0 °C to 564 °C (32 °F to 1047 °F) FSN : 1 mm (0.0394 inch) diameter \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : 2 mm (0.0787 inch) diameter \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10⁴ cycles to 1x10⁷ cycles
4037 (UNS G40370) (WNr 1.5432) (ISO/EN/DIN 42MnMo7) (ASTM A322/A331/A519/A547) (AISI 4037) (SAE J404/J412/J770) (AMS 6300) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SSCC : spheroidize anneal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.61 mm/mm strain
4130 (UNS G41300) (WNr 1.7218) (ISO/EN/DIN 25CrMo4/G26CrMo4) (JIS SCM420/SCM430) (ASTM A322/A331/A505/A513) (AISI 4130) (SAE J404/J412/J770) (AMS 6350/6356/6360) (AFNOR 25CD4) (GB & GB/T 30CrMo/ZG20CrMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hardened & tempered \|\| -249 °C to 1200 °C (-416 °F to 2192 °F) TD : solid \|\| 0 °C to 1050 °C (32 °F to 1922 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : normalized, 1/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.77 mm/mm strain SSC : normalized, 1/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.77 mm/mm strain SSC : normalized, 1/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.39 mm/mm strain SSC : normalized, 1/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.39 mm/mm strain SSC : normalized, 1/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.77 mm/mm strain SSC : normalized, 1/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 1/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.39 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.95 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : normalized, 0.01/s \|\| tested at 649 °C (1200 °F), held for 100 s \|\| 0 to 0.39 mm/mm strain SSC : normalized, 5x10^-⁵/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.8 mm/mm strain SSC : normalized, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.58 mm/mm strain SSC : normalized, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.37 mm/mm strain SSC : normalized, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.75 mm/mm strain SSC : normalized, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.58 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.6 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 1/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.25 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.44 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 0.01/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.58 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.44 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.3 mm/mm strain SSC : oil quenched from 854 °C (1570 °F), tempered at 538 °C (1000 °F), 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 100 s \|\| 0 to 0.3 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 0.01/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.18 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 500/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.4 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 500/s \|\| tested at 224 °C (435 °F) \|\| 0 to 0.33 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 500/s \|\| tested at 466 °C (870 °F) \|\| 0 to 0.27 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 500/s \|\| tested at 707 °C (1305 °F) \|\| 0 to 0.66 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1000/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.4 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1000/s \|\| tested at 224 °C (435 °F) \|\| 0 to 0.35 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1000/s \|\| tested at 466 °C (870 °F) \|\| 0 to 0.32 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1000/s \|\| tested at 707 °C (1305 °F) \|\| 0 to 0.49 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1800/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.45 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1800/s \|\| tested at 224 °C (435 °F) \|\| 0 to 0.28 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1800/s \|\| tested at 466 °C (870 °F) \|\| 0 to 0.27 mm/mm strain SSC : quenched from 913 °C (1675 °F), tempered at 566 °C (1050 °F), 1800/s \|\| tested at 707 °C (1305 °F) \|\| 0 to 0.66 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, as-quenched \|\| 0 to 0.38 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 350 °C (662 °F) \|\| 0 to 0.19 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 400 °C (752 °F) \|\| 0 to 0.14 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 430 °C (806 °F) \|\| 0 to 0.18 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 460 °C (860 °F) \|\| 0 to 0.24 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 490 °C (914 °F) \|\| 0 to 0.2 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 520 °C (968 °F) \|\| 0 to 0.34 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 0.0025/s, tempered 1 h at 550 °C (1022 °F) \|\| 0 to 0.4 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, as-quenched, H₂ charged \|\| 0 to 3.07x10^-³ mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 350 °C (662 °F), H₂ charged \|\| 0 to 1.4x10^-³ mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 400 °C (752 °F), H₂ charged \|\| 0 to 1.26x10^-³ mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 430 °C (806 °F), H₂ charged \|\| 0 to 2.1x10^-³ mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 460 °C (860 °F), H₂ charged \|\| 0 to 5.1x10^-³ mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 490 °C (914 °F), H₂ charged \|\| 0 to 0.16 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 520 °C (968 °F), H₂ charged \|\| 0 to 0.27 mm/mm strain SSC : effects of H₂ and temper \|\| tested at 20 °C (68 °F), 1x10^-⁶/s, tempered 1 h at 550 °C (1022 °F), H₂ charged \|\| 0 to 0.28 mm/mm strain UTS : heat-treated to UTS of 690 MPa (100 ksi) \|\| 3.17 mm (0.125 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : heat-treated to UTS of 862 MPa (125 ksi) \|\| 1.59 mm (0.0625 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : heat-treated to UTS of 1.17 GPa (170 ksi) \|\| 3.17 mm (0.125 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : heat-treated to UTS of 1.24 GPa (180 ksi) \|\| bar \|\| 20 °C to 593 °C (68 °F to 1099 °F) UTS : normalized/oil quenched/tempered \|\| 2.77 mm (0.109 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS* : effects of H₂ and temper \|\| as-quenched \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F) \|\| room temperature value UTS* : effects of H₂ and temper \|\| as-quenched, H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F), H₂ charged \|\| room temperature value UTS* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F), H₂ charged \|\| room temperature value YS : heat-treated to UTS of 690 MPa (100 ksi) \|\| 3.17 mm (0.125 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : heat-treated to UTS of 862 MPa (125 ksi) \|\| 1.59 mm (0.0625 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : heat-treated to UTS of 1.17 GPa (170 ksi) \|\| 3.17 mm (0.125 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : heat-treated to UTS of 1.24 GPa (180 ksi) \|\| bar \|\| 20 °C to 593 °C (68 °F to 1099 °F) YS : normalized/oil quenched/tempered \|\| 2.77 mm (0.109 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS* : effects of H₂ and temper \|\| as-quenched \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F) \|\| room temperature value YS* : effects of H₂ and temper \|\| as-quenched, H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F), H₂ charged \|\| room temperature value YS* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F), H₂ charged \|\| room temperature value YSC : heat-treated to UTS of 862 MPa (125 ksi) \|\| 1.59 mm (0.0625 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : effects of H₂ and temper \|\| as-quenched \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F) \|\| room temperature value %El* : effects of H₂ and temper \|\| as-quenched, H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 350 °C (662 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 400 °C (752 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 430 °C (806 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 460 °C (860 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 490 °C (914 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 520 °C (968 °F), H₂ charged \|\| room temperature value %El* : effects of H₂ and temper \|\| tempered 1 h at 550 °C (1022 °F), H₂ charged \|\| room temperature value SR : 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 5 h to 840 h SR : 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 3 h to 740 h SR : 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 590 h SR : 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) FSN : UTS 807 MPa (117 ksi), unnotched \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 3x10³ cycles to 5x10⁷ cycles FSN : UTS 807 MPa (117 ksi), unnotched \|\| tested at 20 °C (68 °F), R = -0.6, axial, maximum stress \|\| 5x10⁴ cycles to 3x10⁶ cycles FSN : UTS 807 MPa (117 ksi), unnotched \|\| tested at 20 °C (68 °F), R = -0.3, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁶ cycles FSN : UTS 807 MPa (117 ksi), unnotched \|\| tested at 20 °C (68 °F), R = 0.02, axial, maximum stress \|\| 5x10⁴ cycles to 5x10⁵ cycles FSN : UTS 807 MPa (117 ksi), K_t = 1.5 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 1.5 \|\| tested at 20 °C (68 °F), 69.0 MPa (10 ksi) mean stress, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 1.5 \|\| tested at 20 °C (68 °F), 138 MPa (20 ksi) mean stress, axial, maximum stress \|\| 5x10⁴ cycles to 3x10⁶ cycles FSN : UTS 807 MPa (117 ksi), K_t = 1.5 \|\| tested at 20 °C (68 °F), 207 MPa (30 ksi) mean stress, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), 69.0 MPa (10 ksi) mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), 138 MPa (20 ksi) mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), 207 MPa (30 ksi) mean stress, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), 69.0 MPa (10 ksi) mean stress, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), 138 MPa (20 ksi) mean stress, axial, maximum stress \|\| 3x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), 207 MPa (30 ksi) mean stress, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 5.0 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 5.0 \|\| tested at 20 °C (68 °F), 69.0 MPa (10 ksi) mean stress, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 5.0 \|\| tested at 20 °C (68 °F), 138 MPa (20 ksi) mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 807 MPa (117 ksi), K_t = 5.0 \|\| tested at 20 °C (68 °F), 207 MPa (30 ksi) mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), unnotched \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 3x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), unnotched \|\| tested at 20 °C (68 °F), 345 MPa (50 ksi) mean stress, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), K_t = 2.0 \|\| tested at 20 °C (68 °F), 345 MPa (50 ksi) mean stress, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 1.24 GPa (180 ksi), K_t = 4.0 \|\| tested at 20 °C (68 °F), 345 MPa (50 ksi) mean stress, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.4 h to 2 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.8 h to 3 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.3 h to 6 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.7 h to 40 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.8 h to 35 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 80 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.7 h to 205 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.5 h to 110 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 210 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.17 h to 640 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.16 h to 580 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.4 h to 573 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.5 h to 210 h CRS : 2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.4 h to 85 h CRS : 2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.8 h to 240 h CRS : 2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 0.9 h to 200 h CRS : 3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 0.7 h to 165 h CRS : 3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.1 h to 220 h CRS : 3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 427 °C (800 °F) \|\| 1.8 h to 490 h CRS : 5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 482 °C (900 °F) \|\| 1 h to 325 h CRS : 5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 350 h CRS : 5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 427 °C (800 °F) \|\| 0.01 h to 0.33 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 482 °C (900 °F) \|\| 0.5 h to 1.1 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 538 °C (1000 °F) \|\| 0.3 h to 1 h CRS : 0.1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 427 °C (800 °F) \|\| 0.3 h to 10 h CRS : 0.2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 482 °C (900 °F) \|\| 0.5 h to 11 h CRS : 0.2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 5 h CRS : 0.2% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 427 °C (800 °F) \|\| 0.14 h to 30 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 482 °C (900 °F) \|\| 0.2 h to 25 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 538 °C (1000 °F) \|\| 0.6 h to 16 h CRS : 0.3% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 427 °C (800 °F) \|\| 0.9 h to 140 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 482 °C (900 °F) \|\| 0.47 h to 65 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 538 °C (1000 °F) \|\| 1 h to 60 h CRS : 0.5% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 427 °C (800 °F) \|\| 8 h to 200 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 482 °C (900 °F) \|\| 7.8 h to 270 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| tested at 538 °C (1000 °F) \|\| 4 h to 275 h CRS : 1% plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.3 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 1.6 mm (0.063 inch) thick sheet, normalized, in compression \|\| 1 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| hardened & tempered \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| hardened & tempered \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
4135 (UNS G41350) (WNr 1.7220) (ISO/EN/DIN 34CrMo4/35CrMo4) (JIS SCM435H) (ASTM A29/A331/A355/A519/A519/A711/A829) (AISI 4135) (SAE J1397/J404/J412/J770) (AMS 6352/6365/6372/6372C/6372D) (AFNOR 34CD4/35CD4) (GB & GB/T 35CrMo/ZG35CrMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hardened & tempered \|\| -249 °C to 1200 °C (-416 °F to 2192 °F) TD : solid \|\| 0 °C to 1050 °C (32 °F to 1922 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : austenitized at 860 °C (1580 °F), oil quenched, tempered 460 °C (860 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.43 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 800 °C (1472 °F), 1/s, in torsion \|\| 0 to 2.83 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 900 °C (1652 °F), 1/s, in torsion \|\| 0 to 4 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 1000 °C (1832 °F), 1/s, in torsion \|\| 0 to 2 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 1100 °C (2012 °F), 1/s, in torsion \|\| 0 to 2 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 1000 °C (1832 °F), 0.1/s, in torsion \|\| 0 to 0.94 mm/mm strain SSC : homogenized at 1100 °C (2012 °F) \|\| tested at 1100 °C (2012 °F), 10/s, in torsion \|\| 0 to 0.93 mm/mm strain SSC : normalized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain
4140 (UNS G41400) (WNr 1.3563/1.7223/1.7225/1.7227) (ISO/EN/DIN 40Cr4Mo3/42CrMo4/42CrMoS4) (JIS SCM440/SCM440H) (ASTM A193/A194/A29/A320/A322/A331/A505/A506/A513/A519/A547/A646/A711/A752/A829) (AISI 4140) (SAE J404/J412/J770) (AMS 6349/6381/6382/6390/6395/6529) (AFNOR 42CD4) (GB & GB/T 42CrMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| hardened & tempered \|\| 20 °C to 575 °C (68 °F to 1067 °F) TD : liquid \|\| 1556 °C to 2230 °C (2833 °F to 4046 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : austenitized at 1000 °C (1832 °F) \|\| tested at 20 °C (68 °F), tempered at 200 °C (392 °F), 0.00833/s \|\| 0 to 0.2 mm/mm strain SSC : austenitized at 1000 °C (1832 °F) \|\| tested at 20 °C (68 °F), tempered at 400 °C (752 °F), 0.00833/s \|\| 0 to 0.15 mm/mm strain SSC : forged 1100 °C (2012 °F) to 1200 °C (2192 °F), hardened 820 °C (1508 °F) to 860 °C (1580 °F) \|\| tested at 20 °C (68 °F), annealed at 540 °C (1004 °F) for 1 h, unknown strain rate \|\| 0 to 0.55 mm/mm strain SSC : forged 1100 °C (2012 °F) to 1200 °C (2192 °F), hardened 820 °C (1508 °F) to 860 °C (1580 °F) \|\| tested at 20 °C (68 °F), annealed at 580 °C (1076 °F) for 1 h, unknown strain rate \|\| 0 to 0.59 mm/mm strain SSC : forged 1100 °C (2012 °F) to 1200 °C (2192 °F), hardened 820 °C (1508 °F) to 860 °C (1580 °F) \|\| tested at 20 °C (68 °F), annealed at 620 °C (1148 °F) for 1 h, unknown strain rate \|\| 0 to 0.61 mm/mm strain SSC : forged 1100 °C (2012 °F) to 1200 °C (2192 °F), hardened 820 °C (1508 °F) to 860 °C (1580 °F) \|\| tested at 20 °C (68 °F), annealed at 680 °C (1256 °F) for 1 h, unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed at 816 °C (1500 °F) \|\| tested at 20 °C (68 °F), 6.67x10^-⁵/s \|\| 0 to 0.118 mm/mm strain SSC : soft annealed & cold-drawn, pearlite with some ferrite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.33 mm/mm strain SSC : soft annealed & cold-drawn, pearlite with some ferrite \|\| tested at 400 °C (752 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSCC : tempered at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.2 mm/mm strain SSCC : tempered at 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.15 mm/mm strain SSCC : tempered at 560 °C (1040 °F) \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.31 mm/mm strain SSCC : tempered at 560 °C (1040 °F) \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.313 mm/mm strain SSCC : tempered at 560 °C (1040 °F) \|\| tested at 20 °C (68 °F), 2400/s \|\| 0 to 0.182 mm/mm strain SSCC : tempered at 560 °C (1040 °F) \|\| tested at 20 °C (68 °F), 3200/s \|\| 0 to 0.258 mm/mm strain SSCC : tempered at 560 °C (1040 °F) \|\| tested at 20 °C (68 °F), 4500/s \|\| 0 to 0.4 mm/mm strain SSCC : tempered at 650 °C (1202 °F) \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.35 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.285 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.151 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.1 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.85 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.37 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.21 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.15 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.16 mm/mm strain SSCC : forging temperatures, 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.38 mm/mm strain SSCC : forging temperatures, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.366 mm/mm strain SSCC : forging temperatures, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.29 mm/mm strain SSCC : forging temperatures, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.257 mm/mm strain SSCC : forging temperatures, 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.455 mm/mm strain SSCC : forging temperatures, 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.421 mm/mm strain SSCC : forging temperatures, 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.362 mm/mm strain SSCC : forging temperatures, 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.32 mm/mm strain SSCC : forging temperatures, 50/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.39 mm/mm strain SSCC : forging temperatures, 50/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.364 mm/mm strain SSCC : forging temperatures, 50/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.344 mm/mm strain SSCC : forging temperatures, 50/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.331 mm/mm strain UTS : solid \|\| tempered at 427 °C (800 °F) \|\| -18 °C to 93 °C (-1 °F to 199 °F) UTS : solid \|\| tempered at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| tempered at 510 °C (950 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| tempered at 607 °C (1125 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| tempered at 657 °C (1215 °F) \|\| 20 °C to 565 °C (68 °F to 1049 °F) YS : solid \|\| bar tempered at 427 °C (800 °F) \|\| -18 °C to 93 °C (-1 °F to 199 °F) FEN : as-received, at RT: UTS = 1.09 GPa (159 ksi), YS = 940 MPa (136 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 5 cycles to 5x10⁶ cycles FEN : annealed at 816 °C (1500 °F), at RT: UTS = 667 MPa (96.7 ksi), YS = 385 MPa (55.8 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 5 cycles to 6x10⁶ cycles FSN : martensitic structure \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, longitudinal, maximum stress \|\| 1.2x10⁵ cycles to 1x10⁹ cycles FSN : martensitic structure \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, transverse, maximum stress \|\| 5.8x10⁴ cycles to 2x10⁹ cycles FSN : stress relieved at 550 °C (1022 °F) \|\| tested at 20 °C (68 °F) in air, R = -1, bending, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : stress relieved at 550 °C (1022 °F) \|\| tested at 20 °C (68 °F) in aerated 3% NaCl, R = -1, bending, maximum stress \|\| 1.2x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 625 °C (1157 °F) \|\| tested at 20 °C (68 °F) in dry or 93% RH air, R = -1, bending, maximum stress \|\| 9x10⁴ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 515 °C (959 °F) \|\| tested at 20 °C (68 °F) in dry air, R = -1, bending, maximum stress \|\| 8x10⁴ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 515 °C (959 °F) \|\| tested at 20 °C (68 °F) in 93% RH air, R = -1, bending, maximum stress \|\| 8.6x10⁴ cycles to 9x10⁶ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 515 °C (959 °F) \|\| tested at 20 °C (68 °F) in aerated 3% NaCl, R = -1, bending, maximum stress \|\| 5.3x10⁴ cycles to 6.3x10⁶ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 415 °C (779 °F) \|\| tested at 20 °C (68 °F) in dry air, R = -1, bending, maximum stress \|\| 1.1x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 415 °C (779 °F) \|\| tested at 20 °C (68 °F) in 93% RH air, R = -1, bending, maximum stress \|\| 1.1x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered for 1 h at 415 °C (779 °F) \|\| tested at 20 °C (68 °F) in aerated 3% NaCl, R = -1, bending, maximum stress \|\| 3.3x10⁴ cycles to 1x10⁶ cycles FSN : oil quenched from 850 °C (1562 °F) \|\| tested at 20 °C (68 °F) in dry air, R = -1, bending, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F) \|\| tested at 20 °C (68 °F) in 93% RH air, R = -1, bending, maximum stress \|\| 1.6x10⁴ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F) \|\| tested at 20 °C (68 °F) in aerated 3% NaCl, R = -1, bending, maximum stress \|\| 1.2x10⁴ cycles to 5x10⁵ cycles FSN : oil quenched from 840 °C (1544 °F), tempered for 2 h at 550 °C (1022 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 3x10⁴ cycles to 1.4x10⁶ cycles RHO : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) RHO : liquid \|\| 1556 °C to 2230 °C (2833 °F to 4046 °F) SIGMA : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : liquid \|\| 1556 °C to 2230 °C (2833 °F to 4046 °F)
4142 (UNS G41420) (WNr 1.3563/1.7223/1.7225/1.7227) (ISO/EN/DIN 40Cr4Mo3/42Cr4Mo2) (AISI 4142) (AFNOR 40CD4/42CD4/42CDTS) (GB & GB/T 40CrMnMo/42CrMn/42CrMnMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FEN : heat A \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : heat B \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : heat C \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FEN : average \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁶ cycles FSN : heat A \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : heat B \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : heat C \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : average \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles ST : liquid \|\| 1427 °C to 1647 °C (2600 °F to 2996 °F)
4150 (WNr 1.7228) (ISO/EN/DIN 49CrMo4/50CrMo4) (AISI 4150) (AFNOR 50CD4) (GB & GB/T 50CrMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : induction hardened, tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.07 microns, stress amplitude \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : induction hardened, tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 2.1 microns, stress amplitude \|\| 8x10³ cycles to 4x10⁵ cycles FSN : induction hardened, tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, average of all, stress amplitude \|\| 8x10³ cycles to 4x10⁶ cycles FSN : tempered at 550 °C (1022 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, 95 Hz, stress amplitude \|\| 7x10⁴ cycles to 1x10⁷ cycles FSN : tempered at 550 °C (1022 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, 20 kHz, stress amplitude \|\| 3x10⁴ cycles to 1x10⁸ cycles
SCM 415 (WNr 1.7262) (ISO/EN/DIN 15CrMo) (JIS SCM415) (AFNOR 15CD4.05) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : carburized \|\| tested at 20 °C (68 °F) in air, R = 0.05, 4-pt bending, stress range \|\| 1.5x10³ cycles to 1x10⁸ cycles FSN : carburized \|\| tested at 20 °C (68 °F) in diesel oil, R = 0.05, 4-pt bending, stress range \|\| 7.2x10³ cycles to 1x10⁸ cycles
4310 (UNS G43100) (AISI 4310) (SAE 4310) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SSCC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.01 mm/mm strain
4320 (UNS G43200) (WNr 1.8988) (ISO/EN/DIN 15NiVCr1Mo15) (AISI 4320) (SAE 4320) (GB & GB/T G20CrNi2Mo/G20CrNiMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SSCC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.01 mm/mm strain
4330 (UNS G43300) (AISI 4330) (SAE 4330)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : as-quenched \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SSC : oil quenched \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.4 mm/mm strain SSC : tempered at 150 °C (302 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.2 mm/mm strain SSC : tempered at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.18 mm/mm strain SSC : tempered at 175 °C (347 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.2 mm/mm strain SSCC : as-quenched \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.01 mm/mm strain
4330V	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) FSN : oil quenched from 904 °C (1660 °F), tempered at 132 °C (270 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 6x10³ cycles to 1x10⁷ cycles FSN : oil quenched from 904 °C (1660 °F), tempered at 204 °C (400 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2.7x10³ cycles to 8x10⁶ cycles FSN : oil quenched from 904 °C (1660 °F), tempered at 260 °C (500 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3.8x10³ cycles to 1x10⁷ cycles FSN : oil quenched from 904 °C (1660 °F), tempered at 343 °C (650 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.3x10³ cycles to 1x10⁷ cycles FSN : oil quenched from 904 °C (1660 °F), tempered at 427 °C (800 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles
4340 (UNS G43400) (WNr 1.6565) (ISO/EN/DIN 36CrNiMo6/40NiCr4Mo3/40NiCrMo6) (JIS G4103SNCM439) (ASTM A322/A331/A505/A519/A547/A646) (AISI 4340) (SAE J404/J412/J770) (AMS 5331/6359/6414/6415) (AFNOR 35NCD6) (GB & GB/T 34CrNi1Mo/40CrNiMo/40CrNiMoA) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| oil quenched \|\| -150 °C to 540 °C (-238 °F to 1004 °F) TC : solid \|\| normalized \|\| -150 °C to 540 °C (-238 °F to 1004 °F) TD : solid \|\| 0 °C to 1040 °C (32 °F to 1904 °F) SH : solid \|\| -7 °C to 1520 °C (19 °F to 2768 °F) SSC : austenitized, oil quenched, tempered at 204 °C (400 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : austenitized, oil quenched, tempered at 316 °C (600 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.65 mm/mm strain SSC : austenitized, oil quenched, tempered at 427 °C (800 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.65 mm/mm strain SSC : austenitized, oil quenched, tempered at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.75 mm/mm strain SSC : lower bainite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 20 °C (68 °F), 4x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 20 °C (68 °F), 4/s \|\| 0 to 0.94 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 20 °C (68 °F), 570/s \|\| 0 to 0.145 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 20 °C (68 °F), 700/s \|\| 0 to 0.121 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 227 °C (440 °F), 604/s \|\| 0 to 0.146 mm/mm strain SSC : annealed, HRc = 30 \|\| tested at 462 °C (863 °F), 650/s \|\| 0 to 0.145 mm/mm strain SSCC : austenitized, oil quenched, tempered at 204 °C (400 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSCC : austenitized, oil quenched, tempered at 316 °C (600 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSCC : austenitized, oil quenched, tempered at 427 °C (800 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.65 mm/mm strain SSCC : austenitized, oil quenched, tempered at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSCC : lower bainite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.01 mm/mm strain UTS : solid \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| forged plate \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : solid \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| forged plate \|\| 20 °C to 371 °C (68 °F to 700 °F) YSC : solid \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : normalized \|\| tested at 538 °C (1000 °F) \|\| 50 h to 3,400 h SR : normalized \|\| tested at 593 °C (1100 °F) \|\| 35 h to 240 h SR : normalized \|\| Master curve (LMP) \|\| 538 °C to 593 °C (1000 °F to 1099 °F) SR : oil quenched \|\| tested at 538 °C (1000 °F) \|\| 35 h to 1,230 h SR : oil quenched \|\| tested at 593 °C (1100 °F) \|\| 30 h to 290 h FSN : UTS 862 MPa (125 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁷ cycles FSN : UTS 862 MPa (125 ksi) \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 2x10⁴ cycles to 2x10⁷ cycles FSN : UTS 862 MPa (125 ksi) \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 1x10⁴ cycles to 2x10⁷ cycles FSN : UTS 862 MPa (125 ksi) \|\| tested at 20 °C (68 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 5x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 1x10⁴ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 20 °C (68 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 316 °C (600 °F), R = -1, axial, maximum stress \|\| 5x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 316 °C (600 °F), R = 0, axial, maximum stress \|\| 5x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 316 °C (600 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 3x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 316 °C (600 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 3x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 3x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 427 °C (800 °F), R = 0, axial, maximum stress \|\| 3x10³ cycles to 2x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 427 °C (800 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 3x10³ cycles to 5x10⁶ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 427 °C (800 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 538 °C (1000 °F), R = 0, axial, maximum stress \|\| 3x10³ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 5x10³ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 538 °C (1000 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : UTS 1.03 GPa (150 ksi) \|\| tested at 538 °C (1000 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 8x10³ cycles to 2x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 8x10³ cycles to 2x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0.43, axial, maximum stress \|\| 5x10⁴ cycles to 2x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.3, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0, K_t = 3.3, axial, maximum stress \|\| 5x10³ cycles to 1x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0.43, K_t = 3.3, axial, maximum stress \|\| 6x10³ cycles to 1x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0.6, K_t = 3.3, axial, maximum stress \|\| 8x10³ cycles to 1x10⁷ cycles FSN : UTS 1.38 GPa (200 ksi) \|\| tested at 20 °C (68 °F), R = 0.74, K_t = 3.3, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0.25, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0.54, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = -1, K_t = 2, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0, K_t = 2, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0.54, K_t = 2, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = -1, K_t = 3, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0, K_t = 3, axial, maximum stress \|\| 8x10³ cycles to 1x10⁷ cycles FSN : UTS 1.79 GPa (260 ksi) \|\| tested at 20 °C (68 °F), R = 0.54, K_t = 3, axial, maximum stress \|\| 5x10³ cycles to 3x10⁶ cycles FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at -196.1 °C (-321.1 °F), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at -196.1 °C (-321.1 °F), R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles CRS : 0.5% total strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 80 h to 460 h CRS : 0.5% total strain, normalized \|\| tested at 593 °C (1100 °F) \|\| 2 h to 30 h CRS : 0.5% total strain, normalized \|\| Master curve (LMP) \|\| 538 °C to 593 °C (1000 °F to 1099 °F) CRS : 0.5% total strain, oil quenched \|\| tested at 538 °C (1000 °F) \|\| 15 h to 90 h CRS : 0.5% total strain, oil quenched \|\| tested at 593 °C (1100 °F) \|\| 2 h to 40 h CRS : 1% total strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,600 h CRS : 1% total strain, normalized \|\| tested at 593 °C (1100 °F) \|\| 5 h to 140 h CRS : 1% total strain, normalized \|\| Master curve (LMP) \|\| 538 °C to 593 °C (1000 °F to 1099 °F) CRS : 1% total strain, oil quenched \|\| tested at 538 °C (1000 °F) \|\| 10 h to 300 h CRS : 1% total strain, oil quenched \|\| tested at 593 °C (1100 °F) \|\| 2 h to 50 h IC : tested at 538 °C (1000 °F), plastic strain, normalized \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), plastic strain, normalized \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), plastic strain, normalized \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, oil quenched \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), plastic strain, oil quenched \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), plastic strain, oil quenched \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), plastic strain, oil quenched \|\| 30 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| cold-drawn, annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| cold-drawn, annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F)
4350 (UNS G43500) (AISI 4350) (SAE 4350) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : tempered at 150 °C (302 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.3 mm/mm strain SSC : tempered at 175 °C (347 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.3 mm/mm strain SSC : tempered at 200 °C (392 °F) \|\| tested at 20 °C (68 °F), 0.0033/s \|\| 0 to 0.27 mm/mm strain
4615 (UNS G46150) (AISI 4615) (SAE 4615) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) RHO : solid \|\| 20 °C to 200 °C (68 °F to 392 °F) SIGMA : solid \|\| 20 °C to 200 °C (68 °F to 392 °F)
20MnCr5 (UNS G48200/H51200) (WNr 1.7147/1.7149) (ISO/EN/DIN 20MnCr1/20MnCr5/20MnCrS5) (ASTM A29/A29M) (AISI 4820/5120) (AFNOR 20MC5) (GB & GB/T 20CrMn/20MnCrH)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain SSC : annealed \|\| tested at 200 °C (392 °F), unknown strain rate \|\| 0 to 0.13 mm/mm strain SSC : annealed \|\| tested at 400 °C (752 °F), unknown strain rate \|\| 0 to 0.67 mm/mm strain SSC : annealed \|\| tested at 600 °C (1112 °F), unknown strain rate \|\| 0 to 4.65x10^-³ mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
27MnCr5	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : before forging \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.148 mm/mm strain SSC : 18% cold reduction in cross-section \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.19 mm/mm strain SSC : 75% cold reduction in cross-section \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.28 mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
5115 (UNS G51150) (WNr 1.7131) (ISO/EN/DIN 16MnCr5/17Mn1Cr95) (AISI 5115) (AFNOR 16MC5) (GB & GB/T 15Cr/15CrMn/16MnCr/20Cr) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-received condition \|\| tested at 20 °C (68 °F), 0.0011/s \|\| 0 to 0.13 mm/mm strain SSC : 50% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 6 min intercritical anneal \|\| 0 to 0.152 mm/mm strain SSC : 50% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 8 min intercritical anneal \|\| 0 to 0.137 mm/mm strain SSC : 50% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 10 min intercritical anneal \|\| 0 to 0.133 mm/mm strain SSC : 50% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 12 min intercritical anneal \|\| 0 to 0.119 mm/mm strain SSC : 50% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 14 min intercritical anneal \|\| 0 to 0.119 mm/mm strain SSC : 80% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 6 min intercritical anneal \|\| 0 to 0.144 mm/mm strain SSC : 80% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 8 min intercritical anneal \|\| 0 to 0.133 mm/mm strain SSC : 80% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 10 min intercritical anneal \|\| 0 to 0.11 mm/mm strain SSC : 80% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 12 min intercritical anneal \|\| 0 to 0.93 mm/mm strain SSC : 80% cold reduced \|\| tested at 20 °C (68 °F), 0.0011/s, 14 min intercritical anneal \|\| 0 to 0.79 mm/mm strain
5132 (UNS G51320) (WNr 1.7033/1.7037/1.8401) (ISO/EN/DIN 34Cr4/34CrS4) (ASTM A331/A332/A505/A519) (AISI 5132) (SAE J404/J412/J770) (AFNOR 32C4) (GB & GB/T 30Cr/30CrMnSi) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) RHO : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SIGMA : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F)
5140 (UNS G51400) (WNr 1.7035/1.7039/1.7045) (ISO/EN/DIN 37Cr4/40Cr/40Cr1/41Cr4) (JIS SCR440) (ASTM A331/A332/A505/A519) (AISI 5140) (SAE J404/J412/J770) (AFNOR 42C4) (GB & GB/T 38CrA/40Cr) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| hardened & tempered \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SSC : 1.6/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.8 mm/mm strain SSC : 1.6/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.8 mm/mm strain SSC : 1.6/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.8 mm/mm strain SSC : 8/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.8 mm/mm strain SSC : 8/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.8 mm/mm strain SSC : 8/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.8 mm/mm strain SSC : 40/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.8 mm/mm strain SSC : 40/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.8 mm/mm strain SSC : 40/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.8 mm/mm strain FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 7x10⁴ cycles to 4x10⁸ cycles RHO : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F)
5160 (UNS G51600) (ASTM A29/A322/A331/A505/A519/A752/A829) (AISI 5160) (SAE J1397/J404/J412/J770) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : 880 °C (1616 °F), quenched, tempered at 375 °C (707 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 1x10³ cycles to 1x10⁶ cycles
100CrMnMoSi8 (WNr 1.3539)	D* : solid \|\| room temperature value FSN : Bainite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.07 microns, stress amplitude \|\| 2x10⁴ cycles to 4x10⁷ cycles FSN : Bainite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.32 microns, stress amplitude \|\| 3x10³ cycles to 4x10⁴ cycles FSN : Bainite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.85 microns, stress amplitude \|\| 3x10³ cycles to 1x10⁷ cycles FSN : Bainite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 1.16 microns, stress amplitude \|\| 2x10³ cycles to 3x10⁵ cycles FSN : Bainite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, average of all, stress amplitude \|\| 2x10³ cycles to 1x10⁷ cycles FSN : Martensite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.07 microns, stress amplitude \|\| 3x10⁴ cycles to 4x10⁷ cycles FSN : Martensite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, Ra of 0.85 microns, stress amplitude \|\| 2x10³ cycles to 2x10⁷ cycles FSN : Martensite \|\| tested at 20 °C (68 °F), R = -1, rotating beam, average of all, stress amplitude \|\| 2x10³ cycles to 2x10⁷ cycles
52100 (UNS G52986) (ISO/EN/DIN 100Cr6/103Cr1) (JIS G4805SUJ2) (AMS 6444) (AFNOR 100Cr6/100Cr6RR) (GB & GB/T Cr2/GCr15)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value SSC : bainitic condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.28 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.64 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.64 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.64 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.641 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.643 mm/mm strain SSCC : 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.645 mm/mm strain SSCC : 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.647 mm/mm strain SSCC : 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.645 mm/mm strain SSCC : 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.647 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.676 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.687 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.683 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.685 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.68 mm/mm strain SSCC : bainitic condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.56 mm/mm strain YSC : heat-treated to hardness HRC 59 \|\| 0.1% offset \|\| 204 °C to 427 °C (399 °F to 800 °F) YSC : heat-treated to hardness HRC 59 \|\| 0.2% offset \|\| 204 °C to 427 °C (399 °F to 800 °F) FSN : quenched from 735 °C (1355 °F) & tempered at 180 °C (356 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, ground & buffed surface, maximum stress \|\| 5x10³ cycles to 2x10⁹ cycles FSN : quenched from 835 °C (1535 °F) & tempered at 180 °C (356 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, ground surface, maximum stress \|\| 2x10³ cycles to 1.3x10⁵ cycles FSN : quenched from 835 °C (1535 °F) & tempered at 180 °C (356 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, electro-polished surface, maximum stress \|\| 5x10³ cycles to 3x10⁴ cycles FSN : quenched from 835 °C (1535 °F) & tempered at 180 °C (356 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, ground & electro-polished surface, maximum stress \|\| 1x10⁵ cycles to 1x10⁹ cycles FSN : quenched from 840 °C (1544 °F) & tempered at 210 °C (410 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, polished surface, maximum stress \|\| 3.8x10⁴ cycles to 1x10⁹ cycles FSN : quenched from 845 °C (1553 °F) & tempered at 180 °C (356 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4x10⁴ cycles to 4x10⁸ cycles FSN : quenched from 855 °C (1571 °F) & tempered at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), R = 0.1, bending, stress amplitude \|\| 1.8x10⁴ cycles to 7.1x10⁶ cycles FSN : bainitic condition \|\| tested at 20 °C (68 °F), R = -1, ultrasonic axial, stress amplitude \|\| 3.7x10⁵ cycles to 1x10⁹ cycles FSN : bainitic condition \|\| tested at 20 °C (68 °F), ultrasonic axial, constant min stress of -1.45 GPa (-210 ksi)stress amplitude \|\| 1.6x10⁵ cycles to 1x10⁹ cycles FSN : bainitic condition \|\| tested at 20 °C (68 °F), ultrasonic axial, constant min stress of -2.45 GPa (-355 ksi), stress amplitude \|\| 1.4x10⁵ cycles to 1x10⁹ cycles
6125 (AISI 6125) (SAE 6125)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
6140 (UNS G61400) (AISI 6140) (SAE J1249) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : 880 °C (1616 °F), quenched, tempered at 425 °C (797 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 3x10³ cycles to 1x10⁶ cycles
6150 (UNS G61500) (WNr 1.8159) (ISO/EN/DIN 50CrV2/50CrV4/51CrV4) (JIS G4801SUP10) (AISI 6150) (SAE 6150) (AFNOR 50CV4/50CrV4/51CrV4) (GB & GB/T 50CrVA) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : intercritical annealed at 740 °C (1364 °F) & quenched \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.13 mm/mm strain SSC : austenitized at 900 °C (1652 °F), quenched & tempered at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.157 mm/mm strain SSC : shot peened \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.165 mm/mm strain SSC : oil quenched from 860 °C (1580 °F) & tempered at 480 °C (896 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain FSN : quenched from at 850 °C (1562 °F) & tempered at 420 °C (788 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : as-received \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 1.3x10⁵ cycles to 2x10⁶ cycles FSN : shot peened \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 1.5x10⁵ cycles to 2x10⁶ cycles FSN : oil quenched from 860 °C (1580 °F) & tempered at 480 °C (896 °F) \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 7x10⁴ cycles to 2x10⁶ cycles
8620 (WNr 1.7321) (ISO/EN/DIN 20MoCr4/20NiCrMo2) (SAE 8620) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F)
8630 (UNS G86300) (WNr 1.6545) (ISO/EN/DIN 30NiCrMo2) (ASTM A322/A505) (AISI 8630) (AMS 5333) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| 827 MPa (120 ksi) 0.5 h at T \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| 827 MPa (120 ksi) 100 h at T \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| 1.10 GPa (160 ksi) 0.5 h at T \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| 1.10 GPa (160 ksi) 100 h at T \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : normalized \|\| -196 °C to 27 °C (-321 °F to 80 °F) YS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| tempered to 827 MPa (120 ksi) UTS \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| tempered to 862 MPa (125 ksi) UTS \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| tempered to 1.10 GPa (160 ksi) UTS \|\| 20 °C to 650 °C (68 °F to 1202 °F) YSC : quenched & tempered 1.59 mm (0.0625 inch) sheet \|\| tempered to 1.24 GPa (180 ksi) UTS \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : normalized \|\| -196 °C to 27 °C (-321 °F to 80 °F) FEN : axial loading \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 95 cycles to 2.55x10⁶ cycles FEN : axial loading \|\| tested at -46 °C (-50 °F), R = -1, total strain amplitude \|\| 90 cycles to 3.35x10⁶ cycles FSN : normalized at 899 °C (1650 °F), tempered at 649 °C (1200 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2.6x10⁴ cycles to 1x10⁷ cycles FSN : quenched from 843 °C (1550 °F), tempered at 649 °C (1200 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles
8640 (UNS G86400) (WNr 1.6546) (ISO/EN/DIN 40NiCrMo2) (ASTM A29/A331/A332/A506/A519/A752/A829) (AISI 8640) (AFNOR 40NCD2)	D* : solid \|\| room temperature value FSN : normalized at 899 °C (1650 °F), tempered at 649 °C (1200 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : quenched from 829 °C (1525 °F), tempered at 649 °C (1200 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles
S690QL (WNr 1.8928) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 5x10^-³ mm/mm strain SSC : as-received \|\| tested at 250 °C (482 °F), 0.002/s \|\| 0 to 0.42 mm/mm strain SSC : as-received \|\| tested at 350 °C (662 °F), 0.002/s \|\| 0 to 0.48 mm/mm strain SSC : as-received \|\| tested at 450 °C (842 °F), 0.002/s \|\| 0 to 0.47 mm/mm strain SSC : as-received \|\| tested at 500 °C (932 °F), 0.002/s \|\| 0 to 0.17 mm/mm strain SSC : as-received \|\| tested at 550 °C (1022 °F), 0.002/s \|\| 0 to 9.1x10^-³ mm/mm strain UTS : as-received \|\| 20 °C to 550 °C (68 °F to 1022 °F) YS : as-received \|\| 20 °C to 550 °C (68 °F to 1022 °F) %El : as-received \|\| 20 °C to 550 °C (68 °F to 1022 °F)
JIS G 4801 SUP12 (JIS G4801SUP12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : Heat A \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 8x10⁴ cycles to 1x10⁸ cycles FSN : Heat A \|\| tested at 20 °C (68 °F), R = 0, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : Heat D1 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : Heat D1 \|\| tested at 20 °C (68 °F), R = 0, rotating beam, maximum stress \|\| 8x10⁴ cycles to 1x10⁸ cycles
9255 (UNS G92550) (WNr 1.0904) (ISO/EN/DIN 55Si2Mn90/55Si7) (AISI 9255) (SAE J404/J412/J770) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 0 °C to 1300 °C (32 °F to 2372 °F) TD : solid \|\| 0 °C to 1300 °C (32 °F to 2372 °F) SH : solid \|\| 0 °C to 1300 °C (32 °F to 2372 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 5.56x10^-⁴/s \|\| 0 to 0.54 mm/mm strain SSC : austenitized, partitioned at 280 °C (536 °F) \|\| tested at 20 °C (68 °F), 5.56x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : austenitized, partitioned at 320 °C (608 °F) \|\| tested at 20 °C (68 °F), 5.56x10^-⁴/s \|\| 0 to 0.34 mm/mm strain SSC : austenitized, partitioned at 360 °C (680 °F) \|\| tested at 20 °C (68 °F), 5.56x10^-⁴/s \|\| 0 to 0.24 mm/mm strain SSC : austenitized, partitioned at 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 5.56x10^-⁴/s \|\| 0 to 0.42 mm/mm strain
9310 (UNS G93106/H93100) (WNr 1.6657) (ISO/EN/DIN 14NiCrMo13) (AISI 9310) (SAE 9310) (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) TD : solid \|\| 1227 °C to 1511 °C (2240 °F to 2752 °F) TD : liquid \|\| 1538 °C to 2377 °C (2800 °F to 4310 °F) SSCC : carburized \|\| tested at 85 °C (185 °F), 0.005/s \|\| 0 to 0.15 mm/mm strain SSCC : carburized \|\| tested at 110 °C (230 °F), 0.005/s \|\| 0 to 0.15 mm/mm strain SSCC : carburized \|\| tested at 160 °C (320 °F), 0.005/s \|\| 0 to 0.15 mm/mm strain SSCC : carburized \|\| tested at 232 °C (450 °F), 0.005/s \|\| 0 to 0.25 mm/mm strain SSCC : uncarburized, quenched from 900 °C (1652 °F) \|\| tested at 230 °C (446 °F), 0.005/s \|\| 0 to 0.3 mm/mm strain SSCC : forging temperatures, 1x10^-⁴/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.54 mm/mm strain SSCC : forging temperatures, 1x10^-⁴/s \|\| tested at 593 °C (1100 °F) \|\| 0 to 0.54 mm/mm strain SSCC : forging temperatures, 1x10^-⁴/s \|\| tested at 649 °C (1200 °F) \|\| 0 to 0.44 mm/mm strain SSCC : forging temperatures, 0.001/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.53 mm/mm strain SSCC : forging temperatures, 0.001/s \|\| tested at 593 °C (1100 °F) \|\| 0 to 0.52 mm/mm strain SSCC : forging temperatures, 0.001/s \|\| tested at 649 °C (1200 °F) \|\| 0 to 0.54 mm/mm strain SSCC : forging temperatures, 0.001/s \|\| tested at 704 °C (1300 °F) \|\| 0 to 0.53 mm/mm strain SSCC : forging temperatures, 0.001/s \|\| tested at 760 °C (1400 °F) \|\| 0 to 0.52 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.51 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 593 °C (1100 °F) \|\| 0 to 0.54 mm/mm strain SSCC : forging temperatures, 0.01/s \|\| tested at 649 °C (1200 °F) \|\| 0 to 0.53 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.51 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 593 °C (1100 °F) \|\| 0 to 0.52 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 649 °C (1200 °F) \|\| 0 to 0.51 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 704 °C (1300 °F) \|\| 0 to 0.54 mm/mm strain SSCC : forging temperatures, 0.1/s \|\| tested at 760 °C (1400 °F) \|\| 0 to 0.51 mm/mm strain FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.1, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : rotor shaft \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : shot peened \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles RHO : solid \|\| 1177 °C to 1511 °C (2150 °F to 2752 °F) RHO : liquid \|\| 1538 °C to 2377 °C (2800 °F to 4310 °F) SIGMA : solid \|\| 1177 °C to 1511 °C (2150 °F to 2752 °F) SIGMA : liquid \|\| 1538 °C to 2377 °C (2800 °F to 4310 °F)
20Cr	D* : solid \|\| room temperature value FSN : carburized \|\| tested at 20 °C (68 °F), R = 0.0, axial, stress amplitude \|\| 3x10⁴ cycles to 5.05x10⁷ cycles
51SiCr7 (WNr 1.7106) (ISO/EN/DIN 51SiCr7)	D* : solid \|\| room temperature value FSN : oil quenched from 985 °C (1805 °F), tempered at 450 °C (842 °F), shot peened \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 985 °C (1805 °F), tempered at 450 °C (842 °F), decarburized to 0.4 mm (0.0157 inch), shot peened \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 985 °C (1805 °F), tempered at 450 °C (842 °F), decarburized to 0.5 mm (0.0197 inch), shot peened \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : oil quenched from 850 °C (1562 °F), tempered at 500 °C (932 °F), decarburized to 0.1 mm (0.00394 inch), shot peened \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 4x10³ cycles to 1x10⁵ cycles
34CrNiMo6 (WNr 1.6582) (ISO/EN/DIN 34CrNiMo6) (JIS SNCM447) (SAE 4340) (AFNOR 35NCD6) (GB & GB/T 34CrNi3Mo/34CrNiMo/ZG34CrNiMo)	D* : solid \|\| room temperature value SSC : oil quenched & tempered \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.76 mm/mm strain UTS* : oil quenched & tempered \|\| tempered at 660 °C (1220 °F) \|\| room temperature value UTS* : oil quenched & tempered \|\| tempered at 570 °C (1058 °F) \|\| room temperature value YS* : oil quenched & tempered \|\| tempered at 660 °C (1220 °F) \|\| room temperature value YS* : oil quenched & tempered \|\| tempered at 570 °C (1058 °F) \|\| room temperature value %El* : oil quenched & tempered \|\| tempered at 660 °C (1220 °F) \|\| room temperature value %El* : oil quenched & tempered \|\| tempered at 570 °C (1058 °F) \|\| room temperature value FEN : oil quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 100 cycles to 5x10⁵ cycles FEN : oil quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude \|\| 100 cycles to 5x10⁵ cycles FEN : oil quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 100 cycles to 5x10⁵ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, ultrasonic axial, stress amplitude, Sander et. al. \|\| 4.8x10⁵ cycles to 1x10⁹ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, ultrasonic axial, in artificial seawater, stress amplitude, Wickmann et. al. \|\| 4x10⁵ cycles to 1x10⁹ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, machined, stress amplitude, Leguinagoicoa et. al. \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, polished, stress amplitude, Leguinagoicoa et. al. \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, shot peened, stress amplitude, Leguinagoicoa et. al. \|\| 1x10⁴ cycles to 1x10⁷ cycles
18CrNi8 (WNr 1.5920) (ISO/EN/DIN 18CrNi8)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : condition not specified \|\| primarily martensite \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : condition not specified, primarily martensite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.188 mm/mm strain SSC : condition not specified, primarily martensite \|\| tested at 400 °C (752 °F), unknown strain rate \|\| 0 to 0.137 mm/mm strain UTS : condition not specified \|\| primarily martensite \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : condition not specified \|\| primarily martensite \|\| 20 °C to 600 °C (68 °F to 1112 °F) FSN : condition not specified, primarily martensite \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 1x10⁸ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
26NiCrMoV14-5 (WNr 1.6957) (ISO/EN/DIN 26NiCrMoV145)	D* : solid \|\| room temperature value FEN : quenched & tempered, radial \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 400 cycles to 1x10⁶ cycles FEN : quenched & tempered, tangential \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 200 cycles to 1x10⁶ cycles
CrNiMoWMnV (ISO/EN/DIN CrNiMoWMnV)	D* : solid \|\| room temperature value SSCC : forging, 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.575 mm/mm strain SSCC : forging, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.575 mm/mm strain SSCC : forging, 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.573 mm/mm strain SSCC : forging, 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.575 mm/mm strain SSCC : forging, 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.566 mm/mm strain SSCC : forging, 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : forging, 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.575 mm/mm strain

A36 (UNS K02600) (ASTM A36) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : hot-rolled 12WF161 flange \|\| tested at 20 °C (68 °F), 8.75x10^-⁵/s \|\| 0 to 0.26 mm/mm strain SSC : hot-rolled 12WF161 flange \|\| tested at 431 °C (808 °F), 4.37x10^-⁵/s \|\| 0 to 0.146 mm/mm strain SSC : hot-rolled 12WF161 flange \|\| tested at 539 °C (1002 °F), 4.37x10^-⁵/s \|\| 0 to 0.8 mm/mm strain SSC : hot-rolled 12WF161 flange \|\| tested at 647 °C (1197 °F), 4.37x10^-⁵/s \|\| 0 to 0.65 mm/mm strain SSC : hot-rolled 12WF161 flange \|\| tested at 701 °C (1294 °F), 4.37x10^-⁵/s \|\| 0 to 0.89 mm/mm strain SSC : hot-rolled 14WF184 flange \|\| tested at 20 °C (68 °F), 8.75x10^-⁵/s \|\| 0 to 0.237 mm/mm strain SSC : hot-rolled 14WF184 flange \|\| tested at 431 °C (808 °F), 4.37x10^-⁵/s \|\| 0 to 0.48 mm/mm strain SSC : hot-rolled 14WF184 flange \|\| tested at 539 °C (1002 °F), 4.37x10^-⁵/s \|\| 0 to 0.19 mm/mm strain SSC : hot-rolled 14WF184 flange \|\| tested at 647 °C (1197 °F), 4.37x10^-⁵/s \|\| 0 to 0.14 mm/mm strain SSC : hot-rolled 14WF184 flange \|\| tested at 701 °C (1294 °F), 4.37x10^-⁵/s \|\| 0 to 0.9 mm/mm strain SSC : hot-rolled core truss seat channel \|\| tested at 20 °C (68 °F), 8.75x10^-⁵/s \|\| 0 to 0.23 mm/mm strain SSC : hot-rolled core truss seat channel \|\| tested at 431 °C (808 °F), 4.37x10^-⁵/s \|\| 0 to 0.19 mm/mm strain SSC : hot-rolled core truss seat channel \|\| tested at 539 °C (1002 °F), 4.37x10^-⁵/s \|\| 0 to 0.16 mm/mm strain SSC : hot-rolled core truss seat channel \|\| tested at 647 °C (1197 °F), 4.37x10^-⁵/s \|\| 0 to 0.13 mm/mm strain SSC : hot-rolled core truss seat channel \|\| tested at 701 °C (1294 °F), 4.37x10^-⁵/s \|\| 0 to 0.92 mm/mm strain SSC : average of hot-rolled materials \|\| tested at 20 °C (68 °F), 8.75x10^-⁵/s \|\| 0 to 0.266 mm/mm strain SSC : average of hot-rolled materials \|\| tested at 431 °C (808 °F), 4.37x10^-⁵/s \|\| 0 to 0.145 mm/mm strain SSC : average of hot-rolled materials \|\| tested at 539 °C (1002 °F), 4.37x10^-⁵/s \|\| 0 to 0.19 mm/mm strain SSC : average of hot-rolled materials \|\| tested at 647 °C (1197 °F), 4.37x10^-⁵/s \|\| 0 to 0.142 mm/mm strain SSC : average of hot-rolled materials \|\| tested at 701 °C (1294 °F), 4.37x10^-⁵/s \|\| 0 to 0.92 mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| normalized & tempered \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| annealed \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| normalized & tempered \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| annealed \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| normalized & tempered \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : annealed \|\| tested at 427 °C (800 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) FSN : axial fatigue \|\| tested at 20 °C (68 °F), R = 0, stress amplitude \|\| 6x10⁴ cycles to 1x10⁶ cycles CRS : 1% plastic strain, annealed \|\| tested at 427 °C (800 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 482 °C (900 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F)
A106 Grade B (UNS K03006) (WNr 1.0405) (ISO/EN/DIN P265GH) (JIS G3454STPG410) (ASTM A106B) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) UTS : grade B seamless pipe \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : grade B seamless pipe \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : grade B seamless pipe \|\| 20 °C to 538 °C (68 °F to 1000 °F) FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles FEN : in air \|\| tested at 288 °C (550 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles
A182 Grade F1 (WNr 1.5415) (ISO/EN/DIN 15Mo3/16Mo3) (SAE A182GradeF1) (AMS A182GradeF1) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) YS : hardened & tempered \|\| up to 60 mm (2.36 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : hardened & tempered \|\| 61 mm to 90 mm (2.4 inch to 3.54 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : hardened & tempered \|\| 91 mm to 150 mm (3.58 inch to 5.91 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) SR : hardened & tempered \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 460 °C (860 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| Master curve (LMP) \|\| 450 °C to 561 °C (842 °F to 1042 °F) FEN : axial loading \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 250 cycles to 1.4x10⁵ cycles FEN : bending loading \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 600 cycles to 7.8x10⁴ cycles CRS : 1% plastic strain, hardened & tempered \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 2x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 460 °C (860 °F) \|\| 1x10⁴ h to 2x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 2x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 2x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| Master curve (LMP) \|\| 450 °C to 521 °C (842 °F to 970 °F)
A182 Grade F11 (WNr 1.7335) (ISO/EN/DIN 13CrMo44/13CrMo45) (JIS SFVAF12) (SAE A182GradeF11) (AMS A182GradeF11) (GB & GB/T 12CrMo) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) YS : hardened & tempered \|\| up to 60 mm (2.36 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : hardened & tempered \|\| 61 mm to 90 mm (2.4 inch to 3.54 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : hardened & tempered \|\| 91 mm to 150 mm (3.58 inch to 5.91 inch) \|\| 20 °C to 500 °C (68 °F to 932 °F) SR : hardened & tempered \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 460 °C (860 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| Master curve (LMP) \|\| 450 °C to 560 °C (842 °F to 1040 °F) CRS : 1% plastic strain, hardened & tempered \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 460 °C (860 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hardened & tempered \|\| Master curve (LMP) \|\| 450 °C to 560 °C (842 °F to 1040 °F)
A201 Grade B (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) UTS : plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : plate \|\| 20 °C to 538 °C (68 °F to 1000 °F)
A302 Grade B (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : stress-relief anneal \|\| tested at 82 °C (180 °F), 4x10^-⁵/s \|\| 0 to 0.73 mm/mm strain FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles FEN : in air \|\| tested at 288 °C (550 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles
A283C (S235) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) Vis : semi-solid state \|\| 1486 °C to 1505 °C (2707 °F to 2741 °F) AV : semi-solid state \|\| tested at 1485 °C (2705 °F) \|\| 0.1/s to 20/s
A333 Grade 6 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles FEN : in air \|\| tested at 288 °C (550 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles
A441 (UNS K12211) (ASTM A441) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : as-received \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 0.003125/s \|\| 0 to 0.129 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 0.003125/s, average \|\| 0 to 0.1 mm/mm strain UTS : solid \|\| 20 °C to 1038 °C (68 °F to 1900 °F) YS : solid \|\| 20 °C to 1038 °C (68 °F to 1900 °F)
A500 Grade A (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| -196 °C to 982 °C (-321 °F to 1800 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : 8.33x10^-⁴/s \|\| tested at -120 °C (-184 °F) in liquid N₂ \|\| 0 to 0.15 mm/mm strain SSC : 8.33x10^-⁴/s \|\| tested at -72 °C (-98 °F) in dry-ice \|\| 0 to 0.15 mm/mm strain SSC : 8.33x10^-⁴/s \|\| tested at -60 °C (-76 °F) in liquid N₂ \|\| 0 to 0.15 mm/mm strain SSC : 8.33x10^-⁴/s \|\| tested at -50 °C (-58 °F) in dry-ice \|\| 0 to 0.15 mm/mm strain SSC : 8.33x10^-⁴/s \|\| tested at -40 °C (-40 °F) in liquid N₂ \|\| 0 to 0.15 mm/mm strain SSC : 8.33x10^-⁴/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.15 mm/mm strain UTS : solid \|\| -160 °C to 20 °C (-256 °F to 68 °F) YS : solid \|\| -160 °C to 20 °C (-256 °F to 68 °F) %El : solid \|\| -160 °C to 20 °C (-256 °F to 68 °F)
A508 Cl.3 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles FEN : in air \|\| tested at 288 °C (550 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles
A508 Gr.1A (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : 0.2 C, 0.3 Ni, 0.2 Cr, 0.06 Mo, 0.005 V (wt %) \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s \|\| 0 to 0.153 mm/mm strain SSC : 0.2 C, 0.3 Ni, 0.2 Cr, 0.06 Mo, 0.005 V (wt %) \|\| tested at 286 °C (547 °F), 5.2x10^-⁴/s \|\| 0 to 0.146 mm/mm strain SSC : 0.2 C, 0.3 Ni, 0.2 Cr, 0.1 Mo, 0.05 V (wt %) \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : 0.2 C, 0.3 Ni, 0.2 Cr, 0.1 Mo, 0.05 V (wt %) \|\| tested at 286 °C (547 °F), 5.2x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : 0.15 C, 0.4 Ni, 0.25 Cr, 0.1 Mo, 0.05 V (wt %) \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : 0.15 C, 0.4 Ni, 0.25 Cr, 0.1 Mo, 0.05 V (wt %) \|\| tested at 286 °C (547 °F), 5.2x10^-⁴/s \|\| 0 to 0.95 mm/mm strain SSC : 0.15 C, 0.37 Ni, 0.23 Cr, 0.08 Mo, 0.04 V (wt %) \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : 0.15 C, 0.37 Ni, 0.23 Cr, 0.08 Mo, 0.04 V (wt %) \|\| tested at 286 °C (547 °F), 5.2x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : average of all compositions \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : average of all compositions \|\| tested at 286 °C (547 °F), 5.2x10^-⁴/s \|\| 0 to 0.1 mm/mm strain
A514 (UNS K11872) (JIS ADC6) (ASTM G4A) (AFNOR A-G3T) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : as-received \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.1 mm/mm strain
A529 (WNr 1.0044) (JIS SS400) (ASTM A529) (AFNOR E28-2) (GB & GB/T Q225A/Q275Z) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : hot-rolled \|\| tested at 20 °C (68 °F), 0.0025/s \|\| 0 to 0.371 mm/mm strain SSC : hot-rolled \|\| tested at 100 °C (212 °F), 0.0025/s \|\| 0 to 0.264 mm/mm strain SSC : hot-rolled \|\| tested at 200 °C (392 °F), 0.0025/s \|\| 0 to 0.315 mm/mm strain SSC : hot-rolled \|\| tested at 300 °C (572 °F), 0.0025/s \|\| 0 to 0.135 mm/mm strain SSC : hot-rolled \|\| tested at 400 °C (752 °F), 0.0025/s \|\| 0 to 0.156 mm/mm strain SSC : hot-rolled \|\| tested at 500 °C (932 °F), 0.0025/s \|\| 0 to 0.145 mm/mm strain UTS : hot-rolled \|\| 20 °C to 602 °C (68 °F to 1115 °F) YS : hot-rolled \|\| 20 °C to 602 °C (68 °F to 1115 °F) %El : hot-rolled \|\| 20 °C to 602 °C (68 °F to 1115 °F)
A537 Gr 1 & 2 (S185) (UNS K02400) (ASTM A537) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : unknown condition \|\| tested at 20 °C (68 °F), 0.00333/s \|\| 0 to 0.73 mm/mm strain SSC : unknown condition \|\| tested at 20 °C (68 °F), 0.00333/s, extended strain range \|\| 0 to 1.2 mm/mm strain UTS : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 100 mm to 150 mm (3.94 inch to 5.91 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 100 mm to 150 mm (3.94 inch to 5.91 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : Class 1, UTS of 483 MPa (70 ksi) to 586 MPa (85 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm (2.56 inch) and less \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 65 mm to 100 mm (2.56 inch to 3.94 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : Class 2, UTS of 552 MPa (80 ksi) to 690 MPa (100 ksi) \|\| 100 mm to 150 mm (3.94 inch to 5.91 inch) \|\| 20 °C to 650 °C (68 °F to 1202 °F) FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 5 cycles to 1x10⁵ cycles
A533 Grade B (WNr 1.7703) (ISO/EN/DIN 13CrMoV9-10) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1190 °C (68 °F to 2174 °F) DLL : solid \|\| 20 °C to 1190 °C (68 °F to 2174 °F) MTE : solid \|\| 20 °C to 1190 °C (68 °F to 2174 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) UTS : Grade B1 \|\| 20 °C to 1204 °C (68 °F to 2199 °F) SR : Grade B1 \|\| tested at 627 °C (1160 °F) \|\| 9 h to 240 h SR : Grade B1 \|\| tested at 727 °C (1340 °F) \|\| 3 h to 14 h SR : Grade B1 \|\| tested at 777 °C (1430 °F) \|\| 15 h to 330 h SR : Grade B1 \|\| tested at 877 °C (1610 °F) \|\| 3 h to 72 h SR : Grade B1 \|\| tested at 977 °C (1790 °F) \|\| 0.3 h to 70 h SR : Grade B1 \|\| tested at 1100 °C (2012 °F) \|\| 0.4 h to 57 h FEN : in air \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles FEN : in air \|\| tested at 288 °C (550 °F), R = -1, total strain amplitude \|\| 100 cycles to 2x10⁸ cycles
A572 Grade 50 (WNr 1.0045) (JIS SM490A/SS490) (ASTM A572) (AFNOR E36-2) (GB & GB/T Q345B/Q345C) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hot-rolled \|\| 20 °C to 500 °C (68 °F to 932 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 8x10^-⁴/s, Sajid et. al. \|\| 0 to 2 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, Kodur et. al. \|\| 0 to 0.126 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), unknown strain rate, Sajid & Kodur averaged \|\| 0 to 0.126 mm/mm strain SSC : as-received \|\| tested at 200 °C (392 °F), 6.9x10^-⁵/s \|\| 0 to 0.57 mm/mm strain SSC : as-received \|\| tested at 400 °C (752 °F), 6.9x10^-⁵/s \|\| 0 to 0.63 mm/mm strain SSC : as-received \|\| tested at 500 °C (932 °F), 6.9x10^-⁵/s \|\| 0 to 0.28 mm/mm strain SSC : as-received \|\| tested at 600 °C (1112 °F), 6.9x10^-⁵/s \|\| 0 to 0.35 mm/mm strain SSC : as-received \|\| tested at 700 °C (1292 °F), 6.9x10^-⁵/s \|\| 0 to 0.13 mm/mm strain SSC : as-received \|\| tested at 800 °C (1472 °F), 6.9x10^-⁵/s \|\| 0 to 0.28 mm/mm strain SSC : 900 °C (1652 °F) for 1 h, air cooled \|\| tested at 20 °C (68 °F), 8x10^-⁴/s \|\| 0 to 1.26 mm/mm strain SSC : 1000 °C (1832 °F) for 1 h, air cooled \|\| tested at 20 °C (68 °F), 8x10^-⁴/s \|\| 0 to 1.26 mm/mm strain SSC : 800 °C (1472 °F) for 1 h, water cooled \|\| tested at 20 °C (68 °F), 8x10^-⁴/s \|\| 0 to 2 mm/mm strain SSC : 900 °C (1652 °F) for 1 h, water cooled \|\| tested at 20 °C (68 °F), 8x10^-⁴/s \|\| 0 to 2 mm/mm strain SSC : 1000 °C (1832 °F) for 1 h, water cooled \|\| tested at 20 °C (68 °F), 8x10^-⁴/s \|\| 0 to 2 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 400 °C (752 °F) \|\| 0 to 0.6 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 500 °C (932 °F) \|\| 0 to 0.93 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 600 °C (1112 °F) \|\| 0 to 0.78 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 700 °C (1292 °F) \|\| 0 to 0.78 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 800 °C (1472 °F) \|\| 0 to 0.149 mm/mm strain SSC : high temperature hold, air cooled \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 1000 °C (1832 °F) \|\| 0 to 0.2 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 200 °C (392 °F) \|\| 0 to 0.56 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 400 °C (752 °F) \|\| 0 to 0.73 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 500 °C (932 °F) \|\| 0 to 0.83 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 600 °C (1112 °F) \|\| 0 to 0.11 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 700 °C (1292 °F) \|\| 0 to 0.94 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 800 °C (1472 °F) \|\| 0 to 0.45 mm/mm strain SSC : high temperature hold, water quenched \|\| tested at 20 °C (68 °F), 6.9x10^-⁵/s, held at 1000 °C (1832 °F) \|\| 0 to 0.36 mm/mm strain UTS : as-received \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : as-received \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : as-received \|\| 20 °C to 800 °C (68 °F to 1472 °F) CRS : 1.5% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.68 h to 1.3 h CRS : 1.5% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 0.11 h to 0.89 h CRS : 1.5% plastic strain \|\| Master curve (LMP) \|\| 650 °C to 701 °C (1202 °F to 1294 °F) CRS : 2% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.15 h to 2.17 h CRS : 2% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 0.25 h to 2.73 h CRS : 2% plastic strain \|\| Master curve (LMP) \|\| 650 °C to 701 °C (1202 °F to 1294 °F) CRS : 2.5% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.19 h to 3 h CRS : 2.5% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 0.33 h to 5.69 h CRS : 2.5% plastic strain \|\| Master curve (LMP) \|\| 650 °C to 701 °C (1202 °F to 1294 °F) CRS : 3% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.22 h to 3.6 h CRS : 4% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.26 h to 4.31 h CRS : 5% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.29 h to 4.67 h IC : tested at 650 °C (1202 °F), plastic strain, as-received \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, as-received \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, as-received \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, as-received \|\| 0.1 h \|\| 0 to 0.25 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, as-received \|\| 1 h \|\| 0 to 0.25 mm/mm strain
A572 Grade 65 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| hot-rolled \|\| 20 °C to 500 °C (68 °F to 932 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 0.003125/s \|\| 0 to 0.125 mm/mm strain
A992 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 7.87x10^-⁴/s \|\| 0 to 0.293 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 7.87x10^-⁴/s, extended strain range \|\| 0 to 2 mm/mm strain
A633 Grade C (UNS K12000) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F)
ASTM A723 (UNS K25550) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 575 °C (68 °F to 1067 °F) FEN : grade 1 class 4 \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 15 cycles to 2x10⁵ cycles

500C rebar (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : TEMPCORE \|\| tested at 20 °C (68 °F), 0.00835/s \|\| 0 to 0.152 mm/mm strain
BS 460B (steel reinforcing bar) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) FEN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 7 cycles to 60 cycles FEN : as-received \|\| tested at 20 °C (68 °F), R = -0.5, axial, total strain amplitude \|\| 16 cycles to 54 cycles FEN : as-received \|\| tested at 20 °C (68 °F), R = 0, axial, total strain amplitude \|\| 37 cycles to 220 cycles
BS B500B (steel reinforcing bar) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) FEN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 5 cycles to 38 cycles FEN : as-received \|\| tested at 20 °C (68 °F), R = -0.5, axial, total strain amplitude \|\| 12 cycles to 51 cycles FEN : as-received \|\| tested at 20 °C (68 °F), R = 0, axial, total strain amplitude \|\| 37 cycles to 130 cycles
B500SP (steel reinforcing bar) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) Vis : semi-solid state \|\| 1452 °C to 1473 °C (2645 °F to 2683 °F) AV : semi-solid state \|\| tested at 1456 °C (2653 °F) \|\| 0.15/s to 20/s AV : semi-solid state \|\| tested at 1460 °C (2660 °F) \|\| 0.15/s to 20/s AV : semi-solid state \|\| tested at 1462 °C (2664 °F) \|\| 0.15/s to 20/s AV : semi-solid state \|\| tested at 1466 °C (2671 °F) \|\| 0.15/s to 20/s AV : semi-solid state \|\| tested at 1468 °C (2674 °F) \|\| 0.15/s to 20/s
A881/A881M rebar (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : average of samples from 10 different suppliers \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.33 mm/mm strain
Grade 60 (420 MPa) rebar (ASTM A615/A615M)	D* : solid \|\| room temperature value SSC : as-received \|\| tested at 20 °C (68 °F), 4.17x10^-⁴/s \|\| 0 to 0.31 mm/mm strain
Grade 550 rebar (ASTM A615/A615M)	D* : solid \|\| room temperature value SSC : as-received \|\| tested at 20 °C (68 °F), 4.17x10^-⁴/s \|\| 0 to 0.23 mm/mm strain
Grade 650 rebar (ASTM A615/A615M)	D* : solid \|\| room temperature value SSC : as-received \|\| tested at 20 °C (68 °F), 4.17x10^-⁴/s \|\| 0 to 0.17 mm/mm strain
Grade 700 rebar (ASTM A615/A615M)	D* : solid \|\| room temperature value SSC : as-received \|\| tested at 20 °C (68 °F), 4.17x10^-⁴/s \|\| 0 to 0.155 mm/mm strain

P690Q (WNr 1.8879) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : quenched & tempered \|\| tested at -196.1 °C (-321.1 °F), unknown strain rate \|\| 0 to 0.12 mm/mm strain SSC : quenched & tempered \|\| tested at -117 °C (-179 °F), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : quenched & tempered \|\| tested at -94 °C (-137 °F), unknown strain rate \|\| 0 to 0.67 mm/mm strain
10GN2MFA (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC* : solid \|\| as-received \|\| room temperature value TC* : solid \|\| annealed at 900 °C (1652 °F), 10 micron grain size \|\| room temperature value TC* : solid \|\| annealed at 1000 °C (1832 °F), 25 micron grain size \|\| room temperature value TC* : solid \|\| annealed at 1100 °C (2012 °F), 90 micron grain size \|\| room temperature value TD* : solid \|\| as-received \|\| room temperature value TD* : solid \|\| annealed at 900 °C (1652 °F), 10 micron grain size \|\| room temperature value TD* : solid \|\| annealed at 1000 °C (1832 °F), 25 micron grain size \|\| room temperature value TD* : solid \|\| annealed at 1100 °C (2012 °F), 90 micron grain size \|\| room temperature value SH* : solid \|\| as-received \|\| room temperature value SH* : solid \|\| annealed at 900 °C (1652 °F), 10 micron grain size \|\| room temperature value SH* : solid \|\| annealed at 1000 °C (1832 °F), 25 micron grain size \|\| room temperature value SH* : solid \|\| annealed at 1100 °C (2012 °F), 90 micron grain size \|\| room temperature value UTS : unknown condition \|\| -120 °C to 20 °C (-184 °F to 68 °F) YS : unknown condition \|\| -120 °C to 20 °C (-184 °F to 68 °F) %El : unknown condition \|\| -120 °C to 20 °C (-184 °F to 68 °F) FEN : unknown condition \|\| tested at 20 °C (68 °F), R = -1, 0.03 Hz, axial, total strain amplitude \|\| 500 cycles to 1.7x10³ cycles FEN : unknown condition \|\| tested at 20 °C (68 °F), R = -1, 0.2 Hz, axial, total strain amplitude \|\| 600 cycles to 2.5x10³ cycles FSN : unknown condition \|\| tested at 20 °C (68 °F), R = -1, 0.03 Hz, axial, maximum stress \|\| 500 cycles to 1.7x10³ cycles FSN : unknown condition \|\| tested at 20 °C (68 °F), R = -1, 0.2 Hz, axial, maximum stress \|\| 600 cycles to 2.5x10³ cycles FSN : unknown condition \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : unknown condition \|\| tested at -50 °C (-58 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : unknown condition \|\| tested at -70 °C (-94 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : unknown condition \|\| tested at -120 °C (-184 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles
JIS G4053-SMn443 (JIS G4053SMn443) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = 0, rotating beam, maximum stress \|\| 4x10⁴ cycles to 1x10⁸ cycles
P500QL2 (WNr 1.8865) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) YS : vacuum treated, quenched & tempered \|\| 30 mm (1.18 inch) thick \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : vacuum treated, quenched & tempered \|\| 25.4 mm (1 inch) thick \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : vacuum treated, quenched & tempered \|\| 80 mm (3.15 inch) thick \|\| 20 °C to 400 °C (68 °F to 752 °F)
DIROS 500 S (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) UTS : vacuum treated, quenched & tempered \|\| 41 mm to 132 mm (1.61 inch to 5.2 inch) thick plate \|\| 20 °C to 550 °C (68 °F to 1022 °F) YS : vacuum treated, quenched & tempered \|\| 41 mm to 132 mm (1.61 inch to 5.2 inch) thick plate \|\| 20 °C to 550 °C (68 °F to 1022 °F)
Fe - 2 Mn - 1.3 Si - 0.7 Cr - 0.4 C (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSCC : base alloy, 0.1/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : base alloy, 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.56 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.52 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.6 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy, 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.54 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.56 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.54 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.57 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.56 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.58 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.57 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.59 mm/mm strain SSCC : base alloy with 0.3 Mo and 0.03 Nb additions, 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.59 mm/mm strain
Strenx 700 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) DLL : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) MTE : solid \|\| -273 °C to 687 °C (-460 °F to 1268 °F) CTE : solid \|\| -182 °C to 687 °C (-296 °F to 1268 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : cold-formed, as-received \|\| tested at 20 °C (68 °F), R = -1, rotating beam, stress amplitude \|\| 3.3x10⁶ cycles to unknown strain rate cycles FSN : cold-formed, as-received \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 4x10⁴ cycles to 1x10⁷ cycles
Strenx 960 Plus (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : hot-rolled, quenched & tempered 8 mm (0.315 inch) thick strip \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, parallel to the rolling direction \|\| 0 to 1 mm/mm strain SSC : hot-rolled, quenched & tempered 8 mm (0.315 inch) thick strip \|\| tested at -40 °C (-40 °F), 5x10^-⁴/s, parallel to the rolling direction \|\| 0 to 1 mm/mm strain SSC : hot-rolled, quenched & tempered 8 mm (0.315 inch) thick strip \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, 45 degrees to the rolling direction \|\| 0 to 0.9 mm/mm strain SSC : hot-rolled, quenched & tempered 8 mm (0.315 inch) thick strip \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, 90 degrees to the rolling direction \|\| 0 to 0.86 mm/mm strain
Docol S355 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : 2 mm (0.0787 inch) thick sheet, longitudinal \|\| tested at 20 °C (68 °F), as-received, 0.001/s \|\| 0 to 0.21 mm/mm strain SSC : 2 mm (0.0787 inch) thick sheet, longitudinal \|\| tested at 20 °C (68 °F), 700 °C (1292 °F) for 10 min, 0.001/s \|\| 0 to 0.124 mm/mm strain
D38MSV5S	D* : solid \|\| room temperature value FSN : ultrasonic at 20 kHz \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 1x10⁴ cycles to 1.1x10⁹ cycles

1 Cr - 0.25 Mo (wt %) (WNr 1.7335) (ISO/EN/DIN 15CrMo5)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) G : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) v : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) K : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F)
1 Cr - 0.5 Mo (wt %) (UNS K11562) (ISO/EN/DIN 13CrMo44)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) G : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) v : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) K : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TD : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) FEN : tempered \|\| tested at 535 °C (995 °F), R = -1, axial, plastic strain range \|\| 400 cycles to 4.5x10³ cycles
1 Cr - 1 Mo - 0.1 V (wt %) (AISI 604)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) G : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) v : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) K : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) UTS : hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : rolled bar \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : rolled bar \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : rolled bar \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : rolled bar \|\| Master curve (LMP) \|\| 482 °C to 594 °C (899 °F to 1101 °F)
1 Cr - 1 Mo - 0.25 V (wt %)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) G : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) v : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) K : solid \|\| 20 °C to 677 °C (68 °F to 1250 °F) SSC : not aged \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : aged at 630 °C (1166 °F) \|\| tested at 20 °C (68 °F), unknown strain rate, aged 453 h \|\| 0 to 0.2 mm/mm strain SSC : aged at 630 °C (1166 °F) \|\| tested at 20 °C (68 °F), unknown strain rate, aged 933 h \|\| 0 to 0.25 mm/mm strain SSC : aged at 630 °C (1166 °F) \|\| tested at 20 °C (68 °F), unknown strain rate, aged 1820 h \|\| 0 to 0.25 mm/mm strain
Temper Tough alloy (UNS K63835) (AMS 6482)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F)
PremoMet alloy (UNS K63835) (AMS 6482)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : heat-treated 19 mm (0.75 inch) bar \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles
JIS G4105 SCM435 (JIS G4105SCM435)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) G : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) v : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) K : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = 0, rotating beam, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles
28CrMoV5-8 (ISO/EN/DIN 28CrMoV5-8)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC* : solid \|\| room temperature value UTS : hardened at 880 °C (1616 °F) & tempered at 660 °C (1220 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS* : oil quenched from 1000 °C (1832 °F), tempered at 710 °C (1310 °F) \|\| room temperature value YS : hardened at 880 °C (1616 °F) & tempered at 660 °C (1220 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS* : oil quenched from 1000 °C (1832 °F), tempered at 710 °C (1310 °F) \|\| room temperature value %El : hardened at 880 °C (1616 °F) & tempered at 660 °C (1220 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El* : oil quenched from 1000 °C (1832 °F), tempered at 710 °C (1310 °F) \|\| room temperature value SR : solid \|\| tested at 550 °C (1022 °F) \|\| 100 h to 1,000 h FEN : axial test \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 200 cycles to 1x10⁵ cycles FEN : axial test \|\| tested at 200 °C (392 °F), R = -1, axial, total strain amplitude \|\| 200 cycles to 1x10⁵ cycles FEN : axial test \|\| tested at 400 °C (752 °F), R = -1, axial, total strain amplitude \|\| 200 cycles to 1x10⁵ cycles FEN : axial test \|\| tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude \|\| 200 cycles to 1x10⁵ cycles FSN : quenched & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1 cycles to 300 cycles CRS : 1% plastic strain \|\| tested at 550 °C (1022 °F) \|\| 100 h to 1,000 h
34CrNi3MoV (GB & GB/T 34CrNi3MoV)	SSCC : 0.01/s, forging stock \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s, forging stock \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s, forging stock \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s, forging stock \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s, forging stock \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s, forging stock \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s, forging stock \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s, forging stock \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s, forging stock \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s, forging stock \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s, forging stock \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s, forging stock \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s, forging stock \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s, forging stock \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s, forging stock \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s, forging stock \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s, forging stock \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s, forging stock \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s, forging stock \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s, forging stock \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain
2.25 Cr - 1 Mo (ASTM A542) (UNS K21590) (WNr 1.7383) (ISO/EN/DIN 11CrMo9-10) (ASTM A182/A199/A200/A213/A234/A335/A336/A369/A387/A541/A542)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) G : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) v : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) K : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TD : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 0.55 mm/mm strain SSC : annealed \|\| tested at 302 °C (575 °F), 1.67x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : annealed \|\| tested at 399 °C (750 °F), 1.67x10^-⁴/s \|\| 0 to 0.56 mm/mm strain SSC : annealed \|\| tested at 482 °C (900 °F), 1.67x10^-⁴/s \|\| 0 to 0.56 mm/mm strain SSC : annealed \|\| tested at 566 °C (1050 °F), 1.67x10^-⁴/s \|\| 0 to 0.57 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 1.67x10^-⁴/s \|\| 0 to 0.67 mm/mm strain SSC : normalized & tempered \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 0.55 mm/mm strain SSC : normalized & tempered \|\| tested at 302 °C (575 °F), 1.67x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : normalized & tempered \|\| tested at 399 °C (750 °F), 1.67x10^-⁴/s \|\| 0 to 0.55 mm/mm strain SSC : normalized & tempered \|\| tested at 482 °C (900 °F), 1.67x10^-⁴/s \|\| 0 to 0.56 mm/mm strain SSC : normalized & tempered \|\| tested at 566 °C (1050 °F), 1.67x10^-⁴/s \|\| 0 to 0.56 mm/mm strain SSC : normalized & tempered \|\| tested at 649 °C (1200 °F), 1.67x10^-⁴/s \|\| 0 to 0.67 mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| hardened & tempered \|\| 20 °C to 550 °C (68 °F to 1022 °F) YS : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| hardened & tempered \|\| 20 °C to 550 °C (68 °F to 1022 °F) %El : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) SR : normalized & tempered \|\| tested at 450 °C (842 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 475 °C (887 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 500 °C (932 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 525 °C (977 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 550 °C (1022 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 575 °C (1067 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 600 °C (1112 °F) \|\| 100 h to 3x10⁵ h SR : normalized & tempered \|\| tested at 625 °C (1157 °F) \|\| 100 h to 1x10⁵ h SR : normalized & tempered \|\| tested at 650 °C (1202 °F) \|\| 100 h to 3x10⁴ h SR : normalized & tempered \|\| Master curve (LMP) \|\| 450 °C to 651 °C (842 °F to 1204 °F) SR : annealed \|\| tested at 454 °C (850 °F) \|\| 50 h to 1,500 h SR : annealed \|\| tested at 510 °C (950 °F) \|\| 50 h to 3,000 h SR : annealed \|\| tested at 566 °C (1050 °F) \|\| 40 h to 2,000 h SR : annealed \|\| Master curve (LMP) \|\| 454 °C to 566 °C (849 °F to 1051 °F) FEN : in air \|\| tested at 371 °C (700 °F), R = -1, total strain range \|\| 1x10³ cycles to 4.3x10⁵ cycles FEN : in air \|\| tested at 427 °C (800 °F), R = -1, total strain range \|\| 1x10³ cycles to 1.4x10⁶ cycles FEN : in air \|\| tested at 538 °C (1000 °F), R = -1, total strain range \|\| 350 cycles to 9x10⁵ cycles FEN : in sodium \|\| tested at 538 °C (1000 °F), R = -1, total strain range \|\| 1x10³ cycles to 4.3x10⁵ cycles CRS : 0.5% plastic strain, normalized & tempered \|\| tested at 482 °C (900 °F) \|\| 1 h to 1x10⁵ h CRS : 0.5% plastic strain, normalized & tempered \|\| tested at 510 °C (950 °F) \|\| 1 h to 1x10⁵ h CRS : 0.5% plastic strain, normalized & tempered \|\| tested at 538 °C (1000 °F) \|\| 1 h to 1x10⁵ h CRS : 0.5% plastic strain, normalized & tempered \|\| tested at 566 °C (1050 °F) \|\| 1 h to 1x10⁵ h CRS : 0.5% plastic strain, normalized & tempered \|\| Master curve (LMP) \|\| 482 °C to 566 °C (899 °F to 1051 °F) CRS : 1% plastic strain, normalized & tempered \|\| tested at 482 °C (900 °F) \|\| 1 h to 1x10⁵ h CRS : 1% plastic strain, normalized & tempered \|\| tested at 510 °C (950 °F) \|\| 1 h to 1x10⁵ h CRS : 1% plastic strain, normalized & tempered \|\| tested at 538 °C (1000 °F) \|\| 1 h to 1x10⁵ h CRS : 1% plastic strain, normalized & tempered \|\| tested at 566 °C (1050 °F) \|\| 1 h to 1x10⁵ h CRS : 1% plastic strain, normalized & tempered \|\| Master curve (LMP) \|\| 482 °C to 566 °C (899 °F to 1051 °F) IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, normalized & tempered \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, normalized & tempered \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized & tempered \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 566 °C (1050 °F), plastic strain, normalized & tempered \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain
17-22A (UNS K14675) (AISI 601) (AMS 6304)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) G : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) v : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) K : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : hardened & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : annealed \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 426 °C to 594 °C (799 °F to 1101 °F)
17-22AS (UNS K23015) (AISI 602) (AMS 6302/6385/6458)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| normalized & tempered to 235HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| normalized & tempered to 285HB \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| normalized & tempered to 320HB \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| quenched & tempered to 262HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| quenched & tempered to 420HB \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| quenched & tempered to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) YS : solid \|\| normalized & tempered to 235HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| normalized & tempered to 285HB \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| normalized & tempered to 320HB \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| quenched & tempered to 262HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| quenched & tempered to 420HB \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| quenched & tempered to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : solid \|\| normalized & tempered to 235HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| normalized & tempered to 285HB \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| normalized & tempered to 320HB \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| quenched & tempered to 262HB \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| quenched & tempered to 420HB \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| quenched & tempered to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) SR : normalized & tempered at 649 °C (1200 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 649 °C (1200 °F) \|\| tested at 566 °C (1050 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 649 °C (1200 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 649 °C (1200 °F) \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) SR : normalized & tempered at 704 °C (1300 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 704 °C (1300 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 704 °C (1300 °F) \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) SR : normalized & tempered at 732 °C (1350 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 732 °C (1350 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 732 °C (1350 °F) \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) SR : normalized & tempered at 1066 °C (1950 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 1066 °C (1950 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : normalized & tempered at 1066 °C (1950 °F) \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) SR : oil quenched & tempered at 649 °C (1200 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h CRS : 0.2% plastic strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, normalized \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h IC : tested at 538 °C (1000 °F), plastic strain, normalized \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, normalized \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
17-22AV (UNS K22770) (AISI 603) (AMS 6303/6436)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| quenched & tempered at 427 °C (800 °F) to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) UTS : solid \|\| quenched & tempered at 538 °C (1000 °F) to 444HB \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| normalized & tempered at 649 °C (1200 °F) to 341HB \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| quenched & tempered at 427 °C (800 °F) to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) YS : solid \|\| quenched & tempered at 538 °C (1000 °F) to 444HB \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| normalized & tempered at 649 °C (1200 °F) to 341HB \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| quenched & tempered at 427 °C (800 °F) to 444HB \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : solid \|\| quenched & tempered at 538 °C (1000 °F) to 444HB \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| normalized & tempered at 649 °C (1200 °F) to 341HB \|\| 20 °C to 704 °C (68 °F to 1299 °F)
D6a/D6ac (UNS K24728) (ASTM A355/A579) (AMS 5027/5028/6431/6438/6439) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SSC : B-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSC : B-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : B-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : B-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain UTS : normalized at 899 °C (1650 °F) & tempered \|\| tempered 28C (50F) above the test temperature \|\| 20 °C to 595 °C (68 °F to 1103 °F) UTS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 899 °C (1650 °F) & tempered \|\| tempered 28C (50F) above the test temperature \|\| 20 °C to 595 °C (68 °F to 1103 °F) YS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 899 °C (1650 °F) & tempered \|\| tempered 28C (50F) above the test temperature \|\| 20 °C to 595 °C (68 °F to 1103 °F) %El : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 927 °C (1700 °F), austenitized at 899 °C (1650 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) SR : quenched & tempered \|\| tested at 232 °C (450 °F) \|\| 0.4 h to 120 h SR : quenched & tempered \|\| tested at 288 °C (550 °F) \|\| 0.01 h to 70 h SR : quenched & tempered \|\| Master curve (LMP) \|\| 232 °C to 288 °C (449 °F to 550 °F) FSN : quenched & tempered \|\| tested at 24 °C (75 °F), R = 0, axial, maximum stress \|\| 2.6x10⁴ cycles to 1x10⁶ cycles FSN : quenched & tempered \|\| tested at 24 °C (75 °F), R = -1, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : quenched & tempered \|\| tested at 232 °C (450 °F), R = 0, axial, maximum stress \|\| 2.3x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 232 °C (450 °F), R = -1, axial, maximum stress \|\| 4.6x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 288 °C (550 °F), R = 0, axial, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁸ cycles FSN : quenched & tempered \|\| tested at 288 °C (550 °F), R = -1, axial, maximum stress \|\| 1.9x10⁴ cycles to 1x10⁸ cycles RHO* : solid \|\| heat-treated \|\| room temperature value SIGMA*: solid \|\| heat-treated \|\| room temperature value RPB : heat-treated \|\| tested at 20 °C (68 °F) AP : heat-treated \|\| tested at 20 °C (68 °F) BH : heat-treated \|\| tested at 20 °C (68 °F) HB : heat-treated \|\| tested at 20 °C (68 °F)
SIQUAL 5122 (WNr 1.5122) (ISO/EN/DIN 37MnSi5)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value
SIQUAL 5752 (WNr 1.5752) (ISO/EN/DIN 14NiCr14/15NiCr13) (AISI 3310/3415) (SAE 3310/3415)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SIQUAL 5919 (WNr 1.5919) (ISO/EN/DIN 15CrNi6) (AISI 3115) (SAE 3115)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value
SIQUAL 6587 (WNr 1.6587) (ISO/EN/DIN 17CrNiMo6/17CrNiMo7/18CrNiMo7-6) (SAE 4820) (GB & GB/T 17Cr2Ni2Mo)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.787 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.787 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.788 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.785 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.788 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.788 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.784 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.787 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.786 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.787 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.788 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.786 mm/mm strain SSCC : 5/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.771 mm/mm strain SSCC : 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.779 mm/mm strain SSCC : 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.764 mm/mm strain SSCC : 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.773 mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SIQUAL 7016 (WNr 1.7016) (ISO/EN/DIN 17Cr3) (SAE 4615/5117)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SIQUAL 7131 (WNr 1.7131) (ISO/EN/DIN 16MnCr5/17Mn1Cr95) (SAE 5115/5117) (AFNOR 16MC5) (GB & GB/T 15CrMn/16MnCr)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SIQUAL 7147 (WNr 1.7147) (ISO/EN/DIN 20MnCr5) (JIS SMnC420H) (SAE 4820) (AFNOR 20MC5) (GB & GB/T 20CrMn/20CrMnTi/20MnCr)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SIQUAL 7264 (WNr 1.7264) (ISO/EN/DIN 20MnCr5)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F)
SIQUAL 8509 (WNr 1.8509) (ISO/EN/DIN 41CrAlMo7/41CrAlMo7-10) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) DLL : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) MTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) CTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F)
SIQUAL 8519 (WNr 1.8519) (ISO/EN/DIN 31CrMoV9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) DLL : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) MTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) CTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F)
SIQUAL 8550 (WNr 1.8550) (ISO/EN/DIN 34CrAlNi7/34CrAlNi7-10) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) DLL : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) MTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) CTE : solid \|\| -191 °C to 500 °C (-312 °F to 932 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F)
HY-80 (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value E* : solid \|\| after 55 years in service as a submarine hull \|\| room temperature value TC : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 1.27 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 519/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 245 °C (473 °F), 549/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 395 °C (743 °F), 568/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 545 °C (1013 °F), 585/s \|\| 0 to 0.2 mm/mm strain SSC : after 55 years in service as a submarine hull \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.92 mm/mm strain UTS* : solid \|\| after 55 years in service as a submarine hull \|\| room temperature value YS* : solid \|\| after 55 years in service as a submarine hull \|\| room temperature value %El* : solid \|\| after 55 years in service as a submarine hull \|\| room temperature value FSN : as-received \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles RHO : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F) SIGMA : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F)
HY-100 (UNS K32045) (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 1 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 521/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 245 °C (473 °F), 547/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 395 °C (743 °F), 578/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 545 °C (1013 °F), 594/s \|\| 0 to 0.157 mm/mm strain SSCC : quenched & tempered \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.45 mm/mm strain UTS* : solid \|\| quenched & tempered \|\| room temperature value YS* : solid \|\| quenched & tempered \|\| room temperature value %El* : solid \|\| quenched & tempered \|\| room temperature value FSN : as-received \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles RHO : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F) SIGMA : solid \|\| hardened & tempered \|\| 0 °C to 800 °C (32 °F to 1472 °F)
HY-130 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 624 °C (68 °F to 1155 °F) DLL : solid \|\| 20 °C to 624 °C (68 °F to 1155 °F) MTE : solid \|\| 20 °C to 624 °C (68 °F to 1155 °F) CTE : solid \|\| 20 °C to 624 °C (68 °F to 1155 °F) SSC : as-received \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 1.2 mm/mm strain SSC : as-received \|\| tested at 20 °C (68 °F), 523/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 245 °C (473 °F), 555/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 395 °C (743 °F), 580/s \|\| 0 to 0.2 mm/mm strain SSC : as-received \|\| tested at 545 °C (1013 °F), 591/s \|\| 0 to 0.157 mm/mm strain UTS : as-received \|\| plates \|\| -192 °C to 148 °C (-314 °F to 298 °F) UTS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : plates \|\| as-received \|\| -192 °C to 148 °C (-314 °F to 298 °F) YS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : plates \|\| as-received \|\| -192 °C to 20 °C (-314 °F to 68 °F) %El : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 871 °C (1600 °F), austenitized at 816 °C (1500 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) FSN : as-received \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles
30Cr1Mo1V	D* : solid \|\| room temperature value FSN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : SAW weld \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : TIG weld \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles
30Cr2Ni4MoV	D* : solid \|\| room temperature value SSCC : 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.25/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain FSN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : SAW weld \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : TIG weld \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles
ASME Grade P23/T23 (UNS K41650) (ISO/EN/DIN 7CrWVMoNb9-6)	D* : solid \|\| room temperature value SR : normalized & tempered \|\| tested at 500 °C (932 °F) \|\| 10 h to 3.4x10⁴ h SR : normalized & tempered \|\| tested at 550 °C (1022 °F) \|\| 50 h to 1x10⁴ h SR : normalized & tempered \|\| tested at 600 °C (1112 °F) \|\| 50 h to 1x10⁴ h SR : normalized & tempered \|\| Master curve (LMP) \|\| 500 °C to 601 °C (932 °F to 1114 °F)
ASME Grade T23 (ISO/EN/DIN 7CrWVMoNb9-6) (JIS STBA24J1/STPA24J1)	D* : solid \|\| room temperature value SR : normalized 10 min & tempered \|\| tested at 500 °C (932 °F) \|\| 100 h to 3.2x10⁴ h SR : normalized 10 min & tempered \|\| tested at 550 °C (1022 °F) \|\| 200 h to 8,000 h SR : normalized 10 min & tempered \|\| tested at 600 °C (1112 °F) \|\| 90 h to 6x10⁴ h SR : normalized 10 min & tempered \|\| Master curve (LMP) \|\| 500 °C to 601 °C (932 °F to 1114 °F) SR : normalized 0.5 h & tempered \|\| tested at 500 °C (932 °F) \|\| 180 h to 1.8x10⁴ h SR : normalized 0.5 h & tempered \|\| tested at 550 °C (1022 °F) \|\| 220 h to 6,500 h SR : normalized 0.5 h & tempered \|\| tested at 600 °C (1112 °F) \|\| 90 h to 3.2x10⁴ h SR : normalized 0.5 h & tempered \|\| Master curve (LMP) \|\| 500 °C to 601 °C (932 °F to 1114 °F)

P9 (9 Cr - 1 Mo (wt %)) (UNS S50400) (WNr 1.7386) (ASTM A335/A387)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| normalized & tempered \|\| 20 °C to 727 °C (68 °F to 1340 °F) TD : solid \|\| normalized & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| normalized & tempered \|\| 20 °C to 733 °C (68 °F to 1351 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 5000 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 650 °C (1202 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| martensite \|\| 20 °C to 610 °C (68 °F to 1130 °F) SSC : quenched & tempered, 0.00126/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.127 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.95 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.13 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 350 °C (662 °F) \|\| 0 to 0.1 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.95 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 450 °C (842 °F) \|\| 0 to 0.85 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.81 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.74 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 520 °C (968 °F) \|\| 0 to 0.6 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.49 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 575 °C (1067 °F) \|\| 0 to 0.34 mm/mm strain SSC : quenched & tempered, 0.00126/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.2 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.95 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.74 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.79 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 350 °C (662 °F) \|\| 0 to 0.72 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.62 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 450 °C (842 °F) \|\| 0 to 0.55 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 475 °C (887 °F) \|\| 0 to 0.52 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.38 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 520 °C (968 °F) \|\| 0 to 0.21 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.13 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 575 °C (1067 °F) \|\| 0 to 0.01 mm/mm strain SSC : normalized & tempered, 3.16x10^-⁴/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 8.2x10^-³ mm/mm strain RHO : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) SIGMA : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) S : solid \|\| normalized & tempered \|\| 20 °C to 727 °C (68 °F to 1340 °F)
P91 (9 Cr - 1 Mo (wt %)) (UNS K90901/K91560) (WNr 1.4903) (ISO/EN/DIN X10CrMoVNb9-1)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) TD* : solid \|\| room temperature value SH : solid \|\| normalized & tempered \|\| 20 °C to 733 °C (68 °F to 1351 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 5000 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 650 °C (1202 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| martensite \|\| 20 °C to 610 °C (68 °F to 1130 °F) SSC : hot-rolled plate \|\| tested at 27 °C (80 °F), 0.00126/s \|\| 0 to 0.64 mm/mm strain SSC : hot-rolled plate \|\| tested at 350 °C (662 °F), 0.00126/s \|\| 0 to 0.34 mm/mm strain SSC : hot-rolled plate \|\| tested at 450 °C (842 °F), 0.00126/s \|\| 0 to 0.31 mm/mm strain UTS : solid \|\| initial state \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : solid \|\| initial state \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : solid \|\| after 90,000 h of service \|\| 20 °C to 600 °C (68 °F to 1112 °F) SR : short rupture times \|\| tested at 620 °C (1148 °F) \|\| 1.6x10³ h to 1x10⁴ h SR : short rupture times \|\| tested at 640 °C (1184 °F) \|\| 400 h to 1,300 h SR : short rupture times \|\| tested at 660 °C (1220 °F) \|\| 50 h to 300 h SR : short rupture times \|\| tested at 680 °C (1256 °F) \|\| 10 h to 30 h SR : short rupture times \|\| tested at 700 °C (1292 °F) \|\| 1 h to 10 h SR : short rupture times \|\| Master curve (LMP) \|\| 620 °C to 700 °C (1148 °F to 1292 °F) SR : long rupture times \|\| tested at 500 °C (932 °F) \|\| 560 h to 5.6x10⁴ h SR : long rupture times \|\| tested at 550 °C (1022 °F) \|\| 660 h to 8.2x10⁴ h SR : long rupture times \|\| tested at 600 °C (1112 °F) \|\| 37 h to 7.9x10⁴ h SR : long rupture times \|\| tested at 650 °C (1202 °F) \|\| 18 h to 5.8x10⁴ h SR : long rupture times \|\| tested at 700 °C (1292 °F) \|\| 350 h to 1.4x10⁴ h SR : long rupture times \|\| Master curve (LMP) \|\| 500 °C to 700 °C (932 °F to 1292 °F) FEN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 450 cycles to 3x10³ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
ASME P92 (9 Cr - 0.5 Mo - 2 W (wt %)) (UNS K92460) (ISO/EN/DIN X10CrWMoVNb9-2) (ASTM A182)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : normalized & tempered \|\| 20 °C to 648 °C (68 °F to 1198 °F) TC : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) SSC : normalized & tempered, 0.00126/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.75 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.53 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.4 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.42 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 450 °C (842 °F) \|\| 0 to 0.33 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.36 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 550 °C (1022 °F) \|\| 0 to 0.28 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.18 mm/mm strain SSC : normalized & tempered, 0.00126/s \|\| tested at 650 °C (1202 °F) \|\| 0 to 9.85x10^-³ mm/mm strain SSCC : 0.01/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.95 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.95 mm/mm strain SSCC : 0.1/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 1/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.94 mm/mm strain SSCC : 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.97 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 10/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.96 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.97 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.97 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.97 mm/mm strain UTS : normalized & tempered \|\| 0.0000316/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) UTS : normalized & tempered \|\| 3.16x10^-⁴/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) UTS : normalized & tempered \|\| 0.00126/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) YS : normalized & tempered \|\| 0.0000316/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) YS : normalized & tempered \|\| 3.16x10^-⁴/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) YS : normalized & tempered \|\| 0.00126/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) %El : normalized & tempered \|\| 3.16x10^-⁴/s strain rate \|\| 20 °C to 648 °C (68 °F to 1198 °F) SR : various conditions \|\| tested at 550 °C (1022 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 600 °C (1112 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 650 °C (1202 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 700 °C (1292 °F) \|\| 10 h to 5x10⁴ h SR : various conditions \|\| tested at 750 °C (1382 °F) \|\| 1 h to 3,000 h SR : various conditions \|\| Master curve (LMP) \|\| 550 °C to 751 °C (1022 °F to 1384 °F) FEN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 450 cycles to 3x10³ cycles FEN : normalized & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 550 °C (1022 °F), R = -1, axial, total strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 550 °C (1022 °F), R = -1, axial, elastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 600 °C (1112 °F), R = -1, axial, elastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 650 °C (1202 °F), R = -1, axial, elastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 650 °C (1202 °F), R = -1, axial, plastic strain amplitude, Wang et. al. \|\| 250 cycles to 1x10⁴ cycles FEN : normalized & tempered \|\| tested at 300 °C (572 °F), R = -1, axial, total strain amplitude, Jurgens et. al. \|\| 2.4x10³ cycles to 1.1x10⁴ cycles FEN : normalized & tempered \|\| tested at 500 °C (932 °F), R = -1, axial, total strain amplitude, Jurgens et. al. \|\| 1.2x10³ cycles to 4.2x10⁴ cycles FEN : normalized & tempered \|\| tested at 620 °C (1148 °F), R = -1, axial, total strain amplitude, Jurgens et. al. \|\| 680 cycles to 9x10³ cycles FEN : thermo-mechanical fatigue \|\| tested at 300 °C (572 °F) to 620 °C (1148 °F), axial, in-phase, total strain amplitude, Jurgens et. al. \|\| 800 cycles to 6.2x10³ cycles FEN : thermo-mechanical fatigue \|\| tested at 300 °C (572 °F) to 620 °C (1148 °F), axial, out-of-phase, total strain amplitude, Jurgens et. al. \|\| 730 cycles to 4.9x10³ cycles FEN : thermo-mechanical fatigue \|\| tested at 300 °C (572 °F) to 620 °C (1148 °F), axial, in-phase, 180 s hold, total strain amplitude, Jurgens et. al. \|\| 430 cycles to 2.5x10³ cycles FEN : thermo-mechanical fatigue \|\| tested at 300 °C (572 °F) to 620 °C (1148 °F), axial, out-of-phase, 180 s hold, total strain amplitude, Jurgens et. al. \|\| 700 cycles to 3x10³ cycles
ASTM A213 / SA-387 (9 Cr - 1 Mo (wt %) or G91) (ASTM A213)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : tempered \|\| 20 °C to 648 °C (68 °F to 1198 °F) SH : solid \|\| normalized & tempered \|\| 20 °C to 733 °C (68 °F to 1351 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 5000 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 650 °C (1202 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| martensite \|\| 20 °C to 610 °C (68 °F to 1130 °F) UTS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : in air \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁶ h SR : in air \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁶ h FEN : in air \|\| tested at 538 °C (1000 °F), R = -1, axial, total strain range \|\| 500 cycles to 1x10⁵ cycles FEN : in air \|\| tested at 593 °C (1100 °F), R = -1, axial, total strain range \|\| 500 cycles to 1x10⁵ cycles
Modified 9 Cr - 1 Mo (wt %) (Gr. 91) (UNS K91560)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : tempered \|\| 20 °C to 648 °C (68 °F to 1198 °F) SH : solid \|\| normalized & tempered \|\| 20 °C to 733 °C (68 °F to 1351 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 5000 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 650 °C (1202 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| martensite \|\| 20 °C to 610 °C (68 °F to 1130 °F) SR : tempered \|\| tested at 550 °C (1022 °F) \|\| 17 h to 5,300 h SR : tempered \|\| tested at 600 °C (1112 °F) \|\| 15 h to 5,200 h SR : tempered \|\| Master curve (LMP) \|\| 550 °C to 601 °C (1022 °F to 1114 °F) SR : normalized & tempered, tube MGA \|\| tested at 550 °C (1022 °F) \|\| 500 h to 5.6x10⁴ h SR : normalized & tempered, tube MGA \|\| tested at 600 °C (1112 °F) \|\| 700 h to 3.62x10⁴ h SR : normalized & tempered, tube MGA \|\| tested at 650 °C (1202 °F) \|\| 630 h to 2.4x10⁴ h SR : normalized & tempered, tube MGA \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : normalized & tempered, tube MGB \|\| tested at 550 °C (1022 °F) \|\| 200 h to 6.9x10⁴ h SR : normalized & tempered, tube MGB \|\| tested at 600 °C (1112 °F) \|\| 780 h to 4.8x10⁴ h SR : normalized & tempered, tube MGB \|\| tested at 650 °C (1202 °F) \|\| 300 h to 5.1x10⁴ h SR : normalized & tempered, tube MGB \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : normalized & tempered, tube MGC \|\| tested at 550 °C (1022 °F) \|\| 650 h to 1.5x10⁴ h SR : normalized & tempered, tube MGC \|\| tested at 600 °C (1112 °F) \|\| 40 h to 3.6x10⁴ h SR : normalized & tempered, tube MGC \|\| tested at 650 °C (1202 °F) \|\| 250 h to 4.3x10⁴ h SR : normalized & tempered, tube MGC \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : normalized & tempered, plate MgA \|\| tested at 550 °C (1022 °F) \|\| 420 h to 4.2x10⁴ h SR : normalized & tempered, plate MgA \|\| tested at 600 °C (1112 °F) \|\| 160 h to 6.1x10⁴ h SR : normalized & tempered, plate MgA \|\| tested at 650 °C (1202 °F) \|\| 140 h to 4.3x10⁴ h SR : normalized & tempered, plate MgA \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : normalized & tempered, plate MgB \|\| tested at 550 °C (1022 °F) \|\| 160 h to 4.7x10⁴ h SR : normalized & tempered, plate MgB \|\| tested at 600 °C (1112 °F) \|\| 180 h to 6.5x10⁴ h SR : normalized & tempered, plate MgB \|\| tested at 650 °C (1202 °F) \|\| 170 h to 4.2x10⁴ h SR : normalized & tempered, plate MgB \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : normalized & tempered, plate MgC \|\| tested at 550 °C (1022 °F) \|\| 700 h to 3.6x10⁴ h SR : normalized & tempered, plate MgC \|\| tested at 600 °C (1112 °F) \|\| 900 h to 3.62x10⁴ h SR : normalized & tempered, plate MgC \|\| tested at 650 °C (1202 °F) \|\| 200 h to 6.1x10⁴ h SR : normalized & tempered, plate MgC \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F) SR : average of tubes & plates \|\| tested at 550 °C (1022 °F) \|\| 160 h to 6.9x10⁴ h SR : average of tubes & plates \|\| tested at 600 °C (1112 °F) \|\| 40 h to 6.5x10⁴ h SR : average of tubes & plates \|\| tested at 650 °C (1202 °F) \|\| 140 h to 6.1x10⁴ h SR : average of tubes & plates \|\| Master curve (LMP) \|\| 550 °C to 650 °C (1022 °F to 1202 °F) FEN : tempered \|\| tested at 550 °C (1022 °F), R = -1, axial, total strain amplitude \|\| 140 cycles to 4.7x10³ cycles FEN : no axial static load \|\| tested at 550 °C (1022 °F), R = -1, torsion, equivalent strain range \|\| 700 cycles to 3.5x10⁵ cycles FEN : 150 MPa (21.8 ksi) axial static load \|\| tested at 550 °C (1022 °F), R = -1, torsion, equivalent strain range \|\| 200 cycles to 1.4x10⁴ cycles FSN : tempered \|\| tested at 500 °C (932 °F), R = -1, axial, maximum stress \|\| 2 cycles to 930 cycles FSN : tempered \|\| tested at 550 °C (1022 °F), R = -1, axial, maximum stress \|\| 2 cycles to 875 cycles
9 Cr - 1 Mo - V - Nb (wt %) (T91)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : tempered \|\| 20 °C to 648 °C (68 °F to 1198 °F) TC : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) TD* : solid \|\| room temperature value SH : solid \|\| normalized & tempered \|\| 20 °C to 733 °C (68 °F to 1351 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 550 °C (1022 °F) for 5000 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| normalized, tempered & aged at 650 °C (1202 °F) for 500 h \|\| 20 °C to 736 °C (68 °F to 1357 °F) SH : solid \|\| martensite \|\| 20 °C to 610 °C (68 °F to 1130 °F) SR : heat-treated tube \|\| tested at 550 °C (1022 °F) \|\| 10 h to 9x10⁴ h SR : heat-treated tube \|\| tested at 600 °C (1112 °F) \|\| 10 h to 3.5x10⁴ h SR : heat-treated tube \|\| tested at 650 °C (1202 °F) \|\| 15 h to 4x10⁴ h SR : heat-treated tube \|\| tested at 700 °C (1292 °F) \|\| 10 h to 3.2x10⁴ h SR : heat-treated tube \|\| tested at 725 °C (1337 °F) \|\| 360 h to 2,000 h SR : heat-treated tube \|\| Master curve (LMP) \|\| 550 °C to 726 °C (1022 °F to 1339 °F)
E911 (9 Cr - 1 Mo - 1 W (wt %)) (WNr 1.4905) (ISO/EN/DIN X11CrMoWVNb9-1-1) (ASTM E911)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : tempered \|\| 20 °C to 648 °C (68 °F to 1198 °F) SR : austenitized & tempered \|\| tested at 550 °C (1022 °F) \|\| 10 h to 5.7x10⁴ h SR : austenitized & tempered \|\| tested at 600 °C (1112 °F) \|\| 10 h to 5.3x10⁴ h SR : austenitized & tempered \|\| tested at 650 °C (1202 °F) \|\| 10 h to 5.2x10⁴ h SR : austenitized & tempered \|\| Master curve (LMP) \|\| 550 °C to 651 °C (1022 °F to 1204 °F)
SINOXX 4903 (WNr 1.4903) (ISO/EN/DIN X10CrMoVNb9-1) (ASTM A213)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value YS : normalized & annealed \|\| diameters up to 130 mm (5.12 inch) \|\| 20 °C to 600 °C (68 °F to 1112 °F) SR : normalized & annealed \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 580 °C (1076 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 620 °C (1148 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 640 °C (1184 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| tested at 660 °C (1220 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : normalized & annealed \|\| Master curve (LMP) \|\| 500 °C to 660 °C (932 °F to 1220 °F)
ASTM A289 (ISO/EN/DIN 18Mn18Cr)	D* : solid \|\| room temperature value FEN : forging, radial \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 10 cycles to 1x10⁶ cycles FEN : forging, tangential \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 10 cycles to 1x10⁶ cycles
9Cr2W	D* : solid \|\| room temperature value SSC : tempered martensite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.66 mm/mm strain SSC : tempered martensite \|\| tested at 650 °C (1202 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SR : tempered martensite \|\| tested at 650 °C (1202 °F) \|\| 30 h to 1.1x10⁴ h
9Cr3W	D* : solid \|\| room temperature value SSC : tempered martensite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.63 mm/mm strain SSC : tempered martensite \|\| tested at 650 °C (1202 °F), 0.002/s \|\| 0 to 0.01 mm/mm strain SR : tempered martensite \|\| tested at 650 °C (1202 °F) \|\| 50 h to 2.2x10⁴ h
GP91 (ISO/EN/DIN GX12CrMoVNbN9-1)	D* : solid \|\| room temperature value FEN : cast \|\| tested at 20 °C (68 °F), R = -1, rotating beam, total strain amplitude \|\| 100 cycles to 3x10⁵ cycles
P122 steel	D* : solid \|\| room temperature value SR : various conditions \|\| tested at 550 °C (1022 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 600 °C (1112 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 650 °C (1202 °F) \|\| 10 h to 1x10⁵ h SR : various conditions \|\| tested at 700 °C (1292 °F) \|\| 10 h to 6x10⁴ h SR : various conditions \|\| Master curve (LMP) \|\| 550 °C to 701 °C (1022 °F to 1294 °F)
9 Cr - 2 Mo (wt %)	D* : solid \|\| room temperature value UTS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F)
9 Cr - 3 Mo (wt %)	D* : solid \|\| room temperature value UTS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered at 704 °C (1300 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F)
RAFM steel (9 Cr - 1 W (wt %)) (some datasets are for temperatures below 20 °C)	D : solid \|\| normalized & tempered \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| normalized & tempered \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| normalized & tempered \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| normalized & tempered \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : austenite + martensite \|\| on heating \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : austenite + martensite \|\| on cooling \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : martensite \|\| on cooling \|\| 20 °C to 327 °C (68 °F to 620 °F) E : austenite \|\| on cooling \|\| -16 °C to 990 °C (3 °F to 1814 °F) G : austenite + martensite \|\| on heating \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : austenite + martensite \|\| on cooling \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : martensite \|\| on cooling \|\| 20 °C to 327 °C (68 °F to 620 °F) G : austenite \|\| on cooling \|\| -16 °C to 990 °C (3 °F to 1814 °F) v : austenite + martensite \|\| on heating \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : austenite + martensite \|\| on cooling \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : martensite \|\| on cooling \|\| 20 °C to 327 °C (68 °F to 620 °F) v : austenite \|\| on cooling \|\| -16 °C to 990 °C (3 °F to 1814 °F) K : austenite + martensite \|\| on heating \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : austenite + martensite \|\| on cooling \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : martensite \|\| on cooling \|\| 20 °C to 327 °C (68 °F to 620 °F) K : austenite \|\| on cooling \|\| -16 °C to 990 °C (3 °F to 1814 °F) SH : solid \|\| solution treated & quenched \|\| 20 °C to 737 °C (68 °F to 1358 °F) SSCC : quenched & tempered, 0.001/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.37 mm/mm strain SSCC : quenched & tempered, 0.001/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.63 mm/mm strain SSCC : quenched & tempered, 0.001/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.58 mm/mm strain SSCC : quenched & tempered, 0.001/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.63 mm/mm strain YSC : tempered martensite \|\| 20 °C to 600 °C (68 °F to 1112 °F)
S65007 (UNS S65007) (ISO/EN/DIN X45CrSi93)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : solid \|\| tempered at 788 °C (1450 °F) & water quenched \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered at 788 °C (1450 °F) & water quenched \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered at 788 °C (1450 °F) & water quenched \|\| 20 °C to 650 °C (68 °F to 1202 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
VM12-SHC (ASME Code Case 2781) (WNr 1.4915) (ISO/EN/DIN X12CrCoWMoVNb12-2-2)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : tempered \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 570 °C (1058 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 580 °C (1076 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 590 °C (1094 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 610 °C (1130 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| tested at 620 °C (1148 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : tempered \|\| Master curve (LMP) \|\| 550 °C to 621 °C (1022 °F to 1150 °F)
AFC-260 (Fe - 16 Cr - 13 Co - 5 Mo - 2 Ni (wt %))	D : solid \|\| aged sheet \|\| 20 °C to 316 °C (68 °F to 600 °F) DLL : solid \|\| aged sheet \|\| 20 °C to 316 °C (68 °F to 600 °F) MTE : solid \|\| aged sheet \|\| 20 °C to 316 °C (68 °F to 600 °F) CTE : solid \|\| aged sheet \|\| 20 °C to 316 °C (68 °F to 600 °F) E : sheet, in tension \|\| aged, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : sheet, in tension \|\| aged, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : sheet, in tension \|\| aged, average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : sheet, in compression \|\| aged, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : sheet, in compression \|\| aged, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : sheet, in compression \|\| aged, average \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : aged sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : aged sheet \|\| tested at 510 °C (950 °F) \|\| 10 h to 1,000 h SR : aged sheet \|\| Master curve (LMP) \|\| 482 °C to 511 °C (899 °F to 952 °F) FSN : aged sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 4.4x10³ cycles to 1x10⁷ cycles FSN : aged sheet, smooth \|\| tested at 260 °C (500 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : aged sheet, smooth \|\| tested at 482 °C (900 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 7x10⁶ cycles FSN : aged sheet, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 3.2x10³ cycles to 1x10⁷ cycles FSN : aged sheet, notched \|\| tested at 260 °C (500 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : aged sheet, notched \|\| tested at 482 °C (900 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, aged sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, aged sheet \|\| tested at 510 °C (950 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, aged sheet \|\| Master curve (LMP) \|\| 482 °C to 510 °C (899 °F to 950 °F) CRS : 0.5% plastic strain, aged sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, aged sheet \|\| tested at 510 °C (950 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, aged sheet \|\| Master curve (LMP) \|\| 482 °C to 510 °C (899 °F to 950 °F) IC : tested at 482 °C (900 °F), plastic strain, aged sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, aged sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, aged sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, aged sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, aged sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, aged sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, aged sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, aged sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, aged sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 510 °C (950 °F), plastic strain, aged sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain
UNS S65006 (UNS S65006) (WNr 1.4747) (ISO/EN/DIN X80CrNiSi20) (JIS SUH4) (SAE HNV-6) (AFNOR Z80CSN20-02)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| annealed \|\| 20 °C to 777 °C (68 °F to 1430 °F)
ASME TP347HFG (UNS S34710) (ISO/EN/DIN X8CrNiNb1811) (ASTM A213/A213M)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 10 h to 6,000 h SR : solution treated \|\| Master curve (LMP) \|\| 600 °C to 801 °C (1112 °F to 1474 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
XA704 (UNS S34705) (ASTM A213)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 8x10³ h to 1x10⁵ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 500 h to 1x10⁵ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 180 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 120 h to 1x10⁵ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 190 h to 3x10⁴ h SR : solution treated \|\| tested at 850 °C (1562 °F) \|\| 580 h to 2,400 h SR : solution treated \|\| Master curve (LMP) \|\| 600 °C to 851 °C (1112 °F to 1564 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
Alloy 709 (NF 709) (UNS S31025) (ISO/EN/DIN X6CrNiMo17132) (ASTM A213)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SSC : hot-forged plate \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.37 mm/mm strain SSC : hot-forged plate \|\| tested at 100 °C (212 °F), 0.001/s \|\| 0 to 0.42 mm/mm strain SSC : hot-forged plate \|\| tested at 400 °C (752 °F), 0.001/s \|\| 0 to 0.42 mm/mm strain SSC : hot-forged plate \|\| tested at 500 °C (932 °F), 0.001/s \|\| 0 to 0.46 mm/mm strain SSC : hot-forged plate \|\| tested at 600 °C (1112 °F), 0.001/s \|\| 0 to 0.42 mm/mm strain SSC : hot-forged plate \|\| tested at 700 °C (1292 °F), 0.001/s \|\| 0 to 0.31 mm/mm strain SSC : hot-forged plate \|\| tested at 800 °C (1472 °F), 0.001/s \|\| 0 to 0.28 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 500 °C (932 °F), 1x10^-⁴/s \|\| 0 to 0.29 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 700 °C (1292 °F), 1x10^-⁴/s \|\| 0 to 0.12 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 800 °C (1472 °F), 1x10^-⁴/s \|\| 0 to 0.45 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 900 °C (1652 °F), 1x10^-⁴/s \|\| 0 to 0.12 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 500 °C (932 °F), 1x10^-⁵/s \|\| 0 to 0.31 mm/mm strain SSC : hot-forged plate, annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| tested at 700 °C (1292 °F), 1x10^-⁵/s \|\| 0 to 0.16 mm/mm strain UTS : hot-forged plate \|\| as-forged \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : hot-forged plate \|\| annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : hot-forged plate \|\| as-forged \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : hot-forged plate \|\| annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| 20 °C to 900 °C (68 °F to 1652 °F) %El : hot-forged plate \|\| as-forged \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : hot-forged plate \|\| annealed at 1100 °C (2012 °F) for 2 h, rapid cooling \|\| 20 °C to 900 °C (68 °F to 1652 °F) SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 3x10³ h to 4x10⁴ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 300 h to 5x10⁴ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 70 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 100 h to 8x10⁴ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 50 h to 8x10⁴ h SR : solution treated \|\| tested at 850 °C (1562 °F) \|\| 60 h to 2x10⁴ h SR : solution treated \|\| tested at 900 °C (1652 °F) \|\| 70 h to 2x10⁴ h SR : solution treated \|\| tested at 950 °C (1742 °F) \|\| 80 h to 2,000 h SR : solution treated \|\| Master curve (LMP) \|\| 600 °C to 951 °C (1112 °F to 1744 °F) FEN : solution annealed at 1100 °C (2012 °F) \|\| tested at 750 °C (1382 °F), R = -1, axial, total strain amplitude \|\| 450 cycles to 1.1x10⁵ cycles
HR3C (UNS S31042) (ISO/EN/DIN X6CrNiNbN2520) (ASTM A213)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 40 h to 1x10⁵ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| Master curve (LMP) \|\| 600 °C to 801 °C (1112 °F to 1474 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
MN25R (UNS S30925) (ASTM A213)	D* : solid \|\| room temperature value SR : solution treated \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 700 h to 1x10⁵ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 200 h to 6x10⁴ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 100 h to 5x10⁴ h SR : solution treated \|\| Master curve (LMP) \|\| 550 °C to 701 °C (1022 °F to 1294 °F)
ATI 20-25+Nb (UNS S35140) (ASTM A240)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F)
UNS N08354 (UNS N08354)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS K63017 (UNS K63017)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E* : solid \|\| room temperature value UTS : solution annealed & quenched \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solution annealed & quenched \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution annealed & quenched \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : annealed \|\| tested at 732 °C (1350 °F) \|\| 10 h to 500 h RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
2101 duplex stainless (UNS S32101) (WNr 1.4162)	D : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) DLL : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) MTE : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) CTE : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) E : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) TD : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) SH : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) SSCC : 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.77 mm/mm strain RHO : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) SIGMA : solid \|\| 20 °C to 316 °C (68 °F to 600 °F)

CA6NM (UNS J91540) (ASTM A352/A487/A743/A757)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| 20 °C to 577 °C (68 °F to 1070 °F) UTS : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : solid \|\| hardened & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) SR : hardened & tempered \|\| tested at 427 °C (800 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hardened & tempered \|\| tested at 454 °C (850 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hardened & tempered \|\| tested at 482 °C (900 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hardened & tempered \|\| tested at 510 °C (950 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hardened & tempered \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hardened & tempered \|\| Master curve (LMP) \|\| 426 °C to 538 °C (799 °F to 1000 °F) FSN : tested in water \|\| tested at 20 °C (68 °F), R = -1, rotating beam, stress amplitude \|\| 7x10³ cycles to 3x10⁵ cycles FSN : tested in air \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 7.2x10⁵ cycles to 1x10⁸ cycles FSN : tested in air \|\| tested at 20 °C (68 °F), axial, -100 MPa (-14.5 ksi) mean stress, stress amplitude \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : tested in air \|\| tested at 20 °C (68 °F), axial, -200 MPa (-29.0 ksi) mean stress, stress amplitude \|\| 4x10⁵ cycles to 1x10⁸ cycles FSN : tested in air \|\| tested at 20 °C (68 °F), axial, -300 MPa (-43.5 ksi) mean stress, stress amplitude \|\| 2.4x10⁶ cycles to 1x10⁸ cycles RHO : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SIGMA : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
CA15 (UNS J91150) (ASTM A217/A426/A487/A743) (SAE 60410) (AMS 5351B) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| -253 °C to 900 °C (-424 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -18 °C to 1093 °C (-1 °F to 2000 °F) UTS : air cooled from 982 °C (1800 °F) \|\| tempered at 316 °C (600 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : air cooled from 982 °C (1800 °F) \|\| tempered at 593 °C (1100 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : air cooled from 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : air cooled from 982 °C (1800 °F) \|\| tempered at 788 °C (1450 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : air cooled from 982 °C (1800 °F) \|\| tempered at 316 °C (600 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : air cooled from 982 °C (1800 °F) \|\| tempered at 593 °C (1100 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : air cooled from 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : air cooled from 982 °C (1800 °F) \|\| tempered at 788 °C (1450 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : air cooled from 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SIGMA : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
CA40 (UNS J91153) (ASTM A743) (SAE 60420)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| 20 °C to 876 °C (68 °F to 1609 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SIGMA : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
CB7Cu-1 (UNS J92180) (ASTM A747) (AMS 5398B) (some datasets are for temperatures below 20 °C)	D : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) D : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) E : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) E : wrought \|\| in tension \|\| 20 °C to 316 °C (68 °F to 600 °F) E : wrought \|\| in compression \|\| 20 °C to 316 °C (68 °F to 600 °F) G : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) G* : wrought \|\| room temperature value v : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) v* : wrought \|\| room temperature value K : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) K* : wrought \|\| room temperature value TC : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) TD : solid \|\| cast, overaged \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : solid \|\| cast, overaged \|\| 20 °C to 652 °C (68 °F to 1205 °F) SH : solid \|\| wrought \|\| -18 °C to 865 °C (-1 °F to 1589 °F) UTS : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F)
CB7Cu-2 (UNS J92110) (ASTM A747) (AMS 5398B) (some datasets are for temperatures below 20 °C)	D : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) D : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| aged at 593 °C (1100 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) E : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) E : wrought \|\| in tension \|\| 20 °C to 316 °C (68 °F to 600 °F) E : wrought \|\| in compression \|\| 20 °C to 316 °C (68 °F to 600 °F) G : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) G* : wrought \|\| room temperature value v : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) v* : wrought \|\| room temperature value K : overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) K* : wrought \|\| room temperature value TC : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) TD : solid \|\| cast, overaged \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : solid \|\| cast, overaged \|\| 20 °C to 652 °C (68 °F to 1205 °F) SH : solid \|\| wrought \|\| -18 °C to 865 °C (-1 °F to 1589 °F) UTS : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| aged at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F)
CB30 (UNS J91803) (ASTM A743) (SAE 60442)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) G : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) v : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) K : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F)
CC50 (UNS J92615) (ASTM A743) (SAE 60446) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) G : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) v : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) NE : solid \|\| surface finish #1 \|\| -173 °C to 927 °C (-280 °F to 1700 °F) NE : solid \|\| surface finish #8 \|\| -173 °C to 927 °C (-280 °F to 1700 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
CD4MCu (UNS J93370) (ASTM A890)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F)
CE30 (UNS J93423) (ASTM A743)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF3 (UNS J92500) (WNr 1.4306/1.4307) (ISO/EN/DIN X2CrNi18-9/X2CrNi19-11) (ASTM A351/A451/A743/A744) (AMS 5511/5639/5647/5697) (AFNOR Z2CN18-10/Z3CN18-10/Z3CN19-10M) (GB & GB/T 00Cr19Ni10) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) UTS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) UTS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) YS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) %El : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF3M (UNS J92800) (ISO/EN/DIN X2CrNiMo17-12-2) (JIS SUS316/SUS316L) (ASTM A351/A451/A743/A744) (GB & GB/T 00Cr17Ni14Mo2/0Cr18Ni12Mo2Ti) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) DLL : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) MTE : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) CTE : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) UTS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) YS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) %El : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF8 (UNS J92600) (ASTM A351/A451/A743/A743/A744) (SAE 60304) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) DLL : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) MTE : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) CTE : solid \|\| -198 °C to 650 °C (-325 °F to 1202 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) UTS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) UTS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) YS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) %El : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 10 h to 6,000 h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 20 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 35 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) HE : solid \|\| grit blasted black oxidized \|\| -98 °C to 77 °C (-145 °F to 170 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : solid \|\| 1000 °C to 1225 °C (1832 °F to 2237 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) ST : liquid \|\| 30 ppm sulfur \|\| 1576 °C to 1805 °C (2869 °F to 3281 °F) ST : liquid \|\| 80 ppm sulfur \|\| 1579 °C to 1781 °C (2874 °F to 3238 °F) ST : liquid \|\| 100 ppm sulfur \|\| 1550 °C to 1890 °C (2822 °F to 3434 °F) ST : liquid \|\| 250 ppm sulfur \|\| 1580 °C to 1775 °C (2876 °F to 3227 °F) ST : liquid \|\| average of all \|\| 1417 °C to 1892 °C (2582 °F to 3437 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF8C (UNS J92710) (ASTM A351/A451/A743/A744) (SAE 60347) (AMS 5363B) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -193 °C to 871 °C (-316 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 982 °C (-452 °F to 1800 °F) UTS : solid \|\| water quenched from 1121 °C (2050 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| water quenched from 1121 °C (2050 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| water quenched from 1121 °C (2050 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : as-cast \|\| tested at 550 °C (1022 °F) \|\| 4.2x10⁴ h to unknown strain rate h SR : as-cast \|\| tested at 600 °C (1112 °F) \|\| 1.6x10³ h to unknown strain rate h SR : as-cast \|\| tested at 650 °C (1202 °F) \|\| 90 h to 2x10⁸ h SR : as-cast \|\| tested at 700 °C (1292 °F) \|\| 7 h to 7x10⁶ h SR : as-cast \|\| tested at 750 °C (1382 °F) \|\| 1 h to 3.4x10⁵ h SR : as-cast \|\| tested at 800 °C (1472 °F) \|\| 1 h to 2.2x10⁴ h SR : as-cast \|\| tested at 850 °C (1562 °F) \|\| 1 h to 1,800 h SR : as-cast \|\| Master curve (LMP) \|\| 550 °C to 851 °C (1022 °F to 1564 °F) SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 90 h to 1x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 60 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 25 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) HE : solid \|\| oxidized \|\| 315 °C to 1093 °C (599 °F to 2000 °F) NE : solid \|\| in air at 802 °C (1475 °F) \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF8M (UNS J92900) (ASTM A351/A743/A744) (SAE 60316) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 982 °C (-452 °F to 1800 °F) UTS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) UTS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) YS : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : as-cast \|\| -100 °C to 400 °C (-148 °F to 752 °F) %El : cast, aged at 290 °C (554 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 330 °C (626 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 360 °C (680 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : cast, aged at 400 °C (752 °F) for 1500 h \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 10 h to 3,000 h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF12M (ASTM A451) (SAE 60316) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 982 °C (-452 °F to 1800 °F) NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF16F (UNS J92701) (WNr 1.4305) (ISO/EN/DIN X8CrNiS18-9) (ASTM A743) (SAE 60303/60303a) (AFNOR Z10CNF18-09/Z8CNF18-09) (GB & GB/T Y1Cr18Ni9/Y1Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -273 °C to 320 °C (-460 °F to 608 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value HE : solid \|\| polished then oxidized \|\| 315 °C to 1093 °C (599 °F to 2000 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CF20 (UNS J92602) (ASTM A743) (SAE 60302) (AFNOR Z10CN18.09) (GB & GB/T 1Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) G : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) v : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) K : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) UTS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 15 h to 5,000 h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 20 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 20 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CG8M (UNS J93000) (ASTM A743/A744) (AFNOR Z8CND18.10.3M) (GB & GB/T 0Cr19Ni13Mo3) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
CH20 (UNS J93402) (ASTM A351/A451) (SAE 60309) (GB & GB/T 0Cr23Ni13)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : 2 h at 1121 °C (2050 °F) & water quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 30 h to 7,000 h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 40 h to 1x10⁴ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 30 h to 1x10⁴ h RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CK20 (UNS J94202) (ASTM A351/A451/A743) (SAE 60310) (AMS 5365A) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) G : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) v : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) K : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) TC : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) UTS : water quenched from 1093 °C (2000 °F) \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : water quenched from 1093 °C (2000 °F) \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : water quenched from 1093 °C (2000 °F) \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 20 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 20 h to 1x10⁴ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 25 h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) HE : solid \|\| unoxidized \|\| 537 °C to 1115 °C (998 °F to 2039 °F) HE : solid \|\| oxidized \|\| 81 °C to 1117 °C (178 °F to 2042 °F) HE : solid \|\| grit blasted & oxidized \|\| 67 °C to 977 °C (152 °F to 1790 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
CN7M (UNS J95150/N08007/N80020) (ASTM A351/A743/A744)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
HG10MnN (UNS J92604) (ASTM A297)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) TC : solid \|\| 20 °C to 827 °C (68 °F to 1520 °F) UTS : solid \|\| as-cast \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : solid \|\| as-cast \|\| 20 °C to 900 °C (68 °F to 1652 °F) SR : as-cast \|\| tested at 550 °C (1022 °F) \|\| 2.8x10⁶ h to unknown strain rate h SR : as-cast \|\| tested at 600 °C (1112 °F) \|\| 8.7x10⁴ h to unknown strain rate h SR : as-cast \|\| tested at 650 °C (1202 °F) \|\| 3.9x10³ h to 4.5x10⁹ h SR : as-cast \|\| tested at 700 °C (1292 °F) \|\| 240 h to 1.36x10⁸ h SR : as-cast \|\| tested at 750 °C (1382 °F) \|\| 19 h to 5.75x10⁶ h SR : as-cast \|\| tested at 800 °C (1472 °F) \|\| 2 h to 3.26x10⁵ h SR : as-cast \|\| tested at 850 °C (1562 °F) \|\| 1 h to 2.38x10⁴ h SR : as-cast \|\| Master curve (LMP) \|\| 550 °C to 851 °C (1022 °F to 1564 °F)

Hardox 400 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -100 °C to 20 °C (-148 °F to 68 °F) SSC : tempered martensite-bainite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.41 mm/mm strain SSC : tempered martensite-bainite \|\| tested at 0 °C (32 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : tempered martensite-bainite \|\| tested at -50 °C (-58 °F), unknown strain rate \|\| 0 to 0.39 mm/mm strain SSC : tempered martensite-bainite \|\| tested at -80 °C (-112 °F), unknown strain rate \|\| 0 to 0.56 mm/mm strain SSC : tempered martensite-bainite \|\| tested at -100 °C (-148 °F), unknown strain rate \|\| 0 to 0.67 mm/mm strain UTS : solution annealed & aged \|\| -100 °C to 20 °C (-148 °F to 68 °F) YS : solution annealed & aged \|\| -100 °C to 20 °C (-148 °F to 68 °F) %El : solution annealed & aged \|\| -100 °C to 20 °C (-148 °F to 68 °F)
Toolox 33	D : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : as-received \|\| 20 °C to 200 °C (68 °F to 392 °F) YS : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F) %El : as-received \|\| 20 °C to 200 °C (68 °F to 392 °F)
Toolox 40	D* : solid \|\| room temperature value UTS : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F) %El : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F)
Toolox 44	D : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : as-received \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F) %El : as-received \|\| 20 °C to 500 °C (68 °F to 932 °F)
45CrNiMoVA	D* : solid \|\| room temperature value SSCC : 1x10^-⁴/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.153 mm/mm strain SSCC : 0.001/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.148 mm/mm strain SSCC : 1000/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.92 mm/mm strain SSCC : 1000/s, annealed \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 1000/s, annealed \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 2000/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 3000/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 3000/s, annealed \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.91 mm/mm strain SSCC : 3000/s, annealed \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 5000/s, annealed \|\| tested at 25 °C (77 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 5000/s, annealed \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.92 mm/mm strain SSCC : 5000/s, annealed \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain SSCC : 8000/s, annealed \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 8000/s, annealed \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.93 mm/mm strain

HY-180 (UNS K91970)	D* : solid \|\| room temperature value E* : solid \|\| room temperature value SSC : H-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSC : H-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : H-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : H-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain UTS* : FMS-1111 grade \|\| 9.52 mm to 50.8 mm (0.375 inch to 2 inch) thick \|\| room temperature value UTS* : FMS-1111 grade \|\| 50.8 mm to 102 mm (2 inch to 4 inch) thick \|\| room temperature value YS* : FMS-1111 grade \|\| 9.52 mm to 50.8 mm (0.375 inch to 2 inch) thick \|\| room temperature value YS* : FMS-1111 grade \|\| 50.8 mm to 102 mm (2 inch to 4 inch) thick \|\| room temperature value %El* : FMS-1111 grade \|\| 9.52 mm to 50.8 mm (0.375 inch to 2 inch) thick \|\| room temperature value %El* : FMS-1111 grade \|\| 50.8 mm to 102 mm (2 inch to 4 inch) thick \|\| room temperature value
HY-TUF (UNS K32550) (ASTM A579) (AMS 6418)	D* : solid \|\| room temperature value E : solid \|\| in tension \|\| 20 °C to 343 °C (68 °F to 649 °F) E : solid \|\| in compression \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : hardened & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : hardened & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : 857 °C (1575 °F), oil quenched, tempered at 260 °C (500 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10³ cycles to 1x10⁷ cycles
Super HY-TUF (UNS K32550) (ASTM A322) (AMS 2300/2301/2304/6418/6425/S-7108)	D* : solid \|\| room temperature value E : solid \|\| in tension \|\| 20 °C to 343 °C (68 °F to 649 °F) E : solid \|\| in compression \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : 927 °C (1700 °F), oil quenched, tempered at 427 °C (800 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3.6x10³ cycles to 1x10⁷ cycles
300M (UNS K44220) (ASTM A579) (AMS 6419) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) DLL : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) MTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) CTE : solid \|\| -273 °C to 704 °C (-460 °F to 1299 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 20 °C (68 °F), longitudinal direction \|\| 0 to 0.22 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 121 °C (250 °F), longitudinal direction \|\| 0 to 0.22 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 204 °C (400 °F), longitudinal direction \|\| 0 to 0.23 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 288 °C (550 °F), longitudinal direction \|\| 0 to 0.23 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 20 °C (68 °F), transverse direction \|\| 0 to 0.22 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 121 °C (250 °F), transverse direction \|\| 0 to 0.22 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 204 °C (400 °F), transverse direction \|\| 0 to 0.23 mm/mm strain SSC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 0.00167/s \|\| tested at 288 °C (550 °F), transverse direction \|\| 0 to 0.23 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 20 °C (68 °F), longitudinal direction \|\| 0 to 0.21 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 121 °C (250 °F), longitudinal direction \|\| 0 to 0.22 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 204 °C (400 °F), longitudinal direction \|\| 0 to 0.23 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 288 °C (550 °F), longitudinal direction \|\| 0 to 0.23 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 20 °C (68 °F), transverse direction \|\| 0 to 0.22 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 121 °C (250 °F), transverse direction \|\| 0 to 0.22 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 204 °C (400 °F), transverse direction \|\| 0 to 0.23 mm/mm strain SSCC : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), 8.3x10^-⁵/s \|\| tested at 288 °C (550 °F), transverse direction \|\| 0 to 0.23 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.78 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.78 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.76 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.77 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.77 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.8 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 0.1/s \|\| tested at 1140 °C (2084 °F) \|\| 0 to 0.55 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 1/s \|\| tested at 1140 °C (2084 °F) \|\| 0 to 0.58 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.55 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.52 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 10/s \|\| tested at 1140 °C (2084 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 25/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 25/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 25/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : austenitized at 1250 °C (2282 °F), 25/s \|\| tested at 1140 °C (2084 °F) \|\| 0 to 0.57 mm/mm strain UTS : solution annealed at 871 °C (1600 °F), oil quenched, tempered at 316 °C (600 °F) \|\| -18 °C to 371 °C (-1 °F to 700 °F) YS : solution annealed at 871 °C (1600 °F), oil quenched, tempered at 316 °C (600 °F) \|\| -18 °C to 371 °C (-1 °F to 700 °F) %El : solution annealed at 871 °C (1600 °F), oil quenched, tempered at 316 °C (600 °F) \|\| -18 °C to 371 °C (-1 °F to 700 °F) SR : heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| tested at 260 °C (500 °F) \|\| 1 h to 1,100 h FEN : forgings \|\| tested at 20 °C (68 °F), R = -1, axial, equivalent strain range \|\| 100 cycles to 1x10⁷ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), R = -2, axial, maximum stress \|\| 8x10⁴ cycles to 1x10⁷ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 500 cycles to 3x10⁶ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), R = 0.05, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 4x10³ cycles to 2x10⁶ cycles FSN : unnotched \|\| tested at 20 °C (68 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 3x10³ cycles to 1x10⁷ cycles FSN : unnotched \|\| tested at 149 °C (300 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : unnotched \|\| tested at 260 °C (500 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : notched, K_t = 2 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 2x10⁶ cycles FSN : notched, K_t = 2 \|\| tested at 20 °C (68 °F), R = -0.33, axial, maximum stress \|\| 6x10³ cycles to 3x10⁶ cycles FSN : notched, K_t = 2 \|\| tested at 20 °C (68 °F), R = 0.33, axial, maximum stress \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : notched, K_t = 3 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 100 cycles to 2x10⁶ cycles FSN : notched, K_t = 3 \|\| tested at 20 °C (68 °F), R = -0.3, axial, maximum stress \|\| 1x10⁴ cycles to 3x10⁶ cycles FSN : notched, K_t = 3 \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 500 cycles to 1x10⁷ cycles FSN : notched, K_t = 3 \|\| tested at 20 °C (68 °F), R = 0.33, axial, maximum stress \|\| 1x10⁴ cycles to 4x10⁵ cycles FSN : notched, K_t = 3 \|\| tested at 20 °C (68 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : notched, K_t = 3 \|\| tested at 149 °C (300 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : notched, K_t = 3 \|\| tested at 260 °C (500 °F), heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : notched, K_t = 5 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 3x10⁶ cycles FSN : notched, K_t = 5 \|\| tested at 20 °C (68 °F), R = -0.3, axial, maximum stress \|\| 8x10³ cycles to 2x10⁶ cycles FSN : notched, K_t = 5 \|\| tested at 20 °C (68 °F), R = 0.33, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles CRS : 0.2% plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| tested at 260 °C (500 °F) \|\| 0.4 h to 1,300 h CRS : 0.5% plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| tested at 260 °C (500 °F) \|\| 0.2 h to 950 h CRS : 1% plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| tested at 260 °C (500 °F) \|\| 0.4 h to 9,300 h IC : tested at 260 °C (500 °F), plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, heated to 871 °C (1600 °F), oil quenched, tempered at 302 °C (575 °F) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
AMS 5700 (UNS K66009) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| solution annealed \|\| 0 °C to 727 °C (32 °F to 1340 °F) TD : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) SH : solid \|\| 20 °C to 802 °C (68 °F to 1475 °F) UTS : annealed at 899 °C (1650 °F) & water treated \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : annealed at 899 °C (1650 °F) & water treated \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : annealed at 899 °C (1650 °F) & water treated \|\| 20 °C to 816 °C (68 °F to 1500 °F)
19-9 DL (UNS K63198) (ASTM A453/A457/A458/A477) (AISI 651) (SAE J467) (AMS 5526/5527/5579/5720/5721/5722)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : warm rolled \|\| stress relieved at 732 °C (1350 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : annealed \|\| 20 °C to 995 °C (68 °F to 1823 °F) YS : warm rolled \|\| stress relieved at 732 °C (1350 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : annealed \|\| 20 °C to 995 °C (68 °F to 1823 °F) %El : warm rolled \|\| stress relieved at 732 °C (1350 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F)
19-9 DX (UNS S63199) (AISI 652) (AMS 5538)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : hot-rolled & annealed \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : hot-rolled & annealed \|\| 2.54 mm (0.1 inch) sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : hot-rolled & annealed \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : hot-rolled & annealed \|\| average \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : hot-rolled & stress relieved \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : hot-rolled & stress relieved \|\| 2.54 mm (0.1 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : hot-rolled & stress relieved \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : hot-rolled & stress relieved \|\| average \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & annealed \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : hot-rolled & annealed \|\| 2.54 mm (0.1 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & annealed \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & annealed \|\| average \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & stress relieved \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : hot-rolled & stress relieved \|\| 2.54 mm (0.1 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & stress relieved \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled & stress relieved \|\| average \|\| 20 °C to 816 °C (68 °F to 1500 °F) YSC : hot-rolled & annealed \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : hot-rolled & stress relieved \|\| AMS 5538 sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 28 h to 640 h SR : sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 2 h to 650 h SR : sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 1 h to 775 h SR : sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 2 h to 810 h SR : sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) SR : bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 1 h to 190 h SR : bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 2 h to 285 h SR : bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 8 h to 340 h SR : bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 1 h to 310 h SR : bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.2 h to 100 h CRS : 0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 22 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 0.25 h to 3 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 35 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.01 h to 200 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 105 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 5 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 115 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.2 h to 320 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.8 h to 200 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 0.75 h to 15 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 355 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.35 h to 680 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.14 h to 405 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 2 h to 55 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.6 h to 715 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.8 h to 1,600 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 1,000 h CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 4.5 h to 200 h CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 305 h CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.17 h to 340 h CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 0.6 h to 215 h CRS : 5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 538 °C (1000 °F) \|\| 10 h to 420 h CRS : 5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 649 °C (1200 °F) \|\| 0.7 h to 525 h CRS : 5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 732 °C (1350 °F) \|\| 0.4 h to 570 h CRS : 5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| tested at 816 °C (1500 °F) \|\| 1 h to 430 h CRS : 5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 1 h CRS : 0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 2 h to 85 h CRS : 0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 8 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 0.3 h to 260 h CRS : 0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 34 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 1 h to 440 h CRS : 0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.4% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.3 h to 115 h CRS : 0.4% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 2 h to 620 h CRS : 0.4% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 225 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 4 h to 805 h CRS : 0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 649 °C (1200 °F) \|\| 1 h to 690 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 26 h to 165 h CRS : 1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| tested at 732 °C (1350 °F) \|\| 62 h to 142 h CRS : 2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 0.6 h to 3 h CRS : 0.1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 3 h CRS : 0.1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.2 h to 3 h CRS : 0.1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 1 h CRS : 0.1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 0.17 h to 10 h CRS : 0.2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 0.7 h to 5 h CRS : 0.2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.4 h to 10 h CRS : 0.2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 4 h CRS : 0.2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.3% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 21 h CRS : 0.3% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 1 h to 10 h CRS : 0.3% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.7 h to 24 h CRS : 0.3% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 7 h CRS : 0.3% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 0.1 h to 42 h CRS : 0.5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 3 h to 30 h CRS : 0.5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.5 h to 58 h CRS : 0.5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.1 h to 13 h CRS : 0.5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 0.3 h to 67 h CRS : 1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 8 h to 67 h CRS : 1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 1 h to 101 h CRS : 1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.18 h to 26 h CRS : 1% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 2.5 h to 43 h CRS : 2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 649 °C (1200 °F) \|\| 20 h to 56 h CRS : 2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 732 °C (1350 °F) \|\| 2 h to 143 h CRS : 2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.4 h to 48 h CRS : 2% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 120 h CRS : 5% plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) IC : tested at 538 °C (1000 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.1 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.3 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 10,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled, in compression \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 1 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, bar, hot-rolled, stress relieved at 677 °C (1250 °F) \|\| 10 h \|\| 0 to 0.2 mm/mm strain
8 Ni steel	SSC : martensite \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s \|\| 0 to 0.49 mm/mm strain UTS* : martensite \|\| room temperature value YS* : martensite \|\| room temperature value %El* : martensite \|\| room temperature value FSN : martensite \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 600 cycles to 1x10⁷ cycles
9 Ni steel (UNS K81340) (ASTM A1334/A333/A353M/A522/A553M) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -221 °C to 538 °C (-366 °F to 1000 °F) DLL : solid \|\| -221 °C to 538 °C (-366 °F to 1000 °F) MTE : solid \|\| -221 °C to 538 °C (-366 °F to 1000 °F) CTE : solid \|\| -221 °C to 538 °C (-366 °F to 1000 °F) E : solid \|\| -198 °C to 38 °C (-325 °F to 100 °F) TC : solid \|\| heat-treated \|\| -221 °C to 538 °C (-366 °F to 1000 °F) SSC : double normalized & stress relieved \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : double normalized & stress relieved \|\| tested at -79 °C (-110 °F), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : double normalized & stress relieved \|\| tested at -195.6 °C (-320 °F), 3.3x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSC : double normalized & stress relieved \|\| tested at -252.7 °C (-422.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.002/s \|\| 0 to 0.2 mm/mm strain SSCC : as-quenched martensite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.2 mm/mm strain UTS : solid \|\| heat-treated at 802 °C (1475 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| heat-treated at 899 °C (1650 °F) \|\| -253 °C to 482 °C (-424 °F to 900 °F) YS : solid \|\| heat-treated at 802 °C (1475 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| heat-treated at 899 °C (1650 °F) \|\| -253 °C to 482 °C (-424 °F to 900 °F) %El : solid \|\| heat-treated at 899 °C (1650 °F) \|\| -253 °C to 482 °C (-424 °F to 900 °F) FEN : normalized & aged \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum strain \|\| 1.9x10⁴ cycles to 1x10⁷ cycles FEN : normalized & aged \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum strain \|\| 1x10⁴ cycles to 7.7x10⁵ cycles FEN : normalized & aged \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain \|\| 2.4x10⁴ cycles to 1x10⁷ cycles FEN : normalized & aged \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain \|\| 1.3x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 6x10⁵ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 4x10⁵ cycles
HP 9-4-20 (UNS K91461/K91472) (AMS 6468/6523/6525) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -251 °C to 1002 °C (-420 °F to 1835 °F) DLL : solid \|\| -251 °C to 1002 °C (-420 °F to 1835 °F) MTE : solid \|\| -251 °C to 1002 °C (-420 °F to 1835 °F) E : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) SH : solid \|\| 20 °C to 1438 °C (68 °F to 2620 °F) SH : liquid \|\| 1464 °C to 1747 °C (2667 °F to 3176 °F) SSC : C-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSC : C-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : C-1 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain SSCC : C-11 temper \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 0.7 mm/mm strain UTS : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : plate \|\| quenched & tempered \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : plate \|\| quenched & tempered \|\| 20 °C to 482 °C (68 °F to 900 °F)
HP 9-4-25 (UNS K91122) (AMS 6546) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) DLL : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) MTE : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) CTE : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) E : plate, in tension \|\| 1025 T temper, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : plate, in tension \|\| 1025 T temper, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : plate, in tension \|\| 1025 T temper, average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : plate, in compression \|\| 1025 T temper, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : plate, in compression \|\| 1025 T temper, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : plate, in compression \|\| 1025 T temper, average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in tension \|\| 1025 T temper, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in tension \|\| 1025 T temper, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in tension \|\| 1025 T temper, average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in compression \|\| 1025 T temper, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in compression \|\| 1025 T temper, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : forgings, in compression \|\| 1025 T temper, average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : average of all in tension \|\| 1025 T temper \|\| 20 °C to 482 °C (68 °F to 900 °F) E : average of all in compression \|\| 1025 T temper \|\| 20 °C to 482 °C (68 °F to 900 °F) E : average of all in tension & in compression \|\| 1025 T temper \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : plate \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : plate \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : forgings \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : forgings \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : plate \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : plate \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : forgings \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : forgings \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : plate \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : plate \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : forgings \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : forgings \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : plate \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : plate \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : forgings \|\| 1025 T temper, 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : forgings \|\| 1025 T temper, 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : plate, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h SR : plate, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : forgings, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h SR : forgings, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : forgings, 1025 T temper \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) FSN : plate, 1025 T temper, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, 1025 T temper, smooth \|\| tested at 260 °C (500 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, 1025 T temper, smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, 1025 T temper, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, 1025 T temper, notched \|\| tested at 260 °C (500 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, 1025 T temper, notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, smooth \|\| tested at 260 °C (500 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, notched \|\| tested at 260 °C (500 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, 1025 T temper, notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, plate, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, plate, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, plate, 1025 T temper \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 0.5% plastic strain, plate, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, plate, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, plate, 1025 T temper \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 0.2% plastic strain, forgings, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, forgings, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, forgings, 1025 T temper \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 0.5% plastic strain, forgings, 1025 T temper \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, forgings, 1025 T temper \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, forgings, 1025 T temper \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, plate, 1025 T temper \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, plate, 1025 T temper \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, plate, 1025 T temper \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, plate, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, plate, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, forgings, 1025 T temper \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, forgings, 1025 T temper \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, forgings, 1025 T temper \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 454 °C (850 °F), plastic strain, forgings, 1025 T temper \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, forgings, 1025 T temper \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, forgings, 1025 T temper \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, forgings, 1025 T temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, forgings, 1025 T temper \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, forgings, 1025 T temper \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain
HP 9-4-30 (UNS K91283) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) DLL : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) MTE : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) CTE : solid \|\| -251 °C to 93 °C (-420 °F to 199 °F) E : solid \|\| in tension \|\| -85 °C to 260 °C (-121 °F to 500 °F) E : solid \|\| in compression \|\| -85 °C to 260 °C (-121 °F to 500 °F) SSC : long transverse \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : long transverse \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : long transverse \|\| tested at 149 °C (300 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : long transverse \|\| tested at 260 °C (500 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : short transverse \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : short transverse \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : short transverse \|\| tested at 149 °C (300 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : short transverse \|\| tested at 260 °C (500 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : longitudinal \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : longitudinal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : longitudinal \|\| tested at 149 °C (300 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : longitudinal \|\| tested at 260 °C (500 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain UTS : unknown condition \|\| hand forging \|\| -73 °C to 260 °C (-100 °F to 500 °F) UTS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : unknown condition \|\| hand forging \|\| -73 °C to 260 °C (-100 °F to 500 °F) YS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) YSC : unknown condition \|\| hand forging \|\| -73 °C to 260 °C (-100 °F to 500 °F) %El : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : normalized at 899 °C (1650 °F), austenitized at 829 °C (1525 °F), tempered at 538 °C (1000 °F) \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) FSN : forged & heat-treated \|\| tested at 20 °C (68 °F), R = 0.1, axial, longitudinal, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : forged & heat-treated \|\| tested at 20 °C (68 °F), R = 0.1, axial, short transverse, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles
HP 9-4-45	D : solid \|\| bainitic treatment \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| bainitic treatment \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| bainitic treatment \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| bainitic treatment \|\| 20 °C to 427 °C (68 °F to 800 °F) E : in tension \|\| bainitic treatment, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : in tension \|\| bainitic treatment, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : in tension \|\| bainitic treatment, average \|\| 20 °C to 260 °C (68 °F to 500 °F) E : in compression \|\| bainitic treatment, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : in compression \|\| bainitic treatment, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : in compression \|\| bainitic treatment, average \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : plate \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : plate \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : forgings \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : forgings \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : plate \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : plate \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : forgings \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : forgings \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : plate \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : plate \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : forgings \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : forgings \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : plate \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : plate \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : forgings \|\| bainitic treatment, 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : forgings \|\| bainitic treatment, 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) FSN : plate, bainitic treatment, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, bainitic treatment, smooth \|\| tested at 149 °C (300 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, bainitic treatment, smooth \|\| tested at 260 °C (500 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, bainitic treatment, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, bainitic treatment, notched \|\| tested at 149 °C (300 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : plate, bainitic treatment, notched \|\| tested at 260 °C (500 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, smooth \|\| tested at 149 °C (300 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, smooth \|\| tested at 260 °C (500 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, notched \|\| tested at 149 °C (300 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : forgings, bainitic treatment, notched \|\| tested at 260 °C (500 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles

AerMet 100 (UNS K92580) (AMS 6478/6532)	D : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) D : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) D : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 0.0013/s \|\| 0 to 0.92 mm/mm strain SSC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 560/s \|\| 0 to 0.3 mm/mm strain SSC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 1200/s \|\| 0 to 0.86 mm/mm strain SSC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 2500/s \|\| 0 to 0.16 mm/mm strain SSC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 4200/s \|\| 0 to 0.215 mm/mm strain SSCC : austenitized/refrigerated/aged \|\| tested at 20 °C (68 °F), 0.0013/s \|\| 0 to 0.167 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.88 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.88 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : high temperature, 50/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.89 mm/mm strain UTS : solution annealed & aged \|\| sub-zero cooled \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solution annealed & aged \|\| sub-zero cooled \|\| 20 °C to 427 °C (68 °F to 800 °F) FSN : heat-treated to AMS 2759/2F \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4.3x10³ cycles to 2.25x10⁶ cycles RPB : solution treat & aged \|\| tested at 20 °C (68 °F) RPB : overaged annealed \|\| tested at 20 °C (68 °F) AP : solution treat & aged \|\| tested at 20 °C (68 °F) AP : overaged annealed \|\| tested at 20 °C (68 °F) BH : solution treat & aged \|\| tested at 20 °C (68 °F) BH : overaged annealed \|\| tested at 20 °C (68 °F) HB : solution treat & aged \|\| tested at 20 °C (68 °F) HB : overaged annealed \|\| tested at 20 °C (68 °F)
AerMet 340	D : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) D : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) D : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| heat-treated \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| average \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : heat-treated \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles
AF1410 (AMS 6527)	D* : solid \|\| room temperature value E : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) E : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) E : forged material, double austenitization & aged \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) G : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) G : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) G : forged material, double austenitization & aged \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) v : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) v : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) v : forged material, double austenitization & aged \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) K : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) K : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) K : forged material, double austenitization & aged \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) SSCC : homogenized, 0.001/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.89 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.9 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.88 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.88 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.88 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.88 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.87 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.88 mm/mm strain SSCC : homogenized, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.88 mm/mm strain UTS : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : forged material, double austenitization & aged \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : forged material, double austenitization & aged \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) FEN : normalized & overaged plate \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 100 cycles to 1x10⁷ cycles
Ferrium C61 (AMS 6517) (UNS K93061)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : tempered to 47 HRC to 50 HRC \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : tempered to 47 HRC to 50 HRC \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : tempered to 47 HRC to 50 HRC \|\| 20 °C to 427 °C (68 °F to 800 °F) FSN : shot peened \|\| tested at 20 °C (68 °F), R = 0.1, K_t = 1.0, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.1, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress \|\| 9x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress \|\| 800 cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles
Ferrium C64 (AMS 6509) (UNS K92731) (AMS 6509)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : bending \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.1, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress \|\| 5.1x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress \|\| 490 cycles to 1x10⁷ cycles
Ferrium M54 (AMS 6516)	D : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) DLL : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) MTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) CTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) UTS* : solid \|\| room temperature value YS* : solid \|\| room temperature value %El* : solid \|\| room temperature value FSN : in air \|\| tested at 20 °C (68 °F), R = 0.1, axial, uncoated, maximum stress \|\| 1.6x10⁴ cycles to 9.2x10⁶ cycles FSN : in air \|\| tested at 20 °C (68 °F), R = 0.1, axial, coated, maximum stress \|\| 8.3x10³ cycles to 9.8x10⁶ cycles FSN : in NaCl \|\| tested at 20 °C (68 °F), R = 0.1, axial, uncoated, maximum stress \|\| 3.3x10⁴ cycles to 1.7x10⁶ cycles FSN : in NaCl \|\| tested at 20 °C (68 °F), R = 0.1, axial, coated, maximum stress \|\| 2.6x10⁴ cycles to 9.6x10⁶ cycles
Ferrium S53 (UNS S10500)	D : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) DLL : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) MTE : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) CTE : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) E* : solid \|\| room temperature value TC : solid \|\| aged \|\| 20 °C to 593 °C (68 °F to 1099 °F) TD : solid \|\| aged \|\| 20 °C to 575 °C (68 °F to 1067 °F) SH : aged \|\| 20 °C to 575 °C (68 °F to 1067 °F) UTS* : solid \|\| room temperature value YS* : solid \|\| room temperature value %El* : solid \|\| room temperature value FSN : in air \|\| tested at 20 °C (68 °F), R = -0.33, K_t = 1.0, maximum stress \|\| 2.5x10⁵ cycles to 1x10⁷ cycles FSN : in 3.5 wt% NaCl \|\| tested at 20 °C (68 °F), R = -0.33, K_t = 1.0, maximum stress \|\| 2.3x10⁴ cycles to 5.5x10⁵ cycles
Boehler P800	D* : solid \|\| room temperature value TD : solid \|\| 1020 °C to 1451 °C (1868 °F to 2644 °F) TD : liquid \|\| 1474 °C to 1900 °C (2685 °F to 3452 °F) RHO : solid \|\| 1020 °C to 1461 °C (1868 °F to 2662 °F) RHO : liquid \|\| 1474 °C to 1900 °C (2685 °F to 3452 °F) SIGMA : solid \|\| 1020 °C to 1461 °C (1868 °F to 2662 °F) SIGMA : liquid \|\| 1474 °C to 1900 °C (2685 °F to 3452 °F)

255 (UNS S32520/S32550) (WNr 1.4507) (ISO/EN/DIN X2CrNiMoCuN25-6-3) (ASTM A240/A276M/A479)	D : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) DLL : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) MTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) CTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 502 °C (68 °F to 935 °F) SH : solid \|\| 20 °C to 502 °C (68 °F to 935 °F) UTS : heat-treated at 1120 °C (2048 °F), cooled rapidly \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : heat-treated at 1120 °C (2048 °F), cooled rapidly \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : heat-treated at 1120 °C (2048 °F), cooled rapidly \|\| 20 °C to 540 °C (68 °F to 1004 °F) RHO : solid \|\| 20 °C to 596 °C (68 °F to 1105 °F) SIGMA : solid \|\| 20 °C to 596 °C (68 °F to 1105 °F)
ATI 332Mo (UNS S35125) (ASTM A240)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E* : solid \|\| room temperature value UTS : 0.762 mm (0.03 inch) sheet \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : 0.762 mm (0.03 inch) sheet \|\| 20 °C to 900 °C (68 °F to 1652 °F) %El : 0.762 mm (0.03 inch) sheet \|\| 20 °C to 900 °C (68 °F to 1652 °F) FSN : 0.762 mm (0.03 inch) sheet \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 6x10⁴ cycles to 5x10⁶ cycles
ATI 334Mo (UNS S33425) (ASTM A240/A480)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E* : solid \|\| room temperature value UTS : 0.5 mm (0.0197 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : 0.5 mm (0.0197 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : 0.5 mm (0.0197 inch) sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) FSN : 1.02 mm (0.04 inch) sheet \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 2.65x10³ cycles to 1x10⁷ cycles
AL-6XN (UNS N08367) (WNr 1.4529) (ISO/EN/DIN X1NiCrMoCuN25-20-7) (JIS SUS836L) (ASTM A182/A194/A240/A249/A269/A270/A351/A358/A409/A479/A688/A743/A744/A813/A814/B366/B462/B472/B472/B564/B675/B676/B688/B690/B691/B804/B834) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1316 °C (68 °F to 2400 °F) DLL : solid \|\| 20 °C to 1316 °C (68 °F to 2400 °F) MTE : solid \|\| 20 °C to 1316 °C (68 °F to 2400 °F) CTE : solid \|\| 20 °C to 1316 °C (68 °F to 2400 °F) E : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 1316 °C (68 °F to 2400 °F) TD : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SH : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) SSC : 0.002/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.22 mm/mm strain SSC : 0.002/s \|\| tested at 500 °C (932 °F) \|\| 0 to 0.25 mm/mm strain SSC : 0.002/s \|\| tested at 600 °C (1112 °F) \|\| 0 to 0.254 mm/mm strain SSCC : as-received plate \|\| tested at -196.1 °C (-321.1 °F), 0.001/s \|\| 0 to 0.45 mm/mm strain SSCC : as-received plate \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 127 °C (260 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 227 °C (440 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 327 °C (620 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 427 °C (800 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 527 °C (980 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 627 °C (1160 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at 727 °C (1340 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSCC : as-received plate \|\| tested at -196.1 °C (-321.1 °F), 3500/s \|\| 0 to 0.34 mm/mm strain SSCC : as-received plate \|\| tested at 20 °C (68 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 227 °C (440 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 327 °C (620 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 427 °C (800 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 527 °C (980 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 627 °C (1160 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 727 °C (1340 °F), 3500/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at -196.1 °C (-321.1 °F), 8300/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 20 °C (68 °F), 8300/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 227 °C (440 °F), 8300/s \|\| 0 to 0.35 mm/mm strain SSCC : as-received plate \|\| tested at 727 °C (1340 °F), 8300/s \|\| 0 to 0.35 mm/mm strain UTS : annealed \|\| -268 °C to 538 °C (-451 °F to 1000 °F) YS : annealed \|\| -268 °C to 538 °C (-451 °F to 1000 °F) %El : annealed \|\| -268 °C to 538 °C (-451 °F to 1000 °F) FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
HT-9	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| tempered martensite \|\| 20 °C to 925 °C (68 °F to 1697 °F) TD : solid \|\| tempered martensite \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) RHO : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
IN-519 (WNr 1.4855) (ISO/EN/DIN GX40CrNiSiNb24-24)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : as-cast \|\| tested at 700 °C (1292 °F) \|\| 30 h to unknown strain rate h SR : as-cast \|\| tested at 750 °C (1382 °F) \|\| 4 h to unknown strain rate h SR : as-cast \|\| tested at 800 °C (1472 °F) \|\| 0.7 h to 3x10⁸ h SR : as-cast \|\| tested at 850 °C (1562 °F) \|\| 0.1 h to 2x10⁷ h SR : as-cast \|\| tested at 900 °C (1652 °F) \|\| 0.1 h to 2x10⁶ h SR : as-cast \|\| tested at 950 °C (1742 °F) \|\| 0.1 h to 3x10⁵ h SR : as-cast \|\| tested at 1000 °C (1832 °F) \|\| 0.1 h to 4x10⁴ h SR : as-cast \|\| tested at 1050 °C (1922 °F) \|\| 0.1 h to 7,000 h SR : as-cast \|\| tested at 1100 °C (2012 °F) \|\| 0.1 h to 1,300 h SR : as-cast \|\| Master curve (LMP) \|\| 700 °C to 1101 °C (1292 °F to 2014 °F) CRS : 1% total strain, as-cast \|\| tested at 800 °C (1472 °F) \|\| 100 h to 1x10⁴ h CRS : 1% total strain, as-cast \|\| tested at 900 °C (1652 °F) \|\| 100 h to 2x10⁴ h CRS : 1% total strain, as-cast \|\| tested at 1000 °C (1832 °F) \|\| 100 h to 2x10⁴ h CRS : 1% total strain, as-cast \|\| Master curve (LMP) \|\| 800 °C to 1001 °C (1472 °F to 1834 °F) RHO : solid \|\| as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| as-cast \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Lapelloy C	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : hardened & tempered \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : hardened & tempered \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : hardened & tempered \|\| 20 °C to 704 °C (68 °F to 1299 °F)
H-46	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E* : solid \|\| room temperature value TC : solid \|\| unknown condition \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS : 1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : 1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : 1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled \|\| 20 °C to 650 °C (68 °F to 1202 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Chromium steel (12.25 Cr wt%)	D : solid \|\| annealed \|\| 20 °C to 770 °C (68 °F to 1418 °F) DLL : solid \|\| annealed \|\| 20 °C to 770 °C (68 °F to 1418 °F) MTE : solid \|\| annealed \|\| 20 °C to 770 °C (68 °F to 1418 °F) CTE : solid \|\| annealed \|\| 20 °C to 770 °C (68 °F to 1418 °F) SSCC : 0.002/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.626 mm/mm strain SSCC : 0.002/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.71 mm/mm strain SSCC : 0.002/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 0.002/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.867 mm/mm strain SSCC : 0.002/s \|\| tested at 1232 °C (2250 °F) \|\| 0 to 0.754 mm/mm strain SSCC : 0.02/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.63 mm/mm strain SSCC : 0.02/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.02/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.02/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.66 mm/mm strain SSCC : 0.02/s \|\| tested at 1232 °C (2250 °F) \|\| 0 to 0.71 mm/mm strain SSCC : 0.5/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.5/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 0.5/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.5/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.5/s \|\| tested at 1232 °C (2250 °F) \|\| 0 to 0.65 mm/mm strain
NCF 3015 (UNS S66315)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : hardened & tempered \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : hardened & tempered \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 400 h SR : bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 100 h SR : bar \|\| Master curve (LMP) \|\| 732 °C to 816 °C (1349 °F to 1501 °F)
1.3964 (WNr 1.3964) (ISO/EN/DIN X2CrNiMnMoNNb21-16-5-3)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
1.4037 (WNr 1.4037) (ISO/EN/DIN X65Cr13)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
1.4122 (WNr 1.4122) (ISO/EN/DIN X39CrMo17-1)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4713 (WNr 1.4713) (ISO/EN/DIN X10CrAl7/X10CrAlSi7) (AFNOR Z8CA7)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4724 (WNr 1.4724) (ISO/EN/DIN X10CrAl13/X10CrAlSi13) (AFNOR Z10C13/Z13C13) (GB & GB/T OCr13Al)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4732 (WNr 1.4732) (ISO/EN/DIN X80CrSiMoW15-2)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4736 (WNr 1.4736) (ISO/EN/DIN X3CrAlTi18-2)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
1.4821 (WNr 1.4821) (ISO/EN/DIN X15CrNiSi25-4/X20CrNiSi25-4) (AFNOR Z20CNS25-04) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| solution annealed \|\| 0 °C to 727 °C (32 °F to 1340 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4873 (WNr 1.4873) (ISO/EN/DIN X45CrNiW18-9) (SAE EV9)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : solution treated \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solution treated \|\| 20 °C to 800 °C (68 °F to 1472 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4887 (WNr 1.4887) (ISO/EN/DIN X6NiCrNbCe32-27)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 600 °C to 1001 °C (1112 °F to 1834 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
1.4910 (WNr 1.4910) (ISO/EN/DIN X3CrNiMoBN17-13-3)	D : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) DLL : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) MTE : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) CTE : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) TC : solid \|\| solution annealed \|\| 20 °C to 827 °C (68 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
1.4922 (WNr 1.4922) (ISO/EN/DIN X20CrMoV11-1/X22CrMoV11-1) (GB & GB/T 1Cr11MoV) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) TC : solid \|\| solution annealed \|\| 0 °C to 627 °C (32 °F to 1160 °F) YS : hardened & tempered \|\| diameters up to 160 mm (6.3 inch) \|\| 20 °C to 601 °C (68 °F to 1114 °F) SR : hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : hardened & tempered \|\| Master curve (LMP) \|\| 480 °C to 560 °C (896 °F to 1040 °F) CRS : 1% total strain, hardened & tempered \|\| tested at 480 °C (896 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% total strain, hardened & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% total strain, hardened & tempered \|\| tested at 520 °C (968 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% total strain, hardened & tempered \|\| tested at 540 °C (1004 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% total strain, hardened & tempered \|\| tested at 560 °C (1040 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% total strain, hardened & tempered \|\| Master curve (LMP) \|\| 480 °C to 560 °C (896 °F to 1040 °F)
1.4923 (WNr 1.4923) (ISO/EN/DIN X21CrMoNiV12-1/X22CrMoV12-1)	D : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) DLL : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) MTE : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) CTE : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) TC : solid \|\| 20 °C to 651 °C (68 °F to 1204 °F) TD : solid \|\| 20 °C to 601 °C (68 °F to 1114 °F) SH : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : austenitized at 1010 °C (1850 °F) & tempered at 510 °C (950 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : austenitized at 1010 °C (1850 °F) & tempered at 510 °C (950 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : austenitized at 1010 °C (1850 °F) & tempered at 510 °C (950 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
1.4960 (WNr 1.4960) (ISO/EN/DIN X40CrNiCoNb1313) (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC : solid \|\| solution annealed plus anneal \|\| 0 °C to 727 °C (32 °F to 1340 °F)
Ferrotherm 4742 (WNr 1.4742) (ISO/EN/DIN X10CrAl18/X10CrAlSi18) (AFNOR Z10CAS18) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E* : solid \|\| room temperature value TC : solid \|\| solution annealed \|\| 0 °C to 827 °C (32 °F to 1520 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Ferrotherm 4828 (WNr 1.4828) (ISO/EN/DIN X15CrNiSi2012) (JIS SUH309/SUS309) (AFNOR Z17CNS20-12) (GB & GB/T 1Cr20Ni14Si2) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| solution annealed \|\| 0 °C to 827 °C (32 °F to 1520 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Thermodur E40K	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Dynaflex Vac-Arc	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : austenitized & tempered \|\| tested at 232 °C (450 °F) \|\| 0.01 h to 770 h SR : austenitized & tempered \|\| tested at 427 °C (800 °F) \|\| 0.2 h to 400 h SR : austenitized & tempered \|\| tested at 538 °C (1000 °F) \|\| 0.01 h to 30 h FSN : austenitized & tempered \|\| tested at 24 °C (75 °F), R = 0, axial, maximum stress \|\| 4.9x10⁴ cycles to 1x10⁷ cycles FSN : austenitized & tempered \|\| tested at 24 °C (75 °F), R = -1, axial, maximum stress \|\| 7.9x10⁴ cycles to 1x10⁷ cycles FSN : austenitized & tempered \|\| tested at 427 °C (800 °F), R = 0, axial, maximum stress \|\| 7.1x10⁴ cycles to 1x10⁸ cycles FSN : austenitized & tempered \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 3.6x10⁴ cycles to 1x10⁸ cycles FSN : austenitized & tempered \|\| tested at 538 °C (1000 °F), R = 0, axial, maximum stress \|\| 2.5x10⁵ cycles to 1x10⁸ cycles FSN : austenitized & tempered \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 6.1x10⁴ cycles to 1x10⁸ cycles
COST E	YS : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : annealed \|\| tested at 566 °C (1050 °F) \|\| 1.5x10³ h to 2x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1.4x10³ h to 3x10⁴ h SR : annealed \|\| tested at 621 °C (1150 °F) \|\| 900 h to 3x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 230 h to 4x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 565 °C to 650 °C (1049 °F to 1202 °F)
COST FB2 (ISO/EN/DIN X13CrMoCoVNbNB921)	SSCC : solution annealed, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.6 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.62 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1179 °C (2155 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1230 °C (2246 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.001/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.59 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1179 °C (2155 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1230 °C (2246 °F) \|\| 0 to 0.62 mm/mm strain SSCC : solution annealed, 0.01/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.59 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.59 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1179 °C (2155 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1230 °C (2246 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.1/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.63 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.59 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1179 °C (2155 °F) \|\| 0 to 0.58 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1230 °C (2246 °F) \|\| 0 to 0.58 mm/mm strain SSCC : solution annealed, 0.5/s \|\| tested at 1300 °C (2372 °F) \|\| 0 to 0.61 mm/mm strain
CBS-50 NiL (UNS K91231) (AMS 6278)	D : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) E* : solid \|\| room temperature value FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress \|\| 9x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress \|\| 2.5x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress \|\| 8.4x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress \|\| 5x10³ cycles to 1x10⁷ cycles
CBS-600 (AMS 6255) (AMS 6255)	D : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) E : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) G : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) v : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) K : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) TC : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) TD : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : solid \|\| 20 °C to 551 °C (68 °F to 1024 °F) UTS : tempered at 843 °C (1550 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS : tempered at 927 °C (1700 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : tempered at 843 °C (1550 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : tempered at 927 °C (1700 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : tempered at 843 °C (1550 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : tempered at 927 °C (1700 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F)
CSS-42L VIM-VAR (AMS 5932) (AMS 5932)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| 20 °C to 901 °C (68 °F to 1654 °F) TD : solid \|\| 20 °C to 901 °C (68 °F to 1654 °F) SH : solid \|\| 20 °C to 901 °C (68 °F to 1654 °F) FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress \|\| 4.2x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress \|\| 110 cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress \|\| 5.8x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress \|\| 110 cycles to 2x10⁴ cycles
CRB-7 alloy	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
Sanicro 25 (UNS S31035)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SSC : annealed \|\| tested at 23 °C (73 °F), 0.002/s \|\| 0 to 0.46 mm/mm strain SSC : annealed \|\| tested at 700 °C (1292 °F), 0.002/s \|\| 0 to 0.41 mm/mm strain UTS : tubes \|\| cold pilgered \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : tubes \|\| extruded \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : tubes \|\| cold pilgered \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : tubes \|\| extruded \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : annealed cold worked tube \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed cold worked tube \|\| Master curve (LMP) \|\| 600 °C to 751 °C (1112 °F to 1384 °F) FEN : annealed \|\| tested at 23 °C (73 °F), R = -1, axial, plastic strain amplitude \|\| 2x10³ cycles to 2x10⁵ cycles FEN : annealed \|\| tested at 700 °C (1292 °F), R = -1, axial, plastic strain amplitude \|\| 155 cycles to 2x10⁵ cycles FSN : annealed \|\| tested at 23 °C (73 °F), R = -1, axial, stress amplitude \|\| 820 cycles to 2x10⁵ cycles FSN : annealed \|\| tested at 700 °C (1292 °F), R = -1, axial, stress amplitude \|\| 210 cycles to 2x10⁵ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value

201 (UNS S20100) (WNr 1.4372) (ISO/EN/DIN X12CrMnNiN17-7-5) (JIS SUS201) (ASTM A412/A429/A666) (AISI 201) (SAE J405) (AFNOR Z12CMN17-07Az) (GB & GB/T 1Cr17Mn6Ni5N) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 871 °C (32 °F to 1600 °F) DLL : solid \|\| 0 °C to 871 °C (32 °F to 1600 °F) MTE : solid \|\| 0 °C to 871 °C (32 °F to 1600 °F) CTE : solid \|\| 0 °C to 871 °C (32 °F to 1600 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : annealed \|\| tested at 20 °C (68 °F), longitudinal, unknown strain rate \|\| 0 to 0.01 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), transverse, unknown strain rate \|\| 0 to 0.01 mm/mm strain SSC : 10% cold worked \|\| tested at 20 °C (68 °F), longitudinal, unknown strain rate \|\| 0 to 3.5x10^-³ mm/mm strain SSC : 10% cold worked \|\| tested at 20 °C (68 °F), transverse, unknown strain rate \|\| 0 to 8x10^-³ mm/mm strain SSC : 18% cold worked \|\| tested at 20 °C (68 °F), longitudinal, unknown strain rate \|\| 0 to 6.2x10^-³ mm/mm strain SSC : 18% cold worked \|\| tested at 20 °C (68 °F), transverse, unknown strain rate \|\| 0 to 6.9x10^-³ mm/mm strain SSC : 36% cold worked \|\| tested at 20 °C (68 °F), longitudinal, unknown strain rate \|\| 0 to 5.7x10^-³ mm/mm strain SSC : 36% cold worked \|\| tested at 20 °C (68 °F), transverse, unknown strain rate \|\| 0 to 6x10^-³ mm/mm strain SSC : 2 mm (0.0787 inch) thick sheet, longitudinal \|\| tested at 20 °C (68 °F), as-received, 0.001/s \|\| 0 to 0.43 mm/mm strain SSC : 2 mm (0.0787 inch) thick sheet, longitudinal \|\| tested at 20 °C (68 °F), 700 °C (1292 °F) for 10 min, 0.001/s \|\| 0 to 0.48 mm/mm strain UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : annealed \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F) HE : solid \|\| foil \|\| 20 °C to 500 °C (68 °F to 932 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
201L (UNS S20103) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E* : effect of cold work on RT value, in tension \|\| annealed \|\| room temperature value E* : effect of cold work on RT value, in tension \|\| 10% cold reduction \|\| room temperature value E* : effect of cold work on RT value, in tension \|\| 20% cold reduction \|\| room temperature value E* : effect of cold work on RT value, in tension \|\| 40% cold reduction \|\| room temperature value E* : effect of cold work on RT value, in compression \|\| annealed \|\| room temperature value E* : effect of cold work on RT value, in compression \|\| 10% cold reduction \|\| room temperature value E* : effect of cold work on RT value, in compression \|\| 20% cold reduction \|\| room temperature value E* : effect of cold work on RT value, in compression \|\| 40% cold reduction \|\| room temperature value TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : annealed, pickled and skin-passed condition \|\| tested at 0 °C (32 °F), 1x10^-⁴/s \|\| 0 to 0.42 mm/mm strain SSC : annealed, pickled and skin-passed condition \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.456 mm/mm strain SSC : annealed, pickled and skin-passed condition \|\| tested at 50 °C (122 °F), 1x10^-⁴/s \|\| 0 to 0.536 mm/mm strain SSC : annealed, pickled and skin-passed condition \|\| tested at 150 °C (302 °F), 1x10^-⁴/s \|\| 0 to 0.439 mm/mm strain SSC : annealed, pickled and skin-passed condition \|\| tested at 200 °C (392 °F), 1x10^-⁴/s \|\| 0 to 0.343 mm/mm strain UTS : annealed, pickled and skin-passed condition \|\| 0 °C to 200 °C (32 °F to 392 °F) UTS* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value UTS* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value UTS* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value YS : annealed, pickled and skin-passed condition \|\| 0 °C to 200 °C (32 °F to 392 °F) YS* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value YS* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value YS* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value %El : annealed, pickled and skin-passed condition \|\| 0 °C to 200 °C (32 °F to 392 °F) %El* : effect of cold work on RT value, longitudinal \|\| 0% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 5% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 10% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 20% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 30% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 40% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 50% cold work \|\| room temperature value %El* : effect of cold work on RT value, longitudinal \|\| 60% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 0% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 5% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 10% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 20% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 30% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 40% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 50% cold work \|\| room temperature value %El* : effect of cold work on RT value, transverse \|\| 60% cold work \|\| room temperature value HE : solid \|\| foil \|\| 20 °C to 500 °C (68 °F to 932 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
201LN (UNS S20153) (WNr 1.4371) (ISO/EN/DIN X2CrMnNiN17-7-5) (ASTM A240) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| solution annealed \|\| 0 °C to 727 °C (32 °F to 1340 °F) TD : solid \|\| solution annealed \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.538 mm/mm strain SSC : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 500 °C (932 °F), 0.001/s \|\| 0 to 0.31 mm/mm strain SSC : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 600 °C (1112 °F), 0.001/s \|\| 0 to 0.284 mm/mm strain SSC : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 700 °C (1292 °F), 0.001/s \|\| 0 to 0.263 mm/mm strain SSC : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 800 °C (1472 °F), 0.001/s \|\| 0 to 0.253 mm/mm strain UTS : annealed \|\| -206 °C to 800 °C (-339 °F to 1472 °F) YS : annealed \|\| -206 °C to 800 °C (-339 °F to 1472 °F) %El : annealed \|\| -184 °C to 800 °C (-299 °F to 1472 °F) SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 600 °C (1112 °F) \|\| 6 h to 3,000 h SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 650 °C (1202 °F) \|\| 10 h to 45 h SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 700 °C (1292 °F) \|\| 2 h to 1,320 h SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 750 °C (1382 °F) \|\| 5 h to 100 h SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| tested at 800 °C (1472 °F) \|\| 1 h to 800 h SR : continuous cast 28 mm (1.1 inch) plate, solution treated at 1150 °C (2102 °F) \|\| Master curve (LMP) \|\| 600 °C to 801 °C (1112 °F to 1474 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
202 (UNS S20200) (WNr 1.4373) (ISO/EN/DIN X18CrMnNiN18-9-5) (JIS SUS202) (ASTM A314/A412/A429/A473/A666) (AISI 202) (SAE J405) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 761 °C (32 °F to 1402 °F) DLL : solid \|\| 0 °C to 761 °C (32 °F to 1402 °F) MTE : solid \|\| 0 °C to 761 °C (32 °F to 1402 °F) CTE : solid \|\| 0 °C to 761 °C (32 °F to 1402 °F) TC : solid \|\| annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F)
301 (UNS S30100) (WNr 1.4310) (ISO/EN/DIN X10CrNi18-8) (JIS SUS301) (ASTM A167/A177/A554/A666) (AISI 301) (SAE J405) (AMS 5517/5518/5519) (AFNOR Z11CN18-08/Z12CN17-07) (GB & GB/T 1Cr17Ni7/1Cr17Ni8) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) DLL : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) MTE : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) E : average \|\| -253 °C to 500 °C (-424 °F to 932 °F) E : 60% cold reduction \|\| longitudinal \|\| -253 °C to 27 °C (-424 °F to 80 °F) E : 60% cold reduction \|\| transverse \|\| -253 °C to 27 °C (-424 °F to 80 °F) E : extra hard sheet \|\| -253 °C to 27 °C (-424 °F to 80 °F) E : full hard rod \|\| -196 °C to 27 °C (-321 °F to 80 °F) G : average \|\| -253 °C to 27 °C (-424 °F to 80 °F) v : average \|\| -253 °C to 27 °C (-424 °F to 80 °F) K : average \|\| -253 °C to 27 °C (-424 °F to 80 °F) TC : solid \|\| -137 °C to 943 °C (-215 °F to 1729 °F) TD : solid \|\| cold-rolled \|\| 18 °C to 943 °C (64 °F to 1729 °F) TD : solid \|\| annealed \|\| -157 °C to 982 °C (-251 °F to 1800 °F) SH : solid \|\| -200 °C to 982 °C (-328 °F to 1800 °F) SSC : annealed at 600 °C (1112 °F) \|\| tested at 0 °C (32 °F), 0.00103/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 10 °C (50 °F), 0.00103/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 20 °C (68 °F), 0.00103/s \|\| 0 to 0.52 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 30 °C (86 °F), 0.00103/s \|\| 0 to 0.52 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 40 °C (104 °F), 0.00103/s \|\| 0 to 0.63 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 50 °C (122 °F), 0.00103/s \|\| 0 to 0.63 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 60 °C (140 °F), 0.00103/s \|\| 0 to 0.69 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 70 °C (158 °F), 0.00103/s \|\| 0 to 0.58 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 80 °C (176 °F), 0.00103/s \|\| 0 to 0.53 mm/mm strain SSC : annealed at 600 °C (1112 °F) \|\| tested at 90 °C (194 °F), 0.00103/s \|\| 0 to 0.53 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.41 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.41 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.42 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.37 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 85/s \|\| 0 to 0.32 mm/mm strain UTS : annealed \|\| -269 °C to 871 °C (-452 °F to 1600 °F) UTS : cold-rolled quarter hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : cold-rolled half hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : extra hard \|\| -253 °C to 20 °C (-424 °F to 68 °F) UTS : 60% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 3.2, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 3.2, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 6.3, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 6.3, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 19, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| notched, K_t = 19, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| weld joint, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 60% cold-rolled \|\| weld joint, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) YS : annealed \|\| -196 °C to 871 °C (-321 °F to 1600 °F) YS : cold-rolled quarter hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : cold-rolled half hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : extra hard \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS : 60% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) YS : 60% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : annealed \|\| -269 °C to 871 °C (-452 °F to 1600 °F) %El : cold-rolled quarter hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : cold-rolled half hard \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : extra hard \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El : 60% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| weld joint, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| weld joint, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) SR : half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 0.3 h to 10 h SR : half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 0.2 h to 14 h SR : half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 0.8 h to 55 h SR : half-hard 1.27 mm (0.05 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) SR : full-hard & stress relieved 0.813 mm (0.032 inch) sheet \|\| tested at 427 °C (800 °F) \|\| 0.2 h to 173 h SR : full-hard & stress relieved 0.813 mm (0.032 inch) sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 316 h SR : full-hard & stress relieved 0.813 mm (0.032 inch) sheet \|\| tested at 538 °C (1000 °F) \|\| 3 h to 260 h SR : full-hard & stress relieved 0.813 mm (0.032 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 250 h SR : full-hard & stress relieved 0.813 mm (0.032 inch) sheet \|\| Master curve (LMP) \|\| 426 °C to 650 °C (799 °F to 1202 °F) SR : annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 2 h to 2,110 h SR : annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 0.5 h to 805 h SR : annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at -252.7 °C (-422.9 °F), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 8x10⁴ cycles FSN : full hard \|\| tested at 20 °C (68 °F), axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.43x10⁴ cycles to 1x10⁷ cycles FSN : full hard \|\| tested at 20 °C (68 °F), axial, K_t = 4, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.42x10⁴ cycles to 1x10⁷ cycles FSN : full hard \|\| tested at 20 °C (68 °F), axial, fusion welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 3.26x10⁴ cycles to 1x10⁷ cycles FSN : full hard \|\| tested at 20 °C (68 °F), axial, spot welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.4x10⁴ cycles to 1x10⁷ cycles CRS : 1% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 0.6 h to 100 h CRS : 1% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 0.3 h to 10 h CRS : 1% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 0.3 h to 10 h CRS : 1% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) CRS : 2% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 5 h CRS : 2% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 0.8 h to 14 h CRS : 2% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 0.5 h to 20 h CRS : 2% plastic strain, half-hard 1.27 mm (0.05 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) CRS : 0.1% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 0.9 h to 5 h CRS : 0.2% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 0.32 h to 35 h CRS : 0.2% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 0.2 h to 45 h CRS : 0.3% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 0.67 h to 90 h CRS : 0.5% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 0.16 h to 315 h CRS : 0.5% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 0.7 h to 400 h CRS : 0.5% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 1% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 0.43 h to 1,400 h CRS : 1% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 0.15 h to 1,000 h CRS : 1% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 2% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 649 °C (1200 °F) \|\| 1.75 h to 115 h CRS : 2% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 0.3 h to 570 h CRS : 2% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 3% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 8 h to 220 h CRS : 4% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 9 h to 260 h CRS : 5% plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| tested at 732 °C (1350 °F) \|\| 11.5 h to 285 h IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 3,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1,000 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, half-hard 1.27 mm (0.05 inch) sheet \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 10 h \|\| 0 to 0.4 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed then cold-drawn 12.7 mm (0.5 inch) rod \|\| 300 h \|\| 0 to 0.2 mm/mm strain NE : solid \|\| in air at 802 °C (1475 °F) \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished \|\| -185 °C to 841 °C (-301 °F to 1546 °F) NE : solid \|\| clean & smooth \|\| -185 °C to 817 °C (-301 °F to 1502 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SIGMA : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
301LN (UNS S30153) (WNr 1.4318) (ISO/EN/DIN X2CrNiN18-7) (JIS G4305/SUS301L) (ASTM A666)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 0% additional cold-rolling \|\| 0 to 0.34 mm/mm strain SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 5% additional cold-rolling \|\| 0 to 0.265 mm/mm strain SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 14.5% additional cold-rolling \|\| 0 to 0.2 mm/mm strain SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 19% additional cold-rolling \|\| 0 to 0.175 mm/mm strain SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 26% additional cold-rolling \|\| 0 to 0.14 mm/mm strain SSC : annealed sheet, effect of cold-rolling \|\| tested at 25 °C (77 °F), 6.67x10^-⁴/s, 32% additional cold-rolling \|\| 0 to 0.7 mm/mm strain SSC : annealed sheet, effect of grain size \|\| tested at 20 °C (68 °F), 1.5/s, 16 micron grains, as-received \|\| 0 to 0.335 mm/mm strain SSC : annealed sheet, effect of grain size \|\| tested at 20 °C (68 °F), 1.5/s, 0.75 micron grains, reversion annealed \|\| 0 to 0.335 mm/mm strain UTS* : 1.5 mm (0.0591 inch) sheet \|\| annealed \|\| room temperature value UTS* : 1.5 mm (0.0591 inch) sheet \|\| cold-rolled 30% \|\| room temperature value YS* : 1.5 mm (0.0591 inch) sheet \|\| annealed \|\| room temperature value YS* : 1.5 mm (0.0591 inch) sheet \|\| cold-rolled 30% \|\| room temperature value %El* : 1.5 mm (0.0591 inch) sheet \|\| annealed \|\| room temperature value %El* : 1.5 mm (0.0591 inch) sheet \|\| cold-rolled 30% \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
302 (UNS S30200) (WNr 1.4300) (ISO/EN/DIN X12CrNi18-8) (JIS SUS302) (ASTM A167/A240/A276/A313/A479/A580) (AISI 302) (SAE J230/J405) (AMS 5515/5516/5600) (AFNOR Z10CN18.09) (GB & GB/T 1Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) DLL : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) MTE : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) E : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) G : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) v : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) K : solid \|\| -240 °C to 816 °C (-400 °F to 1500 °F) TC : solid \|\| annealed \|\| 0 °C to 927 °C (32 °F to 1700 °F) TD : solid \|\| annealed \|\| 17 °C to 950 °C (62 °F to 1742 °F) SH : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) UTS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) UTS : cold-drawn \|\| -253 °C to 20 °C (-424 °F to 68 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) YS : cold-drawn \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) %El : cold-drawn \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : solid \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : solid \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 704 °C (1300 °F) \|\| 6 h to 1x10⁵ h SR : solid \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 816 °C (1500 °F) \|\| 2 h to 1x10⁵ h SR : solid \|\| tested at 927 °C (1700 °F) \|\| 1 h to 6 h SR : solid \|\| tested at 1077 °C (1970 °F) \|\| 2 h to 23 h SR : solid \|\| Master curve (LMP) \|\| 480 °C to 1077 °C (896 °F to 1970 °F) CRS : 1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) SIGMA : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F)
302HQ (UNS S30430) (JIS SUSXM7) (ASTM A276/A493/F593) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F) YS : annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
302HQ-FM (UNS S30431) (JIS SUS304J3)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
303 (UNS S30300) (WNr 1.4305) (ISO/EN/DIN X8CrNiS18-9) (JIS SUS303) (ASTM A194/A314/A320/A473/A473/A581/A582/A895) (AISI 303) (SAE J405) (AMS 5640) (AFNOR Z10CNF18-09/Z8CNF18-09) (GB & GB/T Y1Cr18Ni9/Y1Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 650 °C (-460 °F to 1202 °F) DLL : solid \|\| -273 °C to 650 °C (-460 °F to 1202 °F) MTE : solid \|\| -273 °C to 650 °C (-460 °F to 1202 °F) E : solid \|\| -273 °C to 320 °C (-460 °F to 608 °F) TC : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed at 1038 °C (1900 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : annealed at 1038 °C (1900 °F) \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed at 1038 °C (1900 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) HE : solid \|\| polished then oxidized \|\| 315 °C to 1093 °C (599 °F to 2000 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -269 °C to 902 °C (-452 °F to 1655 °F) SIGMA : solid \|\| -269 °C to 902 °C (-452 °F to 1655 °F)
303Al (UNS S30345)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)
304 (UNS S30400) (WNr 1.4301) (ISO/EN/DIN X5CrNi18-10/X5CrNi18-9) (JIS SUS304) (ASTM A167/A182/A193/A276/A314/A320/A479) (AISI 304) (SAE J405) (AMS 5501/5513/5639/5647/5697) (AFNOR Z6CN18-09/Z7CN18-09) (GB & GB/T 0Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : annealed at 1093 °C (2000 °F) \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 1.8 mm/mm strain SSC : annealed at 1093 °C (2000 °F) \|\| tested at 430 °C (806 °F), 0.004/s \|\| 0 to 0.6 mm/mm strain SSC : annealed at 1093 °C (2000 °F) \|\| tested at 649 °C (1200 °F), 0.004/s \|\| 0 to 0.45 mm/mm strain SSC : annealed at 1093 °C (2000 °F) \|\| tested at 816 °C (1500 °F), 0.004/s \|\| 0 to 0.5 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at -196.1 °C (-321.1 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at -120 °C (-184 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at -80 °C (-112 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at -40 °C (-40 °F), unknown strain rate \|\| 0 to 0.47 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 0 °C (32 °F), unknown strain rate \|\| 0 to 0.7 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 23 °C (73 °F), unknown strain rate \|\| 0 to 0.75 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 40 °C (104 °F), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 80 °C (176 °F), unknown strain rate \|\| 0 to 0.675 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 120 °C (248 °F), unknown strain rate \|\| 0 to 0.475 mm/mm strain SSC : annealed at 1050 °C (1922 °F), water quenched \|\| tested at 160 °C (320 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1041 °C (1905 °F), water cooled \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 1.37 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.56 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 550 °C (1022 °F), 4x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 600 °C (1112 °F), 4x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 650 °C (1202 °F), 4x10^-⁴/s \|\| 0 to 0.36 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 700 °C (1292 °F), 4x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 750 °C (1382 °F), 4x10^-⁴/s \|\| 0 to 0.33 mm/mm strain SSCC : annealed at 1041 °C (1905 °F), water cooled \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.125 mm/mm strain SSCC : 0.001/s, hot-rolled \|\| tested at 25 °C (77 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.001/s, hot-rolled \|\| tested at 100 °C (212 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.001/s, hot-rolled \|\| tested at 200 °C (392 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.001/s, hot-rolled \|\| tested at 300 °C (572 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.001/s, hot-rolled \|\| tested at 400 °C (752 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s, hot-rolled \|\| tested at 25 °C (77 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s, hot-rolled \|\| tested at 100 °C (212 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s, hot-rolled \|\| tested at 200 °C (392 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s, hot-rolled \|\| tested at 300 °C (572 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s, hot-rolled \|\| tested at 400 °C (752 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.1/s, hot-rolled \|\| tested at 25 °C (77 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.1/s, hot-rolled \|\| tested at 100 °C (212 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.1/s, hot-rolled \|\| tested at 200 °C (392 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.1/s, hot-rolled \|\| tested at 300 °C (572 °F) \|\| 0 to 0.9 mm/mm strain SSCC : 0.1/s, hot-rolled \|\| tested at 400 °C (752 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 1/s, hot-rolled \|\| tested at 25 °C (77 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 1/s, hot-rolled \|\| tested at 100 °C (212 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 1/s, hot-rolled \|\| tested at 200 °C (392 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 1/s, hot-rolled \|\| tested at 300 °C (572 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 1/s, hot-rolled \|\| tested at 400 °C (752 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 10/s, hot-rolled \|\| tested at 25 °C (77 °F) \|\| 0 to 0.49 mm/mm strain SSCC : 10/s, hot-rolled \|\| tested at 100 °C (212 °F) \|\| 0 to 0.49 mm/mm strain SSCC : 10/s, hot-rolled \|\| tested at 200 °C (392 °F) \|\| 0 to 0.49 mm/mm strain SSCC : 10/s, hot-rolled \|\| tested at 300 °C (572 °F) \|\| 0 to 0.49 mm/mm strain SSCC : 10/s, hot-rolled \|\| tested at 400 °C (752 °F) \|\| 0 to 0.49 mm/mm strain UTS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) UTS : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) UTS : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) YS : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) %El : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : solid \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : solid \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 704 °C (1300 °F) \|\| 6 h to 1x10⁵ h SR : solid \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 816 °C (1500 °F) \|\| 2 h to 1x10⁵ h SR : solid \|\| tested at 927 °C (1700 °F) \|\| 1 h to 6 h SR : solid \|\| tested at 1077 °C (1970 °F) \|\| 2 h to 23 h SR : solid \|\| Master curve (LMP) \|\| 480 °C to 1077 °C (896 °F to 1970 °F) SR : burst test of seamless tubing \|\| tested at 593 °C (1100 °F) \|\| 5 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 704 °C (1300 °F) \|\| 1 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 760 °C (1400 °F) \|\| 1 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 871 °C (1600 °F) \|\| 1 h to 1x10⁴ h SR : burst test of seamless tubing \|\| tested at 982 °C (1800 °F) \|\| 1 h to 200 h SR : burst test of seamless tubing \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) FEN : solution annealed at 1050 °C (1922 °F) for 0.5 h \|\| tested at 288 °C (550 °F), R = -1, axial, total strain amplitude \|\| 1x10³ cycles to 5x10⁶ cycles FEN : annealed at 1066 °C (1950 °F), water quenched, stress relieved at 1010 °C (1850 °F), water quenched, annealed at 1093 °C (2000 °F) \|\| tested at 430 °C (806 °F), R = -1, axial, 0.004/s, total strain range \|\| 1x10³ cycles to 3.4x10⁴ cycles FEN : annealed at 1066 °C (1950 °F), water quenched, stress relieved at 1010 °C (1850 °F), water quenched, annealed at 1093 °C (2000 °F) \|\| tested at 650 °C (1202 °F), R = -1, axial, 0.004/s, total strain range \|\| 560 cycles to 8x10³ cycles FEN : annealed at 1066 °C (1950 °F), water quenched, stress relieved at 1010 °C (1850 °F), water quenched, annealed at 1093 °C (2000 °F) \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.004/s, total strain range \|\| 230 cycles to 2.3x10³ cycles FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, 0.005/s strain rate, total strain amplitude \|\| 160 cycles to 5.25x10³ cycles FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, 0.005/s strain rate, elastic strain amplitude \|\| 160 cycles to 5.25x10³ cycles FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, 0.005/s strain rate, plastic strain amplitude \|\| 160 cycles to 5.25x10³ cycles FEN : annealed \|\| tested at 21 °C (70 °F), R = -1, axial, 0.004/s strain rate, elastic strain range \|\| 1x10³ cycles to 1.2x10⁴ cycles FEN : annealed \|\| tested at 430 °C (806 °F), R = -1, axial, 0.004/s strain rate, elastic strain range \|\| 1x10³ cycles to 4x10⁴ cycles FEN : annealed \|\| tested at 649 °C (1200 °F), R = -1, axial, 0.004/s strain rate, elastic strain range \|\| 500 cycles to 1.2x10⁴ cycles FEN : annealed \|\| tested at 649 °C (1200 °F), R = -1, axial, 4x10^-⁵/s strain rate, elastic strain range \|\| 200 cycles to 3.5x10³ cycles FEN : annealed \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.004/s strain rate, elastic strain range \|\| 200 cycles to 3x10³ cycles FEN : annealed \|\| tested at 816 °C (1500 °F), R = -1, axial, 4x10^-⁵/s strain rate, elastic strain range \|\| 100 cycles to 1x10³ cycles FEN : solution annealed, aged at 593 °C (1100 °F) \|\| tested at 593 °C (1100 °F), R = -1, axial, total strain range \|\| 100 cycles to 1x10⁵ cycles FEN : solution annealed, aged at 593 °C (1100 °F) \|\| tested at 593 °C (1100 °F), R = -1, axial, plastic strain range \|\| 100 cycles to 1x10⁵ cycles FSN : cold reduced bar \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold reduced bar \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 6x10⁶ cycles FSN : cold reduced bar \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : cold reduced bar \|\| tested at 20 °C (68 °F) R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : cold reduced bar \|\| tested at -195.6 °C (-320 °F) R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : cold reduced bar \|\| tested at -253.1 °C (-423.7 °F) R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : cold reduced bar \|\| tested at 20 °C (68 °F) R = -1, K_t = 3.9, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : cold reduced bar \|\| tested at -195.6 °C (-320 °F) R = -1, K_t = 3.9, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : annealed bar, ASTM grain size 1 \|\| tested at 649 °C (1200 °F), R = -1, bending, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : annealed bar, ASTM grain size 1 \|\| tested at 816 °C (1500 °F), R = -1, bending, maximum stress \|\| 1.7x10³ cycles to 2x10⁶ cycles FSN : annealed bar, ASTM grain size 6 \|\| tested at 649 °C (1200 °F), R = -1, bending, maximum stress \|\| 490 cycles to 2x10⁶ cycles FSN : annealed bar, ASTM grain size 6 \|\| tested at 816 °C (1500 °F), R = -1, bending, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, bending, UTS = 515 MPa (74.7 ksi), YS = 205 MPa (29.7 ksi), maximum stress \|\| 8.3x10⁴ cycles to 1x10⁷ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, rotary, UTS = 690 MPa (100 ksi), YS = 316 MPa (45.8 ksi), maximum stress \|\| 1x10³ cycles to 2x10⁸ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, UTS = 618 MPa (89.6 ksi), YS = 275 MPa (39.9 ksi), maximum stress \|\| 160 cycles to 5.25x10³ cycles CRS : 1% creep strain, elevated T \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain, elevated T \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 0.5% plastic strain, annealed, ambient T \|\| tested at 22 °C (72 °F) \|\| 0.002 h to 0.5 h CRS : 1% plastic strain, annealed, ambient T \|\| tested at 22 °C (72 °F) \|\| 0.001 h to 4.2 h CRS : 2% plastic strain, annealed, ambient T \|\| tested at 22 °C (72 °F) \|\| 3x10^-⁴ h to 0.17 h CRS : 3% plastic strain, annealed, ambient T \|\| tested at 22 °C (72 °F) \|\| 7x10^-⁴ h to 32 h CRS : 4% plastic strain, annealed, ambient T \|\| tested at 22 °C (72 °F) \|\| 0.24 h to 88 h IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 10 s \|\| 0 to 0.34 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 100 s \|\| 0 to 0.41 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 0.1 h \|\| 0 to 0.44 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 0.3 h \|\| 0 to 0.38 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 1 h \|\| 0 to 0.41 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 3 h \|\| 0 to 0.44 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 10 h \|\| 0 to 0.47 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 30 h \|\| 0 to 0.38 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 100 h \|\| 0 to 0.4 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 300 h \|\| 0 to 0.43 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 1,000 h \|\| 0 to 3.25x10^-³ mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, annealed \|\| 3,000 h \|\| 0 to 3.44x10^-³ mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 10 s \|\| 0 to 0.22 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 30 s \|\| 0 to 0.26 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 100 s \|\| 0 to 0.3 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 200 s \|\| 0 to 0.2 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 300 s \|\| 0 to 0.21 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 400 s \|\| 0 to 0.22 mm/mm strain IC : tested at 22 °C (72 °F), plastic strain, cold worked \|\| 500 s \|\| 0 to 0.22 mm/mm strain HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) HE : solid \|\| grit blasted black oxidized \|\| -98 °C to 77 °C (-145 °F to 170 °F) NE : solid \|\| slightly corroded \|\| 327 °C to 655 °C (620 °F to 1211 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : solid \|\| 1000 °C to 1225 °C (1832 °F to 2237 °F) VP : liquid \|\| 1427 °C to 3227 °C (2600 °F to 5840 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) ST : liquid \|\| 30 ppm sulfur \|\| 1576 °C to 1805 °C (2869 °F to 3281 °F) ST : liquid \|\| 80 ppm sulfur \|\| 1579 °C to 1781 °C (2874 °F to 3238 °F) ST : liquid \|\| 100 ppm sulfur \|\| 1550 °C to 1890 °C (2822 °F to 3434 °F) ST : liquid \|\| 250 ppm sulfur \|\| 1580 °C to 1775 °C (2876 °F to 3227 °F) ST : liquid \|\| average of all \|\| 1417 °C to 1892 °C (2582 °F to 3437 °F) RHO : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) SIGMA : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F)
304 Cu (WNr 1.4567) (ISO/EN/DIN X3CrNiCu1894) (JIS SUSXM7) (AISI 304Cu) (AFNOR Z3CNU18-10) (GB & GB/T 0Cr18Ni9Cu3) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F)
304L (UNS S30403) (WNr 1.4306/1.4307) (ISO/EN/DIN X2CrNi18-9/X2CrNi19-11) (JIS SUS304L) (ASTM A167/A182/A193/A213/A276/A314/A320/A479) (SAE J405) (AMS 5511/5639/5647/5697) (AFNOR Z2CN18-10/Z3CN18-10/Z3CN19-10M) (GB & GB/T 00Cr19Ni10) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 1.25x10^-⁴/s \|\| 0 to 0.45 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 0.00125/s \|\| 0 to 0.45 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 0.0125/s \|\| 0 to 0.35 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 0.125/s \|\| 0 to 0.35 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 1.25/s \|\| 0 to 0.35 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 10/s \|\| 0 to 0.35 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 100/s \|\| 0 to 0.35 mm/mm strain SSC : annealed & temper rolled \|\| tested at 20 °C (68 °F), 400/s \|\| 0 to 0.35 mm/mm strain SSC : annealed \|\| tested at -29 °C (-20 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.42 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 7x10^-⁴/s, transverse \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.64 mm/mm strain SSC : annealed \|\| tested at 149 °C (300 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.61 mm/mm strain SSC : annealed \|\| tested at 316 °C (600 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.61 mm/mm strain SSC : annealed & quenched \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s, HIPed material \|\| 0 to 0.37 mm/mm strain SSC : annealed & quenched \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s, forged pipe \|\| 0 to 0.48 mm/mm strain SSC : weld material \|\| tested at 316 °C (600 °F), 3.75x10^-⁴/s \|\| 0 to 0.33 mm/mm strain SSCC : solution annealed & quenched, 0.01/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSCC : solution annealed & quenched, 0.01/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 0.01/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 1/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 1 mm/mm strain SSCC : solution annealed & quenched, 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 1 mm/mm strain SSCC : solution annealed & quenched, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 1 mm/mm strain SSCC : solution annealed & quenched, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 1 mm/mm strain SSCC : solution annealed & quenched, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 1 mm/mm strain SSCC : solution annealed & quenched, 10/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 10/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 10/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & quenched, 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.7 mm/mm strain UTS : annealed plate \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) UTS : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) UTS : 50% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 3.2, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 3.2, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 6.3, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 6.3, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 19, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| notched, K_t = 19, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| weld joint, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) UTS : 50% cold-rolled \|\| weld joint, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) YS : annealed plate \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) YS : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) YS : 50% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) YS : 50% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) YSC : 0.01/s strain rate \|\| flow stress at 0.1 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 0.01/s strain rate \|\| flow stress at 0.2 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 0.01/s strain rate \|\| flow stress at 0.3 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 0.01/s strain rate \|\| flow stress at 0.4 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 0.01/s strain rate \|\| flow stress at 0.6 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 10/s strain rate \|\| flow stress at 0.1 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 10/s strain rate \|\| flow stress at 0.2 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 10/s strain rate \|\| flow stress at 0.3 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 10/s strain rate \|\| flow stress at 0.4 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) YSC : 10/s strain rate \|\| flow stress at 0.6 strain \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : annealed plate \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) %El : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) %El : 60% cold-rolled \|\| unnotched, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| unnotched, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| weld joint, longitudinal \|\| -253 °C to 25 °C (-424 °F to 78 °F) %El : 60% cold-rolled \|\| weld joint, transverse \|\| -253 °C to 25 °C (-424 °F to 78 °F) SR : solution annealed & quenched, bar \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & quenched, bar \|\| tested at 566 °C (1050 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & quenched, bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & quenched, bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & quenched, bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & quenched, bar \|\| Master curve (LMP) \|\| 482 °C to 816 °C (899 °F to 1501 °F) FEN : solution annealed at mill \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 200 cycles to 4x10⁴ cycles FEN : solution annealed at mill \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 100 cycles to 1.6x10⁵ cycles FEN : solution annealed at mill \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 100 cycles to 1x10⁶ cycles FSN : butt weld \|\| tested at -163 °C (-262 °F), PS=2.3%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at -163 °C (-262 °F), PS=50%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at -163 °C (-262 °F), PS=97.7%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at 25 °C (77 °F), PS=2.3%, R = 0.1, maximum stress \|\| 1.5x10⁴ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at 25 °C (77 °F), PS=50%, R = 0.1, maximum stress \|\| 1.5x10⁴ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at 25 °C (77 °F), PS=97.7%, R = 0.1, maximum stress \|\| 1.5x10⁴ cycles to 2x10⁶ cycles FSN : recrystallized, cold-rolled sheet \|\| tested at 20 °C (68 °F), R = -1, axial, 90 Hz, fully austenitic, maximum stress \|\| 2.5x10⁵ cycles to 1x10⁷ cycles FSN : recrystallized, cold-rolled sheet \|\| tested at 20 °C (68 °F), R = -1, axial, 90 Hz, 30% martensite, maximum stress \|\| 1.5x10⁵ cycles to 1x10⁷ cycles FSN : recrystallized, cold-rolled sheet \|\| tested at 20 °C (68 °F), R = -1, axial, 90 Hz, 60% martensite, maximum stress \|\| 1.8x10⁵ cycles to 1x10⁷ cycles FSN : ASTM grain size 6, annealed at 900 °C (1652 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 500 cycles to 6x10⁵ cycles FSN : ASTM grain size 6, annealed at 900 °C (1652 °F) \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 5x10³ cycles to 1x10⁶ cycles FSN : ASTM grain size 1, annealed at 1200 °C (2192 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 1x10³ cycles to 1x10⁵ cycles FSN : ASTM grain size 1, annealed at 1200 °C (2192 °F) \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 2x10³ cycles to 1x10⁶ cycles FSN : average of ASTM grain sizes 1 & 6 \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 500 cycles to 6x10⁵ cycles FSN : average of ASTM grain sizes 1 & 6 \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 2x10³ cycles to 1x10⁶ cycles HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : liquid \|\| 1427 °C to 3227 °C (2600 °F to 5840 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO : solid \|\| -272 °C to 1399 °C (-458 °F to 2550 °F) SIGMA : solid \|\| -272 °C to 1399 °C (-458 °F to 2550 °F) S : solid \|\| 60 °C to 702 °C (140 °F to 1296 °F)
304LN (UNS S30453) (WNr 1.4311) (ISO/EN/DIN X2CrNiN18-10) (JIS SUS304LN) (AFNOR Z2CN18-10Az/Z3CN18-10Az) (GB & GB/T 00Cr18Ni10N) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : pipe \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.38 mm/mm strain SSC : pipe \|\| tested at 285 °C (545 °F), 0.001/s \|\| 0 to 0.273 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.66 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.62 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.64 mm/mm strain FEN : pipe \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 100 cycles to 1x10⁴ cycles FEN : pipe \|\| tested at 285 °C (545 °F), R = -1, axial, plastic strain amplitude \|\| 100 cycles to 1x10⁴ cycles FEN : mill annealed \|\| tested at 500 °C (932 °F), R = -1, axial, total strain amplitude \|\| 250 cycles to 8x10³ cycles FEN : mill annealed \|\| tested at 550 °C (1022 °F), R = -1, axial, total strain amplitude \|\| 150 cycles to 5x10³ cycles FEN : mill annealed \|\| tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude \|\| 130 cycles to 2.32x10³ cycles FEN : mill annealed \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain amplitude \|\| 170 cycles to 1.91x10³ cycles HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) HE : solid \|\| grit blasted black oxidized \|\| -98 °C to 77 °C (-145 °F to 170 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : solid \|\| 1000 °C to 1225 °C (1832 °F to 2237 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
304H (UNS S30409) (WNr 1.4301/1.4948) (ISO/EN/DIN X5CrNi18-10) (JIS SUS304) (AFNOR Z6CN18-09) (GB & GB/T 1Cr18Ni9) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SR : hot-rolled plate \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 500 °C to 751 °C (932 °F to 1384 °F) CRS : 1% plastic strain, hot-rolled plate \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| Master curve (LMP) \|\| 500 °C to 751 °C (932 °F to 1384 °F) HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) HE : solid \|\| grit blasted black oxidized \|\| -98 °C to 77 °C (-145 °F to 170 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : solid \|\| 1000 °C to 1225 °C (1832 °F to 2237 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Super 304H (304HCu) (UNS S30432) (WNr 1.4907) (ISO/EN/DIN X10CrNiCuNb189) (ASTM A213) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| 20 °C to 597 °C (68 °F to 1106 °F) TC : solid \|\| -272 °C to 1427 °C (-458 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 10 h to 1.7x10⁴ h SR : solution treated \|\| Master curve (LMP) \|\| 600 °C to 801 °C (1112 °F to 1474 °F) SR : tube \|\| tested at 700 °C (1292 °F) \|\| 40 h to 1,100 h FEN : as-received tube material \|\| tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude \|\| 275 cycles to 4x10⁵ cycles FEN : welded joint \|\| tested at 500 °C (932 °F), R = -1, axial, total strain amplitude \|\| 360 cycles to 1.2x10⁴ cycles FEN : welded joint \|\| tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude \|\| 260 cycles to 1.4x10⁴ cycles FEN : welded joint \|\| tested at 700 °C (1292 °F), R = -1, axial, total strain amplitude \|\| 120 cycles to 1.4x10⁴ cycles HE : solid \|\| polished \|\| 67 °C to 827 °C (152 °F to 1520 °F) HE : solid \|\| oxidized \|\| 315 °C to 650 °C (599 °F to 1202 °F) HE : solid \|\| grit blasted black oxidized \|\| -98 °C to 77 °C (-145 °F to 170 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : solid \|\| 1000 °C to 1225 °C (1832 °F to 2237 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F)
305 (UNS S30500) (WNr 1.4303) (ISO/EN/DIN X4CrNi18-12) (JIS SUS305J1) (ASTM A167/A193/A240/A249/A314/A320/A473/A580) (AISI 305) (SAE J405) (AMS 5514/5685) (AFNOR Z1CN18-12) (GB & GB/T 1Cr18Ni12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH : solid \|\| -269 °C to 27 °C (-452 °F to 80 °F) UTS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -253 °C to 816 °C (-424 °F to 1500 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : solid \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : solid \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 704 °C (1300 °F) \|\| 6 h to 1x10⁵ h SR : solid \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁵ h SR : solid \|\| tested at 816 °C (1500 °F) \|\| 2 h to 1x10⁵ h SR : solid \|\| tested at 927 °C (1700 °F) \|\| 1 h to 6 h SR : solid \|\| tested at 1077 °C (1970 °F) \|\| 2 h to 23 h SR : solid \|\| Master curve (LMP) \|\| 480 °C to 1077 °C (896 °F to 1970 °F) CRS : 1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) RHO : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SIGMA : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
308 (UNS S30800) (WNr 1.4303) (AISI 308) (AFNOR Z1CN18-12) (GB & GB/T 1Cr18Ni12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : 15% cold-drawn \|\| -253 °C to 27 °C (-424 °F to 80 °F) YS : 15% cold-drawn \|\| -253 °C to 27 °C (-424 °F to 80 °F) %El : 15% cold-drawn \|\| -253 °C to 27 °C (-424 °F to 80 °F) SR : weld metal \|\| tested at 593 °C (1100 °F), tangential \|\| 60 h to 1,100 h SR : weld metal \|\| tested at 593 °C (1100 °F), radial \|\| 2 h to 1,400 h SR : weld metal \|\| tested at 593 °C (1100 °F), average \|\| 2 h to 1,400 h NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SIGMA : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
309 (UNS S30900) (WNr 1.4829/1.4833) (ISO/EN/DIN X12CrNi22-12/X12CrNi24-12/X15CrNiSi20-12) (JIS SUH309) (ASTM A167/A249/A276/A312/A314/A479/A580) (AISI 309) (GB & GB/T 0Cr23Ni13)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 1.25x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 0.00125/s \|\| 0 to 0.35 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 0.0125/s \|\| 0 to 0.3 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 0.125/s \|\| 0 to 0.25 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 1.25/s \|\| 0 to 0.25 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 10/s \|\| 0 to 0.3 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 100/s \|\| 0 to 0.3 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 400/s \|\| 0 to 0.25 mm/mm strain SSC : annealed \|\| tested at 800 °C (1472 °F), 0.00125/s \|\| 0 to 0.187 mm/mm strain SSC : annealed \|\| tested at 900 °C (1652 °F), 0.00125/s \|\| 0 to 0.84 mm/mm strain UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 817 °C (68 °F to 1502 °F) %El : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 982 °C (1800 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 650 °C to 981 °C (1202 °F to 1798 °F) CRS : 1% plastic strain \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
310 (UNS S31000) (WNr 1.4841/1.4845) (ISO/EN/DIN X12CrNi25-20/X12CrNi25-21) (JIS SUH310) (ASTM A167) (AISI 310) (SAE 303010) (AFNOR Z12CN25.20) (GB & GB/T 0Cr25Ni20/2Cr25Ni20) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) DLL : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) MTE : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) E : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) G : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) v : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) K : solid \|\| -268 °C to 871 °C (-451 °F to 1600 °F) TC : solid \|\| -272 °C to 1000 °C (-458 °F to 1832 °F) TD : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) SH : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) SSC : annealed at 1149 °C (2100 °F), plates \|\| tested at -269.1 °C (-452.5 °F), 1.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : annealed at 1149 °C (2100 °F), plates \|\| tested at -196.1 °C (-321.1 °F), 1.67x10^-⁴/s \|\| 0 to 1.18 mm/mm strain SSC : annealed at 1149 °C (2100 °F), plates \|\| tested at -105 °C (-157 °F), 1.67x10^-⁴/s \|\| 0 to 1.4 mm/mm strain SSC : annealed at 1149 °C (2100 °F), plates \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.57 mm/mm strain UTS : annealed \|\| -269 °C to 871 °C (-452 °F to 1600 °F) UTS : 75% cold-rolled \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) UTS : 75% cold-rolled \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : annealed \|\| -253 °C to 871 °C (-424 °F to 1600 °F) YS : 75% cold-rolled \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : 75% cold-rolled \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : annealed \|\| -269 °C to 980 °C (-452 °F to 1796 °F) %El : 75% cold-rolled \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : 75% cold-rolled \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 927 °C (1700 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 982 °C (1800 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 983 °C (998 °F to 1801 °F) SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 538 °C (1000 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 593 °C (1100 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 704 °C (1300 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 760 °C (1400 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 871 °C (1600 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1,000 h SR : treated at 1277 °C (2330 °F), water quenched \|\| Master curve (LMP) \|\| 537 °C to 983 °C (998 °F to 1801 °F) FEN : mill annealed & pickled \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 40 cycles to 6x10⁴ cycles FEN : mill annealed & pickled \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 100 cycles to 6x10⁵ cycles FEN : mill annealed & pickled \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 80 cycles to 6.2x10⁵ cycles HE : solid \|\| unoxidized \|\| 537 °C to 1115 °C (998 °F to 2039 °F) HE : solid \|\| oxidized \|\| 81 °C to 1117 °C (178 °F to 2042 °F) HE : solid \|\| grit blasted & oxidized \|\| 67 °C to 977 °C (152 °F to 1790 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) SIGMA : solid \|\| -269 °C to 1000 °C (-452 °F to 1832 °F)
310S (UNS S31008) (WNr 1.4842/1.4845) (ISO/EN/DIN X12CrNi25-20/X8CrNi25-21) (JIS SUS310/SUS310S) (ASTM A167/A240/A240M/A276/A314) (AISI 310S) (SAE 30310S/J405) (AMS 5521/5572/5577/5651) (AFNOR Z12CN25-20/Z8CN25-20) (GB & GB/T 0Cr25Ni20) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1082 °C (68 °F to 1979 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| -269 °C to 1093 °C (-452 °F to 2000 °F) UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h CRS : 1% plastic strain \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -263 °C to 871 °C (-442 °F to 1600 °F) SIGMA : solid \|\| -263 °C to 871 °C (-442 °F to 1600 °F)
314 (UNS S31400) (WNr 1.4841) (ISO/EN/DIN X15CrNiSi25-20/X15CrNiSi25-21) (ASTM A276/A314/A473/A580) (AISI 314) (SAE J405) (AMS 5522/5652)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : annealed and cold worked \|\| 20 °C to 850 °C (68 °F to 1562 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed and cold worked \|\| tested at 20 °C (68 °F), 0.008/s \|\| 0 to 0.23 mm/mm strain SSC : annealed and cold worked \|\| tested at 150 °C (302 °F), 0.008/s \|\| 0 to 0.237 mm/mm strain SSC : annealed and cold worked \|\| tested at 250 °C (482 °F), 0.008/s \|\| 0 to 0.237 mm/mm strain SSC : annealed and cold worked \|\| tested at 350 °C (662 °F), 0.008/s \|\| 0 to 0.26 mm/mm strain SSC : annealed and cold worked \|\| tested at 450 °C (842 °F), 0.008/s \|\| 0 to 0.267 mm/mm strain SSC : annealed and cold worked \|\| tested at 550 °C (1022 °F), 0.008/s \|\| 0 to 0.175 mm/mm strain SSC : annealed and cold worked \|\| tested at 650 °C (1202 °F), 0.008/s \|\| 0 to 0.52 mm/mm strain SSC : annealed and cold worked \|\| tested at 750 °C (1382 °F), 0.008/s \|\| 0 to 0.21 mm/mm strain SSC : annealed and cold worked \|\| tested at 850 °C (1562 °F), 0.008/s \|\| 0 to 0.47 mm/mm strain UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : annealed and cold worked \|\| 20 °C to 850 °C (68 °F to 1562 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed and cold worked \|\| 20 °C to 850 °C (68 °F to 1562 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed and cold worked \|\| 20 °C to 850 °C (68 °F to 1562 °F) SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1149 °C (2100 °F) & water quenched \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
316 (UNS S31600) (WNr 1.4401/1.4436) (ISO/EN/DIN X3CrNiMo17-13-3/X5CrNiMo17-12-2) (JIS SUS316) (ASTM A182/A276/A314/A479) (AISI 316) (AMS 5648/5653) (AFNOR Z6CND17-11/Z6CND17-12/Z7CND17-11-02/Z7CND18-12-03) (GB & GB/T 0Cr17Ni12Mo2) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| cold-rolled \|\| 20 °C to 960 °C (68 °F to 1760 °F) TD : solid \|\| annealed \|\| -157 °C to 982 °C (-251 °F to 1800 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -269.1 °C (-452.5 °F), 1.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -196.1 °C (-321.1 °F), 1.67x10^-⁴/s \|\| 0 to 1.15 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -105 °C (-157 °F), 1.67x10^-⁴/s \|\| 0 to 1.38 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.35 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 20 °C (68 °F), 5.7x10^-⁵/s \|\| 0 to 0.44 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 149 °C (300 °F), 5.7x10^-⁵/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 538 °C (1000 °F), 5.7x10^-⁵/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 593 °C (1100 °F), 5.7x10^-⁵/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 704 °C (1300 °F), 5.7x10^-⁵/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 649 °C (1200 °F), 5.7x10^-⁵/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 760 °C (1400 °F), 5.7x10^-⁵/s \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1066 °C (1950 °F), rods \|\| tested at 816 °C (1500 °F), 5.7x10^-⁵/s \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at -150 °C (-238 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at -50 °C (-58 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at 100 °C (212 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at 200 °C (392 °F), 0.001/s \|\| 0 to 0.39 mm/mm strain SSC : annealed at 1050 °C (1922 °F), sheet \|\| tested at 400 °C (752 °F), 0.001/s \|\| 0 to 0.36 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.38 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.33 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.335 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.26 mm/mm strain SSC : hot-rolled then cold-rolled 2B finish 2 mm (0.0787 inch) thick sheet \|\| tested at 20 °C (68 °F), 85/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 550 °C (1022 °F), 4x10^-⁴/s \|\| 0 to 0.31 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 600 °C (1112 °F), 4x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 650 °C (1202 °F), 4x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 700 °C (1292 °F), 4x10^-⁴/s \|\| 0 to 0.39 mm/mm strain SSC : annealed at 1025 °C (1877 °F), water quenched \|\| tested at 750 °C (1382 °F), 4x10^-⁴/s \|\| 0 to 0.34 mm/mm strain UTS : annealed \|\| -269 °C to 871 °C (-452 °F to 1600 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -252 °C to 650 °C (-422 °F to 1202 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -269 °C to 871 °C (-452 °F to 1600 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : annealed at 1050 °C (1922 °F) \|\| tested at 450 °C (842 °F) \|\| 1 h to 1x10⁵ h SR : annealed at 1050 °C (1922 °F) \|\| tested at 500 °C (932 °F) \|\| 1 h to 1x10⁵ h SR : annealed at 1050 °C (1922 °F) \|\| tested at 550 °C (1022 °F) \|\| 1 h to 1x10⁵ h SR : annealed at 1050 °C (1922 °F) \|\| tested at 600 °C (1112 °F) \|\| 1 h to 1x10⁵ h SR : annealed at 1050 °C (1922 °F) \|\| tested at 650 °C (1202 °F) \|\| 1 h to 1x10⁵ h SR : annealed at 1050 °C (1922 °F) \|\| tested at 704 °C (1300 °F) \|\| 0.5 h to 4,200 h SR : annealed at 1050 °C (1922 °F) \|\| Master curve (LMP) \|\| 450 °C to 705 °C (842 °F to 1301 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 500 cycles to 2.5x10⁵ cycles FEN : annealed \|\| tested at 600 °C (1112 °F), R = -1, total strain range \|\| 500 cycles to 2.5x10⁵ cycles FEN : annealed \|\| tested at 593 °C (1100 °F), R = -1, total strain range \|\| 440 cycles to 3x10⁴ cycles FEN : annealed \|\| tested at 593 °C (1100 °F), R = -1, plastic strain range \|\| 440 cycles to 3x10⁴ cycles FEN : annealed \|\| tested at 593 °C (1100 °F), R = -1, elastic strain range \|\| 440 cycles to 3x10⁴ cycles FEN : annealed, stress relieved, water quenched, stress relieved \|\| tested at 430 °C (806 °F), R = -1, axial, 0.004/s, total strain range \|\| 1.7x10³ cycles to 2.2x10⁴ cycles FEN : annealed, stress relieved, water quenched, stress relieved \|\| tested at 650 °C (1202 °F), R = -1, axial, 0.004/s, total strain range \|\| 230 cycles to 1.4x10⁴ cycles FEN : annealed, stress relieved, water quenched, stress relieved \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.004/s, total strain range \|\| 240 cycles to 6x10³ cycles FEN : solution annealed, aged 5040 h at 593 °C (1100 °F) \|\| tested at 593 °C (1100 °F), R = -1, total strain range \|\| 530 cycles to 1.1x10⁵ cycles FEN : solution annealed, aged 5040 h at 593 °C (1100 °F) \|\| tested at 593 °C (1100 °F), R = -1, plastic strain range \|\| 530 cycles to 1.1x10⁵ cycles FEN : solution annealed, aged 5040 h at 593 °C (1100 °F) \|\| tested at 593 °C (1100 °F), R = -1, elastic strain range \|\| 530 cycles to 1.1x10⁵ cycles FEN : solution annealed at 1050 °C (1922 °F) \|\| tested at 600 °C (1112 °F), R = -1, axial, 6.7x10^-³/s, total strain range \|\| 350 cycles to 7.3x10³ cycles FEN : solution annealed at 1050 °C (1922 °F) \|\| tested at 600 °C (1112 °F), R = -1, axial, 6.7x10^-⁵/s, total strain range \|\| 130 cycles to 3.3x10³ cycles FEN : solution annealed at 1050 °C (1922 °F) \|\| tested at 700 °C (1292 °F), R = -1, axial, 6.7x10^-³/s, total strain range \|\| 300 cycles to 6.3x10³ cycles FEN : solution annealed at 1050 °C (1922 °F) \|\| tested at 700 °C (1292 °F), R = -1, axial, 6.7x10^-⁵/s, total strain range \|\| 300 cycles to 2.8x10³ cycles FSN : in seawater \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.3x10⁴ cycles to 5.4x10⁷ cycles NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : liquid \|\| 1427 °C to 3227 °C (2600 °F to 5840 °F) Vis : liquid \|\| 1500 °C to 1627 °C (2732 °F to 2960 °F) ST : liquid \|\| 10 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 12 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 50 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 120 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| average of all sulfur levels \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) RHO : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) SIGMA : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F)
316H (UNS S31609) (WNr 1.4401) (ASTM A213/A269/A312/A358) (GB & GB/T 0Cr17Ni12Mo2) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| cold-rolled \|\| 20 °C to 960 °C (68 °F to 1760 °F) TD : solid \|\| annealed \|\| -157 °C to 982 °C (-251 °F to 1800 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.61 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.616 mm/mm strain SR : annealed at 1010 °C (1850 °F) \|\| tested at 566 °C (1050 °F) \|\| 20 h to 2,600 h SR : annealed at 1010 °C (1850 °F) \|\| tested at 649 °C (1200 °F) \|\| 20 h to 2,300 h SR : annealed at 1010 °C (1850 °F) \|\| tested at 760 °C (1400 °F) \|\| 20 h to 590 h SR : annealed at 1010 °C (1850 °F) \|\| Master curve (LMP) \|\| 565 °C to 761 °C (1049 °F to 1402 °F) NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1500 °C to 1627 °C (2732 °F to 2960 °F) ST : liquid \|\| 10 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 12 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 50 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| 120 ppm sulfur \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) ST : liquid \|\| average of all sulfur levels \|\| 1572 °C to 1823 °C (2861 °F to 3313 °F) RHO : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) SIGMA : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F)
316L (UNS S31603) (WNr 1.4404/1.4432/1.4435) (ISO/EN/DIN X2CrNiMo17-12-2/X2CrNiMo17-12-3/X2CrNiMo18-14-3) (JIS SUS316L) (ASTM A240/A666) (AISI 316L) (AMS 5507) (AFNOR Z2CND17-12/Z2CND17-13/Z2CND18-13/Z3CND17-11-02/Z3CND17-12-03/Z3CND18-14-03) (GB & GB/T 00Cr17Ni14Mo2/0Cr18Ni12Mo2Ti) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) E* : laser powder bed fusion \|\| 0 degrees about Z-axis, measured in accordance with ISO 6892-1 \|\| room temperature value E* : laser powder bed fusion \|\| 45 degrees about Z-axis, measured in accordance with ISO 6892-1 \|\| room temperature value E* : laser powder bed fusion \|\| 90 degrees about Z-axis, measured in accordance with ISO 6892-1 \|\| room temperature value E* : laser powder bed fusion \|\| 0 degrees about Z-axis, measured in accordance with ASTM E1876 \|\| room temperature value E* : laser powder bed fusion \|\| 45 degrees about Z-axis, measured in accordance with ASTM E1876 \|\| room temperature value E* : laser powder bed fusion \|\| 90 degrees about Z-axis, measured in accordance with ASTM E1876 \|\| room temperature value E* : laser powder bed fusion \|\| 0 degrees about Z-axis, average of ISO and ASTM methods \|\| room temperature value E* : laser powder bed fusion \|\| 45 degrees about Z-axis, average of ISO and ASTM methods \|\| room temperature value E* : laser powder bed fusion \|\| 90 degrees about Z-axis, average of ISO and ASTM methods \|\| room temperature value G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : quenched \|\| tested at 20 °C (68 °F), 0.001/s, 22 micron grain size \|\| 0 to 0.3 mm/mm strain SSC : quenched \|\| tested at 20 °C (68 °F), 0.001/s, 76 micron grain size \|\| 0 to 0.33 mm/mm strain SSC : quenched \|\| tested at 20 °C (68 °F), 0.001/s, 165 micron grain size \|\| 0 to 0.36 mm/mm strain SSC : torsion \|\| tested at 1000 °C (1832 °F), 0.006/s, 30 micron grain size \|\| 0 to 1.25 mm/mm strain SSC : torsion \|\| tested at 1000 °C (1832 °F), 0.006/s, 100 micron grain size \|\| 0 to 1.25 mm/mm strain SSC : normalized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : annealed \|\| tested at -29 °C (-20 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.84 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 2.1 mm/mm strain SSC : annealed \|\| tested at 149 °C (300 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.73 mm/mm strain SSC : annealed \|\| tested at 316 °C (600 °F), 3.75x10^-⁴/s, longitudinal \|\| 0 to 1.64 mm/mm strain SSC : cold-rolled sheet, quenched and annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.334 mm/mm strain SSC : as-received cold-rolled sheet (probably annealed) \|\| tested at 20 °C (68 °F), 2x10^-⁴/s \|\| 0 to 0.433 mm/mm strain SSC : directed energy deposition \|\| tested at 20 °C (68 °F), 0.008/s, 642 ppm O \|\| 0 to 0.233 mm/mm strain SSC : directed energy deposition \|\| tested at 20 °C (68 °F), 0.008/s, 1600 ppm O \|\| 0 to 0.153 mm/mm strain SSC : directed energy deposition \|\| tested at 20 °C (68 °F), 0.008/s, 3710 ppm O \|\| 0 to 0.14 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, vertical, as-built, Afkhami et. al. \|\| 0 to 0.27 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, vertical, machined, Afkhami et. al. \|\| 0 to 0.21 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, vertical, HFMI treated, Afkhami et. al. \|\| 0 to 0.43 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, horizontal, machined, Afkhami et. al. \|\| 0 to 0.16 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0067/s, vertical, as-built, Riabov et. al. \|\| 0 to 0.63 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0067/s, vertical, 400 °C (752 °F) HT, Riabov et. al. \|\| 0 to 0.1 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0067/s, vertical, 800 °C (1472 °F) HT, Riabov et. al. \|\| 0 to 0.29 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0067/s, vertical, 1200 °C (2192 °F) HT, Riabov et. al. \|\| 0 to 0.33 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 1x10^-⁴/s, as-built, Eskandari Sabzi et. al. \|\| 0 to 0.35 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, as-built, Edin et. al. \|\| 0 to 0.375 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 600 °C (1112 °F), Edin et. al. \|\| 0 to 0.36 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 700 °C (1292 °F), Edin et. al. \|\| 0 to 0.418 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 800 °C (1472 °F), Edin et. al. \|\| 0 to 0.426 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 850 °C (1562 °F), Edin et. al. \|\| 0 to 0.45 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 900 °C (1652 °F), Edin et. al. \|\| 0 to 0.457 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 8.3x10^-⁵/s, 1 h at 950 °C (1742 °F), Edin et. al. \|\| 0 to 0.457 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), unknown strain rate, 0 degrees about Z-axis, Charmi et. al. \|\| 0 to 0.287 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), unknown strain rate, 45 degrees about Z-axis, Charmi et. al. \|\| 0 to 0.32 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), unknown strain rate, 90 degrees about Z-axis, Charmi et. al. \|\| 0 to 0.36 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 2x10^-⁴/s, as-built, Shin et. al. \|\| 0 to 0.26 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 2x10^-⁴/s, 0.5 h at 1100 °C (2012 °F), Shin et. al. \|\| 0 to 0.38 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 2x10^-⁴/s, HIPed 1.5 h at 1100 °C (2012 °F), Shin et. al. \|\| 0 to 0.376 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 3000/s \|\| 0 to 0.7 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 5000/s \|\| 0 to 0.7 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 7000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 83% dense \|\| tested at 20 °C (68 °F), 9000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 3000/s \|\| 0 to 0.7 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 5000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 7000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 88% dense \|\| tested at 20 °C (68 °F), 9000/s \|\| 0 to 0.5 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.8 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 3000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 5000/s \|\| 0 to 0.6 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 7000/s \|\| 0 to 0.5 mm/mm strain SSCC : sintered to 93% dense \|\| tested at 20 °C (68 °F), 9000/s \|\| 0 to 0.5 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 1000/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 1000/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.45 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 1000/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 1000/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.7 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 3000/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 3000/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.45 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 3000/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 3000/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.71 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 5000/s \|\| tested at 25 °C (77 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 5000/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.43 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 5000/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed at 1000 °C (1832 °F), 5000/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.72 mm/mm strain UTS : annealed \|\| -29 °C to 871 °C (-20 °F to 1600 °F) UTS : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -29 °C to 871 °C (-20 °F to 1600 °F) YS : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -29 °C to 871 °C (-20 °F to 1600 °F) %El : weld material \|\| 3.75x10^-⁴/s strain rate \|\| -29 °C to 316 °C (-20 °F to 600 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 31% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 49% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : hot-rolled sheet \|\| tested at 600 °C (1112 °F) \|\| 170 h to 4,300 h SR : hot-rolled sheet \|\| tested at 650 °C (1202 °F) \|\| 10 h to 650 h SR : hot-rolled sheet \|\| Master curve (LMP) \|\| 599 °C to 650 °C (1110 °F to 1202 °F) SR : laser powder bed fusion \|\| tested at 600 °C (1112 °F) \|\| 80 h to 400 h SR : laser powder bed fusion \|\| tested at 650 °C (1202 °F) \|\| 15 h to 160 h SR : laser powder bed fusion \|\| Master curve (LMP) \|\| 599 °C to 650 °C (1110 °F to 1202 °F) FEN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, in air, total strain amplitude \|\| 3.9x10³ cycles to 1x10⁶ cycles FEN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, in water, total strain amplitude \|\| 3x10³ cycles to 1x10⁶ cycles FEN : strain-hardened, effect of hydrogen \|\| tested at 20 °C (68 °F), R = -1, axial, as-received, to initiation, plastic strain amplitude \|\| 600 cycles to 3.15x10⁴ cycles FEN : strain-hardened, effect of hydrogen \|\| tested at 20 °C (68 °F), R = -1, axial, as-received, to failure, plastic strain amplitude \|\| 720 cycles to 3.4x10⁴ cycles FEN : strain-hardened, effect of hydrogen \|\| tested at 20 °C (68 °F), R = -1, axial, H-precharged, to initiation, plastic strain amplitude \|\| 350 cycles to 8.85x10³ cycles FEN : strain-hardened, effect of hydrogen \|\| tested at 20 °C (68 °F), R = -1, axial, H-precharged, to failure, plastic strain amplitude \|\| 640 cycles to 1.3x10⁴ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, stress-relieved at 550 °C (1022 °F), total strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, stress-relieved at 550 °C (1022 °F), elastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, stress-relieved at 550 °C (1022 °F), plastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles FSN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, no pre-strain, stress amplitude \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : as-received \|\| tested at 20 °C (68 °F), R = -1, axial, 6% pre-strain, stress amplitude \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : wrought \|\| tested at 20 °C (68 °F), R = -1, axial, solution annealed & quenched, maximum stress \|\| 650 cycles to 5.4x10⁴ cycles FSN : wrought \|\| tested at 20 °C (68 °F), R = -1, axial, cold worked, maximum stress \|\| 600 cycles to 4.3x10⁴ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), R = -1, axial, solution annealed & quenched, 0 Pa (0 psi) mean stress, in air, stress amplitude \|\| 3.9x10³ cycles to 1x10⁶ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, 50 MPa (7.25 ksi) mean stress, in air, stress amplitude \|\| 8.2x10³ cycles to 1x10⁶ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, -20 MPa (-2.90 ksi) mean stress, in air, stress amplitude \|\| 1.65x10⁴ cycles to 1x10⁶ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), R = -1, axial, solution annealed & quenched, 0 Pa (0 psi) mean stress, in water, stress amplitude \|\| 3x10³ cycles to 1x10⁶ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, 50 MPa (7.25 ksi) mean stress, in water, stress amplitude \|\| 4x10³ cycles to 1x10⁶ cycles FSN : hot finish hollow bar \|\| tested at 288 °C (550 °F), axial, solution annealed & quenched, -20 MPa (-2.90 ksi) mean stress, in water, stress amplitude \|\| 8x10³ cycles to 1x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, as-built, maximum stress, Afkhami et. al. \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, machined, maximum stress, Afkhami et. al. \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, HFMI treated, maximum stress, Afkhami et. al. \|\| 8x10⁴ cycles to 1x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, horizontal, machined, maximum stress, Afkhami et. al. \|\| 6x10⁴ cycles to 1x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, as-built rod sample, maximum stress, Yu et. al. \|\| 600 cycles to 2x10⁵ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, as-built tubular sample, maximum stress, Yu et. al. \|\| 500 cycles to 7.2x10⁴ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, polished tubular sample, maximum stress, Yu et. al. \|\| 500 cycles to 8.4x10⁴ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, as-built, maximum stress, Hamada et. al. \|\| 6x10⁴ cycles to 1x10⁸ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, annealed at 900 °C (1652 °F) for 30 minutes, maximum stress, Hamada et. al. \|\| 1.5x10⁵ cycles to 1x10⁸ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, as-built, 20 micron layer, horizontal, stress amplitude, Dastgerdi et. al. \|\| 6x10⁴ cycles to 3.3x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, as-built, 20 micron layer, vertical, stress amplitude, Dastgerdi et. al. \|\| 7.6x10⁴ cycles to 1.1x10⁶ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, as-built, 40 micron layer, horizontal, stress amplitude, Dastgerdi et. al. \|\| 5.9x10⁴ cycles to 9.4x10⁵ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, as-built, 40 micron layer, vertical, stress amplitude, Dastgerdi et. al. \|\| 5.8x10⁴ cycles to 1.4x10⁶ cycles NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) VP : liquid \|\| 1427 °C to 3227 °C (2600 °F to 5840 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) ST : liquid \|\| 200 ppm sulfur \|\| 1264 °C to 1642 °C (2307 °F to 2987 °F) RHO : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) SIGMA : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F)
316LN (UNS S31653) (WNr 1.4406/1.4429) (ISO/EN/DIN X2CrNiMoN17-11-2/X2CrNiMoN17-13-3) (JIS SUS316LN) (ASTM A240) (AFNOR Z2CND17-13/Z3CND17-11Az/Z3CND17-12Az) (GB & GB/T 00Cr17Ni12Mo2N/00Cr17Ni13Mo2N) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : annealed \|\| tested at -150 °C (-238 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at -50 °C (-58 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 100 °C (212 °F), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 200 °C (392 °F), 0.001/s \|\| 0 to 0.39 mm/mm strain SSC : annealed \|\| tested at 400 °C (752 °F), 0.001/s \|\| 0 to 0.36 mm/mm strain UTS : annealed \|\| annealed at 1066 °C (1950 °F) for 1 h, water quenched \|\| -73 °C to 204 °C (-100 °F to 400 °F) UTS : annealed \|\| annealed at 1050 °C (1922 °F) for 0.5 h \|\| -150 °C to 550 °C (-238 °F to 1022 °F) UTS : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| -73 °C to 204 °C (-100 °F to 400 °F) UTS : 20% cold-rolled \|\| 1 mm (0.0394 inch) thick sheet \|\| -150 °C to 550 °C (-238 °F to 1022 °F) YS : annealed \|\| annealed at 1066 °C (1950 °F) for 1 h, water quenched \|\| -73 °C to 204 °C (-100 °F to 400 °F) YS : annealed \|\| annealed at 1050 °C (1922 °F) for 0.5 h \|\| -150 °C to 550 °C (-238 °F to 1022 °F) YS : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| -73 °C to 204 °C (-100 °F to 400 °F) YS : 20% cold-rolled \|\| 1 mm (0.0394 inch) thick sheet \|\| -150 °C to 550 °C (-238 °F to 1022 °F) %El : annealed \|\| annealed at 1066 °C (1950 °F) for 1 h, water quenched \|\| -73 °C to 204 °C (-100 °F to 400 °F) %El : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| -73 °C to 204 °C (-100 °F to 400 °F) SR : solution treated & water quenched \|\| tested at 525 °C (977 °F) \|\| 100 h to 6x10⁵ h SR : solution treated & water quenched \|\| tested at 550 °C (1022 °F) \|\| 100 h to 6x10⁵ h SR : solution treated & water quenched \|\| tested at 600 °C (1112 °F) \|\| 100 h to 6x10⁵ h SR : solution treated & water quenched \|\| tested at 650 °C (1202 °F) \|\| 100 h to 6x10⁵ h SR : solution treated & water quenched \|\| tested at 700 °C (1292 °F) \|\| 100 h to 6x10⁵ h SR : solution treated & water quenched \|\| Master curve (LMP) \|\| 525 °C to 701 °C (977 °F to 1294 °F) SR : effect of welding process \|\| tested at 650 °C (1202 °F), base material \|\| 30 h to 3,700 h SR : effect of welding process \|\| tested at 650 °C (1202 °F), HW-TIG welded \|\| 30 h to 3,900 h SR : effect of welding process \|\| tested at 650 °C (1202 °F), A-TIG welded \|\| 70 h to 4,850 h SR : effect of welding process \|\| tested at 650 °C (1202 °F), HLM welded \|\| 100 h to 8,400 h FEN : solution annealed, 0.07 wt% N \|\| tested at 500 °C (932 °F), R = -1, axial, plastic strain amplitude \|\| 400 cycles to 1x10⁴ cycles FEN : solution annealed, 0.07 wt% N \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 250 cycles to 1x10⁴ cycles FEN : solution annealed, 0.07 wt% N \|\| tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude \|\| 200 cycles to 1x10⁴ cycles FEN : solution annealed, 0.11 wt% N \|\| tested at 500 °C (932 °F), R = -1, axial, plastic strain amplitude \|\| 350 cycles to 1x10⁴ cycles FEN : solution annealed, 0.11 wt% N \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 250 cycles to 1x10⁴ cycles FEN : solution annealed, 0.11 wt% N \|\| tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude \|\| 150 cycles to 1x10⁴ cycles FEN : solution annealed, 0.14 wt% N \|\| tested at 500 °C (932 °F), R = -1, axial, plastic strain amplitude \|\| 450 cycles to 1x10⁴ cycles FEN : solution annealed, 0.14 wt% N \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 250 cycles to 1x10⁴ cycles FEN : solution annealed, 0.14 wt% N \|\| tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude \|\| 200 cycles to 1x10⁴ cycles FEN : solution annealed, 0.22 wt% N \|\| tested at 500 °C (932 °F), R = -1, axial, plastic strain amplitude \|\| 350 cycles to 2x10⁴ cycles FEN : solution annealed, 0.22 wt% N \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 250 cycles to 1.5x10⁴ cycles FEN : solution annealed, 0.22 wt% N \|\| tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude \|\| 200 cycles to 2x10⁴ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, vertical, total strain amplitude \|\| 1.6x10³ cycles to 2.4x10⁵ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, axial, diagonal, total strain amplitude \|\| 400 cycles to 7x10⁴ cycles FSN : mill annealed, in air \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4.9x10³ cycles to 1x10⁵ cycles FSN : mill annealed, in mercury \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2.2x10³ cycles to 8x10⁴ cycles NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) SIGMA : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F)
316LS / 316LVM (UNS S31653) (WNr 1.4406/1.4429) (ISO/EN/DIN X2CrNiMoN17-11-2/X2CrNiMoN17-13-3) (ASTM A240/F138) (AFNOR Z2CND17-13/Z3CND17-11Az) (GB & GB/T 00Cr17Ni12Mo2N/00Cr17Ni13Mo2N) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) TD : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) FSN : as-machined surface \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁷ cycles FSN : blasted surface \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
316NG (UNS S31600) (WNr 1.4401) (ISO/EN/DIN X5CrNiMo17-12-2) (GB & GB/T 0Cr17Ni12Mo2) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) FEN : air \|\| tested at 288 °C (550 °F), R = -1, axial, total strain amplitude \|\| 2x10³ cycles to 5x10⁶ cycles NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F)
316 Ti (UNS S31635) (WNr 1.4571) (ISO/EN/DIN X6CrNiMoTi17-12-2) (JIS SUS316Ti) (AFNOR Z6CNDT17-12) (GB & GB/T 0Cr18Ni12Mo2Ti/1Cr18Ni12Mo3Ti) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| solution annealed \|\| 0 °C to 727 °C (32 °F to 1340 °F) TC : liquid \|\| 1436 °C to 2627 °C (2617 °F to 4760 °F) TD : solid \|\| solution annealed \|\| 20 °C to 727 °C (68 °F to 1340 °F) TD : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 25 °C (77 °F), 4x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 550 °C (1022 °F), 4x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 600 °C (1112 °F), 4x10^-⁴/s \|\| 0 to 0.29 mm/mm strain SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 650 °C (1202 °F), 4x10^-⁴/s \|\| 0 to 0.31 mm/mm strain SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 700 °C (1292 °F), 4x10^-⁴/s \|\| 0 to 0.34 mm/mm strain SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 750 °C (1382 °F), 4x10^-⁴/s \|\| 0 to 0.4 mm/mm strain UTS : condition not specified, probably annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : condition not specified, probably annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : condition not specified, probably annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Alloy D9 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) TC : solid \|\| solution annealed & 20% cold worked \|\| 20 °C to 950 °C (68 °F to 1742 °F) TD : solid \|\| solution annealed & 20% cold worked \|\| 20 °C to 950 °C (68 °F to 1742 °F) SH : solid \|\| 20 °C to 1047 °C (68 °F to 1917 °F) FEN : solution annealed \|\| tested at 550 °C (1022 °F), R = -1, axial, total strain amplitude \|\| 225 cycles to 9x10³ cycles FEN : solution annealed \|\| tested at 550 °C (1022 °F), R = -1, axial, elastic strain amplitude \|\| 225 cycles to 9x10³ cycles FEN : solution annealed \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 225 cycles to 9x10³ cycles FEN : solution annealed \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain amplitude \|\| 180 cycles to 2.3x10³ cycles FEN : solution annealed \|\| tested at 650 °C (1202 °F), R = -1, axial, elastic strain amplitude \|\| 180 cycles to 2.3x10³ cycles FEN : solution annealed \|\| tested at 650 °C (1202 °F), R = -1, axial, plastic strain amplitude \|\| 180 cycles to 2.3x10³ cycles FEN : swaged 20% \|\| tested at 550 °C (1022 °F), R = -1, axial, total strain amplitude \|\| 160 cycles to 2.6x10³ cycles FEN : swaged 20% \|\| tested at 550 °C (1022 °F), R = -1, axial, elastic strain amplitude \|\| 160 cycles to 2.6x10³ cycles FEN : swaged 20% \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 160 cycles to 2.6x10³ cycles FEN : swaged 20% \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain amplitude \|\| 100 cycles to 4x10³ cycles FEN : swaged 20% \|\| tested at 650 °C (1202 °F), R = -1, axial, plastic strain amplitude \|\| 100 cycles to 4x10³ cycles
CF-8M (UNS S31600) (WNr 1.4401) (ISO/EN/DIN X5CrNiMo17-12-2) (GB & GB/T 0Cr17Ni12Mo2) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 0 °C to 648 °C (32 °F to 1198 °F) DLL : solid \|\| 0 °C to 648 °C (32 °F to 1198 °F) MTE : solid \|\| 0 °C to 648 °C (32 °F to 1198 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) E : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) G : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) v : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) K : solid \|\| -268 °C to 900 °C (-451 °F to 1652 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) FEN : air \|\| tested at 288 °C (550 °F), R = -1, axial, total strain amplitude \|\| 1x10³ cycles to 2x10⁶ cycles FEN : air \|\| tested at 325 °C (617 °F), R = -1, axial, total strain amplitude \|\| 2x10³ cycles to 2x10⁶ cycles NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F)
317 (UNS S31700) (WNr 1.4449) (ISO/EN/DIN X5CrNiMo17-13/X5CrNiMo18-15-4) (JIS SUS317) (ASTM A182/A213/A240/A249/A276/A312/A358/A376/A403/A430) (AISI 317) (AFNOR Z8CND18.10.3M) (GB & GB/T 0Cr19Ni13Mo3) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| -272 °C to 1371 °C (-458 °F to 2500 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -272 °C to 1371 °C (-458 °F to 2500 °F) SIGMA : solid \|\| -272 °C to 1371 °C (-458 °F to 2500 °F)
317L (UNS S31703) (WNr 1.4438) (ISO/EN/DIN X2CrNiMo18-15-4/X2CrNiMoN18-15-4) (JIS SUS317L) (ASTM A167/A240) (AISI 317L) (AFNOR Z2CND19-15/Z3CND19-15-04) (GB & GB/T 00Cr19Ni13Mo3) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) D : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) DLL : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) DLL : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) MTE : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) MTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) CTE : solid \|\| -263 °C to 27 °C (-442 °F to 80 °F) CTE : liquid \|\| 1434 °C to 1658 °C (2613 °F to 3016 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| -269 °C to 600 °C (-452 °F to 1112 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
321 (UNS S32100) (WNr 1.4541) (ISO/EN/DIN X6CrNiTi18-10) (JIS SUS321) (ASTM A167/A182/A193) (AISI 321) (SAE J405) (AMS 5510/5557/5570) (AFNOR Z6CNT18-10) (GB & GB/T 0Cr18Ni10Ti/1Cr18Ni11Ti/H0Cr20Ni10Ti) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) DLL : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) MTE : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) E : solid \|\| -273 °C to 816 °C (-460 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| -272 °C to 1399 °C (-458 °F to 2550 °F) TD : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SSC : annealed, 1/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.31 mm/mm strain SSC : annealed, 1/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 1/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 1/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.15 mm/mm strain SSC : annealed, 1/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.25 mm/mm strain SSC : annealed, 1/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : annealed, 1/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.22 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.11 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain SSC : annealed, 0.01/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.31 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.11 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.15 mm/mm strain SSC : annealed, 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain UTS : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : mill annealed \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : mill annealed \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : mill annealed \|\| -253 °C to 20 °C (-424 °F to 68 °F) SR : annealed \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 22 h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 8 h to 1x10⁵ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 732 °C (1350 °F) \|\| 1 h to 1,150 h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 482 °C to 816 °C (899 °F to 1501 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles FEN : annealed \|\| tested at 600 °C (1112 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 800 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at -196.1 °C (-321.1 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : annealed \|\| tested at -253.1 °C (-423.7 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 8x10⁷ cycles FSN : annealed \|\| tested at -196.1 °C (-321.1 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at -253.1 °C (-423.7 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles CRS : 0.2% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 100 h CRS : 0.2% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 0.3 h to 90 h CRS : 0.3% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 19 h to 155 h CRS : 0.5% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 80 h to 275 h CRS : 0.5% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 200 h CRS : 0.5% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 0.5 h to 150 h CRS : 0.7% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 105 h to 345 h CRS : 1% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 119 h to 420 h CRS : 1% plastic strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 0.9 h to 225 h CRS : 1% plastic strain, annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 2% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 150 h to 320 h CRS : 2% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 1.2 h to 770 h CRS : 2% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 1.8 h to 360 h CRS : 3% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 3.5 h to 510 h CRS : 3% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 2.4 h to 500 h CRS : 4% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 5 h to 600 h CRS : 4% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 3 h to 640 h CRS : 5% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 6.9 h to 660 h CRS : 5% plastic strain, annealed \|\| tested at 732 °C (1350 °F) \|\| 3.6 h to 760 h CRS : 0.1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 649 °C (1200 °F) \|\| 1 h to 46 h CRS : 0.1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 0.1 h to 20 h CRS : 0.1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.2% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 70 h CRS : 0.2% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 0.25 h to 55 h CRS : 0.2% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.3% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 85 h CRS : 0.3% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 0.4 h to 85 h CRS : 0.3% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 0.5% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 649 °C (1200 °F) \|\| 0.3 h to 110 h CRS : 0.5% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 0.8 h to 155 h CRS : 0.5% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 649 °C (1200 °F) \|\| 6 h to 170 h CRS : 1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 1 h to 375 h CRS : 1% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| Master curve (LMP) \|\| 648 °C to 733 °C (1198 °F to 1351 °F) CRS : 2% plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| tested at 732 °C (1350 °F) \|\| 1 h to 105 h IC : tested at 538 °C (1000 °F), plastic strain \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 3 h \|\| 0 to 0.4 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 0.3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 0.3 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, 1.65 mm (0.065 inch) thick sheet, annealed, in compression \|\| 100 h \|\| 0 to 0.2 mm/mm strain HE : solid \|\| foil \|\| 20 °C to 500 °C (68 °F to 932 °F) NE : solid \|\| polished to 6 micro-inch RMS \|\| -188 °C to 980 °C (-307 °F to 1796 °F) NE : solid \|\| slightly oxidized \|\| -197 °C to 890 °C (-323 °F to 1634 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) SIGMA : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F)
321H (UNS S32109) (WNr 1.4541/1.4878) (ISO/EN/DIN X6CrNiTi18-10/Z12CrNiTi189) (JIS SUS321) (AFNOR Z6CNT18-10/Z6CNT18-12(B)) (GB & GB/T 0Cr18Ni10Ti/1Cr18Ni9Ti) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) DLL : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) MTE : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) E : solid \|\| -273 °C to 816 °C (-460 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 1399 °C (68 °F to 2550 °F) TD : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SH : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 600 °C to 801 °C (1112 °F to 1474 °F) CRS : 1% total strain, annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 599 °C to 800 °C (1110 °F to 1472 °F) HE : solid \|\| foil \|\| 20 °C to 500 °C (68 °F to 932 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
S32053 (UNS S32053) (JIS SUS836L) (ASTM A240)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : 2 mm (0.0787 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
329 (UNS S31200/S32900) (WNr 1.4460) (ISO/EN/DIN X3CrNiMoN27-5-2/X4CrNiMo27-5-1/XBCrNiMo27-5) (JIS SUS329J1) (ASTM A268/A511) (AISI 329) (AFNOR Z5CND27-05Az) (GB & GB/T 0Cr26Ni5Mo2)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) G : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) v : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) K : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) TC : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) TD : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : annealed \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : annealed \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : annealed \|\| 20 °C to 371 °C (68 °F to 700 °F)
334 (UNS S33400) (ASTM 334)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : annealed \|\| 20 °C to 1037 °C (68 °F to 1898 °F) YS : annealed \|\| 20 °C to 1037 °C (68 °F to 1898 °F) %El : annealed \|\| 20 °C to 1037 °C (68 °F to 1898 °F) RHO : solid \|\| 20 °C to 648 °C (68 °F to 1198 °F) SIGMA : solid \|\| 20 °C to 648 °C (68 °F to 1198 °F)
347 (UNS S34700) (WNr 1.4550) (ISO/EN/DIN X6CrNiNb18-10) (JIS SUS347) (ASTM A167/A182/A193/A479) (AISI 347) (SAE J405) (AMS 55125556) (AFNOR Z6CNNb18-10) (GB & GB/T 0Cr18Ni11Nb) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) DLL : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) MTE : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) E : solid \|\| -193 °C to 871 °C (-316 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| annealed \|\| -273 °C to 1392 °C (-460 °F to 2538 °F) TC : liquid \|\| 1527 °C to 1627 °C (2780 °F to 2961 °F) TD : solid \|\| cold-rolled \|\| 20 °C to 878 °C (68 °F to 1612 °F) TD : solid \|\| annealed \|\| -157 °C to 982 °C (-251 °F to 1800 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -269.1 °C (-452.5 °F), 1.67x10^-⁴/s \|\| 0 to 0.67 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -196.1 °C (-321.1 °F), 1.67x10^-⁴/s \|\| 0 to 0.87 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at -105 °C (-157 °F), 1.67x10^-⁴/s \|\| 0 to 1.1 mm/mm strain SSC : annealed at 1093 °C (2000 °F), plates \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.2 mm/mm strain UTS : stabilized at 1093 °C (2000 °F) \|\| -253 °C to 816 °C (-424 °F to 1500 °F) UTS : mill annealed \|\| -253 °C to 254 °C (-424 °F to 489 °F) UTS : 10% cold-drawn \|\| -256 °C to 23 °C (-429 °F to 73 °F) YS : stabilized at 1093 °C (2000 °F) \|\| -253 °C to 816 °C (-424 °F to 1500 °F) YS : annealed \|\| -253 °C to 256 °C (-424 °F to 493 °F) YS : 10% cold-drawn \|\| -253 °C to 23 °C (-424 °F to 73 °F) %El : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : annealed \|\| -253 °C to 260 °C (-424 °F to 500 °F) %El : 10% cold-drawn \|\| -253 °C to 23 °C (-424 °F to 73 °F) SR : annealed bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) FEN : solution treated \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain range \|\| 1 cycles to 2.38x10⁵ cycles FEN : annealed sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum strain \|\| 1.9x10⁴ cycles to 1.1x10⁶ cycles FEN : annealed sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum strain \|\| 3x10⁴ cycles to 1.1x10⁶ cycles FEN : annealed sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain \|\| 2.4x10⁴ cycles to 1.4x10⁶ cycles FEN : annealed sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain \|\| 3.7x10⁴ cycles to 6.6x10⁵ cycles FSN : annealed sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 2x10⁶ cycles FSN : annealed sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 5x10⁴ cycles to 8x10⁵ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 8x10⁶ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10³ cycles to 8x10⁵ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution annealed \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : solution annealed \|\| tested at 300 °C (572 °F), R = -1, ultrasonic, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles CRS : 1% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.17 h to 31 h CRS : 1% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.3 h to 40 h CRS : 1% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.6 h to 3.1 h CRS : 1% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 2% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.15 h to 30 h CRS : 2% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.01 h to 70 h CRS : 2% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 7.2 h CRS : 2% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 5% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.11 h to 30 h CRS : 5% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.3 h to 100 h CRS : 5% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 12 h CRS : 5% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 1% plastic strain, annealed, long time \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain HE : solid \|\| oxidized \|\| 315 °C to 1093 °C (599 °F to 2000 °F) NE : solid \|\| polished \|\| -185 °C to 810 °C (-301 °F to 1490 °F) NE : solid \|\| oxidized in air at 802 °C (1475 °F) \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| oxidized in air at 1093 °C (2000 °F) \|\| 290 °C to 1130 °C (554 °F to 2066 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO : solid \|\| -269 °C to 800 °C (-452 °F to 1472 °F) SIGMA : solid \|\| -269 °C to 800 °C (-452 °F to 1472 °F)
348 (UNS S34800) (ASTM A167/A182/A213/A240/A249/A269/A276/A312/A314) (AISI 348) (AFNOR Z6CNNb18.10) (GB & GB/T 1Cr19Ni11Nb) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| -193 °C to 816 °C (-316 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 878 °C (68 °F to 1612 °F) SH : solid \|\| -269 °C to 982 °C (-452 °F to 1800 °F) SSC : annealed \|\| tested at 430 °C (806 °F), 4x10^-⁵/s \|\| 0 to 0.75 mm/mm strain SSC : annealed \|\| tested at 650 °C (1202 °F), 4x10^-⁵/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 816 °C (1500 °F), 4x10^-⁵/s \|\| 0 to 1 mm/mm strain SSC : annealed \|\| tested at 430 °C (806 °F), 0.004/s \|\| 0 to 0.975 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 0.004/s \|\| 0 to 0.95 mm/mm strain SSC : annealed \|\| tested at 816 °C (1500 °F), 0.004/s \|\| 0 to 0.75 mm/mm strain UTS : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : stabilized at 1093 °C (2000 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : annealed bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : annealed bar \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) FEN : annealed, stress relieved, water quenched, annealed \|\| tested at 430 °C (806 °F), R = -1, axial, 0.004/s, total strain range \|\| 330 cycles to 1.1x10⁵ cycles FEN : annealed, stress relieved, water quenched, annealed \|\| tested at 650 °C (1202 °F), R = -1, axial, 0.004/s, total strain range \|\| 230 cycles to 5.8x10⁴ cycles FEN : annealed, stress relieved, water quenched, annealed \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.004/s, total strain range \|\| 120 cycles to 1x10⁴ cycles CRS : 1% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.17 h to 31 h CRS : 1% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.3 h to 40 h CRS : 1% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.6 h to 3.1 h CRS : 1% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 2% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.15 h to 30 h CRS : 2% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.01 h to 70 h CRS : 2% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 7.2 h CRS : 2% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 5% plastic strain, annealed, short time \|\| tested at 649 °C (1200 °F) \|\| 0.11 h to 30 h CRS : 5% plastic strain, annealed, short time \|\| tested at 760 °C (1400 °F) \|\| 0.3 h to 100 h CRS : 5% plastic strain, annealed, short time \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 12 h CRS : 5% plastic strain, annealed, short time \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 1% plastic strain, annealed, long time \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed, long time \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, annealed, short time \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, annealed, short time \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, annealed, short time \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, annealed, short time \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, annealed, short time \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, annealed, short time \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, annealed, short time \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, annealed, short time \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, annealed, short time \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, annealed, short time \|\| 1 h \|\| 0 to 0.5 mm/mm strain NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SIGMA : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
P558 (UNS S29225)	D* : solid \|\| room temperature value D : liquid \|\| 1450 °C to 2327 °C (2642 °F to 4220 °F) DLL : liquid \|\| 1450 °C to 2327 °C (2642 °F to 4220 °F) MTE : liquid \|\| 1450 °C to 2327 °C (2642 °F to 4220 °F) CTE : liquid \|\| 1450 °C to 2327 °C (2642 °F to 4220 °F) TC : liquid \|\| 1450 °C to 2227 °C (2642 °F to 4040 °F) TD : liquid \|\| 1450 °C to 2227 °C (2642 °F to 4040 °F) SH : liquid \|\| 1450 °C to 2227 °C (2642 °F to 4040 °F) SSC : metal injection molded \|\| tested at 20 °C (68 °F), unknown strain rate, as sintered \|\| 0 to 0.8 mm/mm strain SSC : metal injection molded \|\| tested at 20 °C (68 °F), unknown strain rate, solution annealed \|\| 0 to 0.26 mm/mm strain UTS* : metal injection molded \|\| as sintered \|\| room temperature value UTS* : metal injection molded \|\| solution annealed \|\| room temperature value YS* : metal injection molded \|\| as sintered \|\| room temperature value YS* : metal injection molded \|\| solution annealed \|\| room temperature value %El* : metal injection molded \|\| as sintered \|\| room temperature value %El* : metal injection molded \|\| solution annealed \|\| room temperature value RHO : liquid \|\| 1450 °C to 2227 °C (2642 °F to 4040 °F) SIGMA : liquid \|\| 1450 °C to 2227 °C (2642 °F to 4040 °F)
15Cr15Ni1MoTi (ISO/EN/DIN 15Cr15Ni1MoTi)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| solution annealed \|\| 20 °C to 827 °C (68 °F to 1520 °F) SR : solution treated \|\| tested at 550 °C (1022 °F) \|\| 970 h to 6.1x10⁴ h SR : solution treated \|\| tested at 600 °C (1112 °F) \|\| 620 h to 6.1x10⁴ h SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 620 h to 6.1x10⁴ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 620 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 630 h to 3.8x10⁴ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 4x10³ h to 6.1x10⁴ h SR : solution treated \|\| Master curve (LMP) \|\| 550 °C to 701 °C (1022 °F to 1294 °F)
X10NiCrMoTiB1515 (DIN 1.4970) (WNr 1.4970) (ISO/EN/DIN X10NiCrMoTiB15-15)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| annealed & quenched \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| annealed & quenched \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) HE : solid \|\| 1047 °C to 1217 °C (1916 °F to 2222 °F) RHO : solid \|\| annealed \|\| 20 °C to 1227 °C (68 °F to 2240 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1227 °C (68 °F to 2240 °F)
Esshete 1250 (UNS S21500) (WNr 1.4982) (ASTM A213) (AFNOR X10CrNiMoMnNbVB15-10-1)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 610 °C (1130 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 620 °C (1148 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 630 °C (1166 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 640 °C (1184 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 660 °C (1220 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 670 °C (1238 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 680 °C (1256 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 690 °C (1274 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 710 °C (1310 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 720 °C (1328 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 730 °C (1346 °F) \|\| 1x10⁴ h to 2.5x10⁵ h SR : annealed \|\| tested at 740 °C (1364 °F) \|\| 1x10⁴ h to 1.5x10⁵ h SR : annealed \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 600 °C to 751 °C (1112 °F to 1384 °F) RHO : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Crucible HNM	D : solid \|\| 20 °C to 1265 °C (68 °F to 2309 °F) DLL : solid \|\| 20 °C to 1265 °C (68 °F to 2309 °F) MTE : solid \|\| 20 °C to 1265 °C (68 °F to 2309 °F) TC : solid \|\| 20 °C to 1227 °C (68 °F to 2240 °F) TD : solid \|\| 20 °C to 1187 °C (68 °F to 2168 °F) SH : solid \|\| 20 °C to 1187 °C (68 °F to 2168 °F)

403 (UNS S40300) (WNr 1.4004/1.4024) (ISO/EN/DIN X10Cr12/X15Cr13) (JIS SUS403) (ASTM A176/A276/A314/A473) (AISI 403/614) (AFNOR Z12C13M) (GB & GB/T 1Cr12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) E : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) K : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) SH : solid \|\| -173 °C to 1227 °C (-280 °F to 2240 °F) SSCC : 0.001/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.001/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.48 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.47 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.44 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.46 mm/mm strain UTS : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : solid \|\| tempered at 607 °C (1125 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solid \|\| tempered at 607 °C (1125 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| tempered at 607 °C (1125 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : hardened \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁵ h SR : hardened \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁵ h SR : hardened \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁵ h SR : hardened \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : hardened \|\| tested at 760 °C (1400 °F) \|\| 10 h to 100 h SR : hardened \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) FSN : hardened & tempered \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5.2x10⁴ cycles to 7.3x10⁷ cycles FSN : hardened & tempered \|\| tested at 482 °C (900 °F), R = -1, rotating beam, maximum stress \|\| 3.5x10⁴ cycles to 3x10⁷ cycles RHO : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SIGMA : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
403Nb (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) E : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) K : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) SSCC : 0.001/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.515 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.52 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.53 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.53 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.53 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.52 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.535 mm/mm strain YS : 40 mm (1.57 inch) diameter bar \|\| austenitized, tempered at 650 °C (1202 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 750 °C (1382 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 800 °C (1472 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 850 °C (1562 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 850 °C (1562 °F), tempered at 650 °C (1202 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : 40 mm (1.57 inch) diameter bar \|\| austenitized, tempered at 650 °C (1202 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 750 °C (1382 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 800 °C (1472 °F) \|\| 400 °C to 700 °C (752 °F to 1292 °F) %El : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 850 °C (1562 °F) \|\| 400 °C to 700 °C (752 °F to 1292 °F) %El : 40 mm (1.57 inch) diameter bar \|\| austenitized, hot-rolled at 850 °C (1562 °F), tempered at 650 °C (1202 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) RHO : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SIGMA : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F)
405 (UNS S40500) (WNr 1.4002) (ISO/EN/DIN X6CrAl13) (JIS SUS438HP) (ASTM A176/A240/A268/A276/A314) (AISI 405) (AFNOR Z6CA13) (GB & GB/T 0Cr13Al)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 470 °C (68 °F to 878 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : annealed \|\| 20 °C to 870 °C (68 °F to 1598 °F) YS : annealed \|\| 20 °C to 870 °C (68 °F to 1598 °F) %El : annealed \|\| 20 °C to 870 °C (68 °F to 1598 °F) SR : annealed \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 482 °C to 816 °C (899 °F to 1501 °F) CRS : 0.1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) CRS : 0.2% creep strain \|\| tested at 538 °C (1000 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 593 °C (1100 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) CRS : 0.5% creep strain \|\| tested at 538 °C (1000 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 593 °C (1100 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) CRS : 1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) IC : tested at 538 °C (1000 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain
409 (UNS S40900) (WNr 1.4512) (ISO/EN/DIN X2CrTi12) (JIS SUH409) (ASTM A176/A268/A651) (AISI 409) (SAE J405) (AFNOR Z6CT12) (GB & GB/T 00Cr12/0Cr11Ti)	D : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) SSC : sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) FSN : galvanized wire, axial fatigue \|\| tested at 20 °C (68 °F), R = 0.2 to 0.4, mean stress of 350 MPa (50.8 ksi), stress amplitude \|\| 915 cycles to 1.2x10⁷ cycles FSN : galvanized wire, axial fatigue \|\| tested at 20 °C (68 °F), immersed in NaCl, R = 0.2 to 0.4, mean stress of 350 MPa (50.8 ksi), stress amplitude \|\| 2.13x10³ cycles to 6.26x10⁶ cycles RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
409HP (S40910) (UNS S40910) (AISI 409HP)	D : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
409HP (S40920) (UNS S40920) (AISI 409HP)	D : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
409HP (S40930) (UNS S40930) (AISI 409HP)	D : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 2 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 2 h to 200 h SR : annealed \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
410 (UNS S41000) (WNr 1.4006) (ISO/EN/DIN X10Cr13/X12Cr13) (JIS SUS410) (ASTM A176/A182/A276/A479/A493/A580/F899) (AISI 410) (SAE J405) (AMS 5504/5505/5613) (AFNOR Z10C13/Z13C13) (GB & GB/T 1Cr12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 648 °C (-460 °F to 1198 °F) DLL : solid \|\| -273 °C to 648 °C (-460 °F to 1198 °F) MTE : solid \|\| -273 °C to 648 °C (-460 °F to 1198 °F) E : solid \|\| -253 °C to 900 °C (-424 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| -272 °C to 1327 °C (-458 °F to 2420 °F) TD : solid \|\| 20 °C to 882 °C (68 °F to 1619 °F) SH : solid \|\| -18 °C to 1093 °C (-1 °F to 2000 °F) SSC : hardened, 19 mm (0.75 inch) diameter bar \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 4.4x10^-⁴/s \|\| 0 to 0.115 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 4/s \|\| 0 to 0.73 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 20/s \|\| 0 to 0.83 mm/mm strain SSC : annealed \|\| tested at 20 °C (68 °F), 700/s \|\| 0 to 0.14 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, partitioned at 400 °C (752 °F), held 2 minutes \|\| 0 to 0.117 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, partitioned at 450 °C (842 °F), held 2 minutes \|\| 0 to 0.126 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, partitioned at 450 °C (842 °F), held 5 minutes \|\| 0 to 0.117 mm/mm strain SSCC : hardened, 19 mm (0.75 inch) diameter bar \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain UTS : solid \|\| annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| tempered at 604 °C (1120 °F) \|\| 20 °C to 595 °C (68 °F to 1103 °F) UTS : solid \|\| tempered at 540 °C (1004 °F) \|\| 20 °C to 870 °C (68 °F to 1598 °F) UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value YS : solid \|\| annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered at 604 °C (1120 °F) \|\| 20 °C to 595 °C (68 °F to 1103 °F) YS : solid \|\| tempered at 540 °C (1004 °F) \|\| 20 °C to 870 °C (68 °F to 1598 °F) YS : solid \|\| hardened & tempered to UTS = 650 MPa (94.3 ksi) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value %El : solid \|\| annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered at 604 °C (1120 °F) \|\| 20 °C to 413 °C (68 °F to 775 °F) %El : solid \|\| tempered at 540 °C (1004 °F) \|\| 20 °C to 870 °C (68 °F to 1598 °F) SR : hardened \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁵ h SR : hardened \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁵ h SR : hardened \|\| Master curve (LMP) \|\| 482 °C to 538 °C (899 °F to 1000 °F) SR : annealed \|\| tested at 427 °C (800 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 426 °C to 760 °C (799 °F to 1400 °F) CRS : 0.1% creep strain \|\| tested at 427 °C (800 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.2% creep strain \|\| tested at 427 °C (800 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 482 °C (900 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 538 °C (1000 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 593 °C (1100 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 649 °C (1200 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 704 °C (1300 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 760 °C (1400 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.5% creep strain \|\| tested at 427 °C (800 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 482 °C (900 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 538 °C (1000 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 593 °C (1100 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 649 °C (1200 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 704 °C (1300 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 760 °C (1400 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 1% creep strain \|\| tested at 427 °C (800 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 482 °C (900 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h IC : tested at 427 °C (800 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| -269 °C to 700 °C (-452 °F to 1292 °F) SIGMA : solid \|\| -269 °C to 700 °C (-452 °F to 1292 °F)
410S (UNS S41008) (WNr 1.4000) (ISO/EN/DIN X6Cr13) (JIS SUS403) (ASTM A240) (AFNOR Z6C13) (GB & GB/T 0Cr13) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : annealed \|\| room temperature value YS* : annealed \|\| room temperature value %El* : annealed \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
414 (UNS S41400) (WNr 1.4313) (ISO/EN/DIN X3CrNiMo13-4/X8CrNi13) (JIS SUSTi6NM) (ASTM A276/A314/A473/A511/A580) (AISI 414) (SAE J405) (AMS 5615) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F)
416 (UNS S41600) (WNr 1.4005) (ISO/EN/DIN X12CrS13) (JIS SUS416) (ASTM A194/A314/A473/A581/A582) (AISI 416) (SAE J405) (AMS 5610) (AFNOR Z12C13/Z6C13) (GB & GB/T 1Cr13/Y1Cr13) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 507 °C (-460 °F to 944 °F) DLL : solid \|\| -273 °C to 507 °C (-460 °F to 944 °F) MTE : solid \|\| -273 °C to 507 °C (-460 °F to 944 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 43 °C to 200 °C (109 °F to 392 °F) TD : solid \|\| 20 °C to 880 °C (68 °F to 1616 °F) SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : heat-treated \|\| -253 °C to 20 °C (-424 °F to 68 °F) UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value YS : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : heat-treated \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value %El : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : heat-treated \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value SR : annealed \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : annealed \|\| Master curve (LMP) \|\| 426 °C to 650 °C (799 °F to 1202 °F) FEN : cold-rolled, tested in air \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, total strain amplitude \|\| 120 cycles to 4x10⁵ cycles FEN : cold-rolled, tested in air \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, elastic strain amplitude \|\| 120 cycles to 4x10⁵ cycles FEN : cold-rolled, tested in air \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, plastic strain amplitude \|\| 120 cycles to 4x10⁵ cycles FEN : cold-rolled, tested in H₂ \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, total strain amplitude \|\| 150 cycles to 3x10⁵ cycles FEN : cold-rolled, tested in H₂ \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, elastic strain amplitude \|\| 150 cycles to 3x10⁵ cycles FEN : cold-rolled, tested in H₂ \|\| tested at 20 °C (68 °F), R = -1, axial, 0.01/s strain rate, plastic strain amplitude \|\| 150 cycles to 3x10⁵ cycles RHO : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F) SIGMA : solid \|\| -269 °C to 900 °C (-452 °F to 1652 °F)
S42030 (UNS S42030)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
420 (UNS S42000) (WNr 1.4021/1.4028/1.4031/1.4034) (ISO/EN/DIN X20Cr13/X30Cr13/X39Cr13/X39Cr13/X40Cr14/X46Cr13) (JIS SUS420J1/SUS420J1/SUS420J2) (ASTM A276/A314/A473/A580) (AISI 420) (SAE J405) (AMS 5506/5621/7207) (AFNOR X20Cr13/Z20C13/Z33C13/Z40C14) (GB & GB/T 2Cr13/3Cr13/4C13/X20Cr13) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 1000 °C (-424 °F to 1832 °F) DLL : solid \|\| -253 °C to 1000 °C (-424 °F to 1832 °F) MTE : solid \|\| -253 °C to 1000 °C (-424 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| annealed \|\| -263 °C to 927 °C (-442 °F to 1700 °F) TC : solid \|\| hardened \|\| -263 °C to 1227 °C (-442 °F to 2240 °F) TD : solid \|\| annealed \|\| 20 °C to 876 °C (68 °F to 1609 °F) TD : solid \|\| hardened \|\| 20 °C to 876 °C (68 °F to 1609 °F) SH : solid \|\| 20 °C to 876 °C (68 °F to 1609 °F) SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, partitioned at 450 °C (842 °F), quenched to 99 °C (210 °F) \|\| 0 to 0.154 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, partitioned at 450 °C (842 °F), quenched to 29 °C (84 °F) \|\| 0 to 0.65 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 115 °C (239 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.48 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 145 °C (293 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.5 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 170 °C (338 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.57 mm/mm strain UTS : solution treated at 1010 °C (1850 °F) \|\| tempered 50F (28C) above the test temperature \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value YS : solution treated at 1010 °C (1850 °F) \|\| tempered 50F (28C) above the test temperature \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value YS : quenched & tempered at 650 °C (1202 °F) to 750 °C (1382 °F) \|\| tempered to a UTS = 700 MPa (102 ksi) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : quenched & tempered at 650 °C (1202 °F) to 750 °C (1382 °F) \|\| tempered to a UTS = 800 MPa (116 ksi) \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : solution treated at 1010 °C (1850 °F) \|\| tempered 50F (28C) above the test temperature \|\| 204 °C to 650 °C (399 °F to 1202 °F) SR : hardened \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : hardened \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : hardened \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : hardened \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h RHO : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
420 mod (WNr 1.2316) (ISO/EN/DIN X38CrMo16) (AISI 420mod) (AFNOR Z35CD17)	D : solid \|\| quenched & tempered \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| quenched & tempered \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| quenched & tempered \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| quenched & tempered \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| quenched & tempered \|\| 20 °C to 500 °C (68 °F to 932 °F)
10 wt% Cr (similar to 422, slightly lower C & Cr)	D* : solid \|\| room temperature value SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.1/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.76 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.01/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.001/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.79 mm/mm strain
422 (UNS S42200) (JIS SUH616) (ASTM A276/A314/A473/A580) (AISI 422) (SAE J405) (AMS 5506/5621/7207) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) E : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) G : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) v : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) K : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) TC : solid \|\| 2 °C to 650 °C (35 °F to 1202 °F) TD : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| 20 °C to 1227 °C (68 °F to 2240 °F) UTS : austenitized at 1038 °C (1900 °F), oil quenched \|\| tempered at 649 °C (1200 °F) for 4 h \|\| 427 °C to 650 °C (800 °F to 1202 °F) UTS : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia \|\| tempered at 441 °C (825 °F) for 4 h \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : austenitized at 1038 °C (1900 °F), air cooled \|\| tempered at 538 °C (1000 °F) for 2 h \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : austenitized at 1038 °C (1900 °F), oil quenched \|\| tempered at 649 °C (1200 °F) for 4 h \|\| 427 °C to 650 °C (800 °F to 1202 °F) YS : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia \|\| tempered at 441 °C (825 °F) for 4 h \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : austenitized at 1038 °C (1900 °F), air cooled \|\| tempered at 538 °C (1000 °F) for 2 h \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : austenitized at 1038 °C (1900 °F), oil quenched \|\| tempered at 649 °C (1200 °F) for 4 h \|\| 427 °C to 650 °C (800 °F to 1202 °F) %El : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia \|\| tempered at 441 °C (825 °F) for 4 h \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : austenitized at 1038 °C (1900 °F), air cooled \|\| tempered at 538 °C (1000 °F) for 2 h \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁴ h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 4 h \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 4 h \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 4 h \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 4 h \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) SR : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 427 °C (800 °F) \|\| 55 h to 1,220 h SR : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 482 °C (900 °F) \|\| 8 h to 30 h SR : austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| Master curve (LMP) \|\| 427 °C to 482 °C (800 °F to 899 °F) SR : austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 400 h to 800 h SR : austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 482 °C (900 °F) \|\| 9 h to 180 h SR : austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| Master curve (LMP) \|\| 427 °C to 482 °C (800 °F to 899 °F) CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 649 °C (1200 °F) for 2 h \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) CRS : 0.1% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 316 °C (600 °F) \|\| 1 h to 1,100 h CRS : 0.1% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 427 °C (800 °F) \|\| 0.3 h to 1,020 h CRS : 0.3% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 427 °C (800 °F) \|\| 9 h to 1,180 h CRS : 0.3% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 482 °C (900 °F) \|\| 2 h to 470 h CRS : 0.5% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 427 °C (800 °F) \|\| 20 h to 490 h CRS : 0.5% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 482 °C (900 °F) \|\| 3 h to 830 h CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| tested at 482 °C (900 °F) \|\| 6 h to 245 h CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| Master curve (LMP) \|\| 427 °C to 482 °C (800 °F to 899 °F) CRS : 0.1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 0.4 h to 320 h CRS : 0.1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 482 °C (900 °F) \|\| 0.7 h to 10 h CRS : 0.3% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 3 h to 1,000 h CRS : 0.3% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 482 °C (900 °F) \|\| 9 h to 90 h CRS : 0.5% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 2 h to 700 h CRS : 0.5% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 482 °C (900 °F) \|\| 25 h to 290 h CRS : 1% plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| tested at 482 °C (900 °F) \|\| 100 h to 300 h IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 10 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 1,000 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), rapidly cooled in dissociated ammonia, tempered at 441 °C (825 °F) for 4 h \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 10 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, austenitized at 1038 °C (1900 °F), tempered at 538 °C (1000 °F) for 2 h \|\| 100 h \|\| 0 to 0.01 mm/mm strain
422M (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) DLL : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) MTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) CTE : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) E : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) G : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) v : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) K : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) UTS : 1093 °C (2000 °F), oil quenched \|\| tempered at 649 °C (1200 °F) for 2 h \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : 1093 °C (2000 °F), oil quenched \|\| tempered at 704 °C (1300 °F) for 2 h \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : 1093 °C (2000 °F), oil quenched \|\| tempered at 649 °C (1200 °F) for 2 h \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : 1093 °C (2000 °F), oil quenched \|\| tempered at 704 °C (1300 °F) for 2 h \|\| 20 °C to 650 °C (68 °F to 1202 °F)
430 (UNS S43000) (WNr 1.4016) (ISO/EN/DIN X6Cr17) (JIS SUS430) (ASTM A176/A182/A240/A276/A314/A473/A479/A493/A580) (AISI 430) (SAE J405) (AMS 5503/5627) (AFNOR Z8C17) (GB & GB/T 1Cr15/1Cr17) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 0 °C to 816 °C (32 °F to 1500 °F) D : liquid \|\| 1501 °C to 1600 °C (2734 °F to 2912 °F) DLL : solid \|\| 0 °C to 816 °C (32 °F to 1500 °F) DLL : liquid \|\| 1501 °C to 1600 °C (2734 °F to 2912 °F) MTE : solid \|\| 0 °C to 816 °C (32 °F to 1500 °F) MTE : liquid \|\| 1501 °C to 1600 °C (2734 °F to 2912 °F) CTE : solid \|\| 0 °C to 816 °C (32 °F to 1500 °F) CTE : liquid \|\| 1501 °C to 1600 °C (2734 °F to 2912 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| annealed \|\| -272 °C to 1477 °C (-458 °F to 2690 °F) TD : solid \|\| annealed \|\| 20 °C to 750 °C (68 °F to 1382 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) SSC : cold-rolled and annealed \|\| tested at 25 °C (77 °F), 0.001/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 100 °C (212 °F), 0.001/s \|\| 0 to 0.182 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 200 °C (392 °F), 0.001/s \|\| 0 to 0.174 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 250 °C (482 °F), 0.001/s \|\| 0 to 0.172 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 300 °C (572 °F), 0.001/s \|\| 0 to 0.132 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 350 °C (662 °F), 0.001/s \|\| 0 to 0.54 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 400 °C (752 °F), 0.001/s \|\| 0 to 0.14 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 450 °C (842 °F), 0.001/s \|\| 0 to 0.125 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 500 °C (932 °F), 0.001/s \|\| 0 to 0.16 mm/mm strain SSC : cold-rolled and annealed \|\| tested at 600 °C (1112 °F), 0.001/s \|\| 0 to 0.85 mm/mm strain UTS : solid \|\| annealed \|\| -196 °C to 760 °C (-321 °F to 1400 °F) UTS : solid \|\| annealed & cold worked to 89 HRB \|\| 20 °C to 870 °C (68 °F to 1598 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 0% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked, transverse \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked, longitudinal \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked, transverse \|\| room temperature value YS : solid \|\| annealed \|\| -196 °C to 760 °C (-321 °F to 1400 °F) YS : solid \|\| annealed & cold worked to 89 HRB \|\| 20 °C to 870 °C (68 °F to 1598 °F) YS* : effect of cold work on RT value \|\| 0% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 0% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked, transverse \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked, longitudinal \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked, transverse \|\| room temperature value %El : solid \|\| annealed \|\| -196 °C to 760 °C (-321 °F to 1400 °F) %El : solid \|\| annealed & cold worked to 89 HRB \|\| 20 °C to 870 °C (68 °F to 1598 °F) %El* : effect of cold work on RT value \|\| 0% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 0% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked, transverse \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked, longitudinal \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked, transverse \|\| room temperature value SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 566 °C (1050 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 621 °C (1150 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 677 °C (1250 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 732 °C (1350 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) CRS : 0.1% creep strain \|\| tested at 427 °C (800 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| tested at 816 °C (1500 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 0.1% creep strain \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) CRS : 0.2% creep strain \|\| tested at 427 °C (800 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 482 °C (900 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 538 °C (1000 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 593 °C (1100 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 649 °C (1200 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 704 °C (1300 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 760 °C (1400 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| tested at 816 °C (1500 °F) \|\| 2x10³ h to 2x10⁴ h CRS : 0.2% creep strain \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) CRS : 0.5% creep strain \|\| tested at 427 °C (800 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 482 °C (900 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 538 °C (1000 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 593 °C (1100 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 649 °C (1200 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 704 °C (1300 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 760 °C (1400 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| tested at 816 °C (1500 °F) \|\| 5x10³ h to 5x10⁴ h CRS : 0.5% creep strain \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) CRS : 1% creep strain \|\| tested at 427 °C (800 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 482 °C (900 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| tested at 816 °C (1500 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% creep strain \|\| Master curve (LMP) \|\| 426 °C to 816 °C (799 °F to 1501 °F) IC : tested at 427 °C (800 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 5,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 6,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 7,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 8,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 9,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) ST : liquid \|\| 1427 °C to 1727 °C (2600 °F to 3140 °F) RHO : solid \|\| -272 °C to 1477 °C (-458 °F to 2690 °F) SIGMA : solid \|\| -272 °C to 1477 °C (-458 °F to 2690 °F)
430F (UNS S43020) (WNr 1.4104/1.4105) (ISO/EN/DIN X14CrMoS17/X6CrMoS17) (JIS SUS430F) (ASTM A314/A473/A581/A582/A838) (AISI 430F) (SAE J405) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| annealed \|\| 0 °C to 1127 °C (32 °F to 2060 °F) TD : solid \|\| annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
430 Ti (UNS S43036) (WNr 1.4510) (ISO/EN/DIN X6CrTi17) (AFNOR Z8CT17) (GB & GB/T 00Cr12Ti)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value YS* : annealed \|\| room temperature value %El* : annealed \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
431 (UNS S43100) (WNr 1.4057) (ISO/EN/DIN X17CrNi16-2) (JIS SUS431) (ASTM A276/A314/A473/A479/A493/A579/A580) (AISI 431) (SAE J405) (AMS 5628) (AFNOR Z15CN16-02) (GB & GB/T 1Cr17Ni2/ML1Cr17Ni2) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) DLL : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) MTE : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) CTE : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH : solid \|\| 20 °C to 1227 °C (68 °F to 2240 °F) SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 27 °C (81 °F), 0.003/s \|\| 0 to 0.41 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 100 °C (212 °F), 0.003/s \|\| 0 to 0.46 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 175 °C (347 °F), 0.003/s \|\| 0 to 0.46 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 250 °C (482 °F), 0.003/s \|\| 0 to 0.31 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 350 °C (662 °F), 0.003/s \|\| 0 to 0.29 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 420 °C (788 °F), 0.003/s \|\| 0 to 0.22 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 450 °C (842 °F), 0.003/s \|\| 0 to 0.21 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 500 °C (932 °F), 0.003/s \|\| 0 to 0.13 mm/mm strain SSC : hardened at 1010 °C (1850 °F), double tempered at 649 °C (1200 °F) \|\| tested at 550 °C (1022 °F), 0.003/s \|\| 0 to 8.3x10^-³ mm/mm strain UTS : hardened at 982 °C (1800 °F) \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : hardened at 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : hardened at 1010 °C (1850 °F) \|\| tempered 28C (50F) above test temperature \|\| 149 °C to 593 °C (300 °F to 1099 °F) UTS : hardened at 1010 °C (1850 °F) \|\| double tempered at 649 °C (1200 °F) \|\| 20 °C to 550 °C (68 °F to 1022 °F) UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value YS : hardened at 982 °C (1800 °F) \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : hardened at 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : hardened at 980 °C (1796 °F) to 1030 °C (1886 °F) \|\| quenched & tempered at 600 °C (1112 °F) to 650 °C (1202 °F) to a UTS = 900 MPa (131 ksi) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : hardened at 980 °C (1796 °F) to 1030 °C (1886 °F) \|\| quenched & tempered at 750 °C (1382 °F) to 800 °C (1472 °F) to a UTS = 800 MPa (116 ksi) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : hardened at 1010 °C (1850 °F) \|\| double tempered at 649 °C (1200 °F) \|\| 20 °C to 550 °C (68 °F to 1022 °F) YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value %El : hardened at 982 °C (1800 °F) \|\| tempered 28C (50F) above test temperature \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : hardened at 982 °C (1800 °F) \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : hardened at 1010 °C (1850 °F) \|\| tempered 28C (50F) above test temperature \|\| 149 °C to 593 °C (300 °F to 1099 °F) %El : hardened at 1010 °C (1850 °F) \|\| double tempered at 649 °C (1200 °F) \|\| 20 °C to 550 °C (68 °F to 1022 °F) %El* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 300 °C (572 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 400 °C (752 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 500 °C (932 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 600 °C (1112 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 700 °C (1292 °F) \|\| room temperature value SR : oil quenched & tempered at 649 °C (1200 °F) \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁵ h SR : oil quenched & tempered at 649 °C (1200 °F) \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁵ h SR : oil quenched & tempered at 649 °C (1200 °F) \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁵ h SR : oil quenched & tempered at 649 °C (1200 °F) \|\| Master curve (LMP) \|\| 482 °C to 650 °C (899 °F to 1202 °F) SR : oil quenched & tempered at 663 °C (1225 °F) \|\| tested at 482 °C (900 °F) \|\| 1x10³ h to 1x10⁴ h SR : oil quenched & tempered at 663 °C (1225 °F) \|\| tested at 593 °C (1100 °F) \|\| 1x10³ h to 1x10⁴ h SR : oil quenched & tempered at 663 °C (1225 °F) \|\| tested at 649 °C (1200 °F) \|\| 1x10³ h to 1x10⁴ h SR : oil quenched & tempered at 663 °C (1225 °F) \|\| Master curve (LMP) \|\| 482 °C to 650 °C (899 °F to 1202 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
433 (AISI 433)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 1 h to 700 h SR : annealed \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F)
434 (UNS S43400) (WNr 1.4113) (ISO/EN/DIN X6CrMo17-1) (JIS SUS434) (AISI 434)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : strip \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain
436S (AISI 436S)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 1 h to 700 h SR : annealed \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F)
439 (UNS S43035) (WNr 1.4510) (ISO/EN/DIN X3CrTi17) (JIS SUS430LX) (ASTM A240/A268/A479/A651) (AISI 439) (AFNOR Z4CT17/Z8CT17)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
439HP (AISI 439HP)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value YS : annealed \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 2 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 2 h to 700 h SR : annealed \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F) FSN : annealed \|\| tested at 20 °C (68 °F), maximum stress \|\| 8x10⁴ cycles to 2x10⁶ cycles FSN : cold-rolled 66% \|\| tested at 20 °C (68 °F), maximum stress \|\| 4x10³ cycles to 2.6x10⁶ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
440A (UNS S44002) (WNr 1.4116) (ISO/EN/DIN X50CrMoV15) (ASTM A276/A314/A473/A580/F899) (AMS 5631) (GB & GB/T 7Cr17)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 288 °C (550 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 427 °C (800 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
440B (UNS S44003) (WNr 1.2361) (ISO/EN/DIN X91CrMoV18) (ASTM A276/A314/A473/A580/F899) (AISI 440B) (GB & GB/T 8Cr17)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
440C (UNS S44004) (WNr 1.3544/1.4125) (ISO/EN/DIN X105CrMo17) (JIS SUS440C) (ASTM A276/A314/A473/A493/A580/A756) (AISI 440C) (SAE J405) (AMS 5618/5630/5880/7445) (AFNOR Z100CD17) (GB & GB/T 11Cr17) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 700 °C (-460 °F to 1292 °F) DLL : solid \|\| -273 °C to 700 °C (-460 °F to 1292 °F) MTE : solid \|\| -273 °C to 700 °C (-460 °F to 1292 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 0 °C to 500 °C (32 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 260 °C (500 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 371 °C (700 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 260 °C (500 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 371 °C (700 °F) \|\| room temperature value YSC : heat-treated to hardness HRC 61 \|\| 0.1% offset \|\| 204 °C to 427 °C (399 °F to 800 °F) YSC : heat-treated to hardness HRC 61 \|\| 0.2% offset \|\| 204 °C to 427 °C (399 °F to 800 °F) %El* : effect of tempering temperature on RT value \|\| annealed \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 204 °C (400 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 260 °C (500 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 316 °C (600 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 371 °C (700 °F) \|\| room temperature value FSN : quenched & double tempered \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 9x10⁴ cycles to 2x10⁷ cycles NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| hardened \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| hardened \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Cronidur 30 (WNr 1.4108) (ISO/EN/DIN X30CrMoN151) (SAE 5898) (AMS 5659/5898) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| annealed \|\| -196 °C to 121 °C (-321 °F to 250 °F) D : solid \|\| as-hardened \|\| -196 °C to 121 °C (-321 °F to 250 °F) DLL : solid \|\| -196 °C to 121 °C (-321 °F to 250 °F) MTE : solid \|\| -196 °C to 121 °C (-321 °F to 250 °F) CTE : solid \|\| -196 °C to 121 °C (-321 °F to 250 °F) TC : solid \|\| high tempered \|\| -157 °C to 121 °C (-251 °F to 250 °F) TC : solid \|\| as-hardened \|\| -157 °C to 121 °C (-251 °F to 250 °F) TD : solid \|\| high tempered \|\| -157 °C to 121 °C (-251 °F to 250 °F) TD : solid \|\| as-hardened \|\| -157 °C to 121 °C (-251 °F to 250 °F) SH : solid \|\| -196 °C to 121 °C (-321 °F to 250 °F) UTS : solution annealed \|\| 2 minute anneal at 1250 °C (2282 °F) \|\| 20 °C to 230 °C (68 °F to 446 °F) UTS : solution annealed \|\| 5 minute anneal at 1250 °C (2282 °F) \|\| 20 °C to 230 °C (68 °F to 446 °F) %El : solution annealed \|\| 2 minute anneal at 1250 °C (2282 °F) \|\| 20 °C to 230 °C (68 °F to 446 °F) %El : solution annealed \|\| 5 minute anneal at 1250 °C (2282 °F) \|\| 20 °C to 230 °C (68 °F to 446 °F)
M314 (WNr 1.2085) (ISO/EN/DIN X33CrS16)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO : solid \|\| 20 °C to 1459 °C (68 °F to 2658 °F) RHO : liquid \|\| 1532 °C to 2150 °C (2789 °F to 3902 °F) SIGMA : solid \|\| 20 °C to 1459 °C (68 °F to 2658 °F) SIGMA : liquid \|\| 1532 °C to 2150 °C (2789 °F to 3902 °F)
Boehler N685 (WNr 1.2361/1.4112) (ISO/EN/DIN X90CrMoV18/X91CrMoV18)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Boehler N690 (WNr 1.4528) (ISO/EN/DIN X105CrCoMo18-2)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
441 (UNS S44100) (WNr 1.4509) (ISO/EN/DIN X2CrTiNb18) (ASTM A240/A554) (AISI 441)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : unknown condition \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h SR : unknown condition \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1,000 h SR : unknown condition \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
441 HP (AISI 441HP)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : solution annealed \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h SR : solution annealed \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1,000 h SR : solution annealed \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
443 (UNS S44300) (AISI 443) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| solution annealed \|\| 0 °C to 727 °C (32 °F to 1340 °F) UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F)
444 (UNS S44400) (WNr 1.4511/1.4521) (ISO/EN/DIN X2CrMoTi18-2/X3CrNb17) (JIS SUS444) (ASTM A176/A240/A268/A276/SA240/SA268) (SAE 51444) (AFNOR Z3CDT18-02) (GB & GB/T 00Cr18Mo2)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS* : solid \|\| room temperature value YS* : solid \|\| room temperature value %El* : solid \|\| room temperature value RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
446 (UNS S44600) (WNr 1.4749/1.4762/1.4763) (ISO/EN/DIN X10CrAlSi25/X18CrN28/X8Cr24) (JIS SUH446) (ASTM A268) (AFNOR Z10C24) (GB & GB/T 2Cr25N) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 0 °C to 650 °C (32 °F to 1202 °F) G : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) v : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| 0 °C to 1100 °C (32 °F to 2012 °F) TD : solid \|\| 16 °C to 887 °C (61 °F to 1628 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain SSC : annealed \|\| tested at 200 °C (392 °F), unknown strain rate \|\| 0 to 0.19 mm/mm strain SSC : annealed \|\| tested at 400 °C (752 °F), unknown strain rate \|\| 0 to 0.12 mm/mm strain SSC : annealed \|\| tested at 600 °C (1112 °F), unknown strain rate \|\| 0 to 0.33 mm/mm strain UTS : annealed \|\| 20 °C to 760 °C (68 °F to 1401 °F) YS : annealed \|\| 20 °C to 760 °C (68 °F to 1401 °F) %El : annealed \|\| 20 °C to 760 °C (68 °F to 1401 °F) SR : annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 500 °C to 901 °C (932 °F to 1654 °F) CRS : 1% plastic strain, annealed \|\| tested at 482 °C (900 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| tested at 760 °C (1400 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, annealed \|\| Master curve (LMP) \|\| 482 °C to 761 °C (899 °F to 1402 °F) NE : solid \|\| surface finish #1 \|\| -173 °C to 927 °C (-280 °F to 1700 °F) NE : solid \|\| surface finish #8 \|\| -173 °C to 927 °C (-280 °F to 1700 °F) NE : solid \|\| polished \|\| -187 °C to 880 °C (-305 °F to 1616 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| -23 °C to 877 °C (-10 °F to 1610 °F) SIGMA : solid \|\| -23 °C to 877 °C (-10 °F to 1610 °F)

AM-350 (UNS S35000) (ASTM A579/A693) (AISI 633) (SAE J467) (AMS 5546/5548/5554/5745) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) E : in tension \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : in compression \|\| 20 °C to 538 °C (68 °F to 1000 °F) G : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) v : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| solution annealed & aged \|\| 20 °C to 482 °C (68 °F to 900 °F) SSC : 5x10^-⁵/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.1 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.38 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.4 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.4 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.4 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.4 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.6 mm/mm strain SSC : 5x10^-⁵/s \|\| tested at 649 °C (1200 °F), held for 100 s \|\| 0 to 0.6 mm/mm strain SSC : 0.01/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.4 mm/mm strain SSC : 0.01/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.3 mm/mm strain SSC : 0.01/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.2 mm/mm strain SSC : 0.01/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.29 mm/mm strain SSC : 0.01/s \|\| tested at 649 °C (1200 °F), held for 100 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.6 mm/mm strain SSC : 1/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.4 mm/mm strain SSC : 1/s \|\| tested at 649 °C (1200 °F), held for 100 s \|\| 0 to 0.38 mm/mm strain UTS : solid \|\| sub-zero cooled & aged, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| sub-zero cooled & aged, long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| double-aged \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| WQ from 941 °C (1725 °F), 5x10^-⁵/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| WQ from 941 °C (1725 °F), 0.01/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| WQ from 941 °C (1725 °F), 1/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| sub-zero cooled & aged, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| sub-zero cooled & aged, long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| double-aged \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| WQ from 941 °C (1725 °F), 5x10^-⁵/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| WQ from 941 °C (1725 °F), 0.01/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| WQ from 941 °C (1725 °F), 1/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) YSC : solid \|\| sub-zero cooled & aged, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| sub-zero cooled & aged, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| double-aged \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| WQ from 941 °C (1725 °F), 5x10^-⁵/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| WQ from 941 °C (1725 °F), 0.01/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| WQ from 941 °C (1725 °F), 1/s strain rate \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 380 h to 573 h SR : air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 8 h to 860 h SR : sub-zero cooled, tempered at 454 °C (850 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : sub-zero cooled, tempered at 454 °C (850 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : sub-zero cooled, tempered at 538 °C (1000 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : sub-zero cooled, tempered at 538 °C (1000 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h FSN : double-aged \|\| tested at 20 °C (68 °F), axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.87x10⁴ cycles to 1x10⁷ cycles FSN : double-aged \|\| tested at 20 °C (68 °F), notched, K_t = 4, axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 9.8x10³ cycles to 1x10⁷ cycles FSN : double-aged \|\| tested at 20 °C (68 °F), axial, fusion welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.21x10⁴ cycles to 1x10⁷ cycles FSN : double-aged \|\| tested at 20 °C (68 °F), axial, spot welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.65x10⁴ cycles to 1x10⁷ cycles FSN : 20% cold-rolled & annealed \|\| tested at 20 °C (68 °F), axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.89x10⁴ cycles to 1x10⁷ cycles FSN : 20% cold-rolled & annealed \|\| tested at 20 °C (68 °F), notched, K_t = 4, axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 9.5x10³ cycles to 1x10⁷ cycles FSN : 20% cold-rolled & annealed \|\| tested at 20 °C (68 °F), axial, fusion welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.22x10⁴ cycles to 1x10⁷ cycles FSN : 20% cold-rolled & annealed \|\| tested at 20 °C (68 °F), axial, spot welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.69x10⁴ cycles to 1x10⁷ cycles FSN : subzero cooled & tempered 850 condition \|\| tested at 20 °C (68 °F), bending, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles CRS : 0.1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 0.5 h to 40 h CRS : 0.1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 20 h CRS : 0.1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| Master curve (LMP) \|\| 427 °C to 538 °C (800 °F to 1000 °F) CRS : 0.3% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 15 h to 600 h CRS : 0.3% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 700 h CRS : 0.3% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| Master curve (LMP) \|\| 427 °C to 538 °C (800 °F to 1000 °F) CRS : 0.5% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 30 h to 825 h CRS : 0.5% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 1 h to 65 h CRS : 0.5% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| Master curve (LMP) \|\| 427 °C to 538 °C (800 °F to 1000 °F) CRS : 1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 427 °C (800 °F) \|\| 110 h to 185 h CRS : 1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| tested at 538 °C (1000 °F) \|\| 1 h to 145 h CRS : 1% plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| Master curve (LMP) \|\| 427 °C to 538 °C (800 °F to 1000 °F) IC : tested at 427 °C (800 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, air-cooled from 954 °C (1750 °F), 399 °C (750 °F) for 2 h \|\| 100 h \|\| 0 to 0.01 mm/mm strain NE : solid \|\| polished to 2 micro-inch RMS \|\| 107 °C to 940 °C (224 °F to 1724 °F) NE : solid \|\| oxidized \|\| 107 °C to 920 °C (224 °F to 1688 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| solution annealed & aged \|\| -269 °C to 650 °C (-452 °F to 1202 °F) RHO : solid \|\| sub-zero cooled, tempered at 454 °C (850 °F) \|\| 20 °C to 732 °C (68 °F to 1350 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| solution annealed & aged \|\| -269 °C to 650 °C (-452 °F to 1202 °F) SIGMA : solid \|\| sub-zero cooled, tempered at 454 °C (850 °F) \|\| 20 °C to 732 °C (68 °F to 1350 °F)
AM-355 (UNS S35500) (ASTM A564/A579/A693/A705) (AISI 634) (SAE J467) (AMS 5547/5549/5594/5743/5744/5780) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) DLL : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) MTE : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) CTE : solid \|\| -196 °C to 593 °C (-321 °F to 1099 °F) E : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) G : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) v : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| 0 °C to 1350 °C (32 °F to 2462 °F) TD : solid \|\| 0 °C to 871 °C (32 °F to 1600 °F) SH : solid \|\| 0 °C to 1216 °C (32 °F to 2221 °F) UTS : bar \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : plate, 9.52 mm to 25.4 mm (0.375 inch to 1 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : plate, greater than 25.4 mm (1 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) UTS : cold-rolled & tempered, 95% martensite \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : bar \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : plate, 9.52 mm to 25.4 mm (0.375 inch to 1 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : cold-rolled & tempered, 95% martensite \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) YSC : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : bar \|\| subzero cooled & tempered at 454 °C (850 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : sheet, 0.127 mm to 4.76 mm (0.005 inch to 0.1875 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : plate, less than 9.52 mm (0.375 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : plate, 9.52 mm to 25.4 mm (0.375 inch to 1 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : plate, greater than 25.4 mm (1 inch) \|\| subzero cooled & tempered at 454 °C (850 °F), long transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : cold-rolled & tempered, 95% martensite \|\| transverse \|\| -253 °C to 25 °C (-424 °F to 77 °F) SR : subzero cooled & tempered at 454 °C (850 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : subzero cooled & tempered at 454 °C (850 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : subzero cooled & tempered at 454 °C (850 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : subzero cooled & tempered at 538 °C (1000 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : subzero cooled & tempered at 538 °C (1000 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : subzero cooled & tempered at 538 °C (1000 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h RHO : solid \|\| hardened & tempered \|\| 20 °C to 760 °C (68 °F to 1400 °F) SIGMA : solid \|\| hardened & tempered \|\| 20 °C to 760 °C (68 °F to 1400 °F)
13-8 Mo PH (UNS S13800) (WNr 1.4534) (ISO/EN/DIN X3CrNiMoAl13-8-2) (ASTM A564/A693/A705/XM-13) (AMS 5629/5840/5864/5934) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) D : liquid \|\| 1541 °C to 2327 °C (2806 °F to 4220 °F) DLL : solid \|\| H950 \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| H1000 \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| H1050 \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| H1100 \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| average \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : liquid \|\| 1541 °C to 2327 °C (2806 °F to 4220 °F) MTE : solid \|\| H950 \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| H1000 \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| H1050 \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| H1100 \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| average \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : liquid \|\| 1541 °C to 2327 °C (2806 °F to 4220 °F) CTE : solid \|\| H950 \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| H1000 \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| H1050 \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| H1100 \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| average \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : liquid \|\| 1541 °C to 2327 °C (2806 °F to 4220 °F) E : solid \|\| in tension \|\| -74 °C to 538 °C (-101 °F to 1000 °F) E : solid \|\| in compression \|\| 20 °C to 427 °C (68 °F to 800 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) TC : liquid \|\| 1541 °C to 2160 °C (2806 °F to 3920 °F) TD : liquid \|\| 1541 °C to 2160 °C (2806 °F to 3920 °F) SH : liquid \|\| 1541 °C to 2160 °C (2806 °F to 3920 °F) SSC : H1100 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.13 mm/mm strain UTS* : solid \|\| H950 condition \|\| room temperature value UTS : solid \|\| H1000 condition \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS* : solid \|\| H1025 condition \|\| room temperature value UTS* : solid \|\| H1050 condition \|\| room temperature value UTS : solid \|\| H1100 condition \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS* : solid \|\| H1150 condition \|\| room temperature value YS* : solid \|\| H950 condition \|\| room temperature value YS : solid \|\| H1000 condition \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS* : solid \|\| H1025 condition \|\| room temperature value YS* : solid \|\| H1050 condition \|\| room temperature value YS : solid \|\| H1100 condition \|\| 20 °C to 371 °C (68 °F to 700 °F) YS* : solid \|\| H1150 condition \|\| room temperature value %El* : solid \|\| H950 condition \|\| room temperature value %El : solid \|\| H1000 condition \|\| -196 °C to 538 °C (-321 °F to 1000 °F) %El* : solid \|\| H1025 condition \|\| room temperature value %El* : solid \|\| H1050 condition \|\| room temperature value %El : solid \|\| H1100 condition \|\| 20 °C to 371 °C (68 °F to 700 °F) %El* : solid \|\| H1150 condition \|\| room temperature value SR : H1000 forged bar \|\| tested at 260 °C (500 °F) \|\| 10 h to 1,000 h SR : H1000 forged bar \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h SR : H1000 forged bar \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : H1000 forged bar \|\| Master curve (LMP) \|\| 260 °C to 538 °C (500 °F to 1000 °F) FEN : H1000 \|\| tested at 20 °C (68 °F), R = 0, axial, maximum strain \|\| 850 cycles to 4x10⁶ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4.6x10³ cycles to 1.3x10⁷ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = 0.5, axial, maximum stress \|\| 4x10⁵ cycles to 1x10⁷ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.9x10⁴ cycles to 1x10⁸ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, K_t = 2.8, rotating beam, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁸ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.8, rotating beam, maximum stress \|\| 1.7x10⁴ cycles to 1x10⁸ cycles CRS : 0.2% plastic strain, H1000 forged bar \|\| tested at 260 °C (500 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1000 forged bar \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1000 forged bar \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1000 forged bar \|\| Master curve (LMP) \|\| 260 °C to 538 °C (500 °F to 1000 °F) RHO : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) RHO : liquid \|\| 1541 °C to 2160 °C (2806 °F to 3920 °F) SIGMA : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) SIGMA : liquid \|\| 1541 °C to 2160 °C (2806 °F to 3920 °F) RPB : H950 condition \|\| tested at 20 °C (68 °F) AP : H950 condition \|\| tested at 20 °C (68 °F) BH : H950 condition \|\| tested at 20 °C (68 °F) HB : H950 condition \|\| tested at 20 °C (68 °F)
14-8 Mo PH (UNS S14800) (AMS 5601/5603)	D : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) DLL : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) MTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) CTE : solid \|\| 20 °C to 540 °C (68 °F to 1004 °F) E : H1050 sheet, in tension \|\| longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : H1050 sheet, in tension \|\| transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : H1050 sheet, in tension \|\| average \|\| 20 °C to 482 °C (68 °F to 900 °F) E : H1050 sheet, in compression \|\| longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) E : H1050 sheet, in compression \|\| transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) E : H1050 sheet, in compression \|\| average \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : H950 \|\| longitudinal \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : H950 \|\| transverse \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : H1050 sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : H1050 sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : H950 \|\| longitudinal \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : H950 \|\| transverse \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : H1050 sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : H1050 sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : H1050 sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : H1050 sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : H950 \|\| longitudinal \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : H950 \|\| transverse \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : H1050 sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : H1050 sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : H1050 sheet \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h SR : H1050 sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : H1050 sheet \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h FSN : H1050 sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 sheet, smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 sheet, smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 sheet, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 sheet, notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 sheet, notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, H1050 sheet \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1050 sheet \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1050 sheet \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h
15-5 PH (UNS S15500) (WNr 1.4594) (ISO/EN/DIN X5CrNiMoCuNb14-5) (ASTM A564/A693/A705/F899/XM-12) (AMS 5658/5659/5826) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -73 °C to 427 °C (-100 °F to 800 °F) DLL : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) DLL : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| H1150 \|\| -73 °C to 502 °C (-100 °F to 935 °F) MTE : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) MTE : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| H1150 \|\| -73 °C to 502 °C (-100 °F to 935 °F) CTE : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) CTE : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| H1150 \|\| -73 °C to 502 °C (-100 °F to 935 °F) E : solid \|\| in tension \|\| 20 °C to 482 °C (68 °F to 900 °F) E : solid \|\| in compression \|\| 20 °C to 482 °C (68 °F to 900 °F) G* : solid \|\| room temperature value v* : solid \|\| tension \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| H900 \|\| 2 °C to 538 °C (35 °F to 1000 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : bar/forging \|\| H900 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : bar/forging \|\| H925 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : bar/forging \|\| H1025 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : bar/forging \|\| H1075 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : bar/forging \|\| H1100 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : bar/forging \|\| H1150 \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : plate \|\| H1025, 4.76 mm to 15.9 mm (0.1875 inch to 0.625 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : plate \|\| H1025, 15.9 mm to 50.8 mm (0.625 inch to 2 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) UTS : plate \|\| H1025, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H900 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H925 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H1025 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H1075 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H1100 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : bar/forging \|\| H1150 \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : plate \|\| H1025, 4.76 mm to 15.9 mm (0.1875 inch to 0.625 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : plate \|\| H1025, 15.9 mm to 50.8 mm (0.625 inch to 2 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) YS : plate \|\| H1025, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| -196 °C to 427 °C (-321 °F to 800 °F) YSC : bar/forging \|\| H1025 \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : bar/forging \|\| H1150 \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : H1025, forged bar \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h SR : H1025, forged bar \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : H1025, forged bar \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : H1025, forged bar \|\| Master curve (LMP) \|\| 371 °C to 594 °C (700 °F to 1101 °F) FSN : H900 \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 7x10⁴ cycles to 1x10⁷ cycles FSN : H900 \|\| tested at 20 °C (68 °F), shot peened, R = -1, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : H1025, forged bar, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1025, forged bar, smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1025, forged bar, smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 5.2x10³ cycles to 1x10⁷ cycles FSN : H1025, forged bar, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1025, forged bar, notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1025, forged bar, notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1050 \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : H1050 \|\| tested at 20 °C (68 °F), shot peened, R = -1, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, H1025, forged bar \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1025, forged bar \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1025, forged bar \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H1025, forged bar \|\| Master curve (LMP) \|\| 371 °C to 594 °C (700 °F to 1101 °F) RHO* : solid \|\| annealed \|\| room temperature value RHO* : solid \|\| H900 \|\| room temperature value RHO* : solid \|\| H1075 \|\| room temperature value RHO* : solid \|\| H1150 \|\| room temperature value SIGMA: solid \|\| annealed \|\| room temperature value SIGMA: solid \|\| H900 \|\| room temperature value SIGMA: solid \|\| H1075 \|\| room temperature value SIGMA: solid \|\| H1150 \|\| room temperature value RPB : condition A \|\| tested at 20 °C (68 °F) RPB : H900 \|\| tested at 20 °C (68 °F) RPB : H1075 & H1100 conditions \|\| tested at 20 °C (68 °F) RPB : H1150 \|\| tested at 20 °C (68 °F) AP : condition A \|\| tested at 20 °C (68 °F) AP : H900 \|\| tested at 20 °C (68 °F) AP : H1075 & H1100 conditions \|\| tested at 20 °C (68 °F) AP : H1150 \|\| tested at 20 °C (68 °F) BH : condition A \|\| tested at 20 °C (68 °F) BH : H900 \|\| tested at 20 °C (68 °F) BH : H1075 & H1100 conditions \|\| tested at 20 °C (68 °F) BH : H1150 \|\| tested at 20 °C (68 °F) HB : condition A \|\| tested at 20 °C (68 °F) HB : H900 \|\| tested at 20 °C (68 °F) HB : H1075 & H1100 conditions \|\| tested at 20 °C (68 °F) HB : H1150 \|\| tested at 20 °C (68 °F)
15-7 Mo PH (UNS S15700) (WNr 1.4532/1.4574) (ASTM A461/A564/A579/A693/A705) (AISI 632) (SAE J476) (AMS 5520/5657/5812/5813) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| mill annealed, rapid cooled (condition A) \|\| 20 °C to 316 °C (68 °F to 600 °F) D : solid \|\| RH950 \|\| 20 °C to 316 °C (68 °F to 600 °F) D : solid \|\| H1050 \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| mill annealed, rapid cooled (condition A) \|\| 20 °C to 316 °C (68 °F to 600 °F) DLL : solid \|\| RH950 \|\| 20 °C to 316 °C (68 °F to 600 °F) DLL : solid \|\| H1050 \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| mill annealed, rapid cooled (condition A) \|\| 20 °C to 316 °C (68 °F to 600 °F) MTE : solid \|\| RH950 \|\| 20 °C to 316 °C (68 °F to 600 °F) MTE : solid \|\| H1050 \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| mill annealed, rapid cooled (condition A) \|\| 20 °C to 316 °C (68 °F to 600 °F) CTE : solid \|\| RH950 \|\| 20 °C to 316 °C (68 °F to 600 °F) CTE : solid \|\| H1050 \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : in tension \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : in compression \|\| 20 °C to 538 °C (68 °F to 1000 °F) G : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) v : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) K : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TC : solid \|\| 20 °C to 493 °C (68 °F to 919 °F) UTS : solid \|\| CH 900 (longitudinal) \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : solid \|\| CH 900 (transverse) \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : solid \|\| RH 950 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : solid \|\| TH 950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solid \|\| TH 1050 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : solid \|\| CH 900 (longitudinal) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : solid \|\| CH 900 (transverse) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : solid \|\| RH 950 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : solid \|\| TH 950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| TH 1050 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : solid \|\| CH 900 (longitudinal) \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : solid \|\| CH 900 (transverse) \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : solid \|\| RH 950 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : solid \|\| TH 950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| TH 1050 \|\| 20 °C to 540 °C (68 °F to 1004 °F) SR : RH 950 \|\| tested at 316 °C (600 °F) \|\| 100 h to 1,000 h SR : RH 950 \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : RH 950 \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : RH 950 \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : RH 950 \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) SR : TH 950 \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,120 h SR : TH 1050 \|\| tested at 316 °C (600 °F) \|\| 100 h to 1,000 h SR : TH 1050 \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : TH 1050 \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : TH 1050 \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : TH 1050 \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) FSN : TH 1050 \|\| tested at 20 °C (68 °F), axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 3.5x10⁴ cycles to 8.7x10⁶ cycles FSN : TH 1050 \|\| tested at 20 °C (68 °F), notched, K_t = 4, axial, mean stress of 276 MPa (40 ksi), maximum stress \|\| 2.05x10⁴ cycles to 1x10⁷ cycles FSN : TH 1050 \|\| tested at 20 °C (68 °F), axial, fusion welded prior to heat treatment, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.68x10⁴ cycles to 1x10⁷ cycles FSN : TH 1050 \|\| tested at 20 °C (68 °F), axial, fusion welded after heat treatment, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.42x10⁴ cycles to 1x10⁷ cycles FSN : TH 1050 \|\| tested at 20 °C (68 °F), axial, spot welded, mean stress of 276 MPa (40 ksi), maximum stress \|\| 1.57x10⁴ cycles to 1x10⁷ cycles CRS : 0.1% plastic strain, TH 950 \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 1,000 h CRS : 0.3% plastic strain, TH 950 \|\| tested at 538 °C (1000 °F) \|\| 0.5 h to 750 h CRS : 0.5% plastic strain, TH 950 \|\| tested at 538 °C (1000 °F) \|\| 1 h to 370 h CRS : 1% plastic strain, TH 950 \|\| tested at 538 °C (1000 °F) \|\| 0.7 h to 75 h CRS : 0.2% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 0.5 h to 5.4 h CRS : 0.2% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.18 h to 1.7 h CRS : 0.2% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 0.7 h to 9.3 h CRS : 0.2% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 0.3% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 0.13 h to 4.1 h CRS : 0.3% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.26 h to 0.45 h CRS : 0.3% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 0.9 h to 46 h CRS : 0.3% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 0.5% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 0.13 h to 17 h CRS : 0.5% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.43 h to 3.1 h CRS : 0.5% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 0.16 h to 12 h CRS : 0.5% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 1% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 0.45 h to 12 h CRS : 1% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.8 h to 5.3 h CRS : 1% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 0.35 h to 205 h CRS : 1% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 2% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 1.6 h to 70 h CRS : 2% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.16 h to 7.4 h CRS : 2% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 1.2 h to 260 h CRS : 2% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 3% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 4 h to 110 h CRS : 3% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.24 h to 35 h CRS : 3% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 0.75 h to 440 h CRS : 3% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) CRS : 5% plastic strain, TH 1050 \|\| tested at 371 °C (700 °F) \|\| 5.1 h to 34 h CRS : 5% plastic strain, TH 1050 \|\| tested at 427 °C (800 °F) \|\| 0.34 h to 11 h CRS : 5% plastic strain, TH 1050 \|\| tested at 482 °C (900 °F) \|\| 1.3 h to 430 h CRS : 5% plastic strain, TH 1050 \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, TH 950 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, TH 1050 \|\| 0.3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, TH 1050 \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, TH 1050 \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, TH 1050 \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, TH 1050 \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, TH 1050 \|\| 0.3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, TH 1050 \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, TH 1050 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 0.3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, TH 1050 \|\| 100 h \|\| 0 to 0.5 mm/mm strain NE : solid \|\| polished \|\| -229 °C to 770 °C (-380 °F to 1418 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
17-4 PH (UNS S17400) (WNr 1.4542/1.4548) (ISO/EN/DIN X5CrNiCuNb16-4) (JIS SUS630) (ASTM A564/A693/A705) (AISI 630) (AMS 5604/5622/5643/5825/5827/7474) (AFNOR Z6CNU17.04) (GB & GB/T 0Cr17Ni4Cu4Nb) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) D : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) D : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) D : solid \|\| H1100 \|\| -272 °C to 27 °C (-458 °F to 80 °F) D : solid \|\| H1150 \|\| -73 °C to 427 °C (-100 °F to 800 °F) DLL : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) DLL : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| H1100 \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : solid \|\| H1150 \|\| -73 °C to 427 °C (-100 °F to 800 °F) MTE : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) MTE : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| H1100 \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : solid \|\| H1150 \|\| -73 °C to 427 °C (-100 °F to 800 °F) CTE : solid \|\| solution treated \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| H900 \|\| -73 °C to 427 °C (-100 °F to 800 °F) CTE : solid \|\| H1075 \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| H1100 \|\| -253 °C to 27 °C (-424 °F to 80 °F) CTE : solid \|\| H1150 \|\| -73 °C to 427 °C (-100 °F to 800 °F) E : cast, overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) E : wrought \|\| in tension \|\| 20 °C to 316 °C (68 °F to 600 °F) E : wrought \|\| in compression \|\| 20 °C to 316 °C (68 °F to 600 °F) E* : laser powder bed fusion \|\| room temperature value G : cast, overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) G* : wrought \|\| room temperature value v : cast, overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) v* : wrought \|\| room temperature value K : cast, overaged \|\| -25 °C to 889 °C (-13 °F to 1632 °F) K* : wrought \|\| room temperature value TC : solid \|\| wrought \|\| 0 °C to 1395 °C (32 °F to 2543 °F) TC : solid \|\| cast, overaged \|\| 20 °C to 688 °C (68 °F to 1270 °F) TC : solid \|\| H900 \|\| 0 °C to 482 °C (32 °F to 900 °F) TD : solid \|\| wrought \|\| 0 °C to 865 °C (32 °F to 1589 °F) TD : solid \|\| cast, overaged \|\| 20 °C to 688 °C (68 °F to 1270 °F) SH : solid \|\| wrought \|\| -18 °C to 865 °C (-1 °F to 1589 °F) SH : solid \|\| cast, overaged \|\| 20 °C to 652 °C (68 °F to 1205 °F) SSC : H1100 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : H1100 \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : H1100 \|\| tested at -195.6 °C (-320 °F), unknown strain rate \|\| 0 to 0.3 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, as-built, vertical \|\| 0 to 0.46 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, as-built, horizontal \|\| 0 to 0.3 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, H900, vertical \|\| 0 to 0.16 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, H900, horizontal \|\| 0 to 0.71 mm/mm strain SSC : cast, overaged \|\| tested at -40 °C (-40 °F), 1.6x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : cast, overaged \|\| tested at -40 °C (-40 °F), 1.2/s \|\| 0 to 0.78 mm/mm strain SSC : cast, overaged \|\| tested at 24 °C (75 °F), 1.6x10^-⁴/s \|\| 0 to 0.75 mm/mm strain SSC : cast, overaged \|\| tested at 24 °C (75 °F), 1.2/s \|\| 0 to 0.63 mm/mm strain SSC : cast, overaged \|\| tested at 150 °C (302 °F), 1.6x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : cast, overaged \|\| tested at 150 °C (302 °F), 1.2/s \|\| 0 to 0.54 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.83 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.82 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.75 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.8 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.79 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.82 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.8 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.78 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.83 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.82 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.79 mm/mm strain SSCC : austenitized at 1179 °C (2155 °F), 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.77 mm/mm strain SSCC : cast, overaged \|\| tested at -40 °C (-40 °F), 1.3x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSCC : cast, overaged \|\| tested at -40 °C (-40 °F), 1.2/s \|\| 0 to 0.9 mm/mm strain SSCC : cast, overaged \|\| tested at 24 °C (75 °F), 1.3x10^-⁴/s \|\| 0 to 0.12 mm/mm strain SSCC : cast, overaged \|\| tested at 24 °C (75 °F), 1.2/s \|\| 0 to 0.81 mm/mm strain SSCC : cast, overaged \|\| tested at 150 °C (302 °F), 1.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSCC : cast, overaged \|\| tested at 150 °C (302 °F), 1.2/s \|\| 0 to 0.124 mm/mm strain UTS : cast, overaged \|\| 0.00014/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) UTS : cast, overaged \|\| 0.12/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) UTS : wrought \|\| H900 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : wrought \|\| H925 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : wrought \|\| H1025 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : wrought \|\| H1075 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : wrought \|\| H1100 \|\| -253 °C to 20 °C (-424 °F to 68 °F) UTS : wrought \|\| H1150 \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS* : laser powder bed fusion \|\| as-built, vertical \|\| room temperature value UTS* : laser powder bed fusion \|\| as-built, horizontal \|\| room temperature value UTS* : laser powder bed fusion \|\| H900, vertical \|\| room temperature value UTS* : laser powder bed fusion \|\| H900, horizontal \|\| room temperature value YS : cast, overaged \|\| 0.00014/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) YS : cast, overaged \|\| 0.12/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) YS : wrought \|\| H900 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : wrought \|\| H925 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : wrought \|\| H1025 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : wrought \|\| H1075 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : wrought \|\| H1100 \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS : wrought \|\| H1150 \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS* : laser powder bed fusion \|\| as-built, vertical \|\| room temperature value YS* : laser powder bed fusion \|\| as-built, horizontal \|\| room temperature value YS* : laser powder bed fusion \|\| H900, vertical \|\| room temperature value YS* : laser powder bed fusion \|\| H900, horizontal \|\| room temperature value YSC : cast, overaged \|\| 1.3x10^-⁴/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) YSC : cast, overaged \|\| 0.12/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) %El : cast, overaged \|\| 0.00014/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) %El : cast, overaged \|\| 0.12/s strain rate \|\| -39 °C to 150 °C (-38 °F to 302 °F) %El : wrought \|\| H900 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : wrought \|\| H925 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : wrought \|\| H1025 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : wrought \|\| H1075 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El : wrought \|\| H1100 \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El : wrought \|\| H1150 \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El* : laser powder bed fusion \|\| as-built, vertical \|\| room temperature value %El* : laser powder bed fusion \|\| as-built, horizontal \|\| room temperature value %El* : laser powder bed fusion \|\| H900, vertical \|\| room temperature value %El* : laser powder bed fusion \|\| H900, horizontal \|\| room temperature value SR : H900, 25.4 mm (1 inch) bar \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : H900, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : H900, 25.4 mm (1 inch) bar \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : H900, 25.4 mm (1 inch) bar \|\| Master curve (LMP) \|\| 371 °C to 483 °C (700 °F to 901 °F) SR : H925, 25.4 mm (1 inch) bar \|\| tested at 329 °C (625 °F) \|\| 100 h to 1,000 h SR : H925, 25.4 mm (1 inch) bar \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : H925, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : H925, 25.4 mm (1 inch) bar \|\| Master curve (LMP) \|\| 329 °C to 427 °C (624 °F to 800 °F) SR : H1075, 25.4 mm (1 inch) bar \|\| tested at 329 °C (625 °F) \|\| 100 h to 1,000 h SR : H1075, 25.4 mm (1 inch) bar \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : H1075, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : H1075, 25.4 mm (1 inch) bar \|\| Master curve (LMP) \|\| 329 °C to 427 °C (624 °F to 800 °F) SR : H1150, 25.4 mm (1 inch) bar \|\| tested at 329 °C (625 °F) \|\| 100 h to 1,000 h SR : H1150, 25.4 mm (1 inch) bar \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : H1150, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : H1150, 25.4 mm (1 inch) bar \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : H1150, 25.4 mm (1 inch) bar \|\| Master curve (LMP) \|\| 329 °C to 483 °C (624 °F to 901 °F) SR : H900, 83.8 mm (3.3 inch) bar (ESR) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : H900, 83.8 mm (3.3 inch) bar (ESR) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, vertical, total strain amplitude \|\| 210 cycles to 2.4x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, vertical, elastic strain amplitude \|\| 210 cycles to 2.4x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, vertical, plastic strain amplitude \|\| 210 cycles to 1.53x10⁴ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, horizontal, total strain amplitude \|\| 750 cycles to 1.15x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, horizontal, elastic strain amplitude \|\| 750 cycles to 1.15x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, as-built, horizontal, plastic strain amplitude \|\| 750 cycles to 1.15x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, H900, vertical, total strain amplitude \|\| 650 cycles to 1x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, H900, vertical, elastic strain amplitude \|\| 650 cycles to 1x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, H900, vertical, plastic strain amplitude \|\| 650 cycles to 7.6x10³ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, H900, horizontal, total strain amplitude \|\| 1x10³ cycles to 1.3x10⁶ cycles FEN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = -1, H900, horizontal, elastic strain amplitude \|\| 1x10³ cycles to 1.3x10⁶ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900, 83.8 mm (3.3 inch) bar (ESR), notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H1025 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 6x10⁴ cycles to 2x10⁸ cycles FSN : H1150, low cycle \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁴ cycles to 6x10⁷ cycles FSN : H1150, high cycle \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 8x10⁶ cycles to unknown strain rate cycles FSN : H1150, torsion \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, 19 kHz, maximum stress \|\| 1.4x10⁶ cycles to 1x10⁹ cycles FSN : H1150, torsion \|\| tested at 20 °C (68 °F), R = -1, 15 Hz and 35 Hz, maximum stress \|\| 8x10⁵ cycles to 1x10⁷ cycles FSN : H1150, torsion \|\| tested at 20 °C (68 °F), R = -1, with 2-hole defects, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles CRS : 0.2% plastic strain, H900, 83.8 mm (3.3 inch) bar (ESR) \|\| tested at 371 °C (700 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H900, 83.8 mm (3.3 inch) bar (ESR) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, H900, 83.8 mm (3.3 inch) bar (ESR) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h IC : tested at 316 °C (600 °F), plastic strain, H900 \|\| 1,000 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, H900 \|\| 1,000 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, H900 \|\| 1,000 h \|\| 0 to 1x10^-³ mm/mm strain RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO* : solid \|\| H900 \|\| room temperature value RHO* : solid \|\| H1075 \|\| room temperature value RHO* : solid \|\| H1150 \|\| room temperature value SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA: solid \|\| H900 \|\| room temperature value SIGMA: solid \|\| H1075 \|\| room temperature value SIGMA*: solid \|\| H1150 \|\| room temperature value
17-7 PH (UNS S17700) (WNr 1.4568) (ISO/EN/DIN X7CrNiAl17-7) (JIS SUS631) (ASTM A313/A564/A579/A693/A705) (AISI 631) (AMS 5528/5529/5568/5644/5678/5824) (AFNOR Z3CNU18-09FF) (GB & GB/T 0Cr17Ni7Al) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 316 °C (-460 °F to 600 °F) DLL : solid \|\| -273 °C to 316 °C (-460 °F to 600 °F) MTE : solid \|\| -273 °C to 316 °C (-460 °F to 600 °F) E : in tension \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : in compression \|\| 20 °C to 538 °C (68 °F to 1000 °F) G : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) v : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) K : solid \|\| 20 °C to 370 °C (68 °F to 698 °F) TC : solid \|\| 20 °C to 1036 °C (68 °F to 1897 °F) TD : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) SH : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SSC : 5x10^-⁵/s, annealed \|\| tested at 27 °C (80 °F) \|\| 0 to 0.31 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.11 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.25 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.22 mm/mm strain SSC : 5x10^-⁵/s, annealed \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain SSC : 0.01/s, annealed \|\| tested at 27 °C (80 °F) \|\| 0 to 0.28 mm/mm strain SSC : 0.01/s, annealed \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.11 mm/mm strain SSC : 0.01/s, annealed \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.15 mm/mm strain SSC : 0.01/s, annealed \|\| tested at 204 °C (400 °F) \|\| 0 to 0.18 mm/mm strain SSC : 0.01/s, annealed \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain SSC : 1/s, annealed \|\| tested at 27 °C (80 °F) \|\| 0 to 0.31 mm/mm strain SSC : 1/s, annealed \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : 1/s, annealed \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.11 mm/mm strain SSC : 1/s, annealed \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : 1/s, annealed \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : 1/s, annealed \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : 1/s, annealed \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.11 mm/mm strain UTS : solid \|\| transformation hardened at 566 °C (1050 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| refrigeration hardened at -200 °C (-328 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| TH 1050 \|\| -253 °C to 650 °C (-424 °F to 1202 °F) UTS : solid \|\| cold worked & hardened at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) UTS : solid \|\| TH 950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| transformation hardened at 566 °C (1050 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| refrigeration hardened at -200 °C (-328 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| TH 1050 \|\| -197 °C to 650 °C (-323 °F to 1202 °F) YS : solid \|\| cold worked & hardened at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) YS : solid \|\| TH 950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| transformation hardened at 566 °C (1050 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| refrigeration hardened at -200 °C (-328 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : solid \|\| TH 1050 \|\| -253 °C to 650 °C (-424 °F to 1202 °F) %El : solid \|\| cold worked & hardened at 482 °C (900 °F) \|\| 20 °C to 482 °C (68 °F to 900 °F) SR : transformation hardened \|\| tested at 316 °C (600 °F) \|\| 100 h to 1,000 h SR : transformation hardened \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : transformation hardened \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : transformation hardened \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : transformation hardened \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) SR : refrigeration hardened \|\| tested at 316 °C (600 °F) \|\| 100 h to 1,000 h SR : refrigeration hardened \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : refrigeration hardened \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : refrigeration hardened \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : refrigeration hardened \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) SR : cold worked & hardened \|\| tested at 316 °C (600 °F) \|\| 100 h to 1,000 h SR : cold worked & hardened \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : cold worked & hardened \|\| tested at 427 °C (800 °F) \|\| 100 h to 1,000 h SR : cold worked & hardened \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h FSN : TH 1050 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : TH 1050 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : TH 1050 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : TH 1050 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 8x10³ cycles to 8x10⁶ cycles FSN : RH 950 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : RH 950, K_t = 3 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles CRS : 0.05% total strain, RH950 \|\| tested at 316 °C (600 °F) \|\| 0.2 h to 1,200 h CRS : 0.05% total strain, RH950 \|\| tested at 427 °C (800 °F) \|\| 0.2 h to 1,050 h CRS : 0.05% total strain, RH950 \|\| tested at 482 °C (900 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, RH950 \|\| tested at 316 °C (600 °F) \|\| 0.2 h to 1,240 h CRS : 0.1% total strain, RH950 \|\| tested at 427 °C (800 °F) \|\| 0.1 h to 820 h CRS : 0.1% total strain, RH950 \|\| tested at 482 °C (900 °F) \|\| 0.2 h to 220 h CRS : 0.3% total strain, RH950 \|\| tested at 316 °C (600 °F) \|\| 0.4 h to 170 h CRS : 0.3% total strain, RH950 \|\| tested at 427 °C (800 °F) \|\| 0.5 h to 1,000 h CRS : 0.3% total strain, RH950 \|\| tested at 482 °C (900 °F) \|\| 0.1 h to 5,040 h CRS : 0.3% total strain, RH950 \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) CRS : 0.5% total strain, RH950 \|\| tested at 316 °C (600 °F) \|\| 0.4 h to 730 h CRS : 0.5% total strain, RH950 \|\| tested at 427 °C (800 °F) \|\| 0.2 h to 1,100 h CRS : 0.5% total strain, RH950 \|\| tested at 482 °C (900 °F) \|\| 0.9 h to 750 h CRS : 0.5% total strain, RH950 \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) CRS : 1% total strain, RH950 \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 800 h CRS : 1% total strain, RH950 \|\| tested at 427 °C (800 °F) \|\| 0.3 h to 900 h CRS : 1% total strain, RH950 \|\| tested at 482 °C (900 °F) \|\| 0.3 h to 1,000 h CRS : 1% total strain, RH950 \|\| Master curve (LMP) \|\| 315 °C to 483 °C (599 °F to 901 °F) IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, RH950 \|\| 1,000 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), total strain, RH950 \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), total strain, RH950 \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain NE : solid \|\| polished to 2 micro-inch RMS \|\| -218 °C to 720 °C (-361 °F to 1328 °F) NE : solid \|\| polished to 15 micro-inch RMS \|\| -218 °C to 700 °C (-361 °F to 1292 °F) RHO : solid \|\| annealed \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 300 °C (68 °F to 572 °F)

Gall-tough (UNS S20161) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F) YS : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F) %El : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F)
Gall-tough Plus (UNS S20162/S21800) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F) YS : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F) %El : annealed & quenched \|\| -73 °C to 871 °C (-100 °F to 1600 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
ATI S240 alloy (UNS S11900) (AMS 5929) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 430 °C (68 °F to 806 °F) DLL : solid \|\| 20 °C to 430 °C (68 °F to 806 °F) MTE : solid \|\| 20 °C to 430 °C (68 °F to 806 °F) CTE : solid \|\| 20 °C to 430 °C (68 °F to 806 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) TD : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) SH : solid \|\| 20 °C to 425 °C (68 °F to 797 °F) UTS : 102 mm (4 inch) round forged bar \|\| H950 \|\| -73 °C to 440 °C (-100 °F to 824 °F) UTS : 102 mm (4 inch) round forged bar \|\| H1000 \|\| -73 °C to 567 °C (-100 °F to 1052 °F) YS : 102 mm (4 inch) round forged bar \|\| H950 \|\| -73 °C to 440 °C (-100 °F to 824 °F) YS : 102 mm (4 inch) round forged bar \|\| H1000 \|\| -73 °C to 567 °C (-100 °F to 1052 °F) %El : 102 mm (4 inch) round forged bar \|\| H950 \|\| -73 °C to 440 °C (-100 °F to 824 °F) %El : 102 mm (4 inch) round forged bar \|\| H1000 \|\| -73 °C to 567 °C (-100 °F to 1052 °F) FSN : H950 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3.8x10⁴ cycles to 1x10⁸ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.4x10⁴ cycles to 1x10⁸ cycles
EOS StainlessSteel CX	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS* : heat-treated state \|\| vertical \|\| room temperature value UTS* : heat-treated state \|\| horizontal \|\| room temperature value YS* : heat-treated state \|\| vertical \|\| room temperature value YS* : heat-treated state \|\| horizontal \|\| room temperature value %El* : heat-treated state \|\| vertical \|\| room temperature value %El* : heat-treated state \|\| horizontal \|\| room temperature value FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, as-built, stress amplitude \|\| 2.8x10⁴ cycles to 1x10⁷ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, as-built, machined surface, stress amplitude \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, heat-treated, stress amplitude \|\| 1.7x10⁴ cycles to 1x10⁷ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, vertical, heat-treated, machined surface, stress amplitude \|\| 7x10⁴ cycles to 1x10⁷ cycles FSN : laser powder bed fusion \|\| tested at 20 °C (68 °F), R = 0.1, axial, horizontal, heat-treated, machined surface, stress amplitude \|\| 2.7x10⁴ cycles to 1x10⁷ cycles
THERMAK 17	D : solid \|\| 20 °C to 894 °C (68 °F to 1641 °F) DLL : solid \|\| 20 °C to 914 °C (68 °F to 1677 °F) MTE : solid \|\| 20 °C to 914 °C (68 °F to 1677 °F) CTE : solid \|\| 20 °C to 914 °C (68 °F to 1677 °F) SH* : solid \|\| room temperature value UTS* : annealed \|\| at RT \|\| room temperature value UTS : annealed \|\| T > 600 °C (1112 °F) \|\| 600 °C to 892 °C (1112 °F to 1637 °F) YS* : annealed \|\| at RT \|\| room temperature value YS : annealed \|\| T > 600 °C (1112 °F) \|\| 600 °C to 894 °C (1112 °F to 1641 °F) %El* : annealed \|\| room temperature value
Custom 450 (UNS S45000) (ASTM A564/A693/A705/A959/XM-25) (AMS 5763/5773/5863) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) DLL : solid \|\| annealed & quenched \|\| 20 °C to 593 °C (68 °F to 1099 °F) DLL : solid \|\| annealed & aged (condition H900) \|\| 20 °C to 593 °C (68 °F to 1099 °F) MTE : solid \|\| annealed & quenched \|\| 20 °C to 593 °C (68 °F to 1099 °F) MTE : solid \|\| annealed & aged (condition H900) \|\| 20 °C to 593 °C (68 °F to 1099 °F) E : H900 strip, in tension \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) E : H900 strip, in tension \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) E : H900 strip, in tension \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) E : H900 strip, in compression \|\| longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) E : H900 strip, in compression \|\| transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) E : H900 strip, in compression \|\| average \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| annealed & aged (condition H900) \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : solid \|\| solution treated \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : solid \|\| condition H900 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) UTS : solid \|\| condition H1150 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) UTS : solid \|\| aged at 315 °C (599 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) UTS : solid \|\| aged at 425 °C (797 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) UTS : solid \|\| aged at 566 °C (1050 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) YS : solid \|\| solution treated \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : solid \|\| condition H900 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) YS : solid \|\| condition H1150 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) YS : solid \|\| aged at 315 °C (599 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) YS : solid \|\| aged at 425 °C (797 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) YS : solid \|\| aged at 566 °C (1050 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) %El : solid \|\| solution treated \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : solid \|\| condition H900 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) %El : solid \|\| condition H1150 \|\| -196 °C to 566 °C (-321 °F to 1051 °F) %El : solid \|\| aged at 315 °C (599 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) %El : solid \|\| aged at 425 °C (797 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) %El : solid \|\| aged at 566 °C (1050 °F) \|\| 480 °C to 620 °C (896 °F to 1148 °F) SR : H900 strip \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h FSN : H900 strip, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 strip, smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 strip, smooth \|\| tested at 427 °C (800 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 strip, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 strip, notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 strip, notched \|\| tested at 427 °C (800 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H900 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2.2x10⁴ cycles to 2x10⁷ cycles FSN : H1050 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 3.1x10⁴ cycles to 2x10⁷ cycles FSN : H1150 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2.6x10⁴ cycles to 2x10⁷ cycles CRS : 0.2% plastic strain, H900 strip \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h RHO* : solid \|\| annealed \|\| room temperature value RHO* : solid \|\| H900 \|\| room temperature value SIGMA: solid \|\| annealed \|\| room temperature value SIGMA: solid \|\| H900 \|\| room temperature value
Custom 455 (UNS S45500) (ASTM A313/A564/A693/A705/XM-16) (AMS 5578/5647/5860) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) DLL : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) MTE : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) CTE : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) E : bar, in tension \|\| aged, longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) E : bar, in compression \|\| aged, longitudinal \|\| 20 °C to 427 °C (68 °F to 800 °F) G* : aged \|\| room temperature value v* : aged \|\| room temperature value K* : aged \|\| room temperature value TC : solid \|\| annealed & aged \|\| 20 °C to 510 °C (68 °F to 950 °F) UTS : solid \|\| H900 \|\| -184 °C to 425 °C (-299 °F to 797 °F) UTS : solid \|\| H950 \|\| -184 °C to 538 °C (-299 °F to 1000 °F) UTS : solid \|\| H1000 \|\| -184 °C to 538 °C (-299 °F to 1000 °F) YS : solid \|\| H900 \|\| 20 °C to 425 °C (68 °F to 797 °F) YS : solid \|\| H950 \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| H1000 \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| H900 \|\| -184 °C to 425 °C (-299 °F to 797 °F) %El : solid \|\| H950 \|\| -184 °C to 538 °C (-299 °F to 1000 °F) %El : solid \|\| H1000 \|\| -184 °C to 538 °C (-299 °F to 1000 °F) SR : tempered at 482 °C (900 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : tempered at 510 °C (950 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : tempered at 510 °C (950 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1,000 h SR : tempered at 510 °C (950 °F) \|\| Master curve (LMP) \|\| 426 °C to 483 °C (799 °F to 901 °F) FSN : H900 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁵ cycles to 6.7x10⁷ cycles FSN : H950 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁵ cycles to 7.2x10⁷ cycles FSN : H1000 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2x10⁵ cycles to 7.2x10⁷ cycles FSN : H1050 rod \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2.2x10⁵ cycles to 7.4x10⁷ cycles RHO : solid \|\| annealed & aged at 500 °C (932 °F) \|\| 20 °C to 454 °C (68 °F to 849 °F) SIGMA : solid \|\| annealed & aged at 500 °C (932 °F) \|\| 20 °C to 454 °C (68 °F to 849 °F)
Custom 465 (UNS S46500) (ASTM A564/A693/F899) (AMS 5936)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| H900 \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| H1000 \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| H1100 \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| H900 \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| H1000 \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| H1100 \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| H900 \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| H1000 \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| H1100 \|\| 20 °C to 600 °C (68 °F to 1112 °F) E* : solid \|\| H1000 \|\| room temperature value E* : solid \|\| H1100 \|\| room temperature value TC : solid \|\| annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| H900 \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| H1000 \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| H1050 \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : solid \|\| H1000 \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solid \|\| H1000 \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| H1000 \|\| 20 °C to 427 °C (68 °F to 800 °F) FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : H950 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : H1000 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : H1100 \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁷ cycles RHO* : solid \|\| annealed \|\| room temperature value RHO* : solid \|\| H900 \|\| room temperature value RHO* : solid \|\| H1000 \|\| room temperature value RHO* : solid \|\| H1100 \|\| room temperature value SIGMA: solid \|\| annealed \|\| room temperature value SIGMA: solid \|\| H900 \|\| room temperature value SIGMA: solid \|\| H1000 \|\| room temperature value SIGMA: solid \|\| H1100 \|\| room temperature value
JETHETE M-152 (Moly Ascoloy or FV566) (UNS S64152) (WNr 1.4933/1.4938/1.4939) (ISO/EN/DIN X12CrNiMoV12-3) (AFNOR Z12CNDV12)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : after 90,000 h of operation \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : after 90,000 h of operation \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.58 mm/mm strain SSC : after 90,000 h of operation \|\| tested at 350 °C (662 °F), 0.01/s \|\| 0 to 0.3 mm/mm strain SSC : after 90,000 h of operation \|\| tested at 500 °C (932 °F), 0.01/s \|\| 0 to 0.21 mm/mm strain SSC : after 90,000 h of operation \|\| tested at 600 °C (1112 °F), 0.01/s \|\| 0 to 0.13 mm/mm strain UTS : annealed, quenched & tempered \|\| 538 °C to 650 °C (1000 °F to 1202 °F) UTS : after 90,000 h of operation \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : annealed, quenched & tempered \|\| 538 °C to 650 °C (1000 °F to 1202 °F) YS : after 90,000 h of operation \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : annealed, quenched & tempered \|\| 538 °C to 650 °C (1000 °F to 1202 °F) %El : after 90,000 h of operation \|\| 20 °C to 600 °C (68 °F to 1112 °F) SR : hardened \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : hardened \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : hardened \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : hardened \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) FSN : after 90,000 h of operation \|\| tested at 400 °C (752 °F), R = -1, axial, maximum stress \|\| 2 cycles to 100 cycles FSN : after 90,000 h of operation \|\| tested at 500 °C (932 °F), R = -1, axial, maximum stress \|\| 2 cycles to 100 cycles FSN : after 90,000 h of operation \|\| tested at 600 °C (1112 °F), R = -1, axial, maximum stress \|\| 2 cycles to 463 cycles
Stainless W (UNS S17600) (ASTM A564/A693/A705) (AISI 635) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 500 °C (32 °F to 932 °F) DLL : solid \|\| annealed \|\| 0 °C to 500 °C (32 °F to 932 °F) MTE : solid \|\| annealed \|\| 0 °C to 500 °C (32 °F to 932 °F) CTE : solid \|\| annealed \|\| 0 °C to 500 °C (32 °F to 932 °F) E : solid \|\| annealed & air cooled \|\| 20 °C to 371 °C (68 °F to 700 °F) E : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) E : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) G : solid \|\| annealed & air cooled \|\| 20 °C to 371 °C (68 °F to 700 °F) G : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) G : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) v : solid \|\| annealed & air cooled \|\| 20 °C to 371 °C (68 °F to 700 °F) v : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) v : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) K : solid \|\| annealed & air cooled \|\| 20 °C to 371 °C (68 °F to 700 °F) K : solid \|\| tempered at 649 °C (1200 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) K : solid \|\| tempered at 538 °C (1000 °F) \|\| 20 °C to 371 °C (68 °F to 700 °F) TC : solid \|\| annealed \|\| 20 °C to 399 °C (68 °F to 750 °F) TC : solid \|\| aged \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F)
182-FM (UNS S18200)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
SCF 19 Max (UNS S21000)	D : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) DLL : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) MTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) CTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
NAS H840	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : 0.4 mm (0.0157 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : 0.4 mm (0.0157 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : 0.4 mm (0.0157 inch) cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
NAS NM15M	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value YS : annealed sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value %El : annealed sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
NAS NM17	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Datalloy 2 ESR	D* : solid \|\| room temperature value E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value UTS* : standard strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value UTS* : standard strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value UTS* : standard strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value UTS* : high strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value UTS* : high strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value UTS* : high strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value YS* : standard strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value YS* : standard strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value YS* : standard strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value YS* : high strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value YS* : high strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value YS* : high strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value %El* : standard strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value %El* : standard strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value %El* : standard strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value %El* : high strength \|\| less than 178 mm (7 inch) diameter \|\| room temperature value %El* : high strength \|\| 178 mm to 241 mm (7 inch to 9.5 inch) diameter \|\| room temperature value %El* : high strength \|\| greater than 241 mm (9.5 inch) diameter \|\| room temperature value FSN : 724 MPa (105 ksi) yield \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4x10⁴ cycles to 1x10⁸ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Staballoy AG17	D* : solid \|\| room temperature value UTS* : Staballoy AG17 HS, high strength version of alloy \|\| less than 175 mm (6.875 inch) \|\| room temperature value YS* : Staballoy AG17 HS, high strength version of alloy \|\| less than 175 mm (6.875 inch) \|\| room temperature value %El* : Staballoy AG17 HS, high strength version of alloy \|\| less than 175 mm (6.875 inch) \|\| room temperature value FSN : 800 MPa (116 ksi) yield \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.4x10⁵ cycles to 1x10⁸ cycles
15-15HS	D : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) DLL : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) MTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) CTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) FSN : warm-worked \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.7x10⁵ cycles to 1x10⁸ cycles
15-15LC (UNS S21300)	D : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) DLL : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) MTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) CTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) FSN : warm-worked \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.1x10⁴ cycles to 1x10⁷ cycles NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F)

Nitronic 19D	D : solid \|\| 20 °C to 657 °C (68 °F to 1214 °F) DLL : solid \|\| 20 °C to 657 °C (68 °F to 1214 °F) MTE : solid \|\| 20 °C to 657 °C (68 °F to 1214 °F) CTE : solid \|\| 20 °C to 657 °C (68 °F to 1214 °F) SSC : 8.33x10^-⁴/s, cold-rolled, annealed \|\| tested at 20 °C (68 °F) \|\| 0 to 0.19 mm/mm strain UTS : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| longitudinal \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) UTS : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| transverse \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) UTS* : effect of cold work on RT value \|\| 0% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 4% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 9.8% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 15.1% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20.7% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40.7% cold work \|\| room temperature value UTS* : effect of cold work on RT value \|\| 57.8% cold work \|\| room temperature value YS : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| longitudinal \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) YS : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| transverse \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) YS* : effect of cold work on RT value \|\| 0% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 4% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 9.8% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 15.1% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 20.7% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 40.7% cold work \|\| room temperature value YS* : effect of cold work on RT value \|\| 57.8% cold work \|\| room temperature value %El : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| longitudinal \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) %El : cold-rolled, annealed 22.2 mm (0.875 inch) plate \|\| transverse \|\| 871 °C to 1093 °C (1600 °F to 2000 °F) %El* : effect of cold work on RT value \|\| 0% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 4% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 9.8% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 15.1% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 20.7% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 40.7% cold work \|\| room temperature value %El* : effect of cold work on RT value \|\| 57.8% cold work \|\| room temperature value SR : cold-rolled, annealed \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1,000 h FEN : cold-rolled, annealed plate \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain amplitude \|\| 1.45x10³ cycles to 1.26x10⁵ cycles FEN : cold-rolled, annealed plate \|\| tested at 982 °C (1800 °F), R = -1, axial, total strain amplitude \|\| 1.79x10³ cycles to 3.75x10⁴ cycles FSN : cold-rolled, annealed 0.94 mm (0.037 inch) sheet \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1.4x10⁵ cycles to 1x10⁶ cycles
Nitronic 30 (UNS S20400)	D : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) DLL : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) MTE : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) CTE : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) UTS : annealed \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : annealed \|\| plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : effect of cold working at RT \|\| 0% cold work \|\| room temperature value UTS* : effect of cold working at RT \|\| 10% cold work \|\| room temperature value UTS* : effect of cold working at RT \|\| 20% cold work \|\| room temperature value UTS* : effect of cold working at RT \|\| 30% cold work \|\| room temperature value UTS* : effect of cold working at RT \|\| 40% cold work \|\| room temperature value UTS* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), longitudinal \|\| room temperature value UTS* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), transverse \|\| room temperature value UTS* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), longitudinal \|\| room temperature value UTS* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), transverse \|\| room temperature value YS : annealed \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : annealed \|\| plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : effect of cold working at RT \|\| 0% cold work \|\| room temperature value YS* : effect of cold working at RT \|\| 10% cold work \|\| room temperature value YS* : effect of cold working at RT \|\| 20% cold work \|\| room temperature value YS* : effect of cold working at RT \|\| 30% cold work \|\| room temperature value YS* : effect of cold working at RT \|\| 40% cold work \|\| room temperature value YS* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), longitudinal \|\| room temperature value YS* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), transverse \|\| room temperature value YS* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), longitudinal \|\| room temperature value YS* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), transverse \|\| room temperature value %El : annealed \|\| sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : annealed \|\| plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : effect of cold working at RT \|\| 0% cold work \|\| room temperature value %El* : effect of cold working at RT \|\| 10% cold work \|\| room temperature value %El* : effect of cold working at RT \|\| 20% cold work \|\| room temperature value %El* : effect of cold working at RT \|\| 30% cold work \|\| room temperature value %El* : effect of cold working at RT \|\| 40% cold work \|\| room temperature value %El* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), longitudinal \|\| room temperature value %El* : quarter hard plate at RT \|\| 4.76 mm (0.1875 inch), transverse \|\| room temperature value %El* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), longitudinal \|\| room temperature value %El* : quarter hard plate at RT \|\| 6.35 mm (0.25 inch), transverse \|\| room temperature value SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h FSN : hot-rolled & annealed plate \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed sheet \|\| tested at 20 °C (68 °F), R = 0.5, axial, maximum stress \|\| 8x10⁴ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed sheet \|\| tested at 20 °C (68 °F), R = -1, reverse bending, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : notched hot-rolled & annealed plate \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles
Nitronic 32 (UNS S24100) (ASTM XM-28)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value UTS : mill annealed \|\| 25.4 mm (1 inch) bar \|\| 20 °C to 761 °C (68 °F to 1402 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : mill annealed \|\| 25.4 mm (1 inch) bar \|\| 20 °C to 761 °C (68 °F to 1402 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : mill annealed \|\| 25.4 mm (1 inch) bar \|\| 20 °C to 761 °C (68 °F to 1402 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RPB : annealed \|\| tested at 20 °C (68 °F) RPB : cold-drawn 70% \|\| tested at 20 °C (68 °F) AP : annealed \|\| tested at 20 °C (68 °F) AP : cold-drawn 70% \|\| tested at 20 °C (68 °F) BH : annealed \|\| tested at 20 °C (68 °F) BH : cold-drawn 70% \|\| tested at 20 °C (68 °F) HB : annealed \|\| tested at 20 °C (68 °F) HB : cold-drawn 70% \|\| tested at 20 °C (68 °F)
Nitronic 33 (UNS S24000) (ASTM XM-29) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -185 °C to 982 °C (-301 °F to 1800 °F) DLL : solid \|\| -185 °C to 982 °C (-301 °F to 1800 °F) MTE : solid \|\| -185 °C to 982 °C (-301 °F to 1800 °F) CTE : solid \|\| -185 °C to 982 °C (-301 °F to 1800 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : annealed \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : 60% cold-rolled sheet \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : annealed \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : 60% cold rolled sheet \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : annealed \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : 60% cold rolled sheet \|\| -196 °C to 25 °C (-321 °F to 77 °F) FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = -1, bending, K_t = 3, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10⁵ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = 0.5, axial, maximum stress \|\| 1.5x10⁵ cycles to 1x10⁷ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), R = 0.5, axial, K_t = 3, maximum stress \|\| 1x10⁵ cycles to 5x10⁶ cycles NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SIGMA : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
Nitronic 40 (UNS S21900/S21904) (ASTM A276/A314/A412/A429/A473/A580) (AMS 5561) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : annealed \|\| in tension, sheet \|\| 20 °C to 482 °C (68 °F to 900 °F) E : annealed \|\| in compression, sheet \|\| 20 °C to 482 °C (68 °F to 900 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C (68 °F) and above \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| -155 °C (-247 °F) and below \|\| -268 °C to -155 °C (-451 °F to -247 °F) UTS : annealed \|\| sheet, strip & slab \|\| -253 °C to 704 °C (-424 °F to 1299 °F) UTS : cold reduced \|\| 10% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : cold reduced \|\| 25% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : cold reduced \|\| 60% cold reduction \|\| -196 °C to 316 °C (-321 °F to 600 °F) UTS : hot-rolled, rack cooled \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : hot-rolled, rack cooled \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : hot-rolled, rack cooled \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) UTS : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : annealed \|\| sheet, strip & slab \|\| -253 °C to 704 °C (-424 °F to 1299 °F) YS : cold reduced \|\| 10% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : cold reduced \|\| 25% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : cold reduced \|\| 60% cold reduction \|\| 20 °C to 316 °C (68 °F to 600 °F) YS : hot-rolled, rack cooled \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : hot-rolled, rack cooled \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : hot-rolled, rack cooled \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) YS : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YSC : annealed \|\| 0.5 h hold, longitudinal \|\| 20 °C to 482 °C (68 °F to 900 °F) YSC : annealed \|\| 0.5 h hold, transverse \|\| 20 °C to 482 °C (68 °F to 900 °F) %El : annealed \|\| sheet, strip & slab \|\| -253 °C to 704 °C (-424 °F to 1299 °F) %El : cold reduced \|\| 10% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : cold reduced \|\| 25% cold reduction \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : cold reduced \|\| 60% cold reduction \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : hot-rolled, rack cooled \|\| air melted \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : hot-rolled, rack cooled \|\| ESR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : hot-rolled, rack cooled \|\| VAR processed \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| -196 °C to 20 °C (-321 °F to 68 °F) %El : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| -196 °C to 538 °C (-321 °F to 1000 °F) SR : annealed bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : annealed bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1,000 h SR : annealed bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : annealed bar \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) SR : annealed sheet \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : annealed sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : annealed sheet \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) FSN : annealed, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : annealed, smooth \|\| tested at 204 °C (400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : annealed, smooth \|\| tested at 371 °C (700 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 5x10⁶ cycles FSN : annealed, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : annealed, notched \|\| tested at 204 °C (400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : annealed, notched \|\| tested at 371 °C (700 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, annealed \|\| tested at 260 °C (500 °F) \|\| 0.2 h to 3,000 h CRS : 0.2% plastic strain, annealed \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.2% plastic strain, annealed \|\| tested at 482 °C (900 °F) \|\| 0.1 h to 720 h CRS : 0.5% plastic strain, annealed \|\| tested at 260 °C (500 °F) \|\| 0.4 h to 3,300 h CRS : 0.5% plastic strain, annealed \|\| tested at 371 °C (700 °F) \|\| 0.4 h to 900 h CRS : 0.5% plastic strain, annealed \|\| tested at 482 °C (900 °F) \|\| 3 h to 2,100 h CRS : 1% plastic strain, annealed \|\| tested at 260 °C (500 °F) \|\| 2 h to 7,300 h CRS : 1% plastic strain, annealed \|\| tested at 371 °C (700 °F) \|\| 2 h to 1,500 h IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), plastic strain, annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, annealed \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, annealed \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, annealed \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 482 °C (900 °F), plastic strain, annealed \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value RPB : annealed \|\| tested at 20 °C (68 °F) RPB : cold-reduced 15% \|\| tested at 20 °C (68 °F) RPB : cold-reduced 35% \|\| tested at 20 °C (68 °F) RPB : cold-reduced 60% \|\| tested at 20 °C (68 °F) RPB : hot-rolled and pickled \|\| tested at 20 °C (68 °F) AP : annealed \|\| tested at 20 °C (68 °F) AP : cold-reduced 15% \|\| tested at 20 °C (68 °F) AP : cold-reduced 35% \|\| tested at 20 °C (68 °F) AP : cold-reduced 60% \|\| tested at 20 °C (68 °F) AP : hot-rolled and pickled \|\| tested at 20 °C (68 °F) BH : annealed \|\| tested at 20 °C (68 °F) BH : cold-reduced 15% \|\| tested at 20 °C (68 °F) BH : cold-reduced 35% \|\| tested at 20 °C (68 °F) BH : cold-reduced 60% \|\| tested at 20 °C (68 °F) BH : hot-rolled and pickled \|\| tested at 20 °C (68 °F) HB : annealed \|\| tested at 20 °C (68 °F) HB : cold-reduced 15% \|\| tested at 20 °C (68 °F) HB : cold-reduced 35% \|\| tested at 20 °C (68 °F) HB : cold-reduced 60% \|\| tested at 20 °C (68 °F) HB : hot-rolled and pickled \|\| tested at 20 °C (68 °F)
Nitronic 50 (UNS S20910) (WNr 1.3964) (ISO/EN/DIN X2CrNiMnMoN25-18-6-5/X3CrNiMnMoNbN23-17-5-3) (ASTM A240/A276/A412/A479/F1314/X580/XM-19) (AMS 5764/5861) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) DLL : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) MTE : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) CTE : solid \|\| -196 °C to 871 °C (-321 °F to 1600 °F) E : solid \|\| 20 °C to 371 °C (68 °F to 700 °F) G : solid \|\| 20 °C to 371 °C (68 °F to 700 °F) v : solid \|\| 20 °C to 371 °C (68 °F to 700 °F) K : solid \|\| 20 °C to 371 °C (68 °F to 700 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSCC : 0.001/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.41 mm/mm strain SSCC : 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.001/s \|\| tested at 127 °C (260 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.001/s \|\| tested at 227 °C (440 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.001/s \|\| tested at 327 °C (620 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.001/s \|\| tested at 427 °C (800 °F) \|\| 0 to 0.73 mm/mm strain SSCC : 0.001/s \|\| tested at 527 °C (980 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.001/s \|\| tested at 627 °C (1160 °F) \|\| 0 to 0.78 mm/mm strain SSCC : 0.001/s \|\| tested at 727 °C (1340 °F) \|\| 0 to 0.72 mm/mm strain SSCC : 0.1/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.61 mm/mm strain SSCC : 3500/s \|\| tested at -196.1 °C (-321.1 °F) \|\| 0 to 0.3 mm/mm strain SSCC : 3500/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.34 mm/mm strain SSCC : 3500/s \|\| tested at 227 °C (440 °F) \|\| 0 to 0.34 mm/mm strain SSCC : 3500/s \|\| tested at 327 °C (620 °F) \|\| 0 to 0.33 mm/mm strain SSCC : 3500/s \|\| tested at 527 °C (980 °F) \|\| 0 to 0.34 mm/mm strain SSCC : 3500/s \|\| tested at 627 °C (1160 °F) \|\| 0 to 0.34 mm/mm strain SSCC : 3500/s \|\| tested at 727 °C (1340 °F) \|\| 0 to 0.34 mm/mm strain UTS : annealed at 1121 °C (2050 °F) \|\| -196 °C to 816 °C (-321 °F to 1500 °F) UTS : annealed at 1066 °C (1950 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : hot-rolled, unannealed high-strength bars \|\| -196 °C to 593 °C (-321 °F to 1100 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 75% cold worked \|\| room temperature value YS : annealed at 1121 °C (2050 °F) \|\| -196 °C to 816 °C (-321 °F to 1500 °F) YS : annealed at 1066 °C (1950 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled, unannealed high-strength bars \|\| -196 °C to 593 °C (-321 °F to 1100 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 75% cold worked \|\| room temperature value %El : annealed at 1121 °C (2050 °F) \|\| -196 °C to 816 °C (-321 °F to 1500 °F) %El : annealed at 1066 °C (1950 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : hot-rolled, unannealed high-strength bars \|\| -196 °C to 593 °C (-321 °F to 1100 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 15% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 45% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 75% cold worked \|\| room temperature value SR : annealed at 1066 °C (1950 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1066 °C (1950 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1066 °C (1950 °F) \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1066 °C (1950 °F) \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1066 °C (1950 °F) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1066 °C (1950 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) SR : annealed at 1121 °C (2050 °F) \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1121 °C (2050 °F) \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1121 °C (2050 °F) \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1121 °C (2050 °F) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h SR : annealed at 1121 °C (2050 °F) \|\| Master curve (LMP) \|\| 593 °C to 816 °C (1099 °F to 1501 °F) SR : hot-rolled, unannealed high-strength bars \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : hot-rolled, unannealed high-strength bars \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : hot-rolled, unannealed high-strength bars \|\| Master curve (LMP) \|\| 537 °C to 594 °C (998 °F to 1101 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value RPB : wire, annealed \|\| tested at 20 °C (68 °F) RPB : wire, cold-drawn 27% \|\| tested at 20 °C (68 °F) RPB : wire, cold-drawn 56% \|\| tested at 20 °C (68 °F) RPB : wire, cold-drawn 75% \|\| tested at 20 °C (68 °F) AP : wire, annealed \|\| tested at 20 °C (68 °F) AP : wire, cold-drawn 27% \|\| tested at 20 °C (68 °F) AP : wire, cold-drawn 56% \|\| tested at 20 °C (68 °F) AP : wire, cold-drawn 75% \|\| tested at 20 °C (68 °F) BH : wire, annealed \|\| tested at 20 °C (68 °F) BH : wire, cold-drawn 27% \|\| tested at 20 °C (68 °F) BH : wire, cold-drawn 56% \|\| tested at 20 °C (68 °F) BH : wire, cold-drawn 75% \|\| tested at 20 °C (68 °F) HB : wire, annealed \|\| tested at 20 °C (68 °F) HB : wire, cold-drawn 27% \|\| tested at 20 °C (68 °F) HB : wire, cold-drawn 56% \|\| tested at 20 °C (68 °F) HB : wire, cold-drawn 75% \|\| tested at 20 °C (68 °F)
Nitronic 60 (UNS S21800) (ASTM A193/A276/A314/A351/A479/A580/A743) (AMS 5848) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| -253 °C to 20 °C (-424 °F to 68 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : bar \|\| annealed \|\| -196 °C to 871 °C (-321 °F to 1600 °F) UTS : bar \|\| cold swaged 54% \|\| -196 °C to 650 °C (-321 °F to 1202 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value YS : bar \|\| annealed \|\| -196 °C to 871 °C (-321 °F to 1600 °F) YS : bar \|\| cold swaged 54% \|\| -196 °C to 650 °C (-321 °F to 1202 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value %El : bar \|\| annealed \|\| -196 °C to 871 °C (-321 °F to 1600 °F) %El : bar \|\| cold swaged 54% \|\| -196 °C to 650 °C (-321 °F to 1202 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 70% cold worked \|\| room temperature value SR : annealed bar \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : annealed bar \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : annealed bar \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1,000 h SR : annealed bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : annealed bar \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F)

SINOXX 3816 (WNr 1.3816) (ISO/EN/DIN X8CrMnN18-18)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E* : solid \|\| room temperature value
SINOXX 4120 (WNr 1.4120) (ISO/EN/DIN X20CrMo13)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SINOXX 4580 (WNr 1.4580) (ISO/EN/DIN X2CrNiMoN17-13-5/X6CrNiMoNb17-12-2) (JIS SUS316) (AISI 316/316Cb) (AFNOR Z6CNDNb17-12/Z6CNDNb19-13) (GB & GB/T 0Cr17Ni12Mo2) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TC : liquid \|\| 1427 °C to 2627 °C (2600 °F to 4760 °F) TD : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) TD : liquid \|\| 1427 °C to 1658 °C (2600 °F to 3016 °F) SH : solid \|\| -269 °C to 1427 °C (-452 °F to 2600 °F) SH : liquid \|\| 1427 °C to 2727 °C (2600 °F to 4940 °F) YS : solid \|\| solution annealed \|\| 20 °C to 400 °C (68 °F to 752 °F) NE : solid \|\| polished \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| polished & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : solid \|\| rough & oxidized \|\| 127 °C to 827 °C (260 °F to 1520 °F) NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) Vis : liquid \|\| 1427 °C to 2027 °C (2600 °F to 3680 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SINOXX 4747 (WNr 1.4747) (ISO/EN/DIN X80CrNiSi20)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
SINOXX 4748 (WNr 1.4748) (ISO/EN/DIN X85CrMoV18-2)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : hardened & tempered \|\| 20 °C to 750 °C (68 °F to 1382 °F) YS : hardened & tempered \|\| 20 °C to 750 °C (68 °F to 1382 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SINOXX 4871 (UNS S63008) (WNr 1.4871) (ISO/EN/DIN X53CrMnNiN21-9) (JIS SUH35) (AISI EV8) (SAE EV8) (AFNOR Z52CMN21-09) (GB & GB/T 5Cr21Mn9Ni4N)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : hardened & tempered \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : hardened & tempered \|\| 20 °C to 800 °C (68 °F to 1472 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SINOXX 4875 (WNr 1.4875) (ISO/EN/DIN X55CrMnNiN20-8) (AISI EV12) (SAE EV12)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : hardened & tempered \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : hardened & tempered \|\| 20 °C to 800 °C (68 °F to 1472 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SINOXX 4913 (WNr 1.4913) (ISO/EN/DIN X19CrMoNbVN11-1)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value YS : quenched & tempered \|\| 20 °C to 600 °C (68 °F to 1112 °F) SR : quenched & tempered \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : quenched & tempered \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : quenched & tempered \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : quenched & tempered \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 2x10⁵ h SR : quenched & tempered \|\| Master curve (LMP) \|\| 450 °C to 601 °C (842 °F to 1114 °F) CRS : 1% plastic strain \|\| tested at 450 °C (842 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain \|\| tested at 500 °C (932 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain \|\| Master curve (LMP) \|\| 450 °C to 601 °C (842 °F to 1114 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value

SCF 260 alloy	D : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) DLL : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) MTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) CTE : solid \|\| 20 °C to 550 °C (68 °F to 1022 °F) E* : solid \|\| room temperature value TC : solid \|\| as-forged, warm-worked condition \|\| 20 °C to 400 °C (68 °F to 752 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
21 Cr - 6 Ni - 9 Mn (wt %) (UNS S21904) (ISO/EN/DIN X11CrNiMnN19-8-6) (ASTM A182/A269/A276/A312/A314/A412/A473/A479/A580/A666/A813/A814/A965) (AMS 5561/5562/5595/5656) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| -196 °C to 704 °C (-321 °F to 1299 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS : annealed \|\| -196 °C to 704 °C (-321 °F to 1299 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El : annealed \|\| -196 °C to 704 °C (-321 °F to 1299 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : annealed \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
18-18 Plus (UNS S28200)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F)
Type 204-Cu	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS : annealed & quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed & quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed & quenched \|\| 20 °C to 871 °C (68 °F to 1600 °F)
Pyrowear 53 (UNS K71040) (AMS 6308) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : hardened & tempered \|\| -54 °C to 177 °C (-65 °F to 350 °F) YS : hardened & tempered \|\| -54 °C to 177 °C (-65 °F to 350 °F) %El : hardened & tempered \|\| -54 °C to 177 °C (-65 °F to 350 °F) FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.1, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress \|\| 800 cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress \|\| 8x10³ cycles to 1x10⁷ cycles FSN : single tooth bending fatigue \|\| tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress \|\| 635 cycles to 1x10⁶ cycles
Pyrowear 675 (AMS 5930)	D : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) D : solid \|\| hardened & tempered \|\| 20 °C to 700 °C (68 °F to 1292 °F) D : solid \|\| average \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| average \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| average \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| hardened & tempered \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| average \|\| 20 °C to 650 °C (68 °F to 1202 °F)
Greek Ascoloy (UNS S41800) (ASTM A565) (AISI 615) (SAE J467) (AMS 5508/5616/5817)	D : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) DLL : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) MTE : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) CTE : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) E : solid \|\| 20 °C to 593 °C (68 °F to 1099 °F) SH* : solid \|\| room temperature value UTS : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 566 °C (1050 °F) \|\| 425 °C to 760 °C (797 °F to 1400 °F) UTS : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 649 °C (1200 °F) \|\| 20 °C to 593 °C (68 °F to 1099 °F) UTS : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 566 °C (1050 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 649 °C (1200 °F) \|\| 425 °C to 650 °C (797 °F to 1202 °F) UTS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 593 °C (1100 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value UTS* : effect of tempering temperature on RT value \|\| tempered at 704 °C (1300 °F) \|\| room temperature value UTS* : annealed \|\| room temperature value YS : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 566 °C (1050 °F) \|\| 425 °C to 760 °C (797 °F to 1400 °F) YS : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 649 °C (1200 °F) \|\| 20 °C to 593 °C (68 °F to 1099 °F) YS : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 566 °C (1050 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 649 °C (1200 °F) \|\| 425 °C to 650 °C (797 °F to 1202 °F) YS* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 593 °C (1100 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value YS* : effect of tempering temperature on RT value \|\| tempered at 704 °C (1300 °F) \|\| room temperature value YS* : annealed \|\| room temperature value %El : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 566 °C (1050 °F) \|\| 425 °C to 760 °C (797 °F to 1400 °F) %El : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 649 °C (1200 °F) \|\| 20 °C to 593 °C (68 °F to 1099 °F) %El : hardened & tempered \|\| hardened at 954 °C (1750 °F) & tempered at 566 °C (1050 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : hardened & tempered \|\| hardened at 982 °C (1800 °F) & tempered at 649 °C (1200 °F) \|\| 425 °C to 650 °C (797 °F to 1202 °F) %El* : effect of tempering temperature on RT value \|\| tempered at 482 °C (900 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 538 °C (1000 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 593 °C (1100 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 649 °C (1200 °F) \|\| room temperature value %El* : effect of tempering temperature on RT value \|\| tempered at 704 °C (1300 °F) \|\| room temperature value %El* : annealed \|\| room temperature value SR : treated at 954 °C (1750 °F) & OQ, tempered at 566 °C (1050 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 566 °C (1050 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 566 °C (1050 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 566 °C (1050 °F) \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) SR : treated at 954 °C (1750 °F) & OQ, tempered at 649 °C (1200 °F) \|\| tested at 482 °C (900 °F) \|\| 60 h to 2,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 649 °C (1200 °F) \|\| tested at 538 °C (1000 °F) \|\| 60 h to 2,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 649 °C (1200 °F) \|\| tested at 593 °C (1100 °F) \|\| 60 h to 2,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 649 °C (1200 °F) \|\| tested at 649 °C (1200 °F) \|\| 60 h to 2,000 h SR : treated at 954 °C (1750 °F) & OQ, tempered at 649 °C (1200 °F) \|\| Master curve (LMP) \|\| 482 °C to 650 °C (899 °F to 1202 °F) SR : treated at 982 °C (1800 °F) & AC, tempered at 566 °C (1050 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 2,000 h SR : treated at 982 °C (1800 °F) & AC, tempered at 566 °C (1050 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 2,000 h SR : treated at 982 °C (1800 °F) & AC, tempered at 566 °C (1050 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 2,000 h SR : treated at 982 °C (1800 °F) & AC, tempered at 566 °C (1050 °F) \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) SR : treated at 982 °C (1800 °F) & OQ, tempered at 682 °C (1260 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & OQ, tempered at 682 °C (1260 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & OQ, tempered at 682 °C (1260 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & OQ, tempered at 682 °C (1260 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & OQ, tempered at 682 °C (1260 °F) \|\| Master curve (LMP) \|\| 482 °C to 650 °C (899 °F to 1202 °F) SR : treated at 982 °C (1800 °F) & AC, tempered at 682 °C (1260 °F) \|\| tested at 482 °C (900 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & AC, tempered at 682 °C (1260 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & AC, tempered at 682 °C (1260 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & AC, tempered at 682 °C (1260 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : treated at 982 °C (1800 °F) & AC, tempered at 682 °C (1260 °F) \|\| Master curve (LMP) \|\| 482 °C to 650 °C (899 °F to 1202 °F) RHO : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) SIGMA : solid \|\| 20 °C to 482 °C (68 °F to 900 °F)
RR2450	E* : HIPed \|\| in compression \|\| room temperature value SSCC : HIPed \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.17 mm/mm strain YSC* : HIPed \|\| room temperature value
S04 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	SSC : as-received \|\| tested at -180 °C (-292 °F), 0.00167/s \|\| 0 to 0.8 mm/mm strain SSC : after 10 cycles to 1.20 GPa (174 ksi) \|\| tested at -180 °C (-292 °F), 0.00167/s \|\| 0 to 0.62 mm/mm strain SSC : after 10 cycles to 1.27 GPa (184 ksi) \|\| tested at -180 °C (-292 °F), 0.00167/s \|\| 0 to 0.54 mm/mm strain
SAF 2707 HD (UNS S32707) (WNr 1.4658) (ASTM A789/A790)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : solution annealed \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solution annealed \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
SAF 3207 HD (UNS S33207) (ASTM A789/A790)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) UTS : solution annealed \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solution annealed \|\| 20 °C to 300 °C (68 °F to 572 °F) FSN : welded \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value

AISI 613	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F)
16-25-6 (AISI 650) (AISI 650) (AMS 5727B) (some datasets are for temperatures below 20 °C)	D : solid \|\| -16 °C to 1382 °C (3 °F to 2519 °F) DLL : solid \|\| -16 °C to 1382 °C (3 °F to 2519 °F) MTE : solid \|\| -16 °C to 1382 °C (3 °F to 2519 °F) CTE : solid \|\| -16 °C to 1382 °C (3 °F to 2519 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : solid \|\| cold worked 20% & tempered at 677 °C (1250 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS : solid \|\| quenched from 1177 °C (2150 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solid \|\| cold worked 20% & tempered at 677 °C (1250 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solid \|\| quenched from 1177 °C (2150 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solid \|\| cold worked 20% & tempered at 677 °C (1250 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : solid \|\| quenched from 1177 °C (2150 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) SR : solution quenched \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : solution quenched \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : solution quenched \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : solution quenched \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : solution quenched \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : solution quenched \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : solution quenched \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) SR : worked 15% \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : worked 15% \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : worked 15% \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁴ h SR : worked 15% \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F)
17-14 CuMo (AISI 653) (AISI 653)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) UTS : solid \|\| tempered at 732 °C (1350 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS : solid \|\| tempered at 1010 °C (1850 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solid \|\| tempered at 732 °C (1350 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solid \|\| tempered at 1010 °C (1850 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : solid \|\| tempered at 732 °C (1350 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : solid \|\| tempered at 1010 °C (1850 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) SR : held at 1121 °C (2050 °F) for 5 min & AC \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : held at 1121 °C (2050 °F) for 5 min & AC \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁴ h SR : held at 1121 °C (2050 °F) for 5 min & AC \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h SR : held at 1121 °C (2050 °F) for 5 min & AC \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) SR : held at 1121 °C (2050 °F) for 0.5 h & WQ \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h
V-57 (AISI 663) (AISI 663)	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : heat-treated at 982 °C (1800 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : heat-treated at 982 °C (1800 °F) \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) SR : heat-treated at 1010 °C (1850 °F) \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : heat-treated at 1010 °C (1850 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : heat-treated at 1010 °C (1850 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : heat-treated at 1010 °C (1850 °F) \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : heat-treated at 1010 °C (1850 °F) \|\| Master curve (LMP) \|\| 537 °C to 705 °C (998 °F to 1301 °F) CRS : 0.2% plastic strain, heat-treated at 982 °C (1800 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 100 h CRS : 0.2% plastic strain, heat-treated at 982 °C (1800 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 100 h CRS : 0.2% plastic strain, heat-treated at 982 °C (1800 °F) \|\| tested at 677 °C (1250 °F) \|\| 10 h to 100 h CRS : 0.2% plastic strain, heat-treated at 982 °C (1800 °F) \|\| Master curve (LMP) \|\| 593 °C to 678 °C (1099 °F to 1252 °F)
W545 (AISI 665) (UNS S66545) (ASTM A453) (AISI 665) (SAE J467) (AMS 5543/5741)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) G : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) v : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) K : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) TC : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : solid \|\| 2.7% Ti 330 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| 3.3% Ti 400 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 2.7% Ti 330 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 3.3% Ti 400 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| 2.7% Ti 330 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| 3.3% Ti 400 HB \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : unnotched \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : unnotched \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : unnotched \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : unnotched \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : unnotched \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : unnotched \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) SR : notched \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : notched \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1,000 h SR : notched \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : notched \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : notched \|\| Master curve (LMP) \|\| 537 °C to 705 °C (998 °F to 1301 °F)
Ni-SPAN C alloy 902 (Low expansion 43-PH) (UNS N09902) (AMS 5221C/5223C/5225C) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 260 °C (-460 °F to 500 °F) DLL : sheet \|\| as hot-rolled \|\| -40 °C to 260 °C (-40 °F to 500 °F) DLL : sheet \|\| 1 h at 1010 °C (1850 °F), WQ \|\| -40 °C to 260 °C (-40 °F to 500 °F) DLL : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 482 °C (900 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) DLL : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 538 °C (1000 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) DLL : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 593 °C (1100 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) DLL : bar \|\| 5 h at 482 °C (900 °F) \|\| -273 °C to 27 °C (-460 °F to 80 °F) DLL : average value \|\| -273 °C to 260 °C (-460 °F to 500 °F) MTE : sheet \|\| as hot-rolled \|\| -40 °C to 260 °C (-40 °F to 500 °F) MTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ \|\| -40 °C to 260 °C (-40 °F to 500 °F) MTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 482 °C (900 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) MTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 538 °C (1000 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) MTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 593 °C (1100 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) MTE : bar \|\| 5 h at 482 °C (900 °F) \|\| -273 °C to 27 °C (-460 °F to 80 °F) MTE : average value \|\| -273 °C to 260 °C (-460 °F to 500 °F) CTE : sheet \|\| as hot-rolled \|\| -40 °C to 260 °C (-40 °F to 500 °F) CTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ \|\| -40 °C to 260 °C (-40 °F to 500 °F) CTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 482 °C (900 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) CTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 538 °C (1000 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) CTE : sheet \|\| 1 h at 1010 °C (1850 °F), WQ, 5 h at 593 °C (1100 °F) \|\| -40 °C to 260 °C (-40 °F to 500 °F) E : bar \|\| 5 h at 649 °C (1200 °F) \|\| -253 °C to 38 °C (-424 °F to 100 °F) E : cold-rolled strip \|\| 5 h at 482 °C (900 °F) \|\| -35 °C to 204 °C (-31 °F to 400 °F) E : cold-rolled strip \|\| 5 h at 538 °C (1000 °F) \|\| -25 °C to 204 °C (-13 °F to 400 °F) E : cold-rolled strip \|\| 5 h at 704 °C (1300 °F) \|\| -35 °C to 204 °C (-31 °F to 400 °F) G : bar \|\| 5 h at 649 °C (1200 °F) \|\| -253 °C to 38 °C (-424 °F to 100 °F) v : bar \|\| 5 h at 649 °C (1200 °F) \|\| -253 °C to 38 °C (-424 °F to 100 °F) K : bar \|\| -253 °C to 38 °C (-424 °F to 100 °F) TC : solid \|\| solution treated & aged \|\| -150 °C to 540 °C (-238 °F to 1004 °F) TD* : solid \|\| solution treated & aged \|\| room temperature value SH* : solid \|\| room temperature value SSC : solution treated & aged \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.17 mm/mm strain SSC : solution treated & aged \|\| tested at -79 °C (-110 °F), 3.3x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : solution treated & aged \|\| tested at -195.6 °C (-320 °F), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : solution treated & aged \|\| tested at -252.7 °C (-422.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.25 mm/mm strain UTS : solid \|\| solution treated & aged \|\| -253 °C to 38 °C (-424 °F to 100 °F) YS : solid \|\| solution treated & aged \|\| -253 °C to 38 °C (-424 °F to 100 °F) %El : solid \|\| solution treated & aged \|\| -253 °C to 38 °C (-424 °F to 100 °F) FSN : solution treated & aged \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : solution treated & aged \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 6x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value RPB : annealed 5 h at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F) AP : annealed 5 h at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F) BH : annealed 5 h at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F) HB : annealed 5 h at 538 °C (1000 °F) \|\| tested at 20 °C (68 °F)

2003 (UNS S32003) (ASTM A240/A270/A480/A789/A790/A928) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -102 °C to 205 °C (-152 °F to 401 °F) DLL : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -102 °C to 205 °C (-152 °F to 401 °F) MTE : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -102 °C to 205 °C (-152 °F to 401 °F) CTE : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -102 °C to 205 °C (-152 °F to 401 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : sheet, strip, plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -90 °C to 260 °C (-130 °F to 500 °F) YS : sheet, strip, plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -90 °C to 260 °C (-130 °F to 500 °F) %El : sheet, strip, plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -90 °C to 260 °C (-130 °F to 500 °F) FSN : annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| tested at 20 °C (68 °F), R = -1, flexure, maximum stress \|\| 3x10³ cycles to 1x10⁷ cycles
2102 (UNS S82001) (ASTM A240/A480/A789/A790) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -110 °C to 400 °C (-166 °F to 752 °F) DLL : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -110 °C to 400 °C (-166 °F to 752 °F) MTE : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -110 °C to 400 °C (-166 °F to 752 °F) CTE : solid \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -110 °C to 400 °C (-166 °F to 752 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| -18 °C to 400 °C (-1 °F to 752 °F) UTS : plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -91 °C to 530 °C (-132 °F to 986 °F) YS : plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -91 °C to 530 °C (-132 °F to 986 °F) %El : plate \|\| annealed between 1010 °C (1850 °F) & 1099 °C (2010 °F) \|\| -91 °C to 530 °C (-132 °F to 986 °F)
2205 (UNS S31803/S32205) (WNr 1.4462) (ISO/EN/DIN X2CrNiMoN22-5-3) (JIS SUS329J3L) (ASTM A240/A276/A479/A955M) (AFNOR Z2CND22-05Az) (GB & GB/T 00Cr22Ni5Mo3N) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| hot-rolled \|\| 20 °C to 700 °C (68 °F to 1292 °F) D : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) D : solid \|\| average \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| hot-rolled \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| average \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| hot-rolled \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| average \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| hot-rolled \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| annealed \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| average \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) G : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) v : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) K : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : fine grain, 0.0167/s \|\| tested at -73 °C (-99 °F), annealed \|\| 0 to 0.224 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at -47 °C (-53 °F), annealed \|\| 0 to 0.223 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at -16 °C (3 °F), annealed \|\| 0 to 0.238 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at 25 °C (77 °F), annealed \|\| 0 to 0.272 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at 50 °C (122 °F), annealed \|\| 0 to 0.233 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at 78 °C (172 °F), annealed \|\| 0 to 0.231 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at 117 °C (243 °F), annealed \|\| 0 to 0.228 mm/mm strain SSC : fine grain, 0.0167/s \|\| tested at 161 °C (322 °F), annealed \|\| 0 to 0.215 mm/mm strain SSC : medium grain, 6.67x10^-⁴/s \|\| tested at 20 °C (68 °F), annealed \|\| 0 to 0.24 mm/mm strain SSC : medium grain, 6.67x10^-⁴/s \|\| tested at 20 °C (68 °F), held at 475 °C (887 °F) 20 h, quenched \|\| 0 to 0.2 mm/mm strain SSC : medium grain, 6.67x10^-⁴/s \|\| tested at 20 °C (68 °F), held at 475 °C (887 °F) 50 h, quenched \|\| 0 to 0.174 mm/mm strain SSC : medium grain, 6.67x10^-⁴/s \|\| tested at 20 °C (68 °F), held at 475 °C (887 °F) 255 h, quenched \|\| 0 to 0.1 mm/mm strain SSCC : 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.82 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.85 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.85 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.76 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.77 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.71 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.73 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.73 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.75 mm/mm strain UTS : rebar \|\| as-rolled \|\| -74 °C to 205 °C (-101 °F to 401 °F) UTS : rebar \|\| annealed \|\| -74 °C to 205 °C (-101 °F to 401 °F) UTS : fine grain sheet \|\| annealed \|\| -78 °C to 162 °C (-109 °F to 323 °F) YS : rebar \|\| as-rolled \|\| -74 °C to 205 °C (-101 °F to 401 °F) YS : rebar \|\| annealed \|\| -74 °C to 205 °C (-101 °F to 401 °F) YS : fine grain sheet \|\| annealed \|\| -78 °C to 162 °C (-109 °F to 323 °F) %El : rebar \|\| as-rolled \|\| -74 °C to 205 °C (-101 °F to 401 °F) %El : rebar \|\| annealed \|\| -74 °C to 205 °C (-101 °F to 401 °F) %El : fine grain sheet \|\| annealed \|\| -78 °C to 162 °C (-109 °F to 323 °F) FSN : in air \|\| tested at 20 °C (68 °F), R = -1, bending, maximum stress \|\| 1x10⁴ cycles to 7x10⁶ cycles FSN : in air \|\| tested at 20 °C (68 °F), R = -1, ultrasonic axial, stress amplitude \|\| 1.3x10⁶ cycles to 1.5x10⁷ cycles FSN : in seawater \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 3x10⁷ cycles FSN : in seawater \|\| tested at 20 °C (68 °F), R = -1, ultrasonic axial, in artificial seawater, stress amplitude \|\| 6.5x10⁵ cycles to 1.2x10⁸ cycles RHO : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| 20 °C to 300 °C (68 °F to 572 °F)
2304 (UNS S32304) (WNr 1.4362) (ISO/EN/DIN X2CrNiN23-4) (ASTM A276/A479/A955M) (AFNOR Z3CN23-04Az)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) G : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) v : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) K : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) TC : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) TD : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : 0.000556/s \|\| tested at 20 °C (68 °F), annealed at 900 °C (1652 °F) \|\| 0 to 0.223 mm/mm strain SSC : 0.000556/s \|\| tested at 20 °C (68 °F), annealed at 950 °C (1742 °F) \|\| 0 to 0.24 mm/mm strain SSC : 0.000556/s \|\| tested at 20 °C (68 °F), annealed at 1000 °C (1832 °F) \|\| 0 to 0.24 mm/mm strain SSC : 0.000556/s \|\| tested at 20 °C (68 °F), annealed at 1050 °C (1922 °F) \|\| 0 to 0.24 mm/mm strain SSC : 0.000556/s \|\| tested at 20 °C (68 °F), annealed at 1100 °C (2012 °F) \|\| 0 to 0.25 mm/mm strain SSC : 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.57 mm/mm strain SSC : 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.56 mm/mm strain SSC : 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.556 mm/mm strain SSC : 15/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.557 mm/mm strain SSC : 15/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.743 mm/mm strain SSC : 15/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.741 mm/mm strain SSC : 15/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.72 mm/mm strain UTS : hot-rolled plate \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : hot-rolled plate \|\| 20 °C to 300 °C (68 °F to 572 °F) %El : hot-rolled plate \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| 20 °C to 300 °C (68 °F to 572 °F)
2315 (ASTM A203) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -101 °C to 93 °C (-150 °F to 199 °F) DLL : solid \|\| -101 °C to 93 °C (-150 °F to 199 °F) MTE : solid \|\| -101 °C to 93 °C (-150 °F to 199 °F) CTE : solid \|\| -101 °C to 93 °C (-150 °F to 199 °F) TC : solid \|\| normalized & tempered \|\| -150 °C to 540 °C (-238 °F to 1004 °F) UTS : as-rolled \|\| -163 °C to 35 °C (-262 °F to 95 °F) UTS : normalized \|\| -163 °C to 38 °C (-262 °F to 100 °F) UTS : quenched & tempered \|\| -163 °C to 42 °C (-262 °F to 107 °F) YS : as-rolled \|\| -189 °C to 39 °C (-308 °F to 102 °F) YS : normalized \|\| -163 °C to 35 °C (-262 °F to 95 °F) YS : quenched & tempered \|\| -163 °C to 38 °C (-262 °F to 100 °F) FSN : carburized \|\| tested at 20 °C (68 °F), R = -1, rotating beam, BH 363, maximum stress \|\| 2x10⁴ cycles to 1.2x10⁷ cycles FSN : carburized \|\| tested at 20 °C (68 °F), R = -1, rotating beam, BH 341, maximum stress \|\| 2x10⁴ cycles to 1.2x10⁷ cycles FSN : carburized \|\| tested at 20 °C (68 °F), R = -1, rotating beam, BH 187, maximum stress \|\| 2.5x10³ cycles to 1.2x10⁷ cycles
2330 (ASTM A203) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value UTS : annealed \|\| -183 °C to 27 °C (-298 °F to 80 °F) UTS : normalized \|\| -196 °C to 27 °C (-321 °F to 80 °F) UTS : oil quenched & tempered \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : annealed \|\| -183 °C to 27 °C (-298 °F to 80 °F) %El : normalized \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : oil quenched & tempered \|\| -196 °C to 27 °C (-321 °F to 80 °F) FSN : carburized at 899 °C (1650 °F) for 3 h, furnace cooled to 746 °C (1375 °F), oil quenched, tempered at 149 °C (300 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 5x10⁴ cycles to 2x10⁸ cycles FSN : carburized at 899 °C (1650 °F) for 6 h, oil quenched, reheat to 746 °C (1375 °F), oil quenched, tempered at 149 °C (300 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 2x10⁸ cycles FSN : carburized at 899 °C (1650 °F) for 3 h, oil quenched, reheat to 746 °C (1375 °F), oil quenched, tempered at 149 °C (300 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3x10⁵ cycles to 2x10⁸ cycles
2507 (UNS S32750) (WNr 1.4410) (ISO/EN/DIN X2CrNiMoN25-7-4) (ASTM A182/A479) (AFNOR Z3CND25-06Az)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) G : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) v : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) K : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 0.005/s \|\| 0 to 0.25 mm/mm strain SSC : annealed, H-precharged \|\| tested at 20 °C (68 °F), 0.005/s \|\| 0 to 0.22 mm/mm strain SSC : strain-hardened \|\| tested at 20 °C (68 °F), 0.005/s \|\| 0 to 0.4 mm/mm strain SSC : water quenched \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.55 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.74 mm/mm strain UTS : 6.35 mm (0.25 inch) hot-rolled plate \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : 6.35 mm (0.25 inch) hot-rolled plate \|\| 20 °C to 400 °C (68 °F to 752 °F) %El : 6.35 mm (0.25 inch) hot-rolled plate \|\| 20 °C to 400 °C (68 °F to 752 °F) FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 8x10³ cycles to 1x10⁸ cycles RHO : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| 20 °C to 300 °C (68 °F to 572 °F)
2515 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 640 °C (68 °F to 1184 °F) DLL : solid \|\| 20 °C to 640 °C (68 °F to 1184 °F) MTE : solid \|\| 20 °C to 640 °C (68 °F to 1184 °F) CTE : solid \|\| 20 °C to 640 °C (68 °F to 1184 °F) TC : solid \|\| normalized & tempered \|\| -148 °C to 423 °C (-235 °F to 793 °F)

Maraging 200 (C-type) (UNS K92810) (ASTM A538/A538M) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) E : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) G : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) v : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) K : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) TC : solid \|\| 20 °C to 100 °C (68 °F to 212 °F) UTS : solution annealed & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : annealed \|\| room temperature value YS : solution annealed & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : annealed \|\| room temperature value YSC* : solution annealed \|\| room temperature value YSC* : aged \|\| room temperature value %El : solution annealed & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : annealed \|\| room temperature value FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁸ cycles
Maraging 250 (C-type) (UNS K92890) (ASTM A538/A538M) (AMS 6512/6520) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) DLL : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) MTE : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) CTE : solid \|\| -257 °C to 760 °C (-431 °F to 1400 °F) E : in tension \|\| -198 °C to 538 °C (-325 °F to 1000 °F) E : in compression, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : in compression, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) G : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) v : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) K : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) TC : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TD : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : solid \|\| 0 °C to 438 °C (32 °F to 820 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain SSC : aged 4 h \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain SSC : aged 8 h \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain SSCC : annealed \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain SSCC : aged 4 h \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain SSCC : aged 8 h \|\| tested at 20 °C (68 °F), 0.004/s \|\| 0 to 7x10^-³ mm/mm strain UTS : solution annealed & aged, plate \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, plate \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, sheet \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, sheet \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value YS : solution annealed & aged, plate \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, plate \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, sheet \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, sheet \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| 102 mm (4 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value YSC : solution annealed & aged, plate \|\| transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, sheet \|\| transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, sheet \|\| longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solution annealed & aged \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁸ cycles CRS : 0.05% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 100 h CRS : 0.1% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h CRS : 0.1% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 100 h CRS : 0.1% plastic strain, annealed & aged \|\| Master curve (LMP) \|\| 315 °C to 427 °C (599 °F to 800 °F) CRS : 0.5% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 100 h CRS : 0.5% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, annealed & aged \|\| Master curve (LMP) \|\| 315 °C to 427 °C (599 °F to 800 °F) CRS : 1% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, annealed & aged \|\| Master curve (LMP) \|\| 315 °C to 427 °C (599 °F to 800 °F) IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), plastic strain, annealed & aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), plastic strain, annealed & aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 399 °C (750 °F), plastic strain, annealed & aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
Maraging 300 (C-type) (UNS K93120) (ISO/EN/DIN X2NiCoMo18-9-5/X3NiCoMo18-8-5) (ASTM A538/A538M) (AMS 6514/6521) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) D : liquid \|\| 1465 °C to 3027 °C (2669 °F to 5480 °F) DLL : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) DLL : liquid \|\| 1465 °C to 3027 °C (2669 °F to 5480 °F) MTE : solid \|\| -257 °C to 871 °C (-431 °F to 1600 °F) MTE : liquid \|\| 1465 °C to 3027 °C (2669 °F to 5480 °F) CTE : liquid \|\| 1465 °C to 3027 °C (2669 °F to 5480 °F) E : in tension \|\| -198 °C to 538 °C (-325 °F to 1000 °F) E : in compression, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : in compression, longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) G : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) v : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) K : solid \|\| -198 °C to 127 °C (-325 °F to 260 °F) TC : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : liquid \|\| 1465 °C to 2687 °C (2669 °F to 4868 °F) TD : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TD : liquid \|\| 1465 °C to 2687 °C (2669 °F to 4868 °F) SH : solid \|\| 0 °C to 438 °C (32 °F to 820 °F) SH : liquid \|\| 1465 °C to 2687 °C (2669 °F to 4868 °F) SSC : hardened to HRC 53 \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSCC : hardened to HRC 53 \|\| tested at 20 °C (68 °F), 3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain UTS : solution annealed & aged, plate \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, plate \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, sheet \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, sheet \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value YS : solution annealed & aged, plate \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, plate \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, sheet \|\| longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, sheet \|\| transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value YS* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value YSC : solution annealed & aged, plate \|\| transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, sheet \|\| longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, sheet \|\| transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| 20 °C to 538 °C (68 °F to 1000 °F) YSC* : solution annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 454 °C (850 °F) for 3 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 1 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 3 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 482 °C (900 °F) for 6 h \|\| room temperature value %El* : effect of aging temperature on RT value \|\| annealed & aged at 510 °C (950 °F) for 3 h \|\| room temperature value FEN : annealed & aged \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 20 cycles to 7.3x10⁴ cycles FEN : annealed & aged \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 80 cycles to 8.9x10⁴ cycles FEN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 90 cycles to 2.2x10⁴ cycles FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 1x10⁸ cycles FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = 0.1, axial, longitudinal, maximum stress \|\| 3.7x10⁴ cycles to 1x10⁷ cycles FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = 0.1, axial, short transverse, maximum stress \|\| 2.2x10⁴ cycles to 1x10⁷ cycles CRS : 0.05% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h CRS : 0.1% plastic strain, annealed & aged \|\| tested at 316 °C (600 °F) \|\| 10 h to 1,000 h CRS : 0.1% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 0.1% plastic strain, annealed & aged \|\| Master curve (LMP) \|\| 315 °C to 427 °C (599 °F to 800 °F) CRS : 0.5% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, annealed & aged \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 316 °C (600 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 1x10^-³ mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 427 °C (800 °F), plastic strain, annealed & aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain RHO : liquid \|\| 1465 °C to 2692 °C (2669 °F to 4877 °F) SIGMA : liquid \|\| 1465 °C to 2692 °C (2669 °F to 4877 °F)
Maraging 350 (C-type) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) E* : solid \|\| room temperature value TC : solid \|\| data from Allvac \|\| 20 °C to 100 °C (68 °F to 212 °F) TC : solid \|\| data from Koniorczyk et. al., hardness HRC 37 \|\| -73 °C to 1105 °C (-100 °F to 2021 °F) TC : solid \|\| average \|\| 20 °C to 100 °C (68 °F to 212 °F) TD : solid \|\| 20 °C to 480 °C (68 °F to 896 °F) SH : solid \|\| -73 °C to 480 °C (-100 °F to 896 °F) SSC : 1 h at 820 °C (1508 °F), 6 h at 575 °C (1067 °F) \|\| tested at 20 °C (68 °F), 0.00787/s \|\| 0 to 0.34 mm/mm strain SSC : 1 h at 820 °C (1508 °F), 6 h at 600 °C (1112 °F) \|\| tested at 20 °C (68 °F), 0.00787/s \|\| 0 to 0.55 mm/mm strain SSC : 1 h at 820 °C (1508 °F), 6 h at 625 °C (1157 °F) \|\| tested at 20 °C (68 °F), 0.00787/s \|\| 0 to 0.64 mm/mm strain SSC : 1 h at 820 °C (1508 °F), 6 h at 650 °C (1202 °F) \|\| tested at 20 °C (68 °F), 0.00787/s \|\| 0 to 0.11 mm/mm strain UTS : 1 h at 816 °C (1500 °F), 6 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : effect of aging time on RT value \|\| annealed \|\| room temperature value UTS* : effect of aging time on RT value \|\| 0.5 h at 816 °C (1500 °F), 1 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging time on RT value \|\| aged 3 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging time on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging time on RT value \|\| aged 10 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging time on RT value \|\| aged 20 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging time on RT value \|\| aged 30 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled \|\| room temperature value UTS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value YS : 1 h at 816 °C (1500 °F), 6 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : effect of aging time on RT value \|\| annealed \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 1 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 3 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 10 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 20 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging time on RT value \|\| aged 30 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled \|\| room temperature value YS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value YSC* : 1 h at 816 °C (1500 °F), 3 h at 482 °C (900 °F) \|\| room temperature value %El : 1 h at 816 °C (1500 °F), 6 h at 482 °C (900 °F) \|\| 20 °C to 540 °C (68 °F to 1004 °F) %El* : effect of aging time on RT value \|\| annealed \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 1 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 3 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 10 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 20 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging time on RT value \|\| aged 30 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled \|\| room temperature value %El* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of cold work & anneal on RT value \|\| 1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| room temperature value FSN : 0.5 h at 816 °C (1500 °F), 3 h at 482 °C (900 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.4x10⁴ cycles to 1x10⁸ cycles FSN : 1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : 1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁷ cycles FSN : 1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F) \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : 1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1.8x10⁴ cycles to 1x10⁷ cycles FSN : 1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F) \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles
Maraging 200 (T-type)	D : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) E* : solid \|\| room temperature value UTS* : annealed \|\| room temperature value UTS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value YS* : annealed \|\| room temperature value YS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value %El* : annealed \|\| room temperature value %El : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁸ cycles
Maraging 250 (T-type)	D : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) E* : solid \|\| room temperature value UTS* : annealed \|\| room temperature value UTS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value YS* : annealed \|\| room temperature value YS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value %El* : annealed \|\| room temperature value %El : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁸ cycles
Maraging 300 (T-type)	D : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) DLL : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) MTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) CTE : solid \|\| 20 °C to 482 °C (68 °F to 900 °F) E* : solid \|\| room temperature value UTS* : annealed \|\| room temperature value UTS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value YS* : annealed \|\| room temperature value YS : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value %El* : annealed \|\| room temperature value %El : aged 3 h at 482 °C (900 °F) \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El* : effect of aging temperature on RT value \|\| aged 6 h at 316 °C (600 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 371 °C (700 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 427 °C (800 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 454 °C (850 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 482 °C (900 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 510 °C (950 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 6 h at 538 °C (1000 °F) \|\| room temperature value FSN : annealed & aged \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 3x10⁴ cycles to 1x10⁸ cycles

Incoloy	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| 63 °C to 1038 °C (145 °F to 1900 °F)
Incoloy 028 (UNS N08028) (WNr 1.4563) (ISO/EN/DIN FeNi31Cr27Mo4Cu1/NW8028/X1NiCrMoCu31-27-4) (ASTM B668/B709) (AFNOR Z1NCDU31-27-03)	D : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) DLL : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) MTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) CTE : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS* : solid \|\| annealed \|\| room temperature value UTS* : solid \|\| cold worked \|\| room temperature value YS* : solid \|\| annealed \|\| room temperature value YS* : solid \|\| cold worked \|\| room temperature value %El* : solid \|\| annealed \|\| room temperature value %El* : solid \|\| cold worked \|\| room temperature value SR : solution annealed & quenched \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : solution annealed & quenched \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : solution annealed & quenched \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : solution annealed & quenched \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : solution annealed & quenched \|\| Master curve (LMP) \|\| 550 °C to 701 °C (1022 °F to 1294 °F) RHO : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SIGMA : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
ASTM B625 (UNS N08031) (WNr 1.4562) (ASTM B625)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : solid \|\| cold-rolled 2 mm (0.0787 inch) sheet \|\| room temperature value UTS* : solid \|\| hot-rolled 25 mm (0.984 inch) sheet \|\| room temperature value YS* : solid \|\| cold-rolled 2 mm (0.0787 inch) sheet \|\| room temperature value YS* : solid \|\| hot-rolled 25 mm (0.984 inch) sheet \|\| room temperature value %El* : solid \|\| cold-rolled 2 mm (0.0787 inch) sheet \|\| room temperature value %El* : solid \|\| hot-rolled 25 mm (0.984 inch) sheet \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 330 (RA 330) (UNS N08330) (WNr 1.4864/1.4886) (ISO/EN/DIN X12NiCrSi36-16) (JIS SUH330) (ASTM B511/B512/B535/B536/B546) (AISI 330) (SAE J405/J412) (AMS 5592/5716) (AFNOR Z12NC37-18/Z12NCS35-16/Z12NCS37-18) (GB & GB/T 1Cr16Ni35) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : annealed \|\| -196 °C to 1160 °C (-321 °F to 2120 °F) YS : annealed \|\| -196 °C to 1204 °C (-321 °F to 2199 °F) %El : annealed \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) SR : mill annealed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1x10⁴ h SR : mill annealed \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1,000 h SR : mill annealed \|\| tested at 1204 °C (2200 °F) \|\| 100 h to 1,000 h SR : mill annealed \|\| Master curve (LMP) \|\| 537 °C to 1205 °C (998 °F to 2201 °F) CRS : 1% total strain, mill annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 2% total strain, mill annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) IC : tested at 649 °C (1200 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Incoloy 800 (UNS N08800) (WNr 1.4876) (ISO/EN/DIN FeNi32Cr21AlTi/NW8800/X10NiCrAlTi32-20/X10NiCrAlTi32-21) (JIS NCF800) (ASTM B163/B366/B407/B408/B409/B514/B515/B564) (AMS 5871) (AFNOR Z8NC32-21) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) G : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) v : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) K : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) TC : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain UTS : solid \|\| cold-drawn rod \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| hot-rolled rod \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : solid \|\| hot-rolled & annealed at 982 °C (1800 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : solid \|\| hot-rolled & annealed at 1149 °C (2100 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solid \|\| cold-drawn rod \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : solid \|\| hot-rolled rod \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solid \|\| hot-rolled & annealed at 982 °C (1800 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solid \|\| hot-rolled & annealed at 1149 °C (2100 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC* : 0.02% offset \|\| hot-rolled and annealed rod \|\| room temperature value YSC* : 0.02% offset \|\| as-extruded rod \|\| room temperature value YSC* : 0.2% offset \|\| hot-rolled and annealed rod \|\| room temperature value YSC* : 0.2% offset \|\| as-extruded rod \|\| room temperature value %El : solid \|\| cold-drawn rod \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : solid \|\| hot-rolled rod \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solid \|\| hot-rolled & annealed at 982 °C (1800 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solid \|\| hot-rolled & annealed at 1149 °C (2100 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : mill annealed \|\| tested at 500 °C (932 °F) \|\| 800 h to 1x10⁵ h SR : mill annealed \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁵ h SR : mill annealed \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁵ h SR : mill annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁵ h SR : mill annealed \|\| tested at 704 °C (1300 °F) \|\| 60 h to 1x10⁴ h SR : mill annealed \|\| Master curve (LMP) \|\| 500 °C to 705 °C (932 °F to 1301 °F) SR : solution annealed \|\| tested at 538 °C (1000 °F) \|\| 30 h to 1x10⁵ h SR : solution annealed \|\| tested at 593 °C (1100 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 649 °C (1200 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 704 °C (1300 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 760 °C (1400 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 816 °C (1500 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 871 °C (1600 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 927 °C (1700 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 982 °C (1800 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 1093 °C (2000 °F) \|\| 20 h to 1x10⁵ h FEN : mill annealed \|\| tested at 427 °C (800 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 290 cycles to 4.8x10⁴ cycles FEN : mill annealed \|\| tested at 538 °C (1000 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 260 cycles to 5.2x10⁴ cycles FEN : mill annealed \|\| tested at 593 °C (1100 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 200 cycles to 9.6x10³ cycles FEN : solution annealed \|\| tested at 538 °C (1000 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 370 cycles to 2.61x10⁵ cycles FEN : solution annealed \|\| tested at 649 °C (1200 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 120 cycles to 2.3x10⁴ cycles FEN : solution annealed \|\| tested at 704 °C (1300 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 90 cycles to 2.18x10⁵ cycles FEN : solution annealed \|\| tested at 760 °C (1400 °F), R = -1, axial, 0.004/s, bar, total strain range \|\| 130 cycles to 1.5x10⁴ cycles FEN : solution annealed \|\| tested at 649 °C (1200 °F), R = -1, axial, 0.004/s, plate, total strain range \|\| 480 cycles to 7.6x10³ cycles FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, bending, total strain range \|\| 137 cycles to 5x10⁴ cycles FSN : hot-rolled \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : hot-rolled & annealed at 1066 °C (1950 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : cold-drawn \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 1066 °C (1950 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 871 °C (1600 °F) \|\| tested at 29 °C (85 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 871 °C (1600 °F) \|\| tested at 427 °C (800 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 871 °C (1600 °F) \|\| tested at 538 °C (1000 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 871 °C (1600 °F) \|\| tested at 760 °C (1400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : cold-drawn & annealed at 871 °C (1600 °F) \|\| tested at 871 °C (1600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles CRS : 0.5% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 85 h to 5x10⁴ h CRS : 0.5% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 2 h to 5x10⁴ h CRS : 0.5% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 0.5 h to 5x10⁴ h CRS : 0.5% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 5x10⁴ h CRS : 0.5% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 1.3 h to 5x10⁴ h CRS : 0.5% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 1% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 175 h to 1x10⁵ h CRS : 1% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 4 h to 1x10⁵ h CRS : 1% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 1 h to 1x10⁵ h CRS : 1% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1x10⁵ h CRS : 1% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 2.7 h to 1x10⁵ h CRS : 1% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 1.5% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 260 h to 1.5x10⁵ h CRS : 1.5% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 6 h to 1.5x10⁵ h CRS : 1.5% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 1.5 h to 1.5x10⁵ h CRS : 1.5% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 1.6 h to 1.5x10⁵ h CRS : 1.5% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 4 h to 1.5x10⁵ h CRS : 1.5% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 2% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 350 h to 2x10⁵ h CRS : 2% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 8 h to 2x10⁵ h CRS : 2% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 2 h to 2x10⁵ h CRS : 2% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 2 h to 2x10⁵ h CRS : 2% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 5 h to 2x10⁵ h CRS : 2% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 3% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 525 h to 3x10⁵ h CRS : 3% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 11 h to 3x10⁵ h CRS : 3% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 3 h to 3x10⁵ h CRS : 3% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 3.3 h to 3x10⁵ h CRS : 3% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 8 h to 3x10⁵ h CRS : 3% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 4% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 700 h to 4x10⁵ h CRS : 4% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 15 h to 4x10⁵ h CRS : 4% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 4 h to 4x10⁵ h CRS : 4% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 4.4 h to 4x10⁵ h CRS : 4% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 4x10⁵ h CRS : 4% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) CRS : 5% creep strain, annealed \|\| tested at 499 °C (930 °F) \|\| 880 h to 5x10⁵ h CRS : 5% creep strain, annealed \|\| tested at 538 °C (1000 °F) \|\| 19 h to 5x10⁵ h CRS : 5% creep strain, annealed \|\| tested at 593 °C (1100 °F) \|\| 5 h to 5x10⁵ h CRS : 5% creep strain, annealed \|\| tested at 649 °C (1200 °F) \|\| 5.5 h to 5x10⁵ h CRS : 5% creep strain, annealed \|\| tested at 704 °C (1300 °F) \|\| 13.5 h to 5x10⁵ h CRS : 5% creep strain, annealed \|\| Master curve (LMP) \|\| 499 °C to 705 °C (930 °F to 1301 °F) IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 300 h \|\| 0 to 0.15 mm/mm strain IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 499 °C (930 °F), creep strain, annealed \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, annealed \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, annealed \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, annealed \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 10 h \|\| 0 to 0.4 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, annealed \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Incoloy 800H & 800HT (UNS N08810/N08811) (WNr 1.4958/1.4959) (ISO/EN/DIN FeNi32Cr21AlTi4/NW8810/NW8811/X10NiCrAlTi32-20/X5NiCrAlTi31-20/X8NiCrAlTi32-21) (JIS NCF800H) (ASTM B163/B407/B408/B409/B564) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) G : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) v : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) K : solid \|\| -190 °C to 800 °C (-310 °F to 1472 °F) TC : solid \|\| Special Metals \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| Sandvik \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| average of Sandvik & Special Metals \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| average of Sandvik & Special Metals \|\| 20 °C to 800 °C (68 °F to 1472 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : solution annealed \|\| tested at 649 °C (1200 °F) \|\| 40 h to 1x10⁵ h SR : solution annealed \|\| tested at 704 °C (1300 °F) \|\| 40 h to 1x10⁵ h SR : solution annealed \|\| tested at 760 °C (1400 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 816 °C (1500 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 871 °C (1600 °F) \|\| 30 h to 1x10⁵ h SR : solution annealed \|\| tested at 927 °C (1700 °F) \|\| 40 h to 1x10⁵ h SR : solution annealed \|\| tested at 982 °C (1800 °F) \|\| 40 h to 1x10⁵ h SR : solution annealed \|\| tested at 1038 °C (1900 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| tested at 1093 °C (2000 °F) \|\| 20 h to 1x10⁵ h SR : solution annealed \|\| Master curve (LMP) \|\| 650 °C to 1096 °C (1202 °F to 2005 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 122 cycles to 3x10⁴ cycles FEN : annealed \|\| tested at 538 °C (1000 °F), R = -1, axial, total strain range \|\| 300 cycles to 1.25x10⁵ cycles FEN : annealed \|\| tested at 649 °C (1200 °F), R = -1, axial, total strain range \|\| 100 cycles to 1.5x10⁴ cycles FEN : annealed \|\| tested at 760 °C (1400 °F), R = -1, axial, total strain range \|\| 108 cycles to 2.5x10⁴ cycles RHO : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Incoloy 801 (UNS N08801) (ISO/EN/DIN FeNi32Cr20Ti/FeNi32Cr21Ti/NW8801)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : annealed & quenched \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| annealed & quenched \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| annealed & quenched \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| annealed & quenched \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : annealed & quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : annealed & quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : annealed & quenched \|\| 20 °C to 760 °C (68 °F to 1400 °F)
Incoloy 802 (UNS N08802)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) TC : solid \|\| annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Incoloy 803 (UNS S35045)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| annealed \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : solid \|\| annealed plate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| annealed sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| annealed plate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| annealed sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| annealed plate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| annealed sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : solution annealed \|\| tested at 593 °C (1100 °F) \|\| 20 h to 1.8x10⁴ h SR : solution annealed \|\| tested at 649 °C (1200 °F) \|\| 3 h to 1.7x10⁴ h SR : solution annealed \|\| tested at 704 °C (1300 °F) \|\| 3 h to 1.8x10⁴ h SR : solution annealed \|\| tested at 760 °C (1400 °F) \|\| 3 h to 1.8x10⁴ h SR : solution annealed \|\| tested at 816 °C (1500 °F) \|\| 3 h to 1.3x10⁴ h SR : solution annealed \|\| tested at 871 °C (1600 °F) \|\| 3 h to 1.7x10⁴ h SR : solution annealed \|\| tested at 927 °C (1700 °F) \|\| 3 h to 1.8x10⁴ h SR : solution annealed \|\| tested at 982 °C (1800 °F) \|\| 3 h to 1.8x10⁴ h SR : solution annealed \|\| tested at 1038 °C (1900 °F) \|\| 3 h to 1.5x10⁴ h SR : solution annealed \|\| tested at 1093 °C (2000 °F) \|\| 3 h to 2.1x10⁴ h SR : solution annealed \|\| tested at 1149 °C (2100 °F) \|\| 3 h to 1.6x10⁴ h SR : solution annealed \|\| Master curve (LMP) \|\| 593 °C to 1149 °C (1099 °F to 2100 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Incoloy 832	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| cold-rolled \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| cold-rolled \|\| 20 °C to 1150 °C (68 °F to 2102 °F) SH : solid \|\| cold-rolled \|\| 20 °C to 1150 °C (68 °F to 2102 °F) UTS* : solid \|\| ASTM grain size of 10.5 to 11 \|\| room temperature value YS* : solid \|\| ASTM grain size of 10.5 to 11 \|\| room temperature value %El* : solid \|\| ASTM grain size of 10.5 to 11 \|\| room temperature value RHO : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) SIGMA : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F)
Incoloy 840	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| mill-finished \|\| 20 °C to 650 °C (68 °F to 1202 °F) SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : mill-finished \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : mill-finished \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : mill-finished \|\| 20 °C to 871 °C (68 °F to 1600 °F) RHO : solid \|\| mill-finished \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| mill-finished \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Incoloy 864 (UNS S35135) (ASTM A240/A480)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 6 h to 800 h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 6 h to 800 h SR : annealed \|\| tested at 982 °C (1800 °F) \|\| 6 h to 480 h SR : annealed \|\| Master curve (LMP) \|\| 760 °C to 872 °C (1400 °F to 1601 °F) FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles FEN : annealed \|\| tested at 538 °C (1000 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 865 (UNS S35115) (ASTM A240/A480)	D* : solid \|\| cubic \|\| room temperature value E* : solid \|\| room temperature value UTS* : solid \|\| annealed \|\| room temperature value YS* : solid \|\| annealed \|\| room temperature value %El* : solid \|\| annealed \|\| room temperature value FEN : annealed \|\| tested at 538 °C (1000 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 904 (904L) (UNS N08904) (WNr 1.4539) (ISO/EN/DIN X1NiCrMoCu25-20-5) (JIS SUS890L) (ASTM B625/B649/B673/B674/B677) (AISI 904L) (AFNOR Z1NCDU25-20.04/Z2NCDU25-20)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 802 °C (68 °F to 1475 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SSC : cold-rolled sheet, quenched and annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.263 mm/mm strain UTS : 12 mm (0.472 inch) plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : 12 mm (0.472 inch) plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : 12 mm (0.472 inch) plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) RHO : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SIGMA : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F)
Incoloy 25-6MO (UNS N08925/N08926) (WNr 1.4529) (ISO/EN/DIN X1NiCrMoCuN25-20-7) (ASTM A240/A472/A480/B625/B649)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) G : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) v : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) K : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 25-6HN (UNS N08367)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : unknown condition \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : unknown condition \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : unknown condition \|\| 20 °C to 538 °C (68 °F to 1000 °F)
Incoloy 27-7MO (UNS S31277) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -190 °C to 700 °C (-310 °F to 1292 °F) DLL : solid \|\| -190 °C to 700 °C (-310 °F to 1292 °F) MTE : solid \|\| -190 °C to 700 °C (-310 °F to 1292 °F) CTE : solid \|\| -190 °C to 700 °C (-310 °F to 1292 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| annealed \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| -196 °C to 454 °C (-321 °F to 849 °F) YS : annealed \|\| -196 °C to 454 °C (-321 °F to 849 °F) %El : annealed \|\| -196 °C to 454 °C (-321 °F to 849 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy A-286 (UNS S66286) (WNr 1.4944/1.4980) (ISO/EN/DIN X4NiCrTi25-15/X5NiCrTi2615) (JIS SUH660) (ASTM A453/A638) (AISI 660) (SAE J467) (AMS 5525/5728/5731/5732/5734/5735/5736/5737/5804/5805/5858/5895) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) D : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F) DLL : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) DLL : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F) MTE : solid \|\| -251 °C to 871 °C (-420 °F to 1600 °F) MTE : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F) CTE : solid \|\| -129 °C to 871 °C (-200 °F to 1600 °F) CTE : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F) E : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) G : solid \|\| -273 °C to 816 °C (-460 °F to 1500 °F) v : solid \|\| -273 °C to 816 °C (-460 °F to 1500 °F) K : solid \|\| -273 °C to 816 °C (-460 °F to 1500 °F) TC : solid \|\| precipitation hardened \|\| -269 °C to 727 °C (-452 °F to 1340 °F) TC : solid \|\| solution annealed \|\| -269 °C to 1327 °C (-452 °F to 2420 °F) TC : liquid \|\| 1446 °C to 2327 °C (2635 °F to 4220 °F) TD : solid \|\| precipitation hardened \|\| 20 °C to 727 °C (68 °F to 1340 °F) TD : solid \|\| solution annealed \|\| 20 °C to 815 °C (68 °F to 1499 °F) TD : liquid \|\| 1446 °C to 2327 °C (2635 °F to 4220 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SH : liquid \|\| 1446 °C to 2327 °C (2635 °F to 4220 °F) SSC : solution treated at 982 °C (1800 °F), air cooled, aged at 732 °C (1350 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : solution treated at 982 °C (1800 °F), air cooled, aged at 732 °C (1350 °F) \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain SSC : solution treated at 982 °C (1800 °F), air cooled, aged at 732 °C (1350 °F) \|\| tested at -195.6 °C (-320 °F), unknown strain rate \|\| 0 to 0.28 mm/mm strain SSC : solution treated at 982 °C (1800 °F), air cooled, aged at 732 °C (1350 °F) \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate \|\| 0 to 0.29 mm/mm strain SSC : solution treated at 899 °C (1650 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 20 °C (68 °F), 4x10^-⁴/s \|\| 0 to 0.155 mm/mm strain SSC : solution treated at 899 °C (1650 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 20 °C (68 °F), 4/s \|\| 0 to 0.146 mm/mm strain SSC : solution treated at 899 °C (1650 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 20 °C (68 °F), 600/s \|\| 0 to 0.128 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 20 °C (68 °F), 4.17x10^-⁵/s \|\| 0 to 0.28 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 316 °C (600 °F), 4.17x10^-⁵/s, 0.5 h hold \|\| 0 to 0.24 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 316 °C (600 °F), 4.17x10^-⁵/s, 10 h hold \|\| 0 to 0.23 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 316 °C (600 °F), 4.17x10^-⁵/s, 100 h hold \|\| 0 to 0.2 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 316 °C (600 °F), 4.17x10^-⁵/s, 1000 h hold \|\| 0 to 0.2 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 427 °C (800 °F), 4.17x10^-⁵/s, 0.5 h hold \|\| 0 to 0.234 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 427 °C (800 °F), 4.17x10^-⁵/s, 10 h hold \|\| 0 to 0.231 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 427 °C (800 °F), 4.17x10^-⁵/s, 100 h hold \|\| 0 to 0.234 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, up to 427 °C (800 °F) \|\| tested at 427 °C (800 °F), 4.17x10^-⁵/s, 1000 h hold \|\| 0 to 0.24 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 538 °C (1000 °F), 4.17x10^-⁵/s, 0.5 h hold \|\| 0 to 0.217 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 538 °C (1000 °F), 4.17x10^-⁵/s, 10 h hold \|\| 0 to 0.195 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 538 °C (1000 °F), 4.17x10^-⁵/s, 100 h hold \|\| 0 to 0.192 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 538 °C (1000 °F), 4.17x10^-⁵/s, 1000 h hold \|\| 0 to 0.195 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 593 °C (1100 °F), 4.17x10^-⁵/s, 0.5 h hold \|\| 0 to 0.23 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 593 °C (1100 °F), 4.17x10^-⁵/s, 10 h hold \|\| 0 to 0.23 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 593 °C (1100 °F), 4.17x10^-⁵/s, 100 h hold \|\| 0 to 0.19 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 593 °C (1100 °F), 4.17x10^-⁵/s, 1000 h hold \|\| 0 to 0.2 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 649 °C (1200 °F), 4.17x10^-⁵/s, 0.5 h hold \|\| 0 to 0.21 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 649 °C (1200 °F), 4.17x10^-⁵/s, 10 h hold \|\| 0 to 0.19 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 649 °C (1200 °F), 4.17x10^-⁵/s, 100 h hold \|\| 0 to 0.22 mm/mm strain SSC : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F), sheet, above 427 °C (800 °F) \|\| tested at 649 °C (1200 °F), 4.17x10^-⁵/s, 1000 h hold \|\| 0 to 0.218 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 950 °C (1742 °F), 0.001/s \|\| 0 to 0.68 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 950 °C (1742 °F), 0.01/s \|\| 0 to 0.68 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 950 °C (1742 °F), 0.1/s \|\| 0 to 0.68 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 950 °C (1742 °F), 1/s \|\| 0 to 0.65 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 1100 °C (2012 °F), 0.001/s \|\| 0 to 0.63 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 1100 °C (2012 °F), 0.01/s \|\| 0 to 0.69 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 1100 °C (2012 °F), 0.1/s \|\| 0 to 0.69 mm/mm strain SSCC : cast, homogenized & hot-rolled \|\| tested at 1100 °C (2012 °F), 1/s \|\| 0 to 0.69 mm/mm strain UTS : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| bar \|\| -251 °C to 816 °C (-420 °F to 1500 °F) UTS : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| sheet \|\| -251 °C to 650 °C (-420 °F to 1202 °F) UTS : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1.63 mm (0.064 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| bar \|\| -251 °C to 650 °C (-420 °F to 1202 °F) YS : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| sheet \|\| -251 °C to 650 °C (-420 °F to 1202 °F) YS : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1.63 mm (0.064 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| bar \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1.63 mm (0.064 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 316 °C (600 °F) \|\| 1 h to 100 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 371 °C (700 °F) \|\| 1 h to 100 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 427 °C (800 °F) \|\| 1 h to 200 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁴ h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 4,000 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 704 °C (1300 °F) \|\| 10 h to 2,000 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 4 h to 2,000 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 10 h to 500 h SR : solution treated at 982 °C (1800 °F), oil quenched, aged at 718 °C (1325 °F) \|\| Master curve (LMP) \|\| 315 °C to 816 °C (599 °F to 1501 °F) SR : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 9 h to 340 h SR : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 5 h to 50 h SR : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 9 h to 65 h SR : solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) FSN : solution at 899 °C (1650 °F), oil quenched, aged at 704 °C (1300 °F), unnotched \|\| tested at 677 °C (1250 °F), R = -1, axial, maximum stress \|\| 1x10⁵ cycles to 2x10⁷ cycles FSN : solution at 899 °C (1650 °F), oil quenched, aged at 704 °C (1300 °F), unnotched \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 1x10⁵ cycles to 3x10⁷ cycles FSN : solution at 899 °C (1650 °F), oil quenched, aged at 704 °C (1300 °F), unnotched \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 1x10⁵ cycles to 2x10⁷ cycles FSN : solution treated, unnotched \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated, unnotched \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 100 cycles to 4x10⁶ cycles FSN : solution treated, unnotched \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : air melted bar, unnotched \|\| tested at 427 °C (800 °F), R = -0.6, axial, maximum stress \|\| 3x10⁶ cycles to 2x10⁷ cycles FSN : air melted bar, unnotched \|\| tested at 538 °C (1000 °F), R = 0, axial, maximum stress \|\| 7x10⁴ cycles to 4x10⁷ cycles FSN : air melted bar, unnotched \|\| tested at 538 °C (1000 °F), R = 0.48, axial, maximum stress \|\| 4x10⁵ cycles to 5x10⁷ cycles FSN : air melted bar, unnotched \|\| tested at 427 °C (800 °F), R = -0.2, axial, maximum stress \|\| 4x10⁴ cycles to 4x10⁶ cycles FSN : air melted bar, unnotched \|\| tested at 677 °C (1250 °F), R = -0.2, axial, maximum stress \|\| 7x10⁴ cycles to 3x10⁷ cycles FSN : air melted bar, unnotched \|\| tested at 677 °C (1250 °F), R = 0.2, axial, maximum stress \|\| 1x10⁶ cycles to 2x10⁷ cycles FSN : solution treated, TIG welded \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated & aged, K_t = 2 \|\| tested at -196.1 °C (-321.1 °F), R = 0, axial, maximum stress \|\| 2x10³ cycles to 2x10⁵ cycles FSN : solution treated, K_t = 3.5 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated, K_t = 3.5 \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles FSN : solution treated, K_t = 3.5 \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : air melted bar, K_t = 3.4 \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 2x10⁵ cycles FSN : air melted bar, K_t = 3.4 \|\| tested at 427 °C (800 °F), R = 0.2, axial, maximum stress \|\| 2x10⁴ cycles to 3x10⁷ cycles FSN : air melted bar, K_t = 3.4 \|\| tested at 427 °C (800 °F), R = 0.6, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : air melted bar, K_t = 3.4 \|\| tested at 538 °C (1000 °F), R = 0, axial, maximum stress \|\| 6x10⁴ cycles to 3x10⁷ cycles FSN : air melted bar, K_t = 3.4 \|\| tested at 538 °C (1000 °F), R = 0.74, axial, maximum stress \|\| 6x10⁴ cycles to 3x10⁷ cycles CRS : 0.05% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 1,200 h CRS : 0.05% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.4 h to 1,120 h CRS : 0.05% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 300 h CRS : 0.1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 900 h CRS : 0.1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.1 h to 1,150 h CRS : 0.1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.45 h to 940 h CRS : 0.3% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 1 h to 730 h CRS : 0.3% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.1 h to 1,300 h CRS : 0.3% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.1 h to 850 h CRS : 0.5% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 2 h to 650 h CRS : 0.5% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.2 h to 1,000 h CRS : 0.5% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 1,530 h CRS : 1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 649 °C (1200 °F) \|\| 3.2 h to 300 h CRS : 1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 732 °C (1350 °F) \|\| 0.5 h to 900 h CRS : 1% total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| tested at 816 °C (1500 °F) \|\| 1.66 h to 800 h IC : tested at 649 °C (1200 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) \|\| 300 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) RHO : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F) SIGMA : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SIGMA : liquid \|\| 1446 °C to 2227 °C (2635 °F to 4040 °F)
Incoloy DS (WNr 1.4862) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| hot-rolled plate + HT & welded \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) UTS : solid \|\| cold-rolled sheet + HT \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| hot-rolled plate (HT 1020) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) UTS : solid \|\| hot-rolled plate (HT 1150) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) YS : solid \|\| hot-rolled plate + HT & welded \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) YS : solid \|\| cold-rolled sheet + HT \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| hot-rolled plate (HT 1020) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) YS : solid \|\| hot-rolled plate (HT 1150) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) %El : solid \|\| hot-rolled plate + HT & welded \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) %El : solid \|\| cold-rolled sheet + HT \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| hot-rolled plate (HT 1020) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) %El : solid \|\| hot-rolled plate (HT 1150) \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Incoloy MA 956 (UNS S67956)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SSC : transverse \|\| tested at 200 °C (392 °F), 5x10^-⁵/s, as-received \|\| 0 to 0.12 mm/mm strain SSC : transverse \|\| tested at 200 °C (392 °F), 5x10^-⁵/s, 100 h at 475 °C (887 °F) \|\| 0 to 0.18 mm/mm strain SSC : transverse \|\| tested at 200 °C (392 °F), 5x10^-⁵/s, 500 h at 475 °C (887 °F) \|\| 0 to 0.5 mm/mm strain SSC : transverse \|\| tested at 200 °C (392 °F), 5x10^-⁵/s, 1000 h at 475 °C (887 °F) \|\| 0 to 0.4 mm/mm strain UTS : annealed cold-rolled sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed cold-rolled sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed cold-rolled sheet \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : annealed cold-rolled sheet \|\| tested at 1100 °C (2012 °F) \|\| 100 h to 1x10⁴ h RHO : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SIGMA : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)

ATI JS700 (UNS N08700) (ASTM B599/B672/SB-599/SB-672) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 100 °C (32 °F to 212 °F) DLL : solid \|\| 0 °C to 100 °C (32 °F to 212 °F) MTE : solid \|\| 0 °C to 100 °C (32 °F to 212 °F) CTE : solid \|\| 0 °C to 100 °C (32 °F to 212 °F) TC* : solid \|\| unclad \|\| room temperature value
Carpenter 286-LNi alloy (UNS S66285)	D : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) DLL : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) MTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) CTE : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) UTS : solid \|\| solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solid \|\| solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solid \|\| solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Discaloy (UNS S66220) (ASTM A453/A638) (AISI 662) (SAE J467) (AMS 5733)	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| heat-treated at 1010 °C (1850 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| forging 293 HB \|\| 20 °C to 732 °C (68 °F to 1349 °F) UTS : solid \|\| heat-treated at 996 °C (1825 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solid \|\| heat-treated at 1010 °C (1850 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| forging 293 HB \|\| 20 °C to 732 °C (68 °F to 1349 °F) YS : solid \|\| heat-treated at 996 °C (1825 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solid \|\| heat-treated at 1010 °C (1850 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| forging 293 HB \|\| 20 °C to 732 °C (68 °F to 1349 °F) %El : solid \|\| heat-treated at 996 °C (1825 °F) / 732 °C (1350 °F) / 649 °C (1200 °F) \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F)
Haynes 556 (UNS R30556) (WNr 1.4883) (ASTM B435/B572/B619/B622/B626) (AMS 5874)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : solid \|\| cold-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : solid \|\| hot-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : solid \|\| cold-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : solid \|\| hot-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : solid \|\| cold-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : solid \|\| hot-rolled & solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled, sheet, plate & bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SIGMA : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)
S-590 (UNS R30590)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SR : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 732 °C (1350 °F) \|\| 15 h to 1,760 h SR : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 5,140 h SR : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| Master curve (LMP) \|\| 732 °C to 816 °C (1349 °F to 1501 °F) FSN : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 732 °C (1350 °F), R = 0.6, axial, maximum stress \|\| 3.2x10⁶ cycles to 1x10⁹ cycles FSN : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 732 °C (1350 °F), R = 0.2, axial, maximum stress \|\| 3.8x10⁶ cycles to 3.5x10⁸ cycles FSN : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 816 °C (1500 °F), R = 0.6, axial, maximum stress \|\| 2.4x10⁶ cycles to 4x10⁸ cycles FSN : water quenched from 1232 °C (2250 °F), aged 760 °C (1400 °F) for 16 h, furnace cooled \|\| tested at 816 °C (1500 °F), R = 0.2, axial, maximum stress \|\| 2.8x10⁶ cycles to 9x10⁸ cycles
Haynes Multimet (N-155) (UNS R30155) (WNr 1.4971) (JIS SUH661) (ASTM A567/A639) (AISI 661) (AMS 5376/5531/5532/5585/5769/5794/5795) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : solid \|\| solution annealed at 1177 °C (2150 °F) & air cooled \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| solution annealed at 1177 °C (2150 °F) & water quenched \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solid \|\| solution annealed at 1177 °C (2150 °F) & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solid \|\| solution annealed at 1177 °C (2150 °F) & water quenched \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solid \|\| solution annealed at 1177 °C (2150 °F) & air cooled \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| solution annealed at 1177 °C (2150 °F) & water quenched \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : solution treated at 1204 °C (2200 °F) \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : solution treated at 1204 °C (2200 °F) \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1,000 h SR : solution treated at 1204 °C (2200 °F) \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : solution treated at 1204 °C (2200 °F) \|\| tested at 899 °C (1650 °F) \|\| 10 h to 1,000 h SR : solution treated at 1204 °C (2200 °F) \|\| Master curve (LMP) \|\| 649 °C to 899 °C (1200 °F to 1650 °F) SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : heat-treated to 1177 °C (2150 °F), water quenched \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated to 1177 °C (2150 °F), water quenched, plus 816 °C (1500 °F) for 4 h, air cooled \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SR : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 538 °C (1000 °F) \|\| 25 h to 2,000 h SR : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 649 °C (1200 °F) \|\| 25 h to 2,000 h SR : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 732 °C (1350 °F) \|\| 40 h to 2,000 h SR : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 816 °C (1500 °F) \|\| 30 h to 2,000 h SR : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) FSN : hardened & tempered \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 3.1x10⁷ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 732 °C (1350 °F), R = -1, axial, maximum stress \|\| 3.6x10³ cycles to 1.1x10⁵ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 732 °C (1350 °F), R = 0.6, axial, maximum stress \|\| 1.7x10⁶ cycles to 8.2x10⁸ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 732 °C (1350 °F), R = 0.2, axial, maximum stress \|\| 2.4x10⁶ cycles to 7.3x10⁸ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 816 °C (1500 °F), R = -1, axial, maximum stress \|\| 1.8x10⁶ cycles to 2.3x10⁸ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 816 °C (1500 °F), R = 0.6, axial, maximum stress \|\| 1.7x10⁶ cycles to 9x10⁸ cycles FSN : heat-treated at 1204 °C (2200 °F), water quenched, aged 760 °C (1400 °F) for 16 h, air cooled \|\| tested at 816 °C (1500 °F), R = 0.2, axial, maximum stress \|\| 2.3x10⁶ cycles to 9x10⁸ cycles CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| tested at 704 °C (1300 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1x10⁵ h CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| tested at 899 °C (1650 °F) \|\| 100 h to 1x10⁵ h CRS : 1% plastic strain, solution treated at 1177 °C (2150 °F), water quenched \|\| Master curve (LMP) \|\| 649 °C to 900 °C (1200 °F to 1652 °F) NE : solid \|\| polished \|\| -188 °C to 970 °C (-307 °F to 1778 °F) NE : solid \|\| oxidized \|\| -188 °C to 920 °C (-307 °F to 1688 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

UNS S29108 (UNS S29108) (ASTM F2229) (AMS 2630)	D* : solid \|\| room temperature value E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 50% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 70% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 80% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value UTS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value UTS* : effect of forging temperature on RT value \|\| forged at 1204 °C (2200 °F), water quenched \|\| room temperature value UTS* : effect of forging temperature on RT value \|\| forged at 1149 °C (2100 °F), water quenched \|\| room temperature value UTS* : effect of forging temperature on RT value \|\| forged at 1093 °C (2000 °F), water quenched \|\| room temperature value UTS* : effect of forging temperature on RT value \|\| forged at 1038 °C (1900 °F), water quenched \|\| room temperature value UTS* : effect of forging temperature on RT value \|\| forged at 982 °C (1800 °F), water quenched \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 50% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 70% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 80% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value YS* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value YS* : effect of forging temperature on RT value \|\| forged at 1204 °C (2200 °F), water quenched \|\| room temperature value YS* : effect of forging temperature on RT value \|\| forged at 1149 °C (2100 °F), water quenched \|\| room temperature value YS* : effect of forging temperature on RT value \|\| forged at 1093 °C (2000 °F), water quenched \|\| room temperature value YS* : effect of forging temperature on RT value \|\| forged at 1038 °C (1900 °F), water quenched \|\| room temperature value YS* : effect of forging temperature on RT value \|\| forged at 982 °C (1800 °F), water quenched \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 50% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 70% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 2.54 mm (0.1 inch) diameter wire \|\| 80% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 10% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 30% cold worked \|\| room temperature value %El* : effect of cold work on RT value, 25.4 mm (1 inch) diameter wire \|\| 40% cold worked \|\| room temperature value %El* : effect of forging temperature on RT value \|\| forged at 1204 °C (2200 °F), water quenched \|\| room temperature value %El* : effect of forging temperature on RT value \|\| forged at 1149 °C (2100 °F), water quenched \|\| room temperature value %El* : effect of forging temperature on RT value \|\| forged at 1093 °C (2000 °F), water quenched \|\| room temperature value %El* : effect of forging temperature on RT value \|\| forged at 1038 °C (1900 °F), water quenched \|\| room temperature value %El* : effect of forging temperature on RT value \|\| forged at 982 °C (1800 °F), water quenched \|\| room temperature value FSN : annealed \|\| tested at 23 °C (73 °F), R = -1, maximum stress \|\| 3.7x10⁴ cycles to 1x10⁸ cycles
UNS S30415 (UNS S30415) (WNr 1.4818) (ISO/EN/DIN X6CrNiSiNCe19-10)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1001 °C (1022 °F to 1834 °F) CRS : 1% plastic strain, hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1001 °C (1022 °F to 1834 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
UNS S30600 (UNS S30600) (WNr 1.4361) (ISO/EN/DIN X1CrNiS18-15-4)	D : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| solution annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS S30601 (UNS S30601)	D* : solid \|\| room temperature value UTS : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
UNS S30615 (UNS S30615)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F)
UNS S30815 (UNS S30815) (WNr 1.4835/1.4893) (ISO/EN/DIN X10CrNiSiN21-11/X9CrNiSiNCe21-11-2) (ASTM A240/A276/A312/A358/A409/A473/A479/A813/A814)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SR : hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1050 °C (1922 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1100 °C (2012 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1101 °C (1022 °F to 2014 °F) CRS : 1% plastic strain, hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1050 °C (1922 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1100 °C (2012 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1101 °C (1022 °F to 2014 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
UNS S30908 (UNS S30908) (WNr 1.4833) (ISO/EN/DIN X12CrNi23-13/X12CrNi24-12/X7CrNi23-14) (JIS SUS309/SUS309S) (AISI 309S) (SAE 30309S) (AFNOR Z15CN24-13) (GB & GB/T 0Cr23Ni13)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) v : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) K : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TD : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) SH : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : annealed \|\| 20 °C to 1038 °C (68 °F to 1900 °F) YS : annealed \|\| 20 °C to 1038 °C (68 °F to 1900 °F) %El : annealed \|\| 20 °C to 927 °C (68 °F to 1700 °F) SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) CRS : 1% plastic strain, hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
UNS S31002 (UNS S31002) (WNr 1.4335) (ISO/EN/DIN X1CrNi25-21) (ASTM 310L NAG) (AISI 310LC) (AFNOR Z2CN25-20)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 300 °C (68 °F to 572 °F) %El : solid \|\| annealed 1100 °C (2012 °F) to 1150 °C (2102 °F), rapid water cooled \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
UNS S31050 (UNS S31050) (WNr 1.4466) (ISO/EN/DIN X1CrNiMoN25-22-2)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS S31254 (UNS S31254) (WNr 1.4547) (ISO/EN/DIN X1CrNiMoCuN20-18-7) (JIS SUS312L)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : cold-rolled sheet, quenched and annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.27 mm/mm strain UTS : hot-rolled plate \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : hot-rolled plate \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SIGMA : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
UNS S31266 (UNS S31266) (WNr 1.4549/1.4659) (ISO/EN/DIN X1CrNiMoCuNW24-22-6)	D : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) G : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) v : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) K : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) SSCC : annealed and water quenched from 1150 °C (2102 °F), 0.001/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.5 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 0.001/s \|\| tested at 100 °C (212 °F) \|\| 0 to 0.43 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 0.001/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.49 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 0.001/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.46 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 0.001/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.5 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 5.2/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 2500/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 2500/s \|\| tested at 100 °C (212 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 2500/s \|\| tested at 200 °C (392 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 2500/s \|\| tested at 300 °C (572 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed and water quenched from 1150 °C (2102 °F), 2500/s \|\| tested at 400 °C (752 °F) \|\| 0 to 0.58 mm/mm strain UTS : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 300 °C (68 °F to 572 °F) %El : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) SIGMA : solid \|\| annealed and water quenched from 1150 °C (2102 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F)
UNS S31500 (UNS S31500) (WNr 1.4417)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
UNS S31725 (UNS S31725)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS S31726 (UNS S31726) (WNr 1.4439) (AFNOR Z2CND19-15/Z3CND18-14-05Az)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS S32654 (UNS S32654) (WNr 1.4652) (ISO/EN/DIN X1CrNiMoCuN24-22-8)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SSC : cold-rolled sheet, quenched and annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.333 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.01/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 0.1/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 1/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 5/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.69 mm/mm strain SSCC : 10/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.69 mm/mm strain UTS : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SIGMA : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
UNS S32760 / J93380 (UNS J93380/S32760) (WNr 1.4501) (ISO/EN/DIN X2CrNiMoCuWN25-7-4) (ASTM A182/A240/A276/A314/A320/A351/A473/A479/A789/A790/A815/A890/A928/A988/A995)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) TD : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SSC : solution treated \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.21 mm/mm strain SSC : solution treated \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.195 mm/mm strain SSC : solution treated \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.195 mm/mm strain SSC : solution treated, H charged \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : solution treated, H charged \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.146 mm/mm strain SSC : solution treated, H charged \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 0.147 mm/mm strain UTS : solution annealed \|\| cast \|\| 20 °C to 300 °C (68 °F to 572 °F) UTS : solution annealed \|\| forgings/bars/plates up to 30 mm (1.18 inch) \|\| 20 °C to 300 °C (68 °F to 572 °F) UTS : solution annealed \|\| plates 31 mm to 70 mm (1.22 inch to 2.76 inch) \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solution annealed \|\| cast \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solution annealed \|\| forgings/bars/plates up to 30 mm (1.18 inch) \|\| 20 °C to 300 °C (68 °F to 572 °F) YS : solution annealed \|\| plates 31 mm to 70 mm (1.22 inch to 2.76 inch) \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| wrought \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| cast \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| wrought \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| cast \|\| 20 °C to 300 °C (68 °F to 572 °F)
7-Mo Plus (UNS S32950)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) UTS : solid \|\| 1.7 mm (0.0669 inch) cold-rolled & annealed strip \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS : solid \|\| 63.5 mm (2.5 inch) annealed round bar \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS : solid \|\| 19 mm (0.75 inch) OD x 1.65 mm (0.065 inch) wall annealed tubing \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : solid \|\| 1.7 mm (0.0669 inch) cold-rolled & annealed strip \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : solid \|\| 63.5 mm (2.5 inch) annealed round bar \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : solid \|\| 19 mm (0.75 inch) OD x 1.65 mm (0.065 inch) wall annealed tubing \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : solid \|\| 1.7 mm (0.0669 inch) cold-rolled & annealed strip \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : solid \|\| 63.5 mm (2.5 inch) annealed round bar \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : solid \|\| 19 mm (0.75 inch) OD x 1.65 mm (0.065 inch) wall annealed tubing \|\| 20 °C to 371 °C (68 °F to 700 °F)
UNS S34565 (UNS S34565) (WNr 1.4565) (ISO/EN/DIN X2CrNiMnMoN25-18-6-5/X3CrNiMnMoNbN23-17-5-3) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) UTS : solid \|\| 0 °C to 300 °C (32 °F to 572 °F) YS : solid \|\| 0 °C to 300 °C (32 °F to 572 °F) %El : solid \|\| 0 °C to 300 °C (32 °F to 572 °F)
UNS S35315 (UNS S35315) (WNr 1.4854) (ISO/EN/DIN X6NiCrSiNCe35-25)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SR : hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1050 °C (1922 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| tested at 1100 °C (2012 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1101 °C (1022 °F to 2014 °F) CRS : 1% plastic strain, hot-rolled plate \|\| tested at 550 °C (1022 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 750 °C (1382 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 850 °C (1562 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 950 °C (1742 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1050 °C (1922 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| tested at 1100 °C (2012 °F) \|\| 1x10⁴ h to 1x10⁵ h CRS : 1% plastic strain, hot-rolled plate \|\| Master curve (LMP) \|\| 550 °C to 1101 °C (1022 °F to 2014 °F) RHO : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SIGMA : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)
UNS S40977 (3Cr12) (UNS S40977) (WNr 1.4003) (ISO/EN/DIN X2CrNi12)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| annealed \|\| room temperature value SH* : solid \|\| annealed \|\| room temperature value UTS : annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) YS : annealed \|\| 20 °C to 500 °C (68 °F to 932 °F) FSN : annealed \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 9x10⁴ cycles to 1x10⁷ cycles CRS : 1% total strain, annealed \|\| tested at 400 °C (752 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 450 °C (842 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 500 °C (932 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 550 °C (1022 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 400 °C to 551 °C (752 °F to 1024 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
UNS S42010 (UNS S42010) (WNr 1.4021) (JIS SUS420J1) (ASTM A276/A493) (AFNOR X20Cr13/Z20C13) (GB & GB/T 2Cr13/X20Cr13)	D* : solid \|\| room temperature value E* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 115 °C (239 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.48 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 145 °C (293 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.5 mm/mm strain SSC : Q & P \|\| tested at 20 °C (68 °F), 0.001/s, quenched to 170 °C (338 °F), partitioned at 400 °C (752 °F) \|\| 0 to 0.57 mm/mm strain FSN : hardened & tempered \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2.5x10⁵ cycles to 2x10⁷ cycles NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
UNS S44627 (E-BRITE) (UNS S44627) (ASTM XM-27)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E* : solid \|\| room temperature value TC : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| plate & bar \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : annealed \|\| tubing \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 80% cold worked \|\| room temperature value YS : annealed \|\| plate & bar \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| tubing \|\| 20 °C to 371 °C (68 °F to 700 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 80% cold worked \|\| room temperature value %El : annealed \|\| plate & bar \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| tubing \|\| 20 °C to 371 °C (68 °F to 700 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 60% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 80% cold worked \|\| room temperature value NE : liquid \|\| 1510 °C to 1649 °C (2750 °F to 3000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value

X46Cr13-16 (WNr 1.4304) (ISO/EN/DIN X46Cr13-16)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : annealed & cold-drawn \|\| ferrite & pearlite \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : annealed & cold-drawn, ferrite & pearlite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.3 mm/mm strain SSC : annealed & cold-drawn, ferrite & pearlite \|\| tested at 400 °C (752 °F), unknown strain rate \|\| 0 to 9.7x10^-³ mm/mm strain UTS : annealed & cold-drawn \|\| ferrite & pearlite \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : annealed & cold-drawn \|\| ferrite & pearlite \|\| 20 °C to 600 °C (68 °F to 1112 °F) FSN : annealed & cold-drawn, ferrite & pearlite \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10⁵ cycles to 1x10⁸ cycles
1.4418 (WNr 1.4418) (ISO/EN/DIN X4CrNiMo16-5-1) (ASTM A276/A493) (AFNOR Z6CND16-05-01)	D : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) DLL : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) MTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4460 (WNr 1.4460) (ISO/EN/DIN X3CrNiMoN27-5-2/X4CrNiMo27-5-1/XBCrNiMo27-5) (JIS SUS329J1)	D : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) DLL : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) MTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) CTE : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) E : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) G : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) v : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) K : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) TC : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) TD : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
1.4520 (WNr 1.4520) (ISO/EN/DIN X2CrTi17)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F)
1.4589 (UNS S42035) (WNr 1.4589) (ISO/EN/DIN X5CrNiMoTi15-2)	D : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) DLL : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) MTE : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 400 °C (68 °F to 752 °F)
1.4872 (WNr 1.4872) (ISO/EN/DIN X25CrMnNiN25-9-7)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 1% total strain, annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10³ h to 1x10⁴ h CRS : 1% total strain, annealed \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
1.4877 (WNr 1.4877) (ISO/EN/DIN X6NiCrNbCe32-27)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SR : annealed \|\| tested at 600 °C (1112 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 700 °C (1292 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 800 °C (1472 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 900 °C (1652 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| tested at 1000 °C (1832 °F) \|\| 1x10⁴ h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 600 °C to 1001 °C (1112 °F to 1834 °F) RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
1.7224 (WNr 1.7224)	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) RHO : solid \|\| 20 °C to 300 °C (68 °F to 572 °F) SIGMA : solid \|\| 20 °C to 300 °C (68 °F to 572 °F)
F82H	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) G : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) v : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) K : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) TD : solid \|\| un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS : un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : un-irradiated \|\| 20 °C to 700 °C (68 °F to 1292 °F) SR : normalized at 1038 °C (1900 °F), tempered at 750 °C (1382 °F) \|\| tested at 550 °C (1022 °F) \|\| 6 h to 720 h SR : normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) \|\| tested at 635 °C (1175 °F) \|\| 250 h to 5,400 h SR : normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) \|\| tested at 650 °C (1202 °F) \|\| 100 h to 2,500 h SR : normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) \|\| tested at 665 °C (1229 °F) \|\| 70 h to 1,500 h SR : normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) \|\| tested at 635 °C (1175 °F) \|\| 250 h to 5,400 h SR : normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) \|\| tested at 650 °C (1202 °F) \|\| 40 h to 1,500 h SR : normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) \|\| tested at 665 °C (1229 °F) \|\| 40 h to 3,400 h SR : normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) \|\| tested at 550 °C (1022 °F) \|\| 4.4x10⁴ h to 1.1x10⁶ h SR : normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) \|\| tested at 550 °C (1022 °F), 100 at. ppm He \|\| 6.4x10⁴ h to 2.6x10⁶ h SR : normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) \|\| tested at 550 °C (1022 °F), 300 at. ppm He \|\| 2.5x10⁵ h to 4x10⁶ h RHO : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SIGMA : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F)

38MnVS (ISO/EN/DIN 38MnVS) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 1.0, stress amplitude \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 2.0, stress amplitude \|\| 8x10⁴ cycles to 1x10⁷ cycles FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 4.0, stress amplitude \|\| 1.3x10⁵ cycles to 1x10⁷ cycles
25MnCrVS (ISO/EN/DIN 25MnCrVS) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 1.0, stress amplitude \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 2.0, stress amplitude \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : rotating beam \|\| tested at 20 °C (68 °F), 5000 Hz, R = -1, K_t = 4.0, stress amplitude \|\| 1.7x10⁵ cycles to 1x10⁷ cycles
25MnCrSiVB6 (ISO/EN/DIN 25MnCrSiVB6) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SH : solid \|\| -200 °C to 727 °C (-328 °F to 1340 °F) FSN : annealed hot-rolled bars \|\| tested at 20 °C (68 °F), R = -1, axial, 0 degrees from rolling direction, stress amplitude \|\| 9x10⁴ cycles to 2x10⁶ cycles FSN : annealed hot-rolled bars \|\| tested at 20 °C (68 °F), R = -1, axial, 45 degrees from rolling direction, stress amplitude \|\| 8x10⁴ cycles to 2x10⁶ cycles FSN : annealed hot-rolled bars \|\| tested at 20 °C (68 °F), R = -1, axial, 90 degrees from rolling direction, stress amplitude \|\| 1.6x10⁴ cycles to 2x10⁶ cycles
Fe - 3 Mn (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
TRIP 9 Cr - 8 Ni - 4 Mo - 3 Mn - 3 Si (wt %)	SSC : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), deformed 20%, unknown strain rate \|\| 0 to 0.42 mm/mm strain SSC : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), deformed 20%, unknown strain rate \|\| 0 to 0.24 mm/mm strain SSC : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), deformed 80%, unknown strain rate \|\| 0 to 0.28 mm/mm strain SSC : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), deformed 80%, unknown strain rate \|\| 0 to 0.52 mm/mm strain SSC : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), deformed 20%, unknown strain rate \|\| 0 to 0.45 mm/mm strain SSC : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), deformed 20%, unknown strain rate \|\| 0 to 0.275 mm/mm strain SSC : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), deformed 80%, unknown strain rate \|\| 0 to 0.293 mm/mm strain SSC : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), deformed 80%, unknown strain rate \|\| 0 to 0.84 mm/mm strain FEN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, plastic strain range \|\| 30 cycles to 1.4x10³ cycles FEN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, plastic strain range \|\| 70 cycles to 370 cycles FEN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, plastic strain range \|\| 10 cycles to 1.5x10³ cycles FEN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, plastic strain range \|\| 30 cycles to 1.4x10³ cycles FEN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, total strain range \|\| 30 cycles to 1.4x10³ cycles FEN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, total strain range \|\| 70 cycles to 370 cycles FEN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, total strain range \|\| 10 cycles to 1.5x10³ cycles FEN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, total strain range \|\| 30 cycles to 1.4x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, plastic strain range \|\| 25 cycles to 1.46x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, plastic strain range \|\| 35 cycles to 3.17x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, plastic strain range \|\| 20 cycles to 1.6x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, plastic strain range \|\| 25 cycles to 1.07x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, total strain range \|\| 25 cycles to 1.46x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, total strain range \|\| 35 cycles to 3.17x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, total strain range \|\| 20 cycles to 1.6x10³ cycles FEN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, total strain range \|\| 25 cycles to 1.07x10³ cycles FSN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, stress range \|\| 30 cycles to 1.4x10³ cycles FSN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, stress range \|\| 70 cycles to 370 cycles FSN : processed at 450 °C (842 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, stress range \|\| 10 cycles to 1.5x10³ cycles FSN : processed at 450 °C (842 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, stress range \|\| 30 cycles to 1.4x10³ cycles FSN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 20%, stress range \|\| 25 cycles to 1.46x10³ cycles FSN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 20%, stress range \|\| 35 cycles to 3.17x10³ cycles FSN : processed at 250 °C (482 °F) \|\| tested at 25 °C (77 °F), R = -1, axial, deformed 80%, stress range \|\| 20 cycles to 1.6x10³ cycles FSN : processed at 250 °C (482 °F) \|\| tested at 200 °C (392 °F), R = -1, axial, deformed 80%, stress range \|\| 25 cycles to 1.07x10³ cycles
TRIP/TWIP 15 Cr - 6 Mn - 6 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value SSC : cast & homogenized \|\| tested at -60 °C (-76 °F), 4x10^-⁴/s \|\| 0 to 0.26 mm/mm strain SSC : cast & homogenized \|\| tested at 20 °C (68 °F), 4x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : cast & homogenized \|\| tested at 60 °C (140 °F), 4x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : cast & homogenized \|\| tested at 100 °C (212 °F), 4x10^-⁴/s \|\| 0 to 0.43 mm/mm strain SSC : cast & homogenized \|\| tested at 200 °C (392 °F), 4x10^-⁴/s \|\| 0 to 0.25 mm/mm strain UTS : cast & homogenized \|\| -196 °C to 300 °C (-321 °F to 572 °F) YS : cast & homogenized \|\| -196 °C to 300 °C (-321 °F to 572 °F) %El : cast & homogenized \|\| -196 °C to 300 °C (-321 °F to 572 °F)
TWIP steel 8 Mn - 0.8 Al - 0.1 C (wt %)	SSC : hot-rolled & annealed \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : hot-rolled & annealed \|\| tested at 500 °C (932 °F), 1/s \|\| 0 to 0.28 mm/mm strain SSC : cold-rolled \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.42 mm/mm strain SSC : cold-rolled \|\| tested at 500 °C (932 °F), 1/s \|\| 0 to 0.27 mm/mm strain SSC : cold-rolled & annealed \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.47 mm/mm strain SSC : cold-rolled & annealed \|\| tested at 500 °C (932 °F), 1/s \|\| 0 to 0.22 mm/mm strain
TWIP steel 8 Mn - 2 Al - 0.6 C (wt %)	D : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) DLL : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) MTE : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TC : solid \|\| 298 °C to 1000 °C (568 °F to 1832 °F)
TWIP steel 8 Mn - 2.3 Al - 1.3 Si - 0.4 C (wt %)	SSC : water quenched & annealed \|\| tested at 20 °C (68 °F), 0.001/s, annealed 10 minutes at 660 °C (1220 °F) \|\| 0 to 0.2 mm/mm strain SSC : water quenched & annealed \|\| tested at 20 °C (68 °F), 0.001/s, annealed 30 minutes at 660 °C (1220 °F) \|\| 0 to 0.23 mm/mm strain SSC : water quenched & annealed \|\| tested at 20 °C (68 °F), 0.001/s, annealed 2 h at 660 °C (1220 °F) \|\| 0 to 0.26 mm/mm strain SSC : water quenched & annealed \|\| tested at 20 °C (68 °F), 0.001/s, annealed 4 h at 660 °C (1220 °F) \|\| 0 to 0.275 mm/mm strain SSC : water quenched & annealed \|\| tested at 20 °C (68 °F), 0.001/s, annealed 24 h at 660 °C (1220 °F) \|\| 0 to 0.28 mm/mm strain
TWIP steel 18 Mn - 0.5 C (wt %)	D : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) DLL : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) MTE : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TC : solid \|\| 298 °C to 1000 °C (568 °F to 1832 °F) SSC : 1/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.37 mm/mm strain SSC : 100/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.327 mm/mm strain
A128-E2 Hadfield steel (Fe - 13 Mn (wt %)) (WNr 1.3401) (ISO/EN/DIN X120Mn12) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) DLL : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) MTE : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) CTE : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) TC : solid \|\| air cooled \|\| 0 °C to 850 °C (32 °F to 1562 °F) TC : solid \|\| annealed \|\| 0 °C to 850 °C (32 °F to 1562 °F) SSC : austenitized & quenched \|\| tested at -196.1 °C (-321.1 °F), 8.33x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : austenitized & quenched \|\| tested at -100 °C (-148 °F), 8.33x10^-⁴/s \|\| 0 to 0.27 mm/mm strain SSC : austenitized & quenched \|\| tested at -79 °C (-110 °F), 8.33x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : austenitized & quenched \|\| tested at -40 °C (-40 °F), 8.33x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : austenitized & quenched \|\| tested at 100 °C (212 °F), 8.33x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : austenitized & quenched \|\| tested at 20 °C (68 °F), 8.33x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : austenitized & quenched \|\| tested at 250 °C (482 °F), 8.33x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : solution treated \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.631 mm/mm strain SSCC : austenitized & quenched \|\| tested at -100 °C (-148 °F), 6.67x10^-⁴/s \|\| 0 to 0.24 mm/mm strain SSCC : austenitized & quenched \|\| tested at 20 °C (68 °F), 6.67x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSCC : austenitized & quenched \|\| tested at 250 °C (482 °F), 6.67x10^-⁴/s \|\| 0 to 0.21 mm/mm strain YS : solid \|\| -196 °C to 250 °C (-321 °F to 482 °F) YSC : solid \|\| -100 °C to 250 °C (-148 °F to 482 °F)

Fe - 18 Mn - 0.3 C (wt %)	SSC : 520 °C (968 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 2 minutes \|\| 0 to 0.58 mm/mm strain SSC : 520 °C (968 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 4 minutes \|\| 0 to 0.8 mm/mm strain SSC : 520 °C (968 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 8 minutes \|\| 0 to 0.15 mm/mm strain SSC : 550 °C (1022 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 2 minutes \|\| 0 to 0.89 mm/mm strain SSC : 550 °C (1022 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 4 minutes \|\| 0 to 0.16 mm/mm strain SSC : 550 °C (1022 °F) anneal \|\| tested at 20 °C (68 °F), 0.001/s, annealed for 8 minutes \|\| 0 to 0.242 mm/mm strain

Fe - 20 Mn - 10 Al - 0.5 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.235 mm/mm strain
Fe - 20 Mn - 10 Al - 1 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.433 mm/mm strain
Fe - 20 Mn - 10 Al - 1.5 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.14 mm/mm strain
Fe - 20 Mn - 11 Al - 1 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.247 mm/mm strain
Fe - 20 Mn - 13 Al - 0.75 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.41 mm/mm strain

Fe - 20 Mn - 10 Al - 5 Cr - 1.5 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.446 mm/mm strain SSC : annealed at 1100 °C (2012 °F), air cooled \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.284 mm/mm strain
Fe - 20 Mn - 11 Al - 5 Cr - 1.8 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.26 mm/mm strain
Fe - 20 Mn - 12 Al - 5 Cr - 1 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.242 mm/mm strain
Fe - 20 Mn - 13 Al - 5 Cr - 1.3 C (wt %)	D* : solid \|\| room temperature value SSC : annealed at 1100 °C (2012 °F), water quenched \|\| tested at 20 °C (68 °F), 0.00833/s \|\| 0 to 0.19 mm/mm strain

Fe - 3 Mn (wt %)	D : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) DLL : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) MTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) CTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) ST : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F)
Fe - 5 Mn (wt %)	D : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) DLL : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) MTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) CTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) ST : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F)
Fe - 5 Mn - 1.5 C (wt %)	D : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) DLL : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) MTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) CTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F)
Fe - 5 Mn - 4.2 C (wt %)	D : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) DLL : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) MTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) CTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F)
Fe - 10 Mn (wt %)	D : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) DLL : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) MTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) CTE : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F) ST : liquid \|\| 1527 °C to 1587 °C (2780 °F to 2888 °F)
Fe - 10 Mn - 1.6 C (wt %)	D : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) DLL : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) MTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) CTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F)
Fe - 10 Mn - 4.1 C (wt %)	D : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) DLL : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) MTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F) CTE : liquid \|\| 1414 °C to 1570 °C (2577 °F to 2858 °F)
Fe - 22 Mn (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value FSN : axial fatigue \|\| tested at 25 °C (77 °F), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles FSN : axial fatigue \|\| tested at -163 °C (-262 °F), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles
Fe - 22 Mn - 0.6 C (wt %)	D* : solid \|\| room temperature value SSC : austenitized at 1000 °C (1832 °F) & quenched \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.64 mm/mm strain SSC : austenitized at 1000 °C (1832 °F) & quenched \|\| tested at 70 °C (158 °F), 0.001/s \|\| 0 to 0.67 mm/mm strain SSC : austenitized at 1000 °C (1832 °F) & quenched \|\| tested at 120 °C (248 °F), 0.001/s \|\| 0 to 0.74 mm/mm strain SSC : austenitized at 1000 °C (1832 °F) & quenched \|\| tested at 170 °C (338 °F), 0.001/s \|\| 0 to 0.76 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 20 °C (68 °F), 0.001736/s \|\| 0 to 0.33 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 100 °C (212 °F), 0.001736/s \|\| 0 to 0.4 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 200 °C (392 °F), 0.001736/s \|\| 0 to 0.43 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 300 °C (572 °F), 0.001736/s \|\| 0 to 0.4 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 325 °C (617 °F), 0.001736/s \|\| 0 to 0.28 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 350 °C (662 °F), 0.001736/s \|\| 0 to 0.38 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 375 °C (707 °F), 0.001736/s \|\| 0 to 0.36 mm/mm strain SSC : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| tested at 400 °C (752 °F), 0.001736/s \|\| 0 to 0.39 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 0.41 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 100 °C (212 °F), 0.1/s \|\| 0 to 0.43 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 200 °C (392 °F), 0.1/s \|\| 0 to 0.43 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 300 °C (572 °F), 0.1/s \|\| 0 to 0.43 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 400 °C (752 °F), 0.1/s \|\| 0 to 0.44 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 500 °C (932 °F), 0.1/s \|\| 0 to 0.39 mm/mm strain SSCC : annealed at 1150 °C (2102 °F) \|\| tested at 600 °C (1112 °F), 0.1/s \|\| 0 to 0.43 mm/mm strain UTS : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F) YS : austenitized at 1000 °C (1832 °F) & quenched \|\| 20 °C to 170 °C (68 °F to 338 °F) %El : hot-rolled & salt bath quenched at 350 °C (662 °F) \|\| 20 °C to 400 °C (68 °F to 752 °F)
Fe - 24 Mn (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value FSN : axial fatigue \|\| tested at 25 °C (77 °F), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles FSN : axial fatigue \|\| tested at -163 °C (-262 °F), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles
Fe - 27 Mn - 10 Al - 1 C (wt %)	SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.88 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.88 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.89 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.9 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.9 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.88 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.89 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.88 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.89 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.81 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.84 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.84 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.85 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.86 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.87 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.87 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.87 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.87 mm/mm strain SSCC : forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.88 mm/mm strain
Fe - 30 Mn - 1 C (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) DLL : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) MTE : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) CTE : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) TC : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) TD : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F) SH : solid \|\| -269 °C to 27 °C (-452 °F to 81 °F)
Fe - 30 Mn - 3 Si - 3 Al (wt %)	D* : solid \|\| room temperature value SSC : austenitized & quenched \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.63 mm/mm strain SSC : austenitized & quenched \|\| tested at 70 °C (158 °F), 0.001/s \|\| 0 to 0.6 mm/mm strain SSC : austenitized & quenched \|\| tested at 120 °C (248 °F), 0.001/s \|\| 0 to 0.55 mm/mm strain SSC : austenitized & quenched \|\| tested at 170 °C (338 °F), 0.001/s \|\| 0 to 0.51 mm/mm strain
Fe - 35 Mn (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	SSC : 0.45 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.9 mm/mm strain SSC : 0.45 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.178 mm/mm strain SSC : 2 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.29 mm/mm strain SSC : 2 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.373 mm/mm strain SSC : 2.3 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.314 mm/mm strain SSC : 2.3 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.47 mm/mm strain SSC : 3.8 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.292 mm/mm strain SSC : 3.8 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.161 mm/mm strain SSC : 10.8 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.3 mm/mm strain SSC : 10.8 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.6 mm/mm strain SSC : 21 microns \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.278 mm/mm strain SSC : 21 microns \|\| tested at -180 °C (-292 °F), 0.001/s \|\| 0 to 0.58 mm/mm strain UTS* : Effect of grain size \|\| 0.45 microns \|\| room temperature value UTS* : Effect of grain size \|\| 2 microns \|\| room temperature value UTS* : Effect of grain size \|\| 2.3 microns \|\| room temperature value UTS* : Effect of grain size \|\| 3.8 microns \|\| room temperature value UTS* : Effect of grain size \|\| 10.8 microns \|\| room temperature value UTS* : Effect of grain size \|\| 21 microns \|\| room temperature value YS* : Effect of grain size \|\| 0.45 microns \|\| room temperature value YS* : Effect of grain size \|\| 2 microns \|\| room temperature value YS* : Effect of grain size \|\| 2.3 microns \|\| room temperature value YS* : Effect of grain size \|\| 3.8 microns \|\| room temperature value YS* : Effect of grain size \|\| 10.8 microns \|\| room temperature value YS* : Effect of grain size \|\| 21 microns \|\| room temperature value %El* : Effect of grain size \|\| 0.45 microns, uniform elongation \|\| room temperature value %El* : Effect of grain size \|\| 2 microns, uniform elongation \|\| room temperature value %El* : Effect of grain size \|\| 2.3 microns, uniform elongation \|\| room temperature value %El* : Effect of grain size \|\| 3.8 microns, uniform elongation \|\| room temperature value %El* : Effect of grain size \|\| 10.8 microns, uniform elongation \|\| room temperature value %El* : Effect of grain size \|\| 21 microns, uniform elongation \|\| room temperature value

Fe - 0.5 Au (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value YS : quenched from 1000 °C (1832 °F) \|\| -195 °C to 27 °C (-319 °F to 81 °F)

Fe - 8 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 20 Co (at %)	D : liquid \|\| 1525 °C to 1640 °C (2777 °F to 2984 °F) DLL : liquid \|\| 1525 °C to 1640 °C (2777 °F to 2984 °F) MTE : liquid \|\| 1525 °C to 1640 °C (2777 °F to 2984 °F) CTE : liquid \|\| 1525 °C to 1640 °C (2777 °F to 2984 °F)
Fe - 30 Co (at %)	D : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) DLL : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) MTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) CTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F)
Fe - 40 Co (at %)	D : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) DLL : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) MTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) CTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F)
Fe - 50 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) DLL : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) MTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) CTE : liquid \|\| 1427 °C to 1557 °C (2600 °F to 2835 °F) SSCC : disordered \|\| tested at -196.1 °C (-321.1 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at -173 °C (-280 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at -150 °C (-238 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at -103 °C (-154 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at -65 °C (-85 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at 25 °C (77 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at 120 °C (248 °F), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : ordered \|\| tested at -196.1 °C (-321.1 °F), 7.6x10^-⁵/s \|\| 0 to 0.49 mm/mm strain SSCC : ordered \|\| tested at -173 °C (-280 °F), 7.6x10^-⁵/s \|\| 0 to 0.415 mm/mm strain SSCC : ordered \|\| tested at -150 °C (-238 °F), 7.6x10^-⁵/s \|\| 0 to 0.42 mm/mm strain SSCC : ordered \|\| tested at -103 °C (-154 °F), 7.6x10^-⁵/s \|\| 0 to 0.43 mm/mm strain SSCC : ordered \|\| tested at -65 °C (-85 °F), 7.6x10^-⁵/s \|\| 0 to 0.43 mm/mm strain SSCC : ordered \|\| tested at 21 °C (70 °F), 7.6x10^-⁵/s \|\| 0 to 0.46 mm/mm strain SSCC : ordered \|\| tested at 103 °C (217 °F), 7.6x10^-⁵/s \|\| 0 to 0.5 mm/mm strain SSCC : ordered \|\| tested at 176 °C (349 °F), 7.6x10^-⁵/s \|\| 0 to 0.42 mm/mm strain SSCC : ordered \|\| tested at 307 °C (584 °F), 7.6x10^-⁵/s \|\| 0 to 0.62 mm/mm strain YSC : disordered \|\| -196 °C to 170 °C (-321 °F to 338 °F) YSC : ordered \|\| -196 °C to 315 °C (-321 °F to 599 °F) ST : liquid \|\| 1479 °C to 1550 °C (2694 °F to 2822 °F)

Fe₆₀Co₂₀Si₈B₁₂	D : solid \|\| 20 °C to 1082 °C (68 °F to 1979 °F) D : liquid \|\| 1160 °C to 1377 °C (2120 °F to 2510 °F) D : amorphous \|\| 20 °C to 451 °C (68 °F to 844 °F) DLL : solid \|\| 20 °C to 1082 °C (68 °F to 1979 °F) DLL : liquid \|\| 1160 °C to 1377 °C (2120 °F to 2510 °F) DLL : amorphous \|\| 20 °C to 451 °C (68 °F to 844 °F) MTE : solid \|\| 20 °C to 1082 °C (68 °F to 1979 °F) MTE : liquid \|\| 1160 °C to 1377 °C (2120 °F to 2510 °F) MTE : amorphous \|\| 20 °C to 451 °C (68 °F to 844 °F) CTE : solid \|\| 20 °C to 1082 °C (68 °F to 1979 °F) CTE : liquid \|\| 1160 °C to 1377 °C (2120 °F to 2510 °F) CTE : amorphous \|\| 20 °C to 451 °C (68 °F to 844 °F)

Fe - 10 Cr (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1532 °C to 1677 °C (2789 °F to 3051 °F) DLL : liquid \|\| 1532 °C to 1677 °C (2789 °F to 3051 °F) MTE : liquid \|\| 1532 °C to 1677 °C (2789 °F to 3051 °F) CTE : liquid \|\| 1532 °C to 1677 °C (2789 °F to 3051 °F) E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 20 Cr (at %)	D : liquid \|\| 1527 °C to 1677 °C (2780 °F to 3051 °F) DLL : liquid \|\| 1527 °C to 1677 °C (2780 °F to 3051 °F) MTE : liquid \|\| 1527 °C to 1677 °C (2780 °F to 3051 °F) CTE : liquid \|\| 1527 °C to 1677 °C (2780 °F to 3051 °F) Vis : liquid \|\| 1517 °C to 1627 °C (2762 °F to 2961 °F)
Fe - 40 Cr (at %)	D : liquid \|\| 1600 °C to 1677 °C (2912 °F to 3051 °F) DLL : liquid \|\| 1600 °C to 1677 °C (2912 °F to 3051 °F) MTE : liquid \|\| 1600 °C to 1677 °C (2912 °F to 3051 °F) CTE : liquid \|\| 1600 °C to 1677 °C (2912 °F to 3051 °F)

Fe - 1.67 Cu (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| not aged \|\| -196 °C to 27 °C (-321 °F to 81 °F) YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| aged 0.5 h \|\| -196 °C to 27 °C (-321 °F to 81 °F) YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| aged 1 h \|\| -196 °C to 27 °C (-321 °F to 81 °F) YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| aged 2 h \|\| -196 °C to 27 °C (-321 °F to 81 °F) YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| aged 3 h \|\| -196 °C to 27 °C (-321 °F to 81 °F) YS : quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F) \|\| aged 6.5 h \|\| -196 °C to 27 °C (-321 °F to 81 °F)
Fe - 20 Cu (at %)	D : liquid \|\| 1505 °C to 1650 °C (2741 °F to 3002 °F) DLL : liquid \|\| 1505 °C to 1650 °C (2741 °F to 3002 °F) MTE : liquid \|\| 1505 °C to 1650 °C (2741 °F to 3002 °F) CTE : liquid \|\| 1505 °C to 1650 °C (2741 °F to 3002 °F) ST : liquid \|\| 1463 °C to 1650 °C (2665 °F to 3002 °F)
Fe - 40 Cu (at %)	D : liquid \|\| 1495 °C to 1650 °C (2723 °F to 3002 °F) DLL : liquid \|\| 1495 °C to 1650 °C (2723 °F to 3002 °F) MTE : liquid \|\| 1495 °C to 1650 °C (2723 °F to 3002 °F) CTE : liquid \|\| 1495 °C to 1650 °C (2723 °F to 3002 °F)

60 Fe - 20 Co - 20 Cu (at %)	D : liquid \|\| 1438 °C to 1665 °C (2620 °F to 3029 °F) DLL : liquid \|\| 1438 °C to 1665 °C (2620 °F to 3029 °F) MTE : liquid \|\| 1438 °C to 1665 °C (2620 °F to 3029 °F) CTE : liquid \|\| 1438 °C to 1665 °C (2620 °F to 3029 °F) ST : liquid \|\| 1438 °C to 1665 °C (2620 °F to 3029 °F)

Fe - 3 Ir (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)

Fe - 0.5 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E* : solid \|\| martensite \|\| room temperature value G* : solid \|\| martensite \|\| room temperature value v* : solid \|\| martensite \|\| room temperature value K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1535 °C (-458 °F to 2795 °F) RHO : liquid \|\| 1537 °C to 1727 °C (2798 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1535 °C (-458 °F to 2795 °F) SIGMA : liquid \|\| 1537 °C to 1727 °C (2798 °F to 3141 °F)
Fe - 1 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E* : solid \|\| ferrite \|\| room temperature value E* : solid \|\| martensite \|\| room temperature value G* : solid \|\| ferrite \|\| room temperature value G* : solid \|\| martensite \|\| room temperature value v* : solid \|\| ferrite \|\| room temperature value v* : solid \|\| martensite \|\| room temperature value K* : solid \|\| ferrite \|\| room temperature value K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1530 °C (-458 °F to 2786 °F) RHO : liquid \|\| 1535 °C to 1727 °C (2795 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1530 °C (-458 °F to 2786 °F) SIGMA : liquid \|\| 1535 °C to 1727 °C (2795 °F to 3141 °F)
Fe - 3 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| ferrite \|\| -197 °C to 200 °C (-323 °F to 392 °F) E* : solid \|\| martensite \|\| room temperature value G : solid \|\| ferrite \|\| -197 °C to 200 °C (-323 °F to 392 °F) G* : solid \|\| martensite \|\| room temperature value v : solid \|\| ferrite \|\| -197 °C to 200 °C (-323 °F to 392 °F) v* : solid \|\| martensite \|\| room temperature value K : solid \|\| ferrite \|\| -197 °C to 200 °C (-323 °F to 392 °F) K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 327 °C (-458 °F to 621 °F) RHO : solid \|\| austenite \|\| 722 °C to 1518 °C (1331 °F to 2764 °F) RHO : liquid \|\| 1527 °C to 1727 °C (2780 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 327 °C (-458 °F to 621 °F) SIGMA : solid \|\| austenite \|\| 722 °C to 1518 °C (1331 °F to 2764 °F) SIGMA : liquid \|\| 1527 °C to 1727 °C (2780 °F to 3141 °F)
Fe - 5 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E* : solid \|\| martensite \|\| room temperature value G* : solid \|\| martensite \|\| room temperature value v* : solid \|\| martensite \|\| room temperature value K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 762 °C (-458 °F to 1404 °F) RHO : solid \|\| austenite \|\| 652 °C to 1509 °C (1205 °F to 2748 °F) RHO : liquid \|\| 1520 °C to 1727 °C (2768 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 762 °C (-458 °F to 1404 °F) SIGMA : solid \|\| austenite \|\| 652 °C to 1509 °C (1205 °F to 2748 °F) SIGMA : liquid \|\| 1520 °C to 1727 °C (2768 °F to 3141 °F)
Fe - 10 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E* : solid \|\| martensite \|\| room temperature value G* : solid \|\| martensite \|\| room temperature value v* : solid \|\| martensite \|\| room temperature value K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 692 °C (-458 °F to 1278 °F) RHO : solid \|\| austenite \|\| 497 °C to 1489 °C (926 °F to 2712 °F) RHO : liquid \|\| 1504 °C to 1727 °C (2739 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 692 °C (-458 °F to 1278 °F) SIGMA : solid \|\| austenite \|\| 497 °C to 1489 °C (926 °F to 2712 °F) SIGMA : liquid \|\| 1504 °C to 1727 °C (2739 °F to 3141 °F)
Fe - 15 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 647 °C (-458 °F to 1197 °F) RHO : solid \|\| austenite \|\| 362 °C to 1475 °C (683 °F to 2687 °F) RHO : liquid \|\| 1490 °C to 1727 °C (2714 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 647 °C (-458 °F to 1197 °F) SIGMA : solid \|\| austenite \|\| 362 °C to 1475 °C (683 °F to 2687 °F) SIGMA : liquid \|\| 1490 °C to 1727 °C (2714 °F to 3141 °F)
Fe - 20 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1500 °C to 1677 °C (2732 °F to 3051 °F) DLL : liquid \|\| 1500 °C to 1677 °C (2732 °F to 3051 °F) MTE : liquid \|\| 1500 °C to 1677 °C (2732 °F to 3051 °F) CTE : liquid \|\| 1500 °C to 1677 °C (2732 °F to 3051 °F) E* : solid \|\| martensite \|\| room temperature value G* : solid \|\| martensite \|\| room temperature value v* : solid \|\| martensite \|\| room temperature value K* : solid \|\| martensite \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 602 °C (-458 °F to 1116 °F) RHO : solid \|\| austenite \|\| 262 °C to 1464 °C (503 °F to 2667 °F) RHO : liquid \|\| 1478 °C to 1727 °C (2692 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 602 °C (-458 °F to 1116 °F) SIGMA : solid \|\| austenite \|\| 262 °C to 1464 °C (503 °F to 2667 °F) SIGMA : liquid \|\| 1478 °C to 1727 °C (2692 °F to 3141 °F)
Fe - 25 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 537 °C (-458 °F to 999 °F) RHO : solid \|\| austenite \|\| 122 °C to 1455 °C (251 °F to 2651 °F) RHO : liquid \|\| 1468 °C to 1727 °C (2674 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 537 °C (-458 °F to 999 °F) SIGMA : solid \|\| austenite \|\| 122 °C to 1455 °C (251 °F to 2651 °F) SIGMA : liquid \|\| 1468 °C to 1727 °C (2674 °F to 3141 °F)
Fe - 30 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1475 °C to 1677 °C (2687 °F to 3051 °F) DLL : liquid \|\| 1475 °C to 1677 °C (2687 °F to 3051 °F) MTE : liquid \|\| 1475 °C to 1677 °C (2687 °F to 3051 °F) CTE : liquid \|\| 1475 °C to 1677 °C (2687 °F to 3051 °F) TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| martensite \|\| -272 °C to 467 °C (-458 °F to 873 °F) RHO : solid \|\| austenite \|\| -23 °C to 467 °C (-10 °F to 873 °F) RHO : liquid \|\| 1459 °C to 1727 °C (2658 °F to 3141 °F) SIGMA : solid \|\| martensite \|\| -272 °C to 467 °C (-458 °F to 873 °F) SIGMA : solid \|\| austenite \|\| -23 °C to 467 °C (-10 °F to 873 °F) SIGMA : liquid \|\| 1459 °C to 1727 °C (2658 °F to 3141 °F)
Fe - 34 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	SSC : deformed 70% at 25 °C (77 °F) \|\| tested at -78 °C (-108 °F), 6.7x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : deformed 70% at 450 °C (842 °F) \|\| tested at -196 °C (-320.8 °F), 6.7x10^-⁴/s \|\| 0 to 0.115 mm/mm strain SSC : deformed 70% at 450 °C (842 °F) \|\| tested at 22 °C (72 °F), 6.7x10^-⁴/s \|\| 0 to 0.42 mm/mm strain ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F)
Fe - 35 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) RHO : liquid \|\| 1451 °C to 1727 °C (2644 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) SIGMA : liquid \|\| 1451 °C to 1727 °C (2644 °F to 3141 °F)
Fe - 40 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) DLL : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) MTE : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) CTE : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) RHO : liquid \|\| 1445 °C to 1727 °C (2633 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) SIGMA : liquid \|\| 1445 °C to 1727 °C (2633 °F to 3141 °F)
Fe - 45 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1433 °C (-458 °F to 2611 °F) RHO : liquid \|\| 1440 °C to 1727 °C (2624 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1433 °C (-458 °F to 2611 °F) SIGMA : liquid \|\| 1440 °C to 1727 °C (2624 °F to 3141 °F)
Fe - 50 Ni (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1431 °C (-458 °F to 2608 °F) RHO : liquid \|\| 1435 °C to 1727 °C (2615 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1431 °C (-458 °F to 2608 °F) SIGMA : liquid \|\| 1435 °C to 1727 °C (2615 °F to 3141 °F)

Fe₆₅Cu₂₀Ni₁₅	D : liquid \|\| 1329 °C to 1455 °C (2424 °F to 2651 °F) DLL : liquid \|\| 1329 °C to 1455 °C (2424 °F to 2651 °F) MTE : liquid \|\| 1329 °C to 1455 °C (2424 °F to 2651 °F) CTE : liquid \|\| 1329 °C to 1455 °C (2424 °F to 2651 °F)
Fe₄₈Cu₂₀Ni₃₂	D : liquid \|\| 1327 °C to 1425 °C (2420 °F to 2597 °F) DLL : liquid \|\| 1327 °C to 1425 °C (2420 °F to 2597 °F) MTE : liquid \|\| 1327 °C to 1425 °C (2420 °F to 2597 °F) CTE : liquid \|\| 1327 °C to 1425 °C (2420 °F to 2597 °F)

Fe₇₂Ni₁₈Cr₁₀	D : liquid \|\| 1475 °C to 1675 °C (2687 °F to 3047 °F) DLL : liquid \|\| 1475 °C to 1675 °C (2687 °F to 3047 °F) MTE : liquid \|\| 1475 °C to 1675 °C (2687 °F to 3047 °F) CTE : liquid \|\| 1475 °C to 1675 °C (2687 °F to 3047 °F)
Fe₆₄Ni₁₆Cr₂₀	D : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) DLL : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) MTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) CTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) Vis : liquid \|\| 1515 °C to 1590 °C (2759 °F to 2894 °F)
Fe₆₃Ni₂₇Cr₁₀	D : liquid \|\| 1461 °C to 1661 °C (2662 °F to 3022 °F) DLL : liquid \|\| 1461 °C to 1661 °C (2662 °F to 3022 °F) MTE : liquid \|\| 1461 °C to 1661 °C (2662 °F to 3022 °F) CTE : liquid \|\| 1461 °C to 1661 °C (2662 °F to 3022 °F)
Fe₅₆Ni₂₄Cr₂₀	D : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) DLL : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) MTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) CTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F)
Fe₅₄Ni₃₆Cr₁₀	D : liquid \|\| 1449 °C to 1649 °C (2640 °F to 3000 °F) DLL : liquid \|\| 1449 °C to 1649 °C (2640 °F to 3000 °F) MTE : liquid \|\| 1449 °C to 1649 °C (2640 °F to 3000 °F) CTE : liquid \|\| 1449 °C to 1649 °C (2640 °F to 3000 °F)
Fe₄₈Ni₃₂Cr₂₀	D : liquid \|\| 1425 °C to 1625 °C (2597 °F to 2957 °F) DLL : liquid \|\| 1425 °C to 1625 °C (2597 °F to 2957 °F) MTE : liquid \|\| 1425 °C to 1625 °C (2597 °F to 2957 °F) CTE : liquid \|\| 1425 °C to 1625 °C (2597 °F to 2957 °F) Vis : liquid \|\| 1400 °C to 1585 °C (2552 °F to 2885 °F)
Fe₄₈Ni₁₂Cr₄₀	D : liquid \|\| 1525 °C to 1725 °C (2777 °F to 3137 °F) DLL : liquid \|\| 1525 °C to 1725 °C (2777 °F to 3137 °F) MTE : liquid \|\| 1525 °C to 1725 °C (2777 °F to 3137 °F) CTE : liquid \|\| 1525 °C to 1725 °C (2777 °F to 3137 °F)

Fe - 3 Pt (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 5 Pt (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 10 Pt (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)

Fe - 3 Re (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 6 Re (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)

Fe - 3 Rh (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 6 Rh (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 8 Rh (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)

Fe - 6 Ru (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)
Fe - 9 Ru (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) G : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) v : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F) K : solid \|\| -197 °C to 200 °C (-323 °F to 392 °F)

Fe - 1 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -73 °C to 700 °C (-100 °F to 1292 °F) DLL : solid \|\| -73 °C to 700 °C (-100 °F to 1292 °F) MTE : solid \|\| -73 °C to 700 °C (-100 °F to 1292 °F) CTE : solid \|\| -73 °C to 700 °C (-100 °F to 1292 °F) TC : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 770 °C (68 °F to 1418 °F) RHO : solid \|\| -248 °C to 465 °C (-415 °F to 869 °F) SIGMA : solid \|\| -248 °C to 465 °C (-415 °F to 869 °F)
Fe - 1.8 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -73 °C to 675 °C (-100 °F to 1247 °F) DLL : solid \|\| -73 °C to 675 °C (-100 °F to 1247 °F) MTE : solid \|\| -73 °C to 675 °C (-100 °F to 1247 °F) CTE : solid \|\| -73 °C to 675 °C (-100 °F to 1247 °F) TC : solid \|\| 20 °C to 905 °C (68 °F to 1661 °F) TD : solid \|\| 20 °C to 675 °C (68 °F to 1247 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F)
Fe - 2.8 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -73 °C to 760 °C (-100 °F to 1400 °F) DLL : solid \|\| -73 °C to 760 °C (-100 °F to 1400 °F) MTE : solid \|\| -73 °C to 760 °C (-100 °F to 1400 °F) CTE : solid \|\| -73 °C to 760 °C (-100 °F to 1400 °F) E* : non-orientated \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 930 °C (68 °F to 1706 °F) TD : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) SSC : 0.35 mm (0.0138 inch) thick sheet, 0.004/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.187 mm/mm strain UTS* : non-orientated \|\| room temperature value YS* : non-orientated \|\| room temperature value %El* : non-orientated \|\| room temperature value FEN : non-orientated, 0.35 mm (0.0138 inch) thick sheet \|\| tested at 20 °C (68 °F), R = 0.0, axial, 0.01/s strain rate, total strain amplitude \|\| 75 cycles to 2x10⁴ cycles FEN : non-orientated, 0.35 mm (0.0138 inch) thick sheet \|\| tested at 20 °C (68 °F), R = 0.0, axial, 0.01/s strain rate, elastic strain amplitude \|\| 75 cycles to 2x10⁴ cycles FEN : non-orientated, 0.35 mm (0.0138 inch) thick sheet \|\| tested at 20 °C (68 °F), R = 0.0, axial, 0.01/s strain rate, plastic strain amplitude \|\| 75 cycles to 2x10⁴ cycles
Fe - 3.9 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -73 °C to 775 °C (-100 °F to 1427 °F) DLL : solid \|\| -73 °C to 775 °C (-100 °F to 1427 °F) MTE : solid \|\| -73 °C to 775 °C (-100 °F to 1427 °F) CTE : solid \|\| -73 °C to 775 °C (-100 °F to 1427 °F) TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F) TD : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F)
Fe - 4.4 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -73 °C to 770 °C (-100 °F to 1418 °F) DLL : solid \|\| -73 °C to 770 °C (-100 °F to 1418 °F) MTE : solid \|\| -73 °C to 770 °C (-100 °F to 1418 °F) CTE : solid \|\| -73 °C to 770 °C (-100 °F to 1418 °F) TC : solid \|\| 20 °C to 925 °C (68 °F to 1697 °F) TD : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F) SH : solid \|\| 20 °C to 750 °C (68 °F to 1382 °F)
Fe - 8 Si (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| -73 °C to 705 °C (-100 °F to 1301 °F) DLL : solid \|\| -73 °C to 705 °C (-100 °F to 1301 °F) MTE : solid \|\| -73 °C to 705 °C (-100 °F to 1301 °F) CTE : solid \|\| -73 °C to 705 °C (-100 °F to 1301 °F) TC : solid \|\| annealed \|\| 20 °C to 924 °C (68 °F to 1695 °F)
Fe - 10 Si (wt %) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) DLL : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) MTE : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) CTE : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) TC : solid \|\| annealed \|\| 20 °C to 924 °C (68 °F to 1695 °F)
Fe - 12 Si (wt %) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 910 °C (32 °F to 1670 °F) DLL : solid \|\| 0 °C to 910 °C (32 °F to 1670 °F) MTE : solid \|\| 0 °C to 910 °C (32 °F to 1670 °F)
Fe - 15 Si (wt %) (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value RHO : solid \|\| -21 °C to 1200 °C (-6 °F to 2192 °F) SIGMA : solid \|\| -21 °C to 1200 °C (-6 °F to 2192 °F)
Fe - 20 Si (wt %)	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F)
Fe - 38 Si (wt %)	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F)
Fe - 41 Si (wt %) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) DLL : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) MTE : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) CTE : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F)
Fe - 44 Si (wt %)	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F)
Fe - 48 Si (wt %)	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 920 °C (68 °F to 1688 °F)
Fe - 50 Si (wt %) (some datasets are for temperatures below 20 °C)	D : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) DLL : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) MTE : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F) CTE : solid \|\| 0 °C to 627 °C (32 °F to 1160 °F)
Fe - 53 Si (wt %)	D : solid \|\| alpha phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| alpha phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| beta phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| alpha phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| beta phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| alpha phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| beta phase \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Fe - 58 Si (wt %)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Fe - 69 Si (wt %)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Fe - 75 Si (wt %)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)

Fe - 6 Ni - 0.2 C (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	YS : tempered martensite \|\| tempered at 250 °C (482 °F) \|\| -196 °C to 22 °C (-321 °F to 72 °F) YSC : tempered martensite \|\| tempered at 250 °C (482 °F) \|\| -196 °C to 22 °C (-321 °F to 72 °F)
Fe - 11 Ni - 6.5 Si - 2.5 Cr (wt %)	SSCC : 5x10^-⁴/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.838 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.878 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 5x10^-⁴/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 0.005/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.847 mm/mm strain SSCC : 0.005/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.863 mm/mm strain SSCC : 0.005/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.85 mm/mm strain SSCC : 0.005/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.877 mm/mm strain SSCC : 0.05/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.818 mm/mm strain SSCC : 0.05/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.05/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.829 mm/mm strain SSCC : 0.05/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.841 mm/mm strain

TRIP 590 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : quenched & partitioned \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, partitioned at 350 °C (662 °F) \|\| 0 to 0.11 mm/mm strain SSC : quenched & partitioned \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, partitioned at 400 °C (752 °F) \|\| 0 to 0.18 mm/mm strain SSC : quenched & partitioned \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, partitioned at 450 °C (842 °F) \|\| 0 to 0.21 mm/mm strain SSC : quenched & tempered \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, tempered at 350 °C (662 °F) \|\| 0 to 0.6 mm/mm strain SSC : quenched & tempered \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, tempered at 400 °C (752 °F) \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at 20 °C (68 °F), 5.6x10^-⁴/s, tempered at 450 °C (842 °F) \|\| 0 to 0.6 mm/mm strain
TRIP 600 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain
TRIP 700 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) DLL : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) MTE : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) CTE : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : hot-rolled, 0.033/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.175 mm/mm strain SSC : cold-rolled, 0.033/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.224 mm/mm strain SSC : as-received, 800/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.145 mm/mm strain FEN : hot-rolled \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁵ cycles FEN : cold-rolled \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 1x10⁵ cycles FSN : hot-rolled \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-rolled \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles
TRIP 780 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) DLL : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) MTE : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) CTE : solid \|\| -8 °C to 741 °C (17 °F to 1366 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate, YS of 444 MPa (64.4 ksi) \|\| 0 to 0.225 mm/mm strain SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate, YS of 455 MPa (66.0 ksi) \|\| 0 to 0.165 mm/mm strain SSC : as-delivered condition \|\| tested at 20 °C (68 °F), YS of 590 MPa (85.6 ksi), 0.001/s \|\| 0 to 0.25 mm/mm strain
TRIP 800 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : 15% austenite before testing \|\| tested at 20 °C (68 °F), unknown strain rate, YS of 444 MPa (64.4 ksi) \|\| 0 to 0.225 mm/mm strain SSC : 18% austenite before testing, 0.0067/s \|\| tested at 20 °C (68 °F), YS of 400 MPa (58.0 ksi) \|\| 0 to 0.24 mm/mm strain
TRIP 980	D* : solid \|\| room temperature value SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.87 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.845 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.89 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.88 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.86 mm/mm strain UTS : continuous cast slabs \|\| longitudinal \|\| 600 °C to 1300 °C (1112 °F to 2372 °F) UTS : continuous cast slabs \|\| transverse \|\| 600 °C to 1300 °C (1112 °F to 2372 °F)
TRIP 1000 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -44 °C to 639 °C (-47 °F to 1182 °F) DLL : solid \|\| -44 °C to 639 °C (-47 °F to 1182 °F) MTE : solid \|\| -44 °C to 639 °C (-47 °F to 1182 °F) CTE : solid \|\| -44 °C to 639 °C (-47 °F to 1182 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 3.3x10^-⁶/s \|\| 0 to 0.29 mm/mm strain SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 3.3x10^-²/s \|\| 0 to 0.21 mm/mm strain SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 1/s \|\| 0 to 0.16 mm/mm strain SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 10/s \|\| 0 to 0.16 mm/mm strain SSC : austempered & quenched \|\| tested at 20 °C (68 °F), 1000/s \|\| 0 to 0.15 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 3.3x10^-⁶/s \|\| 0 to 0.21 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 3.3x10^-²/s \|\| 0 to 0.18 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 1/s \|\| 0 to 0.16 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 10/s \|\| 0 to 0.14 mm/mm strain SSC : austempered & air-cooled \|\| tested at 20 °C (68 °F), 1000/s \|\| 0 to 0.15 mm/mm strain
DUAL-TEN 590 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.188 mm/mm strain
DUAL-TEN 600 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.188 mm/mm strain
DUAL-TEN 780 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.145 mm/mm strain
DUAL-TEN 800 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.145 mm/mm strain
HSLA 100	D* : solid \|\| room temperature value SSCC : quenched & tempered \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.37 mm/mm strain
H220LAD (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : hot-dipped galvanized sheet \|\| tested at 20 °C (68 °F), R = -1, bending, longitudinal, maximum stress \|\| 6.8x10⁴ cycles to 1x10⁷ cycles
HSLA 280 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : hot dipped galvanized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain
HSLA 340 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.21 mm/mm strain SSC : hot dipped galvanized \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.13 mm/mm strain
H380LAD (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) FSN : hot-dipped galvanized sheet \|\| tested at 20 °C (68 °F), R = -1, bending, longitudinal, maximum stress \|\| 6.8x10⁴ cycles to 1x10⁷ cycles
HSLA 550 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain
DP 450 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : 1.2 mm (0.0472 inch) sheet, 7 vol % martensite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain UTS* : 1.2 mm (0.0472 inch) sheet, 7 vol % martensite \|\| room temperature value YS* : 1.2 mm (0.0472 inch) sheet, 7 vol % martensite \|\| room temperature value %El* : 1.2 mm (0.0472 inch) sheet, 7 vol % martensite \|\| room temperature value
DP 500 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSC : as-delivered condition, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain SSC : electrogalvanized DI-FORM T500, Arcelor Mittal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.17 mm/mm strain UTS* : bare DI-FORM T500, Arcelor Mittal \|\| room temperature value UTS* : electrogalvanized DI-FORM T500, Arcelor Mittal \|\| room temperature value YS* : bare DI-FORM T500, Arcelor Mittal \|\| room temperature value YS* : electrogalvanized DI-FORM T500, Arcelor Mittal \|\| room temperature value %El* : bare DI-FORM T500, Arcelor Mittal \|\| room temperature value %El* : electrogalvanized DI-FORM T500, Arcelor Mittal \|\| room temperature value
DP 550 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : HF 70Y80T, Arcelor Mittal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.12 mm/mm strain UTS* : bare HF 70Y80T, Arcelor Mittal \|\| room temperature value YS* : bare HF 70Y80T, Arcelor Mittal \|\| room temperature value %El* : bare HF 70Y80T, Arcelor Mittal \|\| room temperature value
DP 590 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), 0.001/s, YS of 500 MPa (72.5 ksi) \|\| 0 to 0.175 mm/mm strain SSC : DI FORM T590, Arcelor Mittal \|\| tested at 20 °C (68 °F), uncoated, unknown strain rate \|\| 0 to 0.16 mm/mm strain SSC : DI FORM T590, Arcelor Mittal \|\| tested at 20 °C (68 °F), hot-dip galvannealed, unknown strain rate \|\| 0 to 0.146 mm/mm strain UTS* : bare DI FORM T590, Arcelor Mittal \|\| room temperature value UTS* : hot-dip-galvannealed DI FORM T590, Arcelor Mittal \|\| room temperature value YS* : bare DI FORM T590T, Arcelor Mittal \|\| room temperature value YS* : hot-dip-galvannealed DI FORM T590T, Arcelor Mittal \|\| room temperature value %El* : bare DI FORM T590, Arcelor Mittal \|\| room temperature value %El* : hot-dip-galvannealed DI FORM T590, Arcelor Mittal \|\| room temperature value
DP 600 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : galvannealed sheet \|\| tested at 20 °C (68 °F), 3x10^-⁴/s, YS of 360 MPa (52.2 ksi) \|\| 0 to 0.11 mm/mm strain SSC : DI FORM T600, Arcelor Mittal \|\| tested at 20 °C (68 °F), uncoated, unknown strain rate \|\| 0 to 0.14 mm/mm strain SSC : DI FORM T600, Arcelor Mittal \|\| tested at 20 °C (68 °F), hot-dip galvanized, unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : 1.6 mm (0.063 inch) sheet, 23 vol % martensite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.164 mm/mm strain UTS* : bare DI FORM T600, Arcelor Mittal \|\| room temperature value UTS* : hot-dip galvanized DI FORM T600, Arcelor Mittal \|\| room temperature value UTS* : 1.6 mm (0.063 inch) sheet, 23 vol % martensite \|\| room temperature value YS* : bare DI FORM T600, Arcelor Mittal \|\| room temperature value YS* : hot-dip galvanized DI FORM T600, Arcelor Mittal \|\| room temperature value %El* : bare DI FORM T600, Arcelor Mittal \|\| room temperature value %El* : hot-dip galvanized DI FORM T600, Arcelor Mittal \|\| room temperature value %El* : 1.6 mm (0.063 inch) sheet, 23 vol % martensite \|\| room temperature value RHO : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) SIGMA : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) RPB : 1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) RPB : 1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) RPB : 1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) RPB : 1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) AP : 1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) AP : 1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) AP : 1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) AP : 1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) BH : 1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) BH : 1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) BH : 1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) BH : 1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) HB : 1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) HB : 1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) HB : 1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) HB : 1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) CL : 1.6 mm (0.063 inch) thick sheet \|\| tested at 20 °C (68 °F), 280 kHz
DP 690 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : HF 80Y100T, Arcelor Mittal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.1 mm/mm strain UTS* : bare HF 80Y100T, Arcelor Mittal \|\| room temperature value YS* : bare HF 80Y100T, Arcelor Mittal \|\| room temperature value %El* : bare HF 80Y100T, Arcelor Mittal \|\| room temperature value RHO : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) SIGMA : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F)
DP 780 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition \|\| tested at 20 °C (68 °F), unknown strain rate, YS of 420 MPa (60.9 ksi) \|\| 0 to 0.16 mm/mm strain SSC : as-delivered condition \|\| tested at 20 °C (68 °F), 0.001/s, YS of 550 MPa (79.8 ksi) \|\| 0 to 0.117 mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, as-quenched \|\| 0 to 0.29 mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80% \|\| 0 to 3.1x10^-³ mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80%, intercritical annealed at 780 °C (1436 °F) \|\| 0 to 0.78 mm/mm strain
DP 800 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : 1.25 mm (0.0492 inch) sheet, 54 vol % martensite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain SSC : 1.2 mm (0.0472 inch) sheet, 30 vol % martensite \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.13 mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, as-quenched \|\| 0 to 0.29 mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80% \|\| 0 to 3.1x10^-³ mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80%, intercritical annealed at 800 °C (1472 °F) \|\| 0 to 0.63 mm/mm strain UTS* : 1.25 mm (0.0492 inch) sheet, 54 vol % martensite \|\| room temperature value UTS* : 1.2 mm (0.0472 inch) sheet, 30 vol % martensite \|\| room temperature value YS* : 1.25 mm (0.0492 inch) sheet, 54 vol % martensite \|\| room temperature value %El* : 1.25 mm (0.0492 inch) sheet, 54 vol % martensite \|\| room temperature value %El* : 1.2 mm (0.0472 inch) sheet, 30 vol % martensite \|\| room temperature value
DP 820 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, as-quenched \|\| 0 to 0.29 mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80% \|\| 0 to 3.1x10^-³ mm/mm strain SSC : Huang et. al. \|\| tested at 20 °C (68 °F), 0.003/s, reduced 80%, intercritical annealed at 820 °C (1508 °F) \|\| 0 to 0.5 mm/mm strain
DP 965 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : DI FORM 140T, Arcelor Mittal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.76 mm/mm strain UTS* : bare DI FORM 140T, Arcelor Mittal \|\| room temperature value YS* : bare DI FORM 140T, Arcelor Mittal \|\| room temperature value %El* : bare DI FORM 140T, Arcelor Mittal \|\| room temperature value
DP 980 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : 26% by volume martensite \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.126 mm/mm strain SSC : 30% by volume martensite \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.76 mm/mm strain SSC : 38% by volume martensite \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.85 mm/mm strain SSC : 49% by volume martensite \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.11 mm/mm strain SSC : 1.4 mm (0.0551 inch) thick, hot-dip galvannealed sheet \|\| tested at 25 °C (77 °F), 2x10^-⁴/s \|\| 0 to 0.71 mm/mm strain SSC : 1.4 mm (0.0551 inch) thick, hot-dip galvannealed sheet \|\| tested at 100 °C (212 °F), 2x10^-⁴/s \|\| 0 to 0.87 mm/mm strain SSC : 1.4 mm (0.0551 inch) thick, hot-dip galvannealed sheet \|\| tested at 175 °C (347 °F), 2x10^-⁴/s \|\| 0 to 0.95 mm/mm strain SSC : 1.4 mm (0.0551 inch) thick, hot-dip galvannealed sheet \|\| tested at 250 °C (482 °F), 2x10^-⁴/s \|\| 0 to 0.88 mm/mm strain FSN : as-received \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 750 cycles to 1x10⁸ cycles FSN : welded joints \|\| tested at 20 °C (68 °F), R = 0.1, axial, MIG weld, stress range \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : welded joints \|\| tested at 20 °C (68 °F), R = 0.1, axial, MAG weld, stress range \|\| 2x10⁴ cycles to 1.7x10⁶ cycles RHO : solid \|\| 20 °C to 950 °C (68 °F to 1742 °F) SIGMA : solid \|\| 20 °C to 950 °C (68 °F to 1742 °F)
QP 980 (3GAHSS) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 25 °C (77 °F), 2x10^-⁴/s \|\| 0 to 0.17 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 100 °C (212 °F), 2x10^-⁴/s \|\| 0 to 0.138 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 175 °C (347 °F), 2x10^-⁴/s \|\| 0 to 0.21 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 250 °C (482 °F), 2x10^-⁴/s \|\| 0 to 0.226 mm/mm strain SSCC : 11.5% retained austenite \|\| tested at 20 °C (68 °F), 0.003/s \|\| 0 to 0.17 mm/mm strain
QP 1180	SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 25 °C (77 °F), 2x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 100 °C (212 °F), 2x10^-⁴/s \|\| 0 to 0.52 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 175 °C (347 °F), 2x10^-⁴/s \|\| 0 to 0.67 mm/mm strain SSC : 1 mm (0.0394 inch) thick, hot-dip galvannealed sheet \|\| tested at 250 °C (482 °F), 2x10^-⁴/s \|\| 0 to 0.15 mm/mm strain
DQSK (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-delivered condition, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain
EDDS (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : electro-galvanneal, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : electro-galvanized, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : hot dipped galvanized, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.26 mm/mm strain SSC : hot dipped galvanneal, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : cold-rolled, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain
DDS (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : electro-galvanneal, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : hot dipped galvanneal, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain
DS Type B (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : electro-galvanized, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : cold-rolled, United States Steel \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain
FB 590	D* : solid \|\| room temperature value FSN : base metal \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 2.4x10⁴ cycles to 1x10⁹ cycles FSN : weld \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 3x10⁴ cycles to 1x10⁹ cycles
FB 780	D* : solid \|\| room temperature value E* : solid \|\| room temperature value FSN : base metal \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 1.4x10⁴ cycles to 1.3x10⁹ cycles FSN : weld \|\| tested at 20 °C (68 °F), R = -1, ultrasonic, maximum stress \|\| 3x10⁴ cycles to 1.16x10⁹ cycles
S700	FSN : weld \|\| tested at 20 °C (68 °F), R = 0.1, axial, as-weld, stress range \|\| 3x10⁴ cycles to 2x10⁷ cycles FSN : weld \|\| tested at 20 °C (68 °F), R = 0.1, axial, HFMI treated, stress range \|\| 6x10⁴ cycles to 2x10⁷ cycles FSN : weld \|\| tested at 20 °C (68 °F), R = 0.5, axial, HFMI treated, stress range \|\| 3x10⁴ cycles to 2x10⁷ cycles
800DH	D* : solid \|\| room temperature value SSC : as-received, 1x10^-⁴/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.135 mm/mm strain SSC : as-received, 0.01/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.124 mm/mm strain SSC : as-received, 0.5/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.96 mm/mm strain SSC : as-received, 800/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.117 mm/mm strain
980 XG3	D* : solid \|\| room temperature value SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 0.01/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 0.1/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 1/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 10/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 100/s \|\| 0 to 1 mm/mm strain SSC : mixture of ferrite, martensite & austenite, United States Steel \|\| tested at 20 °C (68 °F), 1000/s \|\| 0 to 1 mm/mm strain
55SiCrVNb	D* : solid \|\| room temperature value SSC : austempered at 240 °C (464 °F) \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.86 mm/mm strain SSC : austempered at 280 °C (536 °F) \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.42 mm/mm strain SSC : austempered at 320 °C (608 °F) \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.34 mm/mm strain SSC : austempered at 360 °C (680 °F) \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : austempered at 400 °C (752 °F) \|\| tested at 20 °C (68 °F), 2.5x10^-⁴/s \|\| 0 to 0.1 mm/mm strain

API 5ST CT80 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : as-received, ASTM 13 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : normalized at 800 °C (1472 °F), ASTM 13 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : annealed at 860 °C (1580 °F), ASTM 10 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : annealed at 941 °C (1725 °F), ASTM 8 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain

S350 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 20 °C (68 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 100 °C (212 °F), 7x10^-⁵/s \|\| 0 to 0.124 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 200 °C (392 °F), 7x10^-⁵/s \|\| 0 to 0.14 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 300 °C (572 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 350 °C (662 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 400 °C (752 °F), 7x10^-⁵/s \|\| 0 to 0.172 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 500 °C (932 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 600 °C (1112 °F), 7x10^-⁵/s \|\| 0 to 0.2 mm/mm strain SSC : cold-rolled, annealed at 730 °C (1346 °F) \|\| tested at 700 °C (1292 °F), 7x10^-⁵/s \|\| 0 to 0.76 mm/mm strain UTS : cold-rolled, annealed at 730 °C (1346 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : cold-rolled, annealed at 730 °C (1346 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : cold-rolled, annealed at 730 °C (1346 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F)
S420 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 20 °C (68 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 100 °C (212 °F), 7x10^-⁵/s \|\| 0 to 0.15 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 200 °C (392 °F), 7x10^-⁵/s \|\| 0 to 0.17 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 300 °C (572 °F), 7x10^-⁵/s \|\| 0 to 0.175 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 350 °C (662 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 400 °C (752 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 500 °C (932 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 600 °C (1112 °F), 7x10^-⁵/s \|\| 0 to 0.18 mm/mm strain SSC : cold-rolled, annealed at 700 °C (1292 °F) \|\| tested at 700 °C (1292 °F), 7x10^-⁵/s \|\| 0 to 0.17 mm/mm strain UTS : cold-rolled, annealed at 700 °C (1292 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : cold-rolled, annealed at 700 °C (1292 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : cold-rolled, annealed at 700 °C (1292 °F) \|\| 20 °C to 700 °C (68 °F to 1292 °F)
G500 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) CTE : solid \|\| 20 °C to 792 °C (68 °F to 1457 °F) E : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) G : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) v : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) K : solid \|\| -269 °C to 1227 °C (-452 °F to 2240 °F) SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 20 °C (68 °F), 7x10^-⁵/s \|\| 0 to 6.7x10^-³ mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 100 °C (212 °F), 7x10^-⁵/s \|\| 0 to 0.4 mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 200 °C (392 °F), 7x10^-⁵/s \|\| 0 to 0.23 mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 300 °C (572 °F), 7x10^-⁵/s \|\| 0 to 0.25 mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 400 °C (752 °F), 7x10^-⁵/s \|\| 0 to 0.13 mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 500 °C (932 °F), 7x10^-⁵/s \|\| 0 to 0.3 mm/mm strain SSC : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| tested at 600 °C (1112 °F), 7x10^-⁵/s \|\| 0 to 0.115 mm/mm strain UTS : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : warm-rolled at 870 °C (1598 °F), stress relief annealed at 500 °C (932 °F) \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Nickel alloys	Property : Condition // Data range
Nickel (commercially pure) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) DLL : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) MTE : solid \|\| -273 °C to 900 °C (-460 °F to 1652 °F) E : solid \|\| -273 °C to 1050 °C (-460 °F to 1922 °F) G : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) v : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) K : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| 0 °C to 900 °C (32 °F to 1652 °F) TC : liquid \|\| 1450 °C to 2727 °C (2642 °F to 4940 °F) TD : solid \|\| 0 °C to 900 °C (32 °F to 1652 °F) TD : liquid \|\| 1450 °C to 1650 °C (2642 °F to 3002 °F) SH : solid \|\| -173 °C to 1455 °C (-280 °F to 2651 °F) SH : liquid \|\| 1273 °C to 2911 °C (2323 °F to 5272 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : annealed \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.45 mm/mm strain SSC : annealed \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SR : annealed \|\| tested at 149 °C (300 °F) \|\| 3 h to 8,100 h SR : annealed \|\| tested at 371 °C (700 °F) \|\| 20 h to 2.1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 50 h to 4,000 h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 4 h to 10 h SR : annealed \|\| Master curve (LMP) \|\| 149 °C to 650 °C (300 °F to 1202 °F) FEN : hot finished \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles FEN : hot finished \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 180 cycles to 7.6x10⁴ cycles FSN : annealed \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 8x10⁴ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 6x10⁴ cycles to 1x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : annealed, K_t = 3 \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁶ cycles VP : solid \|\| 20 °C to 1455 °C (68 °F to 2651 °F) VP : liquid \|\| 1455 °C to 1877 °C (2651 °F to 3410 °F) Vis : liquid \|\| 1394 °C to 1657 °C (2541 °F to 3014 °F) ST : liquid \|\| 1455 °C to 1955 °C (2651 °F to 3551 °F)
Nickel D (211) (UNS N02211) (WNr 2.4116) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -192 °C to 900 °C (-314 °F to 1652 °F) DLL : solid \|\| -192 °C to 900 °C (-314 °F to 1652 °F) MTE : solid \|\| -192 °C to 900 °C (-314 °F to 1652 °F) CTE : solid \|\| -223 °C to 527 °C (-370 °F to 980 °F) TC : solid \|\| 0 °C to 900 °C (32 °F to 1652 °F)
Nickel 200 (UNS N02200) (WNr 2.4036/2.4040) (ISO/EN/DIN Ni99.0) (ASTM B160/B161/B162) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -200 °C to 1100 °C (-328 °F to 2012 °F) DLL : solid \|\| -200 °C to 1100 °C (-328 °F to 2012 °F) MTE : solid \|\| -200 °C to 1100 °C (-328 °F to 2012 °F) CTE : solid \|\| -200 °C to 1100 °C (-328 °F to 2012 °F) E : solid \|\| -273 °C to 1050 °C (-460 °F to 1922 °F) G : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) v : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) K : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| annealed \|\| -100 °C to 1000 °C (-148 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| annealed \|\| 20 °C to 1453 °C (68 °F to 2647 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : annealed bar \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed bar \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed bar \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.438 mm/mm strain SSC : annealed bar \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.438 mm/mm strain UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 871 °C (68 °F to 1600 °F) FEN : hot finished \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles FEN : hot finished \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 180 cycles to 7.6x10⁴ cycles FSN : cold-drawn rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in air, maximum stress \|\| 1x10⁴ cycles to 1x10⁹ cycles FSN : cold-drawn rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in fresh water, maximum stress \|\| 1x10⁴ cycles to 1x10⁹ cycles FSN : cold-drawn rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in salt water, maximum stress \|\| 1x10⁶ cycles to 1x10⁹ cycles FSN : annealed rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in air, maximum stress \|\| 1x10⁵ cycles to 1x10⁹ cycles FSN : annealed rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in fresh water, maximum stress \|\| 1x10⁵ cycles to 1x10⁹ cycles FSN : annealed rod \|\| tested at 20 °C (68 °F), R = -1, flexure, in salt water, maximum stress \|\| 1x10⁵ cycles to 1x10⁹ cycles FSN : annealed sheet \|\| tested at 20 °C (68 °F), reverse bending, R = -1, maximum stress \|\| 8.56x10⁴ cycles to 2.74x10⁶ cycles FSN : annealed sheet \|\| tested at -79 °C (-110 °F), reverse bending, R = -1, maximum stress \|\| 1.49x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at -196.1 °C (-321.1 °F), reverse bending, R = -1, maximum stress \|\| 2.93x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at -253.1 °C (-423.7 °F), reverse bending, R = -1, maximum stress \|\| 6x10⁴ cycles to 1x10⁶ cycles RHO : solid \|\| -100 °C to 1100 °C (-148 °F to 2012 °F) SIGMA : solid \|\| -100 °C to 1100 °C (-148 °F to 2012 °F)
Nickel 201 (UNS N02201) (WNr 2.4068) (ISO/EN/DIN LC-Ni99) (JIS NW2201) (ASTM B160/B161/B162) (SAE 5553) (AMS 5553) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) E : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) G : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) v : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) K : solid \|\| 20 °C to 500 °C (68 °F to 932 °F) TC : solid \|\| annealed \|\| -100 °C to 1000 °C (-148 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| annealed \|\| 20 °C to 1453 °C (68 °F to 2647 °F) UTS : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : annealed \|\| 20 °C to 593 °C (68 °F to 1099 °F) SR : annealed \|\| tested at 427 °C (800 °F) \|\| 600 h to 4,000 h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 600 h to 5,000 h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| Master curve (LMP) \|\| 426 °C to 649 °C (799 °F to 1200 °F) RHO : solid \|\| -100 °C to 1000 °C (-148 °F to 1832 °F) SIGMA : solid \|\| -100 °C to 1000 °C (-148 °F to 1832 °F)
Nickel 270 (UNS N02270) (WNr 2.4050) (ISO/EN/DIN NR9995/Ni99.8) (ASTM F3)	D : solid \|\| 20 °C to 95 °C (68 °F to 203 °F) DLL : solid \|\| 20 °C to 95 °C (68 °F to 203 °F) MTE : solid \|\| 20 °C to 95 °C (68 °F to 203 °F) CTE : solid \|\| 20 °C to 95 °C (68 °F to 203 °F) TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : solid \|\| annealed \|\| room temperature value YS* : solid \|\| annealed \|\| room temperature value %El* : solid \|\| annealed \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Duranickel 301 (UNS N03301) (WNr 2.4128)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 595 °C (68 °F to 1103 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : age hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : age hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : age hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) RHO : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SIGMA : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)

Nickel TD (UNS N03260) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SSC : as-received bar \|\| tested at 25 °C (77 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : as-received bar \|\| tested at 124 °C (255 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : as-received bar \|\| tested at 250 °C (482 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 25 °C (77 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 100 °C (212 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 200 °C (392 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 285 °C (545 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 500 °C (932 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 400 °C (752 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 600 °C (1112 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 700 °C (1292 °F), 1.67x10^-⁴/s \|\| 0 to 0.49 mm/mm strain SSC : sheet recrystallized at 1300 °C (2372 °F) \|\| tested at 800 °C (1472 °F), 1.67x10^-⁴/s \|\| 0 to 0.34 mm/mm strain UTS : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, longitudinal \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, longitudinal \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : sheet \|\| recrystallized at 1300 °C (2372 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : bar \|\| as-received \|\| 20 °C to 250 °C (68 °F to 482 °F) YSC : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, longitudinal \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YSC : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, longitudinal \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : sheet \|\| stress-relieved at 1093 °C (2000 °F), 0.5 h hold, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 1149 °C (2100 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 1204 °C (2200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 1205 °C (1200 °F to 2201 °F) SR : sheet material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 1149 °C (2100 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 1204 °C (2200 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| Master curve (LMP) \|\| 649 °C to 1205 °C (1200 °F to 2201 °F) FEN : plate, stress-relieved \|\| tested at 982 °C (1800 °F), R = 0, axial, total strain range \|\| 1 cycles to 6.3x10³ cycles FSN : rod, stress relieved at 1010 °C (1850 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 1.1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), smooth \|\| tested at 871 °C (1600 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), smooth \|\| tested at 982 °C (1800 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), notched \|\| tested at 871 °C (1600 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : sheet, stress-relieved at 1093 °C (2000 °F), notched \|\| tested at 982 °C (1800 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, sheet, stress-relieved at 1093 °C (2000 °F) \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, sheet, stress-relieved at 1093 °C (2000 °F) \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, sheet, stress-relieved at 1093 °C (2000 °F) \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, sheet, stress-relieved at 1093 °C (2000 °F) \|\| Master curve (LMP) \|\| 871 °C to 1094 °C (1600 °F to 2001 °F) RHO : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F)
TD-NiCr	D* : solid \|\| room temperature value UTS : cold-rolled, annealed \|\| 51.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) UTS : cold-rolled, annealed \|\| 19.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) UTS : cold-rolled, annealed \|\| 6.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) UTS : cold-rolled, annealed \|\| 3.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) YS : cold-rolled, annealed \|\| 51.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) YS : cold-rolled, annealed \|\| 19.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) YS : cold-rolled, annealed \|\| 6.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) YS : cold-rolled, annealed \|\| 3.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) %El : cold-rolled, annealed \|\| 51.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) %El : cold-rolled, annealed \|\| 19.5 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) %El : cold-rolled, annealed \|\| 6.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) %El : cold-rolled, annealed \|\| 3.7 micron grain size \|\| 593 °C to 1093 °C (1099 °F to 2000 °F) SR : cold-rolled, annealed \|\| tested at 1093 °C (2000 °F), single crystal <001> \|\| 0.4 h to 300 h SR : cold-rolled, annealed \|\| tested at 1093 °C (2000 °F), 0.19 mm (0.00748 inch) average grain size \|\| 0.3 h to 850 h SR : cold-rolled, annealed \|\| tested at 1093 °C (2000 °F), 8.6 micron average grain size \|\| 0.2 h to 280 h SR : cold-rolled, annealed \|\| tested at 1093 °C (2000 °F), 3.7 micron average grain size \|\| 0.5 h to 100 h
PM 1000	D* : solid \|\| room temperature value FEN : fully recrystallized, 0.001/s \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude \|\| 140 cycles to 6.6x10³ cycles FEN : fully recrystallized, 0.001/s \|\| tested at 1000 °C (1832 °F), R = -1, axial, total strain amplitude \|\| 40 cycles to 4x10³ cycles FEN : fully recrystallized, 1x10^-⁵/s \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude \|\| 17 cycles to 700 cycles FEN : fully recrystallized, 1x10^-⁵/s \|\| tested at 1000 °C (1832 °F), R = -1, axial, total strain amplitude \|\| 8 cycles to 400 cycles

Monel 400 (UNS N04400) (WNr 2.4360) (ISO/EN/DIN NW4400/NiCu30/NiCu30Fe) (JIS NW4400) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) DLL : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) MTE : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) CTE : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -269 °C to 982 °C (-452 °F to 1800 °F) TC : solid \|\| hard-drawn, cold-rolled \|\| -269 °C to 27 °C (-452 °F to 80 °F) TD : solid \|\| annealed \|\| -185 °C to 316 °C (-301 °F to 600 °F) TD : solid \|\| hard-drawn, cold-rolled \|\| -185 °C to 27 °C (-301 °F to 80 °F) SH : solid \|\| -185 °C to 316 °C (-301 °F to 600 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 1.67x10^-⁴/s \|\| 0 to 1.25 mm/mm strain UTS : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : cold-drawn & annealed at 816 °C (1500 °F) for 0.5 h \|\| tested at 371 °C (700 °F) \|\| 100 h to 1,000 h SR : cold-drawn & annealed at 816 °C (1500 °F) for 0.5 h \|\| tested at 482 °C (900 °F) \|\| 100 h to 1,000 h SR : cold-drawn & annealed at 816 °C (1500 °F) for 0.5 h \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & annealed at 816 °C (1500 °F) for 0.5 h \|\| Master curve (LMP) \|\| 371 °C to 594 °C (700 °F to 1101 °F) SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 371 °C (700 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 454 °C (850 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 510 °C (950 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : cold-drawn & stress relieved at 593 °C (1100 °F) for 8 h \|\| Master curve (LMP) \|\| 371 °C to 538 °C (700 °F to 1000 °F) SR : mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 1.5 h to 860 h SR : mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 4 h to 1,510 h SR : mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| Master curve (LMP) \|\| 537 °C to 649 °C (998 °F to 1200 °F) FSN : wire, cold-drawn 75% after final anneal \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 2.1x10⁵ cycles to 1x10⁸ cycles FSN : rod, cold-drawn, annealed at 816 °C (1500 °F) for 3 h \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles CRS : 0.2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 85 h CRS : 0.2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 45 h CRS : 0.5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 0.2 h to 210 h CRS : 0.5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 0.17 h to 200 h CRS : 1% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 0.14 h to 15 h CRS : 1% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 1,180 h CRS : 1% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| Master curve (LMP) \|\| 537 °C to 649 °C (998 °F to 1200 °F) CRS : 2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 0.3 h to 320 h CRS : 2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 530 h CRS : 2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| Master curve (LMP) \|\| 537 °C to 649 °C (998 °F to 1200 °F) CRS : 3% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 1 h to 185 h CRS : 3% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 0.4 h to 365 h CRS : 3% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| Master curve (LMP) \|\| 537 °C to 649 °C (998 °F to 1200 °F) CRS : 5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 3.2 h to 280 h CRS : 5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 649 °C (1200 °F) \|\| 2.3 h to 685 h CRS : 5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| Master curve (LMP) \|\| 537 °C to 649 °C (998 °F to 1200 °F) CRS : 10% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| tested at 538 °C (1000 °F) \|\| 53 h to 315 h IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 100 h \|\| 0 to 0.1 mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 300 h \|\| 0 to 0.1 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at RT: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) \|\| 300 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) SIGMA : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F)
Monel 401 (UNS N04401) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) DLL : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) MTE : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) CTE : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F)
Monel 404 (UNS N04404)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) G : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) v : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) K : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Monel K-500 (UNS N05500) (WNr 2.4374/2.4375) (ISO/EN/DIN NW5500/NiCu30Al/NiCu30Al3Ti) (ASTM B865) (AMS 4676) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| -273 °C to 1016 °C (-460 °F to 1861 °F) D : solid \|\| age hardened \|\| -200 °C to 800 °C (-328 °F to 1472 °F) DLL : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| -273 °C to 1016 °C (-460 °F to 1861 °F) DLL : solid \|\| age hardened \|\| -200 °C to 800 °C (-328 °F to 1472 °F) MTE : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| -273 °C to 1016 °C (-460 °F to 1861 °F) MTE : solid \|\| age hardened \|\| -200 °C to 800 °C (-328 °F to 1472 °F) CTE : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| -273 °C to 1016 °C (-460 °F to 1861 °F) CTE : solid \|\| age hardened \|\| -200 °C to 800 °C (-328 °F to 1472 °F) E : solid \|\| 20 °C to 537 °C (68 °F to 998 °F) TC : solid \|\| annealed & quenched \|\| -142 °C to 912 °C (-224 °F to 1673 °F) TD : solid \|\| annealed & quenched \|\| -157 °C to 871 °C (-251 °F to 1600 °F) SH : solid \|\| -200 °C to 871 °C (-328 °F to 1600 °F) SSC : bar aged at 593 °C (1100 °F) \|\| tested at 27 °C (80 °F), 3.3x10^-⁴/s \|\| 0 to 0.22 mm/mm strain SSC : bar aged at 593 °C (1100 °F) \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.22 mm/mm strain SSC : bar aged at 593 °C (1100 °F) \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : bar aged at 593 °C (1100 °F) \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : wire aged at 527 °C (980 °F) \|\| tested at -196.1 °C (-321.1 °F), 2.2x10^-⁴/s \|\| 0 to 0.111 mm/mm strain SSC : wire aged at 527 °C (980 °F) \|\| tested at -196.1 °C (-321.1 °F), 2.2x10^-⁴/s, 300 ppm H₂ \|\| 0 to 0.113 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.001/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.55 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.01/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.05/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.53 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.1/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.52 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 0.5/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.57 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 1/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.51 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.53 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.47 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.48 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.45 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.55 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.27 mm/mm strain SSCC : 5/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.55 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.45 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.64 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.48 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.3 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.49 mm/mm strain SSCC : 20/s, heat-treated & aged condition \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.51 mm/mm strain UTS : solid \|\| rod, annealed & aged \|\| 20 °C to 371 °C (68 °F to 700 °F) UTS : solid \|\| rod, hot-rolled & as-rolled \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| rod, hot finished & aged \|\| 20 °C to 593 °C (68 °F to 1099 °F) YS : solid \|\| rod, annealed & aged \|\| 20 °C to 371 °C (68 °F to 700 °F) YS : solid \|\| rod, hot-rolled, as-rolled \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| rod, hot finished & aged \|\| 20 °C to 593 °C (68 °F to 1099 °F) %El : solid \|\| rod, annealed & aged \|\| 20 °C to 371 °C (68 °F to 700 °F) %El : solid \|\| rod, hot-rolled, as-rolled \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| rod, hot finished & aged \|\| 20 °C to 593 °C (68 °F to 1099 °F) SR : hot-finished & aged \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁴ h SR : hot-finished & aged \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : hot-finished & aged \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : hot-finished & aged \|\| Master curve (LMP) \|\| 482 °C to 594 °C (899 °F to 1101 °F) FSN : sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1.8x10⁴ cycles to 1x10⁸ cycles FSN : sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 2.7x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1.7x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress \|\| 3.3x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.1x10⁴ cycles to 1.1x10⁷ cycles FSN : sheet \|\| tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.9x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.75x10⁴ cycles to 1.34x10⁶ cycles FSN : sheet \|\| tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 4x10⁴ cycles to 1.33x10⁶ cycles FSN : rotating beam \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 4.08x10⁵ cycles to 1.3x10⁸ cycles FSN : stress-equalized \|\| tested at 20 °C (68 °F), R = -1, wire, maximum stress \|\| 4.3x10⁵ cycles to 1x10⁸ cycles FSN : age-hardened \|\| tested at 20 °C (68 °F), R = -1, bar & sheet, maximum stress \|\| 100 cycles to 1x10⁶ cycles FSN : age-hardened \|\| tested at 20 °C (68 °F), R = -1, wire, maximum stress \|\| 2.3x10⁶ cycles to 1x10⁸ cycles NE : polished \|\| -185 °C to 982 °C (-301 °F to 1800 °F) NE : clean & smooth \|\| -185 °C to 816 °C (-301 °F to 1500 °F) NE : as-received \|\| -185 °C to 816 °C (-301 °F to 1500 °F) NE : prolonged heating above 1093 °C (2000 °F) \|\| 204 °C to 982 °C (399 °F to 1800 °F) RHO : solid \|\| -196 °C to 982 °C (-321 °F to 1800 °F) SIGMA : solid \|\| -196 °C to 982 °C (-321 °F to 1800 °F)
Monel R-405 (UNS N04405) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) DLL : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) MTE : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) CTE : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| annealed \|\| -269 °C to 982 °C (-452 °F to 1800 °F) TD : solid \|\| annealed \|\| -31 °C to 316 °C (-24 °F to 600 °F) SH : solid \|\| -185 °C to 316 °C (-301 °F to 600 °F) UTS* : solid \|\| annealed \|\| room temperature value YS* : solid \|\| annealed \|\| room temperature value %El* : solid \|\| annealed \|\| room temperature value RHO : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F) SIGMA : solid \|\| -196 °C to 1093 °C (-321 °F to 2000 °F)

UNS N06025 (RA 602 CA) (UNS N06025) (WNr 2.4633)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| solution annealed, quenched \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| solution annealed, quenched \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| solution annealed, quenched \|\| 20 °C to 1204 °C (68 °F to 2200 °F) FSN : solution annealed, quenched \|\| tested at 1000 °C (1832 °F), R = -1, maximum stress \|\| 640 cycles to 1.8x10⁶ cycles FSN : solution annealed, quenched \|\| tested at 1100 °C (2012 °F), R = -1, maximum stress \|\| 310 cycles to 1.8x10⁶ cycles FSN : solution annealed, quenched \|\| tested at 1150 °C (2102 °F), R = -1, maximum stress \|\| 210 cycles to 1.8x10⁶ cycles
UNS N06333 (RA333) (UNS N06333) (WNr 2.4608)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : as-formed \|\| 20 °C to 1204 °C (68 °F to 2199 °F) UTS* : effect of aging temperature on RT value \|\| mill annealed \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 1000 h at 649 °C (1200 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 1000 h at 760 °C (1400 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 1000 h at 816 °C (1500 °F) \|\| room temperature value UTS* : effect of aging temperature on RT value \|\| aged 1000 h at 982 °C (1800 °F) \|\| room temperature value YS : as-formed \|\| 20 °C to 1204 °C (68 °F to 2199 °F) YS* : effect of aging temperature on RT value \|\| mill annealed \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 1000 h at 649 °C (1200 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 1000 h at 760 °C (1400 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 1000 h at 816 °C (1500 °F) \|\| room temperature value YS* : effect of aging temperature on RT value \|\| aged 1000 h at 982 °C (1800 °F) \|\| room temperature value %El : as-formed \|\| 20 °C to 1204 °C (68 °F to 2199 °F) %El* : effect of aging temperature on RT value \|\| mill annealed \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 1000 h at 649 °C (1200 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 1000 h at 760 °C (1400 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 1000 h at 816 °C (1500 °F) \|\| room temperature value %El* : effect of aging temperature on RT value \|\| aged 1000 h at 982 °C (1800 °F) \|\| room temperature value SR : mill annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : mill annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1x10⁵ h SR : mill annealed \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1x10⁴ h SR : mill annealed \|\| tested at 1204 °C (2200 °F) \|\| 100 h to 1x10⁴ h SR : mill annealed \|\| Master curve (LMP) \|\| 593 °C to 1205 °C (1099 °F to 2201 °F) FEN : mill annealed & solution annealed samples \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁴ cycles FEN : mill annealed & solution annealed samples \|\| tested at 20 °C (68 °F), R = -1, plastic strain range \|\| 1x10³ cycles to 1x10⁴ cycles FEN : solution annealed & aged \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁴ cycles FEN : solution annealed & aged \|\| tested at 20 °C (68 °F), R = -1, plastic strain range \|\| 1x10³ cycles to 1x10⁴ cycles FEN : hot-rolled, annealed, bar \|\| tested at 871 °C (1600 °F), R = -1, total strain range \|\| 575 cycles to 9x10³ cycles CRS : 0.5% total strain, mill annealed \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% total strain, mill annealed \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) CRS : 2% total strain, mill annealed \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 2% total strain, mill annealed \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) CRS : 5% total strain, mill annealed \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1x10⁴ h CRS : 5% total strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 5% total strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 5% total strain, mill annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 5% total strain, mill annealed \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), total strain, mill annealed \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
20Cb-3 (Incoloy 020) (UNS N08020) (WNr 2.4660) (ISO/EN/DIN FeNi35Cr20Cu4Mo2/NW8020/NiCr20CuMo) (ASTM B366/B462/B463/B464/B468/B471/B472/B473/B475/B747) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) G : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) v : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| -252 °C to 871 °C (-422 °F to 1600 °F) YS : annealed \|\| -252 °C to 871 °C (-422 °F to 1600 °F) %El : annealed \|\| -252 °C to 871 °C (-422 °F to 1600 °F) SR : annealed \|\| tested at 427 °C (800 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 482 °C (900 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : annealed \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h RHO* : solid \|\| annealed \|\| room temperature value SIGMA*: solid \|\| annealed \|\| room temperature value
20Mo-4 (UNS N08024)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : annealed \|\| 20 °C to 538 °C (68 °F to 1000 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
20Mo-6 (UNS N08026) (ASTM B463/B464/B468/B471/B472/B473/B474/B475/B729)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 400 °C (68 °F to 752 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 593 °C (68 °F to 1099 °F) YS : annealed \|\| 20 °C to 593 °C (68 °F to 1099 °F) %El : annealed \|\| 20 °C to 593 °C (68 °F to 1099 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
20Mo-6 HS (UNS N08036)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Pyromet alloy 31 (UNS N07031)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) RHO : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SIGMA : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Pyromet alloy 31V (UNS N07032)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : aged \|\| 3 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : aged \|\| 2 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : aged \|\| 2 step (oil quenched) \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : aged \|\| 3 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : aged \|\| 2 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : aged \|\| 2 step (oil quenched) \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : aged \|\| 3 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : aged \|\| 2 step (air cooled) \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : aged \|\| 2 step (oil quenched) \|\| 20 °C to 650 °C (68 °F to 1202 °F) RHO : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SIGMA : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Custom Age 625 Plus (UNS N07716) (ASTM B805) (AMS 5854)	D : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) DLL : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) MTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) CTE : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SSCC : 0.001/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 0.001/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 0.001/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 0.1/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 0.1/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 0.1/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.8 mm/mm strain SSCC : 20/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.66 mm/mm strain SSCC : 20/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.71 mm/mm strain SSCC : 20/s, solutionized at 1035 °C (1895 °F), air cooled, aged \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.64 mm/mm strain UTS : double-aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : cold worked & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : double-aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : cold worked & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : double-aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : cold worked & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) FSN : smooth \|\| tested at 20 °C (68 °F), R = 0.05, axial, maximum stress \|\| 5x10⁴ cycles to 7x10⁶ cycles FSN : notched \|\| tested at 20 °C (68 °F), R = 0.05, K_t = 2, axial, maximum stress \|\| 3x10⁴ cycles to 4x10⁶ cycles
HR6W (UNS N06674) (ASTM B166/B167/B167-08/B168/B168-18)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSC : tube \|\| tested at 700 °C (1292 °F), 1x10^-⁶/s \|\| 0 to 0.54 mm/mm strain SR : solution treated \|\| tested at 650 °C (1202 °F) \|\| 90 h to 1x10⁵ h SR : solution treated \|\| tested at 700 °C (1292 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 750 °C (1382 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 800 °C (1472 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 850 °C (1562 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 900 °C (1652 °F) \|\| 10 h to 2x10⁴ h SR : solution treated \|\| Master curve (LMP) \|\| 650 °C to 901 °C (1202 °F to 1654 °F) FEN : unknown condition \|\| tested at 700 °C (1292 °F), R = -1, axial, total strain range \|\| 160 cycles to 5.2x10³ cycles

Inconel 22 (Hastelloy C-22) (UNS N06022) (WNr 2.4602) (ISO/EN/DIN NW6022/NiCr21Mo13Fe4W3/NiCr21Mo14W) (JIS NW6022)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SSCC : annealed, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.51 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.48 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.51 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.48 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.47 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.51 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 20/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.29 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.49 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.157 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.51 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.275 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.51 mm/mm strain UTS : solution heat-treated \|\| sheet \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solution heat-treated \|\| plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solution heat-treated \|\| bar \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution heat-treated \|\| sheet \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution heat-treated \|\| plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution heat-treated \|\| bar \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution heat-treated \|\| sheet \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution heat-treated \|\| plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution heat-treated \|\| bar \|\| 20 °C to 760 °C (68 °F to 1400 °F) RHO : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Inconel 600 (UNS N06600) (WNr 2.4640/2.4816) (ISO/EN/DIN NW6600/NiCr15Fe/NiCr15Fe8) (JIS NCF600) (AMS 5540/5580/5665) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) DLL : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) MTE : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) CTE : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) E : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) G : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) v : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) K : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) TC : solid \|\| annealed \|\| -269 °C to 800 °C (-452 °F to 1472 °F) TC : solid \|\| drawn \|\| -269 °C to 1000 °C (-452 °F to 1832 °F) TD : solid \|\| annealed \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) SH : solid \|\| -200 °C to 1000 °C (-328 °F to 1832 °F) SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain SSC : annealed \|\| tested at 232 °C (450 °F), 3x10^-⁵/s \|\| 0 to 0.28 mm/mm strain SSC : annealed \|\| tested at 427 °C (800 °F), 3x10^-⁵/s \|\| 0 to 0.32 mm/mm strain SSC : annealed \|\| tested at 593 °C (1100 °F), 3x10^-⁵/s \|\| 0 to 0.21 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 3x10^-⁵/s \|\| 0 to 0.11 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 3x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 0.03/s \|\| 0 to 0.24 mm/mm strain SSC : annealed \|\| tested at 649 °C (1200 °F), 0.3/s \|\| 0 to 0.25 mm/mm strain SSCC : 0.002/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.002/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.002/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.81 mm/mm strain SSCC : 0.002/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.76 mm/mm strain SSCC : 0.002/s \|\| tested at 1204 °C (2200 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.02/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.02/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.63 mm/mm strain SSCC : 0.02/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.65 mm/mm strain SSCC : 0.02/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.02/s \|\| tested at 1204 °C (2200 °F) \|\| 0 to 0.86 mm/mm strain SSCC : 0.2/s \|\| tested at 816 °C (1500 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.2/s \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.2/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.61 mm/mm strain SSCC : 0.2/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.2/s \|\| tested at 1232 °C (2250 °F) \|\| 0 to 0.74 mm/mm strain UTS : annealed \|\| hot-rolled rod \|\| -79 °C to 982 °C (-110 °F to 1800 °F) UTS : annealed \|\| hot-rolled plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : cold-drawn \|\| rod \|\| -250 °C to 700 °C (-418 °F to 1292 °F) YS : annealed \|\| hot-rolled rod \|\| -79 °C to 982 °C (-110 °F to 1800 °F) YS : annealed \|\| hot-rolled plate \|\| -79 °C to 982 °C (-110 °F to 1800 °F) YS : cold-drawn \|\| rod \|\| -250 °C to 700 °C (-418 °F to 1292 °F) %El : annealed \|\| hot-rolled rod \|\| -79 °C to 982 °C (-110 °F to 1800 °F) %El : annealed \|\| hot-rolled plate \|\| -79 °C to 982 °C (-110 °F to 1800 °F) %El : cold-drawn \|\| rod \|\| -250 °C to 700 °C (-418 °F to 1292 °F) SR : cold-drawn & annealed \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁵ h SR : cold-drawn & annealed \|\| Master curve (LMP) \|\| 537 °C to 1094 °C (998 °F to 2001 °F) SR : hot-rolled & annealed \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1x10⁵ h SR : hot-rolled & annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁵ h SR : hot-rolled & annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁵ h SR : hot-rolled & annealed \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁵ h SR : hot-rolled & annealed \|\| Master curve (LMP) \|\| 732 °C to 1094 °C (1349 °F to 2001 °F) SR : solution treated \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 1149 °C (2100 °F) \|\| 10 h to 100 h SR : solution treated \|\| Master curve (LMP) \|\| 732 °C to 1149 °C (1349 °F to 2100 °F) FEN : annealed rod \|\| tested at 20 °C (68 °F), R = -1, total strain amplitude \|\| 1x10⁴ cycles to 1x10⁵ cycles FEN : annealed rod \|\| tested at 93 °C (200 °F), R = -1, total strain amplitude \|\| 1x10⁴ cycles to 1x10⁵ cycles FEN : annealed rod \|\| tested at 204 °C (400 °F), R = -1, total strain amplitude \|\| 1x10⁴ cycles to 1x10⁵ cycles FEN : annealed rod \|\| tested at 316 °C (600 °F), R = -1, total strain amplitude \|\| 1x10⁴ cycles to 1x10⁵ cycles FEN : forgings \|\| tested at 20 °C (68 °F), R = -1, as-forged, total strain amplitude \|\| 1x10³ cycles to 5x10⁴ cycles FEN : forgings \|\| tested at 20 °C (68 °F), R = -1, stress-relieved, total strain amplitude \|\| 1x10³ cycles to 5x10⁴ cycles FEN : sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum strain \|\| 1.1x10⁴ cycles to 1x10⁸ cycles FEN : sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum strain \|\| 1.1x10⁴ cycles to 1x10⁷ cycles FEN : sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain \|\| 1.34x10⁴ cycles to 1x10⁸ cycles FEN : sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain \|\| 3.13x10⁴ cycles to 8.4x10⁵ cycles FSN : forgings \|\| tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, hard, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : forgings \|\| tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, soft, maximum stress \|\| 7.6x10⁴ cycles to 1x10⁸ cycles FSN : forgings \|\| tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, hard, maximum stress \|\| 5.2x10⁵ cycles to 1x10⁸ cycles FSN : forgings \|\| tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, soft, maximum stress \|\| 5.78x10⁴ cycles to 1x10⁸ cycles FSN : ASTM grain size 9, annealed at 700 °C (1292 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 4x10³ cycles to 8.4x10⁵ cycles FSN : ASTM grain size 9, annealed at 900 °C (1652 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 2.5x10³ cycles to 2.4x10⁶ cycles FSN : ASTM grain size 9, annealed at 900 °C (1652 °F) \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 8.3x10³ cycles to 1.5x10⁶ cycles FSN : average of ASTM grain size 9, annealed at 700 °C (1292 °F) and 900 °C (1652 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 2.5x10³ cycles to 2.4x10⁶ cycles FSN : ASTM grain size 2, annealed at 1100 °C (2012 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 8.2x10³ cycles to 4.6x10⁶ cycles FSN : ASTM grain size 2, annealed at 1100 °C (2012 °F) \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 3.1x10³ cycles to 2.35x10⁵ cycles FSN : sheet \|\| tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.1x10³ cycles to 6.75x10⁶ cycles FSN : sheet \|\| tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 6.1x10³ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 7.7x10³ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, maximum stress \|\| 4.4x10⁴ cycles to 1x10⁶ cycles CRS : 0.5% plastic strain, ASTM grain size 9 \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 2.6 h CRS : 1% plastic strain, ASTM grain size 9 \|\| tested at 649 °C (1200 °F) \|\| 0.13 h to 5.5 h CRS : 1% plastic strain, ASTM grain size 9 \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 35 h CRS : 2% plastic strain, ASTM grain size 9 \|\| tested at 649 °C (1200 °F) \|\| 0.3 h to 11 h CRS : 2% plastic strain, ASTM grain size 9 \|\| tested at 816 °C (1500 °F) \|\| 0.6 h to 60 h CRS : 3% plastic strain, ASTM grain size 9 \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 16 h CRS : 3% plastic strain, ASTM grain size 9 \|\| tested at 816 °C (1500 °F) \|\| 1 h to 90 h CRS : 5% plastic strain, ASTM grain size 9 \|\| tested at 649 °C (1200 °F) \|\| 1 h to 25 h CRS : 5% plastic strain, ASTM grain size 9 \|\| tested at 816 °C (1500 °F) \|\| 2.3 h to 140 h CRS : 0.5% plastic strain, ASTM grain size 1 \|\| tested at 649 °C (1200 °F) \|\| 0.2 h to 2 h CRS : 1% plastic strain, ASTM grain size 1 \|\| tested at 649 °C (1200 °F) \|\| 0.6 h to 4.2 h CRS : 2% plastic strain, ASTM grain size 1 \|\| tested at 649 °C (1200 °F) \|\| 0.15 h to 9 h CRS : 3% plastic strain, ASTM grain size 1 \|\| tested at 649 °C (1200 °F) \|\| 0.25 h to 16 h CRS : 5% plastic strain, ASTM grain size 1 \|\| tested at 649 °C (1200 °F) \|\| 0.45 h to 26 h CRS : 0.5% plastic strain, average of ASTM grain sizes 1 & 9 \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 2.6 h CRS : 1% plastic strain, average of ASTM grain sizes 1 & 9 \|\| tested at 649 °C (1200 °F) \|\| 0.6 h to 5.5 h CRS : 2% plastic strain, average of ASTM grain sizes 1 & 9 \|\| tested at 649 °C (1200 °F) \|\| 0.15 h to 11 h CRS : 3% plastic strain, average of ASTM grain sizes 1 & 9 \|\| tested at 649 °C (1200 °F) \|\| 0.25 h to 16 h CRS : 5% plastic strain, average of ASTM grain sizes 1 & 9 \|\| tested at 649 °C (1200 °F) \|\| 0.45 h to 26 h IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 9 \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 9 \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 9 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 9 \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, ASTM grain size 9 \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, ASTM grain size 9 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, ASTM grain size 9 \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, ASTM grain size 9 \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 1 \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 1 \|\| 0.3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 1 \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 1 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, ASTM grain size 1 \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, average of ASTM grain sizes 1 & 9 \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, average of ASTM grain sizes 1 & 9 \|\| 0.3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, average of ASTM grain sizes 1 & 9 \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, average of ASTM grain sizes 1 & 9 \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, average of ASTM grain sizes 1 & 9 \|\| 10 h \|\| 0 to 0.5 mm/mm strain HE : solid \|\| 316 °C to 982 °C (601 °F to 1800 °F) NE : solid \|\| as-rolled & oxidized \|\| 482 °C to 1093 °C (899 °F to 2000 °F) NE : solid \|\| sand-blasted & oxidized \|\| 482 °C to 1093 °C (899 °F to 2000 °F) VP : solid \|\| 1050 °C to 1275 °C (1922 °F to 2327 °F) RHO : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SIGMA : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
Inconel 601 (UNS N06601) (WNr 2.4851) (ISO/EN/DIN NW6601/NiCr23Fe/NiCr23Fe15Al) (JIS NCF601)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain UTS : hot finished rod \|\| solution treated at 1149 °C (2100 °F) \|\| 20 °C to 1149 °C (68 °F to 2100 °F) UTS : hot finished rod \|\| annealed at 1093 °C (2000 °F) \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : hot finished rod \|\| solution treated at 1149 °C (2100 °F) \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : hot finished rod \|\| annealed at 1093 °C (2000 °F) \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : hot finished rod \|\| solution treated at 1149 °C (2100 °F) \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : hot finished rod \|\| annealed at 1093 °C (2000 °F) \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : annealed \|\| tested at 1093 °C (2000 °F) \|\| 130 h to 2,000 h SR : annealed \|\| tested at 1149 °C (2100 °F) \|\| 100 h to 8,000 h SR : annealed \|\| tested at 1177 °C (2150 °F) \|\| 130 h to 1,500 h SR : solution treated \|\| tested at 538 °C (1000 °F) \|\| 25 h to 1.12x10⁴ h SR : solution treated \|\| tested at 593 °C (1100 °F) \|\| 15 h to 1.07x10⁴ h SR : solution treated \|\| tested at 649 °C (1200 °F) \|\| 50 h to 1.15x10⁴ h SR : solution treated \|\| tested at 704 °C (1300 °F) \|\| 20 h to 1.16x10⁴ h SR : solution treated \|\| tested at 760 °C (1400 °F) \|\| 40 h to 1.09x10⁴ h SR : solution treated \|\| tested at 816 °C (1500 °F) \|\| 40 h to 1.12x10⁴ h SR : solution treated \|\| tested at 871 °C (1600 °F) \|\| 50 h to 1.1x10⁴ h SR : solution treated \|\| tested at 982 °C (1800 °F) \|\| 60 h to 1.12x10⁴ h SR : solution treated \|\| tested at 1093 °C (2000 °F) \|\| 65 h to 8,025 h SR : solution treated \|\| tested at 1149 °C (2100 °F) \|\| 85 h to 9,230 h SR : solution treated \|\| Master curve (LMP), 593 °C (1100 °F) and below \|\| 537 °C to 594 °C (998 °F to 1101 °F) SR : solution treated \|\| Master curve (LMP), 593 °C (1100 °F) to 649 °C (1200 °F) \|\| 593 °C to 649 °C (1099 °F to 1200 °F) SR : solution treated \|\| Master curve (LMP), 649 °C (1200 °F) and above \|\| 648 °C to 1149 °C (1198 °F to 2100 °F) FEN : hot-finished flat \|\| tested at 20 °C (68 °F), R = -1, total strain range \|\| 400 cycles to 1x10⁶ cycles FEN : hot-finished flat \|\| tested at 760 °C (1400 °F), R = -1, total strain range \|\| 100 cycles to 8x10⁵ cycles FSN : annealed \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : solution treated \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 18 h to 5,050 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 16 h to 4,900 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 3.5 h to 5,100 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 1 h to 5,160 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 1.3 h to 4,800 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 1.1 h to 4,800 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 2 h to 4,800 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 1.7 h to 4,950 h CRS : 0.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 2 h to 4,770 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 35 h to 1.01x10⁴ h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 30 h to 9,700 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 7 h to 1.02x10⁴ h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 2.1 h to 1.03x10⁴ h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 2.8 h to 9,700 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 2.3 h to 9,700 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 3.9 h to 9,500 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 3.4 h to 9,900 h CRS : 1% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 4 h to 9,550 h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 50 h to 1.51x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 50 h to 1.45x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1.53x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 3 h to 1.55x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 4.1 h to 1.45x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 3.4 h to 1.45x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 5.8 h to 1.43x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 5.1 h to 1.48x10⁴ h CRS : 1.5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 6 h to 1.43x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 70 h to 2.02x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 65 h to 1.93x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 14 h to 2.04x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 4.2 h to 2.06x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 5.5 h to 1.93x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 4.5 h to 1.93x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 7.8 h to 1.91x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 6.9 h to 1.97x10⁴ h CRS : 2% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 8 h to 1.91x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 105 h to 3.03x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 100 h to 2.9x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 20 h to 3.06x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 6.3 h to 3.1x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 8.3 h to 2.9x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 6.8 h to 2.9x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 11.6 h to 2.9x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 10.3 h to 2.96x10⁴ h CRS : 3% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 12 h to 2.87x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 538 °C (1000 °F) \|\| 180 h to 5.05x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 593 °C (1100 °F) \|\| 165 h to 4.83x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 649 °C (1200 °F) \|\| 35 h to 5.1x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 10.5 h to 5.16x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 760 °C (1400 °F) \|\| 14 h to 4.83x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 11.3 h to 4.83x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 871 °C (1600 °F) \|\| 20 h to 4.78x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 982 °C (1800 °F) \|\| 17.2 h to 4.94x10⁴ h CRS : 5% creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| tested at 1093 °C (2000 °F) \|\| 20 h to 4.77x10⁴ h IC : tested at 538 °C (1000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.3 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.15 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.3 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3 h \|\| 0 to 0.15 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.3 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.3 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.3 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 1093 °C (2000 °F), creep strain, 1 h at 1149 °C (2100 °F), air cooled \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Inconel 603XL	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) G : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) v : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) K : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| annealed \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SR : annealed \|\| tested at 1100 °C (2012 °F) \|\| 130 h to 6,500 h SR : annealed \|\| tested at 1177 °C (2150 °F) \|\| 750 h to 2,300 h SR : annealed \|\| Master curve (LMP) \|\| 1100 °C to 1178 °C (2012 °F to 2152 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Inconel 617 (UNS N06617) (WNr 2.4663) (ISO/EN/DIN NW6617/NiCr22Co12Mo9/NiCr23Co12Mo)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) G : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) v : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) K : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSC : annealed \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain SSC : annealed \|\| tested at 900 °C (1652 °F), 5.85x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : annealed \|\| tested at 950 °C (1742 °F), 5.85x10^-⁴/s \|\| 0 to 0.42 mm/mm strain UTS : cold-rolled & annealed \|\| 0.5 h hold, longitudinal \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : cold-rolled & annealed \|\| 0.5 h hold, long transverse \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : cold-rolled & annealed \|\| 0.5 h hold, longitudinal \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : cold-rolled & annealed \|\| 0.5 h hold, long transverse \|\| 20 °C to 871 °C (68 °F to 1600 °F) YSC : cold-rolled & annealed \|\| 0.5 h hold, longitudinal \|\| 20 °C to 871 °C (68 °F to 1600 °F) YSC : cold-rolled & annealed \|\| 0.5 h hold, long transverse \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : cold-rolled & annealed \|\| 0.5 h hold, longitudinal \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : cold-rolled & annealed \|\| 0.5 h hold, long transverse \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : solution annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed \|\| Master curve (LMP) \|\| 593 °C to 1094 °C (1099 °F to 2001 °F) FEN : sheet \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 100 cycles to 8x10⁵ cycles FEN : sheet \|\| tested at 760 °C (1400 °F), R = -1, axial, total strain range \|\| 600 cycles to 3x10⁵ cycles FEN : sheet \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 100 cycles to 3x10⁵ cycles FEN : solution annealed plate \|\| tested at 950 °C (1742 °F), R = -1, axial, total strain range \|\| 900 cycles to 1x10⁴ cycles FEN : solution annealed plate \|\| tested at 950 °C (1742 °F), R = -1, axial, elastic strain range \|\| 900 cycles to 1x10⁴ cycles FEN : solution annealed plate \|\| tested at 950 °C (1742 °F), R = -1, axial, plastic strain range \|\| 900 cycles to 1x10⁴ cycles FEN : welded plate \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 265 cycles to 5x10⁴ cycles FEN : welded plate \|\| tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude \|\| 150 cycles to 5x10⁴ cycles FEN : welded plate \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 150 cycles to 5x10⁴ cycles FEN : welded plate \|\| tested at 800 °C (1472 °F), R = -1, axial, total strain amplitude \|\| 125 cycles to 5x10³ cycles FEN : welded plate \|\| tested at 800 °C (1472 °F), R = -1, axial, elastic strain amplitude \|\| 85 cycles to 5x10³ cycles FEN : welded plate \|\| tested at 800 °C (1472 °F), R = -1, axial, plastic strain amplitude \|\| 85 cycles to 5x10³ cycles FEN : annealed \|\| tested at 900 °C (1652 °F), R = -1, axial, total strain amplitude \|\| 350 cycles to 1.5x10³ cycles FEN : annealed \|\| tested at 900 °C (1652 °F), R = -1, axial, elastic strain amplitude \|\| 350 cycles to 1.5x10³ cycles FEN : annealed \|\| tested at 900 °C (1652 °F), R = -1, axial, plastic strain amplitude \|\| 350 cycles to 1.5x10³ cycles FEN : annealed \|\| tested at 950 °C (1742 °F), R = -1, axial, total strain amplitude \|\| 350 cycles to 1x10³ cycles FEN : annealed \|\| tested at 950 °C (1742 °F), R = -1, axial, elastic strain amplitude \|\| 350 cycles to 1x10³ cycles FEN : annealed \|\| tested at 950 °C (1742 °F), R = -1, axial, plastic strain amplitude \|\| 350 cycles to 1x10³ cycles FSN : solution annealed \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : solution annealed \|\| tested at 871 °C (1600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : cold-rolled & annealed, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed, smooth \|\| tested at 427 °C (800 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed, smooth \|\| tested at 649 °C (1200 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed, notched \|\| tested at 427 °C (800 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : cold-rolled & annealed, notched \|\| tested at 649 °C (1200 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, cold-rolled & annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, cold-rolled & annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Inconel 625 (UNS N06625) (WNr 2.4856) (ISO/EN/DIN NW6625/NiCr22Mo9Nb) (JIS NCF625) (AMS 5599/5666/5837) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -254 °C to 927 °C (-425 °F to 1700 °F) DLL : solid \|\| -254 °C to 927 °C (-425 °F to 1700 °F) MTE : solid \|\| -254 °C to 927 °C (-425 °F to 1700 °F) CTE : solid \|\| -254 °C to 927 °C (-425 °F to 1700 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| annealed \|\| -157 °C to 1290 °C (-251 °F to 2354 °F) TD : solid \|\| annealed \|\| -157 °C to 927 °C (-251 °F to 1701 °F) SH : solid \|\| annealed \|\| -170 °C to 1093 °C (-274 °F to 2000 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain SSC : annealed at 1149 °C (2100 °F) \|\| tested at 24 °C (75 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1149 °C (2100 °F) \|\| tested at 316 °C (600 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1149 °C (2100 °F) \|\| tested at 482 °C (900 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1149 °C (2100 °F) \|\| tested at 649 °C (1200 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 982 °C (1800 °F) \|\| tested at 24 °C (75 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 982 °C (1800 °F) \|\| tested at 316 °C (600 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 982 °C (1800 °F) \|\| tested at 482 °C (900 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 982 °C (1800 °F) \|\| tested at 649 °C (1200 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 700 °C (1292 °F), 0.001/s \|\| 0 to 0.31 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 700 °C (1292 °F), 0.01/s \|\| 0 to 0.35 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 700 °C (1292 °F), 0.1/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 850 °C (1562 °F), 0.001/s \|\| 0 to 0.29 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 850 °C (1562 °F), 0.01/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 850 °C (1562 °F), 0.1/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 925 °C (1697 °F), 0.001/s \|\| 0 to 0.33 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 925 °C (1697 °F), 0.01/s \|\| 0 to 0.38 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 925 °C (1697 °F), 0.1/s \|\| 0 to 0.38 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 1025 °C (1877 °F), 0.001/s \|\| 0 to 0.32 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 1025 °C (1877 °F), 0.01/s \|\| 0 to 0.31 mm/mm strain SSC : annealed at 930 °C (1706 °F) \|\| tested at 1025 °C (1877 °F), 0.1/s \|\| 0 to 0.38 mm/mm strain SSC : after 100,000 h service \|\| tested at 350 °C (662 °F), 8.8x10^-⁵/s \|\| 0 to 0.23 mm/mm strain SSC : after 100,000 h service \|\| tested at 600 °C (1112 °F), 8.8x10^-⁵/s \|\| 0 to 0.253 mm/mm strain SSC : as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| tested at 20 °C (68 °F), 0.003/s \|\| 0 to 0.54 mm/mm strain SSC : as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| tested at 500 °C (932 °F), 0.003/s \|\| 0 to 0.48 mm/mm strain SSC : as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| tested at 600 °C (1112 °F), 0.003/s \|\| 0 to 0.47 mm/mm strain SSC : as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| tested at 700 °C (1292 °F), 0.003/s \|\| 0 to 0.48 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction \|\| 0 to 0.23 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction \|\| 0 to 0.23 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 95 W \|\| 0 to 0.34 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 95 W \|\| 0 to 0.186 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 110 W \|\| 0 to 0.37 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 110 W \|\| 0 to 0.176 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 120 W \|\| 0 to 0.31 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 120 W \|\| 0 to 0.243 mm/mm strain SSCC : 0.002/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.68 mm/mm strain SSCC : 0.002/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.74 mm/mm strain SSCC : 0.002/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.83 mm/mm strain SSCC : 0.002/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1093 °C (2000 °F) \|\| 0 to 0.75 mm/mm strain SSCC : 0.002/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.79 mm/mm strain SSCC : 0.02/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.64 mm/mm strain SSCC : 0.02/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.02/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.02/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1093 °C (2000 °F) \|\| 0 to 0.73 mm/mm strain SSCC : 0.02/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.2/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 927 °C (1700 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.2/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.71 mm/mm strain SSCC : 0.2/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.2/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1093 °C (2000 °F) \|\| 0 to 0.7 mm/mm strain SSCC : 0.2/s, annealed at 927 °C (1700 °F) & water quenched \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.73 mm/mm strain UTS : effect of temperature \|\| hot-rolled solution treated rod \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : effect of temperature \|\| annealed bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : effect of temperature \|\| cold-rolled annealed sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : effect of temperature \|\| as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value UTS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value UTS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value UTS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value UTS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value UTS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value UTS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value UTS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value UTS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value UTS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value UTS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value UTS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value UTS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value UTS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value UTS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value UTS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value UTS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value UTS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value UTS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value UTS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value UTS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YS : effect of temperature \|\| hot-rolled solution treated rod \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : effect of temperature \|\| annealed bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : effect of temperature \|\| cold-rolled annealed sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : effect of temperature \|\| as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value YS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value YS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value YS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value YS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value YS* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value YS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value YS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value YS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value YS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value YS* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value YS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value YS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value YS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value YS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value YS* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value YS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YS* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value YSC : solid \|\| annealed sheet, longitudinal \|\| 20 °C to 871 °C (68 °F to 1600 °F) YSC : solid \|\| annealed sheet, transverse \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : effect of temperature \|\| hot-rolled solution treated rod \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : effect of temperature \|\| annealed bar \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : effect of temperature \|\| cold-rolled annealed sheet \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : effect of temperature \|\| as-cast, solution treated at 1200 °C (2192 °F) for 10 h, water quenched \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value %El* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value %El* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value %El* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value %El* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value %El* : 1010 °C (1850 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1010 °C (1850 °F) for 5 minutes \|\| room temperature value %El* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value %El* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value %El* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value %El* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value %El* : 1066 °C (1950 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1066 °C (1950 °F) for 5 minutes \|\| room temperature value %El* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value %El* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value %El* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value %El* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value %El* : 1121 °C (2050 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1121 °C (2050 °F) for 5 minutes \|\| room temperature value %El* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 10% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value %El* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 20% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value %El* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 30% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value %El* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 40% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value %El* : 1177 °C (2150 °F) for 5 minutes, effect of cold work on RT value \|\| 50% cold worked, 1177 °C (2150 °F) for 5 minutes \|\| room temperature value SR : cold-rolled & annealed \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h SR : cold-rolled & annealed \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : annealed \|\| tested at 621 °C (1150 °F) \|\| 500 h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 3x10⁴ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 2,000 h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : annealed \|\| tested at 816 °C (1500 °F) \|\| 50 h to 1,000 h SR : annealed \|\| Master curve (LMP) \|\| 593 °C to 816 °C (1099 °F to 1501 °F) SR : solution treated \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁵ h SR : solution treated \|\| tested at 982 °C (1800 °F) \|\| 50 h to 1,000 h SR : solution treated \|\| tested at 1093 °C (2000 °F) \|\| 50 h to 1,000 h SR : solution treated \|\| Master curve (LMP) \|\| 649 °C to 1094 °C (1200 °F to 2001 °F) FEN : annealed \|\| tested at 538 °C (1000 °F), R = -1, total strain range \|\| 500 cycles to 5x10⁵ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 20 °C (68 °F), R = -1, as-rolled, maximum stress \|\| 3.55x10⁴ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 20 °C (68 °F), R = -1, annealed, maximum stress \|\| 2.86x10⁵ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 427 °C (800 °F), R = -1, annealed, maximum stress \|\| 2.86x10⁵ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 538 °C (1000 °F), R = -1, annealed, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 649 °C (1200 °F), R = -1, annealed, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 760 °C (1400 °F), R = -1, annealed, maximum stress \|\| 4.95x10⁵ cycles to 1x10⁸ cycles FSN : rotating beam, hot-rolled bar, 15.9 mm (0.625 inch) diameter \|\| tested at 871 °C (1600 °F), R = -1, annealed, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : bending fatigue, sheet \|\| tested at 20 °C (68 °F), R = -1, annealed, maximum stress \|\| 2x10³ cycles to 1x10⁸ cycles FSN : bending fatigue, sheet \|\| tested at 20 °C (68 °F), R = -1, cold worked, maximum stress \|\| 5x10⁴ cycles to 1x10⁸ cycles FSN : bending fatigue, sheet \|\| tested at 20 °C (68 °F), R = -1, soft forming temper, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles CRS : 0.5% plastic strain, mill annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, mill annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, mill annealed \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, mill annealed \|\| tested at 927 °C (1700 °F) \|\| 10 h to 100 h CRS : 0.5% plastic strain, mill annealed \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) CRS : 1% plastic strain, mill annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, mill annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, mill annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, mill annealed \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, mill annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, mill annealed \|\| tested at 927 °C (1700 °F) \|\| 10 h to 100 h CRS : 1% plastic strain, mill annealed \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, mill annealed \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, mill annealed \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, mill annealed \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, mill annealed \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, mill annealed \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, mill annealed \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, mill annealed \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, mill annealed \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, mill annealed \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, mill annealed \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, mill annealed \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, mill annealed \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, mill annealed \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, mill annealed \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, mill annealed \|\| 100 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| -269 °C to 1290 °C (-452 °F to 2354 °F) SIGMA : solid \|\| -269 °C to 1290 °C (-452 °F to 2354 °F)
Inconel 625LCF (UNS N06626) (WNr 2.4856) (JIS DNiCrMo-3) (ASTM B443/SB443) (AMS 5879) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) G : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) v : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) K : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| -150 °C to 1000 °C (-238 °F to 1832 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS : solid \|\| annealed sheet \|\| 20 °C to 690 °C (68 °F to 1274 °F) YS : solid \|\| annealed sheet \|\| 20 °C to 690 °C (68 °F to 1274 °F) %El : solid \|\| annealed sheet \|\| 20 °C to 700 °C (68 °F to 1292 °F) SR : as-annealed \|\| tested at 593 °C (1100 °F) \|\| 4 h to 446 h SR : as-annealed \|\| tested at 649 °C (1200 °F) \|\| 1 h to 90 h SR : as-annealed \|\| tested at 704 °C (1300 °F) \|\| 0.7 h to 16.3 h SR : as-annealed \|\| Master curve (LMP) \|\| 593 °C to 705 °C (1099 °F to 1301 °F) SR : annealed, aged at 593 °C (1100 °F) for 300 h \|\| tested at 593 °C (1100 °F) \|\| 27 h to 485 h SR : annealed, aged at 593 °C (1100 °F) for 300 h \|\| tested at 649 °C (1200 °F) \|\| 6.7 h to 46 h SR : annealed, aged at 593 °C (1100 °F) for 300 h \|\| tested at 704 °C (1300 °F) \|\| 1 h to 16.4 h SR : annealed, aged at 593 °C (1100 °F) for 300 h \|\| Master curve (LMP) \|\| 593 °C to 705 °C (1099 °F to 1301 °F) SR : annealed, aged at 649 °C (1200 °F) for 300 h \|\| tested at 649 °C (1200 °F) \|\| 1.9 h to 140 h SR : annealed plus 5% cold work \|\| tested at 704 °C (1300 °F) \|\| 7.9 h to 130 h SR : annealed, aged at 704 °C (1300 °F) for 300 h plus 5% cold work \|\| tested at 704 °C (1300 °F) \|\| 3 h to 76 h FSN : bending fatigue, sheet \|\| tested at 20 °C (68 °F), R = -1, annealed, maximum stress \|\| 2x10³ cycles to 1x10⁸ cycles RHO : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Inconel 686 (UNS N06686) (WNr 2.4606) (ISO/EN/DIN NiCr21Mo16W) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) G : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) v : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) K : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) TC : solid \|\| annealed \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| annealed \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| annealed \|\| -15 °C to 700 °C (5 °F to 1292 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain UTS : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : air \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 6.9x10⁴ cycles to 1x10⁷ cycles FSN : sea water \|\| tested at 20 °C (68 °F), R = -1, maximum stress \|\| 4.4x10⁴ cycles to 1x10⁷ cycles RHO : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SIGMA : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F)
Inconel 690 (UNS N06690) (WNr 2.4642) (ISO/EN/DIN NW6690/NiCr29Fe/NiCr29Fe9)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) G : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) v : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) K : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| annealed \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : annealed \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : annealed \|\| tested at 482 °C (900 °F) \|\| 30 h to 1x10⁵ h SR : annealed \|\| tested at 538 °C (1000 °F) \|\| 16 h to 1x10⁵ h SR : annealed \|\| tested at 593 °C (1100 °F) \|\| 1.6 h to 1x10⁵ h SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 1.4 h to 1x10⁵ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 15 h to 1x10⁵ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 1.3 h to 1,000 h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 2 h to 1,000 h SR : annealed \|\| tested at 982 °C (1800 °F) \|\| 3 h to 400 h SR : annealed \|\| tested at 1093 °C (2000 °F) \|\| 5 h to 120 h FEN : annealed \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 112 cycles to 7.4x10⁵ cycles RHO : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SIGMA : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)
Inconel 693 (UNS N06693)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) UTS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : annealed \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : annealed \|\| tested at 649 °C (1200 °F) \|\| 10 h to 3x10⁴ h SR : annealed \|\| tested at 704 °C (1300 °F) \|\| 10 h to 2x10⁴ h SR : annealed \|\| tested at 760 °C (1400 °F) \|\| 10 h to 2x10⁴ h SR : annealed \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : annealed \|\| tested at 982 °C (1800 °F) \|\| 10 h to 5x10⁴ h SR : annealed \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Inconel 700	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solution annealed & treated bar \|\| 20 °C to 977 °C (68 °F to 1790 °F) TC : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : solution annealed & treated bar \|\| aged at 871 °C (1600 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solution annealed & treated bar \|\| aged at 871 °C (1600 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : solution annealed & treated bar \|\| aged at 871 °C (1600 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) SR : solution annealed & treated bar \|\| tested at 816 °C (1500 °F) \|\| 3 h to 540 h SR : solution annealed & treated bar \|\| tested at 871 °C (1600 °F) \|\| 3 h to 1,000 h SR : solution annealed & treated bar \|\| tested at 927 °C (1700 °F) \|\| 4 h to 1,000 h SR : solution annealed & treated bar \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 0.1% plastic strain, solution annealed & treated bar \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 440 h CRS : 0.1% plastic strain, solution annealed & treated bar \|\| tested at 871 °C (1600 °F) \|\| 0.2 h to 335 h CRS : 0.1% plastic strain, solution annealed & treated bar \|\| tested at 927 °C (1700 °F) \|\| 0.2 h to 420 h CRS : 0.1% plastic strain, solution annealed & treated bar \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 0.3% plastic strain, solution annealed & treated bar \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 520 h CRS : 0.3% plastic strain, solution annealed & treated bar \|\| tested at 871 °C (1600 °F) \|\| 0.3 h to 750 h CRS : 0.3% plastic strain, solution annealed & treated bar \|\| tested at 927 °C (1700 °F) \|\| 0.4 h to 660 h CRS : 0.3% plastic strain, solution annealed & treated bar \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 0.5% plastic strain, solution annealed & treated bar \|\| tested at 816 °C (1500 °F) \|\| 0.9 h to 860 h CRS : 0.5% plastic strain, solution annealed & treated bar \|\| tested at 871 °C (1600 °F) \|\| 0.6 h to 485 h CRS : 0.5% plastic strain, solution annealed & treated bar \|\| tested at 927 °C (1700 °F) \|\| 0.7 h to 870 h CRS : 0.5% plastic strain, solution annealed & treated bar \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 1% plastic strain, solution annealed & treated bar \|\| tested at 816 °C (1500 °F) \|\| 1.9 h to 510 h CRS : 1% plastic strain, solution annealed & treated bar \|\| tested at 871 °C (1600 °F) \|\| 1 h to 850 h CRS : 1% plastic strain, solution annealed & treated bar \|\| tested at 927 °C (1700 °F) \|\| 1 h to 960 h CRS : 1% plastic strain, solution annealed & treated bar \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain
Inconel 702 (UNS N07702) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) E : solution treated & aged sheet, in tension \|\| longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : solution treated & aged sheet, in tension \|\| transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : solution treated & aged sheet, in tension \|\| average \|\| 20 °C to 260 °C (68 °F to 500 °F) E : solution treated & aged sheet, in compression \|\| longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : solution treated & aged sheet, in compression \|\| transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : solution treated & aged sheet, in compression \|\| average \|\| 20 °C to 260 °C (68 °F to 500 °F) TC : solid \|\| solution annealed \|\| -150 °C to 1200 °C (-238 °F to 2192 °F) TC : solid \|\| age-hardened \|\| -150 °C to 800 °C (-238 °F to 1472 °F) TD : solid \|\| solution annealed \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| age-hardened \|\| 20 °C to 800 °C (68 °F to 1472 °F) SH : solid \|\| 0 °C to 1038 °C (32 °F to 1900 °F) UTS : AMS 5550, 0.127 mm (0.005 inch) strip \|\| 0.5 h \|\| 20 °C to 1032 °C (68 °F to 1889 °F) UTS : AMS 5550, 0.127 mm (0.005 inch) strip \|\| 1000 h \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 0.5 h \|\| 20 °C to 981 °C (68 °F to 1798 °F) UTS : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 1000 h \|\| 20 °C to 975 °C (68 °F to 1787 °F) YS : AMS 5550, 0.127 mm (0.005 inch) strip \|\| 0.5 h \|\| 20 °C to 1080 °C (68 °F to 1976 °F) YS : AMS 5550, 0.127 mm (0.005 inch) strip \|\| 1000 h \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 0.5 h \|\| 20 °C to 981 °C (68 °F to 1798 °F) YS : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 1000 h \|\| 20 °C to 981 °C (68 °F to 1798 °F) YSC : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 0.5 h \|\| 20 °C to 981 °C (68 °F to 1798 °F) YSC : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 1000 h \|\| 20 °C to 962 °C (68 °F to 1763 °F) %El : AMS 5550, 0.127 mm (0.005 inch) strip \|\| 20 °C to 1900 °C (68 °F to 3452 °F) %El : AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 20 °C to 1800 °C (68 °F to 3272 °F) SR : AMS 5550, 0.127 mm (0.005 inch) strip, longitudinal \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 100 h SR : AMS 5550, 0.127 mm (0.005 inch) strip, longitudinal \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.127 mm (0.005 inch) strip, longitudinal \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.127 mm (0.005 inch) strip, longitudinal \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.127 mm (0.005 inch) strip, longitudinal \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) SR : AMS 5550, 0.508 mm (0.02 inch) sheet, transverse \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.508 mm (0.02 inch) sheet, transverse \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.508 mm (0.02 inch) sheet, transverse \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.508 mm (0.02 inch) sheet, transverse \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 0.508 mm (0.02 inch) sheet, transverse \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) SR : AMS 5550, 1.02 mm (0.04 inch) sheet, longitudinal \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, longitudinal \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, longitudinal \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) SR : AMS 5550, 1.02 mm (0.04 inch) sheet, transverse \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, transverse \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, transverse \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, transverse \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5550, 1.02 mm (0.04 inch) sheet, transverse \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) SR : AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| Master curve (LMP) \|\| 426 °C to 761 °C (799 °F to 1402 °F) FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, smooth \|\| tested at 316 °C (600 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, smooth \|\| tested at 538 °C (1000 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, notched \|\| tested at 316 °C (600 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.27 mm (0.05 inch) sheet, notched \|\| tested at 538 °C (1000 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 760 °C (1400 °F), R = 0.6, axial, maximum stress \|\| 1x10⁵ cycles to 1.1x10⁶ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 204 °C (400 °F), R = 0.2, axial, maximum stress \|\| 6x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 427 °C (800 °F), R = 0.2, axial, maximum stress \|\| 4x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 649 °C (1200 °F), R = 0.2, axial, maximum stress \|\| 5.4x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 760 °C (1400 °F), R = 0.2, axial, maximum stress \|\| 5x10³ cycles to 1x10⁶ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 871 °C (1600 °F), R = 0.2, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.01, axial, maximum stress \|\| 2.25x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 316 °C (600 °F), R = 0.01, axial, maximum stress \|\| 3.2x10⁵ cycles to 1.2x10⁶ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 760 °C (1400 °F), R = 0.01, axial, maximum stress \|\| 1.25x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5550, 1.02 mm (0.04 inch) sheet, smooth \|\| tested at 982 °C (1800 °F), R = 0.01, axial, maximum stress \|\| 6x10⁴ cycles to 1.5x10⁶ cycles CRS : 0.2% plastic strain, AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, AMS 5550, 1.27 mm (0.05 inch) sheet, transverse \|\| Master curve (LMP) \|\| 396 °C to 761 °C (745 °F to 1402 °F) CRS : 0.05% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 2 h to 1,000 h CRS : 0.05% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 0.6 h to 820 h CRS : 0.05% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 1 h to 100 h CRS : 0.1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 2 h to 150 h CRS : 0.1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 4 h to 70 h CRS : 0.1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F) \|\| 9 h to 400 h CRS : 0.1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 0.3% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 50 h to 1,000 h CRS : 0.3% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 8 h to 460 h CRS : 0.3% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 170 h CRS : 0.3% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F) \|\| 30 h to 840 h CRS : 0.3% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 0.5% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 80 h to 1,000 h CRS : 0.5% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 17 h to 370 h CRS : 0.5% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F) \|\| 50 h to 370 h CRS : 0.5% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 140 h to 1,000 h CRS : 1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F) \|\| 25 h to 300 h CRS : 1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F) \|\| 80 h to 400 h CRS : 1% plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 649 °C (1200 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 10 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 30 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5550, 1.02 mm (0.04 inch) sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain HE : solid \|\| 427 °C to 816 °C (800 °F to 1500 °F) RHO : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SIGMA : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F)
Inconel 706 (UNS N09706) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : solid \|\| -196 °C to 816 °C (-321 °F to 1500 °F) DLL : solid \|\| -196 °C to 816 °C (-321 °F to 1500 °F) MTE : solid \|\| -196 °C to 816 °C (-321 °F to 1500 °F) CTE : solid \|\| -196 °C to 816 °C (-321 °F to 1500 °F) E : solid \|\| -196 °C to 700 °C (-321 °F to 1292 °F) G : solid \|\| -196 °C to 700 °C (-321 °F to 1292 °F) v : solid \|\| -196 °C to 700 °C (-321 °F to 1292 °F) K : solid \|\| -196 °C to 700 °C (-321 °F to 1292 °F) TC : solid \|\| precipitation hardened \|\| -196 °C to 600 °C (-321 °F to 1112 °F) TD : solid \|\| precipitation hardened \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| precipitation hardened \|\| 20 °C to 700 °C (68 °F to 1292 °F) SSC : annealed rod \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.01 mm/mm strain SSC : sheet & bar, solution treated at 954 °C (1750 °F) \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain SSCC : 5x10^-⁴/s, cast \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.455 mm/mm strain SSCC : 0.001/s, cast \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.443 mm/mm strain SSCC : 0.01/s, cast \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.31 mm/mm strain SSCC : 0.01/s, cast \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.29 mm/mm strain SSCC : 0.01/s, cast \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.01/s, cast \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.43 mm/mm strain SSCC : 0.01/s, cast \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.45 mm/mm strain SSCC : 0.1/s, cast \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.337 mm/mm strain SSCC : 1/s, cast \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.322 mm/mm strain UTS : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) UTS : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) YS : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) YS : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) YSC : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) YSC : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, longitudinal \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : forged bar, solution treated & aged, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| 0.5 h hold, transverse \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) %El : cold-rolled sheet \|\| heat-treated, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| -196 °C to 760 °C (-321 °F to 1400 °F) SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 593 °C (1100 °F) \|\| 5 h to 1x10⁴ h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 649 °C (1200 °F) \|\| 5 h to 1x10⁴ h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 704 °C (1300 °F) \|\| 5 h to 1x10⁴ h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| tested at 760 °C (1400 °F) \|\| 5 h to 1x10⁴ h SR : optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F) \|\| Master curve (LMP) \|\| 426 °C to 761 °C (799 °F to 1402 °F) FEN : optimized for tensile strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/732 °C (1350 °F)/621 °C (1150 °F) \|\| tested at 20 °C (68 °F), R = -1, hot-rolled plate, total strain range \|\| 138 cycles to 1x10⁶ cycles FEN : optimized for tensile strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/732 °C (1350 °F)/621 °C (1150 °F) \|\| tested at 538 °C (1000 °F), R = -1, hot-rolled plate, total strain range \|\| 138 cycles to 1x10⁶ cycles FEN : optimized for tensile strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/732 °C (1350 °F)/621 °C (1150 °F) \|\| tested at 649 °C (1200 °F), R = -1, hot-rolled plate, total strain range \|\| 100 cycles to 1x10⁶ cycles FSN : optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, hot-rolled rod, maximum stress \|\| 2.17x10⁵ cycles to 1x10⁸ cycles FSN : optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, hot-rolled rod, maximum stress \|\| 2.46x10⁵ cycles to 1x10⁸ cycles FSN : optimized for tensile strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/732 °C (1350 °F)/621 °C (1150 °F) \|\| tested at 20 °C (68 °F), R = -1, rotating beam, hot-rolled rod, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : optimized for tensile strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/732 °C (1350 °F)/621 °C (1150 °F) \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, hot-rolled rod, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), smooth \|\| tested at 316 °C (600 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), smooth \|\| tested at 538 °C (1000 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), notched \|\| tested at 316 °C (600 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : optimized for rupture strength, 982 °C (1800 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F), notched \|\| tested at 538 °C (1000 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F), transverse \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F), transverse \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F), transverse \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, optimized for rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/660 °C (1220 °F)/621 °C (1150 °F), transverse \|\| Master curve (LMP) \|\| 537 °C to 650 °C (998 °F to 1202 °F) RHO : solid \|\| -196 °C to 600 °C (-321 °F to 1112 °F) SIGMA : solid \|\| -196 °C to 600 °C (-321 °F to 1112 °F)
Inconel 713C (UNS N07713) (AMS 5391) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) D : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) TC : liquid \|\| 1350 °C to 1500 °C (2462 °F to 2732 °F) TD : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) TD : liquid \|\| 1050 °C to 1500 °C (1922 °F to 2732 °F) SH : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) UTS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : as-cast \|\| tested at 816 °C (1500 °F) \|\| 10 h to 850 h SR : as-cast \|\| tested at 871 °C (1600 °F) \|\| 7 h to 800 h SR : as-cast \|\| tested at 927 °C (1700 °F) \|\| 7 h to 200 h SR : as-cast \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) FSN : axial fatigue \|\| tested at 927 °C (1700 °F), R = -1, maximum stress \|\| 7x10⁴ cycles to 2.5x10⁷ cycles CRS : 0.1% plastic strain, as-cast \|\| tested at 816 °C (1500 °F) \|\| 0.1 h to 140 h CRS : 0.1% plastic strain, as-cast \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 180 h CRS : 0.1% plastic strain, as-cast \|\| tested at 927 °C (1700 °F) \|\| 0.2 h to 290 h CRS : 0.1% plastic strain, as-cast \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 0.3% plastic strain, as-cast \|\| tested at 816 °C (1500 °F) \|\| 0.8 h to 410 h CRS : 0.3% plastic strain, as-cast \|\| tested at 871 °C (1600 °F) \|\| 0.7 h to 430 h CRS : 0.3% plastic strain, as-cast \|\| tested at 927 °C (1700 °F) \|\| 1 h to 800 h CRS : 0.3% plastic strain, as-cast \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 0.5% plastic strain, as-cast \|\| tested at 816 °C (1500 °F) \|\| 2 h to 810 h CRS : 0.5% plastic strain, as-cast \|\| tested at 871 °C (1600 °F) \|\| 1 h to 750 h CRS : 0.5% plastic strain, as-cast \|\| tested at 927 °C (1700 °F) \|\| 2 h to 700 h CRS : 0.5% plastic strain, as-cast \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) CRS : 1% plastic strain, as-cast \|\| tested at 816 °C (1500 °F) \|\| 4 h to 900 h CRS : 1% plastic strain, as-cast \|\| tested at 871 °C (1600 °F) \|\| 3 h to 820 h CRS : 1% plastic strain, as-cast \|\| tested at 927 °C (1700 °F) \|\| 4 h to 900 h CRS : 1% plastic strain, as-cast \|\| Master curve (LMP) \|\| 815 °C to 927 °C (1499 °F to 1700 °F) IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, as-cast \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, as-cast \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, as-cast \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast \|\| 100 h \|\| 0 to 0.01 mm/mm strain Vis : liquid \|\| 1342 °C to 1439 °C (2447 °F to 2622 °F) RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Inconel 713LC (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) D : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : liquid \|\| 1420 °C to 1560 °C (2588 °F to 2840 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) TC : liquid \|\| 1350 °C to 1500 °C (2462 °F to 2732 °F) TD : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) TD : liquid \|\| 1050 °C to 1500 °C (1922 °F to 2732 °F) SH : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SSC : laser powder bed fusion \|\| tested at 23 °C (73 °F), 8.3x10^-⁴/s, as-built, energy density of 0.157 J/mm \|\| 0 to 0.118 mm/mm strain SSC : laser powder bed fusion \|\| tested at 23 °C (73 °F), 8.3x10^-⁴/s, as-built, energy density of 0.176 J/mm \|\| 0 to 0.94 mm/mm strain SSC : laser powder bed fusion \|\| tested at 23 °C (73 °F), 8.3x10^-⁴/s, solution treated at 1175 °C (2147 °F), energy density of 0.157 J/mm \|\| 0 to 0.63 mm/mm strain SR : as-cast \|\| tested at 730 °C (1346 °F) \|\| 2,200 h to 6,200 h SR : as-cast \|\| tested at 750 °C (1382 °F) \|\| 1,000 h to 3,300 h SR : as-cast \|\| tested at 800 °C (1472 °F) \|\| 60 h to 6,500 h SR : as-cast \|\| tested at 850 °C (1562 °F) \|\| 60 h to 3,500 h SR : as-cast \|\| tested at 900 °C (1652 °F) \|\| 30 h to 3,300 h SR : as-cast \|\| tested at 950 °C (1742 °F) \|\| 40 h to 2,800 h SR : as-cast \|\| tested at 1000 °C (1832 °F) \|\| 120 h to 950 h SR : as-cast \|\| Master curve (LMP) \|\| 730 °C to 1001 °C (1346 °F to 1834 °F) CRS : 1% plastic strain, as-cast \|\| tested at 730 °C (1346 °F) \|\| 600 h to 1,800 h CRS : 1% plastic strain, as-cast \|\| tested at 800 °C (1472 °F) \|\| 60 h to 4,000 h CRS : 1% plastic strain, as-cast \|\| tested at 850 °C (1562 °F) \|\| 115 h to 2,000 h CRS : 1% plastic strain, as-cast \|\| tested at 900 °C (1652 °F) \|\| 30 h to 2,300 h CRS : 1% plastic strain, as-cast \|\| tested at 950 °C (1742 °F) \|\| 30 h to 2,000 h CRS : 1% plastic strain, as-cast \|\| Master curve (LMP) \|\| 730 °C to 951 °C (1346 °F to 1744 °F) Vis : liquid \|\| 1342 °C to 1439 °C (2447 °F to 2622 °F)
Inconel 718 (UNS N07718) (WNr 2.4668) (ISO/EN/DIN NiCr19Fe19Nb5Mo3/NiCr19NbMo) (ASTM B637/B670) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) DLL : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) MTE : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) CTE : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) E : conventionally processed \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) E : laser powder bed fusion \|\| stress relieved, HIPed and aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) G : conventionally processed \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) v : conventionally processed \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) K : conventionally processed \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) TC : solid \|\| -266 °C to 1093 °C (-447 °F to 2000 °F) TD : solid \|\| conventionally processed \|\| -170 °C to 515 °C (-274 °F to 959 °F) TD : solid \|\| directionally solidified \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| as-received \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SH : solid \|\| 4 h at 980 °C (1796 °F), water cooled \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SH : solid \|\| 8 h at 720 °C (1328 °F)/8 h at 620 °C (1148 °F) \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SSC : investment casting, solution treated and aged, AMS 5383 \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.225 mm/mm strain SSC : 15 mm (0.591 inch) bar \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, solution treated \|\| 0 to 0.4 mm/mm strain SSC : 15 mm (0.591 inch) bar \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, over aged \|\| 0 to 0.3 mm/mm strain SSC : 15 mm (0.591 inch) bar \|\| tested at 20 °C (68 °F), 5x10^-⁴/s, severely over aged \|\| 0 to 0.3 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 100 °C (212 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 200 °C (392 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 300 °C (572 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 400 °C (752 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 500 °C (932 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 550 °C (1022 °F), 5x10^-⁴/s \|\| 0 to 0.13 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 600 °C (1112 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 649 °C (1200 °F), 5x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar \|\| tested at 700 °C (1292 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 100 °C (212 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 200 °C (392 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 300 °C (572 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 400 °C (752 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 500 °C (932 °F), 5x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 600 °C (1112 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 20% \|\| tested at 649 °C (1200 °F), 5x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 100 °C (212 °F), 5x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 200 °C (392 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 300 °C (572 °F), 5x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 400 °C (752 °F), 5x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 500 °C (932 °F), 5x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 600 °C (1112 °F), 5x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 10% \|\| tested at 649 °C (1200 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 20 °C (68 °F), 5x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 100 °C (212 °F), 5x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 200 °C (392 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 300 °C (572 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 400 °C (752 °F), 5x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 500 °C (932 °F), 5x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 600 °C (1112 °F), 5x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : peak aged 15 mm (0.591 inch) bar cold-rolled 5% \|\| tested at 649 °C (1200 °F), 5x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 0 degrees to build plane \|\| 0 to 0.175 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 10 degrees to build plane \|\| 0 to 0.222 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 20 degrees to build plane \|\| 0 to 0.178 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 30 degrees to build plane \|\| 0 to 0.225 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 40 degrees to build plane \|\| 0 to 0.186 mm/mm strain SSC : laser powder bed fusion, as-built, Du et. al. \|\| tested at 20 °C (68 °F), 2.38x10^-⁴/s, 45 degrees to build plane \|\| 0 to 0.21 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), vertical, 980 °C (1796 °F)/720 °C (1328 °F)/620 °C (1148 °F), unknown strain rate \|\| 0 to 0.171 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), horizontal, 980 °C (1796 °F)/720 °C (1328 °F)/620 °C (1148 °F), unknown strain rate \|\| 0 to 0.137 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), vertical, 760 °C (1400 °F)/650 °C (1202 °F), unknown strain rate \|\| 0 to 0.16 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), horizontal, 760 °C (1400 °F)/650 °C (1202 °F), unknown strain rate \|\| 0 to 0.126 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), vertical, HIPed 1170 °C (2138 °F)/800 °C (1472 °F)/980 °C (1796 °F)/760 °C (1400 °F)/650 °C (1202 °F), unknown strain rate \|\| 0 to 0.2 mm/mm strain SSC : laser powder bed fusion, He et. al. \|\| tested at 20 °C (68 °F), horizontal, HIPed 1170 °C (2138 °F)/800 °C (1472 °F)/980 °C (1796 °F)/760 °C (1400 °F)/650 °C (1202 °F), unknown strain rate \|\| 0 to 0.167 mm/mm strain SSC : laser powder bed fusion, Georgilas et. al. \|\| tested at 650 °C (1202 °F), horizontal, as-built, unknown strain rate \|\| 0 to 0.143 mm/mm strain SSC : laser powder bed fusion, Georgilas et. al. \|\| tested at 650 °C (1202 °F), horizontal, 980 °C (1796 °F) + aging, unknown strain rate \|\| 0 to 0.36 mm/mm strain SSC : laser powder bed fusion, Georgilas et. al. \|\| tested at 650 °C (1202 °F), horizontal, 1200 °C (2192 °F) + aging, unknown strain rate \|\| 0 to 0.46 mm/mm strain SSC : laser powder bed fusion, Georgilas et. al. \|\| tested at 650 °C (1202 °F), horizontal, HIPed + aging, unknown strain rate \|\| 0 to 0.14 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, as-deposited, vertical \|\| 0 to 0.28 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, as-deposited, horizontal \|\| 0 to 0.29 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, AMS heat-treated, vertical \|\| 0 to 0.118 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, AMS heat-treated, horizontal \|\| 0 to 0.12 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, API heat-treated, vertical \|\| 0 to 0.166 mm/mm strain SSC : wire + arc additive manufacturing (WAAM), Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, API heat-treated, horizontal \|\| 0 to 0.25 mm/mm strain SSC : 3 mm (0.118 inch) thick sheet, Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, solution annealed \|\| 0 to 0.43 mm/mm strain SSC : 3 mm (0.118 inch) thick sheet, Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, AMS heat-treated \|\| 0 to 0.2 mm/mm strain SSC : 3 mm (0.118 inch) thick sheet, Kindermann et. al. \|\| tested at 20 °C (68 °F), 5.2x10^-⁴/s, API heat-treated \|\| 0 to 0.26 mm/mm strain SSCC : 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 100/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.5 mm/mm strain SSCC : 1400/s \|\| tested at 800 °C (1472 °F), annealed \|\| 0 to 0.16 mm/mm strain SSCC : 1500/s \|\| tested at 20 °C (68 °F), annealed \|\| 0 to 0.222 mm/mm strain SSCC : 1500/s \|\| tested at 1100 °C (2012 °F), annealed \|\| 0 to 0.125 mm/mm strain SSCC : 1700/s \|\| tested at 20 °C (68 °F), aged \|\| 0 to 0.144 mm/mm strain SSCC : 1800/s \|\| tested at 1000 °C (1832 °F), aged \|\| 0 to 0.123 mm/mm strain SSCC : 1900/s \|\| tested at 20 °C (68 °F), annealed \|\| 0 to 0.235 mm/mm strain SSCC : 1900/s \|\| tested at 400 °C (752 °F), annealed \|\| 0 to 0.21 mm/mm strain SSCC : 1900/s \|\| tested at 800 °C (1472 °F), aged \|\| 0 to 0.134 mm/mm strain SSCC : 1900/s \|\| tested at 1100 °C (2012 °F), annealed \|\| 0 to 0.195 mm/mm strain SSCC : 1900/s \|\| tested at 1100 °C (2012 °F), aged \|\| 0 to 0.125 mm/mm strain SSCC : 2000/s \|\| tested at 800 °C (1472 °F), annealed \|\| 0 to 0.26 mm/mm strain SSCC : 2000/s \|\| tested at 1000 °C (1832 °F), annealed \|\| 0 to 0.2 mm/mm strain SSCC : 2400/s \|\| tested at 20 °C (68 °F), annealed \|\| 0 to 0.23 mm/mm strain SSCC : 2400/s \|\| tested at 1100 °C (2012 °F), annealed \|\| 0 to 0.161 mm/mm strain SSCC : 2500/s \|\| tested at 800 °C (1472 °F), annealed \|\| 0 to 0.224 mm/mm strain UTS : other conditions \|\| cold-rolled & aged sheet \|\| -196 °C to 538 °C (-321 °F to 1000 °F) UTS : other conditions \|\| hot-rolled, annealed & aged bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : other conditions \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) UTS : other conditions \|\| cold-rolled, annealed & aged sheet \|\| -78 °C to 537 °C (-109 °F to 998 °F) UTS : other conditions \|\| VIM/VAR forging, aged \|\| 20 °C to 620 °C (68 °F to 1148 °F) UTS : peak aged \|\| as-aged \|\| 20 °C to 700 °C (68 °F to 1292 °F) UTS : peak aged \|\| as-aged plus 20% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : peak aged \|\| as-aged plus 10% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : peak aged \|\| as-aged plus 5% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : peak aged \|\| as-aged plus 5% cold-rolled & stress relief \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : laser powder bed fusion \|\| stress relieved, HIPed and aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : other conditions \|\| cold-rolled & aged sheet \|\| -196 °C to 538 °C (-321 °F to 1000 °F) YS : other conditions \|\| hot-rolled, annealed & aged bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : other conditions \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) YS : other conditions \|\| cold-rolled, annealed & aged sheet \|\| -78 °C to 538 °C (-109 °F to 1000 °F) YS : other conditions \|\| VIM/VAR forging, aged \|\| 20 °C to 620 °C (68 °F to 1148 °F) YS : peak aged \|\| as-aged \|\| 20 °C to 700 °C (68 °F to 1292 °F) YS : peak aged \|\| as-aged plus 20% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : peak aged \|\| as-aged plus 10% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : peak aged \|\| as-aged plus 5% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : peak aged \|\| as-aged plus 5% cold-rolled & stress relief \|\| 20 °C to 600 °C (68 °F to 1112 °F) YS : laser powder bed fusion \|\| stress relieved, HIPed and aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : other conditions \|\| cold-rolled & aged sheet \|\| -196 °C to 538 °C (-321 °F to 1000 °F) %El : other conditions \|\| hot-rolled, annealed & aged bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : other conditions \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) %El : other conditions \|\| cold-rolled, annealed & aged sheet \|\| -78 °C to 538 °C (-109 °F to 1000 °F) %El : peak aged \|\| as-aged \|\| 20 °C to 700 °C (68 °F to 1292 °F) %El : peak aged \|\| as-aged plus 20% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : peak aged \|\| as-aged plus 10% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : peak aged \|\| as-aged plus 5% cold-rolled \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : peak aged \|\| as-aged plus 5% cold-rolled & stress relief \|\| 20 °C to 600 °C (68 °F to 1112 °F) %El : laser powder bed fusion \|\| stress relieved, HIPed and aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : solution treated at 982 °C (1800 °F), duplex aged, smooth 15.9 mm (0.625 inch) diameter bar \|\| tested at 538 °C (1000 °F) \|\| 2,300 h to 5,000 h SR : solution treated at 982 °C (1800 °F), duplex aged, smooth 15.9 mm (0.625 inch) diameter bar \|\| tested at 593 °C (1100 °F) \|\| 70 h to 1x10⁴ h SR : solution treated at 982 °C (1800 °F), duplex aged, smooth 15.9 mm (0.625 inch) diameter bar \|\| tested at 649 °C (1200 °F) \|\| 7 h to 8,000 h SR : solution treated at 982 °C (1800 °F), duplex aged, smooth 15.9 mm (0.625 inch) diameter bar \|\| tested at 704 °C (1300 °F) \|\| 30 h to 7,000 h SR : solution treated at 982 °C (1800 °F), duplex aged, smooth 15.9 mm (0.625 inch) diameter bar \|\| Master curve (LMP) \|\| 537 °C to 705 °C (998 °F to 1301 °F) SR : solution treated at 982 °C (1800 °F), duplex aged, notched 15.9 mm (0.625 inch) diameter bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 6,000 h SR : solution treated at 982 °C (1800 °F), duplex aged, notched 15.9 mm (0.625 inch) diameter bar \|\| tested at 704 °C (1300 °F) \|\| 20 h to 800 h SR : solution treated at 982 °C (1800 °F), duplex aged, notched 15.9 mm (0.625 inch) diameter bar \|\| Master curve (LMP) \|\| 649 °C to 705 °C (1200 °F to 1301 °F) SR : solution treated at 954 °C (1750 °F), duplex aged \|\| tested at 538 °C (1000 °F) \|\| 25 h to 2.1x10⁴ h SR : solution treated at 954 °C (1750 °F), duplex aged \|\| tested at 593 °C (1100 °F) \|\| 25 h to 3.3x10⁴ h SR : solution treated at 954 °C (1750 °F), duplex aged \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : solution treated at 954 °C (1750 °F), duplex aged \|\| tested at 704 °C (1300 °F) \|\| 10 h to 6,100 h SR : solution treated at 954 °C (1750 °F), duplex aged \|\| tested at 760 °C (1400 °F) \|\| 4 h to 760 h SR : solution treated at 954 °C (1750 °F), duplex aged \|\| Master curve (LMP) \|\| 537 °C to 761 °C (998 °F to 1402 °F) FEN : solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 100 cycles to 5.1x10⁴ cycles FEN : solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 80 cycles to 1.7x10⁵ cycles FEN : solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 60 cycles to 9x10⁴ cycles FEN : solution treated at 1066 °C (1950 °F) for 1 h, aged at 718 °C (1325 °F) & 621 °C (1150 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 100 cycles to 1x10⁴ cycles FEN : solution annealed at 1066 °C (1950 °F) for 1 h, aged at 621 °C (1150 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 120 cycles to 1x10³ cycles FEN : solution annealed at 1066 °C (1950 °F) for 1 h, aged at 621 °C (1150 °F) \|\| tested at 538 °C (1000 °F), R = -1, axial, total strain range \|\| 160 cycles to 1.1x10³ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 25 °C (77 °F), R = 0, axial, K_t = 3, total strain range \|\| 400 cycles to 1.1x10⁵ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 25 °C (77 °F), R = 0, axial, K_t = 3, elastic strain amplitude \|\| 400 cycles to 1.1x10⁵ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 25 °C (77 °F), R = 0, axial, K_t = 3, plastic strain amplitude \|\| 400 cycles to 1.1x10⁵ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 550 °C (1022 °F), R = -1, axial, plastic strain amplitude \|\| 100 cycles to 2.59x10³ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 650 °C (1202 °F), R = 0, axial, K_t = 3, total strain range \|\| 180 cycles to 4.4x10⁵ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 650 °C (1202 °F), R = 0, axial, K_t = 3, elastic strain amplitude \|\| 180 cycles to 4.4x10⁵ cycles FEN : solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) \|\| tested at 650 °C (1202 °F), R = 0, axial, K_t = 3, plastic strain amplitude \|\| 180 cycles to 4.4x10⁵ cycles FEN : electron beam powder bed fusion \|\| tested at 550 °C (1022 °F), R = 0, axial, total strain amplitude, vertical \|\| 700 cycles to 1x10⁶ cycles FEN : electron beam powder bed fusion \|\| tested at 550 °C (1022 °F), R = 0, axial, total strain amplitude, horizontal \|\| 250 cycles to 2x10⁵ cycles FEN : electron beam powder bed fusion \|\| tested at 550 °C (1022 °F), R = 0, axial, total strain amplitude, average \|\| 250 cycles to 1x10⁶ cycles FEN : forgings, double aged \|\| tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, total strain range \|\| 2.6x10³ cycles to 2.5x10⁴ cycles FEN : forgings, double aged \|\| tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, elastic strain range \|\| 2.8x10³ cycles to 2x10⁴ cycles FEN : forgings, double aged \|\| tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, plastic strain range \|\| 2.8x10³ cycles to 2x10⁴ cycles FEN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, total strain range \|\| 1x10³ cycles to 6.6x10⁴ cycles FEN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, elastic strain range \|\| 1.9x10³ cycles to 6.6x10⁴ cycles FEN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, plastic strain range \|\| 1.9x10³ cycles to 1.4x10⁵ cycles FEN : forgings, double aged \|\| tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, total strain range \|\| 540 cycles to 1.2x10⁵ cycles FEN : forgings, double aged \|\| tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, elastic strain range \|\| 400 cycles to 8x10⁴ cycles FEN : forgings, double aged \|\| tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, plastic strain range \|\| 400 cycles to 8x10⁴ cycles FSN : hot-rolled bar, annealed at 954 °C (1750 °F) for 1 h, air cooled, aged at 718 °C (1325 °F) for 8 h, furnace cooled to 621 °C (1150 °F) held for 18 h \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : hot-rolled bar, annealed at 954 °C (1750 °F) for 1 h, air cooled, aged at 718 °C (1325 °F) for 8 h, furnace cooled to 621 °C (1150 °F) held for 18 h \|\| tested at 316 °C (600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : hot-rolled bar, annealed at 954 °C (1750 °F) for 1 h, air cooled, aged at 718 °C (1325 °F) for 8 h, furnace cooled to 621 °C (1150 °F) held for 18 h \|\| tested at 538 °C (1000 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : hot-rolled bar, annealed at 954 °C (1750 °F) for 1 h, air cooled, aged at 718 °C (1325 °F) for 8 h, furnace cooled to 621 °C (1150 °F) held for 18 h \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : annealed & aged, UTS at 20 °C (68 °F) of 1.33 GPa (193 ksi) \|\| tested at 21 °C (70 °F), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : annealed & aged, UTS at 20 °C (68 °F) of 1.33 GPa (193 ksi) \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁷ cycles FSN : annealed & aged, UTS at 20 °C (68 °F) of 1.33 GPa (193 ksi) \|\| tested at -252.7 °C (-422.9 °F), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 800 cycles to 4x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at 20 °C (68 °F), K_t = 3.5, R = -1, axial, maximum stress \|\| 1.5x10³ cycles to 1x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at -196.1 °C (-321.1 °F), K_t = 3.5, R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : solution treated, UTS at 20 °C (68 °F) of 517 MPa (75 ksi) \|\| tested at -253.1 °C (-423.7 °F), K_t = 3.5, R = -1, axial, maximum stress \|\| 3x10³ cycles to 1x10⁶ cycles FSN : ring forgings, heat-treated at 980 °C (1796 °F) & 620 °C (1148 °F), UTS = 1.25 GPa (181 ksi), YS = 910 MPa (132 ksi) \|\| tested at 20 °C (68 °F), R = -1, rotary bending, maximum stress \|\| 4.8x10⁴ cycles to 1x10⁸ cycles FSN : ring forgings, heat-treated at 980 °C (1796 °F) & 620 °C (1148 °F), UTS = 1.25 GPa (181 ksi), YS = 910 MPa (132 ksi) \|\| tested at 20 °C (68 °F), K_t = 2.7, R = -1, rotary bending, maximum stress \|\| 4.7x10⁴ cycles to 1x10⁸ cycles FSN : solution treated & aged sheet, grain size ASTM 12, UTS = 1.55 GPa (225 ksi) \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 3x10⁵ cycles to 1.4x10⁸ cycles FSN : solution treated & aged, grain size ASTM 10 \|\| tested at 20 °C (68 °F), R = -1, ultrasonic at 19.5 kHz, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude \|\| 3.3x10⁵ cycles to 1x10⁹ cycles FSN : solution treated & aged, grain size ASTM 10 \|\| tested at 20 °C (68 °F), R = -1, rotary bending, 55 Hz, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude \|\| 4x10⁴ cycles to 1x10⁸ cycles FSN : solution treated & aged, grain size ASTM 10 \|\| tested at 20 °C (68 °F), R = -1, axial, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude \|\| 2x10⁵ cycles to 1.3x10⁸ cycles FSN : solution treated & aged, grain size ASTM 10 \|\| tested at 20 °C (68 °F), R = -1, ultrasonic at 20 kHz, UTS = 1.39 GPa (202 ksi), YS = 1.22 GPa (177 ksi), stress amplitude \|\| 3.8x10⁵ cycles to 1x10⁹ cycles FSN : forgings, double aged \|\| tested at 350 °C (662 °F), R = 0.05, axial, ASTM 6/7, maximum stress \|\| 5x10³ cycles to 1.2x10⁵ cycles FSN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 6/7, maximum stress \|\| 2.2x10³ cycles to 1.4x10⁵ cycles FSN : forgings, double aged \|\| tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, stress range \|\| 4x10³ cycles to 1x10⁵ cycles FSN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, stress range \|\| 2x10³ cycles to 5x10⁵ cycles FSN : forgings, double aged \|\| tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, stress range \|\| 1x10³ cycles to 2.5x10⁵ cycles FSN : forgings, double aged \|\| tested at 350 °C (662 °F), R = 0.05, axial, ASTM 10/11, maximum stress \|\| 6.7x10³ cycles to 6.2x10⁵ cycles FSN : forgings, double aged \|\| tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 10/11, maximum stress \|\| 4.1x10³ cycles to 9x10⁵ cycles FSN : solution treated, TIG welded \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 15 minutes \|\| 200 °C to 1050 °C (392 °F to 1922 °F) HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 30 minutes \|\| 200 °C to 1050 °C (392 °F to 1922 °F) HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 1 h \|\| 200 °C to 1200 °C (392 °F to 2192 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 15 minutes \|\| 300 °C to 1050 °C (572 °F to 1922 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 30 minutes \|\| 250 °C to 1000 °C (482 °F to 1832 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 1 h \|\| 400 °C to 1050 °C (752 °F to 1922 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 15 minutes \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 30 minutes \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 1 h \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : as-rolled \|\| not oxidized \|\| 275 °C to 1100 °C (527 °F to 2012 °F) Vis : liquid \|\| 1350 °C to 1475 °C (2462 °F to 2687 °F) ST : liquid \|\| 1529 °C to 1727 °C (2784 °F to 3140 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| full hardened \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| full hardened \|\| 20 °C to 1093 °C (68 °F to 2000 °F)
Inconel 718SPF (UNS N07719) (AMS 5596G) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) DLL : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) MTE : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) CTE : solid \|\| -240 °C to 871 °C (-400 °F to 1600 °F) E : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) G : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) v : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) K : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) TC : solid \|\| -266 °C to 1093 °C (-447 °F to 2000 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSC : annealed & aged \|\| tested at 20 °C (68 °F), 1.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : annealed & quenched \|\| tested at 20 °C (68 °F), 1.3x10^-⁴/s \|\| 0 to 0.21 mm/mm strain UTS* : mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet \|\| room temperature value UTS* : aged, 0.508 mm (0.02 inch) thick sheet \|\| room temperature value UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 13% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 19% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 33% cold worked \|\| room temperature value YS* : mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet \|\| room temperature value YS* : aged, 0.508 mm (0.02 inch) thick sheet \|\| room temperature value YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 13% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 19% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 33% cold worked \|\| room temperature value %El* : mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet \|\| room temperature value %El* : aged, 0.508 mm (0.02 inch) thick sheet \|\| room temperature value %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 13% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 19% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 33% cold worked \|\| room temperature value SR : aged sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 25 h HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 15 minutes \|\| 200 °C to 1050 °C (392 °F to 1922 °F) HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 1 h \|\| 200 °C to 1200 °C (392 °F to 2192 °F) HE : oxidized at 1142 °C (2088 °F) \|\| oxidized for 30 minutes \|\| 200 °C to 1050 °C (392 °F to 1922 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 15 minutes \|\| 300 °C to 1050 °C (572 °F to 1922 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 1 h \|\| 400 °C to 1050 °C (752 °F to 1922 °F) HE : oxidized at 1100 °C (2012 °F) \|\| oxidized for 30 minutes \|\| 250 °C to 1000 °C (482 °F to 1832 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 15 minutes \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 1 h \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : oxidized at 1000 °C (1832 °F) \|\| oxidized for 30 minutes \|\| 200 °C to 1000 °C (392 °F to 1832 °F) HE : as-rolled \|\| not oxidized \|\| 275 °C to 1100 °C (527 °F to 2012 °F) Vis : liquid \|\| 1350 °C to 1475 °C (2462 °F to 2687 °F) ST : liquid \|\| 1529 °C to 1727 °C (2784 °F to 3140 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| full hardened \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| full hardened \|\| 20 °C to 1093 °C (68 °F to 2000 °F)
Inconel 725 (UNS N07725) (ASTM B805)	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) G : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) v : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) K : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| age-hardened \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| age-hardened \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| age-hardened \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.225 mm/mm strain UTS : solution treated & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solution treated & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solution treated & aged \|\| 20 °C to 538 °C (68 °F to 1000 °F) FSN : in air \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 1.3x10⁶ cycles to 1x10⁷ cycles FSN : in sea water \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 1.2x10⁶ cycles to 1x10⁷ cycles RHO : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SIGMA : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
Inconel 740 / Inconel 740H (UNS N07740) (ASTM B983)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) UTS : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| longitudinal \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| transverse \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : solution annealed at 1149 °C (2100 °F) & aged 16 h at 799 °C (1470 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution annealed at 1163 °C (2125 °F) & aged 4 h at 800 °C (1472 °F) \|\| 20 °C to 850 °C (68 °F to 1562 °F) YS : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| longitudinal \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| transverse \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solution annealed at 1149 °C (2100 °F) & aged 16 h at 799 °C (1470 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed at 1163 °C (2125 °F) & aged 4 h at 800 °C (1472 °F) \|\| 20 °C to 850 °C (68 °F to 1562 °F) %El : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| longitudinal \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solution annealed at 1121 °C (2050 °F) & aged 5 h at 800 °C (1472 °F) \|\| transverse \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solution annealed at 1149 °C (2100 °F) & aged 16 h at 799 °C (1470 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed at 1163 °C (2125 °F) & aged 4 h at 800 °C (1472 °F) \|\| 20 °C to 850 °C (68 °F to 1562 °F) SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 650 °C (1202 °F) \|\| 675 h to 2x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 700 °C (1292 °F) \|\| 265 h to 4x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 750 °C (1382 °F) \|\| 130 h to 8x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 800 °C (1472 °F) \|\| 150 h to 2x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 825 °C (1517 °F) \|\| 315 h to 8,000 h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 850 °C (1562 °F) \|\| 85 h to 1.3x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| tested at 875 °C (1607 °F) \|\| 70 h to 8x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F) \|\| Master curve (LMP) \|\| 650 °C to 876 °C (1202 °F to 1609 °F) SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F), welds \|\| tested at 700 °C (1292 °F) \|\| 50 h to 4.3x10⁴ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F), welds \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F), welds \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1x10⁵ h SR : solution annealed at 1120 °C (2048 °F) & aged at 800 °C (1472 °F), welds \|\| Master curve (LMP) \|\| 700 °C to 801 °C (1292 °F to 1474 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Inconel X-750 (UNS N07750) (WNr 2.4669) (ISO/EN/DIN NW7750/NiCr15Fe7Ti2Al/NiCr15Fe7TiAl) (JIS NCF750) (ASTM B637) (AMS 5542/5598/5667/5668/5669/5670/5671/5747) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| heat-treated \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) DLL : solid \|\| heat-treated \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) MTE : solid \|\| heat-treated \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) CTE : solid \|\| heat-treated \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) E : solid \|\| -273 °C to 982 °C (-460 °F to 1800 °F) G : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) v : solid \|\| 20 °C to 527 °C (68 °F to 980 °F) K : solid \|\| 20 °C to 427 °C (68 °F to 800 °F) TC : solid \|\| annealed \|\| -266 °C to 27 °C (-447 °F to 80 °F) TC : solid \|\| heat-treated \|\| -157 °C to 1392 °C (-251 °F to 2537 °F) TD : solid \|\| heat-treated \|\| -157 °C to 982 °C (-251 °F to 1799 °F) SH : solid \|\| -272 °C to 982 °C (-458 °F to 1800 °F) SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 3.3x10^-⁴/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.185 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 3.3x10^-⁴/s \|\| tested at -78 °C (-109 °F) \|\| 0 to 0.23 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 3.3x10^-⁴/s \|\| tested at -197.1 °C (-322.9 °F) \|\| 0 to 0.25 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 3.3x10^-⁴/s \|\| tested at -253.1 °C (-423.7 °F) \|\| 0 to 0.28 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.14 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 649 °C (1200 °F), held for 1800 s \|\| 0 to 0.14 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 871 °C (1600 °F), held for 1800 s \|\| 0 to 0.9 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.14 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 649 °C (1200 °F), held for 10 s \|\| 0 to 0.14 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 1/s \|\| tested at 871 °C (1600 °F), held for 10 s \|\| 0 to 0.9 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 0.01/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.22 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 0.01/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 5x10^-⁵/s \|\| tested at 27 °C (80 °F) \|\| 0 to 0.14 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 1800 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 5x10^-⁵/s \|\| tested at 204 °C (400 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain SSC : aged 20 h at 704 °C (1300 °F) and air cooled, 5x10^-⁵/s \|\| tested at 427 °C (800 °F), held for 10 s \|\| 0 to 0.18 mm/mm strain UTS : bar \|\| hot-rolled, equalized & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : bar \|\| triple heat-treated \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS : bar \|\| aged 20 h at 704 °C (1300 °F) & air cooled \|\| -253 °C to 20 °C (-424 °F to 68 °F) UTS : sheet \|\| cold-rolled & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) YS : bar \|\| hot-rolled, equalized & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : bar \|\| triple heat-treated \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : bar \|\| aged 20 h at 704 °C (1300 °F) & air cooled \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS : sheet \|\| cold-rolled & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) %El : bar \|\| hot-rolled, equalized & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : bar \|\| triple heat-treated \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : bar \|\| aged 20 h at 704 °C (1300 °F) & air cooled \|\| -253 °C to 20 °C (-424 °F to 68 °F) %El : sheet \|\| cold-rolled & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) SR : aged, sheet & strip \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : aged, sheet & strip \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : aged, sheet & strip \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : aged, sheet & strip \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : aged, sheet & strip \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : aged, sheet & strip \|\| tested at 927 °C (1700 °F) \|\| 10 h to 100 h SR : aged, sheet & strip \|\| Master curve (LMP) \|\| 593 °C to 927 °C (1099 °F to 1700 °F) SR : triple heat-treated, bar \|\| tested at 538 °C (1000 °F) \|\| 30 h to 1,120 h SR : triple heat-treated, bar \|\| tested at 593 °C (1100 °F) \|\| 12 h to 890 h SR : triple heat-treated, bar \|\| tested at 649 °C (1200 °F) \|\| 1.3 h to 1x10⁵ h SR : triple heat-treated, bar \|\| tested at 732 °C (1350 °F) \|\| 0.5 h to 1x10⁵ h SR : triple heat-treated, bar \|\| tested at 816 °C (1500 °F) \|\| 0.3 h to 1x10⁵ h SR : triple heat-treated, bar \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 1x10⁴ h SR : triple heat-treated, bar \|\| tested at 927 °C (1700 °F) \|\| 0.5 h to 1,000 h SR : triple heat-treated, bar \|\| tested at 982 °C (1800 °F) \|\| 0.3 h to 100 h FEN : cold-rolled sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain \|\| 5.5x10³ cycles to 1.1x10⁶ cycles FEN : cold-rolled sheet \|\| tested at -79 °C (-110 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain \|\| 1.3x10⁴ cycles to 1.35x10⁶ cycles FEN : cold-rolled sheet \|\| tested at -195.6 °C (-320 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain \|\| 2.5x10⁴ cycles to 9x10⁵ cycles FEN : cold-rolled sheet \|\| tested at -252.8 °C (-423 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain \|\| 4.5x10⁴ cycles to 1x10⁶ cycles FSN : aged, hot-rolled bar \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 2.6x10⁵ cycles to 1x10⁸ cycles FSN : aged, hot-rolled bar \|\| tested at 20 °C (68 °F), R = -1, rotating beam, K_t = 3.4, maximum stress \|\| 2.6x10⁵ cycles to 1x10⁸ cycles FSN : aged, hot-rolled bar \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : cold-rolled sheet \|\| tested at 21 °C (70 °F), R = -1, flexure, aged at 704 °C (1300 °F) for 8 h, maximum stress \|\| 1.3x10⁵ cycles to 1x10⁸ cycles FSN : cold-rolled sheet \|\| tested at 21 °C (70 °F), R = -1, bending, flexure, aged at 704 °C (1300 °F) for 20 h, maximum stress \|\| 1.9x10⁵ cycles to 3.2x10⁷ cycles FSN : cold-rolled sheet \|\| tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 3.7x10⁴ cycles to 1x10⁷ cycles FSN : cold-rolled sheet \|\| tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁷ cycles FSN : cold-rolled sheet \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled sheet \|\| tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 2.7x10⁴ cycles to 1.25x10⁶ cycles FSN : cold-rolled sheet \|\| tested at 21 °C (70 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 2.6x10⁴ cycles to 9x10⁶ cycles FSN : cold-rolled sheet \|\| tested at -79 °C (-110 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 2.8x10⁴ cycles to 1.1x10⁶ cycles FSN : cold-rolled sheet \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress \|\| 2.4x10⁴ cycles to 1x10⁶ cycles CRS : 0.5% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 1.7 h to 100 h CRS : 0.5% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 3.5 h to 390 h CRS : 0.5% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 1.6 h to 200 h CRS : 0.5% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 1 h to 55 h CRS : 0.5% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 1 h to 50 h CRS : 0.5% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 1% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 3.5 h to 200 h CRS : 1% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 7 h to 780 h CRS : 1% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 3.3 h to 400 h CRS : 1% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 2.1 h to 110 h CRS : 1% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 2.1 h to 95 h CRS : 1% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 1.5% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 5.2 h to 300 h CRS : 1.5% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 10.4 h to 1,200 h CRS : 1.5% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 5 h to 600 h CRS : 1.5% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 3.1 h to 165 h CRS : 1.5% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 3.1 h to 145 h CRS : 1.5% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 2% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 7 h to 400 h CRS : 2% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 13.8 h to 1,550 h CRS : 2% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 6.6 h to 810 h CRS : 2% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 4.2 h to 220 h CRS : 2% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 4.2 h to 190 h CRS : 2% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 3% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 10.5 h to 600 h CRS : 3% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 20.8 h to 2,325 h CRS : 3% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 9.9 h to 1,215 h CRS : 3% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 6.3 h to 330 h CRS : 3% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 6.3 h to 285 h CRS : 3% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 4% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 14 h to 800 h CRS : 4% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 27 h to 3,100 h CRS : 4% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 13.1 h to 1,620 h CRS : 4% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 8.4 h to 440 h CRS : 4% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 8.4 h to 375 h CRS : 4% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 5% creep strain, aged, hot-rolled bar \|\| tested at 538 °C (1000 °F) \|\| 17.5 h to 1,000 h CRS : 5% creep strain, aged, hot-rolled bar \|\| tested at 593 °C (1100 °F) \|\| 34.6 h to 3,880 h CRS : 5% creep strain, aged, hot-rolled bar \|\| tested at 649 °C (1200 °F) \|\| 16.4 h to 2,025 h CRS : 5% creep strain, aged, hot-rolled bar \|\| tested at 732 °C (1350 °F) \|\| 10.5 h to 550 h CRS : 5% creep strain, aged, hot-rolled bar \|\| tested at 816 °C (1500 °F) \|\| 10.5 h to 470 h CRS : 5% creep strain, aged, hot-rolled bar \|\| Master curve (LMP) \|\| 538 °C to 817 °C (1000 °F to 1502 °F) CRS : 0.5% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 53 h to 1.2x10⁵ h CRS : 0.5% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 20 h to 1.2x10⁵ h CRS : 0.5% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1.2x10⁵ h CRS : 0.5% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 5 h to 1.1x10⁵ h CRS : 1% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 100 h to 2.4x10⁵ h CRS : 1% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 44 h to 2.3x10⁵ h CRS : 1% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 20 h to 2.4x10⁵ h CRS : 1% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 2.2x10⁵ h CRS : 1.5% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 160 h to 3.6x10⁵ h CRS : 1.5% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 65 h to 3.5x10⁵ h CRS : 1.5% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 30 h to 3.5x10⁵ h CRS : 1.5% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 15 h to 3.4x10⁵ h CRS : 2% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 210 h to 4.8x10⁵ h CRS : 2% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 85 h to 4.7x10⁵ h CRS : 2% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 40 h to 4.7x10⁵ h CRS : 2% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 20 h to 4.5x10⁵ h CRS : 3% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 320 h to 7.2x10⁵ h CRS : 3% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 130 h to 7x10⁵ h CRS : 3% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 60 h to 7x10⁵ h CRS : 3% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 30 h to 6.7x10⁵ h CRS : 4% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 420 h to 9.5x10⁵ h CRS : 4% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 175 h to 9.3x10⁵ h CRS : 4% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 80 h to 9.4x10⁵ h CRS : 4% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 40 h to 9x10⁵ h CRS : 5% creep strain, triple heat-treated \|\| tested at 649 °C (1200 °F) \|\| 530 h to 1.2x10⁶ h CRS : 5% creep strain, triple heat-treated \|\| tested at 732 °C (1350 °F) \|\| 220 h to 1.2x10⁶ h CRS : 5% creep strain, triple heat-treated \|\| tested at 816 °C (1500 °F) \|\| 105 h to 1.2x10⁶ h CRS : 5% creep strain, triple heat-treated \|\| tested at 871 °C (1600 °F) \|\| 50 h to 1.1x10⁶ h IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 538 °C (1000 °F), creep strain, aged, hot-rolled bar \|\| 1,000,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 566 °C (1050 °F), creep strain, aged, hot-rolled bar \|\| 1,000,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.4 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 593 °C (1100 °F), creep strain, aged, hot-rolled bar \|\| 1,000,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 621 °C (1150 °F), creep strain, aged, hot-rolled bar \|\| 1,000,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), creep strain, aged, hot-rolled bar \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), creep strain, aged, hot-rolled bar \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), creep strain, aged, hot-rolled bar \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), creep strain, aged, hot-rolled bar \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), creep strain, aged, hot-rolled bar \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), creep strain, aged, hot-rolled bar \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 0.1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 0.3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 1 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 3 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 10 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), creep strain, aged, hot-rolled bar \|\| 30 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 300 h \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, triple heat-treated \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 100 h \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, triple heat-treated \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 30 h \|\| 0 to 0.15 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 100 h \|\| 0 to 0.4 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, triple heat-treated \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 30 h \|\| 0 to 0.3 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 300 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 1,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 3,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 10,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 30,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 100,000 h \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, triple heat-treated \|\| 300,000 h \|\| 0 to 0.5 mm/mm strain HE : solid \|\| oxidized in air at 1093 °C (2000 °F) \|\| 315 °C to 1093 °C (599 °F to 2000 °F) NE : solid \|\| polished \|\| -185 °C to 910 °C (-301 °F to 1670 °F) NE : solid \|\| oxidized \|\| 987 °C to 1315 °C (1808 °F to 2400 °F) RHO : solid \|\| heat-treated \|\| 20 °C to 871 °C (68 °F to 1600 °F) RHO : solid \|\| hot-rolled & direct aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| heat-treated \|\| 20 °C to 871 °C (68 °F to 1600 °F) SIGMA : solid \|\| hot-rolled & direct aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Inconel 751 (UNS N07751) (JIS NCF751)	D : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) DLL : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) MTE : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) CTE : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : precipitation hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : precipitation hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : precipitation hardened \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : solution treated & aged \|\| tested at 732 °C (1350 °F) \|\| 1 h to 500 h SR : solution treated & aged \|\| tested at 816 °C (1500 °F) \|\| 1 h to 700 h SR : solution treated & aged \|\| tested at 871 °C (1600 °F) \|\| 2 h to 1,000 h SR : solution treated & aged \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : solution treated & aged \|\| Master curve (LMP) \|\| 732 °C to 927 °C (1349 °F to 1700 °F) SR : direct aged for 2 h at 732 °C (1350 °F) \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : direct aged for 2 h at 732 °C (1350 °F) \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1,000 h SR : direct aged for 2 h at 732 °C (1350 °F) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : direct aged for 2 h at 732 °C (1350 °F) \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) FSN : precipitation hardened \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : precipitation hardened \|\| tested at 732 °C (1350 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : precipitation hardened \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Inconel C-276 (UNS N10276) (WNr 2.4375/2.4537/2.4819) (ISO/EN/DIN NW0276/NiMo16Cr/NiMo16Cr15Fe6W4/NiMo16Cr15W) (JIS NW0276) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| -168 °C to 1100 °C (-271 °F to 2012 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.32 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.59 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.67 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.46 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.62 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.64 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.51 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.67 mm/mm strain SSCC : annealed, 20/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.58 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.61 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.6 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.6 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1125 °C (2057 °F) \|\| 0 to 0.42 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.65 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.64 mm/mm strain UTS : cold-drawn \|\| tubing \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : annealed \|\| plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : solution annealed \|\| 1.6 mm to 4.7 mm (0.063 inch to 0.185 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : solution annealed \|\| 4.76 mm to 3.17 mm (0.1875 inch to 0.125 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : cold-drawn \|\| tubing \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : annealed \|\| plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solution annealed \|\| 1.6 mm to 4.7 mm (0.063 inch to 0.185 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solution annealed \|\| 4.76 mm to 3.17 mm (0.1875 inch to 0.125 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : cold-drawn \|\| tubing \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : annealed \|\| plate \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution annealed \|\| 1.6 mm to 4.7 mm (0.063 inch to 0.185 inch) sheet \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solution annealed \|\| 4.76 mm to 3.17 mm (0.1875 inch to 0.125 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) HE : solid \|\| oxidized \|\| 327 °C to 1727 °C (620 °F to 3140 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Inconel G-3 (UNS N06985) (WNr 2.4619) (ISO/EN/DIN NiCr22Mo7Cu)	D : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solid \|\| 20 °C to 593 °C (68 °F to 1100 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : annealed \|\| 20 °C to 1056 °C (68 °F to 1933 °F) YS : annealed \|\| 20 °C to 1086 °C (68 °F to 1987 °F) %El : annealed \|\| 20 °C to 1072 °C (68 °F to 1961 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Inconel HX / Hastelloy X / Nimonic PE13 (UNS N06002) (WNr 2.4665) (ISO/EN/DIN NW6002/NiCr21Fe18Mo9/NiCr22Fe18Mo) (JIS NW6002) (AMS 5536/5588/5754/5798) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) DLL : solid \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) MTE : solid \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) CTE : solid \|\| -273 °C to 1317 °C (-460 °F to 2402 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| annealed \|\| -266 °C to 1000 °C (-447 °F to 1832 °F) TD : solid \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain SSC : laser powder bed fusion \|\| tested at 700 °C (1292 °F), 0.001/s, as-built, vertical, He et. al. \|\| 0 to 0.2 mm/mm strain SSC : laser powder bed fusion \|\| tested at 700 °C (1292 °F), 0.001/s, as-built, horizontal, He et. al. \|\| 0 to 0.15 mm/mm strain SSC : laser powder bed fusion \|\| tested at 815 °C (1499 °F), 2.8x10^-⁶/s, HIPed, Wu et. al. \|\| 0 to 0.122 mm/mm strain SSC : laser powder bed fusion \|\| tested at 815 °C (1499 °F), 2.8x10^-⁶/s, HIPed + 1230 °C (2246 °F) for 2 h, Wu et. al. \|\| 0 to 0.9 mm/mm strain UTS : annealed & rapid cooled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed & rapid cooled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed & rapid cooled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : solution annealed & rapid cooled sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled sheet \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1,000 h SR : solution annealed & rapid cooled sheet \|\| Master curve (LMP) \|\| 649 °C to 1094 °C (1200 °F to 2001 °F) SR : solution annealed & rapid cooled plate & bar \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled plate & bar \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled plate & bar \|\| tested at 899 °C (1650 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapid cooled plate & bar \|\| tested at 1066 °C (1950 °F) \|\| 10 h to 1,000 h SR : solution annealed & rapid cooled plate & bar \|\| tested at 1149 °C (2100 °F) \|\| 10 h to 1,000 h SR : solution annealed & rapid cooled plate & bar \|\| Master curve (LMP) \|\| 649 °C to 1150 °C (1200 °F to 2102 °F) FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 816 °C (1500 °F), R = -1, axial, total strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 816 °C (1500 °F), R = -1, axial, elastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 816 °C (1500 °F), R = -1, axial, plastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 100 cycles to 1.27x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 927 °C (1700 °F), R = -1, axial, total strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 927 °C (1700 °F), R = -1, axial, elastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles FEN : solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled \|\| tested at 927 °C (1700 °F), R = -1, axial, plastic strain amplitude \|\| 400 cycles to 2x10⁴ cycles CRS : 0.5% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & rapid cooled sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapid cooled sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 2% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 2% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 2% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 2% plastic strain, solution annealed & rapid cooled sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 2% plastic strain, solution annealed & rapid cooled sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 899 °C (1650 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapid cooled plate & bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1x10⁴ h CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 899 °C (1650 °F) \|\| 10 h to 1x10⁴ h CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 5% plastic strain, solution annealed & rapid cooled plate & bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapid cooled \|\| 300,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapid cooled \|\| 100,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapid cooled \|\| 30,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapid cooled \|\| 10,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapid cooled \|\| 3,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, sheet \|\| 0 to 0.2 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 0.1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 10 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 30 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 100 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 300 h, plate & bar \|\| 0 to 0.5 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapid cooled \|\| 1,000 h, plate & bar \|\| 0 to 0.5 mm/mm strain HE : solid \|\| oxidized at 1093 °C (2000 °F) \|\| 327 °C to 1727 °C (620 °F to 3140 °F) RHO : solid \|\| -266 °C to 1000 °C (-447 °F to 1832 °F) SIGMA : solid \|\| -266 °C to 1000 °C (-447 °F to 1832 °F)
Inconel MA 753 (UNS N07753)	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 1027 °C (68 °F to 1880 °F)
Inconel MA 754 (UNS N07754)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| transverse \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| transverse \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| transverse \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| untextured bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| textured bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 10/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 700 °C (1292 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 750 °C (1382 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 800 °C (1472 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 850 °C (1562 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.5 mm/mm strain SSCC : recrystallized rod, 100/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : longitudinal \|\| tested at 760 °C (1400 °F) \|\| 10 h to 600 h SR : longitudinal \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1x10⁴ h SR : longitudinal \|\| tested at 1149 °C (2100 °F) \|\| 100 h to 1x10⁴ h SR : longitudinal \|\| Master curve (LMP) \|\| 760 °C to 1149 °C (1400 °F to 2100 °F) SR : long transverse \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1x10⁴ h SR : long transverse \|\| tested at 1149 °C (2100 °F) \|\| 100 h to 1x10⁴ h SR : long transverse \|\| Master curve (LMP) \|\| 1093 °C to 1149 °C (1999 °F to 2100 °F) FEN : secondary recrystallized, polished \|\| tested at 750 °C (1382 °F), R = -1, axial, total strain amplitude \|\| 220 cycles to 8x10³ cycles FEN : secondary recrystallized, polished \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude \|\| 130 cycles to 4.9x10³ cycles FEN : secondary recrystallized, polished \|\| tested at 950 °C (1742 °F), R = -1, axial, total strain amplitude \|\| 75 cycles to 5.6x10³ cycles FEN : secondary recrystallized, polished \|\| tested at 1050 °C (1922 °F), R = -1, axial, total strain amplitude \|\| 55 cycles to 4.5x10³ cycles FEN : secondary recrystallized, polished \|\| tested at 1150 °C (2102 °F), R = -1, axial, total strain amplitude \|\| 31 cycles to 4.5x10³ cycles RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Inconel MA 758	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : extruded bar \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : extruded bar \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : extruded bar \|\| annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) RHO : solid \|\| 20 °C to 1204 °C (68 °F to 2199 °F) SIGMA : solid \|\| 20 °C to 1204 °C (68 °F to 2199 °F)
Inconel MA 6000	D* : solid \|\| room temperature value E : recrystallized \|\| longitudinal \|\| 20 °C to 1012 °C (68 °F to 1853 °F) E : recrystallized \|\| long transverse \|\| 20 °C to 1050 °C (68 °F to 1922 °F) E : extruded \|\| longitudinal \|\| 20 °C to 1050 °C (68 °F to 1922 °F) G : recrystallized \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : recrystallized \|\| long transverse \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : extruded \|\| longitudinal \|\| 20 °C to 850 °C (68 °F to 1562 °F) v : recrystallized \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : recrystallized \|\| long transverse \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : extruded \|\| longitudinal \|\| 20 °C to 850 °C (68 °F to 1562 °F) K : recrystallized \|\| longitudinal \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : recrystallized \|\| long transverse \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : extruded \|\| longitudinal \|\| 20 °C to 850 °C (68 °F to 1562 °F) UTS : solid \|\| longitudinal \|\| 20 °C to 1080 °C (68 °F to 1976 °F) YS : solid \|\| longitudinal \|\| 20 °C to 1080 °C (68 °F to 1976 °F) SR : longitudinal \|\| tested at 700 °C (1292 °F) \|\| 1 h to 2,200 h SR : longitudinal \|\| tested at 750 °C (1382 °F) \|\| 1 h to 2x10⁴ h SR : longitudinal \|\| tested at 760 °C (1400 °F) \|\| 1 h to 4,000 h SR : longitudinal \|\| tested at 800 °C (1472 °F) \|\| 1 h to 2,000 h SR : longitudinal \|\| tested at 816 °C (1500 °F) \|\| 1 h to 1,000 h SR : longitudinal \|\| tested at 871 °C (1600 °F) \|\| 1 h to 3,000 h SR : longitudinal \|\| tested at 900 °C (1652 °F) \|\| 1 h to 1.2x10⁴ h SR : longitudinal \|\| tested at 950 °C (1742 °F) \|\| 1 h to 1x10⁴ h SR : longitudinal \|\| tested at 982 °C (1800 °F) \|\| 1 h to 3x10⁴ h SR : longitudinal \|\| tested at 1000 °C (1832 °F) \|\| 1 h to 4,000 h SR : longitudinal \|\| tested at 1093 °C (2000 °F) \|\| 1 h to 700 h SR : longitudinal \|\| tested at 1100 °C (2012 °F) \|\| 5 h to 700 h SR : longitudinal \|\| tested at 1149 °C (2100 °F) \|\| 1 h to 500 h SR : longitudinal \|\| Master curve (LMP) (region I) \|\| 700 °C to 1093 °C (1292 °F to 1999 °F) SR : longitudinal \|\| Master curve (LMP) (region II) \|\| 750 °C to 1149 °C (1382 °F to 2100 °F) FEN : polished \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude \|\| 5 cycles to 8.5x10⁴ cycles FEN : polished \|\| tested at 1050 °C (1922 °F), R = -1, axial, total strain amplitude \|\| 64 cycles to 7x10³ cycles FSN : longitudinal \|\| tested at 850 °C (1562 °F), R = 0, axial, stress amplitude \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : transverse \|\| tested at 850 °C (1562 °F), R = 0, axial, stress amplitude \|\| 1x10⁴ cycles to 1x10⁸ cycles

MAR-M200	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 852 °C (68 °F to 1565 °F) G : solid \|\| 20 °C to 852 °C (68 °F to 1565 °F) v : solid \|\| 20 °C to 852 °C (68 °F to 1565 °F) K : solid \|\| 20 °C to 852 °C (68 °F to 1565 °F) TC : solid \|\| annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SH : solid \|\| annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : annealed & air cooled \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) FEN : cast \|\| tested at 1000 °C (1832 °F), R = -1, axial, total strain range \|\| 190 cycles to 1.54x10⁴ cycles FEN : cast \|\| tested at 1000 °C (1832 °F), R = -1, axial, plastic strain range \|\| 190 cycles to 1.54x10⁴ cycles FEN : directionally solidified \|\| tested at 760 °C (1400 °F), R = -1, axial, total strain range \|\| 20 cycles to 8.2x10⁶ cycles FEN : directionally solidified \|\| tested at 927 °C (1700 °F), R = -1, axial, total strain range \|\| 100 cycles to 8.2x10⁶ cycles FEN : directionally solidified \|\| tested at 21 °C (70 °F), R = -1, ultrasonic, total strain amplitude \|\| 2x10⁶ cycles to unknown strain rate cycles FSN : cast \|\| tested at 1000 °C (1832 °F), R = -1, axial, maximum stress \|\| 190 cycles to 1.54x10⁴ cycles FSN : single crystal \|\| tested at 20 °C (68 °F), axial, in air, stress range \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : single crystal \|\| tested at 20 °C (68 °F), axial, in vacuum, stress range \|\| 3x10⁴ cycles to 1x10⁷ cycles
MAR-M246	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F)
MAR-M247	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SSC : cast \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.33 mm/mm strain SSC : cast \|\| tested at 760 °C (1400 °F), unknown strain rate \|\| 0 to 0.33 mm/mm strain UTS : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : annealed & air cooled \|\| 20 °C to 982 °C (68 °F to 1800 °F) FEN : heat-treated \|\| tested at 204 °C (400 °F), R = 0, axial, total strain range \|\| 1.27x10³ cycles to 1.45x10⁵ cycles FEN : heat-treated \|\| tested at 427 °C (800 °F), R = 0, axial, total strain range \|\| 370 cycles to 7.65x10⁴ cycles FEN : heat-treated \|\| tested at 760 °C (1400 °F), R = 0, axial, total strain range \|\| 500 cycles to 9.92x10⁴ cycles FSN : heat-treated \|\| tested at 650 °C (1202 °F), R = -1, axial, stress amplitude \|\| 7.5x10⁵ cycles to 1x10⁸ cycles FSN : heat-treated \|\| tested at 800 °C (1472 °F), R = -1, axial, stress amplitude \|\| 1x10⁶ cycles to 1x10⁸ cycles Vis : liquid \|\| 1387 °C to 1520 °C (2528 °F to 2768 °F)

CMSX-3	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| single crystal alloy \|\| 20 °C to 1122 °C (68 °F to 2051 °F)
CMSX-4	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) D : liquid \|\| 1387 °C to 1577 °C (2528 °F to 2870 °F) D : liquid + solid \|\| 1347 °C to 1387 °C (2456 °F to 2528 °F) DLL : solid \|\| [001] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : liquid \|\| 1387 °C to 1577 °C (2528 °F to 2870 °F) DLL : liquid + solid \|\| 1347 °C to 1387 °C (2456 °F to 2528 °F) MTE : solid \|\| [001] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : liquid \|\| 1387 °C to 1577 °C (2528 °F to 2870 °F) MTE : liquid + solid \|\| 1347 °C to 1387 °C (2456 °F to 2528 °F) CTE : solid \|\| [001] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : liquid \|\| 1387 °C to 1577 °C (2528 °F to 2870 °F) CTE : liquid + solid \|\| 1347 °C to 1387 °C (2456 °F to 2528 °F) E : solid \|\| <100> axis \|\| 20 °C to 1200 °C (68 °F to 2192 °F) E : solid \|\| <110> axis \|\| 20 °C to 1200 °C (68 °F to 2192 °F) E : solid \|\| <111> axis \|\| 20 °C to 1200 °C (68 °F to 2192 °F) G : solid \|\| <100> axis \|\| 20 °C to 1027 °C (68 °F to 1880 °F) v : solid \|\| <100> axis \|\| 20 °C to 1027 °C (68 °F to 1880 °F) TC : solid \|\| 20 °C to 1379 °C (68 °F to 2514 °F) TD : solid \|\| 20 °C to 1300 °C (68 °F to 2372 °F) TD : liquid \|\| 1512 °C to 1577 °C (2753 °F to 2870 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSC : additive manufacturing, as-built \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.47 mm/mm strain SSC : additive manufacturing, as-built \|\| tested at 650 °C (1202 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.9 mm/mm strain SSC : additive manufacturing, as-built \|\| tested at 800 °C (1472 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.165 mm/mm strain SSC : additive manufacturing, as-built \|\| tested at 950 °C (1742 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.9 mm/mm strain SSC : additive manufacturing, heat-treated \|\| tested at 20 °C (68 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.7 mm/mm strain SSC : additive manufacturing, heat-treated \|\| tested at 650 °C (1202 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.55 mm/mm strain SSC : additive manufacturing, heat-treated \|\| tested at 800 °C (1472 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.18 mm/mm strain SSC : additive manufacturing, heat-treated \|\| tested at 950 °C (1742 °F), 8.3x10^-⁴/s, [001] direction \|\| 0 to 0.58 mm/mm strain SSCC : heat treated and aged \|\| tested at 1000 °C (1832 °F), 2.5x10^-⁴/s, [001] \|\| 0 to 0.17 mm/mm strain UTS : castings \|\| [001] direction \|\| 20 °C to 1038 °C (68 °F to 1900 °F) UTS : castings \|\| [110] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : castings \|\| [111] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : additive manufacturing \|\| [001] direction, as-built \|\| 20 °C to 950 °C (68 °F to 1742 °F) UTS : additive manufacturing \|\| [001] direction, heat-treated \|\| 20 °C to 950 °C (68 °F to 1742 °F) YS : castings \|\| [001] direction \|\| 20 °C to 1038 °C (68 °F to 1900 °F) YS : castings \|\| [110] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : castings \|\| [111] direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : additive manufacturing \|\| [001] direction, as-built \|\| 20 °C to 950 °C (68 °F to 1742 °F) YS : additive manufacturing \|\| [001] direction, heat-treated \|\| 20 °C to 950 °C (68 °F to 1742 °F) %El : additive manufacturing \|\| [001] direction, as-built \|\| 20 °C to 950 °C (68 °F to 1742 °F) %El : additive manufacturing \|\| [001] direction, heat-treated \|\| 20 °C to 950 °C (68 °F to 1742 °F) SR : castings, solution treated & aged \|\| tested at 982 °C (1800 °F) \|\| 90 h to 9,400 h SR : castings, solution treated & aged \|\| tested at 1038 °C (1900 °F) \|\| 300 h to 4,900 h SR : castings, solution treated & aged \|\| tested at 1121 °C (2050 °F) \|\| 840 h to 2,220 h SR : castings, solution treated & aged \|\| Master curve (LMP) \|\| 982 °C to 1122 °C (1799 °F to 2051 °F) FEN : thermo-mechanical fatigue \|\| tested at 100 °C (212 °F) to 850 °C (1562 °F), <001> direction, axial, total strain range \|\| 40 cycles to 2.55x10³ cycles FEN : thermo-mechanical fatigue \|\| tested at 100 °C (212 °F) to 850 °C (1562 °F), <011> direction, axial, total strain range \|\| 195 cycles to 2.38x10³ cycles FSN : cast along the <001> direction \|\| tested at 850 °C (1562 °F), R = 0, axial, in air, maximum stress \|\| 1.77x10³ cycles to 1.1x10⁵ cycles FSN : cast along the <001> direction \|\| tested at 850 °C (1562 °F), R = 0, axial, in salt + SO₂, maximum stress \|\| 5.5x10³ cycles to 1.1x10⁵ cycles FSN : cast along the <001> direction \|\| tested at 850 °C (1562 °F), R = 0, axial, in salt + SO₂, 55 micron to 70 micron RLT, maximum stress \|\| 6.4x10³ cycles to 9.5x10⁴ cycles FSN : cast along the <001> direction \|\| tested at 850 °C (1562 °F), R = 0, axial, in salt + SO₂, < 50 micron RLT, maximum stress \|\| 1.78x10⁴ cycles to 1.1x10⁵ cycles FSN : cast along the <001> direction \|\| tested at 850 °C (1562 °F), R = 0, axial, in salt + SO₂, > 75 micron RLT, maximum stress \|\| 4.44x10³ cycles to 8.84x10⁴ cycles FSN : cast along the <001> direction \|\| tested at 1000 °C (1832 °F), R = -1, axial, maximum stress \|\| 5x10⁶ cycles to 3x10⁹ cycles FSN : cast along the <001> direction \|\| tested at 1000 °C (1832 °F), R = 0.8, axial, maximum stress \|\| 3x10⁶ cycles to 3x10⁹ cycles CRS : 1% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 75 h to 5,600 h Vis : liquid \|\| 1375 °C to 1600 °C (2507 °F to 2912 °F) ST : liquid \|\| Aune et. al. \|\| 1340 °C to 1576 °C (2444 °F to 2869 °F) ST : liquid \|\| Vinet et. al. \|\| 1312 °C to 1560 °C (2393 °F to 2840 °F) ST : liquid \|\| average \|\| 1312 °C to 1576 °C (2393 °F to 2869 °F)
CMSX-4 Plus	D : solid \|\| 20 °C to 1293 °C (68 °F to 2359 °F) DLL : solid \|\| 20 °C to 1293 °C (68 °F to 2359 °F) MTE : solid \|\| 20 °C to 1293 °C (68 °F to 2359 °F) CTE : solid \|\| 20 °C to 1293 °C (68 °F to 2359 °F) TC : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) TD : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) SH : solid \|\| 20 °C to 1204 °C (68 °F to 2200 °F) FSN : heat treated \|\| tested at 1000 °C (1832 °F), R = -1, ultrasonic, maximum stress \|\| 1x10⁶ cycles to 5.3x10⁶ cycles FSN : HIPed, heat treated \|\| tested at 1000 °C (1832 °F), R = -1, ultrasonic, maximum stress \|\| 2x10⁷ cycles to 5.6x10⁸ cycles
CMSX-6	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) FEN : no hold \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 900 cycles to 5.2x10³ cycles FEN : held for 300 s at the maximum tensile strain \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 570 cycles to 4x10³ cycles FEN : held for 300 s at the maximum compressive strain \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 470 cycles to 1.8x10³ cycles
CMSX-7	D* : solid \|\| room temperature value UTS : solid \|\| within 10 degrees of (001) \|\| 20 °C to 1038 °C (68 °F to 1900 °F) YS : solid \|\| within 10 degrees of (001) \|\| 20 °C to 1038 °C (68 °F to 1900 °F) %El : solid \|\| within 10 degrees of (001) \|\| 20 °C to 1038 °C (68 °F to 1900 °F) FEN : single crystal \|\| tested at 1038 °C (1900 °F), R = 0, total strain range \|\| 2.6x10³ cycles to 1x10⁶ cycles FEN : single crystal \|\| tested at 1038 °C (1900 °F), R = -1, total strain range \|\| 3.7x10³ cycles to 1x10⁶ cycles FEN : single crystal \|\| tested at 1093 °C (2000 °F), R = 0, total strain range \|\| 3.9x10³ cycles to 2.2x10⁶ cycles FEN : single crystal \|\| tested at 1093 °C (2000 °F), R = -1, total strain range \|\| 4.2x10³ cycles to 2.4x10⁶ cycles
CMSX-8	D : solid \|\| 20 °C to 1252 °C (68 °F to 2285 °F) DLL : solid \|\| 20 °C to 1252 °C (68 °F to 2285 °F) MTE : solid \|\| 20 °C to 1252 °C (68 °F to 2285 °F) CTE : solid \|\| 20 °C to 1252 °C (68 °F to 2285 °F) E : solid \|\| near (001) \|\| 20 °C to 1252 °C (68 °F to 2285 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| near (001) \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SH : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : solution annealed & double-aged \|\| 20 °C to 1034 °C (68 °F to 1893 °F) YS : solution annealed & double-aged \|\| 20 °C to 1034 °C (68 °F to 1893 °F) %El : solution annealed & double-aged \|\| 20 °C to 1042 °C (68 °F to 1907 °F) FEN : single crystal \|\| tested at 1038 °C (1900 °F), R = 0, total strain range \|\| 4x10³ cycles to 1x10⁶ cycles FEN : single crystal \|\| tested at 1038 °C (1900 °F), R = -1, total strain range \|\| 4x10³ cycles to 1x10⁶ cycles
CMSX-10	D : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) D : liquid \|\| 1410 °C to 1427 °C (2570 °F to 2600 °F) DLL : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) DLL : liquid \|\| 1410 °C to 1427 °C (2570 °F to 2600 °F) MTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) MTE : liquid \|\| 1410 °C to 1427 °C (2570 °F to 2600 °F) CTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) CTE : liquid \|\| 1410 °C to 1427 °C (2570 °F to 2600 °F) TC : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) TD : solid \|\| 20 °C to 727 °C (68 °F to 1340 °F) SH : solid \|\| 20 °C to 1362 °C (68 °F to 2483 °F) SH : liquid \|\| 1410 °C to 1427 °C (2570 °F to 2600 °F) SR : unknown form \|\| tested at 913 °C (1675 °F) \|\| 1,500 h to 4,000 h SR : unknown form \|\| tested at 954 °C (1750 °F) \|\| 1,100 h to 3,500 h SR : unknown form \|\| tested at 982 °C (1800 °F) \|\| 750 h to 3,000 h SR : unknown form \|\| tested at 1010 °C (1850 °F) \|\| 350 h to 3,000 h SR : unknown form \|\| Master curve (LMP) \|\| 912 °C to 1011 °C (1673 °F to 1852 °F) CRS : 1% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 500 h to 2,000 h Vis : liquid \|\| 1327 °C to 1557 °C (2420 °F to 2834 °F) ST : liquid \|\| 1281 °C to 1682 °C (2338 °F to 3059 °F)
CMSX-486	D* : solid \|\| room temperature value UTS : as-cast \|\| within 10 degrees of (001) \|\| 20 °C to 1035 °C (68 °F to 1895 °F) YS : as-cast \|\| within 10 degrees of (001) \|\| 20 °C to 1035 °C (68 °F to 1895 °F) SR : as-cast \|\| tested at 927 °C (1700 °F) \|\| 75 h to 1.4x10⁴ h SR : as-cast \|\| tested at 982 °C (1800 °F) \|\| 80 h to 1.5x10⁴ h SR : as-cast \|\| tested at 1038 °C (1900 °F) \|\| 80 h to 1.5x10⁴ h SR : as-cast \|\| tested at 1093 °C (2000 °F) \|\| 80 h to 1.5x10⁴ h SR : as-cast \|\| Master curve (LMP) \|\| 926 °C to 1094 °C (1699 °F to 2001 °F) FEN : single crystal within 10 degrees of (001) \|\| tested at 1038 °C (1900 °F), R = 0, total strain range \|\| 2.1x10³ cycles to 1.01x10⁶ cycles FEN : single crystal within 10 degrees of (001) \|\| tested at 1038 °C (1900 °F), R = -1, total strain range \|\| 3.1x10³ cycles to 1.6x10⁶ cycles FEN : single crystal within 10 degrees of (001) \|\| tested at 1093 °C (2000 °F), R = 0, total strain range \|\| 1.9x10³ cycles to 9.3x10⁴ cycles

PWA 1480 (some datasets are for temperatures below 20 °C)	D : solid \|\| -18 °C to 1260 °C (-1 °F to 2300 °F) DLL : solid \|\| -18 °C to 1260 °C (-1 °F to 2300 °F) MTE : solid \|\| -18 °C to 1260 °C (-1 °F to 2300 °F) CTE : solid \|\| -18 °C to 1260 °C (-1 °F to 2300 °F) E : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| unknown strain rate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 0.005/min strain rate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| 0.00833/s strain rate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solid \|\| unknown strain rate \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : condition not specified \|\| tested at 927 °C (1700 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 954 °C (1750 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 982 °C (1800 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 1010 °C (1850 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 1038 °C (1900 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 1066 °C (1950 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| tested at 1093 °C (2000 °F) \|\| 1x10³ h to 2x10⁴ h SR : condition not specified \|\| Master curve (LMP) \|\| 926 °C to 1094 °C (1699 °F to 2001 °F) FSN : in air \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10⁴ cycles to 2.6x10⁶ cycles
PWA 1484	D* : solid \|\| room temperature value TC : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) SSC : <111> direction \|\| tested at 982 °C (1800 °F), unknown strain rate \|\| 0 to 0.14 mm/mm strain SSC : <001> direction \|\| tested at 982 °C (1800 °F), unknown strain rate \|\| 0 to 0.14 mm/mm strain YS : solid \|\| 20 °C to 1088 °C (68 °F to 1990 °F) %El : solid \|\| 20 °C to 1088 °C (68 °F to 1990 °F) SR : casting \|\| tested at 871 °C (1600 °F) \|\| 370 h to 1,300 h SR : casting \|\| tested at 1038 °C (1900 °F) \|\| 15 h to 71 h SR : casting \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) FSN : <001> \|\| tested at 871 °C (1600 °F), R = 0.05, rotating beam, maximum stress \|\| 3x10³ cycles to 2x10⁵ cycles FSN : <001> \|\| tested at 1038 °C (1900 °F), R = -1, rotating beam, maximum stress \|\| 2x10⁵ cycles to 1.6x10⁷ cycles FSN : <001> \|\| tested at 1038 °C (1900 °F), R = -0.33, rotating beam, maximum stress \|\| 5x10⁵ cycles to 1x10⁷ cycles FSN : <001> \|\| tested at 1038 °C (1900 °F), R = 0.1, rotating beam, maximum stress \|\| 5x10⁵ cycles to 1x10⁷ cycles FSN : <001> \|\| tested at 1038 °C (1900 °F), R = 0.5, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁷ cycles FSN : <001> \|\| tested at 1038 °C (1900 °F), R = 0.8, rotating beam, maximum stress \|\| 2x10⁶ cycles to 1x10⁷ cycles CRS : 1% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 29 h to 630 h CRS : 1% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 20 h to 405 h CRS : 1% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 13 h to 155 h CRS : 1% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 2.5% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 80 h to 880 h CRS : 2.5% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 29 h to 540 h CRS : 2.5% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 19 h to 235 h CRS : 2.5% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 5% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 150 h to 1,070 h CRS : 5% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 35 h to 655 h CRS : 5% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 22 h to 285 h CRS : 5% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 7.5% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 180 h to 1,190 h CRS : 7.5% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 40 h to 725 h CRS : 7.5% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 25 h to 310 h CRS : 7.5% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 10% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 210 h to 1,280 h CRS : 10% plastic strain \|\| tested at 982 °C (1800 °F) \|\| 40 h to 770 h CRS : 10% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 25 h to 320 h CRS : 10% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 15% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 250 h to 1,405 h CRS : 15% plastic strain \|\| tested at 1038 °C (1900 °F) \|\| 30 h to 325 h CRS : 15% plastic strain \|\| Master curve (LMP) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 20% plastic strain \|\| tested at 871 °C (1600 °F) \|\| 265 h to 1,475 h IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 300 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 1,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 3,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 10,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 30,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 100,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, (001) direction \|\| 300,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 3 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 10 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 30 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 100 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 300 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 1,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, (001) direction \|\| 3,000 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 0.3 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 1 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 3 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 10 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 30 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 100 h \|\| 0 to 0.15 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, (001) direction \|\| 300 h \|\| 0 to 0.15 mm/mm strain
PWA 1489	FEN : in air \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 5.3x10³ cycles to 1.5x10⁵ cycles FEN : in H₂ \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 38 cycles to 8.1x10³ cycles
GTD111 DS	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| longitudinal \|\| 20 °C to 598 °C (68 °F to 1108 °F) E : solid \|\| transverse \|\| 20 °C to 598 °C (68 °F to 1108 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solid \|\| longitudinal \|\| 427 °C to 982 °C (800 °F to 1800 °F) YS : solid \|\| 0.02% offset longitudinal \|\| 427 °C to 982 °C (800 °F to 1800 °F) YS : solid \|\| 0.2% offset longitudinal \|\| 427 °C to 982 °C (800 °F to 1800 °F) %El : solid \|\| longitudinal \|\| 427 °C to 982 °C (800 °F to 1800 °F) FEN : longitudinal, smooth \|\| tested at 427 °C (800 °F), R = 0, axial, total strain range \|\| 2.7x10³ cycles to 2.3x10⁴ cycles FEN : longitudinal, smooth \|\| tested at 649 °C (1200 °F), R = 0, axial, total strain range \|\| 2x10³ cycles to 1.4x10⁵ cycles FEN : longitudinal, smooth \|\| tested at 816 °C (1500 °F), R = 0, axial, total strain range \|\| 710 cycles to 7.4x10⁵ cycles FEN : longitudinal, smooth \|\| tested at 982 °C (1800 °F), R = 0, axial, total strain range \|\| 1.79x10³ cycles to 1x10⁴ cycles FEN : transverse, smooth \|\| tested at 649 °C (1200 °F), R = 0, axial, total strain range \|\| 930 cycles to 4.8x10³ cycles FEN : transverse, smooth \|\| tested at 816 °C (1500 °F), R = 0, axial, total strain range \|\| 350 cycles to 1.75x10⁵ cycles FEN : longitudinal, notched, K_t = 3 \|\| tested at 816 °C (1500 °F), R = 0, axial, total strain range \|\| 1x10⁴ cycles to 8.3x10⁵ cycles
CM 186 LC	D : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) DLL : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) MTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) CTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) TC : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) TD : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) SH : solid \|\| 20 °C to 1267 °C (68 °F to 2312 °F) SH : liquid \|\| 1394 °C to 1427 °C (2541 °F to 2600 °F) UTS : as-cast \|\| 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) UTS : as-cast \|\| 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) UTS : as-cast \|\| 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) YS : as-cast \|\| 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) YS : as-cast \|\| 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) YS : as-cast \|\| 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) %El : as-cast \|\| 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) %El : as-cast \|\| 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) %El : as-cast \|\| 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h \|\| 550 °C to 950 °C (1022 °F to 1742 °F) SR : as-cast, double aged \|\| tested at 871 °C (1600 °F) \|\| 30 h to 1x10⁷ h SR : as-cast, double aged \|\| tested at 899 °C (1650 °F) \|\| 10 h to 3.5x10⁶ h SR : as-cast, double aged \|\| tested at 927 °C (1700 °F) \|\| 3 h to 7.6x10⁵ h SR : as-cast, double aged \|\| tested at 954 °C (1750 °F) \|\| 1 h to 1.65x10⁵ h SR : as-cast, double aged \|\| tested at 982 °C (1800 °F) \|\| 0.3 h to 4.2x10⁴ h SR : as-cast, double aged \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) CRS : 3% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h CRS : 4% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h CRS : 5% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h CRS : 6% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h CRS : 7% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h CRS : 8% plastic strain, solution annealed & aged <001> orientated bars \|\| tested at 750 °C (1382 °F) \|\| 200 h to 1,000 h IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & aged <001> orientated bars \|\| 200 h \|\| 0 to 0.8 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & aged <001> orientated bars \|\| 300 h \|\| 0 to 0.85 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & aged <001> orientated bars \|\| 700 h \|\| 0 to 0.16 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & aged <001> orientated bars \|\| 1,000 h \|\| 0 to 0.13 mm/mm strain
DD6	D* : solid \|\| room temperature value UTS : fully heat-treated \|\| [001], no low angle boundaries \|\| 800 °C to 980 °C (1472 °F to 1796 °F) UTS : fully heat-treated \|\| [001], 0 degree to 3 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) UTS : fully heat-treated \|\| [001], 3 degree to 6 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) UTS : fully heat-treated \|\| [001], 6 degree to 9 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) UTS : fully heat-treated \|\| [001], 9 degree to 12 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) %El : fully heat-treated \|\| [001], no low angle boundaries \|\| 800 °C to 980 °C (1472 °F to 1796 °F) %El : fully heat-treated \|\| [001], 0 degree to 3 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) %El : fully heat-treated \|\| [001], 3 degree to 6 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) %El : fully heat-treated \|\| [001], 6 degree to 9 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F) %El : fully heat-treated \|\| [001], 9 degree to 12 degree misorientation \|\| 800 °C to 980 °C (1472 °F to 1796 °F)
DS CM 247 LC	D* : solid \|\| room temperature value SSCC : heat treated and aged \|\| tested at 1000 °C (1832 °F), 2.5x10^-⁴/s, [001] \|\| 0 to 0.2 mm/mm strain UTS : 2-step solutioning, aged \|\| longitudinal \|\| 20 °C to 900 °C (68 °F to 1652 °F) UTS : 2-step solutioning, aged \|\| transverse \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : 2-step solutioning, aged \|\| longitudinal \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : 2-step solutioning, aged \|\| transverse \|\| 20 °C to 980 °C (68 °F to 1796 °F) %El : 2-step solutioning, aged \|\| longitudinal \|\| 20 °C to 900 °C (68 °F to 1652 °F) %El : 2-step solutioning, aged \|\| transverse \|\| 20 °C to 980 °C (68 °F to 1796 °F) SR : equiaxed \|\| tested at 871 °C (1600 °F) \|\| 1 h to 1.5x10⁵ h SR : equiaxed \|\| tested at 899 °C (1650 °F) \|\| 0.3 h to 4.5x10⁴ h SR : equiaxed \|\| tested at 927 °C (1700 °F) \|\| 0.1 h to 1.22x10⁴ h SR : equiaxed \|\| tested at 954 °C (1750 °F) \|\| 0.4 h to 3,150 h SR : equiaxed \|\| tested at 982 °C (1800 °F) \|\| 0.2 h to 1,070 h SR : equiaxed \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) SR : transverse \|\| tested at 871 °C (1600 °F) \|\| 1 h to 1.67x10⁶ h SR : transverse \|\| tested at 899 °C (1650 °F) \|\| 0.3 h to 5x10⁵ h SR : transverse \|\| tested at 927 °C (1700 °F) \|\| 0.1 h to 6.95x10⁴ h SR : transverse \|\| tested at 954 °C (1750 °F) \|\| 0.4 h to 3x10⁴ h SR : transverse \|\| tested at 982 °C (1800 °F) \|\| 0.2 h to 7,810 h SR : transverse \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) SR : longitudinal, heat treatment A \|\| tested at 871 °C (1600 °F) \|\| 3 h to 3.86x10⁴ h SR : longitudinal, heat treatment A \|\| tested at 899 °C (1650 °F) \|\| 1 h to 7,360 h SR : longitudinal, heat treatment A \|\| tested at 927 °C (1700 °F) \|\| 0.3 h to 2,860 h SR : longitudinal, heat treatment A \|\| tested at 954 °C (1750 °F) \|\| 0.1 h to 545 h SR : longitudinal, heat treatment A \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 155 h SR : longitudinal, heat treatment A \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) SR : longitudinal, heat treatment B \|\| tested at 871 °C (1600 °F) \|\| 1 h to 4.74x10⁶ h SR : longitudinal, heat treatment B \|\| tested at 899 °C (1650 °F) \|\| 0.3 h to 1.42x10⁶ h SR : longitudinal, heat treatment B \|\| tested at 927 °C (1700 °F) \|\| 0.1 h to 3.17x10⁵ h SR : longitudinal, heat treatment B \|\| tested at 954 °C (1750 °F) \|\| 0.4 h to 7.81x10⁴ h SR : longitudinal, heat treatment B \|\| tested at 982 °C (1800 °F) \|\| 0.2 h to 130 h SR : longitudinal, heat treatment B \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) SR : longitudinal, heat treatment C \|\| tested at 871 °C (1600 °F) \|\| 80 h to 6.05x10⁶ h SR : longitudinal, heat treatment C \|\| tested at 899 °C (1650 °F) \|\| 20 h to 1.2x10⁶ h SR : longitudinal, heat treatment C \|\| tested at 927 °C (1700 °F) \|\| 7 h to 3.9x10⁵ h SR : longitudinal, heat treatment C \|\| tested at 954 °C (1750 °F) \|\| 2 h to 7x10⁴ h SR : longitudinal, heat treatment C \|\| tested at 982 °C (1800 °F) \|\| 1 h to 2.25x10⁴ h SR : longitudinal, heat treatment C \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) SR : longitudinal, heat treatment D \|\| tested at 871 °C (1600 °F) \|\| 100 h to 3.65x10⁶ h SR : longitudinal, heat treatment D \|\| tested at 899 °C (1650 °F) \|\| 3 h to 6.6x10⁵ h SR : longitudinal, heat treatment D \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1.9x10⁵ h SR : longitudinal, heat treatment D \|\| tested at 954 °C (1750 °F) \|\| 3 h to 5.9x10⁴ h SR : longitudinal, heat treatment D \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1.8x10⁴ h SR : longitudinal, heat treatment D \|\| Master curve (LMP) \|\| 871 °C to 983 °C (1600 °F to 1801 °F) FEN : 0.003/s strain rate \|\| tested at 850 °C (1562 °F), R = -1, axial, longitudinal, total strain range \|\| 250 cycles to 3.4x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, longitudinal, total strain range \|\| 280 cycles to 3x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, long transverse, total strain range \|\| 180 cycles to 3.3x10³ cycles FEN : 0.003/s strain rate \|\| tested at 850 °C (1562 °F), R = -1, axial, longitudinal, plastic strain range \|\| 420 cycles to 6.8x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, longitudinal, plastic strain range \|\| 260 cycles to 3.3x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, long transverse, plastic strain range \|\| 180 cycles to 3.7x10³ cycles FEN : 0.003/s strain rate \|\| tested at 850 °C (1562 °F), R = -1, axial, longitudinal, elastic strain range \|\| 260 cycles to 3.4x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, longitudinal, elastic strain range \|\| 420 cycles to 6.8x10³ cycles FEN : 0.003/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, long transverse, elastic strain range \|\| 180 cycles to 3.35x10³ cycles FSN : longitudinal \|\| tested at 871 °C (1600 °F), R = 0.1, axial, maximum stress \|\| 4.2x10⁴ cycles to 2x10⁷ cycles
EP741NP	D : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) E* : discs, HIPed, aged & hardened \|\| room temperature value TC : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| discs, HIPed, aged & hardened \|\| 20 °C to 900 °C (68 °F to 1652 °F) UTS* : discs, HIPed, aged & hardened \|\| room temperature value YS* : discs, HIPed, aged & hardened \|\| room temperature value %El* : discs, HIPed, aged & hardened \|\| room temperature value SR : discs, HIPed, aged & hardened \|\| tested at 343 °C (650 °F) \|\| 120 h to 220 h
LSHR disk alloy	D : solid \|\| average \|\| 20 °C to 1200 °C (68 °F to 2192 °F) DLL : solid \|\| average \|\| 20 °C to 1200 °C (68 °F to 2192 °F) MTE : solid \|\| average \|\| 20 °C to 1200 °C (68 °F to 2192 °F) E : supersolvus material \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| supersolvus material \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TC : solid \|\| subsolvus material \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TC : solid \|\| average \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| supersolvus material \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| subsolvus material \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| average \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SH : solid \|\| average \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : supersolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : supersolvus material \|\| notched \|\| 20 °C to 756 °C (68 °F to 1393 °F) UTS : subsolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : subsolvus material \|\| notched \|\| 20 °C to 756 °C (68 °F to 1393 °F) YS : supersolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : subsolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : supersolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : subsolvus material \|\| smooth \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : supersolvus material \|\| tested at 649 °C (1200 °F) \|\| 3.58x10³ h to 2.45x10⁷ h SR : supersolvus material \|\| tested at 704 °C (1300 °F) \|\| 187 h to 7.75x10⁵ h SR : supersolvus material \|\| tested at 760 °C (1400 °F) \|\| 13.4 h to 3.56x10⁴ h SR : supersolvus material \|\| tested at 816 °C (1500 °F) \|\| 1.26 h to 2,240 h SR : supersolvus material \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) SR : subsolvus material \|\| tested at 649 °C (1200 °F) \|\| 5.26x10³ h to 3.03x10⁶ h SR : subsolvus material \|\| tested at 704 °C (1300 °F) \|\| 194 h to 7.76x10⁴ h SR : subsolvus material \|\| tested at 760 °C (1400 °F) \|\| 10.2 h to 2,960 h SR : subsolvus material \|\| tested at 816 °C (1500 °F) \|\| 0.725 h to 157 h SR : subsolvus material \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) FEN : supersolvus material \|\| tested at 427 °C (800 °F), R = 0, axial, total strain range \|\| 3x10³ cycles to 9.5x10⁴ cycles FEN : supersolvus material \|\| tested at 704 °C (1300 °F), R = 0, axial, total strain range \|\| 1x10³ cycles to 3.33x10⁵ cycles FEN : subsolvus material \|\| tested at 427 °C (800 °F), R = 0, axial, total strain range \|\| 6.58x10³ cycles to 5.74x10⁵ cycles FEN : subsolvus material \|\| tested at 704 °C (1300 °F), R = 0, axial, total strain range \|\| 498 cycles to 9.54x10⁶ cycles CRS : 0.2% plastic strain, supersolvus material \|\| tested at 649 °C (1200 °F) \|\| 3.58x10³ h to 2.45x10⁷ h CRS : 0.2% plastic strain, supersolvus material \|\| tested at 704 °C (1300 °F) \|\| 187 h to 7.75x10⁵ h CRS : 0.2% plastic strain, supersolvus material \|\| tested at 760 °C (1400 °F) \|\| 13.4 h to 3.56x10⁴ h CRS : 0.2% plastic strain, supersolvus material \|\| tested at 816 °C (1500 °F) \|\| 1.26 h to 2,240 h CRS : 0.2% plastic strain, supersolvus material \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) CRS : 0.2% plastic strain, subsolvus material \|\| tested at 649 °C (1200 °F) \|\| 94.4 h to 6.8x10⁵ h CRS : 0.2% plastic strain, subsolvus material \|\| tested at 704 °C (1300 °F) \|\| 3.15 h to 1.38x10⁴ h CRS : 0.2% plastic strain, subsolvus material \|\| tested at 760 °C (1400 °F) \|\| 0.15 h to 421 h CRS : 0.2% plastic strain, subsolvus material \|\| tested at 816 °C (1500 °F) \|\| 0.17 h to 18.5 h CRS : 0.2% plastic strain, subsolvus material \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F)
SC 16	FEN : 0.001/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, total strain range \|\| 220 cycles to 4x10³ cycles FEN : 1x10^-⁵/s strain rate \|\| tested at 950 °C (1742 °F), R = -1, axial, total strain range \|\| 280 cycles to 3x10³ cycles

Incoloy 807	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) UTS : as-extruded \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : as-extruded \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : as-extruded \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 704 °C to 1038 °C (1299 °F to 1900 °F)
Incoloy 825 (UNS N08825) (WNr 2.4858) (ISO/EN/DIN NW8825/NiCr21Mo/NiCr2Mo/NiFe30Cr21Mo3) (JIS NCF825) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| -150 °C to 900 °C (-238 °F to 1652 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : annealed \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : annealed \|\| 20 °C to 927 °C (68 °F to 1700 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Incoloy 890 (UNS N08890)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) G : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) v : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) K : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC* : solid \|\| room temperature value UTS* : solution annealed \|\| hot-rolled plate \|\| room temperature value UTS* : solution annealed \|\| cold-drawn tubing \|\| room temperature value YS* : solution annealed \|\| hot-rolled plate \|\| room temperature value YS* : solution annealed \|\| cold-drawn tubing \|\| room temperature value %El* : solution annealed \|\| hot-rolled plate \|\| room temperature value %El* : solution annealed \|\| cold-drawn tubing \|\| room temperature value SR : tubing & plate \|\| tested at 871 °C (1600 °F) \|\| 400 h to 4x10⁴ h SR : tubing & plate \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁵ h SR : tubing & plate \|\| tested at 1093 °C (2000 °F) \|\| 100 h to 1x10⁵ h SR : tubing & plate \|\| tested at 1177 °C (2150 °F) \|\| 80 h to 2,000 h SR : tubing & plate \|\| Master curve (LMP) \|\| 871 °C to 1177 °C (1600 °F to 2150 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 908 (UNS N09908) (ASTM B872)	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) E* : solid \|\| room temperature value G* : solid \|\| room temperature value v* : solid \|\| room temperature value K* : solid \|\| room temperature value TC* : solid \|\| room temperature value TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS* : as-aged \|\| room temperature value YS* : as-aged \|\| room temperature value %El* : as-aged \|\| room temperature value
Incoloy 925 (UNS N09925)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) E : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) G : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) v : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) K : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) TC : solid \|\| solution-annealed & aged \|\| 20 °C to 1150 °C (68 °F to 2102 °F) TD : solid \|\| solution-annealed & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) SH : solid \|\| solution-annealed & aged \|\| 20 °C to 900 °C (68 °F to 1652 °F) UTS : age hardened \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : age hardened \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : age hardened \|\| 20 °C to 650 °C (68 °F to 1202 °F) FSN : rotating beam \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1.9x10⁵ cycles to 2.7x10⁷ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 945 (UNS N09945)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) G : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) v : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) K : solid \|\| 20 °C to 704 °C (68 °F to 1299 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| 20 °C to 1150 °C (68 °F to 2102 °F) UTS* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 114 mm (4.5 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 305 mm (12 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 356 mm (14 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 114 mm (4.5 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 305 mm (12 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 356 mm (14 inch) rod \|\| room temperature value YS : age hardened \|\| 20 °C to 232 °C (68 °F to 449 °F) %El* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 114 mm (4.5 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 305 mm (12 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 356 mm (14 inch) rod \|\| room temperature value FSN : rotating beam \|\| tested at 20 °C (68 °F), R = -1, rotating beam, K_t = 1.0, maximum stress \|\| 2.5x10⁵ cycles to 1x10⁷ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Incoloy 945X (UNS N09945)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) TC : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) SH : solid \|\| 20 °C to 1149 °C (68 °F to 2100 °F) UTS* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value UTS* : annealed and aged \|\| 216 mm (8.5 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value YS* : annealed and aged \|\| 216 mm (8.5 inch) rod \|\| room temperature value YS : tube \|\| longitudinal \|\| 20 °C to 288 °C (68 °F to 550 °F) YSC : tube \|\| longitudinal \|\| 20 °C to 288 °C (68 °F to 550 °F) %El* : annealed and aged \|\| 25.4 mm (1 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 50.8 mm (2 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 88.9 mm (3.5 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 152 mm (6 inch) rod \|\| room temperature value %El* : annealed and aged \|\| 216 mm (8.5 inch) rod \|\| room temperature value FEN : annealed & aged \|\| tested at 232 °C (450 °F), R = -1, axial, total strain range \|\| 900 cycles to 1x10⁴ cycles RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value

Nimonic 75 (UNS N06075) (WNr 2.4630/2.4951) (ISO/EN/DIN NiCr20Ti) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 0 °C to 800 °C (32 °F to 1472 °F) TD : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.22 mm/mm strain UTS : solid \|\| heat-treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| heat-treated bar \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : solid \|\| heat-treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| heat-treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| heat-treated sheet \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solid \|\| heat-treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : sheet, 1050 °C (1922 °F), air cooled \|\| tested at 450 °C (842 °F) \|\| 1x10⁵ h to unknown strain rate h SR : sheet, 1050 °C (1922 °F), air cooled \|\| tested at 500 °C (932 °F) \|\| 2x10³ h to 1x10⁹ h SR : sheet, 1050 °C (1922 °F), air cooled \|\| tested at 550 °C (1022 °F) \|\| 80 h to 1x10⁸ h SR : sheet, 1050 °C (1922 °F), air cooled \|\| tested at 600 °C (1112 °F) \|\| 5 h to 1x10⁷ h SR : sheet, 1050 °C (1922 °F), air cooled \|\| tested at 625 °C (1157 °F) \|\| 1 h to 1x10⁵ h SR : sheet, 1050 °C (1922 °F), air cooled \|\| Master curve (LMP) \|\| 450 °C to 626 °C (842 °F to 1159 °F) SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 600 °C (1112 °F) \|\| 1x10⁵ h to unknown strain rate h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 650 °C (1202 °F) \|\| 1x10⁴ h to unknown strain rate h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 700 °C (1292 °F) \|\| 1x10³ h to 1x10⁹ h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁸ h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 800 °C (1472 °F) \|\| 10 h to 1x10⁸ h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 850 °C (1562 °F) \|\| 1 h to 5x10⁶ h SR : bar, 1050 °C (1922 °F), air cooled \|\| tested at 450 °C (842 °F) \|\| 0.1 h to 5x10⁴ h SR : bar, 1050 °C (1922 °F), air cooled \|\| Master curve (LMP) \|\| 600 °C to 901 °C (1112 °F to 1654 °F) HE : solid \|\| oxidized \|\| 500 °C to 1000 °C (932 °F to 1832 °F) NE : solid \|\| as-rolled \|\| 315 °C to 730 °C (599 °F to 1346 °F) NE : solid \|\| buffed \|\| 310 °C to 775 °C (590 °F to 1427 °F) NE : solid \|\| shot blasted \|\| 265 °C to 810 °C (509 °F to 1490 °F) NE : solid \|\| as-rolled, oxidized \|\| 315 °C to 760 °C (599 °F to 1400 °F) NE : solid \|\| buffed, oxidized \|\| 315 °C to 760 °C (599 °F to 1400 °F) NE : solid \|\| shot blasted, oxidized \|\| 260 °C to 710 °C (500 °F to 1310 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Nimonic 80A (UNS N07080) (WNr 2.4631/2.4952) (ISO/EN/DIN NW7080/NiCr20Ti2Al/NiCr20TiAl) (JIS NCF80A) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| double aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| triple aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| average \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| double aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| triple aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| average \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| double aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| triple aged \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| average \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : sheet, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : extruded bar, forged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : extruded bar, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : sheet, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : sheet, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : sheet, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| heat-treated \|\| 0 °C to 1000 °C (32 °F to 1832 °F) TD : solid \|\| heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded, stretched, solution annealed & treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| cold-rolled, solution annealed & treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded, cold-rolled, solution annealed & treated section \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded, cold-rolled, solution annealed & treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded, stretched, solution annealed & treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| cold-rolled, solution annealed & treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded, cold-rolled, solution annealed & treated section \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded, cold-rolled, solution annealed & treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded, stretched, solution annealed & treated bar \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solid \|\| cold-rolled, solution annealed & treated sheet \|\| 20 °C to 1100 °C (68 °F to 2012 °F) %El : solid \|\| extruded, cold-rolled, solution annealed & treated section \|\| 20 °C to 900 °C (68 °F to 1652 °F) %El : solid \|\| extruded, cold-rolled, solution annealed & treated bar \|\| 20 °C to 900 °C (68 °F to 1652 °F) SR : solution annealed & treated cold-rolled sheet \|\| tested at 650 °C (1202 °F) \|\| 20 h to 7,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 10 h to 2,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 10 h to 2,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 10 h to 2,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 10 h to 2,000 h SR : solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 650 °C to 851 °C (1202 °F to 1564 °F) FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 300 °C (572 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 480 °C (896 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 600 °C (1112 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 700 °C (1292 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles FSN : extruded, cold-rolled, solution annealed & treated bar \|\| tested at 750 °C (1382 °F), R = -1, axial, maximum stress \|\| 100 cycles to 1x10³ cycles CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 649 °C (1200 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| Master curve (LMP) \|\| 650 °C to 851 °C (1202 °F to 1564 °F) CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 650 °C (1202 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| Master curve (LMP) \|\| 650 °C to 851 °C (1202 °F to 1564 °F) CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 600 °C (1112 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 815 °C (1499 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 600 °C to 816 °C (1112 °F to 1501 °F) CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 600 °C (1112 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 100 h to 3x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 815 °C (1499 °F) \|\| 100 h to 3x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 600 °C to 816 °C (1112 °F to 1501 °F) CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 600 °C (1112 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 650 °C (1202 °F) \|\| 300 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 300 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 815 °C (1499 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 600 °C to 816 °C (1112 °F to 1501 °F) IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 300,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated sheet \|\| 1,000,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated sheet \|\| 300,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic 81	D : solid \|\| bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) D : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : sheet, solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : sheet, solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : sheet, solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : sheet, solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution annealed & aged \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F) FSN : bar \|\| tested at 700 °C (1292 °F), R = -1, rotating beam, maximum stress \|\| 1.4x10⁴ cycles to 6.43x10⁷ cycles RHO : solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic 86	D : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) DLL : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) MTE : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) CTE : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) E : solid \|\| 20 °C to 1050 °C (68 °F to 1922 °F) UTS : solid \|\| forged bar \|\| 300 °C to 850 °C (572 °F to 1562 °F) UTS : solid \|\| cold-rolled sheet \|\| 20 °C to 1050 °C (68 °F to 1922 °F) YS : solid \|\| forged bar \|\| 300 °C to 850 °C (572 °F to 1562 °F) YS : solid \|\| cold-rolled sheet \|\| 20 °C to 1050 °C (68 °F to 1922 °F) %El : solid \|\| forged bar \|\| 300 °C to 850 °C (572 °F to 1562 °F) %El : solid \|\| cold-rolled sheet \|\| 20 °C to 1050 °C (68 °F to 1922 °F) SR : sheet, 1150 °C (2102 °F), air cooled \|\| tested at 700 °C (1292 °F) \|\| 5x10⁵ h to unknown strain rate h SR : sheet, 1150 °C (2102 °F), air cooled \|\| tested at 750 °C (1382 °F) \|\| 3x10⁴ h to 1x10⁹ h SR : sheet, 1150 °C (2102 °F), air cooled \|\| tested at 800 °C (1472 °F) \|\| 2x10³ h to 1x10⁸ h SR : sheet, 1150 °C (2102 °F), air cooled \|\| tested at 850 °C (1562 °F) \|\| 200 h to 1x10⁷ h SR : sheet, 1150 °C (2102 °F), air cooled \|\| tested at 900 °C (1652 °F) \|\| 0.1 h to 5x10⁵ h SR : sheet, 1150 °C (2102 °F), air cooled \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F)
Nimonic 90 (UNS N07090) (WNr 2.4632) (ISO/EN/DIN NW7090/NiCr20Co18Ti/NiCr20Co18Ti3)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| extruded/forged bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| extruded section, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| bar, heat-treated \|\| 20 °C to 760 °C (68 °F to 1400 °F) TC : solid \|\| cold-rolled sheet, heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| bar, heat-treated \|\| 20 °C to 760 °C (68 °F to 1400 °F) TD : solid \|\| cold-rolled sheet, heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded/forged bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded section, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| cold-rolled sheet 0.1% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| cold-rolled sheet 0.2% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded bar 0.1% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded bar 0.2% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded/forged bar 0.1% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded/forged bar 0.2% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded section, cold-rolled 0.1% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded section, cold-rolled 0.2% \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| cold-rolled sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded/forged bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded section, cold-rolled \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : extruded/forged bar \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1x10⁴ h SR : extruded/forged bar \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h SR : extruded/forged bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 3,000 h SR : extruded/forged bar \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : extruded/forged bar \|\| Master curve (LMP) \|\| 700 °C to 872 °C (1292 °F to 1601 °F) SR : cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 3,000 h SR : cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h SR : cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h SR : cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 3,000 h SR : cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h SR : cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) FSN : rotating beam, solution annealed & treated extruded bar \|\| tested at 750 °C (1382 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁷ cycles to 1.5x10⁸ cycles FSN : rotating beam, solution annealed & treated extruded bar \|\| tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁷ cycles to 1.5x10⁸ cycles FSN : rotating beam, solution annealed & treated extruded bar \|\| tested at 871 °C (1600 °F), R = -1, rotating beam, maximum stress \|\| 1.5x10⁷ cycles to 1.5x10⁸ cycles FSN : uniaxial, solution annealed & treated extruded bar \|\| tested at 600 °C (1112 °F), R = -1, axial, maximum stress \|\| 3.6x10⁷ cycles to 1.2x10⁸ cycles FSN : uniaxial, solution annealed & treated extruded bar \|\| tested at 700 °C (1292 °F), R = -1, axial, maximum stress \|\| 3.6x10⁷ cycles to 1.2x10⁸ cycles FSN : uniaxial, solution annealed & treated extruded bar \|\| tested at 750 °C (1382 °F), R = -1, axial, maximum stress \|\| 3.6x10⁷ cycles to 1.2x10⁸ cycles FSN : uniaxial, solution annealed & treated extruded bar \|\| tested at 816 °C (1500 °F), R = -1, axial, maximum stress \|\| 1.2x10⁷ cycles to 1.2x10⁸ cycles FSN : uniaxial, solution annealed & treated extruded bar \|\| tested at 871 °C (1600 °F), R = -1, axial, maximum stress \|\| 1.2x10⁷ cycles to 1.2x10⁸ cycles CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 600 °C (1112 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated extrusions \|\| Master curve (LMP) \|\| 600 °C to 872 °C (1112 °F to 1601 °F) CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 600 °C (1112 °F) \|\| 100 h to 3,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, solution annealed & treated extrusions \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 600 °C (1112 °F) \|\| 300 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 650 °C (1202 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 700 °C (1292 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 750 °C (1382 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & treated extrusions \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 300 h CRS : 0.1% plastic strain, solution annealed & treated sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 300 h CRS : 0.2% plastic strain, solution annealed & treated sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) IC : tested at 600 °C (1112 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 600 °C (1112 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 600 °C (1112 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 600 °C (1112 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 600 °C (1112 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated extrusions \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated extrusions \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated extrusions \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated extrusions \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated extrusions \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 300,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated sheet \|\| 1,000,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated sheet \|\| 300,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated sheet \|\| 100,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated sheet \|\| 30,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated sheet \|\| 10,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated sheet \|\| 3,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated sheet \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 0.1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated sheet \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic 91	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solution annealed & aged \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : extruded & forged bar \|\| tested at 750 °C (1382 °F) \|\| 30 h to 1x10⁵ h SR : extruded & forged bar \|\| tested at 800 °C (1472 °F) \|\| 3 h to 1x10⁴ h SR : extruded & forged bar \|\| tested at 850 °C (1562 °F) \|\| 0.4 h to 1,000 h SR : extruded & forged bar \|\| tested at 870 °C (1598 °F) \|\| 0.2 h to 625 h SR : extruded & forged bar \|\| Master curve (LMP) \|\| 750 °C to 871 °C (1382 °F to 1600 °F)
Nimonic 95 (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC : solid \|\| 0 °C to 800 °C (32 °F to 1472 °F)
Nimonic 100	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Nimonic 101	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic PE16	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 788 °C (68 °F to 1450 °F) SH : solid \|\| 20 °C to 788 °C (68 °F to 1450 °F) UTS : solid \|\| bar heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solid \|\| bar heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| bar heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solid \|\| bar heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| bar heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solid \|\| bar heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 800 °C (1472 °F) / 700 °C (1292 °F) \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solid \|\| sheet heat-treated 1040 °C (1904 °F) / 900 °C (1652 °F) / 750 °C (1382 °F) \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : sheet \|\| tested at 650 °C (1202 °F), 1 h treatment \|\| 50 h to 5,000 h SR : sheet \|\| tested at 700 °C (1292 °F), 1 h treatment \|\| 50 h to 5,000 h SR : sheet \|\| tested at 750 °C (1382 °F), 1 h treatment \|\| 50 h to 5,000 h SR : sheet \|\| tested at 650 °C (1202 °F), 2 h treatment \|\| 50 h to 1,000 h SR : sheet \|\| tested at 700 °C (1292 °F), 2 h treatment \|\| 50 h to 1,000 h SR : sheet \|\| tested at 750 °C (1382 °F), 2 h treatment \|\| 50 h to 1,000 h SR : sheet \|\| Master curve (LMP), 1 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) SR : sheet \|\| Master curve (LMP), 2 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) SR : bar \|\| tested at 650 °C (1202 °F), 1 h treatment \|\| 1x10³ h to 1x10⁴ h SR : bar \|\| tested at 700 °C (1292 °F), 1 h treatment \|\| 30 h to 1x10⁴ h SR : bar \|\| tested at 750 °C (1382 °F), 1 h treatment \|\| 30 h to 1x10⁴ h SR : bar \|\| tested at 650 °C (1202 °F), 2 h treatment \|\| 300 h to 1x10⁴ h SR : bar \|\| tested at 700 °C (1292 °F), 2 h treatment \|\| 100 h to 1x10⁴ h SR : bar \|\| tested at 750 °C (1382 °F), 2 h treatment \|\| 300 h to 1x10⁴ h SR : bar \|\| Master curve (LMP), 1 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) SR : bar \|\| Master curve (LMP), 2 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) SR : bar \|\| Master curve (LMP), solution annealed at 1040 °C (1904 °F) \|\| 450 °C to 701 °C (842 °F to 1294 °F) SR : tube \|\| tested at 650 °C (1202 °F), 1 h treatment \|\| 100 h to 1x10⁴ h SR : tube \|\| tested at 700 °C (1292 °F), 1 h treatment \|\| 50 h to 1x10⁴ h SR : tube \|\| tested at 750 °C (1382 °F), 1 h treatment \|\| 50 h to 1x10⁴ h SR : tube \|\| tested at 650 °C (1202 °F), 2 h treatment \|\| 100 h to 1x10⁴ h SR : tube \|\| tested at 700 °C (1292 °F), 2 h treatment \|\| 100 h to 1x10⁴ h SR : tube \|\| tested at 750 °C (1382 °F), 2 h treatment \|\| 100 h to 1x10⁴ h SR : tube \|\| Master curve (LMP), 1 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) SR : tube \|\| Master curve (LMP), 2 h treatment \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 300 h CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 3,000 h CRS : 0.1% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, 1 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.1% plastic strain, 1 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 5,000 h CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 3,000 h CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 1 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.2% plastic strain, 1 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 1 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.5% plastic strain, 1 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 1% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 5,000 h CRS : 1% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 5,000 h CRS : 1% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 5,000 h CRS : 1% plastic strain, 1 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 1 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 1 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 1 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 1% plastic strain, 1 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, 2 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.1% plastic strain, 2 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, 2 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.2% plastic strain, 2 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 0.5% plastic strain, 2 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 0.5% plastic strain, 2 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 1% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), sheet \|\| 50 h to 1,000 h CRS : 1% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), sheet \|\| 50 h to 1,000 h CRS : 1% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), sheet \|\| 50 h to 1,000 h CRS : 1% plastic strain, 2 h treatment \|\| tested at 650 °C (1202 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 2 h treatment \|\| tested at 700 °C (1292 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 2 h treatment \|\| tested at 750 °C (1382 °F), bar \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, 2 h treatment \|\| Master curve (LMP) sheet \|\| 650 °C to 751 °C (1202 °F to 1384 °F) CRS : 1% plastic strain, 2 h treatment \|\| Master curve (LMP) bar \|\| 650 °C to 751 °C (1202 °F to 1384 °F) IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 1 h treatment, bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 1 h treatment, bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 1 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 1 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 1 h treatment, bar \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, sheet \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, 2 h treatment, bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 675 °C (1247 °F), plastic strain, 2 h treatment, bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, 2 h treatment, bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, 2 h treatment, bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, 2 h treatment, bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic PK33	D : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) D : solid \|\| sheet \|\| 20 °C to 1020 °C (68 °F to 1868 °F) DLL : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) DLL : solid \|\| sheet \|\| 20 °C to 1020 °C (68 °F to 1868 °F) MTE : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) MTE : solid \|\| sheet \|\| 20 °C to 1020 °C (68 °F to 1868 °F) CTE : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) CTE : solid \|\| sheet \|\| 20 °C to 1020 °C (68 °F to 1868 °F) E : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) E : solid \|\| sheet \|\| 20 °C to 1020 °C (68 °F to 1868 °F) G : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) v : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) K : solid \|\| forged bar \|\| 20 °C to 1020 °C (68 °F to 1868 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| precipitation hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| mill annealed \|\| 816 °C to 871 °C (1501 °F to 1600 °F) YS : solid \|\| precipitation hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| mill annealed \|\| 816 °C to 871 °C (1501 °F to 1600 °F) %El : solid \|\| precipitation hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| mill annealed \|\| 816 °C to 871 °C (1501 °F to 1600 °F) SR : solution annealed & treated forged bar \|\| tested at 700 °C (1292 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated forged bar \|\| tested at 750 °C (1382 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated forged bar \|\| tested at 800 °C (1472 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated forged bar \|\| tested at 850 °C (1562 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated forged bar \|\| tested at 900 °C (1652 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated forged bar \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) SR : solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 500 h CRS : 0.1% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 3,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 3,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 3,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 3,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 3,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 3,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain RHO : sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

Rene 77 (some datasets are for temperatures below 20 °C)	D* : solid \|\| room temperature value TC : solid \|\| 0 °C to 343 °C (32 °F to 649 °F)
Rene 80	D : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) D : liquid \|\| 1338 °C to 1427 °C (2440 °F to 2600 °F) DLL : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) DLL : liquid \|\| 1338 °C to 1427 °C (2440 °F to 2600 °F) MTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) MTE : liquid \|\| 1338 °C to 1427 °C (2440 °F to 2600 °F) CTE : solid \|\| 20 °C to 1127 °C (68 °F to 2060 °F) CTE : liquid \|\| 1338 °C to 1427 °C (2440 °F to 2600 °F) E : solid \|\| 20 °C to 1029 °C (68 °F to 1884 °F) TC : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) TD : solid \|\| 20 °C to 927 °C (68 °F to 1700 °F) SH : solid \|\| 20 °C to 1212 °C (68 °F to 2213 °F) SH : liquid \|\| 1338 °C to 1427 °C (2440 °F to 2600 °F) SSC : 4-step heat treatment, 3.3x10^-⁵/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.01 mm/mm strain SSC : 4-step heat treatment, 3.3x10^-⁵/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.13 mm/mm strain SSC : 4-step heat treatment, 3.3x10^-⁴/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.01 mm/mm strain SSC : 4-step heat treatment, 3.3x10^-⁴/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.16 mm/mm strain SSC : 4-step heat treatment, 0.001/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.14 mm/mm strain SSC : 4-step heat treatment, 0.0033/s \|\| tested at 538 °C (1000 °F) \|\| 0 to 0.01 mm/mm strain SSC : 4-step heat treatment, 0.0033/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.01 mm/mm strain FEN : 4-step heat treatment \|\| tested at 871 °C (1600 °F), R = -1, axial, plastic strain range \|\| 300 cycles to 4.5x10³ cycles FEN : 3-step and 4-step heat treatments, 0.01 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 475 cycles to 1x10⁵ cycles FEN : 3-step and 4-step heat treatments, 0.1 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 490 cycles to 1x10⁵ cycles FEN : 3-step and 4-step heat treatments, 1 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 280 cycles to 1x10⁵ cycles FEN : 3-step and 4-step heat treatments, 1 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, plastic strain range \|\| 280 cycles to 1.5x10⁴ cycles FEN : 3-step and 4-step heat treatments, 1 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, elastic strain range \|\| 280 cycles to 1.5x10⁴ cycles FEN : 3-step and 4-step heat treatments, 10 cpm \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 190 cycles to 1x10⁵ cycles CRS : 0.25% plastic strain, 4-step heat treatment \|\| tested at 871 °C (1600 °F) \|\| 0.003 h to 0.21 h CRS : 0.5% plastic strain, 4-step heat treatment \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 6.8 h IC : tested at 871 °C (1600 °F), plastic strain, 4-step heat treatment \|\| 0.1 h \|\| 0 to 5.02x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, 4-step heat treatment \|\| 0.3 h \|\| 0 to 6.65x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, 4-step heat treatment \|\| 1 h \|\| 0 to 9.82x10^-³ mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, 4-step heat treatment \|\| 2 h \|\| 0 to 0.13 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step heat treatment \|\| 0.1 h \|\| 0 to 0.11 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step heat treatment \|\| 0.3 h \|\| 0 to 0.13 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step heat treatment \|\| 1 h \|\| 0 to 0.17 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step heat treatment \|\| 2 h \|\| 0 to 0.2 mm/mm strain
Rene 88 DT	D* : solid \|\| room temperature value SSCC : 0.00032/s \|\| tested at 1052 °C (1925 °F) \|\| 0 to 1.4 mm/mm strain SSCC : 0.0032/s \|\| tested at 1052 °C (1925 °F) \|\| 0 to 1.4 mm/mm strain SSCC : 0.032/s \|\| tested at 1052 °C (1925 °F) \|\| 0 to 1.7 mm/mm strain SSCC : 0.1/s \|\| tested at 1052 °C (1925 °F) \|\| 0 to 1.9 mm/mm strain UTS : annealed \|\| 20 °C to 649 °C (68 °F to 1200 °F) YS : annealed \|\| 20 °C to 649 °C (68 °F to 1200 °F) FSN : forging, supersolvus heat treatment, aged \|\| tested at 593 °C (1100 °F), R = 0.05, axial, 10 Hz, maximum stress \|\| 2x10³ cycles to 1.2x10⁷ cycles FSN : forging, supersolvus heat treatment, aged \|\| tested at 593 °C (1100 °F), R = 0.05, axial, ultrasonic, 19.2 kHz, maximum stress \|\| 6x10⁵ cycles to 1x10⁹ cycles
Rene 90	D : liquid \|\| 1368 °C to 1515 °C (2494 °F to 2759 °F) DLL : liquid \|\| 1368 °C to 1515 °C (2494 °F to 2759 °F) MTE : liquid \|\| 1368 °C to 1515 °C (2494 °F to 2759 °F) CTE : liquid \|\| 1368 °C to 1515 °C (2494 °F to 2759 °F) ST : liquid \|\| 1367 °C to 1477 °C (2492 °F to 2690 °F)
Rene 95	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) TC : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) SSC : cast & wrought \|\| tested at 649 °C (1200 °F), unknown strain rate \|\| 0 to 0.85 mm/mm strain SSCC : 0.1/s \|\| tested at 1038 °C (1900 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1079 °C (1975 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1121 °C (2050 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1038 °C (1900 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1079 °C (1975 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1121 °C (2050 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1038 °C (1900 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1079 °C (1975 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1121 °C (2050 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1038 °C (1900 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1079 °C (1975 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 0.1/s \|\| tested at 1121 °C (2050 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1038 °C (1900 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1079 °C (1975 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1121 °C (2050 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1038 °C (1900 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1079 °C (1975 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1121 °C (2050 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1038 °C (1900 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1079 °C (1975 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1121 °C (2050 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1038 °C (1900 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1079 °C (1975 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 1/s \|\| tested at 1121 °C (2050 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1038 °C (1900 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1079 °C (1975 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1121 °C (2050 °F), +230 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1038 °C (1900 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1079 °C (1975 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1121 °C (2050 °F), -270+400 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1038 °C (1900 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1079 °C (1975 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1121 °C (2050 °F), -500 mesh \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1038 °C (1900 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1079 °C (1975 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain SSCC : 5/s \|\| tested at 1121 °C (2050 °F), average of all mesh sizes \|\| 0 to 0.5 mm/mm strain UTS : heat-treated \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : heat-treated \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : heat-treated \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 705 °C (1200 °F to 1301 °F) FEN : cast & wrought material \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, total strain range \|\| 200 cycles to 3.2x10⁴ cycles FEN : HIPed, forged, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range \|\| 180 cycles to 2.6x10⁵ cycles FEN : HIPed, forged, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range \|\| 260 cycles to 5.1x10³ cycles FEN : forged, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, plastic strain range \|\| 200 cycles to 2.85x10⁴ cycles FSN : cast & wrought material \|\| tested at 649 °C (1200 °F), R = -1, rotating beam, maximum stress \|\| 200 cycles to 3.2x10⁴ cycles CRS : 0.75% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.18 h to 7.3 h CRS : 1% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.36 h to 25 h CRS : 1.5% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.0098 h to 7.51 h CRS : 2% plastic strain \|\| tested at 650 °C (1202 °F) \|\| 0.51 h to 0.39 h IC : tested at 650 °C (1202 °F), plastic strain \|\| 0.1 h \|\| 0 to 0.2 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain \|\| 0.3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain \|\| 1 h \|\| 0 to 0.15 mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain \|\| 3 h \|\| 0 to 0.15 mm/mm strain

SX Rene N5	D : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) D : liquid \|\| 1385 °C to 1485 °C (2525 °F to 2705 °F) DLL : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) DLL : liquid \|\| 1385 °C to 1485 °C (2525 °F to 2705 °F) MTE : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) MTE : liquid \|\| 1385 °C to 1485 °C (2525 °F to 2705 °F) CTE : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) CTE : liquid \|\| 1385 °C to 1485 °C (2525 °F to 2705 °F) E : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TC : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSCC : heat treated and aged \|\| tested at 1000 °C (1832 °F), 2.5x10^-⁴/s, [001] \|\| 0 to 0.23 mm/mm strain ST : liquid \|\| 1367 °C to 1527 °C (2492 °F to 2780 °F)
SX Rene N515	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)

Hastelloy A (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| 0 °C to 900 °C (32 °F to 1652 °F) UTS : rolled & annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F) YS : rolled & annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F) %El : rolled & annealed \|\| -196 °C to 27 °C (-321 °F to 80 °F)
Hastelloy B (UNS N10001) (WNr 2.4600) (JIS NW0001) (AFNOR Ni-Mo28) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -253 °C to 1240 °C (-424 °F to 2264 °F) DLL : solid \|\| -253 °C to 1240 °C (-424 °F to 2264 °F) MTE : solid \|\| -253 °C to 1240 °C (-424 °F to 2264 °F) CTE : solid \|\| -253 °C to 1240 °C (-424 °F to 2264 °F) E : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TC : solid \|\| 0 °C to 1046 °C (32 °F to 1915 °F) TD : solid \|\| 0 °C to 538 °C (32 °F to 1000 °F) SH : solid \|\| 0 °C to 1204 °C (32 °F to 2200 °F) UTS : bright anneal \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : bright anneal \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : bright anneal \|\| 20 °C to 1095 °C (68 °F to 2003 °F) NE : solid \|\| 2 micro-inch RMS finish \|\| -187 °C to 990 °C (-305 °F to 1814 °F) NE : solid \|\| 15 micro-inch RMS finish \|\| -187 °C to 990 °C (-305 °F to 1814 °F) VP : solid \|\| 1100 °C to 1325 °C (2012 °F to 2417 °F) RHO : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F) SIGMA : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F)
Hastelloy B-2 (UNS N10665) (WNr 2.4817) (ISO/EN/DIN NW0665/NiMo28) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TC : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F) TD : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F) SH : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F) UTS : solid \|\| 2.5 mm to 8.9 mm (0.0984 inch to 0.35 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : solid \|\| 9.1 mm to 51 inch plate \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solid \|\| 2.5 mm to 8.9 mm (0.0984 inch to 0.35 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solid \|\| 9.1 mm to 51 inch plate \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| 2.5 mm to 8.9 mm (0.0984 inch to 0.35 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| 9.1 mm to 51 inch plate \|\| 20 °C to 427 °C (68 °F to 800 °F) RHO : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F) SIGMA : solid \|\| 0 °C to 600 °C (32 °F to 1112 °F)
Hastelloy B-3 (UNS N10675)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| plate \|\| 20 °C to 650 °C (68 °F to 1202 °F) UTS : solid \|\| sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| plate \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : solid \|\| sheet \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : solid \|\| plate \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| sheet \|\| 20 °C to 427 °C (68 °F to 800 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Hastelloy C (UNS N10002) (WNr 2.4602) (AFNOR NiMo16Cr15C) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -42 °C to 1154 °C (-44 °F to 2109 °F) DLL : solid \|\| -42 °C to 1154 °C (-44 °F to 2109 °F) MTE : solid \|\| -42 °C to 1154 °C (-44 °F to 2109 °F) CTE : solid \|\| -42 °C to 1154 °C (-44 °F to 2109 °F) TC : solid \|\| 20 °C to 1075 °C (68 °F to 1967 °F) TD : solid \|\| 20 °C to 1075 °C (68 °F to 1967 °F) SH : solid \|\| 20 °C to 1205 °C (68 °F to 2201 °F) UTS : rolled & annealed \|\| -200 °C to 27 °C (-328 °F to 80 °F) YS : rolled & annealed \|\| -200 °C to 27 °C (-328 °F to 80 °F) %El : rolled & annealed \|\| -200 °C to 27 °C (-328 °F to 80 °F) FSN : solution treated \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 600 cycles to 4x10⁶ cycles FSN : solution treated \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 400 cycles to 1x10⁶ cycles FSN : TIG welded \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : TIG welded \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 4x10⁶ cycles FSN : TIG welded \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated, K_t = 3.8 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : solution treated, K_t = 3.8 \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles FSN : solution treated, K_t = 3.8 \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles NE : solid \|\| 2 micro-inch RMS finish \|\| -196 °C to 827 °C (-321 °F to 1520 °F) NE : solid \|\| 15 micro-inch RMS finish \|\| -196 °C to 827 °C (-321 °F to 1520 °F) RHO : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Hastelloy C-4 (UNS N06455) (WNr 2.4610) (ISO/EN/DIN NW6455/NiMo16Cr16Ti)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : solid \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : solid \|\| 9.52 mm (0.375 inch) plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| 9.52 mm (0.375 inch) plate, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| 3.17 mm (0.125 inch) sheet, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solid \|\| 12.7 mm (0.5 inch) plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : solid \|\| 9.52 mm (0.375 inch) plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| 9.52 mm (0.375 inch) plate, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| 3.17 mm (0.125 inch) sheet, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solid \|\| 12.7 mm (0.5 inch) plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| 6.35 mm (0.25 inch) plate \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : solid \|\| 9.52 mm (0.375 inch) plate \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| 9.52 mm (0.375 inch) plate, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| 3.17 mm (0.125 inch) sheet, aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solid \|\| 12.7 mm (0.5 inch) plate \|\| 20 °C to 538 °C (68 °F to 1000 °F) RHO : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Hastelloy C-22 HS	D* : solid \|\| room temperature value SSC : annealed \|\| tested at 20 °C (68 °F), 0.001/s \|\| 0 to 0.3 mm/mm strain
Nimonic 105 (UNS N13021) (WNr 2.4634) (ISO/EN/DIN NW3021/NiCo20Cr15MoAlTi/NiCo21Cr15Mo5Al4Ti)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| extruded & rolled or forged rod \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| extruded rod \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SSCC : heat-treated, 0.38/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 0.38/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 0.38/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 2.22/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 2.22/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 2.22/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 11.8/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 11.8/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 11.8/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 64.3/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 64.3/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.5 mm/mm strain SSCC : heat-treated, 64.3/s \|\| tested at 1250 °C (2282 °F) \|\| 0 to 0.5 mm/mm strain UTS : solid \|\| extruded & stretched bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| extruded bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : solid \|\| extruded & forged bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) UTS : solid \|\| extruded & cold-rolled bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded & stretched bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| extruded bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YS : solid \|\| extruded & forged bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) YS : solid \|\| extruded & cold-rolled bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded & stretched bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| extruded bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) %El : solid \|\| extruded & forged bar \|\| 20 °C to 1100 °C (68 °F to 2012 °F) %El : solid \|\| extruded & cold-rolled bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : heat treatment #1 \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁵ h SR : heat treatment #1 \|\| tested at 815 °C (1499 °F) \|\| 100 h to 1x10⁵ h SR : heat treatment #1 \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁵ h SR : heat treatment #1 \|\| tested at 940 °C (1724 °F) \|\| 100 h to 1x10⁴ h SR : heat treatment #1 \|\| tested at 982 °C (1800 °F) \|\| 100 h to 3,000 h SR : heat treatment #2 \|\| tested at 550 °C (1022 °F) \|\| 90 h to 2,000 h SR : heat treatment #2 \|\| tested at 600 °C (1112 °F) \|\| 90 h to 2,000 h SR : heat treatment #2 \|\| tested at 650 °C (1202 °F) \|\| 90 h to 2,000 h SR : heat treatment #2 \|\| tested at 700 °C (1292 °F) \|\| 80 h to 2,000 h SR : heat treatment #2 \|\| Master curve (LMP) \|\| 550 °C to 701 °C (1022 °F to 1294 °F) CRS : 0.1% plastic strain, heat treatment #1 \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, heat treatment #1 \|\| tested at 750 °C (1382 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, heat treatment #1 \|\| tested at 815 °C (1499 °F) \|\| 100 h to 1x10⁴ h CRS : 0.1% plastic strain, heat treatment #1 \|\| tested at 870 °C (1598 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, heat treatment #1 \|\| tested at 650 °C (1202 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% plastic strain, heat treatment #1 \|\| tested at 750 °C (1382 °F) \|\| 100 h to 3x10⁴ h CRS : 0.2% plastic strain, heat treatment #1 \|\| tested at 815 °C (1499 °F) \|\| 100 h to 3x10⁴ h CRS : 0.2% plastic strain, heat treatment #1 \|\| tested at 870 °C (1598 °F) \|\| 100 h to 3x10⁴ h CRS : 0.2% plastic strain, heat treatment #1 \|\| tested at 980 °C (1796 °F) \|\| 100 h to 300 h CRS : 0.5% plastic strain, heat treatment #1 \|\| tested at 650 °C (1202 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, heat treatment #1 \|\| tested at 750 °C (1382 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, heat treatment #1 \|\| tested at 815 °C (1499 °F) \|\| 300 h to 3x10⁴ h CRS : 0.5% plastic strain, heat treatment #1 \|\| tested at 870 °C (1598 °F) \|\| 100 h to 3x10⁴ h CRS : 0.5% plastic strain, heat treatment #1 \|\| tested at 980 °C (1796 °F) \|\| 100 h to 1,000 h IC : tested at 650 °C (1202 °F), plastic strain, heat treatment #1 \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, heat treatment #1 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, heat treatment #1 \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, heat treatment #1 \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 650 °C (1202 °F), plastic strain, heat treatment #1 \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, heat treatment #1 \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 815 °C (1499 °F), plastic strain, heat treatment #1 \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 870 °C (1598 °F), plastic strain, heat treatment #1 \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 980 °C (1796 °F), plastic strain, heat treatment #1 \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 980 °C (1796 °F), plastic strain, heat treatment #1 \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain RHO : wire \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : wire \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic 115 (WNr 2.4636)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value UTS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 815 °C (1499 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Nimonic 263 (UNS N07263) (WNr 2.4650) (ISO/EN/DIN NW7263/NiCo20Cr20Mo5Ti2Al)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| forged billets \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| forged billets \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| extruded bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| forged billets \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD* : solid \|\| room temperature value SH* : solid \|\| room temperature value SSC : annealed sheet \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.215 mm/mm strain UTS : solid \|\| heat-treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| heat-treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| heat-treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solid \|\| heat-treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| heat-treated sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solid \|\| heat-treated bar \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : solution annealed & treated extrusion \|\| tested at 550 °C (1022 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 600 °C (1112 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 650 °C (1202 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 800 °C (1472 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 850 °C (1562 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| tested at 900 °C (1652 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 550 °C to 901 °C (1022 °F to 1654 °F) SR : solution annealed & treated cold-rolled sheet \|\| tested at 550 °C (1022 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 600 °C (1112 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 650 °C (1202 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 30 h to 3,000 h SR : solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 550 °C to 901 °C (1022 °F to 1654 °F) CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 0.1% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 1% plastic strain, solution annealed & treated extrusion \|\| tested at 700 °C (1292 °F) \|\| 300 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated extrusion \|\| tested at 750 °C (1382 °F) \|\| 50 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated extrusion \|\| tested at 800 °C (1472 °F) \|\| 50 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated extrusion \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated extrusion \|\| tested at 900 °C (1652 °F) \|\| 50 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated extrusion \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 5,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 5,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 5,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 1,000 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 100 h CRS : 0.2% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 700 °C (1292 °F) \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 750 °C (1382 °F) \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 800 °C (1472 °F) \|\| 50 h to 5,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 850 °C (1562 °F) \|\| 50 h to 3,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 900 °C (1652 °F) \|\| 50 h to 100 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 700 °C to 901 °C (1292 °F to 1654 °F) IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated extrusion \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated extrusion \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated extrusion \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated extrusion \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated extrusion \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 700 °C (1292 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 725 °C (1337 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 750 °C (1382 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 775 °C (1427 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 800 °C (1472 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 825 °C (1517 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 850 °C (1562 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 875 °C (1607 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 900 °C (1652 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Nimonic 901 (Alloy 901) (UNS N09901) (WNr 2.4662) (ISO/EN/DIN NW9911/NiFe36Cr12Mo6Ti3) (AISI 681/682) (AMS 5660/5661) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) TD : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) SH : solid \|\| 0 °C to 982 °C (32 °F to 1800 °F) SSC : solution treated & aged bar \|\| tested at 24 °C (75 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : solution treated & aged bar \|\| tested at 650 °C (1202 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain UTS : AMS 5660A, bar and forgings \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : AMS 5660A, bar and forgings \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : AMS 5660A, bar and forgings \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SR : AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 12.7 mm (0.5 inch) bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) SR : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 25.4 mm (1 inch) bar \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) SR : AMS 5660A, 25.4 mm (1 inch) by 76.2 mm (3 inch) forging \|\| tested at 760 °C (1400 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 25.4 mm (1 inch) by 76.2 mm (3 inch) forging \|\| tested at 982 °C (1800 °F) \|\| 0.1 h to 1,000 h SR : AMS 5660A, 25.4 mm (1 inch) by 76.2 mm (3 inch) forging \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) FEN : 15.9 mm (0.625 inch) square bar \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 150 cycles to 1.3x10³ cycles FEN : 15.9 mm (0.625 inch) square bar \|\| tested at 538 °C (1000 °F), R = -1, axial, total strain range \|\| 150 cycles to 1.3x10³ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 2.4x10³ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 204 °C (400 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 7x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 316 °C (600 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 1.5x10⁵ cycles to 1.5x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 1.2x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 538 °C (1000 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 1x10⁵ cycles to 1.5x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 649 °C (1200 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 649 °C (1200 °F), R = 0.2, axial, 60 Hz, maximum stress \|\| 3x10⁴ cycles to 1.5x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 3.7x10⁴ cycles to 3.2x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F), R = 0.2, axial, 60 Hz, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 871 °C (1600 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 982 °C (1800 °F), R = 0.2, axial, 30 Hz, maximum stress \|\| 1.5x10⁵ cycles to 2x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = 0.01, axial, 30 Hz, maximum stress \|\| 1.4x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 316 °C (600 °F), R = 0.01, axial, 30 Hz, maximum stress \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 538 °C (1000 °F), R = 0.01, axial, 30 Hz, maximum stress \|\| 2x10⁴ cycles to 1.7x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F), R = 0.01, axial, 30 Hz, maximum stress \|\| 2.3x10⁴ cycles to 2x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 982 °C (1800 °F), R = 0.01, axial, 30 Hz, maximum stress \|\| 2.3x10⁴ cycles to 3x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = -0.33, axial, 30 Hz, maximum stress \|\| 1x10⁴ cycles to 2x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 316 °C (600 °F), R = -0.33, axial, 30 Hz, maximum stress \|\| 1.4x10⁴ cycles to 4x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 538 °C (1000 °F), R = -0.33, axial, 30 Hz, maximum stress \|\| 1x10⁴ cycles to 3.7x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F), R = -0.33, axial, 30 Hz, maximum stress \|\| 1.7x10⁴ cycles to 9.1x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 982 °C (1800 °F), R = -0.33, axial, 30 Hz, maximum stress \|\| 2.6x10⁴ cycles to 2.4x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = -1, axial, 30 Hz, maximum stress \|\| 1x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 316 °C (600 °F), R = -1, axial, 30 Hz, maximum stress \|\| 1.7x10⁴ cycles to 1.4x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 538 °C (1000 °F), R = -1, axial, 30 Hz, maximum stress \|\| 6x10³ cycles to 8x10⁵ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 760 °C (1400 °F), R = -1, axial, 30 Hz, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5660A, 25.4 mm (1 inch) bar \|\| tested at 982 °C (1800 °F), R = -1, axial, 30 Hz, maximum stress \|\| 4.2x10⁴ cycles to 2x10⁵ cycles CRS : 0.05% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h CRS : 0.05% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 1 h to 100 h CRS : 0.05% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 4 h to 1,000 h CRS : 0.05% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 2 h to 330 h CRS : 0.1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h CRS : 0.1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 2 h to 230 h CRS : 0.1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 2 h to 1,000 h CRS : 0.1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.2 h to 1,000 h CRS : 0.3% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h CRS : 0.3% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 6 h to 500 h CRS : 0.3% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 6 h to 1,000 h CRS : 0.3% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.2 h to 1,000 h CRS : 0.5% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h CRS : 0.5% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 7 h to 1,000 h CRS : 0.5% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.3 h to 1,000 h CRS : 0.5% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 649 °C (1200 °F) \|\| 1 h to 1,000 h CRS : 1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 760 °C (1400 °F) \|\| 18 h to 1,000 h CRS : 1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| tested at 982 °C (1800 °F) \|\| 0.6 h to 1,000 h CRS : 1% plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, AMS 5660A, 12.7 mm (0.5 inch) bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Nimonic 942	D : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solution annealed & aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : solution annealed & aged, bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F)
Nimonic PE11	D : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) CTE : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| aged \|\| 20 °C to 777 °C (68 °F to 1430 °F) TD : solid \|\| aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : precipitation hardened \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : precipitation hardened \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : precipitation hardened \|\| 20 °C to 760 °C (68 °F to 1400 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F)
Hastelloy C-2000 (UNS N06200) (WNr 2.4675) (ISO/EN/DIN NiCr23Mo16Cu)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : average of plates & bars \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : average of plates & bars \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : average of plates & bars \|\| 20 °C to 650 °C (68 °F to 1202 °F) RHO : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SIGMA : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F)
Hastelloy G-30 (UNS N06030) (WNr 2.4603) (ISO/EN/DIN NiCr30FeMo)	D : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) DLL : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) MTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) CTE : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) E : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) TC : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) RHO : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Hastelloy G-35 (UNS N06035) (WNr 2.4643) (ISO/EN/DIN NiCr33Mo8) (some datasets are for temperatures below 20 °C)	D : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) DLL : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) MTE : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) CTE : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) E : solution annealed \|\| 10 °C to 600 °C (50 °F to 1112 °F) TC : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) UTS : sheet/plate/bar \|\| 12.7 mm (0.5 inch) thick plate, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) UTS : sheet/plate/bar \|\| 12.7 mm (0.5 inch) diameter bar, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) UTS : welds \|\| GTAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : welds \|\| GMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : welds \|\| weld metal from GMAW \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) YS : sheet/plate/bar \|\| 12.7 mm (0.5 inch) thick plate, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) YS : sheet/plate/bar \|\| 12.7 mm (0.5 inch) diameter bar, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) YS : welds \|\| GTAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : welds \|\| GMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : welds \|\| weld metal from GMAW \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) %El : sheet/plate/bar \|\| 12.7 mm (0.5 inch) thick plate, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) %El : sheet/plate/bar \|\| 12.7 mm (0.5 inch) diameter bar, solution annealed at 1121 °C (2050 °F) \|\| 20 °C to 649 °C (68 °F to 1200 °F) %El : welds \|\| GTAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : welds \|\| GMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : welds \|\| weld metal from GMAW \|\| 20 °C to 538 °C (68 °F to 1000 °F) RHO : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Hastelloy G-50 (UNS N06950)	D : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) DLL : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) MTE : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) CTE : solid \|\| 20 °C to 316 °C (68 °F to 600 °F) UTS : solid \|\| transverse \|\| 20 °C to 316 °C (68 °F to 600 °F) UTS : solid \|\| longitudinal \|\| 20 °C to 316 °C (68 °F to 600 °F) YS : solid \|\| transverse \|\| 20 °C to 316 °C (68 °F to 600 °F) YS : solid \|\| longitudinal \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : solid \|\| transverse \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : solid \|\| longitudinal \|\| 20 °C to 316 °C (68 °F to 600 °F)
Hastelloy HYBRID-BC1 (UNS N10362) (WNr 2.4708) (ISO/EN/DIN NiMo22Cr15) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solution annealed \|\| -150 °C to 600 °C (-238 °F to 1112 °F) DLL : solution annealed \|\| -150 °C to 600 °C (-238 °F to 1112 °F) MTE : solution annealed \|\| -150 °C to 600 °C (-238 °F to 1112 °F) CTE : solution annealed \|\| -150 °C to 600 °C (-238 °F to 1112 °F) E : solution annealed \|\| values above RT \|\| 10 °C to 600 °C (50 °F to 1112 °F) E : solution annealed \|\| values for 19 mm (0.75 inch) sheet below RT \|\| -157 °C to 24 °C (-251 °F to 75 °F) E : solution annealed \|\| combined values below/above RT \|\| -157 °C to 600 °C (-251 °F to 1112 °F) G* : solution annealed \|\| room temperature value v* : solution annealed \|\| room temperature value K* : solution annealed \|\| room temperature value TC : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) TD : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) SH : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) UTS : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, cold-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : sheet/plate/bar \|\| 19 mm (0.75 inch) thick plate, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : sheet/plate/bar \|\| 25.4 mm (1 inch) bar, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : welds \|\| TIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : welds \|\| GMAW/MIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : welds \|\| SMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) UTS : welds \|\| weld metal from GMAW/MIG \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, cold-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : sheet/plate/bar \|\| 19 mm (0.75 inch) thick plate, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : sheet/plate/bar \|\| 25.4 mm (1 inch) bar, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : welds \|\| TIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : welds \|\| GMAW/MIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : welds \|\| SMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) YS : welds \|\| weld metal from GMAW/MIG \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : sheet/plate/bar \|\| 3.17 mm (0.125 inch) thick sheet, cold-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : sheet/plate/bar \|\| 19 mm (0.75 inch) thick plate, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : sheet/plate/bar \|\| 25.4 mm (1 inch) bar, hot-rolled & solution annealed \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : welds \|\| TIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : welds \|\| GMAW/MIG welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : welds \|\| SMAW welded 12.7 mm (0.5 inch) plate, transverse \|\| 20 °C to 427 °C (68 °F to 800 °F) %El : welds \|\| weld metal from GMAW/MIG \|\| 20 °C to 427 °C (68 °F to 800 °F) RHO : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F) SIGMA : solution annealed \|\| 20 °C to 600 °C (68 °F to 1112 °F)
Hastelloy N (UNS N10003) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 10 °C to 1050 °C (50 °F to 1922 °F) TC : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) TD : solid \|\| 20 °C to 700 °C (68 °F to 1292 °F) SH : solid \|\| 0 °C to 700 °C (32 °F to 1292 °F) UTS : sheet \|\| heat-treated at 1177 °C (2150 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : sheet \|\| heat-treated at 1177 °C (2150 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : sheet \|\| heat-treated at 1177 °C (2150 °F) \|\| 20 °C to 927 °C (68 °F to 1700 °F) SR : sheet \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : sheet \|\| Master curve (LMP) \|\| 593 °C to 927 °C (1099 °F to 1700 °F) SR : investment cast \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : investment cast \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : investment cast \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : investment cast \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : investment cast \|\| Master curve (LMP) \|\| 593 °C to 927 °C (1099 °F to 1700 °F) CRS : 0.1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 0.15 h to 2.5 h CRS : 0.1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 0.1 h to 2.3 h CRS : 0.2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 0.14 h to 53 h CRS : 0.2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 7.5 h CRS : 0.2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 0.5 h to 7.5 h CRS : 0.3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 1.1 h to 60 h CRS : 0.3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 1 h to 12 h CRS : 0.3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 0.8 h to 15 h CRS : 0.3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 0.4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 2.4 h to 65 h CRS : 0.4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 0.48 h to 16 h CRS : 0.4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 1.1 h to 20 h CRS : 0.4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 0.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 5 h to 75 h CRS : 0.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 0.75 h to 21 h CRS : 0.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 1.45 h to 25 h CRS : 0.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 0.75% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 7.5 h to 90 h CRS : 0.75% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 1.5 h to 30 h CRS : 0.75% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 2.2 h to 40 h CRS : 0.75% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 0.5 h to 105 h CRS : 1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 2.3 h to 40 h CRS : 1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 2.9 h to 55 h CRS : 1% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 1.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 0.5 h to 135 h CRS : 1.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 3.9 h to 55 h CRS : 1.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 4 h to 80 h CRS : 1.5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 1.4 h to 160 h CRS : 2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 5.5 h to 75 h CRS : 2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 5 h to 100 h CRS : 2% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 4.4 h to 225 h CRS : 3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 38 h to 105 h CRS : 3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 8 h to 130 h CRS : 3% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 60 h to 330 h CRS : 4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 47 h to 130 h CRS : 4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 155 h CRS : 4% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) CRS : 5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 704 °C (1300 °F) \|\| 75 h to 370 h CRS : 5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 816 °C (1500 °F) \|\| 56 h to 145 h CRS : 5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| tested at 927 °C (1700 °F) \|\| 12 h to 180 h CRS : 5% total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| Master curve (LMP) \|\| 704 °C to 927 °C (1299 °F to 1700 °F) IC : tested at 704 °C (1300 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 1 h \|\| 0 to 0.15 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 3 h \|\| 0 to 0.2 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 10 h \|\| 0 to 0.3 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 30 h \|\| 0 to 0.3 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 100 h \|\| 0 to 0.5 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 0.3 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 10 h \|\| 0 to 0.2 mm/mm strain IC : tested at 816 °C (1500 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 30 h \|\| 0 to 0.2 mm/mm strain IC : tested at 927 °C (1700 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 1 h \|\| 0 to 3x10^-³ mm/mm strain IC : tested at 927 °C (1700 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 10 h \|\| 0 to 0.4 mm/mm strain IC : tested at 927 °C (1700 °F), total strain, 1.6 mm (0.063 inch) sheet, 1177 °C (2150 °F), air cooled \|\| 30 h \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Hastelloy S (UNS N06635) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1095 °C (68 °F to 2003 °F) DLL : solid \|\| 20 °C to 1095 °C (68 °F to 2003 °F) MTE : solid \|\| 20 °C to 1095 °C (68 °F to 2003 °F) CTE : solid \|\| 20 °C to 1095 °C (68 °F to 2003 °F) E : solid \|\| 20 °C to 1095 °C (68 °F to 2003 °F) TC : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) TD : solid \|\| 0 °C to 1000 °C (32 °F to 1832 °F) SH : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solid \|\| solution treated plate \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : solid \|\| solution treated sheet \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : solid \|\| solution treated plate \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : solid \|\| solution treated sheet \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : solid \|\| solution treated plate \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : solid \|\| solution treated sheet \|\| 20 °C to 1095 °C (68 °F to 2003 °F) SR : heat-treated sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : heat-treated sheet \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1,000 h SR : heat-treated sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : heat-treated sheet \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : heat-treated sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SR : heat-treated plate \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated plate \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated plate \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated plate \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated plate \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : heat-treated plate \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) CRS : 0.2% plastic strain, heat-treated sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated sheet \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 100 h CRS : 0.2% plastic strain, heat-treated sheet \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) CRS : 0.5% plastic strain, heat-treated sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated sheet \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 100 h CRS : 0.5% plastic strain, heat-treated sheet \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) CRS : 1% plastic strain, heat-treated sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, heat-treated sheet \|\| tested at 732 °C (1350 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, heat-treated sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 100 h CRS : 1% plastic strain, heat-treated sheet \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F) CRS : 0.2% plastic strain, heat-treated plate \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated plate \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated plate \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated plate \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated plate \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, heat-treated plate \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) CRS : 0.5% plastic strain, heat-treated plate \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated plate \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated plate \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated plate \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated plate \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, heat-treated plate \|\| Master curve (LMP) \|\| 648 °C to 872 °C (1198 °F to 1601 °F) CRS : 1% plastic strain, heat-treated plate \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, heat-treated plate \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, heat-treated plate \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, heat-treated plate \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, heat-treated plate \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, heat-treated plate \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, heat-treated plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, heat-treated plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, heat-treated plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, heat-treated plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, heat-treated plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, heat-treated plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, heat-treated plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, heat-treated plate \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, heat-treated plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
Hastelloy W (UNS N10004)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : annealed & quenched \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : annealed & quenched \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : annealed & quenched \|\| 20 °C to 1095 °C (68 °F to 2003 °F)

Haynes 75	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : annealed \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : annealed \|\| 20 °C to 980 °C (68 °F to 1796 °F) %El : annealed \|\| 20 °C to 980 °C (68 °F to 1796 °F) SR : sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h SR : sheet \|\| Master curve (LMP) \|\| 650 °C to 872 °C (1202 °F to 1601 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes 214 (UNS N07214) (WNr 2.4646)	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) CTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SH : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) UTS : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) SR : solution annealed & rapidly cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed & rapidly cooled \|\| Master curve (LMP) \|\| 760 °C to 1094 °C (1400 °F to 2001 °F) CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 760 °C (1400 °F) to 927 °C (1700 °F) \|\| 760 °C to 927 °C (1400 °F to 1700 °F) CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 871 °C (1600 °F) to 1038 °C (1900 °F) \|\| 871 °C to 1038 °C (1600 °F to 1900 °F) CRS : 0.5% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 982 °C (1800 °F) to 1093 °C (2000 °F) \|\| 982 °C to 1094 °C (1799 °F to 2001 °F) CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 760 °C (1400 °F) to 927 °C (1700 °F) \|\| 760 °C to 927 °C (1400 °F to 1700 °F) CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 927 °C (1700 °F) to 982 °C (1800 °F) \|\| 926 °C to 983 °C (1699 °F to 1801 °F) CRS : 1% plastic strain, solution annealed & rapidly cooled \|\| Master curve (LMP) 982 °C (1800 °F) to 1093 °C (2000 °F) \|\| 981 °C to 1094 °C (1798 °F to 2001 °F) IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed & rapidly cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain, solution annealed & rapidly cooled \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution annealed & rapidly cooled \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1066 °C (1950 °F), plastic strain, solution annealed & rapidly cooled \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution annealed & rapidly cooled \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Haynes 230 (Inconel 230) (UNS N06230/N06231) (WNr 2.4733)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) v : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) K : solid \|\| 20 °C to 850 °C (68 °F to 1562 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSCC : annealed, 0.001/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.001/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.57 mm/mm strain SSCC : annealed, 0.05/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.56 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.55 mm/mm strain SSCC : annealed, 0.5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 1/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 5/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.53 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.52 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.45 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.43 mm/mm strain SSCC : annealed, 5/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.54 mm/mm strain SSCC : annealed, 20/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 0.4 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.43 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.44 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.44 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.23 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1175 °C (2147 °F) \|\| 0 to 0.44 mm/mm strain SSCC : annealed, 20/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.44 mm/mm strain UTS : solid \|\| as-cast \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) UTS : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| as-cast \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| as-cast \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| cold-rolled & solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) SR : solution annealed sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h SR : solution annealed sheet \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1,000 h SR : solution annealed sheet \|\| Master curve (LMP) \|\| 649 °C to 1038 °C (1200 °F to 1900 °F) SR : solution annealed plate & bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution annealed plate & bar \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1,000 h SR : solution annealed plate & bar \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1,000 h SR : solution annealed plate & bar \|\| tested at 1149 °C (2100 °F) \|\| 10 h to 1,000 h SR : solution annealed plate & bar \|\| Master curve (LMP) \|\| 649 °C to 1150 °C (1200 °F to 2102 °F) SR : investment cast, as-cast \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h SR : investment cast, as-cast \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1,000 h SR : investment cast, as-cast \|\| tested at 1149 °C (2100 °F) \|\| 10 h to 1,000 h SR : investment cast, as-cast \|\| Master curve (LMP) \|\| 760 °C to 1150 °C (1400 °F to 2102 °F) FEN : plate \|\| tested at 427 °C (800 °F), R = -1, total strain range \|\| 2.4x10³ cycles to 1x10⁵ cycles FEN : plate \|\| tested at 760 °C (1400 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁵ cycles FEN : plate \|\| tested at 871 °C (1600 °F), R = -1, total strain range \|\| 1.5x10³ cycles to 1x10⁵ cycles FEN : plate \|\| tested at 982 °C (1800 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁵ cycles CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, solution annealed sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed plate & bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed plate & bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed plate & bar \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed plate & bar \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed plate & bar \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed plate & bar \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed plate & bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, solution annealed plate & bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution annealed plate & bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes 233	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 600 °C to 1000 °C (1112 °F to 1832 °F) TD : solid \|\| 600 °C to 1093 °C (1112 °F to 2000 °F) SH : solid \|\| 600 °C to 1000 °C (1112 °F to 1832 °F) UTS : age-hardened \|\| sheet \|\| 20 °C to 816 °C (68 °F to 1501 °F) YS : age-hardened \|\| sheet \|\| 20 °C to 816 °C (68 °F to 1501 °F) %El : age-hardened \|\| sheet \|\| 20 °C to 816 °C (68 °F to 1501 °F) RHO : solid \|\| 600 °C to 1000 °C (1112 °F to 1832 °F) SIGMA : solid \|\| 600 °C to 1000 °C (1112 °F to 1832 °F)
Haynes 242	D : solid \|\| 20 °C to 973 °C (68 °F to 1783 °F) DLL : solid \|\| 20 °C to 973 °C (68 °F to 1783 °F) MTE : solid \|\| 20 °C to 973 °C (68 °F to 1783 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solid \|\| annealed & aged cold-rolled sheet \|\| 20 °C to 980 °C (68 °F to 1796 °F) UTS : solid \|\| annealed & aged rings & bars \|\| 20 °C to 980 °C (68 °F to 1796 °F) UTS : solid \|\| annealed & aged hot-rolled plate \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : solid \|\| annealed & aged cold-rolled sheet \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : solid \|\| annealed & aged rings & bars \|\| 20 °C to 980 °C (68 °F to 1796 °F) YS : solid \|\| annealed & aged hot-rolled plate \|\| 20 °C to 980 °C (68 °F to 1796 °F) %El : solid \|\| annealed & aged cold-rolled sheet \|\| 20 °C to 980 °C (68 °F to 1796 °F) %El : solid \|\| annealed & aged rings & bars \|\| 20 °C to 980 °C (68 °F to 1796 °F) %El : solid \|\| annealed & aged hot-rolled plate \|\| 20 °C to 980 °C (68 °F to 1796 °F) SR : annealed & aged \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : annealed & aged \|\| tested at 871 °C (1600 °F) \|\| 10 h to 100 h SR : annealed & aged \|\| Master curve (LMP) \|\| 540 °C to 871 °C (1004 °F to 1600 °F) FEN : age-hardened \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 460 cycles to 1.12x10⁵ cycles FEN : age-hardened \|\| tested at 760 °C (1400 °F), R = -1, total strain range \|\| 700 cycles to 1.5x10⁵ cycles CRS : 1% plastic strain, annealed & aged plate \|\| tested at 649 °C (1200 °F) \|\| 30 h to 6,650 h CRS : 1% plastic strain, annealed & aged plate \|\| tested at 704 °C (1300 °F) \|\| 10 h to 2,750 h CRS : 1% plastic strain, annealed & aged plate \|\| Master curve (LMP) \|\| 649 °C to 707 °C (1200 °F to 1304 °F) RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes 244	D : solid \|\| 20 °C to 984 °C (68 °F to 1803 °F) DLL : solid \|\| 20 °C to 984 °C (68 °F to 1803 °F) MTE : solid \|\| 20 °C to 984 °C (68 °F to 1803 °F) SH : solid \|\| 20 °C to 980 °C (68 °F to 1796 °F) UTS : annealed \|\| pancake forging \|\| 20 °C to 871 °C (68 °F to 1600 °F) UTS : two-step age-hardened \|\| pancake/plate \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : annealed \|\| pancake forging \|\| 20 °C to 870 °C (68 °F to 1598 °F) YS : two-step age-hardened \|\| pancake/plate \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : annealed \|\| pancake forging \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : two-step age-hardened \|\| pancake/plate \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : two-step age-hardened \|\| tested at 649 °C (1200 °F) \|\| 110 h to 9,100 h SR : two-step age-hardened \|\| tested at 760 °C (1400 °F) \|\| 19 h to 312 h SR : two-step age-hardened \|\| Master curve (LMP) \|\| 648 °C to 761 °C (1198 °F to 1402 °F) FEN : two-step age-hardened \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 1x10³ cycles to 2.51x10⁵ cycles FEN : two-step age-hardened \|\| tested at 760 °C (1400 °F), R = -1, total strain range \|\| 1.6x10³ cycles to 2.59x10⁵ cycles CRS : 1% plastic strain, annealed & aged billet \|\| tested at 649 °C (1200 °F) \|\| 25 h to 660 h CRS : 1% plastic strain, annealed & aged billet \|\| tested at 704 °C (1300 °F) \|\| 11 h to 1,640 h CRS : 1% plastic strain, annealed & aged billet \|\| tested at 760 °C (1400 °F) \|\| 4 h to 975 h CRS : 1% plastic strain, annealed & aged billet \|\| Master curve (LMP) \|\| 649 °C to 761 °C (1200 °F to 1402 °F)
Haynes 263 (UNS N07263)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : sheet \|\| solution treated at 1149 °C (2100 °F), aged at 799 °C (1470 °F) \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) YS : sheet \|\| solution treated at 1149 °C (2100 °F), aged at 799 °C (1470 °F) \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) %El : sheet \|\| solution treated at 1149 °C (2100 °F), aged at 799 °C (1470 °F) \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : sheet \|\| mill annealed \|\| 760 °C to 843 °C (1400 °F to 1549 °F) SR : solution annealed & treated cold-rolled sheet \|\| tested at 540 °C (1004 °F) \|\| 100 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 593 °C (1100 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h SR : solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 540 °C to 871 °C (1004 °F to 1600 °F) SR : age hardened sheet \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) FEN : sheet \|\| tested at 816 °C (1500 °F), R = -1, total strain range \|\| 700 cycles to 7x10⁴ cycles CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 100 h CRS : 0.5% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 704 °C to 872 °C (1299 °F to 1601 °F) CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| tested at 871 °C (1600 °F) \|\| 10 h to 100 h CRS : 1% plastic strain, solution annealed & treated cold-rolled sheet \|\| Master curve (LMP) \|\| 704 °C to 872 °C (1299 °F to 1601 °F) CRS : 1% plastic strain, age hardened sheet \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated cold-rolled sheet \|\| 300 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes 273	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Haynes 282 (UNS N07208) (AMS 5951)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) G : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) v : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) K : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| age-hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solid \|\| age-hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solid \|\| age-hardened \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SSC : wrought & aged plate, 8.3x10^-⁴/s \|\| tested at 20 °C (68 °F) \|\| 0 to 0.294 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, as-received \|\| 0 to 0.44 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 10% cold worked \|\| 0 to 0.32 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 20% cold worked \|\| 0 to 0.22 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 30% cold worked \|\| 0 to 0.51 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 40% cold worked \|\| 0 to 0.22 mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 50% cold worked \|\| 0 to 7.8x10^-³ mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 60% cold worked \|\| 0 to 5x10^-³ mm/mm strain SSC : effect of cold work \|\| tested at 20 °C (68 °F), 0.0064/s, 70% cold worked \|\| 0 to 6.1x10^-³ mm/mm strain SSCC : with carbides \|\| tested at 1080 °C (1976 °F), 0.05/s \|\| 0 to 0.81 mm/mm strain SSCC : with carbides \|\| tested at 1080 °C (1976 °F), 0.5/s \|\| 0 to 0.8 mm/mm strain SSCC : with carbides \|\| tested at 1080 °C (1976 °F), 5/s \|\| 0 to 0.73 mm/mm strain SSCC : without carbides \|\| tested at 1080 °C (1976 °F), 0.05/s \|\| 0 to 0.77 mm/mm strain SSCC : without carbides \|\| tested at 1120 °C (2048 °F), 0.05/s \|\| 0 to 0.69 mm/mm strain SSCC : without carbides \|\| tested at 1080 °C (1976 °F), 0.5/s \|\| 0 to 0.77 mm/mm strain SSCC : without carbides \|\| tested at 1120 °C (2048 °F), 0.5/s \|\| 0 to 0.78 mm/mm strain SSCC : without carbides \|\| tested at 1080 °C (1976 °F), 5/s \|\| 0 to 0.74 mm/mm strain SSCC : without carbides \|\| tested at 1120 °C (2048 °F), 5/s \|\| 0 to 0.72 mm/mm strain UTS : solution annealed & age-hardened sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solution annealed & age-hardened plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 60% cold worked \|\| room temperature value UTS* : annealed, effect of cold work on RT value \|\| annealed, 70% cold worked \|\| room temperature value YS : solution annealed & age-hardened sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : solution annealed & age-hardened plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 60% cold worked \|\| room temperature value YS* : annealed, effect of cold work on RT value \|\| annealed, 70% cold worked \|\| room temperature value %El : solution annealed & age-hardened sheet \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : solution annealed & age-hardened plate \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El* : annealed, effect of cold work on RT value \|\| annealed, 0% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 10% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 20% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 30% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 40% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 50% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 60% cold worked \|\| room temperature value %El* : annealed, effect of cold work on RT value \|\| annealed, 70% cold worked \|\| room temperature value SR : age hardened plate \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : age hardened plate \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : age hardened plate \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : age hardened plate \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : age hardened plate \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : age hardened plate \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) FEN : sheet \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 2x10³ cycles to 1x10⁵ cycles FEN : sheet \|\| tested at 760 °C (1400 °F), R = -1, total strain range \|\| 1.5x10³ cycles to 2.5x10⁵ cycles FEN : sheet \|\| tested at 816 °C (1500 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁵ cycles FEN : sheet \|\| tested at 871 °C (1600 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁵ cycles CRS : 0.5% plastic strain, age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 0.5% plastic strain, age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) CRS : 1% plastic strain, age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 100,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 300,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, age hardened sheet \|\| 1,000,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 100,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 300,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, age hardened sheet \|\| 1,000,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 100,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 300,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, age hardened sheet \|\| 1,000,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 100,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 300,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, age hardened sheet \|\| 1,000,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 100,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, age hardened sheet \|\| 300,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 0.1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, age hardened sheet \|\| 30,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 0.1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, age hardened sheet \|\| 10,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 0.1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, age hardened sheet \|\| 3,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 0.1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 1 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 10 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 30 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 100 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 300 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, age hardened sheet \|\| 1,000 h, solution annealed & rapid cooled plate & bar \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes HR-120 (UNS N08120) (WNr 2.4854)	D : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) CTE : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TD : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SH : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : solution annealed \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solution annealed \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solution annealed \|\| 20 °C to 1095 °C (68 °F to 2003 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Haynes HR-160 (UNS N12160) (WNr 2.4880)	D : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) CTE : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solid \|\| 20 °C to 980 °C (68 °F to 1796 °F) TC : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) TD : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SH : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) UTS : solid \|\| solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) UTS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) YS : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| solution annealed sheet \|\| 20 °C to 1204 °C (68 °F to 2200 °F) %El : solid \|\| hot-rolled & solution annealed plate \|\| 20 °C to 1204 °C (68 °F to 2200 °F) SR : solution annealed & rapidly cooled plate \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁵ h SR : solution annealed & rapidly cooled plate \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1x10⁴ h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| Master curve (LMP) \|\| 593 °C to 983 °C (1099 °F to 1801 °F) RHO : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F) SIGMA : solid \|\| 20 °C to 1200 °C (68 °F to 2192 °F)
Haynes HR-224	D : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) DLL : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) MTE : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TD : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SH : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : solution heat-treated \|\| sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution heat-treated \|\| plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution heat-treated \|\| bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value UTS* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value YS : solution heat-treated \|\| sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution heat-treated \|\| plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution heat-treated \|\| bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value YS* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value %El : solution heat-treated \|\| sheet \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution heat-treated \|\| plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution heat-treated \|\| bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El* : effect of cold work on RT value \|\| 0% cold worked \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1038 °C (1900 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 10% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 20% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 30% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 40% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value %El* : effect of cold work on RT value \|\| 50% cold worked, annealed at 1093 °C (2000 °F) for 5 minutes \|\| room temperature value SR : solution heat-treated \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h SR : solution heat-treated \|\| Master curve (LMP) \|\| 649 °C to 1094 °C (1200 °F to 2001 °F) CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h CRS : 0.1% plastic strain, solution heat-treated \|\| Master curve (LMP) \|\| 649 °C to 1094 °C (1200 °F to 2001 °F) CRS : 1% plastic strain, solution heat-treated \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 1038 °C (1900 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| tested at 1093 °C (2000 °F) \|\| 10 h to 1x10⁴ h CRS : 1% plastic strain, solution heat-treated \|\| Master curve (LMP) \|\| 649 °C to 1094 °C (1200 °F to 2001 °F) IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1038 °C (1900 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain, solution heat-treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain RHO : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes HR-235 (UNS N06235) (ASTM B166/B167/B168/B619/B626)	D : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solution heat-treated \|\| 20 °C to 900 °C (68 °F to 1652 °F) TC : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SH : solution heat-treated \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solution annealed plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : welds \|\| GTAW welded sheet, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : welds \|\| GTAW welded plate, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : welds \|\| weld metal from GTAW \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : solution annealed plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : welds \|\| GTAW welded sheet, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : welds \|\| GTAW welded plate, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : welds \|\| weld metal from GTAW \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : solution annealed plate \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : welds \|\| GTAW welded sheet, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : welds \|\| GTAW welded plate, transverse \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : welds \|\| weld metal from GTAW \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SR : solution annealed & rapidly cooled plate \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : solution annealed & rapidly cooled plate \|\| Master curve (LMP) \|\| 537 °C to 927 °C (998 °F to 1700 °F) CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, solution annealed & rapidly cooled plate \|\| Master curve (LMP) \|\| 537 °C to 927 °C (998 °F to 1700 °F) RHO : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F) SIGMA : solution heat-treated \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Haynes R-41 (Rene 41) (UNS N07041) (WNr 2.4973) (AISI 683) (AMS 5545/5712/5800) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) DLL : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) MTE : solid \|\| -273 °C to 1093 °C (-460 °F to 2000 °F) E : solid \|\| -196 °C to 1000 °C (-321 °F to 1832 °F) G : solid \|\| -196 °C to 732 °C (-321 °F to 1349 °F) v : solid \|\| -196 °C to 732 °C (-321 °F to 1349 °F) K : solid \|\| -196 °C to 732 °C (-321 °F to 1349 °F) TC : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 1210 °C (68 °F to 2210 °F) SSC : annealed \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : annealed \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : annealed \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : annealed \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain UTS : sheet \|\| mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) UTS : sheet \|\| solution treated at 1066 °C (1950 °F) & aged \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS : sheet \|\| solution treated at 1079 °C (1975 °F) & aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : sheet \|\| solution treated at 1121 °C (2050 °F) & aged \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : bar \|\| solution treated at 1079 °C (1975 °F) \|\| -253 °C to 20 °C (-424 °F to 68 °F) YS : sheet \|\| mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) YS : sheet \|\| solution treated at 1066 °C (1950 °F) & aged \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS : sheet \|\| solution treated at 1079 °C (1975 °F) & aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : sheet \|\| solution treated at 1121 °C (2050 °F) & aged \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : bar \|\| solution treated at 1079 °C (1975 °F) \|\| -253 °C to 20 °C (-424 °F to 68 °F) YSC : sheet \|\| solution treated at 1079 °C (1975 °F) & aged, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : sheet \|\| solution treated at 1079 °C (1975 °F) & aged, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : plate, bar, and forgings \|\| solution treated at 1079 °C (1975 °F) & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : sheet \|\| mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) %El : sheet \|\| solution treated at 1066 °C (1950 °F) & aged \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El : sheet \|\| solution treated at 1121 °C (2050 °F) & aged \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : bar \|\| solution treated at 1079 °C (1975 °F) & aged \|\| -253 °C to 20 °C (-424 °F to 68 °F) SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 760 °C (1400 °F) \|\| 5 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 871 °C (1600 °F) \|\| 9.5 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 982 °C (1800 °F) \|\| 3 h to 100 h SR : age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| Master curve (LMP) \|\| 648 °C to 983 °C (1198 °F to 1801 °F) SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| tested at 649 °C (1200 °F) \|\| 4 h to 100 h SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| tested at 704 °C (1300 °F) \|\| 28 h to 95 h SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| tested at 760 °C (1400 °F) \|\| 7.5 h to 18 h SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| tested at 871 °C (1600 °F) \|\| 5 h to 30 h SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| tested at 982 °C (1800 °F) \|\| 6.5 h to 120 h SR : age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) \|\| Master curve (LMP) \|\| 648 °C to 983 °C (1198 °F to 1801 °F) FEN : sheet \|\| tested at 816 °C (1500 °F), R = -1, total strain range \|\| 1x10³ cycles to 1x10⁵ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 427 °C (800 °F), R = 0.6, axial, maximum stress \|\| 3x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F), R = 0.6, axial, maximum stress \|\| 2x10⁵ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F), R = 0.6, axial, maximum stress \|\| 1.8x10⁵ cycles to 2.3x10⁶ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 1.2x10³ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 204 °C (400 °F), R = 0.2, axial, maximum stress \|\| 1.8x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 316 °C (600 °F), R = 0.2, axial, maximum stress \|\| 1.6x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 427 °C (800 °F), R = 0.2, axial, maximum stress \|\| 3.3x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 538 °C (1000 °F), R = 0.2, axial, maximum stress \|\| 1.4x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F), R = 0.2, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 760 °C (1400 °F), R = 0.2, axial, maximum stress \|\| 4x10³ cycles to 1x10⁶ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 871 °C (1600 °F), R = 0.2, axial, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 982 °C (1800 °F), R = 0.2, axial, maximum stress \|\| 2.3x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 20 °C (68 °F), R = 0.01, axial, maximum stress \|\| 5x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 316 °C (600 °F), R = 0.01, axial, maximum stress \|\| 1x10⁴ cycles to 1.2x10⁶ cycles FSN : AMS 5545, 1.02 mm (0.04 inch) sheet \|\| tested at 538 °C (1000 °F), R = 0.01, axial, maximum stress \|\| 2.5x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 20 °C (68 °F), R = 0.6, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 427 °C (800 °F), R = 0.6, axial, maximum stress \|\| 1x10³ cycles to 1.2x10⁷ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 871 °C (1600 °F), R = 0.6, axial, maximum stress \|\| 3.2x10³ cycles to 2.2x10⁵ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 7.3x10³ cycles to 1x10⁷ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 427 °C (800 °F), R = 0.2, axial, maximum stress \|\| 8.6x10³ cycles to 5x10⁵ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 649 °C (1200 °F), R = 0.2, axial, maximum stress \|\| 4.6x10³ cycles to 2.6x10⁴ cycles FSN : AMS 5545, 2.03 mm (0.08 inch) sheet \|\| tested at 871 °C (1600 °F), R = 0.2, axial, maximum stress \|\| 7.7x10³ cycles to 9x10⁵ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = 0.2, axial, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁷ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 204 °C (400 °F), R = 0.2, axial, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 427 °C (800 °F), R = 0.2, axial, maximum stress \|\| 3.3x10⁴ cycles to 2.2x10⁶ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 649 °C (1200 °F), R = 0.2, axial, maximum stress \|\| 7.4x10⁴ cycles to 4.3x10⁶ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 871 °C (1600 °F), R = 0.2, axial, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁶ cycles FSN : AMS 5713, 25.4 mm (1 inch) bar \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10⁴ cycles to 1.4x10⁶ cycles CRS : 0.5% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,500 h CRS : 0.5% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 843 °C (1550 °F) \|\| 95 h to 420 h CRS : 0.5% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 927 °C (1700 °F) \|\| 45 h to 165 h CRS : 0.5% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 1010 °C (1850 °F) \|\| 40 h to 200 h CRS : 0.5% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 1093 °C (2000 °F) \|\| 5 h to 85 h CRS : 1% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 843 °C (1550 °F) \|\| 150 h to 950 h CRS : 1% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 927 °C (1700 °F) \|\| 100 h to 350 h CRS : 1% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 1010 °C (1850 °F) \|\| 75 h to 350 h CRS : 1% plastic strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) \|\| tested at 1093 °C (2000 °F) \|\| 15 h to 250 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) \|\| Master curve (LMP) \|\| 648 °C to 927 °C (1198 °F to 1700 °F) IC : tested at 843 °C (1550 °F), plastic strain \|\| 150 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain \|\| 250 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain \|\| 150 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain \|\| 75 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain \|\| 150 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1010 °C (1850 °F), plastic strain \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 1093 °C (2000 °F), plastic strain \|\| 75 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F)

IN-100 (UNS N13100) (AMS 5397) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 18 °C to 1197 °C (64 °F to 2186 °F) TD : solid \|\| 18 °C to 1197 °C (64 °F to 2186 °F) SH : solid \|\| 18 °C to 1197 °C (64 °F to 2186 °F) SSCC : 0.003/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.393 mm/mm strain SSCC : 0.003/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.248 mm/mm strain SSCC : 0.003/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.3 mm/mm strain SSCC : 0.003/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.003/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.01/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.392 mm/mm strain SSCC : 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.352 mm/mm strain SSCC : 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.01/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.394 mm/mm strain SSCC : 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 0.1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 1/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.24 mm/mm strain SSCC : 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.295 mm/mm strain SSCC : 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 1/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 10/s \|\| tested at 900 °C (1652 °F) \|\| 0 to 0.288 mm/mm strain SSCC : 10/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 10/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.35 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.4 mm/mm strain SSCC : 10/s \|\| tested at 1200 °C (2192 °F) \|\| 0 to 0.4 mm/mm strain UTS : as-cast \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : as-cast \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : as-cast \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1,000 h SR : as-cast \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : as-cast \|\| tested at 927 °C (1700 °F) \|\| 10 h to 1,000 h SR : as-cast \|\| tested at 982 °C (1800 °F) \|\| 10 h to 1,000 h SR : as-cast \|\| tested at 1038 °C (1900 °F) \|\| 100 h to 1,000 h SR : as-cast \|\| Master curve (LMP) \|\| 732 °C to 1038 °C (1349 °F to 1900 °F) FEN : super-plastically forged \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 0.5 cycles to 500 cycles FEN : GATORIZED, forged, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range \|\| 410 cycles to 2.8x10⁵ cycles FEN : GATORIZED, forged, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range \|\| 280 cycles to 2.5x10³ cycles FSN : subsolvus powder processed pancake forging \|\| tested at 650 °C (1202 °F), R = 0.05, axial, maximum stress \|\| 4.8x10³ cycles to 5x10⁵ cycles FSN : subsolvus powder processed pancake forging \|\| tested at 650 °C (1202 °F), R = 0.05, axial, 6 s at peak load, maximum stress \|\| 2x10³ cycles to 5x10⁴ cycles CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 732 °C (1350 °F) \|\| 1 h to 25 h CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 2 h to 50 h CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 0.4 h to 80 h CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 982 °C (1800 °F) \|\| 1 h to 75 h CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 1038 °C (1900 °F) \|\| 2.7 h to 8 h CRS : 0.1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| Master curve (LMP) \|\| 732 °C to 1038 °C (1349 °F to 1900 °F) CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 732 °C (1350 °F) \|\| 2 h to 175 h CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 170 h CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 1 h to 200 h CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 982 °C (1800 °F) \|\| 7 h to 200 h CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 1038 °C (1900 °F) \|\| 6 h to 20 h CRS : 0.2% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| Master curve (LMP) \|\| 732 °C to 1038 °C (1349 °F to 1900 °F) CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 732 °C (1350 °F) \|\| 8 h to 500 h CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 2 h to 400 h CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 3 h to 1,000 h CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 982 °C (1800 °F) \|\| 16 h to 750 h CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 1038 °C (1900 °F) \|\| 25 h to 90 h CRS : 0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| Master curve (LMP) \|\| 732 °C to 1038 °C (1349 °F to 1900 °F) CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 732 °C (1350 °F) \|\| 26 h to 800 h CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 5 h to 560 h CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 5 h to 1,800 h CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 982 °C (1800 °F) \|\| 25 h to 1,400 h CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| tested at 1038 °C (1900 °F) \|\| 58 h to 270 h CRS : 1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| Master curve (LMP) \|\| 732 °C to 1038 °C (1349 °F to 1900 °F) CRS : 0.1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 0.1 h to 8 h CRS : 0.1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 5 h to 60 h CRS : 0.1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| Master curve (LMP) \|\| 815 °C to 983 °C (1499 °F to 1801 °F) CRS : 0.2% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 0.15 h to 40 h CRS : 0.2% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 15 h to 120 h CRS : 0.2% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| Master curve (LMP) \|\| 815 °C to 983 °C (1499 °F to 1801 °F) CRS : 0.5% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 0.4 h to 170 h CRS : 0.5% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 45 h to 260 h CRS : 0.5% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| Master curve (LMP) \|\| 815 °C to 983 °C (1499 °F to 1801 °F) CRS : 1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 816 °C (1500 °F) \|\| 1.85 h to 340 h CRS : 1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| tested at 927 °C (1700 °F) \|\| 79 h to 480 h CRS : 1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| Master curve (LMP) \|\| 815 °C to 983 °C (1499 °F to 1801 °F) IC : tested at 732 °C (1350 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 3 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material \|\| 100 h \|\| 0 to 0.01 mm/mm strain RHO* : solid \|\| room temperature value SIGMA*: solid \|\| room temperature value
IN-162	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F)
IN-738	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) G : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) v : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) K : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : cast material, solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : cast material, solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : cast material, solution annealed & aged \|\| 649 °C to 982 °C (1200 °F to 1800 °F) SR : solution annealed & aged \|\| tested at 732 °C (1350 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged \|\| Master curve (LMP) \|\| 732 °C to 983 °C (1349 °F to 1801 °F) FEN : cast \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain range \|\| 14 cycles to 3.8x10⁴ cycles FEN : cast \|\| tested at 850 °C (1562 °F), R = -1, axial, plastic strain range \|\| 14 cycles to 3.8x10⁴ cycles CRS : 0.1% plastic strain, solution annealed & treated \|\| tested at 732 °C (1350 °F) \|\| 10 h to 90 h CRS : 0.1% plastic strain, solution annealed & treated \|\| tested at 816 °C (1500 °F) \|\| 12 h to 130 h CRS : 0.1% plastic strain, solution annealed & treated \|\| tested at 927 °C (1700 °F) \|\| 38 h to 400 h CRS : 0.1% plastic strain, solution annealed & treated \|\| Master curve (LMP) \|\| 731 °C to 927 °C (1348 °F to 1700 °F) CRS : 0.2% plastic strain, solution annealed & treated \|\| tested at 732 °C (1350 °F) \|\| 20 h to 250 h CRS : 0.2% plastic strain, solution annealed & treated \|\| tested at 816 °C (1500 °F) \|\| 24 h to 290 h CRS : 0.2% plastic strain, solution annealed & treated \|\| tested at 927 °C (1700 °F) \|\| 80 h to 760 h CRS : 0.2% plastic strain, solution annealed & treated \|\| Master curve (LMP) \|\| 731 °C to 927 °C (1348 °F to 1700 °F) CRS : 0.5% plastic strain, solution annealed & treated \|\| tested at 732 °C (1350 °F) \|\| 75 h to 810 h CRS : 0.5% plastic strain, solution annealed & treated \|\| tested at 816 °C (1500 °F) \|\| 110 h to 680 h CRS : 0.5% plastic strain, solution annealed & treated \|\| tested at 927 °C (1700 °F) \|\| 200 h to 2,160 h CRS : 0.5% plastic strain, solution annealed & treated \|\| Master curve (LMP) \|\| 731 °C to 927 °C (1348 °F to 1700 °F) CRS : 1% plastic strain, solution annealed & treated \|\| tested at 732 °C (1350 °F) \|\| 235 h to 1,900 h CRS : 1% plastic strain, solution annealed & treated \|\| tested at 816 °C (1500 °F) \|\| 315 h to 1,200 h CRS : 1% plastic strain, solution annealed & treated \|\| tested at 927 °C (1700 °F) \|\| 375 h to 3,100 h CRS : 1% plastic strain, solution annealed & treated \|\| Master curve (LMP) \|\| 731 °C to 927 °C (1348 °F to 1700 °F) IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & treated \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & treated \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & treated \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 0.1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 0.2 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 0.3 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 0.4 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & treated \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 0.1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 0.2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 0.4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & treated \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 0.2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 0.4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 20,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & treated \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 0.2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 0.4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 2,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, solution annealed & treated \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 0.2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 0.3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 0.4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 0.5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 2 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 3 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 4 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 5 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 20 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 200 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain Vis : liquid \|\| 1375 °C to 1600 °C (2507 °F to 2912 °F)
IN-738LC	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) G : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) v : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) K : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) TD : solid \|\| aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| aged \|\| 20 °C to 1093 °C (68 °F to 2000 °F) SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, as-built \|\| 0 to 0.157 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, HIPed at 1000 °C (1832 °F), STA \|\| 0 to 0.38 mm/mm strain SSC : laser powder bed fusion \|\| tested at 20 °C (68 °F), 0.001/s, HIPed at 1210 °C (2210 °F), STA \|\| 0 to 0.13 mm/mm strain UTS : HIPed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : HIPed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : HIPed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : solution annealed & aged \|\| tested at 732 °C (1350 °F) \|\| 1x10³ h to 1x10⁴ h SR : solution annealed & aged \|\| tested at 816 °C (1500 °F) \|\| 1x10³ h to 1x10⁴ h SR : solution annealed & aged \|\| tested at 927 °C (1700 °F) \|\| 1x10³ h to 1x10⁴ h SR : solution annealed & aged \|\| tested at 982 °C (1800 °F) \|\| 1x10³ h to 1x10⁴ h SR : solution annealed & aged \|\| Master curve (LMP) \|\| 732 °C to 983 °C (1349 °F to 1801 °F) FEN : HIPed & aged \|\| tested at 427 °C (800 °F), R = -1, axial, total strain range \|\| 210 cycles to 5.76x10³ cycles FEN : HIPed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, total strain range \|\| 860 cycles to 6.15x10³ cycles FEN : HIPed & aged \|\| tested at 871 °C (1600 °F), R = -1, axial, total strain range \|\| 140 cycles to 3.87x10³ cycles CRS : 1% plastic strain, as-cast \|\| tested at 750 °C (1382 °F) \|\| 16 h to 320 h CRS : 1% plastic strain, as-cast \|\| tested at 800 °C (1472 °F) \|\| 400 h to 900 h CRS : 1% plastic strain, as-cast \|\| tested at 850 °C (1562 °F) \|\| 40 h to 1,300 h CRS : 1% plastic strain, as-cast \|\| tested at 900 °C (1652 °F) \|\| 50 h to 3,400 h CRS : 1% plastic strain, as-cast \|\| tested at 950 °C (1742 °F) \|\| 120 h to 1,400 h CRS : 1% plastic strain, as-cast \|\| tested at 1000 °C (1832 °F) \|\| 190 h to 700 h CRS : 1% plastic strain, as-cast \|\| Master curve (LMP) \|\| 750 °C to 1001 °C (1382 °F to 1834 °F) Vis : liquid \|\| 1375 °C to 1600 °C (2507 °F to 2912 °F)
IN-792	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)
IN-792 5A	D : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) DLL : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) MTE : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) SR : solution annealed & aged \|\| tested at 750 °C (1382 °F) \|\| 900 h to 1,100 h SR : solution annealed & aged \|\| tested at 775 °C (1427 °F) \|\| 400 h to 3,200 h SR : solution annealed & aged \|\| tested at 800 °C (1472 °F) \|\| 550 h to 6,500 h SR : solution annealed & aged \|\| tested at 825 °C (1517 °F) \|\| 1,100 h to 2,500 h SR : solution annealed & aged \|\| tested at 850 °C (1562 °F) \|\| 400 h to 5,000 h SR : solution annealed & aged \|\| tested at 875 °C (1607 °F) \|\| 60 h to 2,200 h SR : solution annealed & aged \|\| tested at 900 °C (1652 °F) \|\| 70 h to 3,000 h SR : solution annealed & aged \|\| tested at 925 °C (1697 °F) \|\| 80 h to 2,000 h SR : solution annealed & aged \|\| tested at 950 °C (1742 °F) \|\| 30 h to 7,700 h SR : solution annealed & aged \|\| tested at 975 °C (1787 °F) \|\| 40 h to 2,100 h SR : solution annealed & aged \|\| Master curve (LMP) \|\| 750 °C to 976 °C (1382 °F to 1789 °F) CRS : 1% plastic strain, solution annealed & aged \|\| tested at 750 °C (1382 °F) \|\| 160 h to 260 h CRS : 1% plastic strain, solution annealed & aged \|\| tested at 800 °C (1472 °F) \|\| 150 h to 3,100 h CRS : 1% plastic strain, solution annealed & aged \|\| tested at 850 °C (1562 °F) \|\| 40 h to 2,900 h CRS : 1% plastic strain, solution annealed & aged \|\| tested at 900 °C (1652 °F) \|\| 100 h to 2,600 h CRS : 1% plastic strain, solution annealed & aged \|\| tested at 950 °C (1742 °F) \|\| 120 h to 5,700 h CRS : 1% plastic strain, solution annealed & aged \|\| Master curve (LMP) \|\| 750 °C to 951 °C (1382 °F to 1744 °F)
IN-939	D : solid \|\| as manufactured \|\| 20 °C to 900 °C (68 °F to 1652 °F) D : solid \|\| heat treated \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| as manufactured \|\| 20 °C to 900 °C (68 °F to 1652 °F) DLL : solid \|\| heat treated \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| as manufactured \|\| 20 °C to 900 °C (68 °F to 1652 °F) MTE : solid \|\| heat treated \|\| 20 °C to 900 °C (68 °F to 1652 °F) SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 0.5 mm (0.0197 inch) thick, 90 degree build angle \|\| 0 to 0.8 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 1 mm (0.0394 inch) thick, 90 degree build angle \|\| 0 to 0.1 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 2 mm (0.0787 inch) thick, 90 degree build angle \|\| 0 to 0.12 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 7 mm (0.276 inch) thick, 90 degree build angle \|\| 0 to 0.1 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 0.5 mm (0.0197 inch) thick, 45 degree build angle \|\| 0 to 0.6 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 1 mm (0.0394 inch) thick, 45 degree build angle \|\| 0 to 0.72 mm/mm strain SSC : laser powder bed fusion, 2.8x10^-⁴/s \|\| tested at 20 °C (68 °F), 2 mm (0.0787 inch) thick, 45 degree build angle \|\| 0 to 0.72 mm/mm strain SSCC : annealed & air cooled, 0.001/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.001/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.001/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.01/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.01/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.01/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.77 mm/mm strain SSCC : annealed & air cooled, 0.1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 0.1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 0.1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 1/s \|\| tested at 1000 °C (1832 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 1/s \|\| tested at 1050 °C (1922 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.74 mm/mm strain SSCC : annealed & air cooled, 1/s \|\| tested at 1150 °C (2102 °F) \|\| 0 to 0.74 mm/mm strain UTS : solution annealed & aged, cast \|\| 20 °C to 927 °C (68 °F to 1700 °F) UTS* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 90 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 90 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 90 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 45 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 45 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 45 degree build angle \|\| room temperature value UTS* : laser powder bed fusion \|\| 7 mm (0.276 inch) thick, 90 degree build angle \|\| room temperature value YS : solution annealed & aged, cast \|\| 20 °C to 927 °C (68 °F to 1700 °F) YS* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 90 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 90 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 90 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 45 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 45 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 45 degree build angle \|\| room temperature value YS* : laser powder bed fusion \|\| 7 mm (0.276 inch) thick, 90 degree build angle \|\| room temperature value %El : solution annealed & aged, cast \|\| 20 °C to 927 °C (68 °F to 1700 °F) %El* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 90 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 90 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 90 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 0.5 mm (0.0197 inch) thick, 45 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 1 mm (0.0394 inch) thick, 45 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 2 mm (0.0787 inch) thick, 45 degree build angle \|\| room temperature value %El* : laser powder bed fusion \|\| 7 mm (0.276 inch) thick, 90 degree build angle \|\| room temperature value SR : heat-treated & air cooled, cast \|\| tested at 700 °C (1292 °F) \|\| 80 h to 1x10⁴ h SR : heat-treated & air cooled, cast \|\| tested at 760 °C (1400 °F) \|\| 50 h to 7,000 h SR : heat-treated & air cooled, cast \|\| tested at 816 °C (1500 °F) \|\| 50 h to 1x10⁴ h SR : heat-treated & air cooled, cast \|\| tested at 871 °C (1600 °F) \|\| 50 h to 1x10⁴ h SR : heat-treated & air cooled, cast \|\| tested at 927 °C (1700 °F) \|\| 50 h to 1x10⁴ h SR : heat-treated & air cooled, cast \|\| Master curve (LMP) \|\| 700 °C to 927 °C (1292 °F to 1700 °F) FEN : heat treated, vertical \|\| tested at 25 °C (77 °F), R = -1, axial, total strain range \|\| 8.5x10³ cycles to 4x10⁴ cycles FEN : heat treated, vertical \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain range \|\| 2.9x10³ cycles to 4.5x10⁴ cycles FEN : heat treated, vertical \|\| tested at 750 °C (1382 °F), R = -1, axial, total strain range \|\| 1.5x10³ cycles to 3.5x10⁴ cycles FEN : heat treated, vertical \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain range \|\| 1.7x10³ cycles to 2.8x10⁴ cycles FEN : heat treated, horizontal \|\| tested at 25 °C (77 °F), R = -1, axial, total strain range \|\| 6x10³ cycles to 2.8x10⁴ cycles FEN : heat treated, horizontal \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain range \|\| 1.7x10³ cycles to 6x10³ cycles FEN : heat treated, horizontal \|\| tested at 750 °C (1382 °F), R = -1, axial, total strain range \|\| 260 cycles to 1.3x10⁴ cycles FEN : heat treated, horizontal \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain range \|\| 310 cycles to 1.4x10⁴ cycles Vis : liquid \|\| 1375 °C to 1500 °C (2507 °F to 2732 °F)

TMS-26	D* : solid \|\| room temperature value E : solid \|\| <100> \|\| 20 °C to 1000 °C (68 °F to 1832 °F) E : solid \|\| <001> \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
TMS-138A	D* : solid \|\| room temperature value SSC : solution treated & aged (1140 °C (2084 °F) 2 h, 870 °C (1598 °F) 16 h) \|\| tested at 750 °C (1382 °F), 1x10^-⁶/s, [001] \|\| 0 to 0.92 mm/mm strain SSC : solution treated & aged (1140 °C (2084 °F) 2 h, 870 °C (1598 °F) 16 h) \|\| tested at 750 °C (1382 °F), 1x10^-⁴/s, [001] \|\| 0 to 0.78 mm/mm strain
TMW-4M3	SSCC : 5x10^-⁴/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 1 mm/mm strain SSCC : 0.005/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 1 mm/mm strain SSCC : 0.05/s \|\| tested at 950 °C (1742 °F) \|\| 0 to 1 mm/mm strain UTS : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) YS : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) %El : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) SR : solution annealed & aged \|\| tested at 725 °C (1337 °F) \|\| 10 h to 870 h FEN : solution annealed & aged \|\| tested at 400 °C (752 °F), R = 0, axial, total strain range \|\| 5.6x10³ cycles to 5.6x10⁴ cycles FEN : solution annealed & aged \|\| tested at 650 °C (1202 °F), R = 0, axial, total strain range \|\| 1.2x10³ cycles to 5.3x10⁴ cycles FEN : solution annealed & aged \|\| tested at 725 °C (1337 °F), R = 0, axial, total strain range \|\| 800 cycles to 1.8x10⁴ cycles FEN : solution annealed & aged \|\| tested at 400 °C (752 °F), R = 0, axial, plastic strain range \|\| 5.6x10³ cycles to 5.4x10⁴ cycles FEN : solution annealed & aged \|\| tested at 650 °C (1202 °F), R = 0, axial, plastic strain range \|\| 1.2x10³ cycles to 4.4x10⁴ cycles FEN : solution annealed & aged \|\| tested at 725 °C (1337 °F), R = 0, axial, plastic strain range \|\| 900 cycles to 1.3x10⁴ cycles

Udimet 400	D* : solid \|\| room temperature value UTS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) %El : quenched & tempered \|\| 20 °C to 538 °C (68 °F to 1000 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F)
Udimet 500 (UNS N07500) (ASTM B637)	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : aged \|\| tested at 649 °C (1200 °F) \|\| 1 h to 3x10⁴ h SR : aged \|\| tested at 732 °C (1350 °F) \|\| 1 h to 5,400 h SR : aged \|\| tested at 816 °C (1500 °F) \|\| 1 h to 2.4x10⁴ h SR : aged \|\| tested at 899 °C (1650 °F) \|\| 2 h to 2,200 h SR : aged \|\| tested at 982 °C (1800 °F) \|\| 2 h to 2,200 h SR : aged \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) FEN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.0016 cpm, total strain range \|\| 100 cycles to 2x10⁶ cycles FEN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.04 cpm, total strain range \|\| 100 cycles to 2x10⁶ cycles FEN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 1 cpm, total strain range \|\| 100 cycles to 2x10⁶ cycles FEN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 25 cpm, total strain range \|\| 100 cycles to 2x10⁶ cycles FEN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 625 cpm, total strain range \|\| 100 cycles to 2x10⁶ cycles FSN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.0016 cpm, stress amplitude \|\| 10 cycles to 2x10⁶ cycles FSN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 0.04 cpm, stress amplitude \|\| 10 cycles to 2x10⁶ cycles FSN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 1 cpm, stress amplitude \|\| 10 cycles to 2x10⁶ cycles FSN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 25 cpm, stress amplitude \|\| 10 cycles to 2x10⁶ cycles FSN : cast bars \|\| tested at 816 °C (1500 °F), R = -1, axial, 625 cpm, stress amplitude \|\| 10 cycles to 2x10⁶ cycles CRS : 0.1% plastic strain, aged \|\| tested at 649 °C (1200 °F) \|\| 0.8 h to 4,800 h CRS : 0.1% plastic strain, aged \|\| tested at 732 °C (1350 °F) \|\| 0.3 h to 435 h CRS : 0.1% plastic strain, aged \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 3,250 h CRS : 0.1% plastic strain, aged \|\| tested at 899 °C (1650 °F) \|\| 0.2 h to 230 h CRS : 0.1% plastic strain, aged \|\| tested at 982 °C (1800 °F) \|\| 0.3 h to 223 h CRS : 0.1% plastic strain, aged \|\| Master curve (LMP) \|\| 648 °C to 982 °C (1198 °F to 1799 °F) CRS : 0.5% plastic strain, aged \|\| tested at 649 °C (1200 °F) \|\| 0.3 h to 8,000 h CRS : 0.5% plastic strain, aged \|\| tested at 732 °C (1350 °F) \|\| 0.3 h to 2,000 h CRS : 0.5% plastic strain, aged \|\| tested at 816 °C (1500 °F) \|\| 0.1 h to 5,000 h CRS : 0.5% plastic strain, aged \|\| tested at 899 °C (1650 °F) \|\| 0.3 h to 2,000 h CRS : 0.5% plastic strain, aged \|\| tested at 982 °C (1800 °F) \|\| 2 h to 1,000 h CRS : 0.5% plastic strain, aged \|\| Master curve (LMP) \|\| 648 °C to 982 °C (1198 °F to 1799 °F) CRS : 1% plastic strain, aged \|\| tested at 649 °C (1200 °F) \|\| 0.5 h to 1x10⁴ h CRS : 1% plastic strain, aged \|\| tested at 732 °C (1350 °F) \|\| 0.1 h to 2,000 h CRS : 1% plastic strain, aged \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 2,000 h CRS : 1% plastic strain, aged \|\| tested at 899 °C (1650 °F) \|\| 0.5 h to 2,000 h CRS : 1% plastic strain, aged \|\| tested at 982 °C (1800 °F) \|\| 2 h to 1,000 h CRS : 1% plastic strain, aged \|\| Master curve (LMP) \|\| 648 °C to 982 °C (1198 °F to 1799 °F) IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 649 °C (1200 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, aged \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, aged \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, aged \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 899 °C (1650 °F), plastic strain, aged \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 927 °C (1700 °F), plastic strain, aged \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 954 °C (1750 °F), plastic strain, aged \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, aged \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, aged \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, aged \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, aged \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, aged \|\| 100 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F)
Udimet 520	D* : solid \|\| room temperature value UTS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F)
Udimet 630 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value UTS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) YS : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) %El : solution annealed & aged \|\| 20 °C to 760 °C (68 °F to 1400 °F) RHO : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Udimet 700 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solid \|\| 20 °C to 870 °C (68 °F to 1598 °F) TC : solid \|\| 20 °C to 1248 °C (68 °F to 2278 °F) TD : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 1248 °C (68 °F to 2278 °F) UTS : 3-step anneal \|\| bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : 4-step anneal \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : 4-step anneal \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : 3-step anneal \|\| bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) YS : 4-step anneal \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : 4-step anneal \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : 4-step anneal \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : 4-step anneal \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : 3-step anneal \|\| bar \|\| 20 °C to 1093 °C (68 °F to 2000 °F) %El : 4-step anneal \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : 4-step anneal \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : 3-step anneal, bar \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : 3-step anneal, bar \|\| Master curve (LMP) \|\| 704 °C to 983 °C (1299 °F to 1801 °F) SR : 4-step anneal, sheet \|\| tested at 538 °C (1000 °F) \|\| 1 h to 1,000 h SR : 4-step anneal, sheet \|\| tested at 760 °C (1400 °F) \|\| 6 h to 3,000 h SR : 4-step anneal, sheet \|\| tested at 982 °C (1800 °F) \|\| 1 h to 4,100 h SR : 4-step anneal, sheet \|\| Master curve (LMP) \|\| 537 °C to 983 °C (998 °F to 1801 °F) FSN : 4-step anneal, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : 4-step anneal, smooth \|\| tested at 538 °C (1000 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : 4-step anneal, smooth \|\| tested at 760 °C (1400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : 4-step anneal, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : 4-step anneal, notched \|\| tested at 538 °C (1000 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : 4-step anneal, notched \|\| tested at 760 °C (1400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, 4-step anneal, sheet \|\| tested at 538 °C (1000 °F) \|\| 1 h to 460 h CRS : 0.2% plastic strain, 4-step anneal, sheet \|\| tested at 760 °C (1400 °F) \|\| 1 h to 880 h CRS : 0.2% plastic strain, 4-step anneal, sheet \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1,300 h CRS : 0.5% plastic strain, 4-step anneal, sheet \|\| tested at 538 °C (1000 °F) \|\| 1 h to 460 h CRS : 0.5% plastic strain, 4-step anneal, sheet \|\| tested at 760 °C (1400 °F) \|\| 1 h to 880 h CRS : 0.5% plastic strain, 4-step anneal, sheet \|\| tested at 982 °C (1800 °F) \|\| 1 h to 1,300 h IC : tested at 538 °C (1000 °F), plastic strain, 4-step anneal, sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 4-step anneal, sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 4-step anneal, sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 4-step anneal, sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 538 °C (1000 °F), plastic strain, 4-step anneal, sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, 4-step anneal, sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, 4-step anneal, sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, 4-step anneal, sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, 4-step anneal, sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, 4-step anneal, sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, 4-step anneal, sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain RHO : solid \|\| unknown condition \|\| 20 °C to 982 °C (68 °F to 1800 °F) RHO : solid \|\| hot-rolled \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| unknown condition \|\| 20 °C to 982 °C (68 °F to 1800 °F) SIGMA : solid \|\| hot-rolled \|\| -269 °C to 20 °C (-452 °F to 68 °F)
Udimet 710	D : solid \|\| solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solution treated & aged forged bar, in tension \|\| longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) E : solution treated & aged forged bar, in compression \|\| longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| solution treated & aged forged bar \|\| 20 °C to 992 °C (68 °F to 1817 °F) UTS : solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution treated & aged forged bar \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : solution treated & aged forged bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : solution treated & aged forged bar \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) FSN : solution treated & aged forged bar, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged forged bar, smooth \|\| tested at 427 °C (800 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged forged bar, smooth \|\| tested at 649 °C (1200 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged forged bar, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged forged bar, notched \|\| tested at 427 °C (800 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged forged bar, notched \|\| tested at 649 °C (1200 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles
Udimet 720 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 93 °C (68 °F to 199 °F) DLL : solid \|\| 20 °C to 93 °C (68 °F to 199 °F) MTE : solid \|\| 20 °C to 93 °C (68 °F to 199 °F) CTE : solid \|\| 20 °C to 93 °C (68 °F to 199 °F) SH : solid \|\| as-received \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SH : solid \|\| 4 h at 1104 °C (2020 °F)/8 h at 760 °C (1400 °F)/24 h at 649 °C (1200 °F) \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SH : solid \|\| 4 h at 1104 °C (2020 °F)/24 h at 649 °C (1200 °F)/8 h at 760 °C (1400 °F) \|\| -170 °C to 710 °C (-274 °F to 1310 °F) SSCC : 1x10^-⁴/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.54 mm/mm strain SSCC : 0.001/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.56 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.59 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.51 mm/mm strain UTS : precipitation hardened \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : precipitation hardened \|\| 20 °C to 871 °C (68 °F to 1600 °F) FEN : conventionally atomized \|\| tested at 538 °C (1000 °F), R = 0, K_t = 1.0, axial, total strain range \|\| 1.3x10³ cycles to 1.3x10⁵ cycles FEN : HYN atomized \|\| tested at 538 °C (1000 °F), R = 0, K_t = 1.0, axial, total strain range \|\| 800 cycles to 1.2x10⁵ cycles
Udimet 720LI	D* : solid \|\| room temperature value SSC : fully heat-treated \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSC : fully heat-treated \|\| tested at 350 °C (662 °F), 1x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : fully heat-treated \|\| tested at 550 °C (1022 °F), 1x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : fully heat-treated \|\| tested at 650 °C (1202 °F), 1x10^-⁴/s \|\| 0 to 0.12 mm/mm strain UTS : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) YS : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) %El : solution annealed & aged \|\| 20 °C to 750 °C (68 °F to 1382 °F) FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in air, total strain range \|\| 330 cycles to 3x10⁴ cycles FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in vacuum, total strain range \|\| 330 cycles to 2x10⁴ cycles FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in air, plastic strain range \|\| 120 cycles to 8x10³ cycles FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in vacuum, plastic strain range \|\| 330 cycles to 2x10⁴ cycles FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in air, elastic strain range \|\| 120 cycles to 8x10³ cycles FEN : disc sized forging \|\| tested at 700 °C (1292 °F), R = 0, axial, in vacuum, elastic strain range \|\| 330 cycles to 2x10⁴ cycles
Udimet D-979 (UNS N09979) (AISI 664) (SAE J467) (AMS 5509/5746) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) DLL : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) MTE : solid \|\| -273 °C to 871 °C (-460 °F to 1600 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) G : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) v : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) K : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solution annealed & aged \|\| -196 °C to 871 °C (-321 °F to 1600 °F) YS : solution annealed & aged \|\| -196 °C to 871 °C (-321 °F to 1600 °F) %El : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 1 h, oil quench, aged at 843 °C (1550 °F) for 6 h, air cool, re-aged at 704 °C (1300 °F) for 16 h, air cool \|\| Master curve (LMP) \|\| 649 °C to 872 °C (1200 °F to 1601 °F) SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 538 °C (1000 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 593 °C (1100 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : 1038 °C (1900 °F) for 4 h, water quenched, aged at 843 °C (1550 °F) for 12 h, air cooled, re-aged at 704 °C (1300 °F) for 16 h, air cooled \|\| Master curve (LMP) \|\| 537 °C to 816 °C (998 °F to 1501 °F) CRS : 1% plastic strain, solution treated & aged \|\| tested at 593 °C (1100 °F) \|\| 425 h to 4.5x10⁴ h CRS : 1% plastic strain, solution treated & aged \|\| tested at 649 °C (1200 °F) \|\| 125 h to 1.1x10⁴ h CRS : 1% plastic strain, solution treated & aged \|\| tested at 704 °C (1300 °F) \|\| 105 h to 8,100 h CRS : 1% plastic strain, solution treated & aged \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1.65x10⁴ h CRS : 1% plastic strain, solution treated & aged \|\| tested at 816 °C (1500 °F) \|\| 135 h to 1.8x10⁴ h CRS : 1% plastic strain, solution treated & aged \|\| Master curve (LMP) \|\| 593 °C to 816 °C (1099 °F to 1501 °F)

718 Plus (UNS N07818) (AMS 5442)	D : solid \|\| 20 °C to 910 °C (68 °F to 1670 °F) DLL : solid \|\| 20 °C to 910 °C (68 °F to 1670 °F) MTE : solid \|\| 20 °C to 910 °C (68 °F to 1670 °F) E : forged billet \|\| longitudinal direction \|\| 20 °C to 859 °C (68 °F to 1578 °F) E : forged billet \|\| transverse direction \|\| 20 °C to 859 °C (68 °F to 1578 °F) G : forged billet \|\| longitudinal direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) G : forged billet \|\| transverse direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) v : forged billet \|\| longitudinal direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) v : forged billet \|\| transverse direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) K : forged billet \|\| longitudinal direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) K : forged billet \|\| transverse direction \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| 20 °C to 1187 °C (68 °F to 2168 °F) TD : solid \|\| 20 °C to 910 °C (68 °F to 1670 °F) SH : solid \|\| solution treated & aged \|\| 20 °C to 1170 °C (68 °F to 2138 °F) SSC : hot-rolled, solution treated & aged 12.7 mm (0.5 inch) plate \|\| tested at 23 °C (73 °F), 8.3x10^-⁵/s \|\| 0 to 0.188 mm/mm strain SSC : hot-rolled, solution treated & aged 12.7 mm (0.5 inch) plate \|\| tested at 400 °C (752 °F), 8.3x10^-⁵/s \|\| 0 to 0.17 mm/mm strain SSC : hot-rolled, solution treated & aged 12.7 mm (0.5 inch) plate \|\| tested at 650 °C (1202 °F), 8.3x10^-⁵/s \|\| 0 to 0.127 mm/mm strain SSC : hot-rolled, solution treated & aged 12.7 mm (0.5 inch) plate \|\| tested at 704 °C (1300 °F), 8.3x10^-⁵/s \|\| 0 to 0.39 mm/mm strain UTS : hot-rolled, solution treated & aged \|\| aged at 649 °C (1200 °F), 1.02 mm (0.04 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) UTS : hot-rolled, solution treated & aged \|\| aged at 760 °C (1400 °F), 12.7 mm (0.5 inch) plate \|\| 20 °C to 704 °C (68 °F to 1299 °F) YS : hot-rolled, solution treated & aged \|\| aged at 649 °C (1200 °F), 1.02 mm (0.04 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : hot-rolled, solution treated & aged \|\| aged at 760 °C (1400 °F), 12.7 mm (0.5 inch) plate \|\| 20 °C to 704 °C (68 °F to 1299 °F) %El : hot-rolled, solution treated & aged \|\| aged at 649 °C (1200 °F), 1.02 mm (0.04 inch) sheet \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : hot-rolled, solution treated & aged \|\| aged at 760 °C (1400 °F), 12.7 mm (0.5 inch) plate \|\| 20 °C to 704 °C (68 °F to 1299 °F) SR : hot-rolled, solution treated & aged 1.02 mm (0.04 inch) sheet \|\| tested at 649 °C (1200 °F) \|\| 8 h to 70 h FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 1 cycles to 2x10³ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude \|\| 1 cycles to 2x10³ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 1 cycles to 2x10³ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 3.9x10³ cycles to 3.1x10⁴ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 3.1x10³ cycles to 2.65x10⁴ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 4.8x10³ cycles to 8.9x10⁴ cycles FEN : standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.5x10³ cycles to 2.03x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 2.5x10³ cycles to 1.1x10⁵ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 1.9x10³ cycles to 4.1x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 6.3x10³ cycles to 9.8x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.57x10³ cycles to 3.58x10⁴ cycles FEN : 866 °C (1590 °F) for 8 h plus standard heat treatment \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 2.6x10³ cycles to 3.9x10⁴ cycles FEN : 866 °C (1590 °F) for 8 h plus standard heat treatment \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 2.4x10³ cycles to 2.2x10⁴ cycles FEN : 866 °C (1590 °F) for 8 h plus standard heat treatment \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.6x10³ cycles to 8x10⁴ cycles FEN : 866 °C (1590 °F) for 8 h plus standard heat treatment \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.2x10³ cycles to 3.06x10⁴ cycles FEN : overaged \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 3.7x10³ cycles to 5.7x10⁴ cycles FEN : overaged \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 2.4x10³ cycles to 6.2x10⁴ cycles FEN : overaged \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 3.3x10³ cycles to 6.15x10⁴ cycles FEN : overaged \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.47x10³ cycles to 3.3x10⁴ cycles FEN : combination of all 4 heat treatments \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 2.5x10³ cycles to 1.1x10⁵ cycles FEN : combination of all 4 heat treatments \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 1.9x10³ cycles to 6.2x10⁴ cycles FEN : combination of all 4 heat treatments \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.6x10³ cycles to 2.4x10⁵ cycles FEN : combination of all 4 heat treatments \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.2x10³ cycles to 3.6x10⁴ cycles FSN : solution treated & aged \|\| tested at 23 °C (73 °F), R = 0.1, axial, to initiation, maximum stress \|\| 1.8x10⁵ cycles to 5x10⁶ cycles FSN : solution treated & aged \|\| tested at 649 °C (1200 °F), R = 0.1, axial, to initiation, maximum stress \|\| 3.3x10⁵ cycles to 5x10⁶ cycles CRS : 0.2% total strain, solution annealed & treated \|\| tested at 649 °C (1200 °F) \|\| 900 h to 3,200 h CRS : 0.2% total strain, solution annealed & treated \|\| tested at 677 °C (1250 °F) \|\| 100 h to 450 h CRS : 0.2% total strain, solution annealed & treated \|\| tested at 691 °C (1275 °F) \|\| 40 h to 260 h CRS : 0.2% total strain, solution annealed & treated \|\| tested at 704 °C (1300 °F) \|\| 20 h to 160 h CRS : 0.2% total strain, solution annealed & treated \|\| Master curve (LMP) \|\| 649 °C to 705 °C (1200 °F to 1301 °F) CRS : 0.5% total strain, solution annealed & treated \|\| tested at 677 °C (1250 °F) \|\| 200 h to 425 h CRS : 0.5% total strain, solution annealed & treated \|\| tested at 691 °C (1275 °F) \|\| 80 h to 540 h CRS : 0.5% total strain, solution annealed & treated \|\| tested at 704 °C (1300 °F) \|\| 45 h to 320 h CRS : 0.5% total strain, solution annealed & treated \|\| Master curve (LMP) \|\| 676 °C to 705 °C (1249 °F to 1301 °F) CRS : 1% total strain, solution annealed & treated \|\| tested at 677 °C (1250 °F) \|\| 290 h to 605 h CRS : 1% total strain, solution annealed & treated \|\| tested at 691 °C (1275 °F) \|\| 120 h to 720 h CRS : 1% total strain, solution annealed & treated \|\| tested at 704 °C (1300 °F) \|\| 70 h to 450 h CRS : 1% total strain, solution annealed & treated \|\| Master curve (LMP) \|\| 676 °C to 705 °C (1249 °F to 1301 °F) IC : tested at 649 °C (1200 °F), total strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 663 °C (1225 °F), total strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 663 °C (1225 °F), total strain, solution annealed & treated \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 677 °C (1250 °F), total strain, solution annealed & treated \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 691 °C (1275 °F), total strain, solution annealed & treated \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 691 °C (1275 °F), total strain, solution annealed & treated \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 704 °C (1300 °F), total strain, solution annealed & treated \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 704 °C (1300 °F), total strain, solution annealed & treated \|\| 100 h \|\| 0 to 0.01 mm/mm strain
AD730 (ISO/EN/DIN NiCr16Co9Fe4Mo3W3Ti3Al2)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) TC : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) UTS : quenched & tempered \|\| 20 °C to 750 °C (68 °F to 1382 °F) YS : quenched & tempered \|\| 20 °C to 750 °C (68 °F to 1382 °F) %El : quenched & tempered \|\| 20 °C to 750 °C (68 °F to 1382 °F)
AEREX 350 (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : solid \|\| 20 °C to 731 °C (68 °F to 1348 °F) DLL : solid \|\| 20 °C to 731 °C (68 °F to 1348 °F) MTE : solid \|\| 20 °C to 731 °C (68 °F to 1348 °F) CTE : solid \|\| 20 °C to 731 °C (68 °F to 1348 °F) E : solid \|\| 20 °C to 737 °C (68 °F to 1358 °F) G : solid \|\| 20 °C to 737 °C (68 °F to 1358 °F) v : solid \|\| 20 °C to 737 °C (68 °F to 1358 °F) K : solid \|\| 20 °C to 737 °C (68 °F to 1358 °F) TC : solid \|\| -189 °C to 690 °C (-308 °F to 1274 °F) TD : solid \|\| 20 °C to 690 °C (68 °F to 1274 °F) SH : solid \|\| 2 °C to 700 °C (35 °F to 1292 °F) UTS* : cold worked and aged \|\| room temperature value YS* : cold worked and aged \|\| room temperature value %El* : cold worked and aged \|\| room temperature value SR : cold worked & aged \|\| tested at 649 °C (1200 °F) \|\| 5 h to 300 h SR : cold worked & aged \|\| tested at 732 °C (1350 °F) \|\| 20 h to 120 h SR : cold worked & aged \|\| Master curve (LMP) \|\| 649 °C to 733 °C (1200 °F to 1351 °F) RHO : solid \|\| -186 °C to 700 °C (-303 °F to 1292 °F) SIGMA : solid \|\| -186 °C to 700 °C (-303 °F to 1292 °F)
AF955 (UNS N09955)	D* : solid \|\| room temperature value SSC : solution annealed \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : Grade 3 \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.26 mm/mm strain SSC : Grade 3HS \|\| tested at 20 °C (68 °F), 1x10^-⁴/s \|\| 0 to 0.183 mm/mm strain
Alloy 780 (WNr 2.4960) (ISO/EN/DIN NiCr18Co25Nb5Mo3Al2)	D* : solid \|\| room temperature value SSCC : fully recrystallized \|\| tested at 950 °C (1742 °F), 0.001/s \|\| 0 to 0.175 mm/mm strain SSCC : fully recrystallized \|\| tested at 1000 °C (1832 °F), 0.001/s \|\| 0 to 0.175 mm/mm strain SSCC : fully recrystallized \|\| tested at 1050 °C (1922 °F), 0.001/s \|\| 0 to 0.175 mm/mm strain
Astroloy (UNS N13017)	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) UTS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 982 °C (1800 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 983 °C (1200 °F to 1801 °F) FEN : hot isostatically pressed \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 0.5 cycles to 1.5x10³ cycles
B-1900	D : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) DLL : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) MTE : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) CTE : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) TD : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) SH : solid \|\| 20 °C to 1020 °C (68 °F to 1868 °F) UTS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F)
FGH96 / FGH4096	D* : solid \|\| room temperature value E : solid \|\| solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) SSCC : 0.01/s \|\| tested at 1040 °C (1904 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.01/s \|\| tested at 1070 °C (1958 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.01/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.01/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1040 °C (1904 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1070 °C (1958 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 0.1/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 1/s \|\| tested at 1040 °C (1904 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 1/s \|\| tested at 1070 °C (1958 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 1/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 1/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 10/s \|\| tested at 1040 °C (1904 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 10/s \|\| tested at 1070 °C (1958 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 10/s \|\| tested at 1100 °C (2012 °F) \|\| 0 to 0.67 mm/mm strain SSCC : 10/s \|\| tested at 1130 °C (2066 °F) \|\| 0 to 0.67 mm/mm strain FEN : solution annealed & aged \|\| tested at 480 °C (896 °F), R = -1, axial, total strain amplitude \|\| 310 cycles to 5x10⁴ cycles FEN : solution annealed & aged \|\| tested at 650 °C (1202 °F), R = -1, axial, total strain amplitude \|\| 360 cycles to 3.04x10⁴ cycles
LEK94	D* : solid \|\| room temperature value Vis : liquid \|\| 1352 °C to 1587 °C (2465 °F to 2888 °F) ST : liquid \|\| 1284 °C to 1697 °C (2343 °F to 3086 °F)
M-22	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : as-cast \|\| 20 °C to 982 °C (68 °F to 1800 °F)
M252 (UNS N07252) (AISI 689) (AMS 5756/5757) (some datasets are for temperatures below 20 °C)	D : solid \|\| 20 °C to 1274 °C (68 °F to 2325 °F) DLL : solid \|\| 20 °C to 1274 °C (68 °F to 2325 °F) MTE : solid \|\| 20 °C to 1274 °C (68 °F to 2325 °F) CTE : solid \|\| 20 °C to 1274 °C (68 °F to 2325 °F) E : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| annealed \|\| 0 °C to 1154 °C (32 °F to 2109 °F) TD : solid \|\| annealed \|\| 20 °C to 1154 °C (68 °F to 2109 °F) SH : solid \|\| annealed \|\| 20 °C to 1213 °C (68 °F to 2215 °F) UTS : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) SR : solution annealed & aged, bar \|\| tested at 732 °C (1350 °F) \|\| 35 h to 110 h SR : solution annealed & aged, bar \|\| tested at 816 °C (1500 °F) \|\| 4.8 h to 150 h SR : solution annealed & aged, bar \|\| tested at 871 °C (1600 °F) \|\| 8 h to 105 h SR : solution annealed & aged, bar \|\| Master curve (LMP) \|\| 732 °C to 872 °C (1349 °F to 1601 °F) CRS : 0.1% plastic strain, solution annealed & aged bar \|\| tested at 732 °C (1350 °F) \|\| 0.6 h to 27 h CRS : 0.1% plastic strain, solution annealed & aged bar \|\| tested at 816 °C (1500 °F) \|\| 0.2 h to 24 h CRS : 0.1% plastic strain, solution annealed & aged bar \|\| tested at 871 °C (1600 °F) \|\| 0.6 h to 12 h CRS : 0.1% plastic strain, solution annealed & aged bar \|\| Master curve (LMP) \|\| 732 °C to 872 °C (1349 °F to 1601 °F) CRS : 0.3% plastic strain, solution annealed & aged bar \|\| tested at 732 °C (1350 °F) \|\| 1.9 h to 85 h CRS : 0.3% plastic strain, solution annealed & aged bar \|\| tested at 816 °C (1500 °F) \|\| 0.4 h to 95 h CRS : 0.3% plastic strain, solution annealed & aged bar \|\| tested at 871 °C (1600 °F) \|\| 0.1 h to 45 h CRS : 0.3% plastic strain, solution annealed & aged bar \|\| Master curve (LMP) \|\| 732 °C to 872 °C (1349 °F to 1601 °F) CRS : 0.5% plastic strain, solution annealed & aged bar \|\| tested at 732 °C (1350 °F) \|\| 3 h to 105 h CRS : 0.5% plastic strain, solution annealed & aged bar \|\| tested at 816 °C (1500 °F) \|\| 0.5 h to 75 h CRS : 0.5% plastic strain, solution annealed & aged bar \|\| tested at 871 °C (1600 °F) \|\| 0.2 h to 85 h CRS : 0.5% plastic strain, solution annealed & aged bar \|\| Master curve (LMP) \|\| 732 °C to 872 °C (1349 °F to 1601 °F) CRS : 1% plastic strain, solution annealed & aged bar \|\| tested at 732 °C (1350 °F) \|\| 5 h to 105 h CRS : 1% plastic strain, solution annealed & aged bar \|\| tested at 816 °C (1500 °F) \|\| 0.9 h to 80 h CRS : 1% plastic strain, solution annealed & aged bar \|\| tested at 871 °C (1600 °F) \|\| 0.4 h to 85 h CRS : 1% plastic strain, solution annealed & aged bar \|\| Master curve (LMP) \|\| 732 °C to 872 °C (1349 °F to 1601 °F) IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, solution annealed & aged bar \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution annealed & aged bar \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & aged bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & aged bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & aged bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 788 °C (1450 °F), plastic strain, solution annealed & aged bar \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & aged bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & aged bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 816 °C (1500 °F), plastic strain, solution annealed & aged bar \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & aged bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 843 °C (1550 °F), plastic strain, solution annealed & aged bar \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & aged bar \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & aged bar \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 871 °C (1600 °F), plastic strain, solution annealed & aged bar \|\| 10 h \|\| 0 to 0.01 mm/mm strain
MC-102	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution annealed & aged \|\| 20 °C to 982 °C (68 °F to 1800 °F)
MERL 76	D : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : solid \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TD : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : HIPed, solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) YS : HIPed, solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) %El : HIPed, solution annealed & aged \|\| 20 °C to 650 °C (68 °F to 1202 °F) SR : HIPed, solution treated & aged \|\| tested at 649 °C (1200 °F) \|\| 170 h to 1,720 h SR : HIPed, solution treated & aged \|\| tested at 704 °C (1300 °F) \|\| 210 h to 1,100 h SR : HIPed, solution treated & aged \|\| tested at 732 °C (1350 °F) \|\| 10 h to 500 h SR : HIPed, solution treated & aged \|\| tested at 760 °C (1400 °F) \|\| 35 h to 1,400 h SR : HIPed, solution treated & aged \|\| Master curve (LMP) \|\| 648 °C to 760 °C (1198 °F to 1400 °F) FEN : HIPed, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range \|\| 230 cycles to 1.4x10⁵ cycles FEN : HIPed, solution annealed & aged \|\| tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range \|\| 220 cycles to 3x10³ cycles FSN : K_t = 1.0 \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 9x10³ cycles to 3x10⁴ cycles FSN : K_t = 1.0 \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 6x10³ cycles to 2.9x10⁴ cycles FSN : K_t = 1.0 \|\| tested at 635 °C (1175 °F), R = -1, axial, maximum stress \|\| 3.1x10³ cycles to 3x10⁴ cycles FSN : K_t = 2.0 \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 4x10³ cycles to 2x10⁴ cycles FSN : K_t = 2.0 \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 4.9x10³ cycles to 2x10⁴ cycles FSN : K_t = 2.0 \|\| tested at 635 °C (1175 °F), R = -1, axial, maximum stress \|\| 5.7x10³ cycles to 1.9x10⁴ cycles FSN : K_t = 3.0 \|\| tested at 427 °C (800 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 6x10⁴ cycles FSN : K_t = 3.0 \|\| tested at 538 °C (1000 °F), R = -1, axial, maximum stress \|\| 1.7x10⁴ cycles to 5.8x10⁴ cycles FSN : K_t = 3.0 \|\| tested at 635 °C (1175 °F), R = -1, axial, maximum stress \|\| 8.2x10³ cycles to 2.4x10⁴ cycles CRS : 0.1% plastic strain, HIPed, solution treated & aged \|\| tested at 649 °C (1200 °F) \|\| 18 h to 280 h CRS : 0.1% plastic strain, HIPed, solution treated & aged \|\| tested at 732 °C (1350 °F) \|\| 8 h to 460 h CRS : 0.1% plastic strain, HIPed, solution treated & aged \|\| tested at 760 °C (1400 °F) \|\| 10 h to 380 h CRS : 0.2% plastic strain, HIPed, solution treated & aged \|\| tested at 649 °C (1200 °F) \|\| 90 h to 750 h CRS : 0.2% plastic strain, HIPed, solution treated & aged \|\| tested at 732 °C (1350 °F) \|\| 15 h to 850 h CRS : 0.2% plastic strain, HIPed, solution treated & aged \|\| tested at 760 °C (1400 °F) \|\| 35 h to 305 h IC : tested at 649 °C (1200 °F), plastic strain, HIPed, solution treated & aged \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, HIPed, solution treated & aged \|\| 30 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, HIPed, solution treated & aged \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 732 °C (1350 °F), plastic strain, HIPed, solution treated & aged \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, HIPed, solution treated & aged \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, HIPed, solution treated & aged \|\| 300 h \|\| 0 to 2x10^-³ mm/mm strain
Pyromet alloy 860	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : solution annealed & aged \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : solution annealed & aged, bar \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : solution annealed & aged, bar \|\| Master curve (LMP) \|\| 649 °C to 816 °C (1200 °F to 1501 °F)
RGT-4	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F)
RGT-13	D : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) DLL : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) MTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) CTE : solid \|\| 20 °C to 871 °C (68 °F to 1600 °F) TC : solid \|\| 20 °C to 760 °C (68 °F to 1400 °F) UTS : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) YS : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : solution annealed & aged \|\| 20 °C to 871 °C (68 °F to 1600 °F)
RR1000	D* : solid \|\| room temperature value SSCC : as-HIPed billet \|\| tested at 1140 °C (2084 °F), 0.1/s \|\| 0 to 0.95 mm/mm strain SSCC : as-HIPed billet \|\| tested at 1100 °C (2012 °F), 1/s \|\| 0 to 0.91 mm/mm strain SSCC : as-HIPed billet \|\| tested at 1100 °C (2012 °F), 10/s \|\| 0 to 0.9 mm/mm strain UTS : solution treated & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solution treated & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : solution treated & aged \|\| tested at 650 °C (1202 °F) \|\| 70 h to 3.7x10⁷ h SR : solution treated & aged \|\| tested at 700 °C (1292 °F) \|\| 2 h to 1x10⁶ h SR : solution treated & aged \|\| tested at 750 °C (1382 °F) \|\| 0.1 h to 1.8x10⁴ h SR : solution treated & aged \|\| tested at 800 °C (1472 °F) \|\| 0.01 h to 100 h SR : solution treated & aged \|\| Master curve (LMP) \|\| 649 °C to 801 °C (1200 °F to 1474 °F)
SRR99	D* : solid \|\| room temperature value E : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <001> \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <011> \|\| 20 °C to 900 °C (68 °F to 1652 °F) E : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <111> \|\| 20 °C to 900 °C (68 °F to 1652 °F) SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s, <001> \|\| 0 to 0.81 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s, <011> \|\| 0 to 0.167 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s, <111> \|\| 0 to 0.171 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 600 °C (1112 °F), 3.3x10^-⁴/s, <001> \|\| 0 to 0.11 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 600 °C (1112 °F), 3.3x10^-⁴/s, <011> \|\| 0 to 0.12 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 600 °C (1112 °F), 3.3x10^-⁴/s, <111> \|\| 0 to 0.191 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 800 °C (1472 °F), 3.3x10^-⁴/s, <001> \|\| 0 to 0.196 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 800 °C (1472 °F), 3.3x10^-⁴/s, <011> \|\| 0 to 0.152 mm/mm strain SSC : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| tested at 800 °C (1472 °F), 3.3x10^-⁴/s, <111> \|\| 0 to 0.146 mm/mm strain SSC : solution treated & aged (1140 °C (2084 °F) 2 h, 870 °C (1598 °F) 16 h) \|\| tested at 750 °C (1382 °F), 1x10^-⁶/s, [001] \|\| 0 to 0.1 mm/mm strain SSC : solution treated & aged (1140 °C (2084 °F) 2 h, 870 °C (1598 °F) 16 h) \|\| tested at 750 °C (1382 °F), 1x10^-⁴/s, [001] \|\| 0 to 0.18 mm/mm strain YS : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <001> \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <011> \|\| 20 °C to 900 °C (68 °F to 1652 °F) YS : solution treated & aged (1300 °C (2372 °F) 4 h, 1100 °C (2012 °F) 4 h, 870 °C (1598 °F) 16 h) \|\| <111> \|\| 20 °C to 900 °C (68 °F to 1652 °F) FEN : no hold \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 1x10³ cycles to 1.5x10⁴ cycles FEN : held for 300 s at the maximum tensile strain \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 580 cycles to 7.5x10³ cycles FEN : held for 300 s at the maximum compressive strain \|\| tested at 980 °C (1796 °F), R = -1, axial, total strain range \|\| 350 cycles to 1.4x10³ cycles CRS : 2% plastic strain, <111> \|\| tested at 750 °C (1382 °F) \|\| 1.1 h to 9,600 h CRS : 2% plastic strain, <111> \|\| tested at 850 °C (1562 °F) \|\| 0.23 h to 1.1x10⁴ h CRS : 2% plastic strain, <111> \|\| tested at 950 °C (1742 °F) \|\| 0.36 h to 8,400 h CRS : 2% plastic strain, <111> \|\| tested at 1050 °C (1922 °F) \|\| 0.4 h to 1,600 h CRS : 5% plastic strain, <001> \|\| tested at 750 °C (1382 °F) \|\| 0.13 h to 590 h CRS : 5% plastic strain, <001> \|\| tested at 850 °C (1562 °F) \|\| 0.23 h to 240 h CRS : 5% plastic strain, <001> \|\| tested at 900 °C (1652 °F) \|\| 0.4 h to 120 h CRS : 5% plastic strain, <001> \|\| tested at 950 °C (1742 °F) \|\| 0.6 h to 70 h CRS : 5% plastic strain, <001> \|\| tested at 1050 °C (1922 °F) \|\| 0.74 h to 0.85 h
Supertherm	D* : solid \|\| room temperature value E : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F) TC : solid \|\| 20 °C to 1100 °C (68 °F to 2012 °F)
Tribaloy 700	D : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) DLL : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) MTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) CTE : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Unitemp AF2-1 DA (UNS N07012)	D : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) DLL : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) MTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) CTE : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) TC : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution treated & aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) UTS : solution treated & aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution treated & aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) YS : solution treated & aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : solution treated & aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) YSC : solution treated & aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution treated & aged sheet \|\| 0.5 h hold, longitudinal \|\| 20 °C to 982 °C (68 °F to 1800 °F) %El : solution treated & aged sheet \|\| 0.5 h hold, transverse \|\| 20 °C to 982 °C (68 °F to 1800 °F) SR : bar material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : bar material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : bar material \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SR : sheet material \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : sheet material \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) FEN : extruded & annealed \|\| tested at 760 °C (1400 °F), R = 0, axial, total strain range \|\| 280 cycles to 1x10⁵ cycles FSN : solution treated & aged sheet, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged sheet, smooth \|\| tested at 538 °C (1000 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged sheet, smooth \|\| tested at 760 °C (1400 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged sheet, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged sheet, notched \|\| tested at 538 °C (1000 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : solution treated & aged sheet, notched \|\| tested at 760 °C (1400 °F), R = 0.1, axial, K_t = 3, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, solution treated & aged sheet \|\| tested at 538 °C (1000 °F) \|\| 1 h to 1,000 h CRS : 0.2% plastic strain, solution treated & aged sheet \|\| tested at 760 °C (1400 °F) \|\| 4 h to 1,000 h CRS : 0.2% plastic strain, solution treated & aged sheet \|\| tested at 982 °C (1800 °F) \|\| 1 h to 2,200 h CRS : 0.5% plastic strain, solution treated & aged sheet \|\| tested at 760 °C (1400 °F) \|\| 4 h to 1,000 h CRS : 0.5% plastic strain, solution treated & aged sheet \|\| tested at 982 °C (1800 °F) \|\| 1 h to 2,200 h CRS : 0.5% plastic strain, solution treated & aged sheet \|\| Master curve (LMP) \|\| 760 °C to 983 °C (1400 °F to 1801 °F) IC : tested at 760 °C (1400 °F), plastic strain, solution treated & aged sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution treated & aged sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution treated & aged sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution treated & aged sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 760 °C (1400 °F), plastic strain, solution treated & aged sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 1 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 30 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 100 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 300 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 982 °C (1800 °F), plastic strain, solution treated & aged sheet \|\| 1,000 h \|\| 0 to 5x10^-³ mm/mm strain
Waspaloy (UNS N07001) (WNr 2.4654) (ISO/EN/DIN NW7001/NiCr20Co13Mo4Ti3Al) (AISI 685) (AMS 5544/5704/5706/5707/5708/5709/5728/7471) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : AMS 5544 \|\| 20 °C to 1093 °C (68 °F to 2000 °F) DLL : AMS 5544 \|\| 20 °C to 1093 °C (68 °F to 2000 °F) MTE : AMS 5544 \|\| 20 °C to 1093 °C (68 °F to 2000 °F) CTE : AMS 5544 \|\| 20 °C to 1093 °C (68 °F to 2000 °F) E : AMS 5544 \|\| 20 °C to 1000 °C (68 °F to 1832 °F) TC : solid \|\| AMS 5544 \|\| 20 °C to 900 °C (68 °F to 1652 °F) TD : solid \|\| AMS 5544 \|\| 20 °C to 900 °C (68 °F to 1652 °F) SH : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SSC : all forms \|\| tested at 27 °C (80 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : all forms \|\| tested at 427 °C (800 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : all forms \|\| tested at 538 °C (1000 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : all forms \|\| tested at 649 °C (1200 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : all forms \|\| tested at 760 °C (1400 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 950 °C (1742 °F), 5x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 950 °C (1742 °F), 0.005/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 950 °C (1742 °F), 0.083/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 950 °C (1742 °F), 0.38/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1000 °C (1832 °F), 0.083/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1050 °C (1922 °F), 0.093/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1100 °C (2012 °F), 0.0019/s \|\| 0 to 0.75 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1100 °C (2012 °F), 0.0056/s \|\| 0 to 0.75 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1100 °C (2012 °F), 0.093/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1150 °C (2102 °F), 0.093/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed at 1200 °C (2192 °F) \|\| tested at 1220 °C (2228 °F), 0.093/s \|\| 0 to 0.7 mm/mm strain SSCC : solution annealed & aged, 0.01/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.53 mm/mm strain SSCC : solution annealed & aged, 0.01/s \|\| tested at 1010 °C (1850 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed & aged, 0.01/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.59 mm/mm strain SSCC : solution annealed & aged, 0.01/s \|\| tested at 1079 °C (1975 °F) \|\| 0 to 0.6 mm/mm strain SSCC : solution annealed & aged, 0.01/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.6 mm/mm strain SSCC : solution annealed & aged, 0.14/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.55 mm/mm strain SSCC : solution annealed & aged, 0.14/s \|\| tested at 1010 °C (1850 °F) \|\| 0 to 0.58 mm/mm strain SSCC : solution annealed & aged, 0.14/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.62 mm/mm strain SSCC : solution annealed & aged, 0.14/s \|\| tested at 1079 °C (1975 °F) \|\| 0 to 0.62 mm/mm strain SSCC : solution annealed & aged, 0.14/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.61 mm/mm strain SSCC : solution annealed & aged, 1.84/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.54 mm/mm strain SSCC : solution annealed & aged, 1.84/s \|\| tested at 1010 °C (1850 °F) \|\| 0 to 0.56 mm/mm strain SSCC : solution annealed & aged, 1.84/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.57 mm/mm strain SSCC : solution annealed & aged, 1.84/s \|\| tested at 1079 °C (1975 °F) \|\| 0 to 0.57 mm/mm strain SSCC : solution annealed & aged, 1.84/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.6 mm/mm strain SSCC : solution annealed & aged, 25/s \|\| tested at 982 °C (1800 °F) \|\| 0 to 0.46 mm/mm strain SSCC : solution annealed & aged, 25/s \|\| tested at 1010 °C (1850 °F) \|\| 0 to 0.35 mm/mm strain SSCC : solution annealed & aged, 25/s \|\| tested at 1038 °C (1900 °F) \|\| 0 to 0.47 mm/mm strain SSCC : solution annealed & aged, 25/s \|\| tested at 1079 °C (1975 °F) \|\| 0 to 0.55 mm/mm strain SSCC : solution annealed & aged, 25/s \|\| tested at 1149 °C (2100 °F) \|\| 0 to 0.51 mm/mm strain UTS : heat-treated AMS 5544 \|\| 20 °C to 1095 °C (68 °F to 2003 °F) UTS : mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) YS : heat-treated AMS 5544 \|\| 20 °C to 1095 °C (68 °F to 2003 °F) YS : mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) %El : heat-treated AMS 5544 \|\| 20 °C to 1095 °C (68 °F to 2003 °F) %El : mill annealed \|\| 760 °C to 871 °C (1400 °F to 1600 °F) SR : age hardened sheet \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h SR : age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) SR : age hardened sheet AMS 5544 \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h SR : age hardened sheet AMS 5544 \|\| tested at 704 °C (1300 °F) \|\| 10 h to 1,000 h SR : age hardened sheet AMS 5544 \|\| tested at 760 °C (1400 °F) \|\| 10 h to 1,000 h SR : age hardened sheet AMS 5544 \|\| tested at 816 °C (1500 °F) \|\| 10 h to 1,000 h SR : age hardened sheet AMS 5544 \|\| tested at 871 °C (1600 °F) \|\| 10 h to 1,000 h SR : age hardened sheet AMS 5544 \|\| tested at 927 °C (1700 °F) \|\| 10 h to 100 h SR : age hardened sheet AMS 5544 \|\| Master curve (LMP) \|\| 600 °C to 927 °C (1112 °F to 1700 °F) SR : age hardened bar \|\| tested at 649 °C (1200 °F) \|\| 15 h to 1,000 h SR : age hardened bar \|\| tested at 732 °C (1350 °F) \|\| 6 h to 1,000 h SR : age hardened bar \|\| tested at 816 °C (1500 °F) \|\| 2 h to 1,000 h SR : age hardened bar \|\| Master curve (LMP) \|\| 648 °C to 816 °C (1198 °F to 1501 °F) SR : after 60,000 h service \|\| tested at 600 °C (1112 °F) \|\| 400 h to 1x10⁵ h SR : after 60,000 h service \|\| tested at 650 °C (1202 °F) \|\| 20 h to 1x10⁵ h SR : after 60,000 h service \|\| tested at 700 °C (1292 °F) \|\| 1 h to 1x10⁵ h SR : after 60,000 h service \|\| tested at 760 °C (1400 °F) \|\| 1 h to 4x10⁴ h SR : after 60,000 h service \|\| tested at 815 °C (1499 °F) \|\| 1 h to 2,000 h SR : after 60,000 h service \|\| tested at 850 °C (1562 °F) \|\| 1 h to 200 h SR : after 60,000 h service \|\| Master curve (LMP) \|\| 600 °C to 816 °C (1112 °F to 1501 °F) FEN : sheet \|\| tested at 816 °C (1500 °F), R = -1, total strain range \|\| 1x10³ cycles to 2x10⁵ cycles FEN : casting \|\| tested at 649 °C (1200 °F), R = -1, total strain range \|\| 0.5 cycles to 2x10³ cycles FEN : age hardened at 1010 °C (1850 °F), 843 °C (1550 °F) & 760 °C (1400 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 170 cycles to 1.1x10⁴ cycles FEN : age hardened at 1010 °C (1850 °F), 843 °C (1550 °F) & 760 °C (1400 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain range \|\| 160 cycles to 1.1x10⁴ cycles FEN : age hardened at 1010 °C (1850 °F), 843 °C (1550 °F) & 760 °C (1400 °F) \|\| tested at 538 °C (1000 °F), R = -1, axial, total strain range \|\| 120 cycles to 1x10³ cycles FEN : age hardened at 1010 °C (1850 °F), 843 °C (1550 °F) & 760 °C (1400 °F) \|\| tested at 538 °C (1000 °F), R = -1, axial, plastic strain range \|\| 110 cycles to 1x10³ cycles FEN : standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 2.24x10³ cycles to 8.2x10³ cycles FEN : standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 2.4x10³ cycles to 3.75x10⁴ cycles FEN : standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 2.4x10³ cycles to 3.7x10⁴ cycles FEN : standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 1.27x10³ cycles to 1.44x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 1.7x10³ cycles to 2.65x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 1.35x10³ cycles to 1.92x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 1.35x10³ cycles to 2x10⁴ cycles FEN : standard heat treatment plus 732 °C (1350 °F) for 1000 h \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 920 cycles to 5x10³ cycles FEN : combination of both heat treatments from Kearsey et. al. \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range \|\| 1.74x10³ cycles to 2.65x10⁴ cycles FEN : combination of both heat treatments from Kearsey et. al. \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range \|\| 1.35x10³ cycles to 3.75x10⁴ cycles FEN : combination of both heat treatments from Kearsey et. al. \|\| tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 1.35x10³ cycles to 3.7x10⁴ cycles FEN : combination of both heat treatments from Kearsey et. al. \|\| tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range \|\| 920 cycles to 1.44x10⁴ cycles FSN : heat-treated at 840 °C (1544 °F) & 760 °C (1400 °F) \|\| tested at 870 °C (1598 °F), R = -1, axial, stress amplitude \|\| 1.2x10⁴ cycles to 5.6x10⁷ cycles CRS : 1% plastic strain, age hardened sheet \|\| tested at 649 °C (1200 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 704 °C (1300 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 760 °C (1400 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 816 °C (1500 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 871 °C (1600 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| tested at 927 °C (1700 °F) \|\| 100 h to 1,000 h CRS : 1% plastic strain, age hardened sheet \|\| Master curve (LMP) \|\| 649 °C to 927 °C (1200 °F to 1700 °F) RHO : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| aged \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| annealed \|\| -269 °C to 20 °C (-452 °F to 68 °F)

Colmonoy 4	D : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F)
Colmonoy 5	D : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)
Colmonoy 6 (AMS 4775A)	D : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) DLL : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) MTE : solid \|\| as-cast \|\| 20 °C to 650 °C (68 °F to 1202 °F) TC : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F) TD : solid \|\| 20 °C to 650 °C (68 °F to 1202 °F) SH : solid \|\| 20 °C to 816 °C (68 °F to 1500 °F)

CX2MW (UNS N26022) (ISO/EN/DIN C-NiCr21Mo14Fe4W3/NC6022) (ASTM A494/CX2MW)	D : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) DLL : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) MTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) CTE : solid \|\| 20 °C to 538 °C (68 °F to 1000 °F) E : solid \|\| 20 °C to 982 °C (68 °F to 1800 °F) SH : solid \|\| 20 °C to 600 °C (68 °F to 1112 °F)
CY40 (UNS N06040) (ISO/EN/DIN C-NiCr15Fe/NC6040) (ASTM A494/A743/A744/CY-40) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) DLL : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) MTE : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) CTE : solid \|\| -125 °C to 1000 °C (-193 °F to 1832 °F) E : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) G : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) v : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) K : solid \|\| -273 °C to 1000 °C (-460 °F to 1832 °F) SH : solid \|\| -200 °C to 1000 °C (-328 °F to 1832 °F) UTS : as-cast \|\| 20 °C to 816 °C (68 °F to 1500 °F) %El : as-cast \|\| 20 °C to 816 °C (68 °F to 1500 °F) HE : solid \|\| 316 °C to 982 °C (601 °F to 1800 °F) NE : solid \|\| as-rolled & oxidized \|\| 482 °C to 1093 °C (899 °F to 2000 °F) NE : solid \|\| sand-blasted & oxidized \|\| 482 °C to 1093 °C (899 °F to 2000 °F) VP : solid \|\| 1050 °C to 1275 °C (1922 °F to 2327 °F)
GH413	D* : solid \|\| room temperature value UTS* : solution treated & aged \|\| room temperature value YS* : solution treated & aged \|\| room temperature value %El* : solution treated & aged \|\| room temperature value FEN : solution treated & aged \|\| tested at 20 °C (68 °F), R = -1, axial, total strain amplitude \|\| 50 cycles to 2x10⁴ cycles FEN : solution treated & aged \|\| tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude \|\| 50 cycles to 2x10⁴ cycles FEN : solution treated & aged \|\| tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude \|\| 50 cycles to 2x10⁴ cycles FEN : solution treated & aged \|\| tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude \|\| 50 cycles to 2x10⁴ cycles FEN : solution treated & aged \|\| tested at 850 °C (1562 °F), R = -1, axial, elastic strain amplitude \|\| 50 cycles to 2x10⁴ cycles FEN : solution treated & aged \|\| tested at 850 °C (1562 °F), R = -1, axial, plastic strain amplitude \|\| 50 cycles to 2x10⁴ cycles
GH742	D* : solid \|\| room temperature value YSC : solution treated at 1150 °C (2102 °F) \|\| 0.001/s \|\| 950 °C to 1150 °C (1742 °F to 2102 °F) YSC : solution treated at 1150 °C (2102 °F) \|\| 0.01/s \|\| 950 °C to 1150 °C (1742 °F to 2102 °F) YSC : solution treated at 1150 °C (2102 °F) \|\| 0.1/s \|\| 950 °C to 1150 °C (1742 °F to 2102 °F) YSC : solution treated at 1150 °C (2102 °F) \|\| 1/s \|\| 950 °C to 1150 °C (1742 °F to 2102 °F)
GH2984	D* : solid \|\| room temperature value SSC : solution annealed & aged \|\| tested at 20 °C (68 °F), 0.005/s \|\| 0 to 0.15 mm/mm strain SSC : solution annealed & aged \|\| tested at 500 °C (932 °F), 0.005/s \|\| 0 to 0.158 mm/mm strain SSC : solution annealed & aged \|\| tested at 650 °C (1202 °F), 0.005/s \|\| 0 to 0.124 mm/mm strain SSC : solution annealed & aged \|\| tested at 700 °C (1292 °F), 0.005/s \|\| 0 to 0.94 mm/mm strain SSC : solution annealed & aged \|\| tested at 750 °C (1382 °F), 0.005/s \|\| 0 to 0.1 mm/mm strain SSC : solution annealed & aged \|\| tested at 800 °C (1472 °F), 0.005/s \|\| 0 to 0.15 mm/mm strain UTS : solution annealed & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) YS : solution annealed & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) %El : solution annealed & aged \|\| 20 °C to 800 °C (68 °F to 1472 °F) SR : solution annealed & aged \|\| tested at 650 °C (1202 °F) \|\| 900 h to 1x10⁵ h SR : solution annealed & aged \|\| tested at 700 °C (1292 °F) \|\| 2.2x10³ h to 1x10⁵ h SR : solution annealed & aged \|\| tested at 750 °C (1382 °F) \|\| 800 h to 2x10⁴ h SR : solution annealed & aged \|\| Master curve (LMP) \|\| 650 °C to 751 °C (1202 °F to 1384 °F)
IC21	D* : solid \|\| room temperature value SSC : electron beam powder bed fusion \|\| tested at 20 °C (68 °F), parallel to build direction, 0.006/s \|\| 0 to 0.12 mm/mm strain SSC : electron beam powder bed fusion \|\| tested at 1000 °C (1832 °F), parallel to build direction, 0.006/s \|\| 0 to 0.174 mm/mm strain UTS : electron beam powder bed fusion \|\| parallel to build direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) UTS : electron beam powder bed fusion \|\| perpendicular to build direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : electron beam powder bed fusion \|\| parallel to build direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : electron beam powder bed fusion \|\| perpendicular to build direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : electron beam powder bed fusion \|\| parallel to build direction \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

Ni-Ti (Nitinol) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1310 °C to 1500 °C (2390 °F to 2732 °F) DLL : liquid \|\| 1310 °C to 1500 °C (2390 °F to 2732 °F) MTE : liquid \|\| 1310 °C to 1500 °C (2390 °F to 2732 °F) CTE : liquid \|\| 1310 °C to 1500 °C (2390 °F to 2732 °F) E : solid \|\| annealed at 927 °C (1700 °F), M_s = -46 °C (-51 °F) \|\| -173 °C to 77 °C (-280 °F to 170 °F) E : solid \|\| annealed at 400 °C (752 °F), M_s = -50 °C (-58 °F) \|\| -13 °C to 150 °C (8 °F to 302 °F) TD* : solid \|\| martensitic phase \|\| room temperature value TD* : solid \|\| austenitic phase \|\| room temperature value SSC : electron beam powder bed fusion \|\| tested at 20 °C (68 °F), as-built, perpendicular to build direction, 3x10^-⁴/s \|\| 0 to 0.44 mm/mm strain FEN : A_s = 63 °C (145 °F), Af = 88 °C (190 °F) \|\| tested at 50 °C (122 °F), R = -1, rotary bending, total strain amplitude \|\| 1x10⁴ cycles to 6.13x10⁴ cycles FEN : A_s = 56 °C (133 °F), Af = 85 °C (185 °F) \|\| tested at 20 °C (68 °F), R = -1, rotary bending, total strain amplitude \|\| 1x10⁴ cycles to 5.2x10⁴ cycles FEN : A_s = 56 °C (133 °F), Af = 85 °C (185 °F) \|\| tested at 50 °C (122 °F), R = -1, rotary bending, total strain amplitude \|\| 2.5x10³ cycles to 2.5x10⁴ cycles FEN : A_s = 56 °C (133 °F), Af = 85 °C (185 °F) \|\| tested at 80 °C (176 °F), R = -1, rotary bending, total strain amplitude \|\| 400 cycles to 1.7x10⁴ cycles FEN : A_s = 56 °C (133 °F), Af = 85 °C (185 °F) \|\| tested at 110 °C (230 °F), R = -1, rotary bending, total strain amplitude \|\| 346 cycles to 1.3x10⁴ cycles FEN : A_s = 37 °C (99 °F), Af = 60 °C (141 °F) \|\| tested at 50 °C (122 °F), R = -1, rotary bending, total strain amplitude \|\| 970 cycles to 1.7x10⁴ cycles FSN : Af = 10 °C (50 °F), M_s = -30 °C (-22 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 3x10³ cycles to 2x10⁷ cycles FSN : Af = 110 °C (230 °F), M_s = 70 °C (158 °F) \|\| tested at 20 °C (68 °F), R = -1, axial, stress amplitude \|\| 1.4x10⁴ cycles to 1x10⁷ cycles FSN : Af = 27 °C (81 °F) \|\| tested at 30 °C (86 °F), R = 0.0, axial, stress amplitude \|\| 1x10³ cycles to 7x10⁴ cycles FSN : Af = 27 °C (81 °F) \|\| tested at 60 °C (140 °F), R = 0.0, axial, stress amplitude \|\| 700 cycles to 3x10⁵ cycles FSN : Af = 27 °C (81 °F) \|\| tested at 160 °C (320 °F), R = 0.0, axial, stress amplitude \|\| 3x10³ cycles to 4x10⁵ cycles RHO : solid \|\| on heating \|\| -30 °C to 103 °C (-22 °F to 217 °F) RHO : solid \|\| on cooling \|\| -30 °C to 103 °C (-22 °F to 217 °F) SIGMA : solid \|\| on heating \|\| -30 °C to 103 °C (-22 °F to 217 °F) SIGMA : solid \|\| on cooling \|\| -30 °C to 103 °C (-22 °F to 217 °F)

ERNiCr-3 weld metal	UTS : deposited by the GTAW process \|\| 20 °C to 816 °C (68 °F to 1500 °F) YS : deposited by the GTAW process \|\| 20 °C to 816 °C (68 °F to 1500 °F) SR : deposited by the GTAW process \|\| tested at 649 °C (1200 °F) \|\| 10 h to 6x10⁴ h
INCO weld A	UTS : deposited by the SMAW process \|\| 20 °C to 757 °C (68 °F to 1394 °F) YS : deposited by the SMAW process \|\| 20 °C to 871 °C (68 °F to 1600 °F) %El : deposited by the SMAW process \|\| 20 °C to 871 °C (68 °F to 1600 °F)

Ni - 0.5 Co (at %)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F)
Ni - 1 Co (at %)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F)
Ni - 3 Co (at %)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F)
Ni - 5 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 920 °C (-395 °F to 1688 °F) SIGMA : solid \|\| -237 °C to 920 °C (-395 °F to 1688 °F)
Ni - 10 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 920 °C (-395 °F to 1688 °F) SIGMA : solid \|\| -237 °C to 920 °C (-395 °F to 1688 °F)
Ni - 15 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 915 °C (-395 °F to 1679 °F) SIGMA : solid \|\| -237 °C to 915 °C (-395 °F to 1679 °F)
Ni - 20 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	D : liquid \|\| 1515 °C to 1675 °C (2759 °F to 3047 °F) DLL : liquid \|\| 1515 °C to 1675 °C (2759 °F to 3047 °F) MTE : liquid \|\| 1515 °C to 1675 °C (2759 °F to 3047 °F) CTE : liquid \|\| 1515 °C to 1675 °C (2759 °F to 3047 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 1135 °C (-395 °F to 2075 °F) SIGMA : solid \|\| -237 °C to 1135 °C (-395 °F to 2075 °F)
Ni - 22.2 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	RHO : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F) SIGMA : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F)
Ni - 24.6 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	RHO : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F) SIGMA : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F)
Ni - 25 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 1135 °C (-395 °F to 2075 °F) SIGMA : solid \|\| -237 °C to 1135 °C (-395 °F to 2075 °F)
Ni - 26 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	RHO : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F) SIGMA : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F)
Ni - 27.4 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	RHO : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F) SIGMA : solid \|\| -237 °C to 1127 °C (-395 °F to 2061 °F)
Ni - 30 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -203 °C to 1235 °C (-334 °F to 2255 °F) SIGMA : solid \|\| -203 °C to 1235 °C (-334 °F to 2255 °F)
Ni - 35 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -237 °C to 1235 °C (-395 °F to 2255 °F) SIGMA : solid \|\| -237 °C to 1235 °C (-395 °F to 2255 °F)
Ni - 40 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower)	D : liquid \|\| 1510 °C to 1665 °C (2750 °F to 3029 °F) DLL : liquid \|\| 1510 °C to 1665 °C (2750 °F to 3029 °F) MTE : liquid \|\| 1510 °C to 1665 °C (2750 °F to 3029 °F) CTE : liquid \|\| 1510 °C to 1665 °C (2750 °F to 3029 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -180 °C to 1220 °C (-292 °F to 2228 °F) SIGMA : solid \|\| -180 °C to 1220 °C (-292 °F to 2228 °F)
Ni - 45 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -195 °C to 1220 °C (-319 °F to 2228 °F) SIGMA : solid \|\| -195 °C to 1220 °C (-319 °F to 2228 °F)
Ni - 50 Co (at %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower)	ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -195 °C to 1327 °C (-319 °F to 2421 °F) SIGMA : solid \|\| -195 °C to 1327 °C (-319 °F to 2421 °F)

Ni - 8 Cr (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F)
Ni - 10 Cr (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) D : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : liquid \|\| 1437 °C to 1637 °C (2618 °F to 2979 °F) TC : solid \|\| 20 °C to 970 °C (68 °F to 1778 °F)
Ni - 16 Cr (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F)
Ni - 20 Cr (at %)	D : liquid \|\| 1427 °C to 1627 °C (2600 °F to 2961 °F) DLL : liquid \|\| 1427 °C to 1627 °C (2600 °F to 2961 °F) MTE : liquid \|\| 1427 °C to 1627 °C (2600 °F to 2961 °F) CTE : liquid \|\| 1427 °C to 1627 °C (2600 °F to 2961 °F) TC : solid \|\| 20 °C to 890 °C (68 °F to 1634 °F) Vis : liquid \|\| 1407 °C to 1570 °C (2564 °F to 2858 °F)
Ni - 22 Cr (at %)	TC : solid \|\| 20 °C to 690 °C (68 °F to 1274 °F)
Ni - 40 Cr (at %)	D : liquid \|\| 1375 °C to 1575 °C (2507 °F to 2867 °F) DLL : liquid \|\| 1375 °C to 1575 °C (2507 °F to 2867 °F) MTE : liquid \|\| 1375 °C to 1575 °C (2507 °F to 2867 °F) CTE : liquid \|\| 1375 °C to 1575 °C (2507 °F to 2867 °F)

Ni - 0.5 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 1 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 3 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 5 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 10 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1340 °C to 1475 °C (2444 °F to 2687 °F) DLL : liquid \|\| 1340 °C to 1475 °C (2444 °F to 2687 °F) MTE : liquid \|\| 1340 °C to 1475 °C (2444 °F to 2687 °F) CTE : liquid \|\| 1340 °C to 1475 °C (2444 °F to 2687 °F) TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) ST : liquid \|\| 1235 °C to 1835 °C (2255 °F to 3335 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 15 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 20 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1520 °C to 1645 °C (2768 °F to 2993 °F) DLL : liquid \|\| 1520 °C to 1645 °C (2768 °F to 2993 °F) MTE : liquid \|\| 1520 °C to 1645 °C (2768 °F to 2993 °F) CTE : liquid \|\| 1520 °C to 1645 °C (2768 °F to 2993 °F) TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) SH : liquid \|\| 1405 °C to 1727 °C (2561 °F to 3141 °F) ST : liquid \|\| 1220 °C to 1820 °C (2228 °F to 3308 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) RHO : liquid \|\| 1150 °C to 1827 °C (2102 °F to 3321 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : liquid \|\| 1150 °C to 1827 °C (2102 °F to 3321 °F)
Ni - 25 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 30 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1355 °C to 1490 °C (2471 °F to 2714 °F) DLL : liquid \|\| 1355 °C to 1490 °C (2471 °F to 2714 °F) MTE : liquid \|\| 1355 °C to 1490 °C (2471 °F to 2714 °F) CTE : liquid \|\| 1355 °C to 1490 °C (2471 °F to 2714 °F) TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) ST : liquid \|\| 1180 °C to 1780 °C (2156 °F to 3236 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)
Ni - 35 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) SH : liquid \|\| 1365 °C to 1727 °C (2489 °F to 3141 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) RHO : liquid \|\| 1365 °C to 1827 °C (2489 °F to 3321 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : liquid \|\| 1365 °C to 1827 °C (2489 °F to 3321 °F)
Ni - 40 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1405 °C to 1645 °C (2561 °F to 2993 °F) DLL : liquid \|\| 1405 °C to 1645 °C (2561 °F to 2993 °F) MTE : liquid \|\| 1405 °C to 1645 °C (2561 °F to 2993 °F) CTE : liquid \|\| 1405 °C to 1645 °C (2561 °F to 2993 °F) TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) ST : liquid \|\| 1150 °C to 1750 °C (2102 °F to 3182 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) RHO : liquid \|\| 1100 °C to 1430 °C (2012 °F to 2606 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : liquid \|\| 1100 °C to 1430 °C (2012 °F to 2606 °F)
Ni - 45 Cu (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 927 °C (-452 °F to 1700 °F) RHO : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F) SIGMA : solid \|\| -272 °C to 827 °C (-458 °F to 1521 °F)

Ni - 45 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) RHO : liquid \|\| 1432 °C to 1727 °C (2609 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) SIGMA : liquid \|\| 1432 °C to 1727 °C (2609 °F to 3141 °F)
Ni - 40 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) DLL : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) MTE : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) CTE : liquid \|\| 1450 °C to 1700 °C (2642 °F to 3092 °F) TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) RHO : liquid \|\| 1430 °C to 1727 °C (2606 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) SIGMA : liquid \|\| 1430 °C to 1727 °C (2606 °F to 3141 °F)
Ni - 35 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1429 °C (-458 °F to 2604 °F) RHO : liquid \|\| 1430 °C to 1727 °C (2606 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1429 °C (-458 °F to 2604 °F) SIGMA : liquid \|\| 1430 °C to 1727 °C (2606 °F to 3141 °F)
Ni - 30 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1429 °C (-458 °F to 2604 °F) RHO : liquid \|\| 1431 °C to 1727 °C (2608 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1429 °C (-458 °F to 2604 °F) SIGMA : liquid \|\| 1431 °C to 1727 °C (2608 °F to 3141 °F)
Ni - 25 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) RHO : liquid \|\| 1433 °C to 1727 °C (2611 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) SIGMA : liquid \|\| 1433 °C to 1727 °C (2611 °F to 3141 °F)
Ni - 20 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 1453 °C to 1750 °C (2647 °F to 3182 °F) DLL : liquid \|\| 1453 °C to 1750 °C (2647 °F to 3182 °F) MTE : liquid \|\| 1453 °C to 1750 °C (2647 °F to 3182 °F) CTE : liquid \|\| 1453 °C to 1750 °C (2647 °F to 3182 °F) TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) RHO : liquid \|\| 1433 °C to 1727 °C (2611 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1430 °C (-458 °F to 2606 °F) SIGMA : liquid \|\| 1433 °C to 1727 °C (2611 °F to 3141 °F)
Ni - 15 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1434 °C (-458 °F to 2613 °F) RHO : liquid \|\| 1442 °C to 1727 °C (2627 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1434 °C (-458 °F to 2613 °F) SIGMA : liquid \|\| 1442 °C to 1727 °C (2627 °F to 3141 °F)
Ni - 10 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1437 °C (-458 °F to 2619 °F) RHO : liquid \|\| 1446 °C to 1727 °C (2635 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1437 °C (-458 °F to 2619 °F) SIGMA : liquid \|\| 1446 °C to 1727 °C (2635 °F to 3141 °F)
Ni - 5 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) RHO : liquid \|\| 1451 °C to 1727 °C (2644 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1327 °C (-458 °F to 2421 °F) SIGMA : liquid \|\| 1451 °C to 1727 °C (2644 °F to 3141 °F)
Ni - 3 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1447 °C (-458 °F to 2637 °F) RHO : liquid \|\| 1453 °C to 1727 °C (2647 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1447 °C (-458 °F to 2637 °F) SIGMA : liquid \|\| 1453 °C to 1727 °C (2647 °F to 3141 °F)
Ni - 1 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1452 °C (-458 °F to 2646 °F) RHO : liquid \|\| 1454 °C to 1727 °C (2649 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1452 °C (-458 °F to 2646 °F) SIGMA : liquid \|\| 1454 °C to 1727 °C (2649 °F to 3141 °F)
Ni - 0.5 Fe (wt %) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value TC : solid \|\| -269 °C to 827 °C (-452 °F to 1521 °F) ST : liquid \|\| 1100 °C to 1600 °C (2012 °F to 2912 °F) RHO : solid \|\| -272 °C to 1454 °C (-458 °F to 2649 °F) RHO : liquid \|\| 1455 °C to 1727 °C (2651 °F to 3141 °F) SIGMA : solid \|\| -272 °C to 1454 °C (-458 °F to 2649 °F) SIGMA : liquid \|\| 1455 °C to 1727 °C (2651 °F to 3141 °F)

Ni₇₀Cu₂₀Fe₁₀	D : liquid \|\| 1135 °C to 1440 °C (2075 °F to 2624 °F) DLL : liquid \|\| 1135 °C to 1440 °C (2075 °F to 2624 °F) MTE : liquid \|\| 1135 °C to 1440 °C (2075 °F to 2624 °F) CTE : liquid \|\| 1135 °C to 1440 °C (2075 °F to 2624 °F)
Ni₆₀Cu₂₀Fe₂₀	D : liquid \|\| 1272 °C to 1450 °C (2321 °F to 2642 °F) DLL : liquid \|\| 1272 °C to 1450 °C (2321 °F to 2642 °F) MTE : liquid \|\| 1272 °C to 1450 °C (2321 °F to 2642 °F) CTE : liquid \|\| 1272 °C to 1450 °C (2321 °F to 2642 °F)
Ni₄₅Cu₂₀Fe₃₅	D : liquid \|\| 1284 °C to 1430 °C (2343 °F to 2606 °F) DLL : liquid \|\| 1284 °C to 1430 °C (2343 °F to 2606 °F) MTE : liquid \|\| 1284 °C to 1430 °C (2343 °F to 2606 °F) CTE : liquid \|\| 1284 °C to 1430 °C (2343 °F to 2606 °F)

Ni₇₂Fe₁₈Cr₁₀	D : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) DLL : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) MTE : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) CTE : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F)
Ni₆₄Fe₁₆Cr₂₀	D : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) DLL : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) MTE : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) CTE : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) Vis : liquid \|\| 1400 °C to 1575 °C (2552 °F to 2867 °F)
Ni₅₄Fe₃₆Cr₁₀	D : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) DLL : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) MTE : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F) CTE : liquid \|\| 1451 °C to 1651 °C (2644 °F to 3004 °F)
Ni₄₈Fe₃₂Cr₂₀	D : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) DLL : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) MTE : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) CTE : liquid \|\| 1417 °C to 1617 °C (2582 °F to 2943 °F) Vis : liquid \|\| 1400 °C to 1575 °C (2552 °F to 2867 °F)
Ni₄₈Fe₁₂Cr₄₀	D : liquid \|\| 1367 °C to 1567 °C (2492 °F to 2853 °F) DLL : liquid \|\| 1367 °C to 1567 °C (2492 °F to 2853 °F) MTE : liquid \|\| 1367 °C to 1567 °C (2492 °F to 2853 °F) CTE : liquid \|\| 1367 °C to 1567 °C (2492 °F to 2853 °F)

Ni - 5 Mo (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F)
Ni - 10 Mo (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F)
Ni - 15 Mo (at %)	D : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) DLL : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) MTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F) CTE : solid \|\| 20 °C to 610 °C (68 °F to 1130 °F)

Ni - 0.5 Pd (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 1.7 Pd (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 5.7 Pd (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

Ni - 5 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)
Ni - 8 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)
Ni - 10 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)
Ni - 12 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)
Ni - 16 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)
Ni - 25 Re (at %)	D : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) DLL : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) MTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F) CTE : solid \|\| 20 °C to 1030 °C (68 °F to 1886 °F)

Ni - 0.6 Rh (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 1.7 Rh (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 5.9 Rh (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

Ni - 0.6 Ru (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 1.7 Ru (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)
Ni - 6.4 Ru (wt %)	D* : solid \|\| room temperature value UTS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) YS : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F) %El : annealed \|\| 20 °C to 1000 °C (68 °F to 1832 °F)

Ni - 5 W (at %)	D : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) DLL : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) MTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F) CTE : solid \|\| 20 °C to 800 °C (68 °F to 1472 °F)
Aluminum alloys	Property : Condition // Data range
1050 (UNS A91050) (WNr 3.0255) (ISO/EN/DIN Al99.5) (JIS A1050/A199.5) (AFNOR A5) (GB & GB/T T3880-2018) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| annealed \|\| 20 °C to 660 °C (68 °F to 1220 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| -253 °C to 660 °C (-424 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 0.066 mm (0.0026 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 0.39 mm (0.0154 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 1.41 mm (0.0555 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 3.46 mm (0.136 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles FSN : effect of grain size \|\| tested at 20 °C (68 °F), R = 0.1, axial, 9.74 mm (0.383 inch) grains, maximum stress \|\| 3x10⁵ cycles to 1x10⁷ cycles HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)
1060 (UNS A91060) (ISO/EN/DIN Al99.6) (JIS A1060PB/A1060SB/A1060SBC) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| annealed \|\| 20 °C to 660 °C (68 °F to 1220 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| -253 °C to 660 °C (-424 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : O temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : H12 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : H18 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain UTS : 10,000 h hold \|\| O temper \|\| -198 °C to 260 °C (-325 °F to 500 °F) YS : 10,000 h hold \|\| O temper \|\| -198 °C to 260 °C (-325 °F to 500 °F) HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)
1085 (UNS A91085) (ISO/EN/DIN Al99.85) (JIS 1085H/A1085P) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| annealed \|\| 20 °C to 660 °C (68 °F to 1220 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| -253 °C to 660 °C (-424 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : annealed \|\| tested at 23 °C (73 °F), 0.008/s \|\| 0 to 0.42 mm/mm strain SSC : annealed \|\| tested at -196.1 °C (-321.1 °F), 0.008/s \|\| 0 to 0.52 mm/mm strain HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F)

1100 (UNS A91100) (ISO/EN/DIN Al99.0Cu) (AFNOR A45) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| O temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) DLL : solid \|\| O temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) MTE : solid \|\| O temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) CTE : solid \|\| O temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| F temper \|\| -269 °C to 93 °C (-452 °F to 199 °F) TD : solid \|\| F temper \|\| -253 °C to 440 °C (-424 °F to 824 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) SSC : O temper \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.371 mm/mm strain SSC : O temper \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.38 mm/mm strain SSC : O temper \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : O temper \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.262 mm/mm strain SSC : O temper \|\| tested at 93 °C (200 °F), static test, unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : O temper \|\| tested at 177 °C (350 °F), static test, unknown strain rate \|\| 0 to 0.84 mm/mm strain SSC : O temper \|\| tested at 288 °C (550 °F), static test, unknown strain rate \|\| 0 to 0.48 mm/mm strain SSC : H16 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSC : H18 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSC : H12 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : H26 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.35 mm/mm strain UTS : 10,000 h hold \|\| O temper \|\| -254 °C to 260 °C (-425 °F to 500 °F) UTS : 10,000 h hold \|\| H12 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| H14 temper \|\| -269 °C to 370 °C (-452 °F to 698 °F) UTS : 10,000 h hold \|\| H18 temper \|\| -196 °C to 425 °C (-321 °F to 797 °F) YS : 10,000 h hold \|\| O temper \|\| -254 °C to 260 °C (-425 °F to 500 °F) YS : 10,000 h hold \|\| H12 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| H14 temper \|\| -269 °C to 370 °C (-452 °F to 698 °F) YS : 10,000 h hold \|\| H18 temper \|\| -196 °C to 425 °C (-321 °F to 797 °F) SR : O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : O temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : O temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : O temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : O temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : O temper \|\| tested at 232 °C (450 °F) \|\| 5 h to 2,050 h SR : O temper \|\| tested at 260 °C (500 °F) \|\| 15 h to 1,800 h SR : O temper \|\| tested at 288 °C (550 °F) \|\| 30 h to 275 h SR : O temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : H12 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : H12 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : H12 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : H12 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : H12 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) SR : H14 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : H14 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : H14 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : H14 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : H14 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) SR : H18 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : H18 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1x10⁵ h SR : H18 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h SR : H18 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : H18 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : H18 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : H18 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : H18 temper \|\| Master curve (LMP) \|\| 24 °C to 261 °C (75 °F to 502 °F) FSN : O temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : O temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : O temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : O temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : H16 temper \|\| tested at -196.1 °C (-321.1 °F), R = -1, flexure, maximum stress \|\| 3x10³ cycles to 2x10⁶ cycles FSN : H16 temper \|\| tested at -79 °C (-110 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : H16 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10³ cycles to 1x10⁸ cycles FSN : H16 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H16 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H16 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H18 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H18 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H18 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H18 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H26 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H26 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H26 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H26 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles CRS : 0.1% total strain, O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, O temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, O temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, O temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, O temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, O temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.2% total strain, O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, O temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, O temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, O temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, O temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, O temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.5% total strain, O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, O temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, O temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, O temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, O temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, O temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 1% total strain, O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, O temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, O temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, O temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, O temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, O temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.1% total strain, H12 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, H12 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, H12 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, H12 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.2% total strain, H12 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, H12 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, H12 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, H12 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.5% total strain, H12 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, H12 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, H12 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 1% total strain, H12 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, H12 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, H12 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.1% total strain, H14 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, H14 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, H14 temper \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 0.2% total strain, H14 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, H14 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, H14 temper \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 0.5% total strain, H14 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, H14 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, H14 temper \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 1% total strain, H14 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, H14 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, H14 temper \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) IC : tested at 24 °C (75 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, O temper \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, O temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, O temper \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, O temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, O temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, O temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, H12 temper \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H12 temper \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H12 temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H12 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, H14 temper \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H14 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H14 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H14 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H14 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, H14 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H14 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H14 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, H14 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| O temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| O temper \|\| -269 °C to 20 °C (-452 °F to 68 °F)
1145 (UNS A91145) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| annealed \|\| 20 °C to 660 °C (68 °F to 1220 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| -253 °C to 660 °C (-424 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)
1199 (UNS A91199) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| bulk \|\| -273 °C to 660 °C (-460 °F to 1220 °F) TC : solid \|\| 105 nm thin film \|\| 20 °C to 327 °C (68 °F to 620 °F) TC : solid \|\| 82 nm thin film \|\| 20 °C to 327 °C (68 °F to 620 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| -253 °C to 660 °C (-424 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) Vis : liquid \|\| 653 °C to 890 °C (1207 °F to 1634 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)

1350 (UNS A91350) (ISO/EN/DIN E-Al99.5) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) D : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) DLL : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) DLL : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) MTE : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) MTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) CTE : solid \|\| -263 °C to 627 °C (-442 °F to 1160 °F) CTE : liquid \|\| 660 °C to 2627 °C (1220 °F to 4760 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| annealed \|\| -268 °C to 660 °C (-450 °F to 1220 °F) TC : liquid \|\| 660 °C to 8227 °C (1220 °F to 14840 °F) TD : solid \|\| annealed \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : solid \|\| -263 °C to 660 °C (-442 °F to 1220 °F) SH : liquid \|\| 660 °C to 5727 °C (1220 °F to 10340 °F) SH : gas \|\| 20 °C to 1727 °C (68 °F to 3140 °F) FSN : H19 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : H19 temper \|\| tested at 100 °C (212 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles HE : solid \|\| -98 °C to 427 °C (-145 °F to 800 °F) VP : solid \|\| 20 °C to 660 °C (68 °F to 1220 °F) VP : liquid \|\| 660 °C to 1527 °C (1220 °F to 2780 °F) RHO : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) RHO : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F) SIGMA : solid \|\| -272 °C to 660 °C (-458 °F to 1220 °F) SIGMA : liquid \|\| 660 °C to 1727 °C (1220 °F to 3140 °F)

2011 (UNS A92011) (WNr 3.1056/3.1655) (ISO/EN/DIN AlCu4PbMg/AlCu6BiPb) (JIS A2011) (ASTM B210/B211) (SAE J454) (AFNOR A-U5PbBi) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) DLL : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) MTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) CTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) UTS : 0.5 h hold \|\| T8 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 0.5 h hold \|\| T3 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 0.5 h hold \|\| T451 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 1000 h hold \|\| T8 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 1000 h hold \|\| T3 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 1000 h hold \|\| T451 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 0.5 h hold \|\| T8 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 0.5 h hold \|\| T3 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 0.5 h hold \|\| T451 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 1000 h hold \|\| T8 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 1000 h hold \|\| T3 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 1000 h hold \|\| T451 temper \|\| 20 °C to 370 °C (68 °F to 698 °F) SR : T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.1% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T3 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 1% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) IC : tested at 24 °C (75 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
2014 (UNS A92014) (ISO/EN/DIN AlCu4SiMg/AlCuSiMn) (JIS A2014) (AFNOR A-U4SG) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| T6 temper \|\| -253 °C to 300 °C (-424 °F to 572 °F) TD : solid \|\| T6 temper \|\| 20 °C to 260 °C (68 °F to 500 °F) SH : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) SSC : T651X temper, extrusion \|\| tested at 20 °C (68 °F), unknown strain rate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T651X temper, extrusion \|\| tested at 20 °C (68 °F), unknown strain rate, longitudinal \|\| 0 to 0.6 mm/mm strain SSC : T6 temper, sheet \|\| tested at 27 °C (80 °F), 1/s \|\| 0 to 0.76 mm/mm strain SSC : T6 temper, sheet \|\| tested at 232 °C (450 °F), 1/s, held for 1800 s \|\| 0 to 0.2 mm/mm strain SSC : T6 temper, sheet \|\| tested at 316 °C (600 °F), 1/s, held for 1800 s \|\| 0 to 0.39 mm/mm strain SSC : T6 temper, sheet \|\| tested at 149 °C (300 °F), 1/s, held for 1800 s \|\| 0 to 0.39 mm/mm strain SSC : T6 temper, sheet \|\| tested at 232 °C (450 °F), 1/s, held for 10 s \|\| 0 to 0.2 mm/mm strain SSC : T6 temper, sheet \|\| tested at 149 °C (300 °F), 1/s, held for 10 s \|\| 0 to 0.2 mm/mm strain SSC : T6 temper, sheet \|\| tested at 316 °C (600 °F), 1/s, held for 10 s \|\| 0 to 0.2 mm/mm strain SSC : T6 temper, unknown strain rate \|\| tested at 20 °C (68 °F), plate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T6 temper, unknown strain rate \|\| tested at 20 °C (68 °F), forging, transverse \|\| 0 to 0.6 mm/mm strain SSC : T6 temper, unknown strain rate \|\| tested at 20 °C (68 °F), forging, longitudinal \|\| 0 to 0.7 mm/mm strain SSC : T6 temper, unknown strain rate \|\| tested at 20 °C (68 °F), plate, longitudinal \|\| 0 to 0.8 mm/mm strain SSC : T4 temper, unknown strain rate \|\| tested at 20 °C (68 °F), rod \|\| 0 to 0.14 mm/mm strain SSC : T652 temper, unknown strain rate \|\| tested at 20 °C (68 °F), forging, transverse \|\| 0 to 0.6 mm/mm strain SSC : T652 temper, unknown strain rate \|\| tested at 20 °C (68 °F), forging, longitudinal \|\| 0 to 0.5 mm/mm strain UTS : 10,000 h hold \|\| T6 & T652 tempers, forgings \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 10,000 h hold \|\| T4 temper, extrusions \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T6 temper, extrusions \|\| -196 °C to 540 °C (-321 °F to 1004 °F) UTS : 10,000 h hold \|\| T6 temper sheet & T651 temper plate \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T61 temper, forgings \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| O temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T6 & T652 tempers, forgings \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 10,000 h hold \|\| T4 temper, extrusions \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T6 temper, extrusions \|\| -196 °C to 540 °C (-321 °F to 1004 °F) YS : 10,000 h hold \|\| T6 temper sheet & T651 temper plate \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T61 temper, forgings \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| O temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YSC : clad sheet \|\| T6 temper \|\| 20 °C to 316 °C (68 °F to 600 °F) %El : 10,000 hold \|\| T6 temper \|\| -259 °C to 371 °C (-434 °F to 700 °F) SR : T6 temper, rod \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, rod \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 & T652 tempers, forgings, < 50.8 mm (2 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, extrusions, 12.7 mm to 19 mm (0.5 inch to 0.75 inch) thick \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) SR : T651 temper, plate, 6.35 mm to 12.7 mm (0.25 inch to 0.5 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h FEN : T6 temper \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 10 cycles to 7.1x10⁴ cycles FEN : T6 temper \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 30 cycles to 4.3x10⁴ cycles FEN : T6 temper \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 10 cycles to 7.72x10⁴ cycles FSN : T4 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T4 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 7x10⁷ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -0.5, axial, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -0.4, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = 0, axial, maximum stress \|\| 6x10³ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = 0.06, axial, maximum stress \|\| 6x10³ cycles to 7x10⁶ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T6 temper \|\| tested at 316 °C (600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T6 temper, sheet \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T6 temper, sheet \|\| tested at -196.1 °C (-321.1 °F), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T6 temper, sheet \|\| tested at -196.1 °C (-321.1 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at -196.1 °C (-321.1 °F), R = -1, K_t = 8.0, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at -253.1 °C (-423.7 °F), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, TIG welded \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, TIG welded \|\| tested at -196.1 °C (-321.1 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : T6 temper, TIG welded \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 600 cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 1.6 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 3x10⁶ cycles FSN : T6 temper, notched, K_t = 1.6 \|\| tested at 20 °C (68 °F), R = -0.4, axial, maximum stress \|\| 4x10³ cycles to 3x10⁶ cycles FSN : T6 temper, notched, K_t = 1.6 \|\| tested at 20 °C (68 °F), R = -0.06, axial, maximum stress \|\| 5x10³ cycles to 3x10⁶ cycles FSN : T6 temper, notched, K_t = 1.6 \|\| tested at 20 °C (68 °F), R = 0.46, axial, maximum stress \|\| 1x10⁵ cycles to 2x10⁶ cycles FSN : T6 temper, notched, K_t = 2.4 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 3x10⁷ cycles FSN : T6 temper, notched, K_t = 2.4 \|\| tested at 20 °C (68 °F), R = -0.4, axial, maximum stress \|\| 1x10³ cycles to 3x10⁷ cycles FSN : T6 temper, notched, K_t = 2.4 \|\| tested at 20 °C (68 °F), R = 0.06, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T6 temper, notched, K_t = 2.4 \|\| tested at 20 °C (68 °F), R = 0.46, axial, maximum stress \|\| 7x10³ cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 2.4 \|\| tested at 20 °C (68 °F), R = 0.74, axial, maximum stress \|\| 4x10⁴ cycles to 5x10⁵ cycles FSN : T6 temper, notched, K_t = 3.4 \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁷ cycles FSN : T6 temper, notched, K_t = 3.4 \|\| tested at 20 °C (68 °F), R = -0.4, axial, maximum stress \|\| 1x10³ cycles to 5x10⁶ cycles FSN : T6 temper, notched, K_t = 3.4 \|\| tested at 20 °C (68 °F), R = 0.06, axial, maximum stress \|\| 1x10³ cycles to 2x10⁵ cycles FSN : T6 temper, notched, K_t = 3.4 \|\| tested at 20 °C (68 °F), R = 0.46, axial, maximum stress \|\| 4x10³ cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 3.4 \|\| tested at 20 °C (68 °F), R = 0.74, axial, maximum stress \|\| 6x10⁴ cycles to 6x10⁵ cycles FSN : T6 temper, notched, K_t = 3.5 \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 400 cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 8.0 \|\| tested at -253.1 °C (-423.7 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T6 & T652 tempers, forgings \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 & T652 tempers, forgings \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 & T652 tempers, forgings \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) CRS : 1% total strain, T6 & T652 tempers, forgings \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 & T652 tempers, forgings \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 & T652 tempers, forgings \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 & T652 tempers, forgings \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 & T652 tempers, forgings \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 & T652 tempers, forgings \|\| Master curve (LMP) \|\| 24 °C to 205 °C (75 °F to 401 °F) IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 & T652 tempers, forgings \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 160 °C (320 °F), total strain, T6 & T652 tempers, forgings \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 171 °C (340 °F), total strain, T6 & T652 tempers, forgings \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 182 °C (360 °F), total strain, T6 & T652 tempers, forgings \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 193 °C (380 °F), total strain, T6 & T652 tempers, forgings \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 & T652 tempers, forgings \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 & T652 tempers, forgings \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 & T652 tempers, forgings \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 & T652 tempers, forgings \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 & T652 tempers, forgings \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T651 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T651 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T651 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T651 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T651 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain RHO : solid \|\| T651 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| T651 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F)
2017 (UNS A92017) (WNr 3.1325) (ISO/EN/DIN AlCu4MgSi/AlCuMg1) (AFNOR A-U4G) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) SSC : T4 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.14 mm/mm strain UTS : 0.5 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 100 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 1000 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10,000 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 0.5 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 100 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 1000 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10,000 h hold \|\| T4 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) SR : T4 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h SR : T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T4 temper \|\| Master curve (LMP) \|\| 204 °C to 316 °C (399 °F to 601 °F) CRS : 0.1% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 100 h CRS : 0.1% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h CRS : 0.2% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
2018 (UNS A92018) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : solid \|\| -18 °C to 482 °C (-1 °F to 900 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) UTS : 0.5 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 100 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 1000 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 0.5 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 100 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 1000 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T61 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) SR : T61 temper \|\| tested at 100 °C (212 °F) \|\| 1 h to 1,000 h SR : T61 temper \|\| tested at 149 °C (300 °F) \|\| 1 h to 1,000 h SR : T61 temper \|\| tested at 204 °C (400 °F) \|\| 1 h to 1,000 h SR : T61 temper \|\| Master curve (LMP) \|\| 100 °C to 205 °C (212 °F to 401 °F) FSN : T61 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles CRS : 0.1% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 1 h to 100 h CRS : 0.2% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 100 h CRS : 0.5% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 1 h to 100 h CRS : 1% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 1 h to 100 h CRS : 1% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 100 h IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain
2020 (UNS A92020) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| T6 temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) DLL : solid \|\| T6 temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) MTE : solid \|\| T6 temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) CTE : solid \|\| T6 temper \|\| -253 °C to 27 °C (-424 °F to 80 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) SSC : T6 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : T6 temper \|\| tested at -79 °C (-110 °F), unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : T6 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : T6 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate \|\| 0 to 0.6 mm/mm strain UTS : 0.5 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 100 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 1000 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10,000 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 0.5 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 100 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 1000 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10,000 h hold \|\| T6 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) SR : T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| Master curve (LMP) \|\| 24 °C to 261 °C (75 °F to 502 °F) FSN : T6 temper, sheet \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 600 cycles to 1x10⁷ cycles FSN : T6 temper, sheet \|\| tested at -195.6 °C (-320 °F), R = -1, axial, maximum stress \|\| 800 cycles to 1x10⁷ cycles FSN : T6 temper, sheet \|\| tested at -252.7 °C (-422.9 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T6 temper, other forms \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T6 temper, other forms \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T6 temper, other forms \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T651 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T651 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T651 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T651 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T651 temper \|\| tested at 316 °C (600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles CRS : 0.1% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1 h CRS : 0.5% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 10 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1 h CRS : 1% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 100 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 177 °C (350 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 177 °C (350 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 177 °C (350 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 2x10^-³ mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
2021 (UNS A92021) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) UTS : 0.1 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 0.5 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 10 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 100 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 1000 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) UTS : 10,000 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 0.1 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 0.5 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 10 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 100 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 1000 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) YS : 10,000 h hold \|\| T81 temper, plate \|\| -269 °C to 540 °C (-452 °F to 1004 °F) SR : T81 temper, plate \|\| tested at 100 °C (212 °F) \|\| 1x10³ h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 10 h SR : T81 temper, plate \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 0.1% total strain, T81 temper, plate \|\| tested at 100 °C (212 °F) \|\| 100 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T81 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T81 temper, plate \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 0.2% total strain, T81 temper, plate \|\| tested at 100 °C (212 °F) \|\| 100 h to 1x10⁴ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T81 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T81 temper, plate \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 0.5% total strain, T81 temper, plate \|\| tested at 100 °C (212 °F) \|\| 1x10³ h to 1x10⁵ h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1 h CRS : 0.5% total strain, T81 temper, plate \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 1% total strain, T81 temper, plate \|\| tested at 100 °C (212 °F) \|\| 1x10³ h to 1x10⁵ h CRS : 1% total strain, T81 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h CRS : 1% total strain, T81 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h CRS : 1% total strain, T81 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h CRS : 1% total strain, T81 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h CRS : 1% total strain, T81 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1 h CRS : 1% total strain, T81 temper, plate \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) IC : tested at 100 °C (212 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 121 °C (250 °F), total strain, T81 temper, plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 temper, plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 temper, plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 temper, plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 300,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 temper, plate \|\| 1,000,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 30,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 temper, plate \|\| 100,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 288 °C (550 °F), total strain, T81 temper, plate \|\| 10,000 h \|\| 0 to 5x10^-³ mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 temper, plate \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), total strain, T81 temper, plate \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 343 °C (650 °F), total strain, T81 temper, plate \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 temper, plate \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 temper, plate \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 temper, plate \|\| 10 h \|\| 0 to 0.01 mm/mm strain
2024 (UNS A92024) (WNr 3.1355) (ISO/EN/DIN AlCu4Mg1/AlCu4Mg1.5/AlCuMg2) (JIS A2024) (AFNOR A-U4G1) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -273 °C to 482 °C (-460 °F to 900 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -273 °C to 482 °C (-460 °F to 900 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -273 °C to 482 °C (-460 °F to 900 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| T4 temper, as-received \|\| -269 °C to 427 °C (-452 °F to 800 °F) TC : solid \|\| T4 temper, annealed \|\| -157 °C to 427 °C (-251 °F to 800 °F) TC : solid \|\| T8xx temper \|\| -185 °C to 316 °C (-301 °F to 600 °F) TD : solid \|\| T4 temper, as-received \|\| -185 °C to 430 °C (-301 °F to 806 °F) TD : solid \|\| T4 temper, annealed \|\| -157 °C to 427 °C (-251 °F to 800 °F) TD : solid \|\| T8xx temper \|\| -185 °C to 316 °C (-301 °F to 600 °F) SH : solid \|\| -251 °C to 427 °C (-420 °F to 801 °F) SSC : T6 temper, sheet \|\| tested at 232 °C (450 °F), 5x10^-⁵/s, held for 100 s \|\| 0 to 0.39 mm/mm strain SSC : T6 temper, sheet \|\| tested at 232 °C (450 °F), 1/s, held for 100 s \|\| 0 to 0.39 mm/mm strain SSC : T6 temper, sheet \|\| tested at 316 °C (600 °F), 1/s, held for 100 s \|\| 0 to 0.3 mm/mm strain SSC : T6 temper, sheet \|\| tested at 316 °C (600 °F), 5x10^-⁵/s, held for 100 s \|\| 0 to 0.2 mm/mm strain SSC : T3 temper, sheet \|\| tested at 27 °C (80 °F), 1/s, held for 1800 s \|\| 0 to 0.12 mm/mm strain SSC : T3 temper, sheet \|\| tested at 232 °C (450 °F), 1/s, held 1800 s \|\| 0 to 0.5 mm/mm strain SSC : T3 temper, sheet \|\| tested at 316 °C (600 °F), 1/s, held 1800 s \|\| 0 to 0.5 mm/mm strain SSC : T3 temper, sheet \|\| tested at 149 °C (300 °F), 1/s, held 1800 s \|\| 0 to 0.1 mm/mm strain SSC : T3 temper, sheet \|\| tested at 149 °C (300 °F), 1/s, held 10 s \|\| 0 to 0.95 mm/mm strain SSC : T3 temper, sheet \|\| tested at 427 °C (800 °F), 1/s, held 1800 s \|\| 0 to 0.72 mm/mm strain SSC : T3 temper, sheet \|\| tested at 232 °C (450 °F), 1/s, held 10 s \|\| 0 to 0.5 mm/mm strain SSC : T3 temper, sheet \|\| tested at 316 °C (600 °F), 1/s, held 10 s \|\| 0 to 0.25 mm/mm strain SSC : T86 temper \|\| tested at 20 °C (68 °F), 3.3x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : T86 temper \|\| tested at -78 °C (-109 °F), 3.3x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : T86 temper \|\| tested at -197.1 °C (-322.9 °F), 3.3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : T86 temper \|\| tested at -253.1 °C (-423.7 °F), 3.3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain SSC : T3 temper, plate \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.15 mm/mm strain SSC : T36 temper, plate, transverse \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : T36 temper, plate, longitudinal \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : T351 temper \|\| tested at 20 °C (68 °F), 0.0022/s \|\| 0 to 0.5 mm/mm strain SSC : O temper \|\| tested at 21 °C (70 °F), static test, unknown strain rate \|\| 0 to 0.94 mm/mm strain SSC : O temper \|\| tested at 93 °C (200 °F), static test, unknown strain rate \|\| 0 to 0.65 mm/mm strain SSC : O temper \|\| tested at 232 °C (450 °F), static test, unknown strain rate \|\| 0 to 0.38 mm/mm strain SSC : O temper \|\| tested at 316 °C (600 °F), static test, unknown strain rate \|\| 0 to 0.29 mm/mm strain SSCC : O temper, 0.001/s \|\| tested at 145 °C (293 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.001/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.001/s \|\| tested at 365 °C (689 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.001/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.01/s \|\| tested at 145 °C (293 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.01/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.01/s \|\| tested at 365 °C (689 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.01/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.1/s \|\| tested at 145 °C (293 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.1/s \|\| tested at 250 °C (482 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.1/s \|\| tested at 365 °C (689 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 0.1/s \|\| tested at 425 °C (797 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 1/s \|\| tested at 365 °C (689 °F) \|\| 0 to 0.6 mm/mm strain SSCC : O temper, 12.5/s \|\| tested at 365 °C (689 °F) \|\| 0 to 0.6 mm/mm strain UTS : 10,000 h hold \|\| O temper, extrusions \|\| 20 °C to 538 °C (68 °F to 1000 °F) UTS : 10,000 h hold \|\| T3 temper \|\| -253 °C to 540 °C (-424 °F to 1004 °F) UTS : 10,000 h hold \|\| T4 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T6 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T36 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T86 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10,000 h hold \|\| O temper, extrusions \|\| 20 °C to 538 °C (68 °F to 1000 °F) YS : 10,000 h hold \|\| T3 temper \|\| -253 °C to 540 °C (-424 °F to 1004 °F) YS : 10,000 h hold \|\| T4 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T6 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T36 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T86 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) SR : T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T3 temper \|\| tested at 177 °C (350 °F) \|\| 100 h to 1x10⁵ h SR : T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T3 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T3 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T3 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T3 temper \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) SR : T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T81 & T85 tempers, less than 38.1 mm (1.5 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T852 temper, forgings 25.4 mm (1 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T852 temper, forgings greater than 6.35 mm (0.25 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T852 temper, forgings greater than 6.35 mm (0.25 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T852 temper, forgings greater than 6.35 mm (0.25 inch) thick \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) SR : T86 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T86 temper \|\| Master curve (LMP) \|\| 25 °C to 316 °C (77 °F to 601 °F) FEN : T3 temper, sheet \|\| tested at 20 °C (68 °F), R = -1, axial, equivalent strain range \|\| 3x10³ cycles to 1x10⁸ cycles FEN : T4 temper, rod & bar \|\| tested at 20 °C (68 °F), R = -1, axial, equivalent strain range \|\| 10 cycles to 1x10⁷ cycles FSN : T4 temper \|\| tested at -253.1 °C (-423.7 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T4 temper \|\| tested at -196.1 °C (-321.1 °F), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 6x10⁷ cycles FSN : T4 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10³ cycles to 1x10⁸ cycles FSN : T4 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T4 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T4 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles FSN : T4 temper \|\| tested at 316 °C (600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T351 temper \|\| tested at 20 °C (68 °F) in air, R = -1, ultrasonic, maximum stress \|\| 1x10⁵ cycles to 2x10⁹ cycles FSN : T351 temper \|\| tested at 20 °C (68 °F) in distilled water, R = -1, ultrasonic, maximum stress \|\| 3x10⁴ cycles to 1x10⁸ cycles CRS : 0.1% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T3 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T3 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T3 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T3 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.2% total strain, T3 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1 h CRS : 0.2% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T3 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T3 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T3 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T3 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 10 h CRS : 0.5% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T3 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T3 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T3 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T3 temper \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) CRS : 1% total strain, T3 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T3 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T3 temper \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T3 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T3 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T3 temper \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) CRS : 0.1% total strain, T4 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T4 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1 h CRS : 0.1% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T4 temper \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) CRS : 0.2% total strain, T4 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T4 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T4 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T4 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T4 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T4 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T4 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T4 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T4 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T4 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1 h CRS : 0.1% total strain, T6 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T6 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.2% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T6 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T6 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T6 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T6 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T6 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T6 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T6 temper \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T81 & T85 tempers \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T81 & T85 tempers \|\| Master curve (LMP) \|\| 149 °C to 372 °C (300 °F to 701 °F) CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T81 & T85 tempers \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T81 & T85 tempers \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T81 & T85 tempers \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T81 & T85 tempers \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 1% total strain, T81 & T85 tempers \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T81 & T85 tempers \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T81 & T85 tempers \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) CRS : 0.1% total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 0.2% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 0.5% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| Master curve (LMP) \|\| 149 °C to 205 °C (300 °F to 401 °F) CRS : 0.1% total strain, T86 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T86 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T86 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T86 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T86 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T86 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T86 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T86 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T86 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T86 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T86 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T3 temper \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T3 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T3 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T3 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T3 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T3 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T4 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T6 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T6 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T6 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T6 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T6 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T81 & T85 tempers \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T81 & T85 tempers \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 & T85 tempers \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 & T85 tempers \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 & T85 tempers \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 & T85 tempers \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 371 °C (700 °F), total strain, T81 & T85 tempers \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 25.4 mm (1 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 3,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 30 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 300 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T852 temper, forgings, 76.2 mm (3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T86 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T86 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T86 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T86 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T86 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T86 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T86 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T86 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain NE : solid \|\| as-received & polished samples \|\| -218 °C to 549 °C (-361 °F to 1020 °F) RHO : solid \|\| O temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| T4 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| T6 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) RHO : solid \|\| T86 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| O temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| T4 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| T6 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) SIGMA : solid \|\| T86 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F)
2025 (UNS A92025) (JIS A2025FD/A2025FH) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -73 °C to 316 °C (-100 °F to 600 °F) DLL : solid \|\| -73 °C to 316 °C (-100 °F to 600 °F) MTE : solid \|\| -73 °C to 316 °C (-100 °F to 600 °F) CTE : solid \|\| -73 °C to 316 °C (-100 °F to 600 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) SSC : T6 temper, unknown strain rate \|\| tested at 20 °C (68 °F) \|\| 0 to 0.1 mm/mm strain UTS : T6 temper \|\| longitudinal \|\| -51 °C to 121 °C (-60 °F to 250 °F) YS : T6 temper \|\| longitudinal \|\| -51 °C to 121 °C (-60 °F to 250 °F) FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁷ cycles
2036 (UNS A92036) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) DLL : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) MTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) CTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F)
2048 (UNS A92048) (some datasets are for temperatures below 20 °C)	D : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) DLL : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) MTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) CTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) E : T851 temper, plate, in tension \|\| longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : T851 temper, plate, in tension \|\| transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : T851 temper, plate, in tension \|\| average \|\| 20 °C to 260 °C (68 °F to 500 °F) E : T851 temper, plate, in compression \|\| longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) E : T851 temper, plate, in compression \|\| transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) E : T851 temper, plate, in compression \|\| average \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : T851 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : T851 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : T851 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : T851 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : T851 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : T851 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : T851 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : T851 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) SR : T851 temper, plate, longitudinal \|\| tested at 121 °C (250 °F) \|\| 10 h to 1,000 h SR : T851 temper, plate, longitudinal \|\| tested at 177 °C (350 °F) \|\| 10 h to 1,000 h SR : T851 temper, plate, longitudinal \|\| tested at 260 °C (500 °F) \|\| 10 h to 1,000 h SR : T851 temper, plate, longitudinal \|\| Master curve (LMP) \|\| 121 °C to 261 °C (250 °F to 502 °F) FSN : T851 temper, plate, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T851 temper, plate, smooth \|\| tested at 121 °C (250 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T851 temper, plate, smooth \|\| tested at 177 °C (350 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T851 temper, plate, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T851 temper, plate, notched \|\| tested at 121 °C (250 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T851 temper, plate, notched \|\| tested at 177 °C (350 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, T851 temper, plate, longitudinal \|\| tested at 427 °C (800 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, T851 temper, plate, longitudinal \|\| tested at 538 °C (1000 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, T851 temper, plate, longitudinal \|\| tested at 649 °C (1200 °F) \|\| 10 h to 1,000 h
2090 (UNS A92090) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| T81 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) TC : solid \|\| unknown condition \|\| -193 °C to 258 °C (-316 °F to 496 °F) TD : solid \|\| T81 temper \|\| -269 °C to 20 °C (-452 °F to 68 °F) TD : solid \|\| unknown condition \|\| -193 °C to 258 °C (-316 °F to 496 °F) SH : solid \|\| -150 °C to 325 °C (-238 °F to 617 °F) SSC : T4 temper \|\| tested at 25 °C (77 °F), 8x10^-⁴/s \|\| 0 to 0.175 mm/mm strain SSC : T4 temper \|\| tested at -196.1 °C (-321.1 °F), 8x10^-⁴/s \|\| 0 to 0.25 mm/mm strain SSC : T4 temper \|\| tested at -269.1 °C (-452.5 °F), 8x10^-⁴/s \|\| 0 to 0.225 mm/mm strain SSC : T81 temper \|\| tested at 25 °C (77 °F), 8x10^-⁴/s \|\| 0 to 0.75 mm/mm strain SSC : T81 temper \|\| tested at -196.1 °C (-321.1 °F), 8x10^-⁴/s \|\| 0 to 0.125 mm/mm strain SSC : T81 temper \|\| tested at -269.1 °C (-452.5 °F), 8x10^-⁴/s \|\| 0 to 0.175 mm/mm strain UTS : plate, T4 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F) UTS : plate, T8xxx tempers \|\| longitudinal \|\| -269 °C to 260 °C (-452 °F to 500 °F) UTS : plate, T8xxx tempers \|\| transverse \|\| -269 °C to 260 °C (-452 °F to 500 °F) UTS : plate, T8xxx tempers \|\| 45 degrees \|\| -269 °C to 22 °C (-452 °F to 72 °F) UTS : plate, T81 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F) YS : plate, T4 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F) YS : plate, T8xxx tempers \|\| longitudinal \|\| -269 °C to 260 °C (-452 °F to 500 °F) YS : plate, T8xxx tempers \|\| transverse \|\| -269 °C to 260 °C (-452 °F to 500 °F) YS : plate, T8xxx tempers \|\| 45 degrees \|\| -269 °C to 22 °C (-452 °F to 72 °F) YS : plate, T81 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F) %El : plate, T4 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F) %El : plate, T8xxx tempers \|\| longitudinal \|\| -269 °C to 260 °C (-452 °F to 500 °F) %El : plate, T8xxx tempers \|\| transverse \|\| -269 °C to 260 °C (-452 °F to 500 °F) %El : plate, T8xxx tempers \|\| 45 degrees \|\| -269 °C to 22 °C (-452 °F to 72 °F) %El : plate, T81 temper \|\| longitudinal \|\| -269 °C to 25 °C (-452 °F to 77 °F)

2117 (UNS A92117) (WNr 3.1325) (ISO/EN/DIN AlCu2.5Mg/AlCu2.5Mg0.5/AlCuMg0.5/AlCuMg1) (JIS A2017P) (AFNOR A-U2G) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) UTS : T4 temper \|\| 0.5 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : T4 temper \|\| 10 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : T4 temper \|\| 100 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : T4 temper \|\| 1000 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : T4 temper \|\| 10,000 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : T4 temper \|\| 0.5 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : T4 temper \|\| 10 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : T4 temper \|\| 100 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : T4 temper \|\| 1000 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : T4 temper \|\| 10,000 h hold \|\| -253 °C to 370 °C (-424 °F to 698 °F) SR : T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 149 °C (300 °F) \|\| 4.5 h to 820 h SR : T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 232 °C (450 °F) \|\| 1.75 h to 1,000 h SR : T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 316 °C (600 °F) \|\| 1.16 h to 1,000 h SR : T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) CRS : 0.5% plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 232 °C (450 °F) \|\| 1 h to 100 h CRS : 1% plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 232 °C (450 °F) \|\| 20 h to 100 h CRS : 1.5% plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 232 °C (450 °F) \|\| 20 h to 100 h CRS : 2% plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 149 °C (300 °F) \|\| 1 h to 490 h CRS : 3% plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| tested at 149 °C (300 °F) \|\| 0.3 h to 570 h IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 1 h \|\| 0 to 0.3 mm/mm strain IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 3 h \|\| 0 to 0.3 mm/mm strain IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 10 h \|\| 0 to 0.3 mm/mm strain IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 30 h \|\| 0 to 0.3 mm/mm strain IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 100 h \|\| 0 to 0.3 mm/mm strain IC : tested at 149 °C (300 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 300 h \|\| 0 to 0.3 mm/mm strain IC : tested at 232 °C (450 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 30 h \|\| 0 to 0.15 mm/mm strain IC : tested at 232 °C (450 °F), plastic strain, T4 temper, 9.52 mm (0.375 inch) diameter rivet wire \|\| 100 h \|\| 0 to 0.15 mm/mm strain
2124 (UNS A92124) (WNr 3.1355) (ISO/EN/DIN AlCu4Mg1/AlCuMg2) (JIS 2024P) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| T351 temper \|\| 20 °C to 300 °C (68 °F to 572 °F) TD : solid \|\| T351 temper \|\| 20 °C to 300 °C (68 °F to 572 °F) SH : solid \|\| T351 temper \|\| 20 °C to 300 °C (68 °F to 572 °F) UTS : 10,000 h hold \|\| T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : 10,000 h hold \|\| T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : 10,000 h hold \|\| T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) UTS : 10,000 h hold \|\| T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : 10,000 h hold \|\| T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : 10,000 h hold \|\| T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : 10,000 h hold \|\| T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) YS : 10,000 h hold \|\| T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 20 °C to 540 °C (68 °F to 1004 °F) SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) thick \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.2% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 10 h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁴ h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 38.1 mm to 50.8 mm (1.5 inch to 2 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 76.2 mm to 102 mm (3 inch to 4 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 24 °C (75 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 100 °C (212 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 177 °C (350 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 232 °C (450 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 260 °C (500 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T851 temper, plate, 102 mm to 127 mm (4 inch to 5 inch) \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain
2198 (UNS A92198) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D* : solid \|\| room temperature value SSC : T3 temper \|\| tested at 20 °C (68 °F), unknown strain rate \|\| 0 to 0.133 mm/mm strain SSC : T8 temper, base material \|\| tested at -183.1 °C (-297.7 °F), 0.001/s \|\| 0 to 0.116 mm/mm strain SSC : T8 temper, base material \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.75 mm/mm strain SSC : T8 temper, base material \|\| tested at 25 °C (77 °F), 0.001/s \|\| 0 to 0.57 mm/mm strain SSC : T8 temper, friction stir weld at 400 rpm \|\| tested at -196.1 °C (-321.1 °F), 0.001/s \|\| 0 to 0.14 mm/mm strain SSC : T8 temper, friction stir weld at 400 rpm \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.12 mm/mm strain SSC : T8 temper, friction stir weld at 400 rpm \|\| tested at 25 °C (77 °F), 0.001/s \|\| 0 to 0.7 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at -253.1 °C (-423.7 °F), 0.001/s \|\| 0 to 0.13 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at -196.1 °C (-321.1 °F), 0.001/s \|\| 0 to 0.12 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.1 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at 25 °C (77 °F), 0.001/s \|\| 0 to 0.66 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at -253.1 °C (-423.7 °F), 0.001/s \|\| 0 to 0.15 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at -196.1 °C (-321.1 °F), 0.001/s \|\| 0 to 0.11 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at -100 °C (-148 °F), 0.001/s \|\| 0 to 0.11 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at 25 °C (77 °F), 0.001/s \|\| 0 to 0.7 mm/mm strain UTS : T8 temper \|\| base material \|\| -183 °C to 25 °C (-298 °F to 77 °F) UTS : T8 temper \|\| friction stir weld at 400 rpm \|\| -196 °C to 25 °C (-321 °F to 77 °F) UTS : T8 temper \|\| friction stir weld at 600 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F) UTS : T8 temper \|\| friction stir weld at 800 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : T8 temper \|\| base material \|\| -183 °C to 25 °C (-298 °F to 77 °F) YS : T8 temper \|\| friction stir weld at 400 rpm \|\| -196 °C to 25 °C (-321 °F to 77 °F) YS : T8 temper \|\| friction stir weld at 600 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : T8 temper \|\| friction stir weld at 800 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : T8 temper \|\| base material \|\| -183 °C to 25 °C (-298 °F to 77 °F) %El : T8 temper \|\| friction stir weld at 400 rpm \|\| -196 °C to 25 °C (-321 °F to 77 °F) %El : T8 temper \|\| friction stir weld at 600 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F) %El : T8 temper \|\| friction stir weld at 800 rpm \|\| -253 °C to 25 °C (-424 °F to 77 °F)

2214 (UNS A92214) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) D : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) DLL : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) DLL : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) MTE : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) MTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) CTE : solid \|\| -218 °C to 316 °C (-361 °F to 600 °F) CTE : liquid \|\| 649 °C to 1027 °C (1200 °F to 1880 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) SH : solid \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : T351 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) UTS : T351 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : T351 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YS : T351 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : T351 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) YSC : T351 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : T351 temper, plate \|\| 0.5 h hold, longitudinal \|\| 20 °C to 260 °C (68 °F to 500 °F) %El : T351 temper, plate \|\| 0.5 h hold, transverse \|\| 20 °C to 260 °C (68 °F to 500 °F) SR : T351 temper, plate \|\| tested at 121 °C (250 °F) \|\| 10 h to 1,000 h SR : T351 temper, plate \|\| tested at 177 °C (350 °F) \|\| 10 h to 1,000 h SR : T351 temper, plate \|\| tested at 260 °C (500 °F) \|\| 10 h to 1,000 h SR : T351 temper, plate \|\| Master curve (LMP) \|\| 121 °C to 261 °C (250 °F to 502 °F) FSN : T351 temper, plate, smooth \|\| tested at 20 °C (68 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T351 temper, plate, smooth \|\| tested at 121 °C (250 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T351 temper, plate, smooth \|\| tested at 177 °C (350 °F), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T351 temper, plate, notched \|\| tested at 20 °C (68 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T351 temper, plate, notched \|\| tested at 121 °C (250 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T351 temper, plate, notched \|\| tested at 177 °C (350 °F), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles CRS : 0.2% plastic strain, T351 temper, plate \|\| tested at 121 °C (250 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, T351 temper, plate \|\| tested at 177 °C (350 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, T351 temper, plate \|\| tested at 260 °C (500 °F) \|\| 10 h to 1,000 h CRS : 0.2% plastic strain, T351 temper, plate \|\| Master curve (LMP) \|\| 121 °C to 261 °C (250 °F to 502 °F)
2218 (UNS A92218) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) DLL : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) MTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) CTE : solid \|\| -50 °C to 300 °C (-58 °F to 572 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) UTS : T61 temper \|\| 0.5 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : T61 temper \|\| 10 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : T61 temper \|\| 100 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : T61 temper \|\| 1000 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : T61 temper \|\| 10,000 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : T61 temper \|\| 0.5 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : T61 temper \|\| 10 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : T61 temper \|\| 100 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : T61 temper \|\| 1000 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : T61 temper \|\| 10,000 h hold \|\| -196 °C to 370 °C (-321 °F to 698 °F) SR : T61 temper \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T61 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T61 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T61 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h SR : T61 temper \|\| Master curve (LMP) \|\| 100 °C to 316 °C (212 °F to 601 °F) FSN : T61 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 149 °C (300 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 204 °C (400 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁶ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 260 °C (500 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T61 temper \|\| tested at 316 °C (600 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁵ cycles to 1x10⁸ cycles CRS : 0.1% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.1% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 100 h CRS : 0.1% total strain, T61 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 10 h CRS : 0.2% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.2% total strain, T61 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 0.5% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 0.5% total strain, T61 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h CRS : 1% total strain, T61 temper \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T61 temper \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h CRS : 1% total strain, T61 temper \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 100 h IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 149 °C (300 °F), total strain, T61 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain IC : tested at 204 °C (400 °F), total strain, T61 temper \|\| 1,000 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T61 temper \|\| 0.1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T61 temper \|\| 1 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T61 temper \|\| 10 h \|\| 0 to 0.01 mm/mm strain IC : tested at 316 °C (600 °F), total strain, T61 temper \|\| 100 h \|\| 0 to 0.01 mm/mm strain
2219 (UNS A92219) (ISO/EN/DIN AlCu6Mn) (some datasets are for temperatures below 20 °C) (some datasets are for temperatures at 200 K and lower) (some datasets are for temperatures at 80 K and lower) (some datasets are for temperatures at 20 K and lower)	D : solid \|\| -251 °C to 538 °C (-420 °F to 1000 °F) DLL : solid \|\| -251 °C to 538 °C (-420 °F to 1000 °F) MTE : solid \|\| -251 °C to 538 °C (-420 °F to 1000 °F) CTE : solid \|\| -251 °C to 538 °C (-420 °F to 1000 °F) E : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) G : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) v : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) K : solid \|\| -273 °C to 500 °C (-460 °F to 932 °F) TC : solid \|\| T81 temper \|\| -225 °C to 300 °C (-373 °F to 572 °F) TC : solid \|\| T852 temper \|\| -273 °C to 560 °C (-460 °F to 1040 °F) TC : liquid \|\| 652 °C to 727 °C (1205 °F to 1341 °F) TD : solid \|\| T81 temper \|\| -225 °C to 300 °C (-373 °F to 572 °F) TD : solid \|\| T852 temper \|\| -251 °C to 538 °C (-420 °F to 1000 °F) SH : solid \|\| T852 temper \|\| -272 °C to 627 °C (-458 °F to 1161 °F) SSC : T852 temper \|\| tested at 20 °C (68 °F), unknown strain rate, longitudinal \|\| 0 to 0.8 mm/mm strain SSC : T852 temper \|\| tested at 20 °C (68 °F), long transverse, unknown strain rate \|\| 0 to 0.7 mm/mm strain SSC : T852 temper \|\| tested at 20 °C (68 °F), short transverse, unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at 20 °C (68 °F), unknown strain rate, longitudinal \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, longitudinal \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : T62 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, longitudinal \|\| 0 to 0.16 mm/mm strain SSC : T62 temper \|\| tested at 20 °C (68 °F), unknown strain rate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, transverse \|\| 0 to 0.85 mm/mm strain SSC : T62 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, transverse \|\| 0 to 0.12 mm/mm strain SSC : T81 temper \|\| tested at 20 °C (68 °F), unknown strain rate, longitudinal \|\| 0 to 0.6 mm/mm strain SSC : T81 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T81 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : T81 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, longitudinal \|\| 0 to 0.11 mm/mm strain SSC : T81 temper \|\| tested at 20 °C (68 °F), unknown strain rate, transverse \|\| 0 to 0.7 mm/mm strain SSC : T81 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, transverse \|\| 0 to 0.7 mm/mm strain SSC : T81 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, transverse \|\| 0 to 0.75 mm/mm strain SSC : T81 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, transverse \|\| 0 to 0.11 mm/mm strain SSC : T87 temper \|\| tested at 20 °C (68 °F), unknown strain rate, longitudinal \|\| 0 to 0.7 mm/mm strain SSC : T87 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T87 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T87 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, longitudinal \|\| 0 to 0.11 mm/mm strain SSC : T87 temper \|\| tested at 20 °C (68 °F), unknown strain rate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T87 temper \|\| tested at -79 °C (-110 °F), unknown strain rate, transverse \|\| 0 to 0.7 mm/mm strain SSC : T87 temper \|\| tested at -195.6 °C (-320 °F), unknown strain rate, transverse \|\| 0 to 0.8 mm/mm strain SSC : T87 temper \|\| tested at -252.7 °C (-422.9 °F), unknown strain rate, transverse \|\| 0 to 0.11 mm/mm strain SSC : T87 temper, friction stir weld \|\| tested at 25 °C (77 °F), unknown strain rate \|\| 0 to 0.56 mm/mm strain SSC : T87 temper, friction stir weld \|\| tested at -196.1 °C (-321.1 °F), unknown strain rate \|\| 0 to 0.92 mm/mm strain SSC : T87 temper, friction stir weld \|\| tested at -253.1 °C (-423.7 °F), unknown strain rate \|\| 0 to 0.96 mm/mm strain UTS : 10,000 h hold \|\| O temper \|\| 20 °C to 370 °C (68 °F to 698 °F) UTS : 10,000 h hold \|\| T37 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10,000 h hold \|\| T851 temper \|\| -269 °C to 370 °C (-452 °F to 698 °F) UTS : 10,000 h hold \|\| T81 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : 10,000 h hold \|\| T8511 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) UTS : 10,000 h hold \|\| T62 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) UTS : friction stir weld \|\| T87 temper \|\| -253 °C to 25 °C (-424 °F to 77 °F) YS : 10,000 h hold \|\| O temper \|\| 20 °C to 370 °C (68 °F to 698 °F) YS : 10,000 h hold \|\| T37 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10,000 h hold \|\| T851 temper \|\| -269 °C to 370 °C (-452 °F to 698 °F) YS : 10,000 h hold \|\| T81 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : 10,000 h hold \|\| T8511 temper \|\| -196 °C to 370 °C (-321 °F to 698 °F) YS : 10,000 h hold \|\| T62 temper \|\| -253 °C to 370 °C (-424 °F to 698 °F) YS : friction stir weld \|\| T87 temper \|\| -253 °C to 25 °C (-424 °F to 77 °F) YSC : sheet & plate \|\| T62 temper \|\| -203 °C to 376 °C (-334 °F to 709 °F) %El : friction stir weld \|\| T87 temper \|\| -253 °C to 25 °C (-424 °F to 77 °F) SR : O temper \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 288 °C (550 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T81 temper, sheet \|\| Master curve (LMP) \|\| 149 °C to 372 °C (300 °F to 701 °F) SR : T37 temper, sheet longitudinal to rolling direction \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, sheet longitudinal to rolling direction \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, sheet longitudinal to rolling direction \|\| Master curve (LMP) \|\| 260 °C to 316 °C (500 °F to 601 °F) SR : T37 temper, plate longitudinal to rolling direction \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, plate longitudinal to rolling direction \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, plate longitudinal to rolling direction \|\| tested at 288 °C (550 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, plate longitudinal to rolling direction \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, plate longitudinal to rolling direction \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T37 temper, plate longitudinal to rolling direction \|\| Master curve (LMP) \|\| 232 °C to 372 °C (449 °F to 701 °F) SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 18 h at 191 °C (375 °F) \|\| Master curve (LMP) \|\| 24 °C to 372 °C (75 °F to 701 °F) SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T6 temper, forgings aged 16 h at 216 °C (420 °F) \|\| Master curve (LMP) \|\| 24 °C to 372 °C (75 °F to 701 °F) SR : T62 temper, sheet \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 10 h SR : T62 temper, sheet \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 288 °C (550 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, sheet \|\| Master curve (LMP) \|\| 100 °C to 372 °C (212 °F to 701 °F) SR : T62 temper, plate \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 10 h SR : T62 temper, plate \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T62 temper, plate \|\| Master curve (LMP) \|\| 24 °C to 372 °C (75 °F to 701 °F) SR : T851 temper, plate \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T851 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate \|\| tested at 177 °C (350 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1x10⁵ h SR : T851 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1x10⁴ h SR : T851 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1x10⁴ h SR : T851 temper, plate \|\| Master curve (LMP) \|\| 24 °C to 372 °C (75 °F to 701 °F) SR : T8511 temper, extrusions \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T8511 temper, extrusions \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T8511 temper, extrusions \|\| Master curve (LMP) \|\| 204 °C to 261 °C (399 °F to 502 °F) SR : T852 temper, forgings \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T852 temper, forgings \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T852 temper, forgings \|\| Master curve (LMP) \|\| 204 °C to 261 °C (399 °F to 502 °F) SR : T87 temper, sheet \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 288 °C (550 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, sheet \|\| Master curve (LMP) \|\| 149 °C to 316 °C (300 °F to 601 °F) SR : T87 temper, plate \|\| tested at 24 °C (75 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 100 °C (212 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 149 °C (300 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 204 °C (400 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 232 °C (450 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 260 °C (500 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 316 °C (600 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| tested at 371 °C (700 °F) \|\| 0.1 h to 1,000 h SR : T87 temper, plate \|\| Master curve (LMP) \|\| 24 °C to 316 °C (75 °F to 601 °F) FEN : T851 temper \|\| tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range \|\| 180 cycles to 7.1x10⁴ cycles FEN : T851 temper \|\| tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range \|\| 90 cycles to 2x10⁵ cycles FEN : T851 temper \|\| tested at 20 °C (68 °F), R = -1, axial, total strain range \|\| 70 cycles to 6.9x10⁴ cycles FSN : T62 temper \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : T62 temper \|\| tested at -195.6 °C (-320 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 800 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 20 °C (68 °F), R = -1, TIG welded, axial, maximum stress \|\| 800 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at -195.6 °C (-320 °F), R = -1, TIG welded, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, TIG welded, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 20 °C (68 °F), R = -1, axial, maximum stress \|\| 6.1x10³ cycles to 1x10⁷ cycles FSN : T87 temper \|\| tested at -195.6 °C (-320 °F), R = -1, axial, maximum stress \|\| 600 cycles to 6x10⁴ cycles FSN : T87 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 20 °C (68 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T87 temper \|\| tested at -195.6 °C (-320 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 1x10⁷ cycles FSN : T87 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 20 °C (68 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T87 temper \|\| tested at -195.6 °C (-320 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : T87 temper \|\| tested at -252.7 °C (-422.9 °F), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T6 temper \|\| tested at 20 °C (68 °F), R = -1, rotating beam, maximum stress \|\| 1x10⁴ cycles to 1x10⁸ cycles FSN : T6 temper \|\|&en

Dataset listing by material