New and revised materials and properties in MPDB v9.97 as compared to v9.95

Key to property symbols (number of datasets):

DLL = Linear thermal expansion (ΔL/L)	MTE = Mean coefficient of thermal expansion	CTE = Coefficient of thermal expansion	D = Density	AV = Apparent viscosity
TC = Thermal conductivity	SH = Specific heat	HC = Heat capacity	TD = Thermal diffusivity	SV = Specific volume
RHO = Electrical resistivity	SIGMA = Electrical conductivity	SRHO = Surface electrical resistivity	Vis = Viscosity	FS = Flexural strength
E = Elastic/Young's modulus	G = Shear modulus	v = Poisson's ratio	K = Bulk modulus	FM = Flexural modulus
SSC = True stress-strain curve (tension)	SSCC = True stress-strain curve (compression)	HE = Hemispherical total emissivity	NE = Normal total emissivity	ESSC = Engineering stress-strain curve (tension)
UTS = Tensile strength	YS = Yield strength (tension)	UCS = Compressive strength	YSC = Yield strength (compression)	%El = Elongation
FSN = Fatigue S-N curve	FEN = Fatigue ε-N curve	SR = Stress rupture	CRS = Creep strength	ESSCC = Engineering stress-strain curve (compression)
RPB = Relative permeability	AP = Absolute permeability	BH = B-H curve	HB = H-B curve	CRM = Creep modulus
DCRPT = Relative permittivity	DF = Dissipation factor	CL = Core loss	EP = Exciting Power	IC = Isochronous creep
RIW = Refractive index vs λ	RIT = Refractive index vs T	TWL = Transmission vs λ	ST = Surface tension	CRR = Stress vs Creep rate
S = Seebeck coefficient	VP = Vapor pressure

"(N)" indicates the data is new, "(R)" indicates the data has been revised, * indicates the data is the room temperature value only

21 new materials, 2314 new property sets, 2537 revised properties, and 332 new room temperature values

Aluminum alloys

2021	4032	6053	1060 (Revised)	1100 (Revised)
2011 (Revised)	2014 (Revised)	2017 (Revised)	2018 (Revised)	2020 (Revised)
2024 (Revised)	2117 (Revised)	2124 (Revised)	2218 (Revised)	2219 (Revised)
2618 (Revised)	3003 (Revised)	3004 (Revised)	5005 (Revised)	5050 (Revised)
5052 (Revised)	5056 (Revised)	5083 (Revised)	5086 (Revised)	5154 (Revised)
5356 (Revised)	5454 (Revised)	5456 (Revised)	6005 (Revised)	6061 (Revised)
6063 (Revised)	6066 (Revised)	6070 (Revised)	6101 (Revised)	6151 (Revised)
6201 (Revised)	6262 (Revised)	6351 (Revised)	6951 (Revised)	7005 (Revised)
7039 (Revised)	7049 (Revised)	7050 (Revised)	7075 (Revised)	7079 (Revised)
7175 (Revised)	7178 (Revised)	7475 (Revised)	8280 (Revised)	201.0 (Revised)
224.0 (Revised)	242.0 (Revised)	249.0 (Revised)	295.0 (Revised)	319.0 (Revised)
332.0 (Revised)	333.0 (Revised)	336.0 (Revised)	354.0 (Revised)	355.0 (Revised)
356.0 (Revised)	359.0 (Revised)	360.0 (Revised)	380.0 (Revised)	384.0 (Revised)
518.0 (Revised)	520.0 (Revised)	710.0 (Revised)	A206.0	A319
A240.0 (Revised)	A355.0 (Revised)	A356.0 (Revised)	A360.0 (Revised)	A380.0 (Revised)
B443.0 (Revised)	C355.0 (Revised)	Scalmalloy (Revised)

Cast irons

Ductile iron (EN-GJS 700-2) (3.7 C - 2 Si - 1.2 Cu - 0.3 Mn (wt %)) (Revised)	SAE J435 Grade 0030 (Revised)	White iron austenitic (1 C - 2.55 Si - 31 Cr - 15 Ni - 0.5 Mn - 1 Al (wt %)) (Revised)	White iron ferritic (2 C - 0.4 Si - 35 Cr - 0.4 Mn (wt %)) (Revised)	White iron ferritic (1 C - 0.7 Si - 34 Cr - 0.3 Mn (wt %)) (Revised)

Cobalt alloys

Haynes 25 (L-605) (Revised)	Haynes 188 (Revised)	Haynes Ultimet (Revised)	MP159	S-816
Stellite 21	X-40

Controlled expansion alloys

Inconel 783 (Revised)

Copper alloys

Cu - 8 Cr - 4 Nb (wt %)	Cu - 4 Cr - 2 Nb (wt %)	90 Cu - 10 Sn (wt %)	GRCop-84 (Revised)	NARloy-Z
UNS C11000 (ETP)	UNS C10100 (OFE)	UNS C10200 (OFHC/OF) (Revised)	UNS C14200	UNS C15100
UNS C18150	UNS C19000	UNS C23000	UNS C46400	UNS C63000
UNS C65500	UNS C70600	UNS C12200	UNS C87300 (Revised)	UNS C10800 (Revised)
UNS C51000 (Revised)	UNS C61300 (Revised)	UNS C61400 (Revised)	UNS C62400 (Revised)	UNS C26000 (Revised)
UNS C64700 (Revised)	UNS C65100 (Revised)	UNS C28000 (Revised)	UNS C69400 (Revised)	UNS C44400 (Revised)
UNS C71000 (Revised)	UNS C71500 (Revised)

Elements

Aluminum	Molybdenum (Revised)	Nickel	Tantalum (Revised)	Tungsten

Intermetallics

Ti - 46 Al - 2 W - 0.5 Si (at %) (ABB-2)

Iron alloys

19-9 DL	19-9 DX (Revised)	17-7 PH	17-4 PH (Revised)	16-25-6 (AISI 650)
17-22AS	17-22AV	52100	310	316
431	1010	1020	4340	1015 (Revised)
1040 (Revised)	302 (Revised)	304 (Revised)	305 (Revised)	4130 (Revised)
4140 (Revised)	A201 Grade B	A106 Grade B	API X80 pipeline steel (Revised)	ASME Grade P23/T23 (Revised)
ASME Grade T23 (Revised)	ASME P92 (9 Cr - 0.5 Mo - 2 W (wt %)) (Revised)	ASTM A213 / SA-387 (9 Cr - 1 Mo (wt %) or G91) (Revised)	ASTM A192	CA6NM (Revised)
410 Cb (New)	9 Cr - 1 Mo - V - Nb (wt %) (T91) (Revised)	Discaloy	DP 980 (Revised)	EOS StainlessSteel CX (Revised)
Ferrium C61 (AMS 6517) (Revised)	F82H (Revised)	H-46	H-40 (New)	Haynes Multimet (N-155)
HP 9-4-30	HR3C (Revised)	IN-519 (Revised)	Incoloy 800 (Revised)	Incoloy A-286 (Revised)
Incoloy 800H & 800HT (Revised)	316L	304L (Revised)	LZ50	Maraging 300 (C-type)
316NG	Ni-SPAN C alloy 902 (Low expansion 43-PH) (Revised)	Nitronic 40 (Revised)	P91 (9 Cr - 1 Mo (wt %)) (Revised)	S-590
S700	TRIP 700 (Revised)	UNS S44627 (E-BRITE)	XA704 (Revised)

Magnesium alloys

AZ31	AZ61	AZ63	AZ81	AZ92
ZK60

Nickel alloys

IN-792 5A (Revised)	IN-100 (Revised)	Incoloy 925	Inconel 601	Inconel 617
Inconel 625	Inconel 690	Inconel 706	Inconel 751 (Revised)	Inconel 700 (Revised)
Inconel 600 (Revised)	Inconel 718 (Revised)	Inconel 713C (Revised)	Inconel 713LC (Revised)	Inconel MA 754
Inconel MA 6000 (Revised)	Inconel X-750	LSHR disk alloy (Revised)	M-252 (Revised)	MAR-M200 (Revised)
MERL 76 (Revised)	Monel 400	Monel K-500	Nickel 200	Nickel 201
Nickel (commercially pure) (Revised)	Nickel TD	Nimonic 75	Nimonic 105 (Revised)	Nimonic 81 (Revised)
PM 1000	PWA 1480 (Revised)	Refractaloy 26 (GH2026) (New)	Udimet 500 (Revised)	Udimet D-979 (Revised)
Waspaloy (Revised)

Polyesters

Selectron 44 polyester (Revised)

Precious metal & Rare earth alloys

Pt - 3 Au - 0.5 Rh (wt %) (Revised)	Pt - 1 Au - 0.5 Rh (wt %) (Revised)	Pt - 3 Au (wt %) (Revised)	Pt - 1 Au (wt %) (Revised)	Pt - 0.5 Rh (wt %) (Revised)

Refractory metal alloys

W - 15 Mo (wt %) (Revised)

Zircaloy-2 (Revised)

Solders, Brazes, & Low melting alloys

63 Sn - 37 Pb (wt %) (Revised)

Titanium alloys

Ti - 4 Al - 4 Mn (wt %) (Revised)	Ti - 4 Al - 3 Mo - 1 V (wt %)	Ti - 8 Al - 2 Nb - 1 Mo - 1 V (wt %)	Ti - 6 Al - 2 Sn - 4 Zr - 2 Mo (wt %) (Revised)	Ti - 5 Al - 2.5 Sn (Grade 6)
Ti - 8 Al - 1 Ta (wt %) (Revised)	Ti - 6 Al - 4 V (Revised)	Ti - 7 Al - 12 Zr (wt %) (Revised)	Ti - 16 V - 2.5 Al (wt %) (Revised)	Ti Grade 2
Ti Grade 4 (Revised)	Ti-140A (Ti - 2 Cr - 2 Fe - 2 Mo (wt %)) (Revised)

Tool steels

H13 (Revised)

H11 (Revised)

m-PPE (modified polyphenylene ether)

XYRON 300H (New)	XYRON 400H (New)	XYRON 500H (New)	XYRON 600H (New)	XYRON 1000H (New)
XYRON 200H (New)	XYRON 1951J (New)	XYRON 540V (New)	XYRON 200V (New)	XYRON 640V (New)
XYRON 340V (New)	XYRON 240W (New)	XYRON 340W (New)	XYRON 540Z (New)	XYRON 440Z (New)
XYRON 340Z (New)	XYRON 644Z (New)	XYRON 240Z (New)

19-9 DL

    UTS    (N):    hot forged, 1 h at 1149 °C (2100 °F), air cooled, equalized at 649 °C (1200 °F), cold worked 12.5%, annealed 4 h at 649 °C (1200 °F), air cooled || 20 °C (68 °F) to 816 °C (1501 °F)
    UTS   (N*):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || room temperature value
    UTS   (N*):    hot-rolled, 1 h at 649 °C (1200 °F), worked 20% at 649 °C (1200 °F), 1 h at 649 °C (1200 °F) || room temperature value
    UTS   (N*):    as-rolled, stress relieved 1 h at 649 °C (1200 °F) || room temperature value
    UTS   (N*):    forged at 1149 °C (2100 °F), solution treated 2 h at 1177 °C (2150 °F), water quenched, worked at 899 °C (1650 °F) || room temperature value
    UTS   (N*):    forged disk, 1 h at 1149 °C (2100 °F), air cooled, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || room temperature value
    UTS   (N*):    forged disk, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || room temperature value
    UTS   (N*):    disk, forged at 1149 °C (2100 °F), 2 h at 1177 °C (2150 °F), water quenched, worked at 52 °C (125 °F), stress relieved 10 h at 649 °C (1200 °F), air cooled || room temperature value
    UTS   (N*):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || room temperature value
    YS    (N*):    hot-rolled, 1 h at 649 °C (1200 °F), worked 20% at 649 °C (1200 °F), 1 h at 649 °C (1200 °F) || room temperature value
    YS    (N*):    as-rolled, stress relieved 1 h at 649 °C (1200 °F) || room temperature value
    YS    (N*):    forged at 1149 °C (2100 °F), solution treated 2 h at 1177 °C (2150 °F), water quenched, worked at 899 °C (1650 °F) || room temperature value
    YS    (N*):    disk, forged at 1149 °C (2100 °F), 2 h at 1177 °C (2150 °F), water quenched, worked at 52 °C (125 °F), stress relieved 10 h at 649 °C (1200 °F), air cooled || room temperature value
    YS    (N*):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || room temperature value
    %El    (N):    hot forged, 1 h at 1149 °C (2100 °F), air cooled, equalized at 649 °C (1200 °F), cold worked 12.5%, annealed 4 h at 649 °C (1200 °F), air cooled || 20 °C (68 °F) to 816 °C (1501 °F)
    %El   (N*):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || room temperature value
    %El   (N*):    hot-rolled, 1 h at 649 °C (1200 °F), worked 20% at 649 °C (1200 °F), 1 h at 649 °C (1200 °F) || room temperature value
    %El   (N*):    as-rolled, stress relieved 1 h at 649 °C (1200 °F) || room temperature value
    %El   (N*):    forged at 1149 °C (2100 °F), solution treated 2 h at 1177 °C (2150 °F), water quenched, worked at 899 °C (1650 °F) || room temperature value
    %El   (N*):    forged disk, 1 h at 1149 °C (2100 °F), air cooled, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || room temperature value
    %El   (N*):    forged disk, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || room temperature value
    %El   (N*):    disk, forged at 1149 °C (2100 °F), 2 h at 1177 °C (2150 °F), water quenched, worked at 52 °C (125 °F), stress relieved 10 h at 649 °C (1200 °F), air cooled || room temperature value
    %El   (N*):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || room temperature value
    SR     (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), oil quenched, aged 50 h at 816 °C (1500 °F) || tested at 732 °C (1350 °F) || 37 h to 650 h
    SR     (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), oil quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 2 h to 1,000 h
    SR     (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), oil quenched, aged 50 h at 816 °C (1500 °F) || Master curve (LMP) || 23.7 h to 27.2 h
    SR     (N):    rolled bar stock, as-rolled 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 80 h to 650 h
    SR     (N):    wrought bar, 1 h at 1204 °C (2200 °F), water quenched, 4 h at 816 °C (1500 °F), furnace cool || tested at 499 °C (930 °F) || 185 h to 770 h
    SR     (N):    wrought bar, 1 h at 1204 °C (2200 °F), water quenched, 4 h at 816 °C (1500 °F), furnace cool || tested at 593 °C (1100 °F) || 63 h to 1,600 h
    SR     (N):    wrought bar, 1 h at 1204 °C (2200 °F), water quenched, 4 h at 816 °C (1500 °F), furnace cool || tested at 816 °C (1500 °F) || 6 h to 153 h
    SR     (N):    wrought bar, 1 h at 1204 °C (2200 °F), water quenched, 4 h at 816 °C (1500 °F), furnace cool || Master curve (LMP) || 22.6 h to 31.8 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, aged 2 h at 760 °C (1400 °F), air cooled || tested at 593 °C (1100 °F) || 300 h to 6,700 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, aged 2 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 45 h to 6,000 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, aged 2 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 29 h to 32.1 h
    SR     (N):    hot forged, 1 h at 1149 °C (2100 °F), air cooled, equalized at 649 °C (1200 °F), cold worked 12.5%, annealed 4 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 55 h to 380 h
    SR     (N):    hot forged, 1 h at 1149 °C (2100 °F), air cooled, equalized at 649 °C (1200 °F), cold worked 12.5%, annealed 4 h at 649 °C (1200 °F), air cooled || tested at 816 °C (1500 °F) || 20 h to 305 h
    SR     (N):    hot forged, 1 h at 1149 °C (2100 °F), air cooled, equalized at 649 °C (1200 °F), cold worked 12.5%, annealed 4 h at 649 °C (1200 °F), air cooled || Master curve (LMP) || 10.8 h to 13.6 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || tested at 593 °C (1100 °F) || 520 h to 6,000 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || tested at 649 °C (1200 °F) || 27 h to 6,300 h
    SR     (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || Master curve (LMP) || 17.9 h to 20.1 h
    SR     (N):    hot-rolled, 1 h at 649 °C (1200 °F), worked 20% at 649 °C (1200 °F), 1 h at 649 °C (1200 °F) || tested at 649 °C (1200 °F) || 35 h to 1,800 h
    SR     (N):    as-rolled, stress relieved 1 h at 649 °C (1200 °F) || tested at 649 °C (1200 °F) || 67 h to 1,200 h
    SR     (N):    forged at 1149 °C (2100 °F), solution treated 2 h at 1177 °C (2150 °F), water quenched, worked at 899 °C (1650 °F) || tested at 649 °C (1200 °F) || 30 h to 830 h
    SR     (N):    forged disk, 1 h at 1149 °C (2100 °F), air cooled, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || tested at 649 °C (1200 °F) || 33 h to 1,500 h
    SR     (N):    forged disk, 1 h at 1149 °C (2100 °F), air cooled, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || tested at 732 °C (1350 °F) || 60 h to 350 h
    SR     (N):    forged disk, 1 h at 1149 °C (2100 °F), air cooled, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || Master curve (LMP) || 29.1 h to 32.7 h
    SR     (N):    forged disk, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || tested at 649 °C (1200 °F) || 25 h to 1,000 h
    SR     (N):    forged disk, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || tested at 732 °C (1350 °F) || 37 h to 605 h
    SR     (N):    forged disk, worked at 704 °C (1300 °F) to 732 °C (1350 °F), stress relieved 4 h at 649 °C (1200 °F) || Master curve (LMP) || 17.9 h to 20.9 h
    SR     (N):    disk, forged at 1149 °C (2100 °F), 2 h at 1177 °C (2150 °F), water quenched, worked at 52 °C (125 °F), stress relieved 10 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 33 h to 1,900 h
    SR     (N):    wrought sheet, 8 minutes at 982 °C (1800 °F), air cooled || tested at 649 °C (1200 °F) || 2 h to 700 h
    SR     (N):    wrought sheet, 8 minutes at 982 °C (1800 °F), air cooled || tested at 816 °C (1500 °F) || 6 h to 190 h
    SR     (N):    wrought sheet, 8 minutes at 982 °C (1800 °F), air cooled || Master curve (LMP) || 23.4 h to 29.7 h
    SR     (N):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || tested at 649 °C (1200 °F) || 3.5 h to 90 h
    SR     (N):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || tested at 816 °C (1500 °F) || 10 h to 95 h
    SR     (N):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || tested at 927 °C (1700 °F) || 3 h to 30 h
    SR     (N):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || tested at 1038 °C (1900 °F) || 2 h to 7 h
    SR     (N):    1 mm (0.0394 inch) sheet, annealed at 1038 °C (1900 °F) || Master curve (LMP) || 13.5 h to 19.3 h
    SR     (N):    wrought 6.35 mm (0.25 inch) plate, annealed at 816 °C (1500 °F) || tested at 732 °C (1350 °F) || 13 h to 400 h
    SR     (N):    precision cast || tested at 593 °C (1100 °F) || 70 h to 2,800 h
    SR     (N):    0.75 h at 1232 °C (2250 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 17 h to 860 h
    CRR    (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), oil quenched, aged 50 h at 816 °C (1500 °F) || tested at 732 °C (1350 °F) || 9 x 10^-¹¹/s to 3.4 x 10^-⁷/s
    CRR    (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), oil quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 1 x 10^-¹⁰/s to 3 x 10^-⁵/s
    CRR    (N):    rolled bar stock, as-rolled 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 1.5 x 10^-⁹/s to 2 x 10^-⁷/s
    CRR    (N):    rolled bar stock, 0.5 h at 1232 °C (2250 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 2 x 10^-¹⁰/s to 4.2 x 10^-¹⁰/s
    CRR    (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, aged 2 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 3.5 x 10^-¹¹/s to 1.4 x 10^-¹⁰/s
    CRR    (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, aged 2 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 3 x 10^-¹¹/s to 1.2 x 10^-⁹/s
    CRR    (N):    wrought, 1 h at 1149 °C (2100 °F), air cooled, reduced 15% at 649 °C (1200 °F), furnace cooled || tested at 649 °C (1200 °F) || 1.1 x 10^-¹⁰/s to 2.3 x 10^-¹⁰/s
    CRR    (N):    hot-rolled, 1 h at 649 °C (1200 °F), worked 20% at 649 °C (1200 °F), 1 h at 649 °C (1200 °F) || tested at 649 °C (1200 °F) || 2.4 x 10^-¹¹/s to 9 x 10^-¹⁰/s
    CRR    (N):    0.75 h at 1232 °C (2250 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 2 x 10^-⁹/s to 8.5 x 10^-⁹/s

return to listing

19-9 DX

    CRS    (R):    0.1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 16.5 h to 21.2 h
    CRS    (R):    0.2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 17.1 h to 25.1 h
    CRS    (R):    0.3% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 15.8 h to 23.2 h
    CRS    (R):    0.5% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 16.1 h to 23.7 h
    CRS    (R):    1% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 17.5 h to 25.2 h
    CRS    (R):    2% plastic strain, sheet, hot-rolled, annealed at 982 °C (1800 °F), cold-rolled || Master curve (LMP) || 21.4 h to 29.1 h

return to listing

17-7 PH

    FEN    (N):    RH 950 || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 8.6 x 10³ cycles to 6.6 x 10⁶ cycles
    FEN    (N):    RH 950 || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 1.3 x 10⁴ cycles to 1 x 10⁶ cycles
    FEN    (N):    RH 950 || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 1.6 x 10⁴ cycles to 1 x 10⁶ cycles
    FEN    (N):    RH 950 || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 6.7 x 10³ cycles to 1 x 10⁶ cycles

return to listing

17-4 PH

FSN (R): H1150, low cycle || tested at 20 °C (68 °F), R = -1, maximum stress || 3 x 10⁴ cycles to 9 x 10⁷ cycles

return to listing

16-25-6 (AISI 650)

    UTS   (N*):    25.4 mm (1 inch) forged bar, 2 h at 1182 °C (2160 °F), water quenched || room temperature value || room temperature value
    UTS   (N*):    wrought, 20 minutes at 1177 °C (2150 °F), water quenched, 12 h at 732 °C (1350 °F), furnace cooled || room temperature value
    UTS   (N*):    wrought, 1177 °C (2150 °F), water quenched, and drawn || room temperature value
    UTS   (N*):    hot forged, 15% reduction at 732 °C (1350 °F), 4 h at 649 °C (1200 °F), air cooled || room temperature value
    UTS   (N*):    wrought, 1 h 1149 °C (2100 °F), air cooled, worked 20% at 649 °C (1200 °F), 8 h at 649 °C (1200 °F), air cooled || room temperature value
    UTS   (N*):    hot-rolled, worked 649 °C (1200 °F) to 677 °C (1250 °F) || room temperature value
    UTS   (N*):    as-forged 368 mm (14.5 inch) disk || tangential direction || room temperature value
    UTS   (N*):    as-forged 368 mm (14.5 inch) disk || radial direction || room temperature value
    UTS   (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || tangential direction || room temperature value
    UTS   (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || radial direction || room temperature value
    UTS    (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || 20 °C (68 °F) to 982 °C (1799 °F)
    YS    (N*):    25.4 mm (1 inch) forged bar, 2 h at 1182 °C (2160 °F), water quenched || room temperature value || room temperature value
    YS    (N*):    wrought, 1 h 1149 °C (2100 °F), air cooled, worked 20% at 649 °C (1200 °F), 8 h at 649 °C (1200 °F), air cooled || room temperature value
    YS    (N*):    as-forged 368 mm (14.5 inch) disk || tangential direction || room temperature value
    YS    (N*):    as-forged 368 mm (14.5 inch) disk || radial direction || room temperature value
    YS    (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || tangential direction || room temperature value
    YS    (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || radial direction || room temperature value
    YS     (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || 20 °C (68 °F) to 982 °C (1799 °F)
    %El   (N*):    25.4 mm (1 inch) forged bar, 2 h at 1182 °C (2160 °F), water quenched || room temperature value || room temperature value
    %El   (N*):    wrought, 20 minutes at 1177 °C (2150 °F), water quenched, 12 h at 732 °C (1350 °F), furnace cooled || room temperature value
    %El   (N*):    wrought, 1177 °C (2150 °F), water quenched, and drawn || room temperature value
    %El   (N*):    hot forged, 15% reduction at 732 °C (1350 °F), 4 h at 649 °C (1200 °F), air cooled || room temperature value
    %El   (N*):    wrought, 1 h 1149 °C (2100 °F), air cooled, worked 20% at 649 °C (1200 °F), 8 h at 649 °C (1200 °F), air cooled || room temperature value
    %El   (N*):    hot-rolled, worked 649 °C (1200 °F) to 677 °C (1250 °F) || room temperature value
    %El   (N*):    as-forged 368 mm (14.5 inch) disk || tangential direction || room temperature value
    %El   (N*):    as-forged 368 mm (14.5 inch) disk || radial direction || room temperature value
    %El   (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || tangential direction || room temperature value
    %El   (N*):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || radial direction || room temperature value
    %El    (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || 20 °C (68 °F) to 982 °C (1799 °F)
    SR     (N):    25.4 mm (1 inch) forged bar, 2 h at 1182 °C (2160 °F), water quenched || tested at 649 °C (1200 °F) || 19 h to 935 h
    SR     (N):    25.4 mm (1 inch) forged bar, 2 h at 1182 °C (2160 °F), water quenched || tested at 732 °C (1350 °F) || 30 h to 510 h
    SR     (N):    19 mm (0.75 inch) bar, 0.5 h at 843 °C (1550 °F), 0.75 h at 1177 °C (2150 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 5 h to 250 h
    SR     (N):    19 mm (0.75 inch) bar, 0.5 h at 843 °C (1550 °F), 0.75 h at 1177 °C (2150 °F), air cooled, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 7 h to 490 h
    SR     (N):    wrought, 20 minutes at 1177 °C (2150 °F), water quenched, 12 h at 732 °C (1350 °F), furnace cooled || tested at 593 °C (1100 °F) || 53 h to 2,000 h
    SR     (N):    wrought, 20 minutes at 1177 °C (2150 °F), water quenched, 12 h at 732 °C (1350 °F), furnace cooled || tested at 649 °C (1200 °F) || 15 h to 1,100 h
    SR     (N):    wrought, 20 minutes at 1177 °C (2150 °F), water quenched, 12 h at 732 °C (1350 °F), furnace cooled || Master curve (LMP) || 26.6 h to 29.5 h
    SR     (N):    wrought, 1177 °C (2150 °F), water quenched, and drawn || tested at 649 °C (1200 °F) || 15 h to 2,200 h
    SR     (N):    hot-rolled, 593 °C (1100 °F), air cooled || tested at 538 °C (1000 °F) || 600 h to 7,600 h
    SR     (N):    wrought, 1 h 1149 °C (2100 °F), air cooled, worked 20% at 649 °C (1200 °F), 8 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 30 h to 530 h
    SR     (N):    forged at 1066 °C (1950 °F), 20 minutes at 1093 °C (2000 °F), air cooled, worked 10% at 649 °C (1200 °F), 4 h at 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 5 h to 73 h
    SR     (N):    hot-rolled at 1093 °C (2000 °F), worked 12% at 649 °C (1200 °F), 4 h at 704 °C (1300 °F) || tested at 593 °C (1100 °F) || 150 h to 8,500 h
    SR     (N):    hot-rolled at 1093 °C (2000 °F), worked 12% at 649 °C (1200 °F), 4 h at 704 °C (1300 °F) || tested at 649 °C (1200 °F) || 17 h to 3,700 h
    SR     (N):    hot-rolled at 1093 °C (2000 °F), worked 12% at 649 °C (1200 °F), 4 h at 704 °C (1300 °F) || Master curve (LMP) || 19.2 h to 21.7 h
    SR     (N):    hot-rolled, worked 649 °C (1200 °F) to 677 °C (1250 °F) || tested at 482 °C (900 °F) || 620 h to 1 x 10⁴ h
    SR     (N):    hot-rolled, worked 649 °C (1200 °F) to 677 °C (1250 °F) || tested at 593 °C (1100 °F) || 43 h to 1.1 x 10⁴ h
    SR     (N):    hot-rolled, worked 649 °C (1200 °F) to 677 °C (1250 °F) || Master curve (LMP) || 14.9 h to 18.2 h
    SR     (N):    cold-rolled to 300 BHN || tested at 593 °C (1100 °F) || 53 h to 4,900 h
    SR     (N):    cold-rolled to 300 BHN || tested at 649 °C (1200 °F) || 25 h to 9,000 h
    SR     (N):    cold-rolled to 300 BHN || Master curve (LMP) || 18.8 h to 22.1 h
    SR     (N):    cold-rolled to 260 BHN, 4 h at 677 °C (1250 °F), air cooled || tested at 593 °C (1100 °F) || 100 h to 1,530 h
    SR     (N):    cold-rolled to 260 BHN, 4 h at 677 °C (1250 °F), air cooled || tested at 649 °C (1200 °F) || 3 h to 5,100 h
    SR     (N):    cold-rolled to 260 BHN, 4 h at 677 °C (1250 °F), air cooled || Master curve (LMP) || 21.7 h to 24.6 h
    SR     (N):    as-forged 368 mm (14.5 inch) disk || tested at 816 °C (1500 °F), tangential direction || 170 h to 750 h
    SR     (N):    as-forged 368 mm (14.5 inch) disk || tested at 816 °C (1500 °F), radial direction || 120 h to 680 h
    SR     (N):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || tested at 649 °C (1200 °F), tangential direction || 33 h to 750 h
    SR     (N):    as-forged 397 mm x 133 mm (15.625 inch x 5.25 inch) disk || tested at 816 °C (1500 °F), tangential direction || 100 h to 300 h
    SR     (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || tested at 649 °C (1200 °F) || 19 h to 205 h
    SR     (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || tested at 732 °C (1350 °F) || 11 h to 190 h
    SR     (N):    hot-rolled, annealed at 1066 °C (1950 °F), cold reduced 1.59 mm (0.0625 inch) sheet || Master curve (LMP) || 15.9 h to 18.4 h
    CRR    (N):    19 mm (0.75 inch) bar, 0.5 h at 843 °C (1550 °F), 0.75 h at 1177 °C (2150 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 7.5 x 10^-¹⁰/s to 9 x 10^-⁶/s
    CRR    (N):    19 mm (0.75 inch) bar, 0.5 h at 843 °C (1550 °F), 0.75 h at 1177 °C (2150 °F), air cooled, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 6 x 10^-¹⁰/s to 6 x 10^-⁶/s
    CRR    (N):    hot forged, 15% reduction at 732 °C (1350 °F), 4 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 1 x 10^-¹¹/s to 5 x 10^-¹¹/s
    CRR    (N):    hot forged, 15% reduction at 732 °C (1350 °F), 4 h at 649 °C (1200 °F), air cooled || tested at 816 °C (1500 °F) || 3.5 x 10^-¹¹/s to 3.3 x 10^-¹⁰/s

return to listing

17-22AS

    CRR    (N):    1 h at 941 °C (1725 °F), air cooled, 2 h 649 °C (1200 °F) temper, hardness 289 BHN || tested at 454 °C (850 °F) || 2.7 x 10^-¹²/s to 8.5 x 10^-¹²/s
    CRR    (N):    1 h at 941 °C (1725 °F), air cooled, 2 h 649 °C (1200 °F) temper, hardness 289 BHN || tested at 510 °C (950 °F) || 1.6 x 10^-¹¹/s to 2.6 x 10^-⁸/s
    CRR    (N):    1 h at 941 °C (1725 °F), air cooled, 2 h 649 °C (1200 °F) temper, hardness 289 BHN || tested at 566 °C (1050 °F) || 3.3 x 10^-¹⁰/s to 3.7 x 10^-⁸/s
    CRR    (N):    954 °C (1750 °F), air cooled, tempered 10 h at 649 °C (1200 °F), 15% martensite + 85% coarse bainite || tested at 371 °C (700 °F) || 1.9 x 10^-¹⁰/s to 6.2 x 10^-⁸/s
    CRR    (N):    954 °C (1750 °F), air cooled, tempered 10 h at 649 °C (1200 °F), 15% martensite + 85% coarse bainite || tested at 482 °C (900 °F) || 3 x 10^-¹⁰/s to 1.75 x 10^-⁸/s
    CRR    (N):    954 °C (1750 °F), air cooled, tempered 10 h at 649 °C (1200 °F), 15% martensite + 85% coarse bainite || tested at 593 °C (1100 °F) || 4 x 10^-¹⁰/s to 1.75 x 10^-⁸/s
    CRR    (N):    954 °C (1750 °F), air cooled, tempered 10 h at 649 °C (1200 °F), 15% martensite + 85% coarse bainite || tested at 649 °C (1200 °F) || 6.3 x 10^-⁹/s to 1.8 x 10^-⁸/s
    CRR    (N):    transformed 2 h at 482 °C (900 °F), tempered 16 h at 649 °C (1200 °F), 60% medium bainite + 40% martensite || tested at 371 °C (700 °F) || 2.7 x 10^-⁹/s to 5 x 10^-⁸/s
    CRR    (N):    transformed 2 h at 482 °C (900 °F), tempered 16 h at 649 °C (1200 °F), 60% medium bainite + 40% martensite || tested at 482 °C (900 °F) || 2.65 x 10^-⁹/s to 2 x 10^-⁸/s
    CRR    (N):    transformed 2 h at 482 °C (900 °F), tempered 16 h at 649 °C (1200 °F), 60% medium bainite + 40% martensite || tested at 593 °C (1100 °F) || 2.6 x 10^-⁹/s to 3.9 x 10^-⁹/s
    CRR    (N):    transformed 2 h at 427 °C (800 °F), tempered 4 h at 649 °C (1200 °F), 97% fine acicular bainite + 3% martensite || tested at 371 °C (700 °F) || 1.1 x 10^-¹⁰/s to 8.5 x 10^-¹⁰/s
    CRR    (N):    transformed 2 h at 427 °C (800 °F), tempered 4 h at 649 °C (1200 °F), 97% fine acicular bainite + 3% martensite || tested at 482 °C (900 °F) || 3 x 10^-¹⁰/s to 5 x 10^-⁹/s
    CRR    (N):    transformed 2 h at 427 °C (800 °F), tempered 4 h at 649 °C (1200 °F), 97% fine acicular bainite + 3% martensite || tested at 593 °C (1100 °F) || 5 x 10^-¹⁰/s to 1 x 10^-⁸/s
    CRR    (N):    transformed 2 h at 427 °C (800 °F), tempered 4 h at 649 °C (1200 °F), 97% fine acicular bainite + 3% martensite || tested at 649 °C (1200 °F) || 1.35 x 10^-⁹/s to 2.35 x 10^-⁸/s
    CRR    (N):    transformed 5 minutes at 371 °C (700 °F), tempered 0.5 h at 649 °C (1200 °F), 100% fine acicular bainite || tested at 593 °C (1100 °F) || 1.1 x 10^-⁹/s to 4.6 x 10^-⁸/s
    CRR    (N):    transformed 5 minutes at 371 °C (700 °F), tempered 0.5 h at 649 °C (1200 °F), 100% fine acicular bainite || tested at 649 °C (1200 °F) || 1 x 10^-⁸/s to 5.3 x 10^-⁸/s

return to listing

17-22AV

    SR     (N):    hot-rolled and annealed, 0.5 h at 982 °C (1800 °F), air cooled, 6 h at 649 °C (1200 °F), air cooled, hardness 35 Rc || tested at 593 °C (1100 °F) || 0.24 h to 610 h
    CRR    (N):    normalized at 982 °C (1800 °F), tempered 6 h at 649 °C (1200 °F), hardness 331/341 BHN || tested at 538 °C (1000 °F) || 3.8 x 10^-¹¹/s to 1.1 x 10^-¹⁰/s
    CRR    (N):    normalized at 982 °C (1800 °F), tempered 6 h at 649 °C (1200 °F), hardness 331/341 BHN || tested at 593 °C (1100 °F) || 6.1 x 10^-¹¹/s to 4.75 x 10^-¹⁰/s

return to listing

52100

FSN (N): quenched from 735 °C (1355 °F) & tempered at 180 °C (356 °F) || tested at 20 °C (68 °F), R = 0, axial, ground & buffed surface, maximum stress || 2 x 10³ cycles to 6 x 10⁸ cycles
FSN (N): quenched from 735 °C (1355 °F) & tempered at 180 °C (356 °F) || tested at 20 °C (68 °F), R = 0.5, axial, ground & buffed surface, maximum stress || 4.5 x 10⁴ cycles to 3.7 x 10⁸ cycles

return to listing

310

    FEN    (N):    mill annealed & pickled || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 40 cycles to 6 x 10⁴ cycles
    FEN    (N):    mill annealed & pickled || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 40 cycles to 6 x 10⁴ cycles
    FEN    (N):    mill annealed & pickled || tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range || 100 cycles to 6 x 10⁵ cycles
    FEN    (N):    mill annealed & pickled || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 100 cycles to 6 x 10⁵ cycles
    FEN    (N):    mill annealed & pickled || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 100 cycles to 6 x 10⁵ cycles
    FEN    (N):    mill annealed & pickled || tested at 27 °C (80 °F), R = -1, axial, total strain range || 80 cycles to 6.2 x 10⁵ cycles
    FEN    (N):    mill annealed & pickled || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 80 cycles to 6.2 x 10⁵ cycles
    FEN    (N):    mill annealed & pickled || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 80 cycles to 6.2 x 10⁵ cycles

return to listing

316

FSN (N): annealed || tested at 20 °C (68 °F), R = -1, bending, maximum stress || 3.4 x 10⁴ cycles to 8.9 x 10⁵ cycles
FEN (N): 20% cold worked || tested at 550 °C (1022 °F), R = -1, axial, total strain range || 1 x 10³ cycles to 1 x 10⁷ cycles

return to listing

431

    SR     (N):    hardened 982 °C (1800 °F), oil quenched, tempered 4 h at 663 °C (1225 °F) || tested at 482 °C (900 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    hardened 982 °C (1800 °F), oil quenched, tempered 4 h at 663 °C (1225 °F) || tested at 593 °C (1100 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    hardened 982 °C (1800 °F), oil quenched, tempered 4 h at 663 °C (1225 °F) || tested at 649 °C (1200 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    hardened 982 °C (1800 °F), oil quenched, tempered 4 h at 663 °C (1225 °F) || Master curve (LMP) || 16.1 h to 20.6 h

return to listing

1010

    UTS   (N*):    killed steel, normalized at 899 °C (1650 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar || room temperature value
    %El   (N*):    killed steel, normalized at 899 °C (1650 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar || room temperature value
    SR     (N):    killed steel, normalized 0.5 h at 899 °C (1650 °F) || tested at 454 °C (850 °F) || 0.3 h to 1,400 h
    CRR    (N):    killed steel, normalized at 899 °C (1650 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar || tested at 538 °C (1000 °F) || 3.85 x 10^-¹¹/s to 1.1 x 10^-⁹/s
    CRR    (N):    killed steel, normalized 0.5 h at 899 °C (1650 °F) || tested at 454 °C (850 °F) || 7.8 x 10^-⁸/s to 1.3 x 10^-⁴/s

return to listing

1020

    UTS   (N*):    annealed at 885 °C (1625 °F), 22.2 mm (0.875 inch) bar, hardness 103 BHN || room temperature value
    UTS    (N):    annealed at 843 °C (1550 °F), 19 mm (0.75 inch) bar, hardness 134 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    YS     (N):    annealed at 843 °C (1550 °F), 19 mm (0.75 inch) bar, hardness 134 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    %El   (N*):    annealed at 885 °C (1625 °F), 22.2 mm (0.875 inch) bar, hardness 103 BHN || room temperature value
    %El    (N):    annealed at 843 °C (1550 °F), 19 mm (0.75 inch) bar, hardness 134 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    CRR    (N):    annealed at 885 °C (1625 °F), 22.2 mm (0.875 inch) bar, hardness 103 BHN || tested at 427 °C (800 °F) || 1.6 x 10^-¹¹/s to 1.3 x 10^-⁹/s
    CRR    (N):    annealed at 885 °C (1625 °F), 22.2 mm (0.875 inch) bar, hardness 103 BHN || tested at 482 °C (900 °F) || 5.5 x 10^-¹²/s to 1.7 x 10^-⁹/s
    CRR    (N):    annealed at 885 °C (1625 °F), 22.2 mm (0.875 inch) bar, hardness 103 BHN || tested at 538 °C (1000 °F) || 2.5 x 10^-¹¹/s to 1.4 x 10^-¹⁰/s
    CRR    (N):    annealed at 843 °C (1550 °F), 19 mm (0.75 inch) bar, hardness 134 BHN || tested at 427 °C (800 °F) || 1 x 10^-¹⁰/s to 2.8 x 10^-⁹/s
    CRR    (N):    annealed at 843 °C (1550 °F), 19 mm (0.75 inch) bar, hardness 134 BHN || tested at 538 °C (1000 °F) || 1.35 x 10^-¹⁰/s to 4.2 x 10^-⁸/s

return to listing

4340

    UTS    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || 20 °C (68 °F) to 538 °C (1000 °F)
    SR     (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 260 °C (500 °F) || 0.16 h to 83 h
    SR     (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 316 °C (600 °F) || 4 h to 1,350 h
    SR     (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 371 °C (700 °F) || 0.11 h to 1,950 h
    SR     (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || Master curve (LMP) || 8.86 h to 13.3 h
    SR     (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || tested at 454 °C (850 °F) || 35 h to 1,000 h
    SR     (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || tested at 538 °C (1000 °F) || 0.16 h to 1,350 h
    SR     (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || Master curve (LMP) || 20.5 h to 24.2 h
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 260 °C (500 °F) || 6.7 x 10^-⁸/s to 6.7 x 10^-⁵/s
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 316 °C (600 °F) || 1 x 10^-⁸/s to 1.6 x 10^-⁶/s
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 454 °C (850 °F), tempered martensite || tested at 371 °C (700 °F) || 1.05 x 10^-⁸/s to 5.85 x 10^-⁵/s
    CRR    (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || tested at 454 °C (850 °F) || 2.4 x 10^-⁸/s to 4.6 x 10^-⁷/s
    CRR    (N):    wrought, 1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 632 °C (1170 °F), tempered martensite || tested at 538 °C (1000 °F) || 4.3 x 10^-⁸/s to 1.15 x 10^-⁴/s

return to listing

2021

    %El    (N):    T81 temper, plate || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)
    %El    (N):    T81 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)
    %El    (N):    T81 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)
    %El    (N):    T81 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)
    %El    (N):    T81 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)
    %El    (N):    T81 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 540 °C (1004 °F)

return to listing

4032

    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

6053

    UTS   (N*):    O temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value
    UTS   (N*):    T6 temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value
    YS    (N*):    O temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value
    YS    (N*):    T6 temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value
    %El   (N*):    O temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value
    %El   (N*):    T6 temper, 19 mm (0.75 inch) rod || short-time at temperature || room temperature value

return to listing

1015

    UTS    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || 20 °C (68 °F) to 760 °C (1400 °F)
    UTS   (N*):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 134 BHN || room temperature value
    UTS   (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 131 BHN || room temperature value
    UTS   (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 165 BHN || room temperature value
    UTS   (N*):    normalized 941 °C (1725 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar, hardness 118 to 121 BHN || room temperature value
    YS     (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || 20 °C (68 °F) to 760 °C (1400 °F)
    YS    (N*):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 134 BHN || room temperature value
    YS    (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 131 BHN || room temperature value
    YS    (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 165 BHN || room temperature value
    YS    (N*):    normalized 941 °C (1725 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar, hardness 118 to 121 BHN || room temperature value
    %El    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || 20 °C (68 °F) to 650 °C (1202 °F)
    %El   (N*):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 134 BHN || room temperature value
    %El   (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 131 BHN || room temperature value
    %El   (N*):    hot-rolled, 25.4 mm (1 inch) bar, hardness 165 BHN || room temperature value
    %El   (N*):    normalized 941 °C (1725 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar, hardness 118 to 121 BHN || room temperature value
    SR     (R):    killed || tested at 454 °C (850 °F) || 0.3 h to 8,700 h
    SR     (R):    killed || tested at 510 °C (950 °F) || 80 h to 6,700 h
    SR     (R):    killed || tested at 649 °C (1200 °F) || 100 h to 1 x 10⁵ h
    SR     (R):    killed || tested at 760 °C (1400 °F) || 100 h to 1 x 10⁵ h
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 111 BHN || tested at 427 °C (800 °F) || 3.3 x 10^-¹¹/s to 2.8 x 10^-¹⁰/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 111 BHN || tested at 538 °C (1000 °F) || 1 x 10^-¹⁰/s to 2.9 x 10^-⁹/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 111 BHN || tested at 649 °C (1200 °F) || 9 x 10^-¹¹/s to 1.7 x 10^-⁹/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || tested at 427 °C (800 °F) || 4.4 x 10^-¹¹/s to 5.3 x 10^-¹⁰/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || tested at 482 °C (900 °F) || 6 x 10^-¹¹/s to 7 x 10^-¹⁰/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || tested at 538 °C (1000 °F) || 1 x 10^-¹⁰/s to 8.2 x 10^-¹⁰/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || tested at 593 °C (1100 °F) || 1.45 x 10^-¹⁰/s to 1 x 10^-⁹/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 123 BHN || tested at 649 °C (1200 °F) || 6 x 10^-¹¹/s to 4.5 x 10^-⁹/s
    CRR    (N):    annealed at 843 °C (1550 °F), 25.4 mm (1 inch) bar, hardness 134 BHN || tested at 538 °C (1000 °F) || 6.9 x 10^-¹¹/s to 1.35 x 10^-⁹/s
    CRR    (N):    hot-rolled, 25.4 mm (1 inch) bar, hardness 131 BHN || tested at 538 °C (1000 °F) || 9.4 x 10^-¹¹/s to 1.1 x 10^-⁸/s
    CRR    (N):    hot-rolled, 25.4 mm (1 inch) bar, hardness 165 BHN || tested at 538 °C (1000 °F) || 4.4 x 10^-¹¹/s to 3.75 x 10^-⁹/s
    CRR    (N):    normalized 941 °C (1725 °F), drawn at 649 °C (1200 °F), 25.4 mm (1 inch) bar, hardness 118 to 121 BHN || tested at 538 °C (1000 °F) || 2.7 x 10^-¹¹/s to 1.3 x 10^-⁸/s

return to listing

1040

    SR     (R):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 260 °C (500 °F) || 0.7 h to 15 h
    SR     (R):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 371 °C (700 °F) || 3.7 h to 1,400 h
    SR     (R):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 454 °C (850 °F) || 5 h to 750 h
    SR     (R):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 538 °C (1000 °F) || 1 h to 1,800 h
    SR     (R):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || Master curve (LMP) || 9.85 h to 17.7 h
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 371 °C (700 °F) || 2.5 x 10^-⁸/s to 2.7 x 10^-⁶/s
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 454 °C (850 °F) || 8.2 x 10^-⁸/s to 5.5 x 10^-⁶/s
    CRR    (N):    1 h at 843 °C (1550 °F), oil quenched, tempered 2 h at 449 °C (840 °F) || tested at 538 °C (1000 °F) || 5.3 x 10^-⁸/s to 3.7 x 10^-⁵/s

return to listing

302

    SR     (R):    solid || tested at 538 °C (1000 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 593 °C (1100 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 649 °C (1200 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 704 °C (1300 °F) || 7 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 760 °C (1400 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 816 °C (1500 °F) || 2 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 927 °C (1700 °F) || 1.27 h to 1,000 h
    SR     (R):    solid || tested at 1077 °C (1970 °F) || 2 h to 23 h
    SR     (R):    solid || Master curve (LMP) || 14.3 h to 22.8 h

return to listing

304

    SSC    (N):    effect of H₂ || tested at 20 °C (68 °F), not H₂ charged, unknown strain rate || 0 to 0.42 mm/mm strain
    SSC    (N):    effect of H₂ || tested at 20 °C (68 °F), H₂ charged, unknown strain rate || 0 to 0.15 mm/mm strain
    SR     (R):    solid || tested at 538 °C (1000 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 593 °C (1100 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 649 °C (1200 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 704 °C (1300 °F) || 7 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 760 °C (1400 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 816 °C (1500 °F) || 2 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 927 °C (1700 °F) || 1.27 h to 1,000 h
    SR     (R):    solid || tested at 1077 °C (1970 °F) || 2 h to 23 h
    SR     (R):    solid || Master curve (LMP) || 14.3 h to 22.8 h

return to listing

1060

    UTS    (R):    values after hold times of 0.5 h to 10,000 h || O temper || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    values after hold times of 0.5 h to 10,000 h || O temper || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    values after hold times of 0.5 h to 10,000 h || O temper || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    SR     (N):    O temper || tested at 149 °C (300 °F) || 0.1 h to 1,000 h
    SR     (N):    O temper || tested at 204 °C (400 °F) || 10 h to 1,000 h
    SR     (N):    O temper || Master curve (LMP) || 6.5 h to 9.26 h
    CRS    (N):    1% plastic strain, O temper || tested at 149 °C (300 °F) || 0.1 h to 1 h
    CRS    (N):    1% plastic strain, O temper || tested at 204 °C (400 °F) || 0.1 h to 1 h

return to listing

1100

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H12 temper || values after hold times of 0.5 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H12 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H12 temper || values after hold times of 1,000 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H12 temper || values after hold times of 0.5 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H12 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H12 temper || values after hold times of 1,000 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H12 temper || values after hold times of 0.5 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H12 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H12 temper || values after hold times of 1,000 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    SR     (R):    O temper || tested at 24 °C (75 °F) || 0.1 h to 1,000 h
    SR     (R):    O temper || tested at 93 °C (200 °F) || 50 h to 1,750 h
    SR     (R):    O temper || tested at 121 °C (250 °F) || 10 h to 1,100 h
    SR     (R):    O temper || tested at 149 °C (300 °F) || 20 h to 2,400 h
    SR     (R):    O temper || tested at 177 °C (350 °F) || 10 h to 1,300 h
    SR     (R):    O temper || tested at 204 °C (400 °F) || 5 h to 1,200 h
    SR     (R):    O temper || tested at 232 °C (450 °F) || 5 h to 2,050 h
    SR     (R):    O temper || tested at 260 °C (500 °F) || 15 h to 1,800 h
    SR     (R):    O temper || tested at 288 °C (550 °F) || 30 h to 280 h
    SR     (N):    O temper || tested at 316 °C (600 °F) || 5 h to 60 h
    SR     (R):    O temper || Master curve (LMP) || 6.7 h to 10.8 h
    CRR    (N):    sheet, annealed 1 h at 343 °C (650 °F) || tested at 100 °C (212 °F) || 2.78 x 10^-⁹/s to 2.78 x 10^-⁸/s
    CRR    (N):    sheet, annealed 1 h at 510 °C (950 °F) || tested at 100 °C (212 °F) || 2.78 x 10^-⁹/s to 2.78 x 10^-⁸/s
    CRR    (N):    sheet, annealed 1 h at 621 °C (1150 °F) || tested at 100 °C (212 °F) || 2.78 x 10^-⁹/s to 2.78 x 10^-⁸/s

return to listing

2011

    UTS    (R):    T3 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T3 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T3 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T3 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T451 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T451 temper || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T451 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T451 temper || values after 1,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)
    UTS    (R):    T8 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T3 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T3 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T3 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T3 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T451 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T451 temper || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T451 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T451 temper || values after 1,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (R):    T8 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T3 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T3 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T3 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T3 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T451 temper || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T451 temper || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T451 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T451 temper || values after 1,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)
    %El    (N):    T8 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)

return to listing

2014

    UTS    (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper sheet & T651 temper plate || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper sheet & T651 temper plate || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper sheet & T651 temper plate || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper sheet & T651 temper plate || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper sheet & T651 temper plate || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions & die forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions & die forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions & die forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions & die forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions & die forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper sheet & T651 temper plate || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper sheet & T651 temper plate || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper sheet & T651 temper plate || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper sheet & T651 temper plate || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper sheet & T651 temper plate || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions & die forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions & die forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions & die forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions & die forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions & die forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions & die forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions & die forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions & die forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions & die forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions & die forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, rolled and drawn rod ≤ 203 mm (8 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≤ 12.7 mm (0.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions 12.7 mm to 19 mm (0.5 inch to 0.75 inch) || values after 100,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions ≥ 19 mm (0.75 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T652 extrusions ≤ 50.8 mm (2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate 6.35 mm to 50.8 mm (0.25 inch to 2 inch) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    FEN    (N):    T6 temper || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 10 cycles to 7.1 x 10⁴ cycles
    FEN    (N):    T6 temper || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 10 cycles to 130 cycles
    FEN    (N):    T6 temper || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 30 cycles to 4.3 x 10⁴ cycles
    FEN    (N):    T6 temper || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 30 cycles to 1.2 x 10³ cycles
    FEN    (N):    T6 temper || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 10 cycles to 7.8 x 10⁴ cycles
    FEN    (N):    T6 temper || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 10 cycles to 670 cycles
    CRR    (N):    T6 temper || tested at 34 °C (94 °F) || 3.6 x 10^-¹⁰/s to 1.95 x 10^-⁵/s
    CRR    (N):    T6 temper || tested at 100 °C (212 °F) || 2.85 x 10^-⁹/s to 8.6 x 10^-⁵/s
    CRR    (N):    T6 temper || tested at 149 °C (300 °F) || 6.3 x 10^-¹⁰/s to 1.3 x 10^-⁵/s
    CRR    (N):    T6 temper || tested at 191 °C (375 °F) || 8 x 10^-¹⁰/s to 1.2 x 10^-⁵/s

return to listing

2017

    UTS    (R):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)

return to listing

2018

    UTS    (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    T61 temper || tested at 100 °C (212 °F) || 5.6 x 10^-¹⁰/s to 2.1 x 10^-⁷/s
    CRR    (N):    T61 temper || tested at 149 °C (300 °F) || 4 x 10^-¹⁰/s to 1.5 x 10^-⁴/s
    CRR    (N):    T61 temper || tested at 204 °C (400 °F) || 1.1 x 10^-¹⁰/s to 2 x 10^-⁶/s
    CRR    (N):    T61 temper || tested at 260 °C (500 °F) || 2.6 x 10^-¹⁰/s to 2.5 x 10^-⁷/s

return to listing

2020

    UTS    (R):    T6 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)

return to listing

305

    SR     (R):    solid || tested at 538 °C (1000 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 593 °C (1100 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 649 °C (1200 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 704 °C (1300 °F) || 7 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 760 °C (1400 °F) || 1 x 10³ h to 1 x 10⁵ h
    SR     (R):    solid || tested at 816 °C (1500 °F) || 2 h to 1 x 10⁵ h
    SR     (R):    solid || tested at 927 °C (1700 °F) || 1.27 h to 1,000 h
    SR     (R):    solid || tested at 1077 °C (1970 °F) || 2 h to 23 h
    SR     (R):    solid || Master curve (LMP) || 14.3 h to 22.8 h

return to listing

2024

    UTS    (R):    O temper, except extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, sheet || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, sheet || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, sheet || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, sheet || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, sheet || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T3 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T3 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T3 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T3 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T3 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T3 temper || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T36 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T36 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T36 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T36 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T36 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions || values after 0.5 h hold time || -263.1 °C (-441.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions || values after 10 h hold time || -263.1 °C (-441.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions || values after 100 h hold time || -263.1 °C (-441.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions || values after 1,000 h hold time || -263.1 °C (-441.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, except extrusions || values after 10,000 h hold time || -263.1 °C (-441.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T86 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T86 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T86 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T86 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T86 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, sheet || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, sheet || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, sheet || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, sheet || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, sheet || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T3 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T3 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T3 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T3 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T3 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T3 temper || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (N):    T36 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T36 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T36 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T36 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T36 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, except extrusions || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T86 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T86 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T86 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T86 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T86 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, sheet || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, sheet || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, sheet || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, sheet || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, sheet || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T3 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T3 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T3 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T3 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T3 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T3 temper || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 temper, except extrusions || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, except extrusions || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions 19 mm to 38.1 mm (0.75 inch to 1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, extrusions ≥ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T81 & T85 temper, ≤ 38.1 mm (1.5 inch) || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T86 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T86 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T86 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T86 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T86 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    SR     (N):    T4 temper || tested at 149 °C (300 °F) || 100 h to 1,000 h
    SR     (N):    T4 temper || tested at 204 °C (400 °F) || 10 h to 100 h
    SR     (N):    T4 temper || tested at 260 °C (500 °F) || 1 h to 100 h
    SR     (N):    T4 temper || tested at 316 °C (600 °F) || 10 h to 1,000 h
    SR     (N):    T4 temper || Master curve (LMP) || 8.69 h to 12.7 h
    CRR    (N):    T3 temper, all forms || tested at 100 °C (212 °F) || 1.4 x 10^-⁹/s to 3.05 x 10^-⁶/s
    CRR    (N):    T3 temper, all forms || tested at 149 °C (300 °F) || 7.7 x 10^-¹⁰/s to 5.6 x 10^-⁵/s
    CRR    (N):    T3 temper, all forms || tested at 191 °C (375 °F) || 2.8 x 10^-⁹/s to 8.3 x 10^-⁶/s
    CRR    (N):    T3 temper, all forms || tested at 204 °C (400 °F) || 1.2 x 10^-⁹/s to 2.3 x 10^-⁷/s
    CRR    (N):    T3 temper, all forms || tested at 232 °C (450 °F) || 3 x 10^-⁹/s to 3.2 x 10^-⁵/s
    CRR    (N):    T3 temper, all forms || tested at 316 °C (600 °F) || 3.1 x 10^-⁹/s to 1.7 x 10^-⁵/s
    CRR    (N):    T86 temper, 1.02 mm (0.04 inch) sheet || tested at 34 °C (94 °F) || 2.7 x 10^-¹⁰/s to 3.4 x 10^-⁵/s
    CRR    (N):    T86 temper, 1.02 mm (0.04 inch) sheet || tested at 100 °C (212 °F) || 3.8 x 10^-¹⁰/s to 2.75 x 10^-⁵/s
    CRR    (N):    T86 temper, 1.02 mm (0.04 inch) sheet || tested at 149 °C (300 °F) || 1.3 x 10^-⁹/s to 2.2 x 10^-⁵/s
    CRR    (N):    T86 temper, 1.02 mm (0.04 inch) sheet || tested at 191 °C (375 °F) || 1.35 x 10^-⁹/s to 1.1 x 10^-⁵/s

return to listing

2117

    UTS    (R):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)

return to listing

2124

    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 38.1 mm to 50.8 mm (1.5 inch to 2 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 50.8 mm to 76.2 mm (2 inch to 3 inch) || values after 100,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 76.2 mm to 102 mm (3 inch to 4 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 100 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T851 temper, plate 102 mm to 127 mm (4 inch to 5 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)

return to listing

2218

    UTS    (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    T86 temper, forged plate || tested at 32 °C (90 °F) || 9.7 x 10^-¹¹/s to 3.1 x 10^-¹⁰/s
    CRR    (N):    T86 temper, forged plate || tested at 100 °C (212 °F) || 3.3 x 10^-¹⁰/s to 2.1 x 10^-⁹/s
    CRR    (N):    T86 temper, forged plate || tested at 149 °C (300 °F) || 4.3 x 10^-¹⁰/s to 3.45 x 10^-⁷/s
    CRR    (N):    T86 temper, forged plate || tested at 204 °C (400 °F) || 4.5 x 10^-¹⁰/s to 8.4 x 10^-⁸/s

return to listing

2219

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, sheet, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, sheet, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, sheet, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, sheet, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, sheet, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, plate, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, plate, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, plate, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, plate, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T37 temper, plate, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T81 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T81 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T81 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T81 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T81 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T851 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T851 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T851 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T851 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T851 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T8511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T852 temper, forgings || values after 0.5 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    UTS    (R):    T852 temper, forgings || values after 10 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    UTS    (R):    T852 temper, forgings || values after 100 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    UTS    (R):    T852 temper, forgings || values after 1,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    UTS    (R):    T852 temper, forgings || values after 10,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    UTS    (R):    T87 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T87 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, sheet, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, sheet, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, sheet, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, sheet, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, sheet, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, plate, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, plate, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, plate, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, plate, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T37 temper, plate, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T81 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T81 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T81 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T81 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T81 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T851 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T851 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T851 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T851 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T851 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T8511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T852 temper, forgings || values after 0.5 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (R):    T852 temper, forgings || values after 10 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (R):    T852 temper, forgings || values after 100 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (R):    T852 temper, forgings || values after 1,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (R):    T852 temper, forgings || values after 10,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (R):    T87 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T87 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, sheet, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, sheet, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, sheet, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, sheet, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, sheet, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, plate, longitudinal direction || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, plate, longitudinal direction || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, plate, longitudinal direction || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, plate, longitudinal direction || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T37 temper, plate, longitudinal direction || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, plate || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, plate || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, plate || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, plate || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, plate || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 18 h at 191 °C (375 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, forgings, aged 16 h at 216 °C (420 °F) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T81 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T81 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T81 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T81 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T81 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T851 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T851 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T851 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T851 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T851 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T8511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T852 temper, forgings || values after 0.5 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    T852 temper, forgings || values after 10 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    T852 temper, forgings || values after 100 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    T852 temper, forgings || values after 1,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    T852 temper, forgings || values after 10,000 h hold time || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    T87 temper, sheet || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, sheet || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, sheet || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, sheet || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, sheet || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, plate || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, plate || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, plate || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, plate || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T87 temper, plate || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    FEN    (N):    T851 temper || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 180 cycles to 7.1 x 10⁴ cycles
    FEN    (N):    T851 temper || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 180 cycles to 1.1 x 10⁴ cycles
    FEN    (N):    T851 temper || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 90 cycles to 2 x 10⁵ cycles
    FEN    (N):    T851 temper || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 90 cycles to 4.6 x 10³ cycles
    FEN    (N):    T851 temper || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 70 cycles to 7 x 10⁴ cycles
    FEN    (N):    T851 temper || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 70 cycles to 7 x 10⁴ cycles

return to listing

2618

    UTS    (R):    T651 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T651 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T651 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T651 temper, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper, forgings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6511 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6511 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6511 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6511 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6511 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

3003

    UTS    (R):    O temper, rolled & drawn rod || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H12 temper, rolled & drawn rod || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled & drawn rod || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H12 temper, rolled & drawn rod || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, rolled & drawn rod || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H12 temper, rolled & drawn rod || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper, rolled & drawn rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper, rolled & drawn rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper, rolled & drawn rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper, rolled & drawn rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H14 temper, rolled & drawn rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H18 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    H12 temper, 1.65 mm (0.065 inch) sheet || tested at 32 °C (90 °F) || 1 x 10^-⁸/s to 2.3 x 10^-⁵/s
    CRR    (N):    H12 temper, 1.65 mm (0.065 inch) sheet || tested at 100 °C (212 °F) || 2.2 x 10^-¹⁰/s to 6.6 x 10^-⁶/s
    CRR    (N):    H12 temper, 1.65 mm (0.065 inch) sheet || tested at 149 °C (300 °F) || 6.9 x 10^-⁹/s to 7.1 x 10^-⁶/s
    CRR    (N):    H12 temper, 1.65 mm (0.065 inch) sheet || tested at 204 °C (400 °F) || 1.9 x 10^-¹⁰/s to 1.55 x 10^-⁵/s
    CRR    (N):    H18 temper, 1.65 mm (0.065 inch) sheet || tested at 32 °C (90 °F) || 2.4 x 10^-⁹/s to 1.95 x 10^-⁶/s
    CRR    (N):    H18 temper, 1.65 mm (0.065 inch) sheet || tested at 100 °C (212 °F) || 5.5 x 10^-¹¹/s to 4.4 x 10^-⁶/s
    CRR    (N):    H18 temper, 1.65 mm (0.065 inch) sheet || tested at 149 °C (300 °F) || 1.4 x 10^-⁹/s to 8.5 x 10^-⁷/s
    CRR    (N):    H18 temper, 1.65 mm (0.065 inch) sheet || tested at 204 °C (400 °F) || 2.5 x 10^-¹⁰/s to 2 x 10^-⁶/s

return to listing

3004

    UTS    (R):    O temper, rolled and drawn rod || values after hold times of 0.1 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper, rolled and drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled and drawn rod || values after hold times of 0.1 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper, rolled and drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, rolled and drawn rod || values after hold times of 0.1 h to 10 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper, rolled and drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper, rolled and drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper, rolled and drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper, rolled and drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper, rolled and drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    H38 temper, 1.63 mm (0.064 inch) sheet || tested at 32 °C (90 °F) || 3 x 10^-¹⁰/s to 3.65 x 10^-¹⁰/s
    CRR    (N):    H38 temper, 1.63 mm (0.064 inch) sheet || tested at 100 °C (212 °F) || 6.6 x 10^-¹⁰/s to 2.17 x 10^-⁶/s
    CRR    (N):    H38 temper, 1.63 mm (0.064 inch) sheet || tested at 149 °C (300 °F) || 2.6 x 10^-⁸/s to 4.3 x 10^-⁷/s
    CRR    (N):    H38 temper, 1.63 mm (0.064 inch) sheet || tested at 204 °C (400 °F) || 7.4 x 10^-¹⁰/s to 6.4 x 10^-⁶/s

return to listing

4130

    SR     (R):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 538 °C (1000 °F) || 0.5 h to 590 h
    SR     (N):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 649 °C (1200 °F) || 4 h to 310 h
    SR     (R):    1.6 mm (0.063 inch) thick sheet, normalized || Master curve (LMP) || 19.6 h to 27.5 h
    CRR    (R):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 538 °C (1000 °F), in compression and tension || 5.5 x 10^-⁹/s to 1.4 x 10^-⁶/s
    CRR    (N):    1.6 mm (0.063 inch) thick sheet, normalized || tested at 649 °C (1200 °F), in tension || 1 x 10^-⁸/s to 1.1 x 10^-⁵/s

return to listing

5005

    UTS    (R):    O temper, rolled & drawn rod || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H14 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H18 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H19 temper, wire || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H19 temper, wire || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H19 temper, wire || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H19 temper, wire || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H19 temper, wire || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    O temper, rolled & drawn rod || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H14 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H18 temper, rolled & drawn rod || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H19 temper, wire || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H19 temper, wire || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H19 temper, wire || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H19 temper, wire || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H19 temper, wire || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El   (N*):    O temper, rolled & drawn rod || room temperature value
    %El   (N*):    H19 temper, wire || room temperature value

return to listing

5050

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 100 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 0.5 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 100 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 1,000 h hold time || 204 °C (399 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10,000 h hold time || 204 °C (399 °F) to 371 °C (700 °F)

return to listing

5052

    UTS    (R):    O temper || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after hold times of 10 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H112 temper, 25.4 mm (1 inch) plate || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    O temper || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after hold times of 10 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H112 temper, 25.4 mm (1 inch) plate || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    O temper || values after hold times of 0.1 h to 100,000 h || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after hold times of 10 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H112 temper, 25.4 mm (1 inch) plate || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    CRR    (N):    H32 temper, 1.65 mm (0.065 inch) sheet || tested at 32 °C (90 °F) || 3.6 x 10^-¹⁰/s to 6.2 x 10^-¹⁰/s
    CRR    (N):    H32 temper, 1.65 mm (0.065 inch) sheet || tested at 100 °C (212 °F) || 1 x 10^-⁹/s to 2 x 10^-⁷/s
    CRR    (N):    H32 temper, 1.65 mm (0.065 inch) sheet || tested at 149 °C (300 °F) || 1 x 10^-⁸/s to 6.5 x 10^-⁶/s
    CRR    (N):    H32 temper, 1.65 mm (0.065 inch) sheet || tested at 204 °C (400 °F) || 4 x 10^-¹⁰/s to 2.5 x 10^-⁵/s
    CRR    (N):    H38 temper, 1.65 mm (0.065 inch) sheet || tested at 32 °C (90 °F) || 2.4 x 10^-¹⁰/s to 2.6 x 10^-⁹/s
    CRR    (N):    H38 temper, 1.65 mm (0.065 inch) sheet || tested at 100 °C (212 °F) || 7.1 x 10^-⁹/s to 1.3 x 10^-⁶/s
    CRR    (N):    H38 temper, 1.65 mm (0.065 inch) sheet || tested at 149 °C (300 °F) || 5.6 x 10^-⁸/s to 1.65 x 10^-⁶/s
    CRR    (N):    H38 temper, 1.65 mm (0.065 inch) sheet || tested at 204 °C (400 °F) || 5.8 x 10^-⁹/s to 1.9 x 10^-⁵/s

return to listing

5056

    UTS    (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    H32 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H38 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H38 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H38 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H38 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    H38 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    H32 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H38 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H38 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H38 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H38 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    H38 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 0.5 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 10 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 100 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 1,000 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H32 temper || values after 10,000 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H34 temper || values after 10 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H34 temper || values after 100 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || 149 °C (300 °F) to 538 °C (1000 °F)
    %El    (N):    H38 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H38 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H38 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H38 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    H38 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)

return to listing

5083

    UTS    (R):    O temper || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    H321 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    H321 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    H321 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    H321 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    H321 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (N):    H111 temper, extrusions || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    YS     (R):    O temper || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    H321 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    H321 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    H321 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    H321 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    H321 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (N):    H111 temper, extrusions || -196.1 °C (-321.1 °F) to 24 °C (75 °F)
    %El    (N):    O temper || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    H321 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    H321 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    H321 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    H321 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    H321 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    CRR    (N):    O temper, 6.35 mm (0.25 inch) sheet || tested at 93 °C (200 °F) || 1.5 x 10^-⁸/s to 5.4 x 10^-⁶/s
    CRR    (N):    O temper, 6.35 mm (0.25 inch) sheet || tested at 149 °C (300 °F) || 2.9 x 10^-⁸/s to 2.25 x 10^-⁵/s
    CRR    (N):    O temper, 6.35 mm (0.25 inch) sheet || tested at 204 °C (400 °F) || 4.1 x 10^-⁸/s to 1.95 x 10^-⁵/s

return to listing

5086

    UTS    (R):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 93 °C (200 °F) || 6.2 x 10^-⁸/s to 1.8 x 10^-⁵/s
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 149 °C (300 °F) || 1.7 x 10^-⁸/s to 4.25 x 10^-⁵/s
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 204 °C (400 °F) || 7.2 x 10^-⁹/s to 4.35 x 10^-⁵/s

return to listing

5154

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H38 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)

return to listing

5356

    UTS    (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 0.5 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 100 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 1,000 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10,000 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 0.5 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 10 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 100 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 1,000 h hold time || 148 °C (298 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 10,000 h hold time || 148 °C (298 °F) to 371 °C (700 °F)

return to listing

5454

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H32 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H32 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after hold times of 0.5 h to 10,000 h || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H32 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H34 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 93 °C (200 °F) || 6.8 x 10^-⁹/s to 2.6 x 10^-⁵/s
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 149 °C (300 °F) || 1.2 x 10^-⁸/s to 3.2 x 10^-⁵/s
    CRR    (N):    O temper, 1.63 mm (0.064 inch) sheet || tested at 204 °C (400 °F) || 1.8 x 10^-⁸/s to 7.4 x 10^-⁵/s

return to listing

5456

    UTS    (R):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H111 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H111 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H111 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H111 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H111 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    H321 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (N):    H323 temper || -253.1 °C (-423.7 °F) to 24 °C (75 °F)
    UTS    (N):    H343 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (N):    H343 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 149 °C (300 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H111 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H111 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H111 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H111 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H111 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    H321 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (N):    H323 temper || -253.1 °C (-423.7 °F) to 24 °C (75 °F)
    YS     (N):    H343 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (N):    H343 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 149 °C (300 °F)
    %El    (N):    O temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H111 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    H111 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    H111 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    H111 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    H111 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H321 temper || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    H323 temper || -253.1 °C (-423.7 °F) to 24 °C (75 °F)
    %El    (N):    H343 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    H343 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 149 °C (300 °F)

return to listing

6005

    UTS    (R):    T5 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T5 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T5 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T5 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T5 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T5 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T5 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T5 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T5 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T5 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T5 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T5 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)

return to listing

4140

    UTS    (R):    tempered at 482 °C (900 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    tempered at 510 °C (950 °F) || 20 °C (68 °F) to 549 °C (1020 °F)
    UTS    (N):    tempered at 593 °C (1100 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    tempered at 607 °C (1125 °F), hardness 285 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    UTS    (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    YS     (N):    tempered at 482 °C (900 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (N):    tempered at 510 °C (950 °F) || 20 °C (68 °F) to 549 °C (1020 °F)
    YS     (N):    tempered at 593 °C (1100 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    tempered at 607 °C (1125 °F), hardness 285 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    YS     (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    %El    (N):    tempered at 482 °C (900 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    tempered at 510 °C (950 °F) || 20 °C (68 °F) to 549 °C (1020 °F)
    %El    (N):    tempered at 593 °C (1100 °F) || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (R):    tempered at 607 °C (1125 °F), hardness 285 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    %El    (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || 20 °C (68 °F) to 649 °C (1200 °F)
    SR     (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || tested at 454 °C (850 °F) || 100 h to 2,000 h
    SR     (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || tested at 510 °C (950 °F) || 43 h to 223 h
    SR     (N):    1 h at 899 °C (1650 °F), air cooled, 1 h at 649 °C (1200 °F), furnace cooled, hardness 233 BHN || Master curve (LMP) || 22.9 h to 23.9 h
    CRR    (N):    tempered at 593 °C (1100 °F) || tested at 454 °C (850 °F), hardness 269 BHN || 3 x 10^-¹¹/s to 1.7 x 10^-¹⁰/s
    CRR    (N):    tempered at 593 °C (1100 °F) || tested at 482 °C (900 °F), hardness 269 BHN || 6.6 x 10^-¹¹/s to 2.25 x 10^-¹⁰/s
    CRR    (N):    tempered at 593 °C (1100 °F) || tested at 538 °C (1000 °F), hardness 269 BHN || 7.7 x 10^-¹¹/s to 6.7 x 10^-¹⁰/s
    CRR    (N):    tempered at 607 °C (1125 °F) || tested at 538 °C (1000 °F), hardness 285 BHN || 6.9 x 10^-¹¹/s to 1.35 x 10^-⁹/s
    CRR    (N):    tempered at 641 °C (1185 °F) || tested at 454 °C (850 °F), hardness 269 BHN || 1.9 x 10^-¹¹/s to 3.8 x 10^-¹⁰/s
    CRR    (N):    tempered at 657 °C (1215 °F) || tested at 427 °C (800 °F), hardness 277 BHN || 5.5 x 10^-¹¹/s to 2.3 x 10^-¹⁰/s
    CRR    (N):    tempered at 657 °C (1215 °F) || tested at 454 °C (850 °F), hardness 269 BHN || 1.9 x 10^-¹¹/s to 8.7 x 10^-¹⁰/s
    CRR    (N):    tempered at 657 °C (1215 °F) || tested at 482 °C (900 °F), hardness 277 BHN || 5.5 x 10^-¹¹/s to 8.1 x 10^-¹⁰/s
    CRR    (N):    tempered at 657 °C (1215 °F) || tested at 538 °C (1000 °F), hardness 269 BHN || 1 x 10^-¹⁰/s to 2.1 x 10^-⁹/s

return to listing

6061

    UTS    (R):    O temper || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T4 & T451 tempers || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, sheet & rolled-and-drawn products || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    O temper || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T4 & T451 tempers || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, sheet & rolled-and-drawn products || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    O temper || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    O temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T4 & T451 tempers || values after 100,000 h hold time || -253.1 °C (-423.7 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, sheet & rolled-and-drawn products || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6, T651, & T6511 tempers (except T6 sheet & rolled-and-drawn products) || values after 100,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper, solution treated, cold worked 21%, aged 18 h at 160 °C (320 °F) || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    CRR    (N):    T6 temper, sheet || tested at 32 °C (90 °F) || 2.4 x 10^-⁸/s to 1.4 x 10^-⁶/s
    CRR    (N):    T6 temper, sheet || tested at 100 °C (212 °F) || 3 x 10^-⁹/s to 7.4 x 10^-⁷/s
    CRR    (N):    T6 temper, sheet || tested at 149 °C (300 °F) || 7 x 10^-¹⁰/s to 2.5 x 10^-⁵/s
    CRR    (N):    T6 temper, sheet || tested at 204 °C (400 °F) || 5.5 x 10^-¹¹/s to 4.6 x 10^-⁷/s

return to listing

6063

    UTS    (R):    O temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    O temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T1 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T1 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T1 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T1 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T1 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T1 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, extruded rod || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T5 temper, extruded rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T5 temper, extruded rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, extruded rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, extruded rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, extruded rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T1 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T1 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T1 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T1 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T1 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T1 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, extruded rod || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T5 temper, extruded rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T5 temper, extruded rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, extruded rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, extruded rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, extruded rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T1 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T1 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T1 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T1 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T1 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T1 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, extruded rod || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T5 temper, extruded rod || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T5 temper, extruded rod || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, extruded rod || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, extruded rod || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, extruded rod || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions || values after 0.1 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    CRR    (N):    T6 temper, extrusion || tested at 32 °C (90 °F) || 4.3 x 10^-⁹/s to 2.9 x 10^-⁷/s
    CRR    (N):    T6 temper, extrusion || tested at 100 °C (212 °F) || 7 x 10^-⁹/s to 2 x 10^-⁶/s
    CRR    (N):    T6 temper, extrusion || tested at 149 °C (300 °F) || 5 x 10^-¹⁰/s to 2.8 x 10^-⁷/s
    CRR    (N):    T6 temper, extrusion || tested at 204 °C (400 °F) || 1.8 x 10^-¹⁰/s to 1.1 x 10^-⁷/s

return to listing

6066

    UTS    (R):    T6511 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T6511 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T6511 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T6511 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T6511 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T6511 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T6511 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T6511 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T6511 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T6511 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T6511 temper, extrusions || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T6511 temper, extrusions || values after 10 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T6511 temper, extrusions || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T6511 temper, extrusions || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T6511 temper, extrusions || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)

return to listing

6070

    UTS    (R):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)

return to listing

6101

    UTS    (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T63 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T63 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T63 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T63 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T63 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T64 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T64 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T64 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T64 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T64 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T8 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T63 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T63 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T63 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T63 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T63 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T64 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T64 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T64 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T64 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T64 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T8 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T61 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T63 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T63 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T63 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T63 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T63 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T64 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T64 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T64 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T64 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T64 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T8 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

6151

    UTS    (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

6201

    UTS    (R):    T81 temper, wire || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T81 temper, wire || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T81 temper, wire || values after 100 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T81 temper, wire || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T81 temper, wire || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T81 temper, wire || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T81 temper, wire || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T81 temper, wire || values after 100 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T81 temper, wire || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T81 temper, wire || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T81 temper, wire || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T81 temper, wire || values after 10 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T81 temper, wire || values after 100 h hold time || -196.1 °C (-321.1 °F) to 177 °C (350 °F)
    %El    (N):    T81 temper, wire || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 149 °C (300 °F)
    %El    (N):    T81 temper, wire || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 149 °C (300 °F)

return to listing

6262

    UTS    (R):    T9 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T9 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T9 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T9 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T9 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T9 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T9 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T9 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T9 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T9 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T9 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T9 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T9 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T9 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T9 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

6351

    UTS    (R):    T5 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T5 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T5 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T5 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T6 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 149 °C (300 °F)
    YS     (R):    T5 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T5 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T5 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T5 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T6 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 149 °C (300 °F)
    %El    (N):    T5 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T5 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T5 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T5 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T6 temper, extrusions || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T6 temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 149 °C (300 °F)

return to listing

6951

    UTS    (R):    O temper || values after hold times of 0.5 h to 10,000 h || 20 °C (68 °F) to 593 °C (1099 °F)
    UTS    (R):    T4 temper || values after 0.5 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    UTS    (R):    T4 temper || values after 10,000 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    UTS    (R):    T6 temper || values after 0.5 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    YS     (R):    O temper || values after hold times of 0.5 h to 10,000 h || 20 °C (68 °F) to 593 °C (1099 °F)
    YS     (R):    T4 temper || values after 0.5 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    YS     (R):    T4 temper || values after 10,000 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || 20 °C (68 °F) to 593 °C (1099 °F)

return to listing

7005

    UTS    (R):    T53 temper, extrusions || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T53 temper, extrusions || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T53 temper, extrusions || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T53 temper, extrusions || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T53 temper, extrusions || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T53 temper, extrusions || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T63 & T6351 tempers, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T53 temper, extrusions || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T63 & T6351 tempers, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T53 temper, extrusions || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 0.1 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T63 & T6351 tempers, plate || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)

return to listing

7039

    UTS    (R):    T61 & T6151 tempers, sheet & plate || -269.1 °C (-452.5 °F) to 24 °C (75 °F)
    UTS    (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T61 & T6151 tempers, sheet & plate || -269.1 °C (-452.5 °F) to 24 °C (75 °F)
    YS     (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T61 & T6151 tempers, sheet & plate || -269.1 °C (-452.5 °F) to 24 °C (75 °F)
    %El    (N):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T63 & T6351, plate ≤ 38.1 mm (1.5 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)

return to listing

7049

    CRS    (R):    0.1% plastic strain, T7351 temper, plate || tested at 121 °C (250 °F) || 0.5 h to 160 h
    CRS    (R):    0.1% plastic strain, T7351 temper, plate || tested at 177 °C (350 °F) || 0.5 h to 550 h
    CRS    (R):    0.1% plastic strain, T7351 temper, plate || tested at 260 °C (500 °F) || 0.2 h to 50 h
    CRS    (R):    0.1% plastic strain, T7351 temper, plate || Master curve (LMP) || 5.48 h to 9.1 h
    CRS    (R):    0.2% plastic strain, T7351 temper, plate || tested at 121 °C (250 °F) || 0.1 h to 770 h
    CRS    (R):    0.2% plastic strain, T7351 temper, plate || tested at 177 °C (350 °F) || 1.8 h to 1,650 h
    CRS    (R):    0.2% plastic strain, T7351 temper, plate || tested at 260 °C (500 °F) || 0.6 h to 300 h
    CRS    (R):    0.2% plastic strain, T7351 temper, plate || Master curve (LMP) || 5.52 h to 9.32 h
    CRS    (R):    0.5% plastic strain, T7351 temper, plate || tested at 121 °C (250 °F) || 0.3 h to 2,770 h
    CRS    (R):    0.5% plastic strain, T7351 temper, plate || tested at 177 °C (350 °F) || 6 h to 5,200 h
    CRS    (R):    0.5% plastic strain, T7351 temper, plate || tested at 260 °C (500 °F) || 2 h to 2,000 h
    CRS    (R):    0.5% plastic strain, T7351 temper, plate || Master curve (LMP) || 5.2 h to 9.7 h
    CRS    (R):    1% plastic strain, T7351 temper, plate || tested at 121 °C (250 °F) || 0.6 h to 140 h
    CRS    (R):    1% plastic strain, T7351 temper, plate || tested at 177 °C (350 °F) || 8 h to 530 h
    CRS    (R):    1% plastic strain, T7351 temper, plate || tested at 260 °C (500 °F) || 4 h to 4,800 h
    CRS    (R):    1% plastic strain, T7351 temper, plate || Master curve (LMP) || 8.59 h to 13.7 h
    CRS    (R):    2% plastic strain, T7351 temper, plate || Master curve (LMP) || 8.32 h to 12.6 h

return to listing

7050

    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 10 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 100 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    UTS    (R):    T7452 forgings, longitudinal || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 10 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 100 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    YS     (R):    T7452 forgings, longitudinal || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.1 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7451, plate 25.4 mm to 50.8 mm (1 inch to 2 inch) || values after 10,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 10 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 100 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)
    %El    (N):    T7452 forgings, longitudinal || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 205 °C (401 °F)

return to listing

7075

    UTS    (R):    O temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T73 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T73 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T73 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T73 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T73 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T76 & T651 tempers || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T76 & T651 tempers || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T76 & T651 tempers || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T76 & T651 tempers || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    UTS    (R):    T76 & T651 tempers || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    O temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T73 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T73 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T73 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T73 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T73 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T76 & T651 tempers || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T76 & T651 tempers || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T76 & T651 tempers || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T76 & T651 tempers || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    YS     (R):    T76 & T651 tempers || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    O temper, extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    O temper, except extrusions || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 temper, die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T6511 tempers, extrusions 6.35 mm to 76.2 mm (0.25 inch to 3 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T6 & T651 tempers, except die forgings > 50.8 mm (2 inch) || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T73 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T73 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T73 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T73 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T73 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T76 & T651 tempers || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T76 & T651 tempers || values after 10 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T76 & T651 tempers || values after 100 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T76 & T651 tempers || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    %El    (N):    T76 & T651 tempers || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)
    CRR    (N):    T6 temper sheet || tested at 34 °C (94 °F) || 3.6 x 10^-¹⁰/s to 8.7 x 10^-⁷/s
    CRR    (N):    T6 temper sheet || tested at 100 °C (212 °F) || 4.5 x 10^-⁹/s to 7.5 x 10^-⁵/s
    CRR    (N):    T6 temper sheet || tested at 149 °C (300 °F) || 1.3 x 10^-⁹/s to 5.7 x 10^-⁵/s
    CRR    (N):    T6 temper sheet || tested at 191 °C (375 °F) || 9.4 x 10^-¹⁰/s to 7.7 x 10^-⁶/s
    CRR    (N):    T6 temper sheet || tested at 204 °C (400 °F) || 1.2 x 10^-⁸/s to 1.1 x 10^-⁶/s
    CRR    (N):    T6 temper sheet || tested at 316 °C (600 °F) || 3 x 10^-⁸/s to 2.4 x 10^-⁶/s

return to listing

7079

    UTS    (R):    T6 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T651 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T651 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T651 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T651 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 & T651 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T651 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T651 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T651 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T651 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 & T651 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T651 tempers || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T651 tempers || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T651 tempers || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T651 tempers || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 & T651 tempers || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)

return to listing

7175

    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 100 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    UTS    (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 100 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    YS     (R):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.1 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 100 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)
    %El    (N):    T74 & T736 tempers, die forgings ≤ 76.2 mm (3 inch), longitudinal || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 232 °C (449 °F)

return to listing

7178

    UTS    (R):    T6 temper, except extrusions || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, except extrusions || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, except extrusions || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, except extrusions || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, except extrusions || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T76 & T7651 tempers || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T76 & T7651 tempers || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T76 & T7651 tempers || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T76 & T7651 tempers || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T76 & T7651 tempers || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, except extrusions || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, except extrusions || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, except extrusions || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, except extrusions || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, except extrusions || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T76 & T7651 tempers || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T76 & T7651 tempers || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T76 & T7651 tempers || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T76 & T7651 tempers || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T76 & T7651 tempers || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, except extrusions || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, except extrusions || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, except extrusions || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, except extrusions || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, except extrusions || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T76 & T7651 tempers || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T76 & T7651 tempers || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T76 & T7651 tempers || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T76 & T7651 tempers || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T76 & T7651 tempers || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

7475

    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    UTS    (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    YS     (R):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T61 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.1 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 100 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)
    %El    (N):    T761 temper, sheet 1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 538 °C (1000 °F)

return to listing

8280

    UTS    (R):    O temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    O temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    O temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    O temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    H14 temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    H14 temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    H14 temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    UTS    (R):    H14 temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    O temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    O temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    O temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    O temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    H14 temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    H14 temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    H14 temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    YS     (R):    H14 temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    O temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    O temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    O temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    O temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    H14 temper || values after 0.5 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    H14 temper || values after 10 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    H14 temper || values after 100 h hold time || 20 °C (68 °F) to 205 °C (401 °F)
    %El    (N):    H14 temper || values after 1,000 h hold time || 20 °C (68 °F) to 205 °C (401 °F)

return to listing

201.0

    UTS    (R):    T7 temper, sand castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 177 °C (350 °F)
    UTS    (R):    T7 temper, sand castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)
    UTS    (R):    T7 temper, sand castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)
    YS     (R):    T7 temper, sand castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 177 °C (350 °F)
    YS     (R):    T7 temper, sand castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)
    YS     (R):    T7 temper, sand castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)
    %El    (N):    T7 temper, sand castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 177 °C (350 °F)
    %El    (N):    T7 temper, sand castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)
    %El    (N):    T7 temper, sand castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 316 °C (601 °F)

return to listing

224.0

    UTS    (R):    T7 temper || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T7 temper || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T7 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T7 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper || values after 10,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (R):    T7 temper || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T7 temper || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T7 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T7 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper || values after 10,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)
    %El    (N):    T7 temper || values after 0.1 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T7 temper || values after 0.5 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T7 temper || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T7 temper || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper || values after 10,000 h hold time || 20 °C (68 °F) to 260 °C (500 °F)

return to listing

242.0

    UTS    (R):    T571 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T571 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T571 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T571 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T571 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T77 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T77 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T77 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T77 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T77 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T571 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T571 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T571 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T571 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T571 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T77 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T77 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T77 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T77 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T77 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T571 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T571 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T571 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T571 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T571 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T77 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T77 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T77 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T77 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T77 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    T77 temper, sand castings || tested at 149 °C (300 °F) || 2.3 x 10^-¹⁰/s to 5.2 x 10^-⁹/s
    CRR    (N):    T77 temper, sand castings || tested at 204 °C (400 °F) || 2.2 x 10^-⁹/s to 4.55 x 10^-⁷/s

return to listing

249.0

    UTS    (R):    T7 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T7 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T7 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T7 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    UTS    (R):    T7 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T7 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T7 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T7 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T7 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    YS     (R):    T7 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T7 temper || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T7 temper || values after 10 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T7 temper || values after 100 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T7 temper || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)
    %El    (N):    T7 temper || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 205 °C (401 °F)

return to listing

295.0

    UTS    (R):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    CRR    (N):    T6 temper, sand cast || tested at 32 °C (90 °F) || 1 x 10^-⁹/s to 4.4 x 10^-⁹/s
    CRR    (N):    T6 temper, sand cast || tested at 100 °C (212 °F) || 3.8 x 10^-¹⁰/s to 2.8 x 10^-⁹/s
    CRR    (N):    T6 temper, sand cast || tested at 149 °C (300 °F) || 2.2 x 10^-¹⁰/s to 6.6 x 10^-⁸/s
    CRR    (N):    T6 temper, sand cast || tested at 204 °C (400 °F) || 1.1 x 10^-¹⁰/s to 8.8 x 10^-⁸/s
    CRR    (N):    T6 temper, sand cast || tested at 316 °C (600 °F) || 3.6 x 10^-¹⁰/s to 8.1 x 10^-¹⁰/s

return to listing

319.0

    UTS    (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

332.0

    UTS    (R):    T5 temper, permanent mold castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 10,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)

return to listing

333.0

    UTS    (R):    T5 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T5 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T5 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T5 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

336.0

    UTS    (R):    T551 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T551 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T551 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T551 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T551 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS   (N*):    T65 temper, sand castings || room temperature value
    YS     (R):    T551 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T551 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T551 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T551 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T551 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS    (N*):    T65 temper, sand castings || room temperature value
    %El    (N):    T551 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T551 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T551 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T551 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T551 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El   (N*):    T65 temper, sand castings || room temperature value
    SR     (N):    T551 temper, permanent mold cast || tested at 100 °C (212 °F) || 1 h to 1,000 h
    SR     (N):    T551 temper, permanent mold cast || tested at 149 °C (300 °F) || 10 h to 1,000 h
    SR     (N):    T551 temper, permanent mold cast || tested at 204 °C (400 °F) || 10 h to 1,000 h
    SR     (N):    T551 temper, permanent mold cast || Master curve (LMP) || 8.95 h to 12.9 h
    CRS    (N):    0.6% total strain, T551 temper, permanent mold cast || tested at 204 °C (400 °F) || 10 h to 1,000 h
    CRS    (N):    1% total strain, T551 temper, permanent mold cast || tested at 204 °C (400 °F) || 1 h to 100 h
    CRR    (N):    T551 temper, permanent mold cast || tested at 100 °C (212 °F) || 2.7 x 10^-¹¹/s to 1.85 x 10^-¹⁰/s
    CRR    (N):    T551 temper, permanent mold cast || tested at 149 °C (300 °F) || 3.6 x 10^-¹⁰/s to 4.8 x 10^-⁹/s
    CRR    (N):    T551 temper, permanent mold cast || tested at 204 °C (400 °F) || 5.9 x 10^-¹⁰/s to 3.3 x 10^-⁷/s

return to listing

354.0

    UTS    (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)

return to listing

355.0

    UTS    (R):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T771 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T771 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T771 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T771 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T771 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T771 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T771 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T771 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T771 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T771 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T771 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T771 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T771 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T771 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T771 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    CRR    (N):    T71 temper, permanent mold cast || tested at 32 °C (90 °F) || 8 x 10^-¹⁰/s to 6 x 10^-⁸/s
    CRR    (N):    T71 temper, permanent mold cast || tested at 100 °C (212 °F) || 1.3 x 10^-¹⁰/s to 1.05 x 10^-⁸/s
    CRR    (N):    T71 temper, permanent mold cast || tested at 149 °C (300 °F) || 2.1 x 10^-¹⁰/s to 9 x 10^-⁷/s
    CRR    (N):    T71 temper, permanent mold cast || tested at 204 °C (400 °F) || 6 x 10^-¹⁰/s to 1.25 x 10^-⁷/s
    CRR    (N):    T71 temper, sand cast || tested at 32 °C (90 °F) || 1.5 x 10^-¹⁰/s to 3.5 x 10^-¹⁰/s
    CRR    (N):    T71 temper, sand cast || tested at 100 °C (212 °F) || 2.4 x 10^-¹⁰/s to 9 x 10^-⁸/s
    CRR    (N):    T71 temper, sand cast || tested at 149 °C (300 °F) || 1.2 x 10^-¹⁰/s to 1.6 x 10^-⁶/s
    CRR    (N):    T71 temper, sand cast || tested at 204 °C (400 °F) || 3.6 x 10^-¹⁰/s to 7.4 x 10^-⁶/s
    CRR    (N):    T71 temper, sand & permanent mold castings combined || tested at 32 °C (90 °F) || 1.5 x 10^-¹⁰/s to 6 x 10^-⁸/s
    CRR    (N):    T71 temper, sand & permanent mold castings combined || tested at 100 °C (212 °F) || 1.3 x 10^-¹⁰/s to 9 x 10^-⁸/s
    CRR    (N):    T71 temper, sand & permanent mold castings combined || tested at 149 °C (300 °F) || 1.2 x 10^-¹⁰/s to 1.6 x 10^-⁶/s
    CRR    (N):    T71 temper, sand & permanent mold castings combined || tested at 204 °C (400 °F) || 3.6 x 10^-¹⁰/s to 7.4 x 10^-⁶/s

return to listing

356.0

    UTS    (R):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T7 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T7 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 100 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -253.1 °C (-423.7 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T7 temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    T7 temper, sand cast || tested at 32 °C (90 °F) || 1.3 x 10^-⁹/s to 2.1 x 10^-⁸/s
    CRR    (N):    T7 temper, sand cast || tested at 100 °C (212 °F) || 4 x 10^-¹⁰/s to 3.4 x 10^-⁸/s
    CRR    (N):    T7 temper, sand cast || tested at 149 °C (300 °F) || 2.05 x 10^-⁹/s to 1.85 x 10^-⁵/s
    CRR    (N):    T7 temper, sand cast || tested at 204 °C (400 °F) || 1.8 x 10^-¹⁰/s to 1.1 x 10^-⁷/s

return to listing

359.0

    UTS    (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T62 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T62 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T62 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    UTS    (R):    T62 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    T62 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T62 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T62 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T62 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    YS     (R):    T62 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    T62 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T62 temper, permanent mold castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T62 temper, permanent mold castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T62 temper, permanent mold castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 316 °C (601 °F)
    %El    (N):    T62 temper, permanent mold castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    T62 temper, permanent mold castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)

return to listing

360.0

    UTS    (R):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)

return to listing

380.0

    UTS    (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

384.0

    UTS    (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

518.0

    UTS    (R):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    UTS    (R):    F temper, sand castings || values after 5,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    YS     (R):    F temper, sand castings || values after 5,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)
    %El    (N):    F temper, sand castings || values after 5,000 h hold time || 20 °C (68 °F) to 316 °C (601 °F)

return to listing

520.0

    UTS    (R):    T4 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T4 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T4 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T4 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)

return to listing

710.0

    UTS    (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    UTS    (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    YS     (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)
    %El    (N):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 260 °C (500 °F)

return to listing

A201 Grade B

SR (N): stress-relieved 2 h at 621 °C (1150 °F), air cooled, 25.4 mm (1 inch) plate || tested at 538 °C (1000 °F) || 0.1 h to 1 x 10⁴ h
CRR (N): stress-relieved 2 h at 621 °C (1150 °F), air cooled, 25.4 mm (1 inch) plate || tested at 538 °C (1000 °F) || 2.7 x 10^-¹¹/s to 4.45 x 10^-⁴/s

return to listing

A106 Grade B

SR (N): as-rolled pipe || tested at 538 °C (1000 °F) || 0.1 h to 1.2 x 10⁴ h
CRR (N): as-rolled pipe || tested at 538 °C (1000 °F) || 4.7 x 10^-¹⁰/s to 1.65 x 10^-⁶/s

return to listing

A206.0

    FSN    (N):    T7 temper, castings, smooth || tested at 21 °C (70 °F), R = 0.1, axial, maximum stress || 150 cycles to 1 x 10⁷ cycles
    FSN    (N):    T7 temper, castings, smooth || tested at 177 °C (350 °F), R = 0.1, axial, maximum stress || 2 cycles to 1 x 10⁶ cycles
    FSN    (N):    T7 temper, castings, notched || tested at 21 °C (70 °F), R = 0.1, axial, K_t = 3.0, maximum stress || 2 x 10³ cycles to 2.2 x 10⁵ cycles
    FSN    (N):    T7 temper, castings, notched || tested at 177 °C (350 °F), R = 0.1, axial, K_t = 3.0, maximum stress || 1.9 x 10³ cycles to 3 x 10⁶ cycles

return to listing

A319

FSN (N): T7 temper, castings || tested at 20 °C (68 °F), R = -1, aged at 260 °C (500 °F), ultrasonic, 20 kHz, Pf = 10%, stress amplitude || 5 x 10⁴ cycles to 1 x 10⁹ cycles
FSN (N): T7 temper, castings || tested at 20 °C (68 °F), R = -1, aged at 260 °C (500 °F), ultrasonic, 20 kHz, Pf = 90%, stress amplitude || 5 x 10⁴ cycles to 1 x 10⁹ cycles

return to listing

A240.0

    UTS    (R):    F temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)

return to listing

A355.0

    UTS    (R):    T51 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    UTS    (R):    T51 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (R):    T51 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 0.5 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 100 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 1,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    T51 temper, sand castings || values after 10,000 h hold time || 20 °C (68 °F) to 371 °C (700 °F)

return to listing

A356.0

    UTS    (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (N):    T6 temper, permanent mold castings || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (N):    T6 temper, permanent mold castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    UTS    (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (N):    T6 temper, permanent mold castings || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (N):    T6 temper, permanent mold castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    YS     (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 0.5 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 100 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 1,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper, permanent mold castings || values after 10,000 h hold time || -269.1 °C (-452.5 °F) to 371 °C (700 °F)
    SR     (R):    T6 temper, permanent mold || tested at 149 °C (300 °F) || 0.1 h to 1,000 h

return to listing

A360.0

    UTS    (R):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 0.5 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 100 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 1,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10,000 h hold time || -80 °C (-112 °F) to 371 °C (700 °F)

return to listing

A380.0

    UTS    (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, die castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)

return to listing

Aluminum

CRS (N): 1% total strain || tested at 316 °C (600 °F) || 10 h to 100 h
CRR (N): 1.65 mm (0.065 inch) sheet || tested at 316 °C (600 °F) || 2.1 x 10^-⁸/s to 3.2 x 10^-⁷/s

return to listing

API X80 pipeline steel

    FSN    (R):    rotary bending fatigue || tested at 25 °C (77 °F), R = -1, maximum stress || 2 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (R):    rotary bending fatigue || tested at -50 °C (-58 °F), R = -1, maximum stress || 4 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (R):    rotary bending fatigue || tested at -80 °C (-112 °F), R = -1, maximum stress || 6 x 10⁴ cycles to 1 x 10⁸ cycles

return to listing

ASME Grade P23/T23

    SR     (R):    normalized & tempered || tested at 500 °C (932 °F) || 10 h to 3.6 x 10⁴ h
    SR     (R):    normalized & tempered || tested at 550 °C (1022 °F) || 50 h to 1.1 x 10⁴ h
    SR     (R):    normalized & tempered || tested at 600 °C (1112 °F) || 50 h to 1.1 x 10⁴ h
    SR     (R):    normalized & tempered || Master curve (LMP) || 16.1 h to 20.7 h

return to listing

ASME Grade T23

    SR     (R):    normalized 10 min & tempered || tested at 500 °C (932 °F) || 120 h to 3.4 x 10⁴ h
    SR     (R):    normalized 10 min & tempered || tested at 550 °C (1022 °F) || 190 h to 9,000 h
    SR     (R):    normalized 10 min & tempered || tested at 600 °C (1112 °F) || 90 h to 5.3 x 10⁴ h
    SR     (R):    normalized 10 min & tempered || Master curve (LMP) || 20.5 h to 25 h
    SR     (R):    normalized 0.5 h & tempered || tested at 500 °C (932 °F) || 180 h to 1.9 x 10⁴ h
    SR     (R):    normalized 0.5 h & tempered || tested at 550 °C (1022 °F) || 220 h to 7,000 h
    SR     (R):    normalized 0.5 h & tempered || tested at 600 °C (1112 °F) || 290 h to 3.3 x 10⁴ h
    SR     (R):    normalized 0.5 h & tempered || Master curve (LMP) || 10.7 h to 14.1 h

return to listing

ASME P92 (9 Cr - 0.5 Mo - 2 W (wt %))

    FEN    (N):    as-received || tested at 20 °C (68 °F), R = -1, axial, elastic strain range || 450 cycles to 3.4 x 10³ cycles
    FEN    (N):    as-received || tested at 20 °C (68 °F), R = -1, axial, plastic strain range || 450 cycles to 3.4 x 10³ cycles
    FEN    (R):    normalized & tempered || tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude, Wang et al. || 250 cycles to 1 x 10⁴ cycles
    FEN    (R):    normalized & tempered || tested at 600 °C (1112 °F), R = -1, axial, elastic strain amplitude, Wang et al. || 250 cycles to 1 x 10⁴ cycles
    FEN    (R):    normalized & tempered || tested at 600 °C (1112 °F), R = -1, axial, plastic strain amplitude, Wang et al. || 250 cycles to 1 x 10⁴ cycles

return to listing

ASTM A213 / SA-387 (9 Cr - 1 Mo (wt %) or G91)

    SR     (R):    normalized at 1050 °C (1922 °F) for 1 h, air cooled, tempered at 760 °C (1400 °F) for 2 h || tested at 538 °C (1000 °F) || 10 h to 1 x 10⁶ h
    SR     (R):    normalized at 1050 °C (1922 °F) for 1 h, air cooled, tempered at 760 °C (1400 °F) for 2 h || tested at 593 °C (1100 °F) || 10 h to 1 x 10⁶ h
    SR     (R):    normalized at 1050 °C (1922 °F) for 1 h, air cooled, tempered at 760 °C (1400 °F) for 2 h || Master curve (LMP) || 26 h to 30.9 h

return to listing

ASTM A192

    SR     (N):    0.5 h at 704 °C (1300 °F), furnace cooled || tested at 454 °C (850 °F) || 45 h to 8,650 h
    SR     (N):    0.5 h at 704 °C (1300 °F), furnace cooled || tested at 510 °C (950 °F) || 80 h to 6,700 h
    SR     (N):    0.5 h at 704 °C (1300 °F), furnace cooled || Master curve (LMP) || 19.2 h to 22.3 h

return to listing

AZ31

CRR (N): H24 temper, sheet || tested at 149 °C (300 °F) || 5.2 x 10^-⁸/s to 1.1 x 10^-⁵/s
CRR (N): H24 temper, sheet || tested at 232 °C (450 °F) || 2.7 x 10^-⁷/s to 2.05 x 10^-⁵/s

return to listing

AZ61

CRR (N): F temper, extrusion || tested at 35 °C (95 °F) || 4 x 10^-¹¹/s to 9.5 x 10^-¹¹/s

return to listing

AZ63

    CRR    (N):    T6 temper, sand casting || tested at 35 °C (95 °F) || 5 x 10^-¹¹/s to 9.5 x 10^-¹¹/s
    CRR    (N):    T6 temper, sand casting || tested at 93 °C (200 °F) || 7 x 10^-¹¹/s to 1.9 x 10^-¹⁰/s
    CRR    (N):    T6 temper, sand casting || tested at 149 °C (300 °F) || 2.8 x 10^-¹⁰/s to 1.3 x 10^-⁹/s

return to listing

AZ81

FSN (N): T4 temper, castings || tested at 20 °C (68 °F), R = -1, notched, K_t = 2.6, rotating beam, maximum stress || 1.1 x 10⁴ cycles to 2.5 x 10⁸ cycles

return to listing

AZ92

    CRR    (N):    T6 temper, sand casting || tested at 35 °C (95 °F) || 2.2 x 10^-¹¹/s to 1.8 x 10^-¹⁰/s
    CRR    (N):    T6 temper, sand casting || tested at 93 °C (200 °F) || 3.8 x 10^-¹¹/s to 3.2 x 10^-¹⁰/s
    CRR    (N):    T6 temper, sand casting || tested at 149 °C (300 °F) || 1 x 10^-¹⁰/s to 2.3 x 10^-⁹/s

return to listing

B443.0

    UTS    (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 0.5 h hold time || 23 °C (73 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10 h hold time || 23 °C (73 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 100 h hold time || 23 °C (73 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 1,000 h hold time || 23 °C (73 °F) to 371 °C (700 °F)
    %El    (N):    F temper, sand castings || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    CRR    (N):    F temper, sand cast || tested at 32 °C (90 °F) || 4.6 x 10^-⁹/s to 2 x 10^-⁶/s
    CRR    (N):    F temper, sand cast || tested at 100 °C (212 °F) || 5.2 x 10^-¹⁰/s to 3.4 x 10^-⁵/s
    CRR    (N):    F temper, sand cast || tested at 149 °C (300 °F) || 6.3 x 10^-¹⁰/s to 8.6 x 10^-⁶/s
    CRR    (N):    F temper, sand cast || tested at 204 °C (400 °F) || 5.5 x 10^-⁸/s to 9.8 x 10^-⁷/s

return to listing

C355.0

    UTS    (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    UTS    (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    YS     (R):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 0.5 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 100 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 1,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    %El    (N):    T6 temper || values after 10,000 h hold time || -196.1 °C (-321.1 °F) to 371 °C (700 °F)
    SR     (N):    T61 temper, permanent mold cast || tested at 149 °C (300 °F) || 0.1 h to 100 h
    SR     (N):    T61 temper, permanent mold cast || tested at 204 °C (400 °F) || 1 h to 100 h
    SR     (N):    T61 temper, permanent mold cast || tested at 260 °C (500 °F) || 1 h to 100 h
    SR     (N):    T61 temper, permanent mold cast || Master curve (LMP) || 8.73 h to 12.6 h
    CRS    (N):    0.1% plastic strain, T61 temper || tested at 149 °C (300 °F) || 0.1 h to 10 h
    CRS    (N):    0.1% plastic strain, T61 temper || tested at 204 °C (400 °F) || 0.1 h to 1 h
    CRS    (N):    0.1% plastic strain, T61 temper || Master curve (LMP) || 2.83 h to 3.68 h
    CRS    (N):    0.2% plastic strain, T61 temper || tested at 149 °C (300 °F) || 1 h to 10 h
    CRS    (N):    0.2% plastic strain, T61 temper || tested at 204 °C (400 °F) || 0.1 h to 10 h
    CRS    (N):    0.2% plastic strain, T61 temper || Master curve (LMP) || 2.66 h to 3.62 h
    CRS    (N):    0.5% plastic strain, T61 temper || tested at 149 °C (300 °F) || 0.1 h to 100 h
    CRS    (N):    0.5% plastic strain, T61 temper || tested at 204 °C (400 °F) || 1 h to 100 h
    CRS    (N):    0.5% plastic strain, T61 temper || tested at 260 °C (500 °F) || 0.1 h to 100 h
    CRS    (N):    0.5% plastic strain, T61 temper || Master curve (LMP) || 9.15 h to 13.2 h
    CRS    (N):    1% plastic strain, T61 temper || tested at 149 °C (300 °F) || 0.1 h to 100 h
    CRS    (N):    1% plastic strain, T61 temper || tested at 204 °C (400 °F) || 1 h to 100 h
    CRS    (N):    1% plastic strain, T61 temper || tested at 260 °C (500 °F) || 1 h to 100 h
    CRS    (N):    1% plastic strain, T61 temper || Master curve (LMP) || 9.2 h to 13.2 h
    IC     (N):    tested at 149 °C (300 °F), plastic strain, T61 temper || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 149 °C (300 °F), plastic strain, T61 temper || 1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 149 °C (300 °F), plastic strain, T61 temper || 3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 149 °C (300 °F), plastic strain, T61 temper || 10 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 177 °C (350 °F), plastic strain, T61 temper || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 177 °C (350 °F), plastic strain, T61 temper || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 177 °C (350 °F), plastic strain, T61 temper || 1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 204 °C (400 °F), plastic strain, T61 temper || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 204 °C (400 °F), plastic strain, T61 temper || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 232 °C (450 °F), plastic strain, T61 temper || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (N):    tested at 232 °C (450 °F), plastic strain, T61 temper || 0.3 h || 0 to 0.01 mm/mm strain

return to listing

CA6NM

    SR     (R):    hardened & tempered || tested at 482 °C (900 °F) || 50 h to 1 x 10⁵ h
    SR     (R):    hardened & tempered || tested at 538 °C (1000 °F) || 12 h to 1 x 10⁵ h
    SR     (R):    hardened & tempered || Master curve (LMP) || 20.9 h to 25.1 h

return to listing

410 Cb (New)

    UTS   (*):    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || room temperature value
    UTS   (*):    2 h at 1100 °C (2012 °F), air cooled, 2 h at 650 °C (1202 °F), furnace cooled || room temperature value
    UTS   (*):    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || room temperature value
    UTS   (*):    1121 °C (2050 °F), oil quenched, 649 °C (1200 °F), air cooled, 649 °C (1200 °F), air cooled || room temperature value
    UTS   (*):    1093 °C (2000 °F), oil quenched, 649 °C (1200 °F), air cooled || room temperature value
    YS    (*):    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || room temperature value
    YS    (*):    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || room temperature value
    YS    (*):    1121 °C (2050 °F), oil quenched, 649 °C (1200 °F), air cooled, 649 °C (1200 °F), air cooled || room temperature value
    YS    (*):    1093 °C (2000 °F), oil quenched, 649 °C (1200 °F), air cooled || room temperature value
    %El   (*):    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || room temperature value
    %El   (*):    2 h at 1100 °C (2012 °F), air cooled, 2 h at 650 °C (1202 °F), furnace cooled || room temperature value
    %El   (*):    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || room temperature value
    %El   (*):    1121 °C (2050 °F), oil quenched, 649 °C (1200 °F), air cooled, 649 °C (1200 °F), air cooled || room temperature value
    %El   (*):    1093 °C (2000 °F), oil quenched, 649 °C (1200 °F), air cooled || room temperature value
    SR        :    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 1 h to 800 h
    SR        :    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || tested at 593 °C (1100 °F) || 7 h to 700 h
    SR        :    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || Master curve (LMP) || 24.6 h to 28.4 h
    SR        :    2 h at 1100 °C (2012 °F), air cooled, 2 h at 650 °C (1202 °F), furnace cooled || tested at 482 °C (900 °F) || 16 h to 2 x 10⁴ h
    SR        :    2 h at 1100 °C (2012 °F), air cooled, 2 h at 650 °C (1202 °F), furnace cooled || tested at 538 °C (1000 °F) || 2 h to 4,000 h
    SR        :    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 400 h to 2,400 h
    SR        :    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 10 h to 43 h
    SR        :    0.5 h at 1163 °C (2125 °F), oil quenched, 2 h at 649 °C (1200 °F), air cooled, 2 h at 649 °C (1200 °F), air cooled || Master curve (LMP) || 17.9 h to 19.5 h
    SR        :    1121 °C (2050 °F), oil quenched, 649 °C (1200 °F), air cooled, 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 12 h to 2,600 h
    SR        :    1093 °C (2000 °F), oil quenched, 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 400 h to 2,400 h
    CRR       :    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || tested at 538 °C (1000 °F) || 8 x 10^-¹¹/s to 3 x 10^-⁸/s
    CRR       :    1 h at 982 °C (1800 °F), oil quenched, 1 h at 649 °C (1200 °F), air cooled || tested at 593 °C (1100 °F) || 1 x 10^-¹⁰/s to 1.4 x 10^-⁸/s

return to listing

9 Cr - 1 Mo - V - Nb (wt %) (T91)

SR (R): heat treated tube || Master curve (LMP) || 26.2 h to 32.3 h

return to listing

Cu - 8 Cr - 4 Nb (wt %)

    D     (N*):    solid || room temperature value
    TC     (N):    solid || as-extruded || 20 °C (68 °F) to 700 °C (1292 °F)
    SH     (N):    solid || as-extruded || 20 °C (68 °F) to 700 °C (1292 °F)
    TD     (N):    solid || as-extruded || 20 °C (68 °F) to 700 °C (1292 °F)
    FEN    (N):    as-extruded || tested at 20 °C (68 °F), R = -1, axial, total strain range || 420 cycles to 1.7 x 10⁴ cycles
    FEN    (N):    as-extruded || tested at 538 °C (1000 °F), R = -1, axial, total strain range || 1.7 x 10³ cycles to 1.3 x 10⁴ cycles
    FEN    (N):    as-extruded || tested at 649 °C (1200 °F), R = -1, axial, total strain range || 2.2 x 10³ cycles to 1.1 x 10⁴ cycles
    SR     (N):    as-extruded || tested at 500 °C (932 °F) || 30 h to 2,300 h
    SR     (N):    as-extruded || tested at 650 °C (1202 °F) || 10 h to 680 h
    SR     (N):    as-extruded || tested at 800 °C (1472 °F) || 3 h to 100 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 500 °C (932 °F) || 5 h to 50 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 650 °C (1202 °F) || 3 h to 25 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 800 °C (1472 °F) || 0.3 h to 2 h
    CRS    (N):    1% plastic strain, as-extruded || Master curve (LMP) || 15.3 h to 22.4 h
    CRR    (N):    as-extruded || tested at 500 °C (932 °F) || 2.8 x 10^-⁹/s to 4.6 x 10^-⁷/s
    CRR    (N):    as-extruded || tested at 650 °C (1202 °F) || 9.5 x 10^-⁹/s to 7.6 x 10^-⁷/s
    CRR    (N):    as-extruded || tested at 800 °C (1472 °F) || 1 x 10^-⁷/s to 5 x 10^-⁶/s

return to listing

Cu - 4 Cr - 2 Nb (wt %)

    D     (N*):    solid || room temperature value
    TC     (N):    solid || as-extruded || 20 °C (68 °F) to 800 °C (1472 °F)
    SH     (N):    solid || as-extruded || 20 °C (68 °F) to 800 °C (1472 °F)
    TD     (N):    solid || as-extruded || 20 °C (68 °F) to 800 °C (1472 °F)
    SR     (N):    as-extruded || tested at 500 °C (932 °F) || 10 h to 900 h
    SR     (N):    as-extruded || tested at 650 °C (1202 °F) || 5 h to 240 h
    SR     (N):    as-extruded || tested at 800 °C (1472 °F) || 0.01 h to 35 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 500 °C (932 °F) || 1 h to 110 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 650 °C (1202 °F) || 0.3 h to 45 h
    CRS    (N):    1% plastic strain, as-extruded || tested at 800 °C (1472 °F) || 0.3 h to 1.5 h
    CRR    (N):    as-extruded || tested at 500 °C (932 °F) || 5.2 x 10^-⁹/s to 2 x 10^-⁶/s
    CRR    (N):    as-extruded || tested at 650 °C (1202 °F) || 3.2 x 10^-⁸/s to 1.5 x 10^-⁶/s
    CRR    (N):    as-extruded || tested at 800 °C (1472 °F) || 3.7 x 10^-⁷/s to 8.3 x 10^-⁴/s

return to listing

90 Cu - 10 Sn (wt %)

    UTS    (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 315 °C (599 °F)
    YS     (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 315 °C (599 °F)
    %El    (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 315 °C (599 °F)
    SR     (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 316 °C (600 °F) || 270 h to 720 h
    CRR    (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 260 °C (500 °F) || 1.15 x 10^-¹⁰/s to 4.05 x 10^-⁹/s
    CRR    (N):    as=cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 316 °C (600 °F) || 8.3 x 10^-¹¹/s to 5.6 x 10^-⁹/s

return to listing

Discaloy

    UTS   (N*):    forged disk, 1 h at 1038 °C (1900 °F), oil quenched, 20 h at 732 °C (1350 °F), furnace cool, 20 h at 649 °C (1200 °F), furnace cooled || room temperature value
    UTS   (N*):    forged disk, 1 h at 1066 °C (1950 °F), air cooled, 20 h at 732 °C (1350 °F) || room temperature value
    YS    (N*):    forged disk, 1 h at 1038 °C (1900 °F), oil quenched, 20 h at 732 °C (1350 °F), furnace cool, 20 h at 649 °C (1200 °F), furnace cooled || room temperature value
    YS    (N*):    forged disk, 1 h at 1066 °C (1950 °F), air cooled, 20 h at 732 °C (1350 °F) || room temperature value
    %El   (N*):    forged disk, 1 h at 1038 °C (1900 °F), oil quenched, 20 h at 732 °C (1350 °F), furnace cool, 20 h at 649 °C (1200 °F), furnace cooled || room temperature value
    %El   (N*):    forged disk, 1 h at 1066 °C (1950 °F), air cooled, 20 h at 732 °C (1350 °F) || room temperature value
    SR     (N):    forged disk, 1 h at 1066 °C (1950 °F), air cooled, 20 h at 732 °C (1350 °F) || tested at 649 °C (1200 °F) || 19 h to 760 h
    CRR    (N):    forged disk, 1 h at 1038 °C (1900 °F), oil quenched, 20 h at 732 °C (1350 °F), furnace cool, 20 h at 649 °C (1200 °F), furnace cooled || tested at 649 °C (1200 °F) || 2.6 x 10^-¹⁰/s to 1.2 x 10^-⁷/s

return to listing

DP 980

FSN (R): welded joints || tested at 20 °C (68 °F), R = 0.1, axial, MIG weld, stress range || 3 x 10⁴ cycles to 1 x 10⁷ cycles
FSN (R): welded joints || tested at 20 °C (68 °F), R = 0.1, axial, MAG weld, stress range || 2 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

Ductile iron (EN-GJS 700-2) (3.7 C - 2 Si - 1.2 Cu - 0.3 Mn (wt %))

FSN (R): heavy section, Si-Al-Ca inoculant || tested at 20 °C (68 °F), R = 0, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
FSN (R): heavy section, Bi-RE inoculant || tested at 20 °C (68 °F), R = 0, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

EOS StainlessSteel CX

FSN (R): laser powder bed fusion || tested at 20 °C (68 °F), R = 0.1, axial, vertical, as-built, machined surface, stress amplitude || 3 x 10⁴ cycles to 1 x 10⁶ cycles

return to listing

Ferrium C61 (AMS 6517)

    FSN    (R):    single tooth bending fatigue || tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress || 9 x 10³ cycles to 1 x 10⁷ cycles
    FSN    (R):    single tooth bending fatigue || tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress || 800 cycles to 1 x 10⁷ cycles
    FSN    (R):    single tooth bending fatigue || tested at 130 °C (266 °F), R = 0.05, 50% failure probability, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (R):    single tooth bending fatigue || tested at 130 °C (266 °F), R = 0.05, 1% failure probability, maximum stress || 4 x 10³ cycles to 1 x 10⁷ cycles

return to listing

F82H

    SR     (R):    normalized at 1038 °C (1900 °F), tempered at 750 °C (1382 °F) || tested at 550 °C (1022 °F) || 6 h to 720 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) || tested at 635 °C (1175 °F) || 250 h to 5,400 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) || tested at 650 °C (1202 °F) || 100 h to 2,500 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) || tested at 665 °C (1229 °F) || 70 h to 1,500 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 550 °C (1022 °F) & 800 °C (1472 °F) || Master curve (LMP) || 27.1 h to 28.2 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) || tested at 635 °C (1175 °F) || 250 h to 5,400 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) || tested at 650 °C (1202 °F) || 40 h to 1,500 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) || tested at 665 °C (1229 °F) || 40 h to 3,400 h
    SR     (R):    normalized at 1200 °C (2192 °F), tempered at 800 °C (1472 °F) || Master curve (LMP) || 25.7 h to 26.4 h
    SR     (R):    normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) || tested at 550 °C (1022 °F) || 4.4 x 10⁴ h to 1.1 x 10⁶ h
    SR     (R):    normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) || tested at 550 °C (1022 °F), 100 at. ppm He || 6.4 x 10⁴ h to 2.7 x 10⁶ h
    SR     (R):    normalized at 1040 °C (1904 °F), tempered at 750 °C (1382 °F) || tested at 550 °C (1022 °F), 300 at. ppm He || 2.4 x 10⁵ h to 4.1 x 10⁶ h

return to listing

GRCop-84

SR (R): as-extruded || Master curve (LMP) || 26.4 h to 37.1 h

return to listing

H-46

    SR     (N):    1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled || tested at 550 °C (1022 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled || tested at 600 °C (1112 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled || tested at 650 °C (1202 °F) || 100 h to 1 x 10⁴ h
    SR     (N):    1149 °C (2100 °F) 1 h, air cooled, 649 °C (1200 °F) 2 h, air cooled || tested at 700 °C (1292 °F) || 100 h to 1,000 h

return to listing

H-40 (New)

    E         :    quenched & tempered || 20 °C (68 °F) to 593 °C (1099 °F)
    UTS       :    quenched & tempered || 20 °C (68 °F) to 699 °C (1290 °F)
    YS        :    quenched & tempered || 20 °C (68 °F) to 699 °C (1290 °F)
    %El       :    quenched & tempered || 20 °C (68 °F) to 699 °C (1290 °F)
    SR        :    quenched & tempered || tested at 427 °C (800 °F) || 100 h to 1,000 h
    SR        :    quenched & tempered || tested at 538 °C (1000 °F) || 100 h to 1,000 h
    SR        :    quenched & tempered || tested at 593 °C (1100 °F) || 100 h to 1 x 10⁴ h
    SR        :    quenched & tempered || tested at 649 °C (1200 °F) || 100 h to 1,000 h
    SR        :    quenched & tempered || Master curve (LMP) || 15.7 h to 21.6 h
    SR        :    1066 °C (1950 °F), oil quenched, tempered 2 h at 677 °C (1250 °F) || tested at 538 °C (1000 °F) || 14 h to 1,750 h
    SR        :    1066 °C (1950 °F), oil quenched, tempered 2 h at 677 °C (1250 °F) || tested at 593 °C (1100 °F) || 28 h to 1,100 h
    SR        :    1066 °C (1950 °F), oil quenched, tempered 2 h at 677 °C (1250 °F) || Master curve (LMP) || 16.8 h to 19.5 h
    SR        :    1 h at 1066 °C (1950 °F), oil quenched, tempered 12 h at 649 °C (1200 °F), 100% martensite || tested at 593 °C (1100 °F) || 135 h to 870 h
    SR        :    1 h at 1066 °C (1950 °F), air cooled, tempered 18 h at 649 °C (1200 °F), 20% martensite + 80% bainite || tested at 593 °C (1100 °F) || 47 h to 730 h
    SR        :    1 h at 1066 °C (1950 °F), transformed 10 h at 399 °C (750 °F), tempered 1 h at 704 °C (1300 °F), 100% bainite || tested at 593 °C (1100 °F) || 400 h to 950 h
    CRR       :    1 h at 1066 °C (1950 °F), oil quenched, tempered 12 h at 649 °C (1200 °F), 100% martensite || tested at 593 °C (1100 °F) || 2.3 x 10^-⁹/s to 4.5 x 10^-⁸/s
    CRR       :    1 h at 1066 °C (1950 °F), air cooled, tempered 18 h at 649 °C (1200 °F), 20% martensite + 80% bainite || tested at 593 °C (1100 °F) || 1.7 x 10^-⁹/s to 2.1 x 10^-⁸/s
    CRR       :    1 h at 1066 °C (1950 °F), transformed 10 h at 399 °C (750 °F), tempered 1 h at 704 °C (1300 °F), 100% bainite || tested at 593 °C (1100 °F) || 2 x 10^-⁹/s to 1.65 x 10^-⁸/s

return to listing

H13

FSN (R): ESR, triple tempered, hardness 560 HV (53 HRC) || tested at 20 °C (68 °F), R = -1, axial, 90 Hz, maximum stress || 3.3 x 10⁶ cycles to 4.6 x 10⁹ cycles

return to listing

H11

    FSN    (N):    austenitized & tempered || tested at 21 °C (70 °F), R = 0.1, K_t = 2, axial, transverse, maximum stress || 1.2 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (R):    single tooth bending fatigue || tested at 20 °C (68 °F), R = 0.05, 50% failure probability, maximum stress || 1.1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (R):    single tooth bending fatigue || tested at 20 °C (68 °F), R = 0.05, 1% failure probability, maximum stress || 750 cycles to 1 x 10⁷ cycles

return to listing

Haynes 25 (L-605)

    UTS   (N*):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || room temperature value || room temperature value
    UTS    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || elevated temperatures || 649 °C (1200 °F) to 1149 °C (2100 °F)
    UTS   (N*):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || room temperature value || room temperature value
    UTS    (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || elevated temperatures || 399 °C (750 °F) to 982 °C (1799 °F)
    UTS   (N*):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || room temperature value
    YS    (N*):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || room temperature value || room temperature value
    YS     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || elevated temperatures || 649 °C (1200 °F) to 982 °C (1799 °F)
    YS    (N*):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || room temperature value || room temperature value
    YS     (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || elevated temperatures || 399 °C (750 °F) to 982 °C (1799 °F)
    YS    (N*):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || room temperature value
    %El   (N*):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || room temperature value || room temperature value
    %El    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || elevated temperatures || 649 °C (1200 °F) to 1149 °C (2100 °F)
    %El   (N*):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || room temperature value || room temperature value
    %El    (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || elevated temperatures || 399 °C (750 °F) to 982 °C (1799 °F)
    %El   (N*):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || room temperature value
    SR     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 816 °C (1500 °F) || 105 h to 2,900 h
    SR     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 871 °C (1600 °F) || 50 h to 1,700 h
    SR     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 927 °C (1700 °F) || 75 h to 580 h
    SR     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 982 °C (1800 °F) || 190 h to 700 h
    SR     (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || Master curve (LMP) || 19.2 h to 23.1 h
    SR     (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || tested at 649 °C (1200 °F) || 1.1 h to 73 h
    SR     (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || tested at 816 °C (1500 °F) || 8 h to 450 h
    SR     (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || tested at 899 °C (1650 °F) || 1.7 h to 340 h
    SR     (N):    solution treated at 1204 °C (2200 °F), air cooled, 1.57 mm (0.062 inch) hot-rolled sheet || Master curve (LMP) || 16.7 h to 24 h
    SR     (N):    20 minutes at 1204 °C (2200 °F), air cooled, 1.7 mm (0.067 inch) sheet || tested at 816 °C (1500 °F) || 4 h to 760 h
    SR     (N):    20 minutes at 1204 °C (2200 °F), air cooled, 1.7 mm (0.067 inch) sheet || tested at 982 °C (1800 °F) || 1.8 h to 430 h
    SR     (N):    20 minutes at 1204 °C (2200 °F), air cooled, 1.7 mm (0.067 inch) sheet || Master curve (LMP) || 20.9 h to 26.5 h
    SR     (N):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || tested at 649 °C (1200 °F) || 110 h to 240 h
    SR     (N):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || tested at 816 °C (1500 °F) || 14 h to 310 h
    SR     (N):    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || Master curve (LMP) || 17.8 h to 21.5 h
    CRS    (R):    0.1% plastic strain, annealed at 1232 °C (2250 °F) & quenched || Master curve (LMP) || 17.4 h to 21.8 h
    CRS    (R):    0.5% plastic strain, annealed at 1232 °C (2250 °F) & quenched || Master curve (LMP) || 21 h to 28.4 h
    CRS    (R):    1% plastic strain, annealed at 1232 °C (2250 °F) & quenched || Master curve (LMP) || 20.6 h to 29.5 h
    CRR    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 816 °C (1500 °F) || 5.2 x 10^-¹⁰/s to 2.6 x 10^-⁷/s
    CRR    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 871 °C (1600 °F) || 7.2 x 10^-¹⁰/s to 3.9 x 10^-⁷/s
    CRR    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 927 °C (1700 °F) || 2.5 x 10^-⁹/s to 7.5 x 10^-⁷/s
    CRR    (N):    annealed at 1218 °C (2225 °F), air cooled, 1.02 mm (0.04 inch) sheet || tested at 982 °C (1800 °F) || 1.38 x 10^-⁹/s to 1.55 x 10^-⁸/s
    CRR    (N):    20 minutes at 1204 °C (2200 °F), air cooled, 1.7 mm (0.067 inch) sheet || tested at 816 °C (1500 °F) || 1 x 10^-⁸/s to 3.8 x 10^-⁶/s
    CRR    (N):    20 minutes at 1204 °C (2200 °F), air cooled, 1.7 mm (0.067 inch) sheet || tested at 982 °C (1800 °F) || 1.45 x 10^-⁸/s to 9 x 10^-⁶/s

return to listing

Haynes 188

    RHO    (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    SIGMA (R):    solid || 20 °C (68 °F) to 1000 °C (1832 °F)
    E      (R):    solid || -185.1 °C (-301.3 °F) to 1094 °C (2001 °F)
    G      (R):    solid || -185.1 °C (-301.3 °F) to 1094 °C (2001 °F)
    v      (R):    solid || -185.1 °C (-301.3 °F) to 1094 °C (2001 °F)
    K      (R):    solid || -185.1 °C (-301.3 °F) to 1094 °C (2001 °F)

return to listing

Haynes Multimet (N-155)

    UTS   (N*):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || room temperature value
    UTS    (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || 20 °C (68 °F) to 732 °C (1349 °F)
    UTS   (N*):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    UTS   (N*):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    UTS   (N*):    precision cast || room temperature value || room temperature value
    UTS    (N):    precision cast || elevated temperatures || 537 °C (998 °F) to 982 °C (1799 °F)
    YS    (N*):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || room temperature value
    YS     (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || 20 °C (68 °F) to 732 °C (1349 °F)
    YS    (N*):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    YS    (N*):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    YS    (N*):    precision cast || room temperature value || room temperature value
    %El   (N*):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || room temperature value
    %El    (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || 20 °C (68 °F) to 732 °C (1349 °F)
    %El   (N*):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    %El   (N*):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || room temperature value
    %El   (N*):    precision cast || room temperature value || room temperature value
    %El    (N):    precision cast || elevated temperatures || 537 °C (998 °F) to 982 °C (1799 °F)
    SR     (N):    forged, 1 h at 1204 °C (2200 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 4 h to 365 h
    SR     (N):    as-forged, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 105 h to 900 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, no heat treatment || tested at 982 °C (1800 °F) || 35 h to 335 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, no heat treatment || tested at 1093 °C (2000 °F) || 80 h to 350 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, 2 h at 1149 °C (2100 °F), water quenched || tested at 982 °C (1800 °F) || 30 h to 343 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, 2 h at 1149 °C (2100 °F), water quenched || tested at 1093 °C (2000 °F) || 35 h to 780 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, 2 h at 1149 °C (2100 °F), water quenched || Master curve (LMP) || 37 h to 42.2 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled, 2 h at 1288 °C (2350 °F), water quenched || tested at 982 °C (1800 °F) || 11 h to 560 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), no heat treatment || tested at 982 °C (1800 °F) || 24 h to 165 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), no heat treatment || tested at 1093 °C (2000 °F) || 30 h to 60 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), no heat treatment || Master curve (LMP) || 20.6 h to 22.9 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched || tested at 982 °C (1800 °F) || 63 h to 407 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched || tested at 1093 °C (2000 °F) || 39 h to 125 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched || Master curve (LMP) || 36.2 h to 39.7 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched, 48 h at 816 °C (1500 °F) || tested at 982 °C (1800 °F) || 33 h to 207 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched, 48 h at 816 °C (1500 °F) || tested at 1093 °C (2000 °F) || 25 h to 63 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1177 °C (2150 °F), water quenched, 48 h at 816 °C (1500 °F) || Master curve (LMP) || 32.1 h to 35.2 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched || tested at 982 °C (1800 °F) || 57 h to 223 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched || tested at 1093 °C (2000 °F) || 65 h to 183 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched || Master curve (LMP) || 37.4 h to 41.3 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched, 48 h at 816 °C (1500 °F) || tested at 982 °C (1800 °F) || 73 h to 270 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched, 48 h at 816 °C (1500 °F) || tested at 1093 °C (2000 °F) || 25 h to 117 h
    SR     (N):    forged to 57.1 mm (2.25 inch), rolled to 31.8 mm (1.25 inch), 2 h at 1288 °C (2350 °F), water quenched, 48 h at 816 °C (1500 °F) || Master curve (LMP) || 27.1 h to 29.7 h
    SR     (N):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || tested at 649 °C (1200 °F) || 70 h to 540 h
    SR     (N):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || tested at 816 °C (1500 °F) || 17 h to 260 h
    SR     (N):    hot-rolled, 1 h at 1249 °C (2280 °F), water quenched, 4 h at 816 °C (1500 °F), air cooled || Master curve (LMP) || 29.4 h to 35.3 h
    SR     (N):    forged at 982 °C (1800 °F) to 1204 °C (2200 °F), 1 h at 1204 °C (2200 °F), water quenched, 24 h at 760 °C (1400 °F) || tested at 649 °C (1200 °F) || 60 h to 1,200 h
    SR     (N):    forged at 982 °C (1800 °F) to 1204 °C (2200 °F), 1 h at 1204 °C (2200 °F), water quenched, 24 h at 760 °C (1400 °F) || tested at 816 °C (1500 °F) || 45 h to 1,100 h
    SR     (N):    forged at 982 °C (1800 °F) to 1204 °C (2200 °F), 1 h at 1204 °C (2200 °F), water quenched, 24 h at 760 °C (1400 °F) || Master curve (LMP) || 15.5 h to 19.6 h
    SR     (N):    wrought 25.4 mm (1 inch) bars, 1 h at 1204 °C (2200 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 3 h to 1,200 h
    SR     (N):    wrought 25.4 mm (1 inch) bars, 1 h at 1204 °C (2200 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 20 h to 1,010 h
    SR     (N):    wrought 25.4 mm (1 inch) bars, 1 h at 1204 °C (2200 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 19.2 h to 23.4 h
    SR     (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 75 h to 640 h
    SR     (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 10 h to 91 h
    SR     (N):    hot-rolled, aged 16 h at 732 °C (1350 °F) || Master curve (LMP) || 24.4 h to 26.7 h
    SR     (N):    wrought, 1.02 mm to 16.5 mm (0.04 inch to 0.65 inch), annealed at 1177 °C (2150 °F), furnace cooled || tested at 816 °C (1500 °F) || 40 h to 1,700 h
    SR     (N):    mill annealed 1.4 mm (0.055 inch) sheet || tested at 816 °C (1500 °F) || 0.7 h to 65 h
    SR     (N):    mill annealed 1.4 mm (0.055 inch) sheet || tested at 982 °C (1800 °F) || 4 h to 70 h
    SR     (N):    mill annealed 1.4 mm (0.055 inch) sheet || Master curve (LMP) || 23.8 h to 29.9 h
    SR     (N):    wrought & rolled sheet, annealed at 1093 °C (2000 °F) to 1149 °C (2100 °F), furnace cooled || tested at 927 °C (1700 °F) || 21 h to 835 h
    SR     (N):    wrought & rolled sheet, annealed at 1093 °C (2000 °F) to 1149 °C (2100 °F), furnace cooled || tested at 982 °C (1800 °F) || 16 h to 345 h
    SR     (N):    wrought & rolled sheet, annealed at 1093 °C (2000 °F) to 1149 °C (2100 °F), furnace cooled || Master curve (LMP) || 22 h to 24.5 h
    SR     (N):    wrought sheet, annealed 10 minutes at 1093 °C (2000 °F), air cooled || tested at 649 °C (1200 °F) || 16 h to 340 h
    SR     (N):    wrought sheet, annealed 10 minutes at 1093 °C (2000 °F), air cooled || tested at 816 °C (1500 °F) || 4 h to 250 h
    SR     (N):    wrought sheet, annealed 10 minutes at 1093 °C (2000 °F), air cooled || Master curve (LMP) || 17.7 h to 22.2 h
    SR     (N):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 649 °C (1200 °F) || 63 h to 310 h
    SR     (N):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 816 °C (1500 °F) || 20 h to 110 h
    SR     (N):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 927 °C (1700 °F) || 9 h to 22 h
    SR     (N):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 1038 °C (1900 °F) || 1.3 h to 26 h
    SR     (N):    2.16 mm (0.085 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || Master curve (LMP) || 16.9 h to 23.5 h
    SR     (N):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 816 °C (1500 °F) || 8 h to 23 h
    SR     (N):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 927 °C (1700 °F) || 2 h to 16 h
    SR     (N):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || tested at 1038 °C (1900 °F) || 0.25 h to 4 h
    SR     (N):    1.63 mm (0.064 inch) sheet, annealed at 1038 °C (1900 °F), air cooled || Master curve (LMP) || 20.6 h to 24.2 h
    SR     (N):    1.63 mm (0.064 inch) and 2.16 mm (0.085 inch) sheet combined, annealed at 1038 °C (1900 °F), air cooled || tested at 816 °C (1500 °F) || 8 h to 110 h
    SR     (N):    1.63 mm (0.064 inch) and 2.16 mm (0.085 inch) sheet combined, annealed at 1038 °C (1900 °F), air cooled || tested at 927 °C (1700 °F) || 2 h to 22 h
    SR     (N):    1.63 mm (0.064 inch) and 2.16 mm (0.085 inch) sheet combined, annealed at 1038 °C (1900 °F), air cooled || tested at 1038 °C (1900 °F) || 0.25 h to 26 h
    SR     (N):    1.63 mm (0.064 inch) and 2.16 mm (0.085 inch) sheet combined, annealed at 1038 °C (1900 °F), air cooled || Master curve (LMP) || 17.3 h to 21.5 h
    SR     (N):    precision cast || tested at 649 °C (1200 °F) || 110 h to 400 h
    SR     (N):    precision cast || tested at 732 °C (1350 °F) || 120 h to 390 h
    SR     (N):    precision cast || tested at 816 °C (1500 °F) || 60 h to 260 h
    SR     (N):    precision cast || Master curve (LMP) || 19.4 h to 23.3 h
    CRR    (N):    forged, 1 h at 1204 °C (2200 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 649 °C (1200 °F) || 1 x 10^-¹⁰/s to 1 x 10^-⁵/s
    CRR    (N):    as-forged, aged 50 h at 816 °C (1500 °F) || tested at 649 °C (1200 °F) || 1 x 10^-¹⁰/s to 6 x 10^-⁸/s
    CRR    (N):    forged at 982 °C (1800 °F) to 1204 °C (2200 °F), 1 h at 1204 °C (2200 °F), water quenched, 24 h at 760 °C (1400 °F) || tested at 649 °C (1200 °F) || 3.4 x 10^-⁸/s to 4.5 x 10^-⁷/s
    CRR    (N):    forged at 982 °C (1800 °F) to 1204 °C (2200 °F), 1 h at 1204 °C (2200 °F), water quenched, 24 h at 760 °C (1400 °F) || tested at 816 °C (1500 °F) || 8 x 10^-⁹/s to 2.7 x 10^-⁷/s
    CRR    (N):    wrought 25.4 mm (1 inch) bars, 1 h at 1204 °C (2200 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 1 x 10^-⁹/s to 8 x 10^-⁶/s
    CRR    (N):    wrought 25.4 mm (1 inch) bars, 1 h at 1204 °C (2200 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 3 x 10^-⁹/s to 2.4 x 10^-⁶/s
    CRR    (N):    wrought, 1.02 mm to 16.5 mm (0.04 inch to 0.65 inch), annealed at 1177 °C (2150 °F), furnace cooled || tested at 649 °C (1200 °F) || 9.7 x 10^-¹¹/s to 3.5 x 10^-⁸/s
    CRR    (N):    wrought, 1.02 mm to 16.5 mm (0.04 inch to 0.65 inch), annealed at 1177 °C (2150 °F), furnace cooled || tested at 816 °C (1500 °F) || 1.3 x 10^-⁹/s to 1.95 x 10^-⁷/s
    CRR    (N):    mill annealed 1.4 mm (0.055 inch) sheet || tested at 816 °C (1500 °F) || 2.1 x 10^-⁸/s to 4.1 x 10^-⁵/s
    CRR    (N):    mill annealed 1.4 mm (0.055 inch) sheet || tested at 982 °C (1800 °F) || 5 x 10^-⁸/s to 2.2 x 10^-⁶/s
    CRR    (N):    precision cast || tested at 649 °C (1200 °F) || 4 x 10^-¹¹/s to 1 x 10^-⁷/s
    CRR    (N):    precision cast || tested at 732 °C (1350 °F) || 8 x 10^-⁹/s to 4.5 x 10^-⁸/s
    CRR    (N):    precision cast || tested at 816 °C (1500 °F) || 1.5 x 10^-⁸/s to 1.2 x 10^-⁷/s

return to listing

Haynes Ultimet

FSN (R): solution annealed || tested at 20 °C (68 °F), R = 0.05, axial, regular air at 1000 Hz, maximum stress || 1 x 10⁵ cycles to unknown strain rate cycles

return to listing

HP 9-4-30

FSN (N): forged & heat treated || tested at 21 °C (70 °F), R = 0.1, K_t = 2, axial, longitudinal, maximum stress || 4 x 10³ cycles to 1 x 10⁷ cycles
FSN (N): forged & heat treated || tested at 21 °C (70 °F), R = 0.1, K_t = 2, axial, short transverse, maximum stress || 7 x 10³ cycles to 1 x 10⁷ cycles

return to listing

HR3C

SR (R): solution treated || Master curve (LMP) || 16.1 h to 22.3 h

return to listing

IN-792 5A

    SR     (R):    solution annealed & aged || tested at 750 °C (1382 °F) || 900 h to 1,130 h
    SR     (R):    solution annealed & aged || tested at 775 °C (1427 °F) || 400 h to 3,200 h
    SR     (R):    solution annealed & aged || tested at 800 °C (1472 °F) || 550 h to 6,500 h
    SR     (R):    solution annealed & aged || tested at 825 °C (1517 °F) || 1,100 h to 2,500 h
    SR     (R):    solution annealed & aged || tested at 850 °C (1562 °F) || 200 h to 5,000 h
    SR     (R):    solution annealed & aged || tested at 875 °C (1607 °F) || 60 h to 2,200 h
    SR     (R):    solution annealed & aged || tested at 900 °C (1652 °F) || 70 h to 3,000 h
    SR     (R):    solution annealed & aged || tested at 925 °C (1697 °F) || 80 h to 2,000 h
    SR     (R):    solution annealed & aged || tested at 950 °C (1742 °F) || 10 h to 7,700 h
    SR     (R):    solution annealed & aged || tested at 975 °C (1787 °F) || 40 h to 2,100 h
    SR     (R):    solution annealed & aged || Master curve (LMP) || 21.5 h to 26.9 h

return to listing

IN-100

    FEN    (R):    GATORIZED, forged, solution annealed & aged || tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range || 400 cycles to 5 x 10⁵ cycles
    FEN    (R):    GATORIZED, forged, solution annealed & aged || tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range || 200 cycles to 7 x 10³ cycles
    CRS    (R):    0.5% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material || Master curve (LMP) || 26.5 h to 36 h
    CRS    (R):    1% plastic strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material || Master curve (LMP) || 25.2 h to 34.3 h
    CRS    (R):    0.1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material || tested at 816 °C (1500 °F) || 0.1 h to 8 h
    CRS    (R):    0.1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material || Master curve (LMP) || 23.9 h to 30.7 h
    CRS    (R):    0.2% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material || Master curve (LMP) || 21.1 h to 27.8 h
    CRS    (R):    0.5% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material || Master curve (LMP) || 19.7 h to 26 h
    CRS    (R):    1% plastic strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material || Master curve (LMP) || 22.1 h to 29.4 h

return to listing

IN-519

CRS (R): 1% total strain, as-cast || Master curve (LMP) || 31.7 h to 40.3 h

return to listing

Incoloy 925

FSN (N): axial || tested at 20 °C (68 °F), tension-tension, in air, mean stress || 1.43 x 10⁶ cycles to 7.6 x 10⁶ cycles
FSN (N): axial || tested at 20 °C (68 °F), tension-tension, in seawater, mean stress || 1.3 x 10⁶ cycles to 8 x 10⁶ cycles

return to listing

Incoloy 800

    FEN    (R):    annealed || tested at 20 °C (68 °F), R = -1, bending, total strain range || 130 cycles to 5 x 10⁴ cycles
    CRR    (N):    annealed || tested at 499 °C (930 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁸/s
    CRR    (N):    annealed || tested at 538 °C (1000 °F) || 3 x 10^-¹¹/s to 7 x 10^-⁷/s
    CRR    (N):    annealed || tested at 593 °C (1100 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed || tested at 649 °C (1200 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed || tested at 704 °C (1300 °F) || 3 x 10^-¹¹/s to 1 x 10^-⁶/s

return to listing

Incoloy A-286

    CRS    (R):    0.05% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 649 °C (1200 °F) || 0.2 h to 1,200 h
    CRS    (R):    0.05% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 732 °C (1350 °F) || 0.5 h to 1,150 h
    CRS    (R):    0.05% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 816 °C (1500 °F) || 0.2 h to 300 h
    CRS    (R):    0.1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 649 °C (1200 °F) || 0.2 h to 900 h
    CRS    (R):    0.1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 732 °C (1350 °F) || 0.1 h to 1,150 h
    CRS    (R):    0.1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 816 °C (1500 °F) || 0.4 h to 1,020 h
    CRS    (R):    0.1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || Master curve (LMP) || 17.1 h to 24.2 h
    CRS    (R):    0.3% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 649 °C (1200 °F) || 1 h to 730 h
    CRS    (R):    0.3% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 732 °C (1350 °F) || 0.1 h to 1,350 h
    CRS    (R):    0.3% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 816 °C (1500 °F) || 0.1 h to 810 h
    CRS    (R):    0.3% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || Master curve (LMP) || 25 h to 32.6 h
    CRS    (R):    0.5% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 649 °C (1200 °F) || 2 h to 1,150 h
    CRS    (R):    0.5% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 732 °C (1350 °F) || 0.2 h to 900 h
    CRS    (R):    0.5% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 816 °C (1500 °F) || 0.15 h to 1,530 h
    CRS    (R):    0.5% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || Master curve (LMP) || 25.9 h to 33.7 h
    CRS    (R):    1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 649 °C (1200 °F) || 3.2 h to 1,020 h
    CRS    (R):    1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 732 °C (1350 °F) || 0.5 h to 900 h
    CRS    (R):    1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || tested at 816 °C (1500 °F) || 0.3 h to 800 h
    CRS    (R):    1% plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || Master curve (LMP) || 28.7 h to 36.5 h
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 1 h || 0 to 3 x 10^-³ mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 5 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 50 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 649 °C (1200 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 500 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 5 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 50 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 500 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 1,000 h || 0 to 3 x 10^-³ mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 5 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 15 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 50 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 200 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solution treated at 899 °C (1650 °F), aged at 718 °C (1325 °F) || 500 h || 0 to 0.01 mm/mm strain

return to listing

Incoloy 800H & 800HT

    FEN    (R):    annealed || tested at 21 °C (70 °F), R = -1, axial, total strain range || 120 cycles to 3 x 10⁴ cycles
    FEN    (R):    annealed || tested at 538 °C (1000 °F), R = -1, axial, total strain range || 100 cycles to 2 x 10⁵ cycles
    FEN    (R):    annealed || tested at 649 °C (1200 °F), R = -1, axial, total strain range || 100 cycles to 1.5 x 10⁴ cycles
    FEN    (R):    annealed || tested at 760 °C (1400 °F), R = -1, axial, total strain range || 100 cycles to 2.7 x 10⁴ cycles
    CRR    (N):    solution annealed || tested at 649 °C (1200 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 704 °C (1300 °F) || 3 x 10^-¹¹/s to 6 x 10^-⁸/s
    CRR    (N):    solution annealed || tested at 760 °C (1400 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 871 °C (1600 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 927 °C (1700 °F) || 3 x 10^-¹¹/s to 5 x 10^-⁸/s
    CRR    (N):    solution annealed || tested at 982 °C (1800 °F) || 3 x 10^-¹¹/s to 1 x 10^-⁸/s
    CRR    (N):    solution annealed || tested at 1093 °C (2000 °F) || 2 x 10^-⁹/s to 3 x 10^-⁷/s

return to listing

Inconel 601

    CRR    (N):    solution treated || tested at 538 °C (1000 °F) || 2.78 x 10^-¹⁰/s to 8 x 10^-⁸/s
    CRR    (N):    solution treated || tested at 593 °C (1100 °F) || 2.78 x 10^-¹⁰/s to 8 x 10^-⁸/s
    CRR    (N):    solution treated || tested at 649 °C (1200 °F) || 2.78 x 10^-¹⁰/s to 4 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 704 °C (1300 °F) || 2.78 x 10^-¹⁰/s to 1.3 x 10^-⁶/s
    CRR    (N):    solution treated || tested at 760 °C (1400 °F) || 2.78 x 10^-¹⁰/s to 1 x 10^-⁶/s
    CRR    (N):    solution treated || tested at 816 °C (1500 °F) || 2.78 x 10^-¹⁰/s to 1.2 x 10^-⁶/s
    CRR    (N):    solution treated || tested at 871 °C (1600 °F) || 2.78 x 10^-¹⁰/s to 7 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 982 °C (1800 °F) || 2.78 x 10^-¹⁰/s to 8 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 1093 °C (2000 °F) || 2.78 x 10^-¹⁰/s to 7 x 10^-⁷/s

return to listing

Inconel 617

    CRR    (N):    solution annealed || tested at 593 °C (1100 °F) || 1.8 x 10^-¹¹/s to 3 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 649 °C (1200 °F) || 1.9 x 10^-¹¹/s to 2.6 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 760 °C (1400 °F) || 1 x 10^-¹¹/s to 2.6 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 871 °C (1600 °F) || 8 x 10^-¹²/s to 3 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 982 °C (1800 °F) || 2.9 x 10^-¹⁰/s to 3 x 10^-⁷/s
    CRR    (N):    solution annealed || tested at 1093 °C (2000 °F) || 7 x 10^-¹¹/s to 3 x 10^-⁷/s

return to listing

Inconel 625

    CRR    (N):    solution treated || tested at 649 °C (1200 °F) || 6 x 10^-¹²/s to 3 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 704 °C (1300 °F) || 1.8 x 10^-¹¹/s to 3 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 760 °C (1400 °F) || 2 x 10^-¹¹/s to 6 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 816 °C (1500 °F) || 1.2 x 10^-¹¹/s to 3 x 10^-⁵/s
    CRR    (N):    solution treated || tested at 871 °C (1600 °F) || 2.6 x 10^-¹¹/s to 3.2 x 10^-⁶/s
    CRR    (N):    solution treated || tested at 982 °C (1800 °F) || 8 x 10^-¹⁰/s to 6.2 x 10^-⁷/s
    CRR    (N):    solution treated || tested at 1093 °C (2000 °F) || 4 x 10^-⁷/s to 1.8 x 10^-⁶/s
    CRR    (N):    annealed || tested at 593 °C (1100 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁸/s
    CRR    (N):    annealed || tested at 621 °C (1150 °F) || 3 x 10^-¹¹/s to 1 x 10^-⁹/s
    CRR    (N):    annealed || tested at 649 °C (1200 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁶/s
    CRR    (N):    annealed || tested at 704 °C (1300 °F) || 3 x 10^-¹¹/s to 1 x 10^-⁶/s
    CRR    (N):    annealed || tested at 760 °C (1400 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁶/s
    CRR    (N):    annealed || tested at 816 °C (1500 °F) || 8 x 10^-¹¹/s to 4 x 10^-⁷/s

return to listing

Inconel 690

    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 482 °C (900 °F) || 3 x 10^-¹¹/s to 4 x 10^-⁷/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 538 °C (1000 °F) || 3 x 10^-¹¹/s to 2 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 593 °C (1100 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 649 °C (1200 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 704 °C (1300 °F) || 3 x 10^-¹¹/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 760 °C (1400 °F) || 1 x 10^-⁸/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 871 °C (1600 °F) || 8 x 10^-⁷/s to 3 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 982 °C (1800 °F) || 2 x 10^-⁹/s to 2 x 10^-⁶/s
    CRR    (N):    annealed at 1038 °C (1900 °F) || tested at 1093 °C (2000 °F) || 1 x 10^-⁷/s to 2 x 10^-⁶/s

return to listing

Inconel 706

    CRR    (N):    optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) || tested at 593 °C (1100 °F) || 1.2 x 10^-¹⁰/s to 4.5 x 10^-⁷/s
    CRR    (N):    optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) || tested at 649 °C (1200 °F) || 2 x 10^-¹⁰/s to 4.5 x 10^-⁷/s
    CRR    (N):    optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) || tested at 704 °C (1300 °F) || 2 x 10^-¹⁰/s to 3.2 x 10^-⁷/s
    CRR    (N):    optimized for creep & rupture strength, 927 °C (1700 °F) to 1010 °C (1850 °F)/843 °C (1550 °F)/718 °C (1325 °F)/621 °C (1150 °F) || tested at 760 °C (1400 °F) || 1.4 x 10^-⁹/s to 5.3 x 10^-⁷/s

return to listing

Inconel 783

    SR     (R):    standard heat treatment || tested at 538 °C (1000 °F) || 300 h to 1.5 x 10⁴ h
    SR     (R):    standard heat treatment || tested at 593 °C (1100 °F) || 400 h to 1.55 x 10⁴ h
    SR     (R):    standard heat treatment || tested at 649 °C (1200 °F) || 150 h to 2,500 h
    SR     (R):    standard heat treatment || tested at 704 °C (1300 °F) || 370 h to 1,400 h

return to listing

Inconel 751

    FSN    (R):    precipitation hardened || tested at 21 °C (70 °F), R = -1, rotating beam, maximum stress || 1 x 10⁶ cycles to 1 x 10⁸ cycles
    FSN    (R):    precipitation hardened || tested at 732 °C (1350 °F), R = -1, rotating beam, maximum stress || 1 x 10⁶ cycles to 1 x 10⁸ cycles
    FSN    (R):    precipitation hardened || tested at 816 °C (1500 °F), R = -1, rotating beam, maximum stress || 1 x 10⁶ cycles to 1 x 10⁸ cycles

return to listing

Inconel 700

    SR     (R):    solution annealed & treated bar || tested at 816 °C (1500 °F) || 3 h to 1,300 h
    SR     (R):    solution annealed & treated bar || tested at 871 °C (1600 °F) || 3 h to 1,050 h
    SR     (R):    solution annealed & treated bar || tested at 927 °C (1700 °F) || 4 h to 1,000 h
    SR     (R):    solution annealed & treated bar || Master curve (LMP) || 29.4 h to 35.4 h
    CRS    (R):    0.1% plastic strain, solution annealed & treated bar || tested at 816 °C (1500 °F) || 0.3 h to 400 h
    CRS    (R):    0.1% plastic strain, solution annealed & treated bar || tested at 871 °C (1600 °F) || 0.2 h to 360 h
    CRS    (R):    0.1% plastic strain, solution annealed & treated bar || tested at 927 °C (1700 °F) || 0.15 h to 420 h
    CRS    (R):    0.1% plastic strain, solution annealed & treated bar || Master curve (LMP) || 32.2 h to 39.1 h
    CRS    (R):    0.3% plastic strain, solution annealed & treated bar || tested at 816 °C (1500 °F) || 0.5 h to 1,150 h
    CRS    (R):    0.3% plastic strain, solution annealed & treated bar || tested at 871 °C (1600 °F) || 0.3 h to 800 h
    CRS    (R):    0.3% plastic strain, solution annealed & treated bar || tested at 927 °C (1700 °F) || 0.4 h to 720 h
    CRS    (R):    0.3% plastic strain, solution annealed & treated bar || Master curve (LMP) || 29.5 h to 36.3 h
    CRS    (R):    0.5% plastic strain, solution annealed & treated bar || tested at 816 °C (1500 °F) || 0.9 h to 950 h
    CRS    (R):    0.5% plastic strain, solution annealed & treated bar || tested at 871 °C (1600 °F) || 0.6 h to 1,050 h
    CRS    (R):    0.5% plastic strain, solution annealed & treated bar || tested at 927 °C (1700 °F) || 0.6 h to 950 h
    CRS    (R):    0.5% plastic strain, solution annealed & treated bar || Master curve (LMP) || 30 h to 36.7 h
    CRS    (R):    1% plastic strain, solution annealed & treated bar || tested at 816 °C (1500 °F) || 1.9 h to 1,150 h
    CRS    (R):    1% plastic strain, solution annealed & treated bar || tested at 871 °C (1600 °F) || 1 h to 950 h
    CRS    (R):    1% plastic strain, solution annealed & treated bar || tested at 927 °C (1700 °F) || 1 h to 960 h
    CRS    (R):    1% plastic strain, solution annealed & treated bar || Master curve (LMP) || 30.6 h to 36.9 h
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 100,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, solutionized & treated bar || 300,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 0.3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 30,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, solutionized & treated bar || 100,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, solutionized & treated bar || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, solutionized & treated bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, solutionized & treated bar || 300 h || 0 to 0.01 mm/mm strain

return to listing

Inconel 600

    FSN    (R):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, hard, maximum stress || 1 x 10⁵ cycles to 1 x 10⁸ cycles
    FSN    (R):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, soft, maximum stress || 7.6 x 10⁴ cycles to 1 x 10⁸ cycles
    FSN    (R):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, hard, maximum stress || 5.2 x 10⁵ cycles to 1 x 10⁸ cycles
    FSN    (R):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, soft, maximum stress || 5.8 x 10⁴ cycles to 1 x 10⁸ cycles
    FEN    (N):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, hard, total strain amplitude || 600 cycles to 8 x 10⁵ cycles
    FEN    (N):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, fine grain, soft, total strain amplitude || 360 cycles to 1 x 10⁶ cycles
    FEN    (N):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, hard, total strain amplitude || 170 cycles to 3 x 10⁵ cycles
    FEN    (N):    forgings || tested at 20 °C (68 °F), R = -1, rotating beam, coarse grain, soft, total strain amplitude || 300 cycles to 1 x 10⁵ cycles
    CRR    (N):    hot-rolled || tested at 538 °C (1000 °F) || 2.78 x 10^-¹¹/s to 3 x 10^-⁹/s
    CRR    (N):    hot-rolled || tested at 593 °C (1100 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled || tested at 649 °C (1200 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled || tested at 704 °C (1300 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 816 °C (1500 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 871 °C (1600 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 927 °C (1700 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 982 °C (1800 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 1093 °C (2000 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    hot-rolled & solution annealed || tested at 1149 °C (2100 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-⁸/s
    CRR    (N):    cold-drawn & annealed || tested at 427 °C (800 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 482 °C (900 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 538 °C (1000 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 593 °C (1100 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 871 °C (1600 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 982 °C (1800 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 1093 °C (2000 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & annealed || tested at 1149 °C (2100 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s

return to listing

Inconel 718

    FSN    (N):    solution treated & aged, grain size ASTM 10 || tested at 20 °C (68 °F), R = -1, rotary bending at 52.5 Hz, UTS = 1.39 GPa (202 ksi), YS = 1.22 GPa (177 ksi), stress amplitude || 1 x 10⁵ cycles to 1 x 10⁹ cycles
    FEN    (R):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -269.1 °C (-452.5 °F), R = -1, axial, total strain range || 100 cycles to 5.1 x 10⁴ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 100 cycles to 3 x 10³ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 100 cycles to 5.1 x 10⁴ cycles
    FEN    (R):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -195.1 °C (-319.3 °F), R = -1, axial, total strain range || 80 cycles to 1.7 x 10⁵ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 80 cycles to 1.1 x 10⁴ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 80 cycles to 1.7 x 10⁵ cycles
    FEN    (R):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at 27 °C (80 °F), R = -1, axial, total strain range || 60 cycles to 9 x 10⁴ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 60 cycles to 6 x 10³ cycles
    FEN    (N):    solution annealed at 1066 °C (1950 °F) for 1 h, aged at 732 °C (1350 °F) & 649 °C (1200 °F) || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 60 cycles to 9 x 10⁴ cycles
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || tested at 538 °C (1000 °F) || 25 h to 2.1 x 10⁴ h
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || tested at 593 °C (1100 °F) || 25 h to 3.3 x 10⁴ h
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || tested at 649 °C (1200 °F) || 10 h to 1 x 10⁴ h
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || tested at 704 °C (1300 °F) || 10 h to 6,100 h
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || tested at 760 °C (1400 °F) || 4 h to 760 h
    SR     (R):    solution treated at 954 °C (1750 °F), duplex aged || Master curve (LMP) || 24.9 h to 33.2 h
    CRR    (N):    aged || tested at 593 °C (1100 °F) || 1.78 x 10^-¹⁰/s to 1.2 x 10^-⁷/s
    CRR    (N):    aged || tested at 649 °C (1200 °F) || 5 x 10^-¹²/s to 1.4 x 10^-⁷/s
    CRR    (N):    aged || tested at 704 °C (1300 °F) || 1.3 x 10^-¹⁰/s to 3.4 x 10^-⁸/s

return to listing

Inconel 713C

    FSN    (N):    axial fatigue || tested at 927 °C (1700 °F), R = -1, K_t = 2.9, maximum stress || 1.7 x 10⁴ cycles to 5.1 x 10⁷ cycles
    SR     (R):    as-cast || tested at 816 °C (1500 °F) || 9 h to 950 h
    SR     (R):    as-cast || tested at 871 °C (1600 °F) || 7 h to 950 h
    SR     (R):    as-cast || tested at 927 °C (1700 °F) || 7 h to 950 h
    SR     (R):    as-cast || Master curve (LMP) || 25.9 h to 30.9 h
    CRS    (R):    0.1% plastic strain, as-cast || tested at 816 °C (1500 °F) || 0.1 h to 155 h
    CRS    (R):    0.1% plastic strain, as-cast || tested at 871 °C (1600 °F) || 0.1 h to 210 h
    CRS    (R):    0.1% plastic strain, as-cast || tested at 927 °C (1700 °F) || 0.2 h to 290 h
    CRS    (R):    0.1% plastic strain, as-cast || Master curve (LMP) || 16.3 h to 22.1 h
    CRS    (R):    0.3% plastic strain, as-cast || tested at 816 °C (1500 °F) || 0.8 h to 1,050 h
    CRS    (R):    0.3% plastic strain, as-cast || tested at 871 °C (1600 °F) || 0.6 h to 960 h
    CRS    (R):    0.3% plastic strain, as-cast || tested at 927 °C (1700 °F) || 1 h to 910 h
    CRS    (R):    0.3% plastic strain, as-cast || Master curve (LMP) || 18.6 h to 24.1 h
    CRS    (R):    0.5% plastic strain, as-cast || tested at 816 °C (1500 °F) || 2 h to 900 h
    CRS    (R):    0.5% plastic strain, as-cast || tested at 871 °C (1600 °F) || 1 h to 900 h
    CRS    (R):    0.5% plastic strain, as-cast || tested at 927 °C (1700 °F) || 2 h to 1,050 h
    CRS    (R):    0.5% plastic strain, as-cast || Master curve (LMP) || 20.5 h to 25.8 h
    CRS    (R):    1% plastic strain, as-cast || tested at 816 °C (1500 °F) || 4 h to 950 h
    CRS    (R):    1% plastic strain, as-cast || tested at 871 °C (1600 °F) || 2.5 h to 900 h
    CRS    (R):    1% plastic strain, as-cast || tested at 927 °C (1700 °F) || 4 h to 960 h
    CRS    (R):    1% plastic strain, as-cast || Master curve (LMP) || 23 h to 28.2 h
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 1 h || 0 to 3 x 10^-³ mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, as-cast || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, as-cast || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 0.3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, as-cast || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 0.1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 899 °C (1650 °F), plastic strain, as-cast || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 927 °C (1700 °F), plastic strain, as-cast || 100 h || 0 to 0.01 mm/mm strain

return to listing

Inconel 713LC

    SR     (R):    as-cast || tested at 730 °C (1346 °F) || 2,200 h to 6,200 h
    SR     (R):    as-cast || tested at 750 °C (1382 °F) || 1,000 h to 3,300 h
    SR     (R):    as-cast || tested at 800 °C (1472 °F) || 60 h to 6,500 h
    SR     (R):    as-cast || tested at 850 °C (1562 °F) || 60 h to 3,500 h
    SR     (R):    as-cast || tested at 900 °C (1652 °F) || 30 h to 3,300 h
    SR     (R):    as-cast || tested at 950 °C (1742 °F) || 40 h to 2,800 h
    SR     (R):    as-cast || tested at 1000 °C (1832 °F) || 120 h to 950 h
    SR     (R):    as-cast || Master curve (LMP) || 21.7 h to 27.2 h
    CRS    (R):    1% plastic strain, as-cast || Master curve (LMP) || 25 h to 31.2 h

return to listing

Inconel MA 754

CRR (N): recrystallized || tested at 850 °C (1562 °F) || 8 x 10^-¹⁰/s to 0.14/s
CRR (N): recrystallized || tested at 1000 °C (1832 °F) || 4 x 10^-¹⁰/s to 0.4/s

return to listing

Inconel MA 6000

    SR     (R):    longitudinal || tested at 700 °C (1292 °F) || 1 h to 2,200 h
    SR     (R):    longitudinal || tested at 750 °C (1382 °F) || 1 h to 2 x 10⁴ h
    SR     (R):    longitudinal || tested at 760 °C (1400 °F) || 1 h to 4,000 h
    SR     (R):    longitudinal || tested at 800 °C (1472 °F) || 1 h to 2,000 h
    SR     (R):    longitudinal || tested at 816 °C (1500 °F) || 1 h to 1,000 h
    SR     (R):    longitudinal || tested at 871 °C (1600 °F) || 1 h to 3,000 h
    SR     (R):    longitudinal || tested at 900 °C (1652 °F) || 1 h to 1.2 x 10⁴ h
    SR     (R):    longitudinal || tested at 950 °C (1742 °F) || 1 h to 1 x 10⁴ h
    SR     (R):    longitudinal || tested at 982 °C (1800 °F) || 1 h to 3 x 10⁴ h
    SR     (R):    longitudinal || tested at 1000 °C (1832 °F) || 1 h to 4,000 h
    SR     (R):    longitudinal || tested at 1093 °C (2000 °F) || 1 h to 700 h
    SR     (R):    longitudinal || tested at 1100 °C (2012 °F) || 5 h to 700 h
    SR     (R):    longitudinal || tested at 1149 °C (2100 °F) || 1 h to 500 h
    SR     (R):    longitudinal || Master curve (LMP) || 33.4 h to 51.1 h
    CRR    (N):    recrystallized || tested at 850 °C (1562 °F) || 3 x 10^-¹⁰/s to 1.2 x 10^-³/s
    CRR    (N):    recrystallized || tested at 1000 °C (1832 °F) || 3 x 10^-⁹/s to 9 x 10^-³/s

return to listing

Inconel X-750

    CRR    (N):    triple heat treated || tested at 649 °C (1200 °F) || 1 x 10^-¹¹/s to 3 x 10^-⁸/s
    CRR    (N):    triple heat treated || tested at 732 °C (1350 °F) || 1 x 10^-¹¹/s to 7 x 10^-⁸/s
    CRR    (N):    triple heat treated || tested at 816 °C (1500 °F) || 1 x 10^-¹¹/s to 2 x 10^-⁷/s
    CRR    (N):    triple heat treated || tested at 871 °C (1600 °F) || 1 x 10^-¹¹/s to 3 x 10^-⁷/s

return to listing

316L

FEN (N): hydrogen water chemistry || tested at 288 °C (550 °F), R = -1, axial, total strain amplitude || 940 cycles to 5 x 10⁵ cycles

return to listing

304L

    FSN    (R):    effect of martensite content || tested at 20 °C (68 °F), R = -1, axial, 90 Hz, fully austenitic, maximum stress || 1.3 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (R):    effect of martensite content || tested at 20 °C (68 °F), R = -1, axial, 90 Hz, 30% martensite, maximum stress || 1.4 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (R):    effect of martensite content || tested at 20 °C (68 °F), R = -1, axial, 90 Hz, 60% martensite, maximum stress || 1.4 x 10⁵ cycles to 1 x 10⁷ cycles
    FEN    (N):    solution annealed at mill || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 200 cycles to 4 x 10⁴ cycles
    FEN    (N):    solution annealed at mill || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 200 cycles to 4 x 10⁴ cycles
    FEN    (N):    solution annealed at mill || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 100 cycles to 1.6 x 10⁵ cycles
    FEN    (N):    solution annealed at mill || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 100 cycles to 1.6 x 10⁵ cycles
    FEN    (N):    solution annealed at mill || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 100 cycles to 1 x 10⁶ cycles
    FEN    (N):    solution annealed at mill || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 100 cycles to 1 x 10⁶ cycles

return to listing

LSHR disk alloy

    SR     (R):    subsolvus material || Master curve (LMP) || 23.2 h to 25.7 h
    CRS    (R):    0.2% plastic strain, supersolvus material || tested at 649 °C (1200 °F) || 230 h to 2.45 x 10⁷ h
    CRS    (R):    0.2% plastic strain, supersolvus material || tested at 704 °C (1300 °F) || 10 h to 7.75 x 10⁵ h
    CRS    (R):    0.2% plastic strain, supersolvus material || tested at 760 °C (1400 °F) || 13.4 h to 3.56 x 10⁴ h
    CRS    (R):    0.2% plastic strain, supersolvus material || tested at 816 °C (1500 °F) || 1.26 h to 2,240 h
    CRS    (R):    0.2% plastic strain, supersolvus material || Master curve (LMP) || 26.2 h to 31.8 h
    CRS    (R):    0.2% plastic strain, subsolvus material || tested at 649 °C (1200 °F) || 94.4 h to 6.8 x 10⁵ h
    CRS    (R):    0.2% plastic strain, subsolvus material || tested at 704 °C (1300 °F) || 3.15 h to 1.38 x 10⁴ h
    CRS    (R):    0.2% plastic strain, subsolvus material || tested at 760 °C (1400 °F) || 0.15 h to 421 h
    CRS    (R):    0.2% plastic strain, subsolvus material || tested at 816 °C (1500 °F) || 0.17 h to 18.5 h
    CRS    (R):    0.2% plastic strain, subsolvus material || Master curve (LMP) || 24.1 h to 27.7 h

return to listing

LZ50

FSN (N): locomotive axle || tested at 20 °C (68 °F), R = -1, rotating beam, laser shot peened, maximum stress || 8.5 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

M-252

    UTS   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || room temperature value || room temperature value
    UTS    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    UTS   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || room temperature value || room temperature value
    UTS    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    UTS   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || room temperature value || room temperature value
    UTS    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    UTS   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || room temperature value || room temperature value
    UTS    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    YS    (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || room temperature value || room temperature value
    YS     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    YS    (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || room temperature value || room temperature value
    YS     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    YS    (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || room temperature value || room temperature value
    YS     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    YS    (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || room temperature value || room temperature value
    YS     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    %El   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || room temperature value || room temperature value
    %El    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    %El   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || room temperature value || room temperature value
    %El    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    %El   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || room temperature value || room temperature value
    %El    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    %El   (N*):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || room temperature value || room temperature value
    %El    (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || elevated temperatures || 649 °C (1200 °F) to 904 °C (1659 °F)
    SR     (R):    4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 732 °C (1350 °F) || 35 h to 110 h
    SR     (R):    4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 816 °C (1500 °F) || 3.8 h to 170 h
    SR     (R):    4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 871 °C (1600 °F) || 8 h to 105 h
    SR     (R):    4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || Master curve (LMP) || 24.5 h to 28.4 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || tested at 816 °C (1500 °F) || 22 h to 340 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || tested at 871 °C (1600 °F) || 23 h to 55 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat A) || Master curve (LMP) || 25 h to 26.7 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || tested at 816 °C (1500 °F) || 37 h to 225 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || tested at 871 °C (1600 °F) || 12 h to 57 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat B) || Master curve (LMP) || 26.1 h to 27.6 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || tested at 816 °C (1500 °F) || 23 h to 255 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || tested at 871 °C (1600 °F) || 35 h to 68 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heat C) || Master curve (LMP) || 19.7 h to 21.2 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || tested at 816 °C (1500 °F) || 22 h to 340 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || tested at 871 °C (1600 °F) || 13 h to 68 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 1 h at 899 °C (1650 °F), furnace cooled (heats A, B, & C combined) || Master curve (LMP) || 22.9 h to 24.6 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 15 h at 899 °C (1650 °F), air cooled || tested at 816 °C (1500 °F) || 23 h to 650 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 15 h at 899 °C (1650 °F), air cooled || tested at 871 °C (1600 °F) || 67 h to 240 h
    SR     (N):    4 h at 1066 °C (1950 °F), air cooled, aged 15 h at 899 °C (1650 °F), air cooled || Master curve (LMP) || 17.8 h to 19.9 h
    CRS    (R):    0.1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 732 °C (1350 °F) || 0.6 h to 32 h
    CRS    (R):    0.1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 816 °C (1500 °F) || 0.15 h to 28 h
    CRS    (R):    0.1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 871 °C (1600 °F) || 0.6 h to 14 h
    CRS    (R):    0.1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || Master curve (LMP) || 22.4 h to 27 h
    CRS    (R):    0.3% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 732 °C (1350 °F) || 2 h to 100 h
    CRS    (R):    0.3% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 816 °C (1500 °F) || 0.4 h to 110 h
    CRS    (R):    0.3% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 871 °C (1600 °F) || 0.1 h to 60 h
    CRS    (R):    0.3% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || Master curve (LMP) || 25.8 h to 31.1 h
    CRS    (R):    0.5% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 732 °C (1350 °F) || 3 h to 120 h
    CRS    (R):    0.5% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 816 °C (1500 °F) || 0.5 h to 120 h
    CRS    (R):    0.5% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 871 °C (1600 °F) || 0.2 h to 100 h
    CRS    (R):    0.5% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || Master curve (LMP) || 26.5 h to 31.9 h
    CRS    (R):    1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 732 °C (1350 °F) || 4.5 h to 120 h
    CRS    (R):    1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 816 °C (1500 °F) || 0.9 h to 100 h
    CRS    (R):    1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || tested at 871 °C (1600 °F) || 0.4 h to 100 h
    CRS    (R):    1% plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || Master curve (LMP) || 26.3 h to 31.4 h
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 3 x 10^-³ mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 732 °C (1350 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 760 °C (1400 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3,000 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.1 h || 0 to 3 x 10^-³ mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 788 °C (1450 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 300 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 816 °C (1500 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 100 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 843 °C (1550 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 30 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 871 °C (1600 °F), plastic strain, 4 h at 1066 °C (1950 °F), air cooled, aged 4 h at 760 °C (1400 °F), bar || 10 h || 0 to 0.01 mm/mm strain

return to listing

MAR-M200

FEN (R): directionally solidified || tested at 760 °C (1400 °F), R = -1, axial, total strain range || 20 cycles to 1 x 10⁷ cycles

return to listing

Maraging 300 (C-type)

    FSN    (N):    annealed & aged || tested at 21 °C (70 °F), R = 0.1, K_t = 2, axial, longitudinal, maximum stress || 6 x 10³ cycles to 1 x 10⁷ cycles
    FSN    (N):    annealed & aged || tested at 21 °C (70 °F), R = 0.1, K_t = 2, axial, short transverse, maximum stress || 3.6 x 10³ cycles to 1 x 10⁷ cycles
    FEN    (N):    annealed & aged || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 18 cycles to 160 cycles
    FEN    (N):    annealed & aged || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 18 cycles to 7.3 x 10⁴ cycles
    FEN    (N):    annealed & aged || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 80 cycles to 1.4 x 10³ cycles
    FEN    (N):    annealed & aged || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 80 cycles to 8.9 x 10⁴ cycles
    FEN    (N):    annealed & aged || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 90 cycles to 2.2 x 10⁴ cycles
    FEN    (N):    annealed & aged || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 90 cycles to 2.2 x 10⁴ cycles

return to listing

MERL 76

    FSN    (R):    Kt = 1.0 || tested at 427 °C (800 °F), R = -1, axial, maximum stress || 9 x 10³ cycles to 3.2 x 10⁴ cycles
    FSN    (R):    Kt = 1.0 || tested at 538 °C (1000 °F), R = -1, axial, maximum stress || 5.9 x 10³ cycles to 2.8 x 10⁴ cycles
    FSN    (R):    Kt = 1.0 || tested at 635 °C (1175 °F), R = -1, axial, maximum stress || 2.6 x 10³ cycles to 3.2 x 10⁴ cycles
    FSN    (R):    Kt = 2.0 || tested at 427 °C (800 °F), R = -1, axial, maximum stress || 3.6 x 10³ cycles to 2.2 x 10⁴ cycles
    FSN    (R):    Kt = 2.0 || tested at 538 °C (1000 °F), R = -1, axial, maximum stress || 4.6 x 10³ cycles to 2 x 10⁴ cycles
    FSN    (R):    Kt = 3.0 || tested at 538 °C (1000 °F), R = -1, axial, maximum stress || 1.2 x 10⁴ cycles to 5.8 x 10⁴ cycles
    FEN    (R):    HIPed, solution annealed & aged || tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range || 220 cycles to 1 x 10⁴ cycles
    CRS    (N):    0.1% plastic strain, HIPed, solution treated & aged || Master curve (LMP) || 21.5 h to 25.3 h
    CRS    (N):    0.2% plastic strain, HIPed, solution treated & aged || Master curve (LMP) || 22.3 h to 25.8 h

return to listing

Molybdenum

    SR     (R):    sheet || Master curve (LMP) || 18.2 h to 24.2 h
    SR     (N):    disilicide coated sheet, in air || tested at 1538 °C (2800 °F) || 2.44 h to 6.39 h
    SR     (N):    disilicide coated sheet, in air || tested at 1649 °C (3000 °F) || 0.833 h to 4.44 h
    SR     (N):    disilicide coated sheet, in air || tested at 1760 °C (3200 °F) || 2.8 h to 7.22 h
    SR     (N):    disilicide coated sheet, in air || Master curve (LMP) || 26.1 h to 30.2 h
    CRS    (R):    0.05% plastic strain, disilicide coated sheet, in air || Master curve (LMP) || 42.6 h to 50.7 h
    CRS    (R):    0.2% plastic strain, disilicide coated sheet, in air || Master curve (LMP) || 30.5 h to 37 h
    CRS    (R):    4% plastic strain, disilicide coated sheet, in air || tested at 1538 °C (2800 °F) || 2.17 h to 5.83 h
    CRS    (R):    4% plastic strain, disilicide coated sheet, in air || tested at 1649 °C (3000 °F) || 0.689 h to 4.3 h
    CRS    (R):    4% plastic strain, disilicide coated sheet, in air || tested at 1760 °C (3200 °F) || 1.81 h to 6.94 h
    CRS    (R):    4% plastic strain, disilicide coated sheet, in air || Master curve (LMP) || 32.5 h to 37.5 h
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 3 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 10 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, disilicide coated sheet, in air || 30 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, disilicide coated sheet, in air || 1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, disilicide coated sheet, in air || 3 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, disilicide coated sheet, in air || 10 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, disilicide coated sheet, in air || 1 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, disilicide coated sheet, in air || 3 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 0.01 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, disilicide coated sheet, in air || 1 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1677 °C (3050 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1677 °C (3050 °F), plastic strain, disilicide coated sheet, in air || 0.3 h || 0 to 0.4 mm/mm strain
    IC     (R):    tested at 1704 °C (3100 °F), plastic strain, disilicide coated sheet, in air || 0.1 h || 0 to 0.4 mm/mm strain

return to listing

Monel 400

    CRS    (N):    0.2% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at room temperature: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) || Master curve (LMP) || 15 h to 19.2 h
    CRS    (N):    0.5% plastic strain, mill-annealed 12.7 mm (0.5 inch) rod, at room temperature: UTS = 558 MPa (81 ksi), YS = 152 MPa (22 ksi) || Master curve (LMP) || 14 h to 18.7 h
    CRR    (N):    hot-rolled || tested at 371 °C (700 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    hot-rolled || tested at 427 °C (800 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    hot-rolled || tested at 482 °C (900 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    hot-rolled || tested at 538 °C (1000 °F) || 1.3 x 10^-¹⁰/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, annealed 3 h at 816 °C (1500 °F) || tested at 399 °C (750 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, annealed 3 h at 816 °C (1500 °F) || tested at 427 °C (800 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, annealed 3 h at 816 °C (1500 °F) || tested at 482 °C (900 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, annealed 3 h at 816 °C (1500 °F) || tested at 538 °C (1000 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 399 °C (750 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 427 °C (800 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 454 °C (850 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 482 °C (900 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 510 °C (950 °F) || 2.8 x 10^-¹¹/s to 3 x 10^-¹⁰/s
    CRR    (N):    cold-drawn, stress-relieved 8 h at 538 °C (1000 °F) || tested at 538 °C (1000 °F) || 1.6 x 10^-¹⁰/s to 3 x 10^-¹⁰/s

return to listing

Monel K-500

    CRR    (N):    cold-drawn & aged || tested at 399 °C (750 °F) || 2.78 x 10^-¹¹/s to 3.16 x 10^-¹¹/s
    CRR    (N):    cold-drawn & aged || tested at 427 °C (800 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & aged || tested at 482 °C (900 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    cold-drawn & aged || tested at 538 °C (1000 °F) || 5 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s

return to listing

MP159

    CRS    (N):    0.1% plastic strain, annealed || tested at 427 °C (800 °F) || 3 h to 160 h
    CRS    (N):    0.1% plastic strain, annealed || tested at 649 °C (1200 °F) || 0.2 h to 100 h
    CRS    (N):    0.1% plastic strain, annealed || Master curve (LMP) || 5.83 h to 9.7 h
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 100 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 300 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 1,000 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 3,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 10,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 30,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 427 °C (800 °F), plastic strain, annealed || 100,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 30 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 100 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 300 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 1,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 3,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 10,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 454 °C (850 °F), plastic strain, annealed || 30,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 10 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 30 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 100 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 1,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 3,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 482 °C (900 °F), plastic strain, annealed || 10,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 10 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 30 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 1,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 510 °C (950 °F), plastic strain, annealed || 3,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 10 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 30 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 538 °C (1000 °F), plastic strain, annealed || 1,000 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 30 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 566 °C (1050 °F), plastic strain, annealed || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 0.3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 30 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 593 °C (1100 °F), plastic strain, annealed || 300 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 0.1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 0.3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 30 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 621 °C (1150 °F), plastic strain, annealed || 100 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 0.1 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 0.3 h || 0 to 2 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 1 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 3 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 10 h || 0 to 5 x 10^-³ mm/mm strain
    IC     (N):    tested at 649 °C (1200 °F), plastic strain, annealed || 30 h || 0 to 5 x 10^-³ mm/mm strain
    CRR    (N):    annealed || tested at 427 °C (800 °F) || 1.7 x 10^-⁷/s to 1.7 x 10^-⁶/s
    CRR    (N):    annealed || tested at 649 °C (1200 °F) || 2.5 x 10^-⁶/s to 1.7 x 10^-³/s

return to listing

NARloy-Z

    CRR    (N):    solution annealed & aged || tested at 500 °C (932 °F) || 2 x 10^-⁸/s to 2.7 x 10^-⁶/s
    CRR    (N):    solution annealed & aged || tested at 650 °C (1202 °F) || 1 x 10^-⁸/s to 1.3 x 10^-⁵/s
    CRR    (N):    solution annealed & aged || tested at 800 °C (1472 °F) || 7.1 x 10^-⁸/s to 3.7 x 10^-⁵/s

return to listing

316NG

    FEN    (N):    in water || tested at 288 °C (550 °F), R = -1, axial, 5 x 10^-³/s, 0.004 to 0.8 ppm O, total strain amplitude || 1.8 x 10⁴ cycles to 1 x 10⁷ cycles
    FEN    (N):    in water || tested at 288 °C (550 °F), R = -1, axial, 5 x 10^-⁴/s, 0.004 to 0.8 ppm O, total strain amplitude || 1 x 10⁴ cycles to 6 x 10⁴ cycles
    FEN    (N):    in water || tested at 288 °C (550 °F), R = -1, axial, 5 x 10^-⁵/s, 0.8 ppm O, total strain amplitude || 7.4 x 10³ cycles to 2.1 x 10⁴ cycles
    FEN    (N):    in water || tested at 288 °C (550 °F), R = -1, axial, 5 x 10^-⁵/s, 0.004 ppm O, total strain amplitude || 5.2 x 10³ cycles to 1.2 x 10⁴ cycles

return to listing

Ni-SPAN C alloy 902 (Low expansion 43-PH)

FSN (R): solution treated & aged || tested at 21 °C (70 °F), R = -1, flexure, maximum stress || 1.6 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

Nickel 200

    FSN    (N):    annealed sheet || tested at 21 °C (70 °F), R = -1, K_t = 3, reverse bending, maximum stress || 1.8 x 10⁵ cycles to 8 x 10⁶ cycles
    FSN    (N):    annealed sheet || tested at -79 °C (-110 °F), R = -1, K_t = 3, reverse bending, maximum stress || 2 x 10⁵ cycles to 4 x 10⁶ cycles
    FSN    (N):    annealed sheet || tested at -195.6 °C (-320 °F), R = -1, K_t = 3, reverse bending, maximum stress || 1.5 x 10⁵ cycles to 5 x 10⁶ cycles
    FSN    (N):    annealed sheet || tested at -252.8 °C (-423 °F), R = -1, K_t = 3, reverse bending, maximum stress || 2 x 10⁵ cycles to 7 x 10⁷ cycles
    FEN    (N):    annealed || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 8 x 10⁴ cycles to 2.9 x 10⁶ cycles
    FEN    (N):    annealed || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 2 x 10⁴ cycles to 6 x 10⁵ cycles
    FEN    (N):    annealed || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 2.9 x 10⁴ cycles to 1.1 x 10⁶ cycles
    FEN    (N):    annealed || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 5.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 180 cycles to 7.6 x 10⁴ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 180 cycles to 7.6 x 10⁴ cycles
    CRR    (N):    annealed || tested at 316 °C (600 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 343 °C (650 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 371 °C (700 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 399 °C (750 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 427 °C (800 °F) || 2.78 x 10^-¹¹/s to 2.78 x 10^-¹⁰/s

return to listing

Nickel 201

    CRR    (N):    annealed || tested at 427 °C (800 °F) || 2.78 x 10^-¹¹/s to 2.3 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 482 °C (900 °F) || 2.78 x 10^-¹¹/s to 2.4 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 538 °C (1000 °F) || 2.78 x 10^-¹¹/s to 2.6 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 593 °C (1100 °F) || 2.78 x 10^-¹¹/s to 2.6 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 649 °C (1200 °F) || 2.78 x 10^-¹¹/s to 2.6 x 10^-¹⁰/s
    CRR    (N):    annealed || tested at 704 °C (1300 °F) || 2.78 x 10^-¹¹/s to 2.7 x 10^-¹⁰/s

return to listing

Nickel (commercially pure)

    FSN    (R):    annealed, K_t = 3 || tested at 21 °C (70 °F), R = -1, flexure, maximum stress || 2.8 x 10³ cycles to 1 x 10⁷ cycles
    FEN    (N):    annealed || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 8 x 10⁴ cycles to 2.9 x 10⁶ cycles
    FEN    (N):    annealed || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 2 x 10⁴ cycles to 6 x 10⁵ cycles
    FEN    (N):    annealed || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 2.9 x 10⁴ cycles to 1.1 x 10⁶ cycles
    FEN    (N):    annealed || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 5.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 180 cycles to 7.6 x 10⁴ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 180 cycles to 7.6 x 10⁴ cycles

return to listing

Nickel TD

FEN (N): plate, stress-relieved, Al-Cr pack coated || tested at 982 °C (1800 °F), R = 0, axial, total strain range || 300 cycles to 2 x 10³ cycles

return to listing

Nickel

    FEN    (N):    annealed || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 8 x 10⁴ cycles to 2.9 x 10⁶ cycles
    FEN    (N):    annealed || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 2 x 10⁴ cycles to 6 x 10⁵ cycles
    FEN    (N):    annealed || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 2.9 x 10⁴ cycles to 1.1 x 10⁶ cycles
    FEN    (N):    annealed || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 5.5 x 10⁴ cycles to 1 x 10⁶ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 190 cycles to 7 x 10⁴ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 140 cycles to 2.73 x 10⁵ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 180 cycles to 7.6 x 10⁴ cycles
    FEN    (N):    hot finished || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 180 cycles to 7.6 x 10⁴ cycles
    FEN    (N):    50 micron thick foil || tested at 20 °C (68 °F), R = -1, bending, TD-loaded, total strain amplitude || 2 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

Nimonic 75

CRR (N): condition not specified || tested at 850 °C (1562 °F) || 3.6 x 10^-⁸/s to 0.21/s
CRR (N): condition not specified || tested at 1000 °C (1832 °F) || 4.9 x 10^-⁷/s to 0.18/s

return to listing

Nimonic 105

    SR     (R):    heat treatment #1 || tested at 750 °C (1382 °F) || 100 h to 3,000 h
    SR     (R):    heat treatment #1 || tested at 815 °C (1499 °F) || 100 h to 3,000 h
    SR     (R):    heat treatment #1 || tested at 871 °C (1600 °F) || 100 h to 3,000 h
    SR     (R):    heat treatment #1 || tested at 940 °C (1724 °F) || 100 h to 300 h
    SR     (R):    heat treatment #1 || tested at 982 °C (1800 °F) || 100 h to 300 h
    SR     (R):    heat treatment #1 || Master curve (LMP) || 18.9 h to 23.8 h

return to listing

Nimonic 81

FSN (R): bar || tested at 700 °C (1292 °F), R = -1, rotating beam, maximum stress || 1.4 x 10⁴ cycles to 6.43 x 10⁷ cycles

return to listing

Nitronic 40

    CRS    (R):    0.1% plastic strain, annealed || tested at 260 °C (500 °F) || 0.01 h to 5 h
    CRS    (R):    0.2% plastic strain, annealed || tested at 260 °C (500 °F) || 0.2 h to 3,000 h
    CRS    (R):    0.2% plastic strain, annealed || tested at 371 °C (700 °F) || 0.5 h to 1 x 10⁴ h
    CRS    (R):    0.2% plastic strain, annealed || tested at 482 °C (900 °F) || 0.1 h to 720 h

return to listing

P91 (9 Cr - 1 Mo (wt %))

    FEN    (R):    as-received || tested at 20 °C (68 °F), R = -1, axial, total strain range || 650 cycles to 3.6 x 10³ cycles
    FEN    (N):    as-received || tested at 20 °C (68 °F), R = -1, axial, plastic strain range || 650 cycles to 3.6 x 10³ cycles
    FEN    (N):    as-received || tested at 20 °C (68 °F), R = -1, axial, elastic strain range || 650 cycles to 3.6 x 10³ cycles

return to listing

PM 1000

CRR (N): annealed || tested at 600 °C (1112 °F) || 1 x 10^-⁹/s to 1 x 10^-³/s

return to listing

Pt - 3 Au - 0.5 Rh (wt %)

SR (R): condition unknown || tested at 900 °C (1652 °F) || 20 h to 600 h

return to listing

Pt - 1 Au - 0.5 Rh (wt %)

SR (R): condition unknown || tested at 900 °C (1652 °F) || 50 h to 250 h

return to listing

Pt - 3 Au (wt %)

SR (R): condition unknown || tested at 900 °C (1652 °F) || 130 h to 500 h

return to listing

Pt - 1 Au (wt %)

SR (R): condition unknown || tested at 900 °C (1652 °F) || 40 h to 850 h

return to listing

Pt - 0.5 Rh (wt %)

SR (R): condition unknown || tested at 900 °C (1652 °F) || 30 h to 700 h

return to listing

PWA 1480

    FSN    (R):    in air || tested at 20 °C (68 °F), R = -1, 0 mean stress, axial, mean stress || 2 x 10⁴ cycles to 2.8 x 10⁶ cycles
    FSN    (N):    in air || tested at 20 °C (68 °F), 414 MPa (60 ksi) mean stress, axial, mean stress || 1 x 10⁵ cycles to 1 x 10⁷ cycles
    FSN    (N):    in air || tested at 20 °C (68 °F), 827 MPa (120 ksi) mean stress, axial, mean stress || 1 x 10⁵ cycles to 1 x 10⁷ cycles

return to listing

Refractaloy 26 (GH2026) (New)

    UTS       :    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || 20 °C (68 °F) to 815 °C (1499 °F)
    UTS   (*):    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || room temperature value
    YS        :    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || 20 °C (68 °F) to 815 °C (1499 °F)
    YS    (*):    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || room temperature value
    %El       :    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || 20 °C (68 °F) to 815 °C (1499 °F)
    %El   (*):    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || room temperature value
    SR        :    wrought bar, 1 h at 1149 °C (2100 °F), air cooled, 8 h at 760 °C (1400 °F), air cool || tested at 816 °C (1500 °F) || 100 h to 1,000 h
    SR        :    rolled bar, 20 minutes at 982 °C (1800 °F), oil quenched, 44 h at 732 °C (1350 °F), air cool, 20 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 12 h to 2,900 h
    SR        :    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || tested at 871 °C (1600 °F) || 5.5 h to 200 h
    SR        :    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || tested at 982 °C (1800 °F) || 11 h to 100 h
    SR        :    1.63 mm (0.064 inch) sheet, 1121 °C (2050 °F), air cooled || Master curve (LMP) || 31.8 h to 36.4 h
    SR        :    wrought, 1 h at 1149 °C (2100 °F), oil quenched, aged 20 h at 816 °C (1500 °F), air cooled, 20 h at 732 °C (1350 °F), air cooled || tested at 816 °C (1500 °F) || 31 h to 100 h
    CRR       :    rolled bar, 20 minutes at 982 °C (1800 °F), oil quenched, 44 h at 732 °C (1350 °F), air cool, 20 h at 649 °C (1200 °F), air cooled || tested at 649 °C (1200 °F) || 8.5 x 10^-¹⁰/s to 5.2 x 10^-⁷/s

return to listing

S-816

    UTS   (N*):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || room temperature value
    UTS   (N*):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || room temperature value
    UTS   (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || room temperature value || room temperature value
    UTS    (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || elevated temperatures || 537 °C (998 °F) to 871 °C (1600 °F)
    UTS   (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    UTS    (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    UTS   (N*):    wrought, 1 h at 1260 °C (2300 °F), water quenched || room temperature value
    UTS   (N*):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    UTS    (N):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || elevated temperatures || 538 °C (1000 °F) to 871 °C (1600 °F)
    UTS   (N*):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    UTS    (N):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    UTS   (N*):    12.7 mm (0.5 inch) wrought bar, 1 h at 1288 °C (2350 °F), water quenched || room temperature value
    UTS    (N):    12.7 mm (0.5 inch) bar, 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F) || 20 °C (68 °F) to 1204 °C (2199 °F)
    YS    (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || room temperature value || room temperature value
    YS    (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    YS    (N*):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    YS    (N*):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    YS     (N):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    YS    (N*):    12.7 mm (0.5 inch) wrought bar, 1 h at 1288 °C (2350 °F), water quenched || room temperature value
    YS     (N):    12.7 mm (0.5 inch) bar, 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F) || 20 °C (68 °F) to 815 °C (1499 °F)
    %El   (N*):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || room temperature value
    %El   (N*):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || room temperature value
    %El   (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || room temperature value || room temperature value
    %El    (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || elevated temperatures || 537 °C (998 °F) to 871 °C (1600 °F)
    %El   (N*):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    %El    (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    %El   (N*):    wrought, 1 h at 1260 °C (2300 °F), water quenched || room temperature value
    %El   (N*):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    %El    (N):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || elevated temperatures || 538 °C (1000 °F) to 871 °C (1600 °F)
    %El   (N*):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || room temperature value || room temperature value
    %El    (N):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || elevated temperatures || 649 °C (1200 °F) to 815 °C (1499 °F)
    %El   (N*):    12.7 mm (0.5 inch) wrought bar, 1 h at 1288 °C (2350 °F), water quenched || room temperature value
    %El    (N):    12.7 mm (0.5 inch) bar, 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F) || 20 °C (68 °F) to 1204 °C (2199 °F)
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 538 °C (1000 °F) || 36 h to 2,350 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 77 h to 6,500 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 71 h to 2,350 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 83 h to 6,200 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 17.1 h to 25.4 h
    SR     (N):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 593 °C (1100 °F) || 270 h to 1 x 10⁴ h
    SR     (N):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 35 h to 4,800 h
    SR     (N):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 23.8 h to 28.4 h
    SR     (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched, 6 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F), transverse direction || 35 h to 1,900 h
    SR     (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched, 6 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F), longitudinal direction || 30 h to 5,600 h
    SR     (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched, 6 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F), transverse & longitudinal directions || 30 h to 5,600 h
    SR     (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, 12 h at 760 °C (1400 °F), air cooled, hot worked at 760 °C (1400 °F) || tested at 732 °C (1350 °F) || 53 h to 1,400 h
    SR     (N):    forged 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, forged at 1149 °C (2100 °F), 12 h 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 100 h to 670 h
    SR     (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched || tested at 649 °C (1200 °F) || 530 h to 4,000 h
    SR     (N):    102 mm (4 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 47 h to 800 h
    SR     (N):    102 mm (4 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 871 °C (1600 °F) || tested at 871 °C (1600 °F) || 13 h to 710 h
    SR     (N):    203 mm (8 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 13 h to 710 h
    SR     (N):    203 mm (8 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 13 h to 710 h
    SR     (N):    229 mm (9 inch) ingot, forged at 1260 °C (2300 °F), forged at 1232 °C (2250 °F), rolled at 1232 °C (2250 °F), 1 h at 1260 °C (2300 °F), aged 16 h at 760 °C (1400 °F) || tested at 816 °C (1500 °F) || 50 h to 360 h
    SR     (N):    229 mm (9 inch) ingot, forged at 1260 °C (2300 °F), forged at 1232 °C (2250 °F), rolled at 1232 °C (2250 °F), 1 h at 1260 °C (2300 °F), aged 16 h at 760 °C (1400 °F) || tested at 871 °C (1600 °F) || 490 h to 2,350 h
    SR     (N):    229 mm (9 inch) ingot, forged at 1260 °C (2300 °F), forged at 1232 °C (2250 °F), rolled at 1232 °C (2250 °F), 1 h at 1260 °C (2300 °F), aged 16 h at 760 °C (1400 °F) || Master curve (LMP) || 30.7 h to 34.2 h
    SR     (N):    forged at 1149 °C (2100 °F), 1 h at 1177 °C (2150 °F), water quenched, worked at 760 °C (1400 °F), 20 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 90 h to 450 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), 12 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 110 h to 250 h
    SR     (N):    12.7 mm (0.5 inch) wrought bar, 1 h at 1288 °C (2350 °F), water quenched || tested at 816 °C (1500 °F) || 95 h to 1,200 h
    SR     (N):    19.8 mm (0.78125 inch) rolled bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 14 h to 1,300 h
    SR     (N):    19.8 mm (0.78125 inch) rolled bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 7 h to 150 h
    SR     (N):    19.8 mm (0.78125 inch) rolled bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 21.5 h to 24.3 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 29 h to 290 h
    CRR    (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 1.5 x 10^-¹¹/s to 4.6 x 10^-⁹/s
    CRR    (N):    swaged, 1 h at 1260 °C (2300 °F), water quenched, 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 1.4 x 10^-¹¹/s to 2.6 x 10^-⁹/s
    CRR    (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched || tested at 649 °C (1200 °F) || 3.4 x 10^-¹¹/s to 2 x 10^-¹⁰/s
    CRR    (N):    wrought, 1 h at 1260 °C (2300 °F), water quenched || tested at 816 °C (1500 °F) || 1.2 x 10^-¹⁰/s to 7 x 10^-¹⁰/s
    CRR    (N):    102 mm (4 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 1.5 x 10^-¹⁰/s to 1.1 x 10^-⁷/s
    CRR    (N):    102 mm (4 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 871 °C (1600 °F) || tested at 871 °C (1600 °F) || 6.9 x 10^-¹⁰/s to 1.5 x 10^-⁶/s
    CRR    (N):    203 mm (8 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 6 x 10^-¹¹/s to 1.2 x 10^-¹⁰/s
    CRR    (N):    203 mm (8 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 1.5 x 10^-¹⁰/s to 8.1 x 10^-⁷/s
    CRR    (N):    203 mm (8 inch) ingot, forged at 1232 °C (2250 °F), rolled at 1204 °C (2200 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 2.6 x 10^-¹⁰/s to 7.3 x 10^-⁷/s
    CRR    (N):    229 mm (9 inch) ingot, forged at 1260 °C (2300 °F), forged at 1232 °C (2250 °F), rolled at 1232 °C (2250 °F), 1 h at 1260 °C (2300 °F), aged 16 h at 760 °C (1400 °F) || tested at 816 °C (1500 °F) || 2.2 x 10^-¹¹/s to 1.9 x 10^-⁷/s
    CRR    (N):    229 mm (9 inch) ingot, forged at 1260 °C (2300 °F), forged at 1232 °C (2250 °F), rolled at 1232 °C (2250 °F), 1 h at 1260 °C (2300 °F), aged 16 h at 760 °C (1400 °F) || tested at 871 °C (1600 °F) || 5.5 x 10^-¹¹/s to 8.5 x 10^-⁹/s
    CRR    (N):    12.7 mm (0.5 inch) wrought bar, 1 h at 1288 °C (2350 °F), water quenched || tested at 816 °C (1500 °F) || 2.5 x 10^-¹¹/s to 1.15 x 10^-⁷/s
    CRR    (N):    19.8 mm (0.78125 inch) rolled bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 1.3 x 10^-⁸/s to 2.6 x 10^-⁶/s
    CRR    (N):    19.8 mm (0.78125 inch) rolled bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 1.7 x 10^-⁸/s to 2.3 x 10^-⁶/s

return to listing

S-590

    E      (N):    roll bar, 1 h at 1232 °C (2250 °F), water quenched, aged 16 h at 760 °C (1400 °F) || 20 °C (68 °F) to 760 °C (1400 °F)
    UTS    (N):    roll bar, 1 h at 1232 °C (2250 °F), water quenched, aged 16 h at 760 °C (1400 °F) || 20 °C (68 °F) to 760 °C (1400 °F)
    UTS   (N*):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || room temperature value
    UTS   (N*):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || room temperature value
    UTS   (N*):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    UTS   (N*):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    YS     (N):    roll bar, 1 h at 1232 °C (2250 °F), water quenched, aged 16 h at 760 °C (1400 °F) || 20 °C (68 °F) to 760 °C (1400 °F)
    YS    (N*):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || room temperature value
    YS    (N*):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    YS    (N*):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    %El    (N):    roll bar, 1 h at 1232 °C (2250 °F), water quenched, aged 16 h at 760 °C (1400 °F) || 20 °C (68 °F) to 760 °C (1400 °F)
    %El   (N*):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || room temperature value
    %El   (N*):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || room temperature value
    %El   (N*):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    %El   (N*):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || room temperature value
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 538 °C (1000 °F) || 11 h to 5,700 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 70 h to 2,300 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 3.5 h to 3,750 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 19.9 h to 27.2 h
    SR     (N):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || tested at 593 °C (1100 °F) || 50 h to 4,800 h
    SR     (N):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || tested at 649 °C (1200 °F) || 80 h to 2,000 h
    SR     (N):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || Master curve (LMP) || 29.2 h to 32.5 h
    SR     (N):    wrought, 0.5 h at 1246 °C (2275 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 43 h to 1.1 x 10⁴ h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 20 h to 3,650 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 25 h to 1,200 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 0.4 h to 3,200 h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || tested at 927 °C (1700 °F) || 3.7 h to 1.2 x 10⁴ h
    SR     (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 12 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 17.8 h to 26.5 h
    SR     (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 14 h to 1,200 h
    SR     (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 67 h to 900 h
    SR     (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F) || tested at 871 °C (1600 °F) || 73 h to 450 h
    SR     (N):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 55 h to 340 h
    SR     (N):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 5 h to 200 h
    SR     (N):    wrought, 1 h at 1204 °C (2200 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 21.9 h to 26.4 h
    SR     (N):    rolled to bar at 1149 °C (2100 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 816 °C (1500 °F), furnace cooled || tested at 732 °C (1350 °F) || 15 h to 1,800 h
    SR     (N):    rolled to bar at 1149 °C (2100 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 816 °C (1500 °F), furnace cooled || tested at 816 °C (1500 °F) || 10 h to 5,200 h
    SR     (N):    rolled to bar at 1149 °C (2100 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 816 °C (1500 °F), furnace cooled || Master curve (LMP) || 17.3 h to 21.5 h
    SR     (N):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 28 h to 250 h
    SR     (N):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || tested at 816 °C (1500 °F) || 6 h to 180 h
    SR     (N):    1 h at 1149 °C (2100 °F), air cooled, aged 8 h at 760 °C (1400 °F), air cooled || Master curve (LMP) || 22.6 h to 27.5 h
    SR     (N):    wrought, 1 h at 1232 °C (2250 °F), water quench, 2 h at 649 °C (1200 °F), air cooled, 5 h at 649 °C (1200 °F), 24 h at 760 °C (1400 °F) || tested at 732 °C (1350 °F) || 35 h to 1,150 h
    SR     (N):    wrought sheet, annealed at 1177 °C (2150 °F), air cooled || tested at 927 °C (1700 °F) || 2 h to 530 h
    SR     (N):    wrought sheet, annealed at 1177 °C (2150 °F), air cooled || tested at 982 °C (1800 °F) || 1 h to 700 h
    SR     (N):    wrought sheet, annealed at 1177 °C (2150 °F), air cooled || Master curve (LMP) || 20.3 h to 24.3 h
    CRR    (N):    wrought, 1 h at 1177 °C (2150 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 5.5 x 10^-¹²/s to 4.5 x 10^-¹¹/s
    CRR    (N):    wrought, 1 h at 1249 °C (2280 °F), water quenched, aged 16 h at 816 °C (1500 °F), air cooled || tested at 649 °C (1200 °F) || 5.5 x 10^-¹¹/s to 1 x 10^-¹⁰/s
    CRR    (N):    wrought, 0.5 h at 1246 °C (2275 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 649 °C (1200 °F) || 8.5 x 10^-¹²/s to 1.6 x 10^-¹¹/s
    CRR    (N):    wrought, 0.5 h at 1246 °C (2275 °F), water quenched, aged 16 h at 760 °C (1400 °F), air cooled || tested at 732 °C (1350 °F) || 1.1 x 10^-¹¹/s to 4.2 x 10^-¹¹/s
    CRR    (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 5 x 10^-¹¹/s to 2 x 10^-⁹/s
    CRR    (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 2.7 x 10^-¹²/s to 1.4 x 10^-⁶/s
    CRR    (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 5.8 x 10^-¹¹/s to 6.2 x 10^-⁷/s
    CRR    (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 760 °C (1400 °F) || tested at 871 °C (1600 °F) || 5 x 10^-¹¹/s to 6.2 x 10^-⁸/s
    CRR    (N):    25.4 mm (1 inch) bar, 1 h at 1260 °C (2300 °F), water quenched, aged 50 h at 871 °C (1600 °F) || tested at 871 °C (1600 °F) || 2.2 x 10^-¹¹/s to 1.32 x 10^-¹⁰/s
    CRR    (N):    rolled to bar at 1149 °C (2100 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 816 °C (1500 °F), furnace cooled || tested at 732 °C (1350 °F) || 1.8 x 10^-⁸/s to 2.35 x 10^-⁶/s
    CRR    (N):    rolled to bar at 1149 °C (2100 °F), 1 h at 1260 °C (2300 °F), water quenched, aged 16 h at 816 °C (1500 °F), furnace cooled || tested at 816 °C (1500 °F) || 2.3 x 10^-¹⁰/s to 2.2 x 10^-⁶/s

return to listing

S700

    FSN    (N):    weld || tested at 20 °C (68 °F), R = 0.1, axial, as-weld, stress range || 3 x 10⁴ cycles to 2 x 10⁷ cycles
    FSN    (N):    weld || tested at 20 °C (68 °F), R = 0.1, axial, HFMI treated, stress range || 6 x 10⁴ cycles to 2 x 10⁷ cycles
    FSN    (N):    weld || tested at 20 °C (68 °F), R = 0.5, axial, HFMI treated, stress range || 3 x 10⁴ cycles to 2 x 10⁷ cycles

return to listing

SAE J435 Grade 0030

    FEN    (R):    axial loading || tested at 20 °C (68 °F), R = -1, axial, total strain amplitude || 50 cycles to 1 x 10⁷ cycles
    FEN    (N):    axial loading || tested at 20 °C (68 °F), R = -1, axial, plastic strain amplitude || 50 cycles to 9 x 10⁵ cycles
    FEN    (N):    axial loading || tested at 20 °C (68 °F), R = -1, axial, elastic strain amplitude || 50 cycles to 9 x 10⁵ cycles
    FEN    (R):    axial loading || tested at -46 °C (-50 °F), R = -1, axial, total strain amplitude || 240 cycles to 1 x 10⁷ cycles
    FEN    (N):    axial loading || tested at -46 °C (-50 °F), R = -1, axial, plastic strain amplitude || 240 cycles to 6 x 10⁵ cycles
    FEN    (N):    axial loading || tested at -46 °C (-50 °F), R = -1, axial, elastic strain amplitude || 240 cycles to 6 x 10⁵ cycles

return to listing

Scalmalloy

FSN (R): laser powder bed fusion || tested at 20 °C (68 °F), R = -1, axial, maximum stress || 8 x 10³ cycles to 1 x 10⁸ cycles

return to listing

Selectron 44 polyester

    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 0.3 h || 0 to 0.7 mm/mm strain
    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 1 h || 0 to 0.7 mm/mm strain
    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 3 h || 0 to 0.7 mm/mm strain
    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 10 h || 0 to 0.7 mm/mm strain
    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 30 h || 0 to 0.7 mm/mm strain
    IC     (R):    tested at 71 °C (160 °F), total strain, annealed sheet || 100 h || 0 to 0.7 mm/mm strain

return to listing

63 Sn - 37 Pb (wt %)

FEN (R): as-cast || tested at 25 °C (77 °F), R = -1, axial, 0.001/s, total strain range || 140 cycles to 8 x 10³ cycles

return to listing

Stellite 21

    UTS   (N*):    as-cast || room temperature value || room temperature value
    UTS    (N):    as-cast || elevated temperatures || 538 °C (1000 °F) to 982 °C (1799 °F)
    UTS   (N*):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || room temperature value
    UTS   (N*):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || room temperature value
    YS    (N*):    as-cast || room temperature value || room temperature value
    YS     (N):    as-cast || elevated temperatures || 538 °C (1000 °F) to 649 °C (1200 °F)
    YS    (N*):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || room temperature value
    YS    (N*):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || room temperature value
    %El   (N*):    as-cast || room temperature value || room temperature value
    %El    (N):    as-cast || elevated temperatures || 538 °C (1000 °F) to 982 °C (1799 °F)
    %El   (N*):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || room temperature value
    SR     (N):    as-cast || tested at 816 °C (1500 °F) || 31 h to 380 h
    SR     (N):    as-cast || tested at 816 °C (1500 °F), cored dendritic structure || 35 h to 1,510 h
    SR     (N):    precision cast, as-cast, with 0.1 wt% B || tested at 816 °C (1500 °F) || 40 h to 1,350 h
    SR     (N):    cast, aged 732 °C (1350 °F) for 50 h || tested at 732 °C (1350 °F) || 15 h to 640 h
    SR     (N):    cast, aged 732 °C (1350 °F) for 50 h || tested at 816 °C (1500 °F) || 6 h to 840 h
    SR     (N):    cast, aged 732 °C (1350 °F) for 50 h || Master curve (LMP) || 13.3 h to 16.2 h
    SR     (N):    cast, aged 816 °C (1500 °F) for 50 h || tested at 816 °C (1500 °F) || 42 h to 670 h
    SR     (N):    cast, aged 871 °C (1600 °F) for 50 h || tested at 871 °C (1600 °F) || 34 h to 1,700 h
    SR     (N):    forged at 1116 °C (2040 °F) to 1038 °C (1900 °F), rolled at 1149 °C (2100 °F) to 1038 °C (1900 °F), annealed 6 minutes at 1121 °C (2050 °F), pickled || tested at 927 °C (1700 °F) || 0.4 h to 610 h
    SR     (N):    forged at 1116 °C (2040 °F) to 1038 °C (1900 °F), rolled at 1149 °C (2100 °F) to 1038 °C (1900 °F), annealed 6 minutes at 1121 °C (2050 °F), pickled || tested at 982 °C (1800 °F) || 2.3 h to 480 h
    SR     (N):    forged at 1116 °C (2040 °F) to 1038 °C (1900 °F), rolled at 1149 °C (2100 °F) to 1038 °C (1900 °F), annealed 6 minutes at 1121 °C (2050 °F), pickled || Master curve (LMP) || 24.8 h to 29.7 h
    SR     (N):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || tested at 871 °C (1600 °F) || 8 h to 460 h
    SR     (N):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || tested at 982 °C (1800 °F) || 43 h to 270 h
    SR     (N):    1204 °C (2200 °F), furnace cooled, 0.965 mm (0.038 inch) sheet || tested at 1093 °C (2000 °F) || 2.9 h to 13 h
    SR     (N):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || tested at 649 °C (1200 °F) || 8 h to 73 h
    SR     (N):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || tested at 816 °C (1500 °F) || 17 h to 37 h
    SR     (N):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || tested at 927 °C (1700 °F) || 3.7 h to 130 h
    SR     (N):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || tested at 1038 °C (1900 °F) || 6 h to 63 h
    SR     (N):    1038 °C (1900 °F), furnace cooled, 1.6 mm (0.063 inch) sheet || Master curve (LMP) || 12 h to 18.1 h
    CRR    (N):    as-cast || tested at 538 °C (1000 °F) || 5.7 x 10^-¹²/s to 2.7 x 10^-¹¹/s
    CRR    (N):    as-cast || tested at 649 °C (1200 °F) || 3.9 x 10^-¹¹/s to 2.4 x 10^-¹⁰/s
    CRR    (N):    precision cast, as-cast, with 0.1 wt% B || tested at 816 °C (1500 °F), with 0.1 wt% B || 1.35 x 10^-⁹/s to 7.7 x 10^-⁷/s
    CRR    (N):    cast, aged 732 °C (1350 °F) for 50 h || tested at 732 °C (1350 °F) || 1 x 10^-⁸/s to 3 x 10^-⁷/s
    CRR    (N):    cast, aged 732 °C (1350 °F) for 50 h || tested at 816 °C (1500 °F) || 1.8 x 10^-¹⁰/s to 2 x 10^-⁶/s
    CRR    (N):    cast, aged 816 °C (1500 °F) for 50 h || tested at 816 °C (1500 °F) || 2.7 x 10^-¹¹/s to 1.6 x 10^-⁷/s
    CRR    (N):    cast, aged 871 °C (1600 °F) for 50 h || tested at 816 °C (1500 °F) || 8.3 x 10^-⁹/s to 5.9 x 10^-⁷/s

return to listing

Tantalum

    CRS    (R):    1% plastic strain, cold worked sheet || Master curve (LMP) || 22.5 h to 32.8 h
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 30,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 100,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet || 300,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 30,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1232 °C (2250 °F), plastic strain, cold worked sheet || 100,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 30,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1260 °C (2300 °F), plastic strain, cold worked sheet || 100,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1288 °C (2350 °F), plastic strain, cold worked sheet || 30,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1316 °C (2400 °F), plastic strain, cold worked sheet || 30,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.2 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1343 °C (2450 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1371 °C (2500 °F), plastic strain, cold worked sheet || 10,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1399 °C (2550 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.5 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet || 3,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1454 °C (2650 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1482 °C (2700 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1510 °C (2750 °F), plastic strain, cold worked sheet || 1,000 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1538 °C (2800 °F), plastic strain, cold worked sheet || 300 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1566 °C (2850 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1593 °C (2900 °F), plastic strain, cold worked sheet || 100 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1621 °C (2950 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 0.1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 0.3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 1 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 3 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 10 h || 0 to 0.1 mm/mm strain
    IC     (R):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet || 30 h || 0 to 0.1 mm/mm strain

return to listing

Ti - 4 Al - 4 Mn (wt %)

CRS (R): 0.1% plastic strain || tested at 371 °C (700 °F) || 0.2 h to 10 h

return to listing

Ti - 4 Al - 3 Mo - 1 V (wt %)

    FSN    (N):    annealed sheet per MIL-H-81200 || tested at 21 °C (70 °F), R = -0.3, axial, K_t = 1.0, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    annealed sheet per MIL-H-81200 || tested at 21 °C (70 °F), R = 0, axial, K_t = 1.0, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    annealed sheet per MIL-H-81200 || tested at 21 °C (70 °F), R = 0.3, axial, K_t = 1.0, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

Ti - 8 Al - 2 Nb - 1 Mo - 1 V (wt %)

    CRS    (N):    0.3% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || Master curve (LMP) || 16.1 h to 21.3 h
    CRS    (N):    0.5% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || Master curve (LMP) || 14 h to 18.3 h
    CRS    (N):    1% plastic strain, 1 h at 982 °C (1800 °F), aged 8 h at 593 °C (1100 °F) || Master curve (LMP) || 12.1 h to 16.3 h

return to listing

Ti - 6 Al - 2 Sn - 4 Zr - 2 Mo (wt %)

SR (R): as-cast || tested at 482 °C (900 °F) || 4 h to 550 h

return to listing

Ti - 5 Al - 2.5 Sn (Grade 6)

    FEN    (N):    vacuum annealed || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 50 cycles to 7 x 10³ cycles
    FEN    (N):    vacuum annealed || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 50 cycles to 6.5 x 10⁴ cycles
    FEN    (N):    vacuum annealed || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 40 cycles to 3.9 x 10⁴ cycles
    FEN    (N):    vacuum annealed || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 40 cycles to 6.1 x 10⁴ cycles
    FEN    (N):    vacuum annealed || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 50 cycles to 1.6 x 10⁴ cycles
    FEN    (N):    vacuum annealed || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 50 cycles to 1.6 x 10⁴ cycles

return to listing

Ti - 8 Al - 1 Ta (wt %)

    CRS    (R):    0.1% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 0.1 h to 430 h
    CRS    (R):    0.1% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 0.3 h to 150 h
    CRS    (R):    0.3% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 0.6 h to 1,630 h
    CRS    (R):    0.3% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 1 h to 745 h
    CRS    (R):    0.5% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 1 h to 2,900 h
    CRS    (R):    0.5% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 1.5 h to 1,400 h
    CRS    (R):    0.5% plastic strain, mill annealed sheet || Master curve (LMP) || 14.2 h to 17.4 h
    CRS    (R):    1% plastic strain, mill annealed sheet || tested at 538 °C (1000 °F) || 1 h to 2,900 h
    CRS    (R):    1% plastic strain, mill annealed sheet || tested at 593 °C (1100 °F) || 3.8 h to 1,050 h
    CRS    (R):    1% plastic strain, mill annealed sheet || Master curve (LMP) || 11.6 h to 14.3 h

return to listing

Ti - 6 Al - 4 V

    FSN    (R):    annealed || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.1, flexure, maximum stress || 1.1 x 10⁴ cycles to 1.25 x 10⁶ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = -0.3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = 0, axial, maximum stress || 8 x 10³ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = 0.3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = -1, K_t = 3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = -0.3, K_t = 3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = 0, K_t = 3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    solution treated & aged || tested at 20 °C (68 °F), R = 0.3, K_t = 3, axial, maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FEN    (N):    vacuum annealed bar || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 80 cycles to 630 cycles
    FEN    (N):    vacuum annealed bar || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 80 cycles to 2.2 x 10⁴ cycles
    FEN    (N):    vacuum annealed bar || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 40 cycles to 320 cycles
    FEN    (N):    vacuum annealed bar || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 40 cycles to 3.5 x 10⁴ cycles
    FEN    (N):    vacuum annealed bar || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 80 cycles to 3.8 x 10³ cycles
    FEN    (N):    vacuum annealed bar || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 80 cycles to 6.2 x 10⁴ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, horizontal, total strain amplitude, Syed et al. || 270 cycles to 3.4 x 10⁶ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, horizontal, elastic strain amplitude, Syed et al. || 270 cycles to 3.4 x 10⁶ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, horizontal, plastic strain amplitude, Syed et al. || 270 cycles to 3.2 x 10³ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, vertical, total strain amplitude, Syed et al. || 400 cycles to 1.4 x 10⁶ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, vertical, elastic strain amplitude, Syed et al. || 400 cycles to 1.4 x 10⁶ cycles
    FEN    (R):    wire + arc additive manufactured || tested at 20 °C (68 °F), R = -1, axial, vertical, plastic strain amplitude, Syed et al. || 400 cycles to 1.1 x 10⁴ cycles

return to listing

Ti - 46 Al - 2 W - 0.5 Si (at %) (ABB-2)

    CRR    (N):    cast bar || tested at 371 °C (700 °F) || 1.9 x 10^-¹⁰/s to 2.9 x 10^-⁸/s
    CRR    (N):    cast bar || tested at 399 °C (750 °F) || 3 x 10^-⁹/s to 5.8 x 10^-⁷/s
    CRR    (N):    cast bar || tested at 427 °C (800 °F) || 2.2 x 10^-⁸/s to 3.5 x 10^-⁶/s
    CRR    (N):    cast bar || tested at 482 °C (900 °F) || 3.1 x 10^-⁹/s to 1.5 x 10^-⁶/s

return to listing

Ti - 7 Al - 12 Zr (wt %)

    CRS    (R):    0.1% plastic strain, annealed at 871 °C (1600 °F) || tested at 427 °C (800 °F) || 10 h to 200 h
    CRS    (R):    0.1% plastic strain, annealed at 871 °C (1600 °F) || tested at 482 °C (900 °F) || 3 h to 200 h
    CRS    (R):    0.1% plastic strain, annealed at 871 °C (1600 °F) || tested at 538 °C (1000 °F) || 5 h to 200 h
    CRS    (R):    0.1% plastic strain, annealed at 871 °C (1600 °F) || tested at 593 °C (1100 °F) || 15 h to 30 h
    CRS    (R):    0.1% plastic strain, annealed at 871 °C (1600 °F) || Master curve (LMP) || 30.1 h to 37.7 h

return to listing

Ti - 16 V - 2.5 Al (wt %)

CRS (R): 0.3% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || Master curve (LMP) || 7.91 h to 12.1 h
CRS (R): 0.5% plastic strain, heat treated at 760 °C (1400 °F), aged at 516 °C (960 °F) || Master curve (LMP) || 8.16 h to 12.1 h

return to listing

Ti Grade 2

    FSN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = 0, axial, longitudinal, YS = 248 MPa (36 ksi), maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = 0, axial, transverse, YS = 337 MPa (48.9 ksi), maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = 0.3, axial, longitudinal, YS = 248 MPa (36 ksi), maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles
    FSN    (N):    hot-rolled plate || tested at 20 °C (68 °F), R = 0.3, axial, transverse, YS = 337 MPa (48.9 ksi), maximum stress || 1 x 10⁴ cycles to 1 x 10⁷ cycles

return to listing

Ti Grade 4

    CRS    (R):    0.1% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 13 h to 15.6 h
    CRS    (R):    0.2% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 19.3 h to 22.4 h
    CRS    (R):    0.3% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 18 h to 20.9 h
    CRS    (R):    0.5% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 16.9 h to 19.6 h
    CRS    (R):    1% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 15.6 h to 17.5 h
    CRS    (R):    2% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 12.9 h to 14.3 h
    CRS    (R):    5% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed || Master curve (LMP) || 13.7 h to 14.8 h
    CRS    (R):    0.3% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed, in compression || Master curve (LMP) || 13.9 h to 15.5 h
    CRS    (R):    0.5% plastic strain, 1.63 mm (0.064 inch) thick sheet, annealed, in compression || Master curve (LMP) || 14 h to 15.2 h

return to listing

Ti-140A (Ti - 2 Cr - 2 Fe - 2 Mo (wt %))

    CRS    (R):    0.1% plastic strain, mill annealed || Master curve (LMP) || 8.69 h to 10.8 h
    CRS    (R):    0.3% plastic strain, mill annealed || Master curve (LMP) || 12.2 h to 14.8 h
    CRS    (R):    0.5% plastic strain, mill annealed || Master curve (LMP) || 14.5 h to 18 h
    CRS    (R):    1% plastic strain, mill annealed || Master curve (LMP) || 15.8 h to 19.2 h

return to listing

TRIP 700

FEN (R): hot-rolled || tested at 20 °C (68 °F), R = -1, axial, total strain amplitude || 220 cycles to 1.4 x 10⁵ cycles
FEN (R): cold-rolled || tested at 20 °C (68 °F), R = -1, axial, total strain amplitude || 50 cycles to 3 x 10⁴ cycles

return to listing

Tungsten

    CRR    (N):    rod || tested at 2250 °C (4082 °F) || 6 x 10^-⁷/s to 7.3 x 10^-⁴/s
    CRR    (N):    rod || tested at 2500 °C (4532 °F) || 1 x 10^-⁶/s to 8.7 x 10^-⁵/s
    CRR    (N):    rod || tested at 2700 °C (4892 °F) || 7.6 x 10^-⁶/s to 1 x 10^-³/s
    CRR    (N):    rod || tested at 2800 °C (5072 °F) || 5.4 x 10^-⁶/s to 4.4 x 10^-⁴/s

return to listing

Udimet 500

    SR     (R):    aged || Master curve (LMP) || 26.6 h to 39.2 h
    CRS    (R):    0.1% plastic strain, aged || Master curve (LMP) || 30 h to 43.7 h
    CRS    (R):    0.5% plastic strain, aged || Master curve (LMP) || 25.8 h to 39.2 h
    CRS    (R):    1% plastic strain, aged || Master curve (LMP) || 27 h to 40.9 h

return to listing

Udimet D-979

    CRS    (R):    1% plastic strain, solution treated & aged || tested at 593 °C (1100 °F) || 425 h to 4.6 x 10⁴ h
    CRS    (R):    1% plastic strain, solution treated & aged || tested at 649 °C (1200 °F) || 125 h to 1.1 x 10⁴ h
    CRS    (R):    1% plastic strain, solution treated & aged || tested at 704 °C (1300 °F) || 105 h to 8,200 h
    CRS    (R):    1% plastic strain, solution treated & aged || tested at 760 °C (1400 °F) || 100 h to 1.65 x 10⁴ h
    CRS    (R):    1% plastic strain, solution treated & aged || tested at 816 °C (1500 °F) || 135 h to 1.8 x 10⁴ h
    CRS    (R):    1% plastic strain, solution treated & aged || Master curve (LMP) || 20 h to 26.8 h

return to listing

UNS C11000 (ETP)

    UTS   (N*):    cold worked || 3.17 mm (0.125 inch) rod, cold drawn 84% || room temperature value
    YS    (N*):    cold worked || 3.17 mm (0.125 inch) rod, cold drawn 84% || room temperature value
    %El   (N*):    cold worked || 3.17 mm (0.125 inch) rod, cold drawn 84% || room temperature value
    SR     (N):    annealed || tested at 149 °C (300 °F) || 2.5 h to 910 h
    SR     (N):    annealed || tested at 204 °C (400 °F) || 1.7 h to 940 h
    SR     (N):    annealed || Master curve (LMP) || 4.39 h to 6.19 h
    CRR    (N):    cold rolled || tested at 130 °C (266 °F), 2.54 mm (0.1 inch) rolled strip, cold rolled 50%, 0.086 wt% Ag || 4.1 x 10^-¹²/s to 8.4 x 10^-¹²/s
    CRR    (N):    cold rolled || tested at 175 °C (347 °F), 2.54 mm (0.1 inch) rolled strip, cold rolled 50%, 0.086 wt% Ag || 6.9 x 10^-¹²/s to 5.3 x 10^-¹¹/s
    CRR    (N):    cold rolled || tested at 205 °C (401 °F), 2.54 mm (0.1 inch) rolled strip, cold rolled 50%, 0.086 wt% Ag || 3.6 x 10^-¹¹/s to 3.1 x 10^-¹⁰/s
    CRR    (N):    cold worked || tested at 149 °C (300 °F), 3.17 mm (0.125 inch) rod, cold drawn 84% || 1.3 x 10^-¹¹/s to 2.8 x 10^-¹¹/s
    CRR    (N):    cold worked || tested at 204 °C (400 °F), 3.17 mm (0.125 inch) rod, cold drawn 84% || 3 x 10^-¹²/s to 1.25 x 10^-⁹/s
    CRR    (N):    cold worked || tested at 149 °C (300 °F), 3.17 mm (0.125 inch) rod, cold drawn 84%, 0.033 wt% Ag || 8.3 x 10^-¹³/s to 1.6 x 10^-¹⁰/s

return to listing

UNS C10100 (OFE)

    FEN    (N):    annealed || tested at -269.1 °C (-452.5 °F), R = -1, axial, elastic strain range || 150 cycles to 9.2 x 10⁴ cycles
    FEN    (N):    annealed || tested at -269.1 °C (-452.5 °F), R = -1, axial, plastic strain range || 150 cycles to 9.2 x 10⁴ cycles
    FEN    (N):    annealed || tested at -195.1 °C (-319.3 °F), R = -1, axial, elastic strain range || 80 cycles to 2.2 x 10⁵ cycles
    FEN    (N):    annealed || tested at -195.1 °C (-319.3 °F), R = -1, axial, plastic strain range || 80 cycles to 2.2 x 10⁵ cycles
    FEN    (N):    annealed || tested at 27 °C (80 °F), R = -1, axial, elastic strain range || 80 cycles to 6.4 x 10⁴ cycles
    FEN    (N):    annealed || tested at 27 °C (80 °F), R = -1, axial, plastic strain range || 80 cycles to 6.4 x 10⁴ cycles

return to listing

UNS C10200 (OFHC/OF)

FEN (R): annealed || tested at 538 °C (1000 °F), R = -1, axial, 0.002/s, total strain range || 100 cycles to 3.2 x 10³ cycles
FEN (R): cold worked || tested at 20 °C (68 °F), R = -1, axial, plastic strain range || 1 cycles to 420 cycles

return to listing

UNS C14200

    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || tested at 149 °C (300 °F) || 1.7 h to 1,800 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || tested at 204 °C (400 °F) || 0.17 h to 400 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || Master curve (LMP) || 10.7 h to 13.2 h
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || tested at 149 °C (300 °F) || 6.5 x 10^-¹²/s to 5.3 x 10^-¹¹/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || tested at 204 °C (400 °F) || 6.3 x 10^-¹²/s to 6.2 x 10^-¹¹/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 45 micron grain size || tested at 260 °C (500 °F) || 1.35 x 10^-¹²/s to 4.3 x 10^-¹⁰/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 6.6 x 10^-¹³/s to 1.2 x 10^-⁹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 2.7 x 10^-¹³/s to 3.3 x 10^-⁹/s

return to listing

UNS C15100

SR (N): cold worked 84% || Master curve (LMP) || 7.68 h to 9.56 h

return to listing

UNS C18150

    FEN    (N):    solution annealed & aged || tested at 20 °C (68 °F), R = -1, axial, a 10 s hold at max tensile and max compression, total strain amplitude || 850 cycles to 7 x 10⁴ cycles
    FEN    (N):    aged + 1 h at 600 °C (1112 °F) || tested at 20 °C (68 °F), R = -1, axial, a 10 s hold at max tensile and max compression, total strain amplitude || 850 cycles to 7 x 10⁴ cycles
    FEN    (N):    aged + 4 h at 600 °C (1112 °F) || tested at 20 °C (68 °F), R = -1, axial, a 10 s hold at max tensile and max compression, total strain amplitude || 850 cycles to 7 x 10⁴ cycles

return to listing

UNS C19000

    UTS   (N*):    age hardened || 3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || room temperature value
    UTS   (N*):    age hardened || 3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F), drawn 84% || room temperature value
    %El   (N*):    age hardened || 3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || room temperature value
    %El   (N*):    age hardened || 3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F), drawn 84% || room temperature value
    SR     (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || tested at 204 °C (400 °F) || 0.1 h to 150 h
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || tested at 149 °C (300 °F) || 1.12 x 10^-¹²/s to 6.4 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || tested at 204 °C (400 °F) || 8.3 x 10^-¹³/s to 4.2 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F) || tested at 260 °C (500 °F) || 1.6 x 10^-¹²/s to 2 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F), drawn 84% || tested at 149 °C (300 °F) || 8.3 x 10^-¹³/s to 1.2 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F), drawn 84% || tested at 204 °C (400 °F) || 1.6 x 10^-¹²/s to 8.1 x 10^-¹²/s
    CRR    (N):    3.17 mm (0.125 inch) rod, quenched from 788 °C (1450 °F), aged 4 h at 454 °C (850 °F), drawn 84% || tested at 260 °C (500 °F) || 2.4 x 10^-¹²/s to 3.9 x 10^-¹⁰/s

return to listing

UNS C23000

    SR     (N):    3.17 mm (0.125 inch) diameter bar, annealed, 60 micron grain size || tested at 149 °C (300 °F) || 9 h to 3,300 h
    SR     (N):    3.17 mm (0.125 inch) diameter bar, annealed, 60 micron grain size || tested at 204 °C (400 °F) || 0.3 h to 850 h
    SR     (N):    3.17 mm (0.125 inch) diameter bar, annealed, 60 micron grain size || Master curve (LMP) || 5.69 h to 7.36 h

return to listing

UNS C46400

    SR     (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || tested at 149 °C (300 °F) || 8.8 h to 3,100 h
    SR     (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || tested at 204 °C (400 °F) || 0.37 h to 1,500 h
    SR     (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || Master curve (LMP) || 8.21 h to 10.3 h
    CRR    (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || tested at 149 °C (300 °F) || 1.1 x 10^-¹²/s to 4.9 x 10^-¹¹/s
    CRR    (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || tested at 204 °C (400 °F) || 1 x 10^-¹¹/s to 5.2 x 10^-¹⁰/s
    CRR    (N):    annealed at 538 °C (1000 °F), 3.17 mm (0.125 inch) bar || tested at 260 °C (500 °F) || 5.5 x 10^-¹¹/s to 2 x 10^-⁹/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) bar || tested at 149 °C (300 °F) || 1.9 x 10^-¹²/s to 2.75 x 10^-¹⁰/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) bar || tested at 204 °C (400 °F) || 1.3 x 10^-¹¹/s to 1.35 x 10^-⁹/s

return to listing

UNS C63000

    UTS    (N):    hot-rolled || Upthegrove et al. || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (N):    hot-rolled || Upthegrove et al. || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    hot-rolled || Upthegrove et al. || 20 °C (68 °F) to 371 °C (700 °F)
    CRR    (N):    annealed || tested at 260 °C (500 °F) || 3.3 x 10^-¹¹/s to 5.9 x 10^-¹⁰/s
    CRR    (N):    wrought, hot-rolled || tested at 316 °C (600 °F) || 1.1 x 10^-¹¹/s to 8.7 x 10^-¹¹/s
    CRR    (N):    wrought, hot-rolled || tested at 371 °C (700 °F) || 1.6 x 10^-¹¹/s to 2.35 x 10^-¹⁰/s

return to listing

UNS C65500

    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 8 micron grain size || tested at 149 °C (300 °F) || 2.4 x 10^-¹²/s to 7 x 10^-¹¹/s
    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 8 micron grain size || tested at 204 °C (400 °F) || 5 x 10^-¹²/s to 2.1 x 10^-¹⁰/s
    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 8 micron grain size || tested at 260 °C (500 °F) || 6.9 x 10^-¹²/s to 1.55 x 10^-⁹/s
    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 100 micron grain size || tested at 149 °C (300 °F) || 5.5 x 10^-¹³/s to 5.6 x 10^-¹¹/s
    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 100 micron grain size || tested at 204 °C (400 °F) || 2.7 x 10^-¹²/s to 8.9 x 10^-¹¹/s
    CRR    (N):    annealed, 3.17 mm (0.125 inch) rod, 100 micron grain size || tested at 260 °C (500 °F) || 1.1 x 10^-¹¹/s to 3.3 x 10^-¹⁰/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 6.3 x 10^-¹²/s to 1.15 x 10^-¹⁰/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 6.6 x 10^-¹²/s to 3.3 x 10^-¹¹/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) rod || tested at 260 °C (500 °F) || 1.6 x 10^-¹¹/s to 4 x 10^-¹¹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 2.2 x 10^-¹²/s to 8.4 x 10^-¹¹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 4.7 x 10^-¹²/s to 3.2 x 10^-¹¹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 260 °C (500 °F) || 1.2 x 10^-¹¹/s to 2.7 x 10^-⁹/s

return to listing

UNS C70600

    CRR    (N):    annealed rod, 30 micron grain size || tested at 149 °C (300 °F) || 8.3 x 10^-¹³/s to 1.45 x 10^-¹¹/s
    CRR    (N):    annealed rod, 30 micron grain size || tested at 204 °C (400 °F) || 6.1 x 10^-¹²/s to 1.25 x 10^-¹⁰/s
    CRR    (N):    annealed rod, 30 micron grain size || tested at 260 °C (500 °F) || 1.6 x 10^-¹²/s to 3.6 x 10^-¹⁰/s
    CRR    (N):    annealed rod, 30 micron grain size || tested at 316 °C (600 °F) || 2.5 x 10^-¹²/s to 1.7 x 10^-¹⁰/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 5.5 x 10^-¹³/s to 9.8 x 10^-¹²/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 5.5 x 10^-¹³/s to 1.05 x 10^-¹⁰/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) rod || tested at 260 °C (500 °F) || 6.1 x 10^-¹²/s to 1.3 x 10^-¹⁰/s

return to listing

UNS C12200

    UTS   (N*):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || room temperature value
    UTS   (N*):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || room temperature value
    UTS   (N*):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || room temperature value
    UTS   (N*):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    UTS   (N*):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    UTS   (N*):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    YS     (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (N):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (N):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || 20 °C (68 °F) to 260 °C (500 °F)
    YS     (N):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || 20 °C (68 °F) to 260 °C (500 °F)
    %El   (N*):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || room temperature value
    %El   (N*):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || room temperature value
    %El   (N*):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || room temperature value
    %El   (N*):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    %El   (N*):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    %El   (N*):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || tested at 149 °C (300 °F) || 0.8 h to 1,050 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || tested at 204 °C (400 °F) || 0.17 h to 1,150 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || Master curve (LMP) || 6.39 h to 8.71 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || tested at 149 °C (300 °F) || 1.1 h to 1,600 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || tested at 204 °C (400 °F) || 0.1 h to 830 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || Master curve (LMP) || 6.62 h to 8.84 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || tested at 149 °C (300 °F) || 0.6 h to 950 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || tested at 204 °C (400 °F) || 2 h to 310 h
    SR     (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || Master curve (LMP) || 8.25 h to 10.6 h
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || tested at 149 °C (300 °F) || 1.6 x 10^-¹²/s to 2 x 10^-¹⁰/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || tested at 204 °C (400 °F) || 3.8 x 10^-¹²/s to 4.15 x 10^-¹⁰/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 15 micron grain size || tested at 260 °C (500 °F) || 3.9 x 10^-¹¹/s to 4.3 x 10^-⁹/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || tested at 149 °C (300 °F) || 1.1 x 10^-¹²/s to 1.05 x 10^-¹⁰/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || tested at 204 °C (400 °F) || 2.7 x 10^-¹²/s to 3.4 x 10^-¹⁰/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 32 micron grain size || tested at 260 °C (500 °F) || 1.1 x 10^-¹¹/s to 1.05 x 10^-⁹/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || tested at 149 °C (300 °F) || 5.5 x 10^-¹³/s to 3.9 x 10^-¹¹/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || tested at 204 °C (400 °F) || 3.3 x 10^-¹²/s to 2.4 x 10^-¹⁰/s
    CRR    (N):    annealed 3.17 mm (0.125 inch) rod, 70 micron grain size || tested at 260 °C (500 °F) || 4.1 x 10^-¹²/s to 1.1 x 10^-¹⁰/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || tested at 149 °C (300 °F) || 1.6 x 10^-¹²/s to 1.1 x 10^-¹⁰/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || tested at 204 °C (400 °F) || 3.6 x 10^-¹²/s to 6.4 x 10^-¹¹/s
    CRR    (N):    drawn 21%, 3.17 mm (0.125 inch) diameter bar || tested at 260 °C (500 °F) || 1.1 x 10^-¹¹/s to 3.05 x 10^-¹⁰/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || tested at 149 °C (300 °F) || 1.9 x 10^-¹²/s to 5.2 x 10^-¹⁰/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || tested at 204 °C (400 °F) || 4.4 x 10^-¹²/s to 2.05 x 10^-⁹/s
    CRR    (N):    drawn 37%, 3.17 mm (0.125 inch) diameter bar || tested at 260 °C (500 °F) || 1.1 x 10^-¹¹/s to 4.4 x 10^-¹⁰/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || tested at 149 °C (300 °F) || 4.1 x 10^-¹³/s to 3.1 x 10^-¹¹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || tested at 204 °C (400 °F) || 4.2 x 10^-¹¹/s to 1.55 x 10^-¹⁰/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || tested at 260 °C (500 °F) || 1.6 x 10^-¹⁰/s to 1.9 x 10^-⁹/s

return to listing

UNS C87300

    E      (R):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 300 °C (572 °F)
    UTS    (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 371 °C (700 °F)
    YS     (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 371 °C (700 °F)
    %El    (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || 20 °C (68 °F) to 371 °C (700 °F)
    SR     (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 316 °C (600 °F) || 9 h to 2,300 h
    SR     (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 371 °C (700 °F) || 160 h to 3,250 h
    SR     (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || Master curve (LMP) || 6.72 h to 8.96 h
    CRR    (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 316 °C (600 °F) || 1.65 x 10^-¹¹/s to 1.7 x 10^-⁶/s
    CRR    (N):    as-cast, 25.4 mm x 178 mm (1 inch x 7 inch) block || tested at 371 °C (700 °F) || 8.3 x 10^-¹²/s to 6.2 x 10^-⁸/s

return to listing

UNS C10800

    UTS   (N*):    annealed rod, 13 micron grain size || room temperature value
    UTS   (N*):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    YS    (N*):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    %El   (N*):    annealed rod, 13 micron grain size || room temperature value
    %El   (N*):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || room temperature value
    SR     (N):    annealed rod, 13 micron grain size || tested at 149 °C (300 °F) || 1.5 h to 840 h
    SR     (N):    annealed rod, 13 micron grain size || tested at 204 °C (400 °F) || 1.6 h to 1,300 h
    SR     (N):    annealed rod, 13 micron grain size || Master curve (LMP) || 7.43 h to 9.79 h
    CRR    (R):    drawn 84%, 3.17 mm (0.125 inch) diameter bar || tested at 260 °C (500 °F) || 1.9 x 10^-¹¹/s to 5.6 x 10^-¹⁰/s

return to listing

UNS C51000

    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || tested at 149 °C (300 °F) || 520 h to 1,320 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || tested at 204 °C (400 °F) || 3 h to 1,280 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || Master curve (LMP) || 11.6 h to 13.3 h
    SR     (R):    spring || tested at 200 °C (392 °F) || 5 h to 190 h
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || tested at 149 °C (300 °F) || 8.3 x 10^-¹³/s to 3.65 x 10^-¹¹/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || tested at 204 °C (400 °F) || 8.3 x 10^-¹³/s to 1.5 x 10^-¹¹/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 50 micron grain size || tested at 260 °C (500 °F) || 1.1 x 10^-¹²/s to 5.1 x 10^-¹¹/s
    CRR    (R):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 2.5 x 10^-¹²/s to 7.6 x 10^-¹¹/s
    CRR    (R):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 8 x 10^-¹²/s to 7.8 x 10^-¹¹/s
    CRR    (R):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 260 °C (500 °F) || 4.5 x 10^-¹¹/s to 1.8 x 10^-¹⁰/s

return to listing

UNS C61300

E (R): solid || annealed || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)

return to listing

UNS C61400

E (R): solid || annealed || -269.1 °C (-452.5 °F) to 538 °C (1000 °F)

return to listing

UNS C62400

    E      (R):    sand cast || 20 °C (68 °F) to 538 °C (1000 °F)
    G     (R*):    solid || room temperature value
    K     (R*):    solid || room temperature value
    UTS    (N):    sand cast || 20 °C (68 °F) to 482 °C (899 °F)
    YS     (N):    sand cast || 20 °C (68 °F) to 538 °C (1000 °F)
    %El    (N):    sand cast || 20 °C (68 °F) to 538 °C (1000 °F)
    SR     (N):    sand cast || tested at 371 °C (700 °F) || 2.85 h to 3,250 h
    SR     (N):    sand cast || tested at 427 °C (800 °F) || 1.55 h to 3,050 h
    SR     (N):    sand cast || tested at 482 °C (900 °F) || 8.8 h to 160 h
    SR     (N):    sand cast || Master curve (LMP) || 9.7 h to 12.7 h
    CRR    (N):    sand cast || tested at 316 °C (600 °F) || 1.1 x 10^-¹⁰/s to 3.9 x 10^-⁷/s
    CRR    (N):    sand cast || tested at 371 °C (700 °F) || 1.4 x 10^-¹⁰/s to 8.7 x 10^-⁶/s
    CRR    (N):    sand cast || tested at 427 °C (800 °F) || 3 x 10^-¹¹/s to 1.45 x 10^-⁵/s
    CRR    (N):    sand cast || tested at 482 °C (900 °F) || 1.1 x 10^-¹⁰/s to 1.1 x 10^-⁶/s

return to listing

UNS C26000

    SR     (R):    annealed at 675 °C (1247 °F) || tested at 324 °C (615 °F) || 0.5 h to 170 h
    SR     (R):    annealed at 675 °C (1247 °F) || tested at 413 °C (775 °F) || 0.3 h to 200 h
    SR     (R):    annealed at 675 °C (1247 °F) || tested at 503 °C (937 °F) || 0.3 h to 270 h
    SR     (R):    annealed at 675 °C (1247 °F) || tested at 550 °C (1022 °F) || 0.2 h to 60 h
    SR     (R):    annealed at 675 °C (1247 °F) || Master curve (LMP) || 5.32 h to 8.99 h
    SR     (N):    annealed, 85 micron grain size || tested at 149 °C (300 °F) || 21 h to 2,100 h
    SR     (N):    annealed, 85 micron grain size || tested at 204 °C (400 °F) || 1.3 h to 680 h
    SR     (N):    annealed, 85 micron grain size || Master curve (LMP) || 7.11 h to 8.75 h
    SR     (N):    annealed, 16 micron grain size || tested at 149 °C (300 °F) || 53 h to 3,700 h
    SR     (N):    annealed, 16 micron grain size || tested at 204 °C (400 °F) || 2.2 h to 970 h
    SR     (N):    annealed, 16 micron grain size || Master curve (LMP) || 8.7 h to 9.73 h
    CRR    (N):    drawn 37% || tested at 149 °C (300 °F), 3.17 mm (0.125 inch) diameter bar, drawn 37% || 1.65 x 10^-¹²/s to 6.2 x 10^-¹⁰/s
    CRR    (N):    drawn 37% || tested at 260 °C (500 °F), 3.17 mm (0.125 inch) diameter bar, drawn 37% || 2.6 x 10^-¹¹/s to 1.05 x 10^-⁹/s
    CRR    (N):    drawn 84% || tested at 149 °C (300 °F), 3.17 mm (0.125 inch) diameter bar, drawn 37% || 6.9 x 10^-¹²/s to 2.8 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 204 °C (400 °F), 3.17 mm (0.125 inch) diameter bar, drawn 37% || 1.8 x 10^-¹¹/s to 7.4 x 10^-¹⁰/s
    CRR    (N):    drawn 84% || tested at 260 °C (500 °F), 3.17 mm (0.125 inch) diameter bar, drawn 37% || 1 x 10^-¹⁰/s to 3 x 10^-⁹/s

return to listing

UNS C64700

    SR     (R):    solution treated || Master curve (LMP) || 4.78 h to 6.76 h
    SR     (R):    precipitation hardened || Master curve (LMP) || 6.29 h to 10.3 h
    SR     (R):    precipitation hardened after 75% cold work || Master curve (LMP) || 6.99 h to 9.56 h
    SR     (R):    precipitation hardened after 88% cold work || Master curve (LMP) || 8.2 h to 10 h

return to listing

UNS C65100

    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 149 °C (300 °F) || 28 h to 2,150 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 204 °C (400 °F) || 57 h to 1,350 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 25 micron grain size || Master curve (LMP) || 6.7 h to 8.37 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 60 micron grain size || tested at 149 °C (300 °F) || 63 h to 2,700 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 60 micron grain size || tested at 204 °C (400 °F) || 6 h to 1,650 h
    SR     (N):    annealed, 3.17 mm (0.125 inch) rod, 60 micron grain size || Master curve (LMP) || 7.94 h to 9.65 h
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 149 °C (300 °F) || 1.35 x 10^-¹²/s to 8 x 10^-¹¹/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 204 °C (400 °F) || 1 x 10^-¹¹/s to 1.52 x 10^-¹⁰/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 60 micron grain size || tested at 149 °C (300 °F) || 3.3 x 10^-¹²/s to 3.4 x 10^-¹¹/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 60 micron grain size || tested at 204 °C (400 °F) || 5.8 x 10^-¹³/s to 6.2 x 10^-¹¹/s
    CRR    (R):    cold drawn 21%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 3.85 x 10^-¹²/s to 1.8 x 10^-¹⁰/s
    CRR    (R):    cold drawn 21%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 1.9 x 10^-¹²/s to 2.2 x 10^-¹⁰/s
    CRR    (R):    cold drawn 60%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 2.2 x 10^-¹²/s to 7.3 x 10^-¹¹/s
    CRR    (R):    cold drawn 60%, 3.17 mm (0.125 inch) rod || tested at 204 °C (400 °F) || 1.5 x 10^-¹²/s to 3 x 10^-¹⁰/s

return to listing

UNS C28000

    SR     (R):    annealed at 566 °C (1050 °F), 3.17 mm (0.125 inch) bar || tested at 149 °C (300 °F) || 50 h to 1,550 h
    SR     (R):    annealed at 566 °C (1050 °F), 3.17 mm (0.125 inch) bar || tested at 204 °C (400 °F) || 1.4 h to 1,100 h
    SR     (R):    annealed at 566 °C (1050 °F), 3.17 mm (0.125 inch) bar || Master curve (LMP) || 9.16 h to 11 h

return to listing

UNS C69400

    E      (R):    solid || 20 °C (68 °F) to 371 °C (700 °F)
    UTS   (N*):    as-cast || room temperature value
    YS    (N*):    as-cast || room temperature value
    %El   (N*):    as-cast || room temperature value
    CRR    (N):    as-cast || tested at 371 °C (700 °F) || 2 x 10^-⁹/s to 1.9 x 10^-⁵/s

return to listing

UNS C44400

    E      (R):    solid || 20 °C (68 °F) to 260 °C (500 °F)
    SR     (N):    3.17 mm (0.125 inch) diameter bar, annealed, 18 micron grain size || tested at 204 °C (400 °F) || 4.4 h to 1,500 h
    SR     (N):    3.17 mm (0.125 inch) diameter bar, annealed, 55 micron grain size || tested at 204 °C (400 °F) || 1.8 h to 1,250 h
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 18 micron grain size || tested at 149 °C (300 °F) || 5.5 x 10^-¹³/s to 1.4 x 10^-¹⁰/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 18 micron grain size || tested at 204 °C (400 °F) || 7.2 x 10^-¹²/s to 3.5 x 10^-¹⁰/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 18 micron grain size || tested at 260 °C (500 °F) || 5.5 x 10^-¹¹/s to 1.3 x 10^-⁹/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 55 micron grain size || tested at 149 °C (300 °F) || 3.8 x 10^-¹²/s to 7.8 x 10^-¹²/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 55 micron grain size || tested at 204 °C (400 °F) || 1.35 x 10^-¹²/s to 5.05 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, annealed, 55 micron grain size || tested at 260 °C (500 °F) || 1 x 10^-¹¹/s to 5.9 x 10^-¹¹/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, drawn 60% || tested at 149 °C (300 °F) || 4.4 x 10^-¹²/s to 1.7 x 10^-¹⁰/s
    CRR    (N):    3.17 mm (0.125 inch) diameter bar, drawn 60% || tested at 260 °C (500 °F) || 5.3 x 10^-¹¹/s to 2.4 x 10^-⁹/s

return to listing

UNS C71000

    UTS   (N*):    annealed 3.17 mm (0.125 inch) rod, 25 micron grain size || typical value || room temperature value
    YS     (N):    annealed 3.17 mm (0.125 inch) rod, 25 micron grain size || 20 °C (68 °F) to 261 °C (502 °F)
    CRR    (R):    annealed 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 149 °C (300 °F) || 2.7 x 10^-¹³/s to 1.15 x 10^-¹²/s
    CRR    (R):    annealed 3.17 mm (0.125 inch) rod, 25 micron grain size || tested at 260 °C (500 °F) || 1.1 x 10^-¹²/s to 1.4 x 10^-¹¹/s

return to listing

UNS C71500

    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 20 micron grain size || tested at 149 °C (300 °F) || 1.1 x 10^-¹²/s to 2.8 x 10^-¹²/s
    CRR    (R):    annealed, 3.17 mm (0.125 inch) rod, 20 micron grain size || tested at 260 °C (500 °F) || 2.5 x 10^-¹²/s to 2.4 x 10^-¹¹/s
    CRR    (N):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 149 °C (300 °F) || 1.35 x 10^-¹²/s to 2.55 x 10^-¹²/s
    CRR    (R):    drawn 84%, 3.17 mm (0.125 inch) rod || tested at 260 °C (500 °F) || 1.9 x 10^-¹²/s to 3.4 x 10^-¹¹/s

return to listing

UNS S44627 (E-BRITE)

    SR     (N):    annealed || tested at 800 °C (1472 °F) || 60 h to 550 h
    SR     (N):    annealed || tested at 850 °C (1562 °F) || 50 h to 540 h
    SR     (N):    annealed || tested at 900 °C (1652 °F) || 20 h to 2,200 h
    SR     (N):    annealed || Master curve (LMP) || 24.4 h to 28.4 h

return to listing

W - 15 Mo (wt %)

    CRS    (R):    1% plastic strain, universal forgings || Master curve (LMP) || 16.5 h to 19 h
    CRS    (R):    2% plastic strain, universal forgings || Master curve (LMP) || 23.6 h to 26.8 h
    CRS    (R):    3% plastic strain, universal forgings || Master curve (LMP) || 27.4 h to 31.2 h

return to listing

Waspaloy

    FEN    (N):    casting || tested at 649 °C (1200 °F), R = -1, plastic strain range || 1 cycles to 2 x 10³ cycles
    SR     (R):    age hardened bar || tested at 649 °C (1200 °F) || 25 h to 450 h
    SR     (R):    age hardened bar || tested at 732 °C (1350 °F) || 2 h to 170 h
    SR     (R):    age hardened bar || tested at 816 °C (1500 °F) || 0.3 h to 210 h
    SR     (R):    age hardened bar || Master curve (LMP) || 26.7 h to 32.4 h

return to listing

White iron austenitic (1 C - 2.55 Si - 31 Cr - 15 Ni - 0.5 Mn - 1 Al (wt %))

SR (R): austenitic || Master curve (LMP) || 21.6 h to 27.1 h

return to listing

White iron ferritic (2 C - 0.4 Si - 35 Cr - 0.4 Mn (wt %))

SR (R): ferritic || Master curve (LMP) || 12.3 h to 15.4 h

return to listing

White iron ferritic (1 C - 0.7 Si - 34 Cr - 0.3 Mn (wt %))

SR (R): ferritic || Master curve (LMP) || 14 h to 17.5 h

return to listing

X-40

    E      (N):    precision cast || 20 °C (68 °F) to 649 °C (1200 °F)
    UTS   (N*):    precision cast || room temperature value || room temperature value
    UTS    (N):    precision cast || elevated temperatures || 538 °C (1000 °F) to 982 °C (1799 °F)
    UTS   (N*):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || room temperature value || room temperature value
    UTS    (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || elevated temperatures || 871 °C (1600 °F) to 1093 °C (1999 °F)
    UTS   (N*):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || room temperature value
    YS    (N*):    precision cast || room temperature value || room temperature value
    YS     (N):    precision cast || elevated temperatures || 538 °C (1000 °F) to 649 °C (1200 °F)
    YS    (N*):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || room temperature value || room temperature value
    YS     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || elevated temperatures || 871 °C (1600 °F) to 1093 °C (1999 °F)
    YS    (N*):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || room temperature value
    %El   (N*):    precision cast || room temperature value || room temperature value
    %El    (N):    precision cast || elevated temperatures || 538 °C (1000 °F) to 982 °C (1799 °F)
    %El   (N*):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || room temperature value || room temperature value
    %El    (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || elevated temperatures || 871 °C (1600 °F) to 1093 °C (1999 °F)
    %El   (N*):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || room temperature value
    SR     (N):    as-cast || tested at 649 °C (1200 °F) || 50 h to 1.4 x 10⁴ h
    SR     (N):    as-cast || tested at 816 °C (1500 °F) || 1.9 h to 7,800 h
    SR     (N):    as-cast || Master curve (LMP) || 19.1 h to 24.9 h
    SR     (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 732 °C (1350 °F) || 100 h to 1,200 h
    SR     (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 27 h to 1,100 h
    SR     (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 1093 °C (2000 °F) || 0.8 h to 90 h
    SR     (N):    cast, aged 50 h at 732 °C (1350 °F) || Master curve (LMP) || 28.2 h to 36.1 h
    SR     (N):    cast, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 13 h to 2,050 h
    SR     (N):    cast, aged 50 h at 871 °C (1600 °F) || tested at 871 °C (1600 °F) || 35 h to 2,600 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || tested at 871 °C (1600 °F) || 17 h to 260 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || tested at 927 °C (1700 °F) || 85 h to 430 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || tested at 982 °C (1800 °F) || 6 h to 165 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || tested at 1038 °C (1900 °F) || 18 h to 90 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || tested at 1093 °C (2000 °F) || 3.5 h to 35 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) sheet || Master curve (LMP) || 21.2 h to 25.7 h
    SR     (N):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || tested at 871 °C (1600 °F) || 23 h to 180 h
    SR     (N):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || tested at 982 °C (1800 °F) || 18 h to 115 h
    SR     (N):    1204 °C (2200 °F), air cooled, 1.63 mm (0.064 inch) sheet || Master curve (LMP) || 20.8 h to 23.6 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) and 1.63 mm (0.064 inch) sheets || tested at 871 °C (1600 °F) || 17 h to 260 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) and 1.63 mm (0.064 inch) sheets || tested at 982 °C (1800 °F) || 6 h to 170 h
    SR     (N):    1204 °C (2200 °F), air cooled, 0.965 mm (0.038 inch) and 1.63 mm (0.064 inch) sheets || Master curve (LMP) || 18 h to 21 h
    CRR    (N):    as-cast || tested at 649 °C (1200 °F) || 2 x 10^-¹¹/s to 1.1 x 10^-¹⁰/s
    CRR    (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F) || 8.3 x 10^-¹⁰/s to 2.6 x 10^-⁷/s
    CRR    (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 1093 °C (2000 °F) || 6.6 x 10^-⁹/s to 4.2 x 10^-⁵/s
    CRR    (N):    cast, aged 50 h at 732 °C (1350 °F) || tested at 816 °C (1500 °F), cored dendritic structure || 5.5 x 10^-¹²/s to 8.5 x 10^-⁸/s
    CRR    (N):    cast, aged 50 h at 816 °C (1500 °F) || tested at 816 °C (1500 °F) || 3.3 x 10^-¹¹/s to 3 x 10^-⁷/s
    CRR    (N):    cast, aged 50 h at 871 °C (1600 °F) || tested at 871 °C (1600 °F) || 6.9 x 10^-¹¹/s to 2.8 x 10^-⁸/s

return to listing

XA704

    SR     (R):    solution treated || tested at 600 °C (1112 °F) || 5.3 x 10³ h to 5.3 x 10⁴ h
    SR     (R):    solution treated || tested at 650 °C (1202 °F) || 660 h to 7.4 x 10⁴ h
    SR     (R):    solution treated || tested at 700 °C (1292 °F) || 230 h to 4.8 x 10⁴ h
    SR     (R):    solution treated || tested at 750 °C (1382 °F) || 130 h to 1.8 x 10⁴ h
    SR     (R):    solution treated || tested at 800 °C (1472 °F) || 170 h to 1.4 x 10⁴ h
    SR     (R):    solution treated || tested at 850 °C (1562 °F) || 830 h to 2,800 h
    SR     (R):    solution treated || Master curve (LMP) || 16.8 h to 21.3 h

return to listing

XYRON 300H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 400H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

XYRON 500H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 600H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

XYRON 1000H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 200H (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 1951J (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 540V (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 200V (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 640V (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

XYRON 340V (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 240W (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

XYRON 340W (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 1 MHz

return to listing

XYRON 540Z (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 440Z (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 340Z (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 644Z (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

XYRON 240Z (New)

    DLL       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    DLL       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    MTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || parallel to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || transverse to the flow direction || -30 °C (-22 °F) to 65 °C (149 °F)
    CTE       :    solid || calculated as the weighted average of the flow and cross-flow directions || -30 °C (-22 °F) to 65 °C (149 °F)
    D         :    solid || -30 °C (-22 °F) to 65 °C (149 °F)
    RHO   (*):    solid || room temperature value
    SIGMA (*):    solid || room temperature value
    SRHO (*):    solid || room temperature value
    FS    (*):    ISO 178 || typical value || room temperature value
    FM    (*):    ISO 178 || typical value || room temperature value
    YS    (*):    ISO 527 || typical value || room temperature value
    %El   (*):    ISO 527 || at break || room temperature value
    DCRPT    :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz
    DF        :    IEC 60250 || tested at 23 °C (73 °F) || 100 Hz to 5.2 GHz

return to listing

Zircaloy-2

    SR     (R):    annealed sheet || tested at 150 °C (302 °F) || 0.3 h to 120 h
    SR     (R):    annealed sheet || tested at 230 °C (446 °F) || 0.2 h to 120 h
    SR     (R):    annealed sheet || tested at 425 °C (797 °F) || 3 h to 670 h
    SR     (R):    annealed sheet || tested at 500 °C (932 °F) || 0.3 h to 200 h
    SR     (R):    annealed sheet || Master curve (LMP) || 2.68 h to 6.98 h
    CRS    (R):    0.1% total strain, annealed sheet || tested at 425 °C (797 °F) || 0.5 h to 130 h
    CRS    (R):    0.1% total strain, annealed sheet || tested at 500 °C (932 °F) || 0.1 h to 620 h
    CRS    (R):    0.2% total strain, annealed sheet || tested at 345 °C (653 °F) || 0.1 h to 1,000 h
    CRS    (R):    0.2% total strain, annealed sheet || tested at 425 °C (797 °F) || 0.14 h to 700 h
    CRS    (R):    0.2% total strain, annealed sheet || tested at 500 °C (932 °F) || 0.1 h to 1,100 h
    CRS    (R):    0.5% total strain, annealed sheet || tested at 150 °C (302 °F) || 0.5 h to 100 h
    CRS    (R):    0.5% total strain, annealed sheet || tested at 345 °C (653 °F) || 0.5 h to 1,000 h
    CRS    (R):    0.5% total strain, annealed sheet || tested at 425 °C (797 °F) || 0.5 h to 270 h
    CRS    (R):    0.5% total strain, annealed sheet || tested at 500 °C (932 °F) || 0.5 h to 1,100 h
    CRS    (R):    1% total strain, annealed sheet || tested at 150 °C (302 °F) || 0.1 h to 160 h
    CRS    (R):    1% total strain, annealed sheet || tested at 230 °C (446 °F) || 0.01 h to 130 h
    CRS    (R):    1% total strain, annealed sheet || tested at 345 °C (653 °F) || 0.5 h to 1,000 h
    CRS    (R):    1% total strain, annealed sheet || tested at 425 °C (797 °F) || 0.5 h to 550 h
    CRS    (R):    1% total strain, annealed sheet || tested at 500 °C (932 °F) || 0.25 h to 900 h

return to listing

ZK60

    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = -1, K_t = 2.4, 60 Hz, axial, maximum stress || 4 x 10³ cycles to 5 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = -0.17, K_t = 2.4, 60 Hz, axial, maximum stress || 4 x 10³ cycles to 5 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = 0.25, K_t = 2.4, 60 Hz, axial, maximum stress || 3 x 10³ cycles to 5 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = 0.6, K_t = 2.4, 60 Hz, axial, maximum stress || 4 x 10³ cycles to 5 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = -1, K_t = 3.4, 60 Hz, axial, maximum stress || 3 x 10³ cycles to 2 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = -0.17, K_t = 3.4, 60 Hz, axial, maximum stress || 3 x 10³ cycles to 2 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = 0.25, K_t = 3.4, 60 Hz, axial, maximum stress || 1 x 10³ cycles to 2.2 x 10⁷ cycles
    FSN    (N):    ZK60A-T5 extrusions || tested at 20 °C (68 °F), R = 0.6, K_t = 3.4, 60 Hz, axial, maximum stress || 4 x 10³ cycles to 5 x 10⁷ cycles

return to listing

Changes